Summary
Large weight losses occurred in thin veneers of radiata pine (P. radiata) during natural weathering due mainly to loss of lignin and hemicelluloses. This was demonstrated by direct chemical analysis and by spectrocopic techniques. Treatment of veneers with dilute aqueous solutions of the recognized surface stabilizing compound chromium trioxide was found to dramatically restrict weight loss during weathering, but similar applications of ferric compound were less effective (Evans, Schmalzl 1989). In order to rationalize these protective effects FTIR internal reflectance spectroscopy was used to study chemical changes taking place at the wood surface upon treatment and during weathering. The spectra obtained provide direct evidence for the modification and stabilization of the lignin aromatic system with aqueous chromium trioxide and to a lesser extent with ferric salts. It is postulated that photostable lignin complexes are formed. The implications of these findings for the development of improved surface stabilizing compounds for wood are discussed briefly.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Ashton, H. E. 1967: Clear finishes for exterior wood, field exposure tests. J. Paint Technol. 39: 212–224
Azuma, J.-I. 1989: Analysis of lignin-carbohydrate complexes of plant cell walls. In: Linskens, H. F.; Jackson, J. F. (Eds.) Plant fibers. New series, Modern methods of plant analysis, Vol. 10, pp 100–126. Berlin: Springer
Browning, B. L. 1967: Methods of wood chemistry. Vol, 2, Chap. 5, pp. 79–81, Chap. 19, pp. 394–408. New York: J. Wiley
Chang, S. T.; Hon, D. N. S.; Feist, W. C. 1982: Photodegradation and photoprotection of wood surfaces. Wood Fiber. 14: 104–117
Derbyshire, H.; Miller, E. R. 1981: The photodegradation of wood during solar irradiation. Part 1. Effects on the structural integrity of thin wood strips. Holz Roh-Werkstoff 39: 341–350
Evans, P. D. 1988: A note on assessing the deterioration of thin wood veneers during weathering. Wood Fiber Sci. 20: 487–492
Evans, P. D. 1989: Effect of angle of exposure on the weathering of wood surfaces. Polym. Degrad. Stabil. 24: 81–87
Evans, P. D.; Banks, W. B. 1988: Degradation of wood surfaces by water. Changes in mechanical properties of thin wood strips. Holz Roh-Werkstoff 46: 427–435
Evans, P. D.; Schmalzl, K. J. 1989: A quantitative weathering study of wood surfaces modified by chromium VI and iron III compounds. Part 1. Loss in zero-span tensile strength and weight of thin wood veneers. Holzforschung 43: 289–292
Feist, W. C. 1977: Finishing wood for exterior applications —paints, stains, and pretreatments. In: Goldstein, I. S. (Ed.): Wood Technology, Chemical Aspects. Ser. 43., Chap. 19, pp. 294–300. Washington D. C.: Amer. Chem. Soc.
Harrington, K. J.; Higgins, H. G.; Michell, A. J. 1964: Infrared spectra of Eucalyptus regnans F. Muell and Pinus radiata D. Don. Holzforschung 18: 108–113
Michell, A. J. 1988: Note on a technique for obtaining infrared spectra of treated wood surfaces. Wood Fiber Sci. 20: 272–276
Michell, A. J. 1989: Second derivative FTIR spectra of woods. In: Schuerch, C. (Ed.): Cellulose and wood; Chemistry and technology. Proceedings of the 10th Cellulose Conference, pp 995–1009. New York: J. Wiley
Michell, A. J. 1990: Unpublished results
Ohtani, K. 1987: Chromium trioxide enhances the durability of wooden doors. Chromium Rev. 8: 4–7
Pizzi, A. 1980: Wood water proofing and lignin cross linking by means of chromium trioxide/ guaiacyl units complexes. J. Appl. Polym. Sci. 25: 2547–2553
Ritter, G. J.; Seborg, R. M.; Mitchell, R. L. 1932: Factors affecting quantitative determination of lignin by 72 per cent sulfuric acid method. Ind. Eng. Chem. (Anal. Ed.). 4: 202–204
Schmalzl, K. J.; Vickers, L. J. 1990: Unpublished results
Smelstorius, J. A. 1974: Chemical composition of wood of Australian-grown Pinus radiata D. Don. II. Polysaccharides. Holzforschung 28: 67–73
Williams, R. S.; Feist, W. C. 1985: Wood modified by inorganic salts: mechanism and properties. I. Weathering rate, water repellency, and dimensional stability of wood modified with chromium (III) nitrate versus chromic acid. Wood Fiber Sci. 17: 184–198
Williams, R. S.; Feist, W. C. 1988: Performance of finishes on wood modified with chromium nitrate versus chromic acid. Forest Prod. J. 38 (11/12): 32–35
Author information
Authors and Affiliations
Additional information
The authors wish to thank the following: Tom Syers and Lloyd Vickers (C.S.I.R.O., Division of Forestry and Forest Products); Helen Neave, and Clive Hilliker (Australian National University, Department of Forestry) for technical assistance, and the Stanley Melbourne Bruce fund for financially supporting part of the work
Rights and permissions
About this article
Cite this article
Evans, P.D., Michell, A.J. & Schmalzl, K.J. Studies of the degradation and protection of wood surfaces. Wood Sci.Technol. 26, 151–163 (1992). https://doi.org/10.1007/BF00194471
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00194471