Ciprofloxacin degradation with a defective TiO2-x nanomaterial under sunlight

TiO2 nanoparticles obtained by microwave-assisted hydrothermal synthesis were subjected to facile post-processing based on vacuum annealing. The resulting defective (TiO2-x) material showed extended light absorption in the visible range, enhancing sunlight compatibility. Structural and optical characterization point to the arising of an Urbach tail as the main reason. TiO2-x was then employed as photocatalyst for the inactivation of ciprofloxacin, an emerging environmental threat and source of antimicrobial resistance, under sunlight. TiO2-x performed significantly better than its parent compound and mechanistic analysis of the degradation pathway indicates that this material is a promising candidate for solar treatment of fluoroquinolones residues in water.


Introduction
Titanium dioxide is a benchmark material for heterogeneous photocatalysis, owing to a combination of good catalytic performance with remarkable chemical stability in a wide range of experimental conditions. [1]However, decades of research notwithstanding, actual applications to solar photocatalysis of this material are still limited because of poor, owing to a band structure only allowing absorption of the UV fraction of the spectrum. [2]A variety of methods have been developed over time to address this issue, including tweaking the electronic structure by doping, [3,4] sensitization by coupling with molecular or plasmonic absorbers, [5,6] and the fabrication of composites. [7,8]Another approach relies on inducing surface defects in the material which result in a smaller optical band gap and/or the rising of an Urbach tail. [9,10]To this scope, oxygen vacancies and Ti 3+ have been shown to be particularly effective for photocatalysis purpose. [11,12]A different approach to the issue of low compatibility between TiO 2 absorption and sunlight spectrum is that of working not on the material but on the illumination source, for example, by manipulating solar radiation using concentrating collectors. [13]In this case, the increasing availability of economically viable concentrator-based processes is an important progress towards applications. [14]he equipment to make an effective use of the UV fraction of sunlight remains significantly complex though, requiring for example especially designed mirrors based on anodized aluminum. [15]Thus, improving the optical matching between TiO 2 and sunlight would be greatly beneficial also in this context.
In this work, we investigated a facile modification of a TiO 2 nanomaterial, resulting in extended light absorption in the visible range.A microwave-assisted hydrothermal synthesis was employed to obtain TiO 2 nanopowders, which were then annealed in vacuum.The resulting material (TiO 2-x ) shows a color change to light-brown, a decreased, albeit modestly optical band gap, but especially the arising of an absorption tail in the visible range.Optical and structural properties were investigated by UV-Vis and micro-Raman spectroscopy, electron microscopy both in scanning (SEM) and transmission (TEM) mode, and selected area electron diffraction (SAED).To verify the suitability of this material for solar photocatalysis, the degradation of Ciprofloxacin (CIP) under direct sunlight was studied and a reaction mechanism investigated by determining intermediates with High-Performance Liquid Chromatography (HPLC) methods.CIP, a fluoroquinolone antibiotic used in both medicine and veterinary medicine, was selected as the target pollutant for several reasons: (a) it is one of the most used fluoroquinolones worldwide, employed in massive quantities; (b) current wastewater treatment processes are only marginally effective at removing CIP, and consequently, it has been detected in surface waters worldwide; (c) as such, it can heavily contribute to the rise of antimicrobial resistance (AMR), a top threat to public health. [16]In this framework, solar photocatalysis is a promising approach for a potentially cost-effective, sunlight-driven pollutant degradation process with high efficiency.Also, it is worth considering that while the ultimate goal of solar photocatalysis treatments is generally considered as the total removal of pollutants via mineralization, AMR reduction in principle only requires the inactivation of antibiotic residues in water.This is, at least on paper, a less demanding goal. [17]aterials and methods Reagents TiO 2 nanopowders were synthesized using titanium butoxide (Ti(C 4 H 9 O) 4 purum, ≥ 97.0% gravimetric, Sigma-Aldrich) as precursor and 2-butanol (C 4 H 10 O, purity ≥ 99.5% gravimetric, Sigma-Aldrich) as solvent.Ciprofloxacin (C 17 H 18 FN 3 O 3 , MW: 385.82 g/mol, Standard PHR1044-1G, Sigma-Aldrich).All reagents and chemicals were used as received.

Synthesis
TiO 2 nanopowders were produced employing a microwaveassisted protocol adapted from the literature: [18] 16 ml of titanium butoxide was mixed with 100 ml of 2-butanol and 5 ml of deionized water (DI) was then added in droplets.The resulting suspension was stirred under cooling (ice bath) for 30 min, followed by overnight stirring at room temperature and then transferred to a 35 ml CEM microwave vessel.TiO 2 was then obtained via microwave-assisted hydrothermal treatment of the suspension at 180°C for 1 h (3°C/min) using a CEM Discover S-Class microwave system set to a power of 220 watts and 2455 MHz frequency.The resulting powder was washed with water and ethanol, dried at 60°C, crushed, and calcined in a muffle furnace at 400°C for 4 h with a heating rate of 9°C/min.To obtain the TiO 2-x material, the protocol was followed by overnight thermal annealing in a custom-built vacuum oven (10 -8 mBar, 400°C, at 5°C/min) equipped with a drag-stage turbomolecular pump and a membrane pump for pre-vacuum.

Characterization
Raman measurements were performed on a Horiba LabAramis setup equipped with a HeNe 633 nm laser as source and a confocal microscope (100 × objective) coupled to a 460 mm focal length CCD-based spectrograph equipped with a four interchangeable gratings turret.Wavenumber accuracy was 1 cm −1 with an 1800 L/mm grating.A field emission scanning electron microscope (FESEM, JSM 7001 F, JEOL) equipped with energy-dispersive X-Ray spectroscopy analysis (EDXS, Oxford INCA PentaFET-× 3) was used to investigate particle morphology and composition.Further structural analysis was performed with TEM and high-resolution-TEM (HRTEM) imaging, as well as SAED patterns obtained with a Thermo Scientific™ Talos™ F200S scanning/transmission electron microscope (S/TEM) set to 200 kV accelerating voltage.UV-Vis reflectance was measured using a VARIAN Cary 5000 UV-Vis-NIR spectrophotometer over a wavelength range of 200 to 800 nm.Both the Kubelka-Munk function and the Tauc equation were used to evaluate the indirect bandgap of the synthesized nanomaterials.In Eq. 1, the Kubelka-Munk function F(R) is defined as follows: where R is the reflectance of the sample.
The Tauc equation for indirect electronic transitions is where α is the optical absorption coefficient, which can be replaced in the Tauc equation by F(R) calculated from the Kubelka-Munk function; hν is the incident photon energy in eV; A is the material-dependent absorption constant; and Eg is the nanomaterial's bandgap energy.
Photocatalysis experiments were carried out in a pyrex vessel containing 50 ml of 10 ppm CIP solution, and samples were kept in the dark for 30 min to achieve adsorption-desorption equilibrium and afterwards exposed to direct sunlight for 180 min., in the period of November and December 2022 in Trento (Italy, coordinates 46.066408° N, 11.150723° E) between 10:30 and 14:00 local time.The spectrum of incident sunlight was measured with a portable mini-spectrometer (Hamamatsu C10082CA) and is reported in supplementary Figure S1, while solar irradiation measurements were performed using a Kipp & Zonnen CHP1 pyrheliometer with monitored readings between 720 and 750 W/m 2 .Blank experiments were performed to test for the effects of direct photolysis of CIP by either sunlight, artificial 365 nm UV light (Actinic Philips BL TL-D 15W/10 1SL/25, luminous flux of 130 lumens, positioned at 40 cm above the solution) or thermolysis at 50°C.Where the catalysts are present, a loading of 0.5 g/l was adopted.Mixing and catalyst dispersion were ensured by means of a Hielscher UP400s probe sonicator at 1 cycle, 50% amplitude.Except where otherwise noted, samples were taken at − 30 (ref), 0, 15, 30, 45, 60, 90, 120, 150, and 180 min.The degradation of CIP was monitored by acquiring the absorption spectra using a VARIAN Cary 5000 UV-Vis-NIR spectrophotometer over a wavelength range of 200 to 400 nm. 1 ml of solution was filtered over a 0.2 µm cellulose acetate membrane syringe filter (VWR) to avoid excessive scattering by the photocatalyst.
The degradation of CIP was calculated using the following equation: where C o is the initial molar concentration of CIP obtained from A o (the initial absorbance at λ max = 272 nm) and C is the molar concentration of CIP after each sampling interval obtained from the absorbance A (the absorbance of CIP at λ max after each sampling interval).A verification of the Lambert-Beer law indicating a linear correlation between CIP Abs and concentration in the explored range is provided in figure S10. (1) Analysis of the products related to CIP photocatalytic degradation was conducted by liquid chromatography (Model 1100 Series, HP) coupled to photodiode-array detector (Model Agilent, 1100 Series, PDA), and to mass spectrometer (Bruker Esquire-LC quadrupole ion trap) in positive-ion-mode Electrospray ionization source (ESI +).Chromatographic separation was carried out on a C18 column at 303 K (Eclipse XDB-C18, Agilent Technologies, 3.5µ 150 × 4.6 mm; flow 1.0 ml/min; T = 30°C; injected volume = 10 ul).The mobile phase consisted of solvent 1 (water 20% + trifluoroacetic acid 0.1%) and solvent 2 (MeOH 80% + trifluoroacetic acid 0.1%) at a flow of 1 mL/min.The DataAnalysis 3.0 software was used to integrate the collected ion chromatograms from the positive-ion full scan mode (50-500 Da) for the structural assignment of species (Bruker Daltonik, Bremen, Germany).A working curve of the available standard of CIP was built by recording UV (λ = 280 nm) peak areas for several solution of CIP obtained by sequential dilution of a 10 mg/L mother solution.The rate constant of disappearance (degradation) was calculated assuming a pseudo-first-order kinetics: where C o and C are, respectively, the initial and the actual molar concentration of CIP at λ = 278 nm at a given timepoint of the CIP degradation and k obs is the total observed kinetic constant.A qualitative determination of CO 2 evolution along the degradation experiment was measured to detect eventual mineralization, using a sensor (5% model GSS COZIR, Gaslab software monitor) with an acquisition every 30 s with the device placed 3 cm above the reactor.This measurement provides a qualitative data of the variation in the atmospheric level of CO 2 at the experiment immediate surroundings.

Results and discussion
Micro-Raman spectroscopy was used to identify the crystal phases in TiO 2 and TiO 2-x nanopowders, and related spectra are reported in Figure S2.Both materials show the characteristic peaks of both anatase and brookite phases: the highintensity sharp shape peak at 143 cm −1 is consistent to Eg and A1g modes of, respectively, anatase and brookite phases.The peaks at 196 (Eg), 398 (B1g), 516 (A1g), and 638 (Eg) reveal the presence of anatase while the characteristic peaks of brookite appear with low intensities at 245 (A1g), 320 (B1g), and 367 cm −1 (B2g). [19]The similarity between TiO 2 and TiO 2-x nanomaterials reveals that no significant change in the crystallinity of TiO 2-x is observed after annealing under vacuum.Morphology and size of both synthesized materials were investigated by using SEM and HRTEM techniques.SEM images shown in Fig. S3 indicate both TiO 2 (a) and TiO 2-x (b) consisting of agglomerated small particles in the range from 10 to 20 nm, mostly spherical in shape.This indicates that morphology is not significantly affected by the vacuum annealing.This  Further analysis of the SAED data confirms this initial observation.Starting from the diffraction ring patterns, the integral intensities were calculated as function of the scattering angles, thus, obtaining the diffraction data reported in Figure S4.22] Conclusively, we can say that annealing under vacuum does not have a significant detectable effect on the crystalline phase of the material.
UV-visible spectroscopy data are shown in Fig. 2 below.While structural characterization did not show appreciable differences in the two synthesized materials, their optical properties are remarkably different.After vacuum annealing, the powders show a clear change in color from white to lightbrown, arising from an absorption tail in the spectrum of TiO 2-x (Fig. 2, top) extending into the visible range.Tauc plots (Fig. 2, bottom) are compatible with an indirect optical band gap of 3.18 eV for TiO 2 , slightly narrowed to 3.11 eV for TiO 2-x .From these data, the change in color is primarily due to the absorption tail into the visible range.This is compatible with an Urbach model, where point surface defects are responsible for localized color centers, generally involving oxygen vacancies and showing a wide range of excitation energies altering the electronic structure of TiO 2 . [23]The improved absorption due to the slightly lower band gap in defective TiO 2-x than TiO 2 could be related to the presence of localized defects states in the band gap of TiO 2-x .These localized defects could produce an absorption tail extending into forbidden gap. [24,25]Therefore, in case of TiO 2-x, the high Urbach energy is expected due to the presence of more oxygen vacancies and surface defects.Further, a qualitatively higher brightness of SAED for TiO 2-x can be observed when compared to TiO 2 [Fig.1(c, f)] which, according to the literature Refs.24,25, is related to changes on the surface defects states, as the crystalline phases are the same in both samples.In fact, in-depth XPS analysis in the literature for materials obtained in similar conditions, frequently shows the features of undervalent Ti(III). [26,27]This hypothesis is also supported by the characterization for TiO 2 and TiO 2-x , where both morphology and crystal phase are very similar, more compatible with the low density, surface-localized point defects of the Urbach model than with the presence of bulk defects and/or an high density of point defects extending into the bulk.
Given that the optical properties of TiO 2-x suggest an increased compatibility with the sunlight spectrum than for TiO 2 , CIP photodegradation experiments where performed to investigate a possible application of this material for solar wastewater remediation.Blank experiments to evaluate the effect of CIP thermolysis, photolysis under UV 365 nm light, and under sunlight, are reported in the Supplementary Figure S5.In the experimental conditions and time scale explored (180 min treatments), CIP is shown to be substantially stable, with a maximum of about 10% degradation under sunlight at the end of irradiation, while no thermolysis was detected.Significant degradation is instead observed when TiO 2 and TiO 2-x were present, as reported in Fig. 3 below.
In these experiments, TiO 2-x showed both better adsorption capability, likely due to the presence of surface defects as previously reported in the literature, [28] and increased rate constant with respect to TiO 2 , resulting in earlier (90 min) significant disappearance of the CIP absorption.CIP degradation products of the experiment performed with TiO 2-x were investigated by LC-UV-MS measurements.The chromatogram is reported in Supplementary Figure S6, with the main signals (labeled from 1 to 10), as detected by PDA at λ 278 nm after 60 min of treatment, attributed to ciprofloxacin derivatives since none of these peaks were detected in the CIP standard before treatment.The structures were tentatively assigned by analyzing their LC-MS spectra and   by comparison with MS data previously reported in the literature. [29]The degradation products shown in Fig. 4 and their corresponding UV absorption peaks (Supplementary Fig. S7) mainly derive from the partial • OH radicals attack towards the cleavage of the piperazynilic ring of the ciprofloxacin molecule, leading to 8 fragmented subproducts with masses of m/z values 332.14.334.16, 348.14, 362.11, 306.12, 165.06, 263.08, and 291.11. [30,31]n agreement with Ohko et al. [32] and Zhang et al. [33] , the pathway for CIP degradation is here based on the photo-hole (h + ) oxidation and hydroxylation given by the TiO 2-x photocatalyst.In the first step, the fluorine atom electronegativity subjects the piperazynilic ring to angle stresses which likely lead to a partial release of ethylene groups and formation of desethylene.In CIP, defluorination and decarboxylation are the main events given the existence of two powerful electron extracting substituents (carboxylic and fluorine groups).The concomitance of the degradation of both piperazynilic and defluorination is observed and leads to lower molecular weight compounds. [34]Finally, it is observed that the central quinolone and cyclopropyl structures remain along all the observed subproducts as confirmed by the literature. [35]he LC-MS degradation kinetics constant k obs , obtained by recording UV (λ = 280 nm) peak areas for the CIP solution and resulting from the sum of all the degradation processes, was 3 × 10 -2 in accordance (Supplementary S8) with the value obtained by spectrophotometry analysis.The CO 2 evolution measurement was also run during the experiment with TiO 2-x .The resulting data (Supplementary Fig. S9) show a significant increase in CO 2 above ambient levels, indicating that also a degree of mineralization occurs.Overall, these results point to a degradation pathway leading to significant modification of CIP, with the potential for application to solar inactivation of CIP in wastewaters.

Conclusions
In this work, a simple vacuum annealing on TiO 2 nanopowders proved to be an effective method to induce optical properties change, extending absorption into the visible range.Structural and optical characterization of the resulting material point to the arising of an Urbach tail as the main reason for this behavior.When tested for photocatalysis of CIP under sunlight, such TiO 2-x material proved to be more performing than its TiO 2 counterpart, showing that the modification is effective at enhancing photoactivity.Analysis of the CIP degradation pathway and products indicates that this material is a promising candidate for solar photocatalytic treatments aimed at fluoroquinolones inactivation.The results reported here are a decisive step forward in this direction.
observation is confirmed by TEM images (Fig.1), where the size and shape of TiO 2 (a, b) and TiO 2-x (d, e) nanoparticles are very similar.In both cases, small (10-20 nm) and spherical nanoparticles have been observed.Their corresponding SAED pattern (c, f) indicates the crystalline nature of nanoparticles, mainly of anatase phase (101) with a d-spacing d = 0.35 nm [magnified images Fig. 1(b, e)].

Figure 3 .
Figure 3. Photocatalysis experiments under sunlight (PCSun) for a 10 ppm CIP solution in presence of 0.5 g/l TiO 2 (black line) or TiO 2-x (red line).Evaluated kinetic constants are reported in the inset.