Abstract
Both in-plane as well as c-axis electrical resistivity of Stage 2 and Stage 5 K-FeCl3 graphite intercalation compounds were measured from room temperature down to 12 K by using a standard four-probe method. The in-plane electrical resistivity exhibited a metallic behaviour. The c-axis resistivity exhibited an activated behaviour and the data were fitted to a model which assumes a variable-range hopping conduction in parallel with band conduction. The Hall effect was measured in a low magnetic field up to 5 kG at temperatures 300, 77 and 12 K. The Hall coefficient was found to be positive, indicating that the conduction takes place by holes. The carrier concentrations were calculated using a one-carrier model.
Similar content being viewed by others
References
M. S. Dresselhaus and G. Dresselhaus, Adv. Phys. 30 (1981) 139.
S. A. Solin, Adv. Chem. Phys. 49 (1982) 455.
B. R. York, S. K. Hark and S. A. Solin, Phys. Rev. Lett. 50 (1983) 1470.
Von K. Steinwede and E. Stumpp, Z. Anorg. Allg. Chem. 469 (1980) 101.
M. Suzuki, I. Oguro and Y. Jinzaki, J. Phys. C 17 (1984) L575.
R. Niess and E. Stumpp, Carbon 16 (1978) 265.
M. Suzuki, P. C. Chow and H. Zabel, Phys. Rev. B 32 (1985) 6800.
P. Lagrange, A. B. Rerhrhaye, J. F. Marêché and E. Mcrae, Synth. Met. 12 (1985) 201.
P. Pernot, J. F. Marêché, E. Mcrae, R. Vangélisti, M. K. Alaoui, L. Piraux, V. Bayot and J.-P. Issi, ibid. 34 (1989) 473.
D. Guérard, L. Elansari, N. E. Elalem, J. F. Marêché and E. Mcrae, ibid. 34 (1989) 27.
G. O. Zimmerman and A. K. Ibrahim, US Pat. 4837377 (1989).
G. H. Kinchin, Proc. R. Soc. A217 (1953) 9.
D. E. Soule, Phys. Rev. 112 (1958) 698.
K. T. Kawamura, T. Saito and T. Tsuzuku, J. Phys. Soc. Jpn. 42 (1977) 574.
J. F. Marêché, E. Mcrae, A. Bendrissrerhrhaye and A. Lagrange, J. Phys. Chem. Soc. 47 (1986) 477.
E. Mcrae, J. F. Marêché, A. B. Rerhrhaye, P. Lagrange and M. Lelaurain, Ann. Phys. 11 (1986) 13.
C. A. Klein, Rev. Mod. Phys. 34 (1962) 56.
W. W. Tyler and A. C. Wilson, Phys. Rev. 89 (1953) 870.
J. J. Murray and A. R. Ubbelohde, Proc. R. Soc. A312 (1969) 371.
R. Powers, A. K. Ibrahim, G. O. Zimmerman and M. Tahar, Phys. Rev. B38 (1988) 680.
B. I. Shklovskii and A. L. Efros, in “Electronic Properties of Doped Semiconductors” (Springer, Berlin, 1984).
K. Sugihara, I. Shiozaki, S. M. Sampere, M. Suzuki, J. T. Nicholis and G. Dresselhaus, Synth. Met. 34 (1989) 543.
I. L. Spain, A. R. Ubbelohde and D. A. Young, Phil. Trans. R. Soc. A262 (1967) 345.
T. Tsuzuku and T. Takezawa, Philos. Mag. 25 (1972) 929.
W. Lang, Synth. Met. 34 (1989) 491.
O. El-Shazly, S. G. Tawfik, A. K. Ibrahim, I. H. Ibrahim, and E. F. El-Wahidy, J. Phys. D. (1993) accepted for publication.
D. Guèrard, G. M. T. Foly, M. Zanini and J. E. Fischer, Nuovo Cimento B38 (1977) 410.
H. Suematsu, K. Higuchi and S. Tanuma, J. Phys. Soc. Jpn. 48 (1980) 1541.
O. El-Shazly and A. I. Abou-Ali, J. Phys. Chem. Solids 52 (1991) 643.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
El-Shazly, O., Tawfik, S.G., Ibrahim, A.K. et al. Electrical resistivity and Hall effect of K-FeCl3 graphite intercalation compounds. JOURNAL OF MATERIALS SCIENCE 28, 5040–5044 (1993). https://doi.org/10.1007/BF00361175
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00361175