Development of an Image-based Method for Tablet Microstructure Description and Its Correlation with API Release Rate

The performance of a pharmaceutical formulation, such as the drug (API) release rate, is significantly influenced by the properties of the materials used, the composition of the final product and the tablet compression process parameters. However, in some cases, the knowledge of these input parameters does not necessarily provide a reliable description or prediction of tablet performance. Therefore, the knowledge of tablet microstructure is desirable to understand such formulations. Commonly used analytical techniques, such as X-ray tomography and intrusion mercury porosimetry, are not widely used in pharmaceutical companies due to their price and/or toxicity, and therefore, efforts are made to develop a tool for fast and easy microstructure description. In this work, we have developed an image-based method for microstructure description and applied it to a model system consisting of ibuprofen and CaHPO4∙2H2O (API and excipient with different deformability). The obtained parameter, the quadratic mean of the equivalent diameter of the non-deformable, brittle excipient CaHPO4∙2H2O, was correlated with tablet composition, compression pressure and API release rate. The obtained results demonstrate the possibility of describing the tablet dissolution performance in the presented model system based on the microstructural parameter, providing a possible model system for compressed solid dosage forms in which a plastic component is present and specific API release is required.


Introduction
There are many steps in the process of making a tablet from the initial powder materials that affect the final performance of the tablet (frequently assessed by in vitro dissolution and disintegration, where the internal structure of the tablet inherently plays a very important role [1]).All of those steps can significantly alter the initially known input properties of the used materials.There is a significant dependence of the final tablet properties on compression process parameters, tablet composition and, of course, different characteristics of the used materials [2][3][4].
The input properties of the used materials/prepared tabletting mixture alone cannot usually sufficiently explain the final tablet disintegration, dissolution, tensile strength and other parameters [5,6].The input properties typically include the particle shape and size and, in more advanced cases, the viscoelastic [7] and surface properties of processed powders [8].Such properties can be used to describe the drug release from particles or agglomerates [9]; however, they alone usually fail to predict the resulting tablet behaviour due to the complexity of the compression process as the force exerted on the tablet mixture by the compression punches leads first to the particle rearrangement within the matrix and eventually to their fragmentation, plastic or elastic deformation (changing the size and shape of individual particles) [10][11][12][13].The dissolution profiles of the tablet may be substantially different from the starting particulate material, even if the disintegration limitations are avoided, as we recently reported [14].Here, information about tablet microstructure can provide a better understanding of the tablet performance [6,8], as it goes one step further from the input material particle properties and the compression parameters and aims to describe their combined result in the final dosage form.A great example here would be the significant tendency of needle-like particles to undergo fragmentation during compression [15][16][17].For such materials, the input particle size will not be of significant use in predicting tablet behaviour.
Hence, designing a pharmaceutical tablet of desirable properties, especially of a desirable dissolution profile, is an intricate process since the particulate starting material properties change in many ways during the production process.Pharmaceutical tablet properties may be multi-correlated to properties of different powders, including active ingredients and excipients, and they can exhibit non-linear, non-monotonous or threshold-like behaviour in relation to compression parameters.Therefore, the traditional way of dissolution tuning is largely empirical, relying on a relatively large number of development batches even if sophisticated tools for the design of experiments are used because the number of variables in the factorial plan is large.
On the other hand, the effect of particle properties and compression parameters on the tablet microstructure is more straightforward as it depends only on the mechanical properties of the materials used.The microstructure can be evaluated by overall tablet density/porosity and pore size distribution often measured by the mercury intrusion porosimetry [18] or by material (and porosity) distribution within the tablet where X-ray microscopy [19,20] and microtomography [5,21] and different chemical imaging methods come in.The most common ones would be methods based on vibrational spectroscopy -near-infrared and Raman mapping [22,23]; moreover, energy-dispersive X-ray spectroscopy based on scanning electron microscopy is also used frequently [6,24,25].While different general behaviour patterns exist, depending on the deformability attributes of the formulation components (such as plastic, elastic and brittle) and their combinations, the combination of a plastically deformable drug and a non-deformable excipient is of special importance.
Since many of the recently discovered drugs suffer from poor water solubility, there is a significant increase in the formulation of such drug candidates into amorphous solid solutions and dispersions to increase the dissolution rate of the drug [26][27][28][29].Particles of such drug formulations can, thanks to their relatively high polymer content then exhibit specific viscoelastic properties [30].It can be presumed that such particles would be fairly well plastically deformable in general so that they can contribute to the formation of a specific tablet microstructure.The microstructure-dissolution relationship is again relatively straightforward as it no longer depends on the mechanical properties of the constituents.
Thus, separating the objective of understanding the relationship between tablet composition, compression parameters and the dissolution properties into two independent problems of the mechanical properties to microstructure correlation (MMC) and the microstructure to dissolution correlation (MDC) is a promising opportunity to streamline the formulation development and improve the understanding of underlying processes.The present study aims at demonstrating the potential of the aforementioned approach using the MMC and MDC analysis in a binary system comprising materials with different viscoelastic properties -a plastically deformable model drug combined with a hard, brittle excipient.

Materials and Methods
In the presented study, directly compressed binary tablets comprised of ibuprofen and CaHPO 4 •2H 2 O (of different compositions and compressed with different loads) were at the centre of attention.Model materials were chosen based on their mechanical properties.Ibuprofen represents welldeformable active substances; thus, it can represent any other plastically deformable API alone and also quite a wide range of formulations of various APIs into various solid dispersion systems.CaHPO 4 •2H 2 O can, on the other hand, represent excipients that are non-deformable, quite hard and under higher pressure brittle [31].Each one of the prepared tablet formulations was subjected to tablet microstructure analysis and dissolution testing, so these two performance parameters could be investigated in correlation with each other.

Materials
Two different batches of ibuprofen were used in this study (marked as Ibu I and Ibu II), both kindly provided by Zentiva, k.s., CZ in combination with CaHPO 4 •2H 2 O (EmCompress®; JRS Pharma GmbH & Co., DE) for the model tablets preparation.One of the ibuprofen batches, Ibu I, was for some of the tested formulations milled, so its particle size was lower than with the two raw batches.
Milling was performed using a planetary ball mill PM 100 CM (Retsch GmbH, DE) at 250 rpm for 15 min.This altered batch is further marked as Ibu Im.Since the importance of initial particle size and morphology of the input materials was taken into consideration, all four materials (CaHPO 4 •2H 2 O and three ibuprofen variants) were characterised using a static light scattering system Mastersizer 3000 (Malvern Instruments, UK) for particle size distribution (Fig. 1).Scanning electron microscopy, SEM, (FE MIRA II LMU, Tescan s.r.o., CZ) was then used to describe and evaluate the particle morphology of these materials (Fig. 2).

Tablet Composition and Preparation
Tablets were prepared from mixtures containing different amounts of CaHPO 4 •2H 2 O and one of the three respective ibuprofen batches (Ibu I, Ibu Im, Ibu II).Homogenisation was done with a Turbula T2F mixer (Willy A. Bachhofen AG, CH) using 55 rpm for 5 min.Each of the mixtures was then subjected to compression with a compaction analyser GTP-1 (Gamlen Instruments, UK) equipped with the 5-mm diameter die under different compaction loads.The mixture weight added into the die was always adjusted, so all the resulting tablets had comparable geometry (height of 2.3 mm ± 15%).All of the tablet variants with the abovementioned parameters prepared are summarised in Table I.

Tablet Microstructure Evaluation
The inner microstructure of tablets was evaluated in the form of a quadratic mean of area equivalent diameter (d Avg ) of CaHPO 4 •2H 2 O particles/aggregates on the tablet radial cross-section areas.Tablets were, for this purpose, incorporated into paraffin wax matrices and cut on rotary microtome RM2255 (Leica Mikro spol.s.r.o., CZ), so the resulting cross-sections are flat and smooth [32].Samples prepared in this way were subsequently sputter coated with 2 nm of platinum (sputter coater Q150R ES, Quorum Technologies Ltd, UK) and analysed using the SEM with detection of backscattered electrons (BSE).Here, the use of CaHPO 4 •2H 2 O as an excipient in model binary formulations and also as the primary source of the microstructural data can be justified.Thanks to its chemical nature, CaHPO 4 •2H 2 O provides a different contrast than ibuprofen during the BSE detection which is necessary for further image analysis.While the SEM-BSE was the most suitable method in the presented model system, other imaging methods such as scanning Raman spectroscopy or SEM-EDS could also be used for different systems as the input data for the subsequent image analysis, depending on the specifics and limitations of the tested systems.

Image Analysis
The original SEM images of tablet cross-sections were subjected to image analysis using a simple script created in the Matlab ® environment (Fig. 3).Its whole workflow is based on a greyscale thresholding thanks to the phase contrast of CaHPO 4 •2H 2 O mentioned earlier.However, a few image adjustments had to be made with the original SEM picture, so the thresholding provides sensible results.Preceding the analysis, each picture was modified using a low-pass filter and contrast enhancement.Since the aim was to analyse the whole cross-section at once, the used magnification is rather low (40×) for such a purpose.It can cause the SEM-BSE pictures to have a horizontal brightness gradient.That is why the thresholding itself is eventually done separately for three vertical bands (left, middle and right) of the image and those three resulting segmentation masks are combined into one final mask only after a proper threshold setting for each one of them separately.From this final mask, where CaHPO 4 •2H 2 O particles/aggregates are properly marked, a particle size distribution (PSD) is constructed, so the d Avg along with its coefficient of variation (d Avg CV) for each tested tablet variant can be calculated.The coefficient of variation is used to represent the sample polydispersity since the final result for each tablet is a mean size rather than a size distribution.To ensure the statistical significance of the results, as many pictures as necessary for the PSD to be constructed from at least 100 particles/aggregates are analysed for each tested tablet variant.Moreover, image analysis of SEM pictures of the raw CaHPO 4 •2H 2 O powder was done, where the clearly observable excipient particles were marked, so a similar particle size distribution to the one from tablet cross-section can be constructed and a comparable excipient d Avg parameter can be used for the tablet microstructure evaluation.

Dissolution Testing
Along with the microstructural characterisation, all prepared variants of tablets were subjected to dissolution testing, so the release profile and release rate of ibuprofen from model tablets can be described.Tests were performed using an apparatus with flow-through cells (USP 4) CE-7smart (Sotax AG, CH).The apparatus was equipped with small tablet cells (12 mm diameter, 32 mm height) with the use of glass beads to ensure laminar flow.Tablets were placed in a holder approximately halfway up the cell.Phosphate buffer (pH 6.8) at a flow rate of 6 mL/min was used as a dissolution medium, and the whole system was tempered to 37°C.The tests were performed using an open-loop configuration; the dissolution medium passed the cell only once, and the samples were collected during the whole sampling intervals which were capped at 1 min, 2 min, 3 min, 4 min, 5 min, 7 min, 10 min, 15 min, 20 min, 25 min, 35 min, 45 min and 60 min after the beginning of the test.

Sample Analysis
Collected samples were analysed for ibuprofen concentration on a UV/VIS spectrophotometer SPECORD 200 PLUS (Analytik Jena AG, DE).Analysis was done at two wavelengths, 234 nm and 264 nm, each with a separate calibration curve.Ibuprofen concentration in samples was then calculated based on the more suitable absorbance value measured at either one of the wavelengths.The concentration values were then used to construct dissolution profiles (in the form of immediate API concentration values plotted against time) for each tablet variant (illustratively in Fig. 4).Measurements were always done in triplicates.The relatively high and variable values of the API concentration observed at the beginning of the test (approximately the first 1% of the released API) are mostly caused by the individual tablet surface characteristics, including adhered particles of the API or excipients and the API domain distribution on the tablet surface.After this 1% is released, tablets provide a consistent matrix tablet-like character.

Limit Release Rate Calculation
Subsequently, the relative release rate (r rel , min −1 ) of the samples was calculated for each time point of the measurement according to Eq. ( 1).
where ṁ is the mass flow of the API from the immediately exposed tablet surface, m 0 is the initial API dose, c is the immediate concentration in each sample and F stands for the flow rate of the dissolution medium [33].
The r rel values were then plotted against the amount of ibuprofen released from the tested tablet at the corresponding time points, so the limit release rate (r lim , -) of the API can be determined (Fig. 5).Its values are equal to the y-intercept of linear regression of relative release rate-released amount of ibuprofen dependency after the release rate (1) became stable and not influenced by any surface inconsistencies and possible adhered particles of either API or the excipient on top of the tablet (typically where the amount of released API is already higher than 1%).

Results and Discussion
All of the prepared tablet variants with differing compositions and used compression pressure were subjected to analyses described in the "Materials and Methods" section in order to study their microstructural and dissolution properties and their respective relationship with the tablet composition and preparation, as well as their relationship with each other.

Mechanical Properties to Microstructure Correlation (MMC)
The first studied relationship was the one between the input material and process properties and the created tablet microstructure (mechanical properties to microstructure correlation, MMC), where the input material viscoelastic properties, the compression pressure and the tablet composition were taken into account.

API Particle Properties and Their Influence on Tablet Microstructure
The model materials were specifically chosen to represent different groups of viscoelastic behaviour -ductile, deformable API and a non-deformable hard excipient prone to brittle fracture.Another reason behind the choice of these materials lies in their different contrast while subjected to the SEM-BSE analysis.The excipient, CaHPO 4 •2H 2 O, provides higher intensity of the back-scattered electrons, leading to a brighter appearance on the produced images.In contrast, the API appears darker in the images, thanks to the lack of elements heavier than oxygen in its molecule.Lastly, if there are any pores or voids present on the tablet cross-section, they are generally seen in black in the original unprocessed images.After preparation of the first tablets (containing only ibuprofen batch Ibu II with the particle size distribution closest to the excipient one) and performing SEM imaging of them, an observation was made that the ductility of the API causes its particles to form continuous domains when subjected to compression (shown in a darker shade of grey in the following Figs.6 and 7), in which the crystalline areas of excipient are spread (lighter shades of grey to white areas in Figs. 6 and 7).Following this fact, it was decided to prepare tablets with APIs having different particle size distributions (and shape to some extent) to see if the tablet microstructure will be somehow changed.For example, if the smaller API particles would be able to separate the excipient particles more efficiently within the tablet mass and how the size affects their ability of continuous domain creation.The first mentioned phenomenon, separation of excipient by the API particles differing in size, was evaluated on formulations having 25 wt.% of API, and it was compared with the use of tablets prepared with compaction pressure of 125 MPa (Fig. 6).The tabletting pressure was chosen to be the middle point of all the tested ones, so it allows a certain degree of manifestation of the particulate viscoelastic properties in the final tablet.SEM images show no significant difference in compact structure when the different particle size of API was used.Formation of the API continuous domains was best observable in tablets having the highest amount of API (in the presented study that would be tablets with 85 wt.% of ibuprofen, Fig. 7).Here, the tabletting pressure chosen for the illustration has a value of 62.5 MPa, since even at this low compression pressure the borders between the API particles are already very poorly or not distinguishable, as seen in the representative images in Fig. 7.The results were strongly comparable for all three API variants.From the SEM pictures presented in Figs. 6 and 7, it can be concluded that neither of those phenomena is manifesting excessively, and the influence of initial particle size and morphology is, in terms of the resulting tablet microstructure, negligible for well-deformable materials (in this case the API).

Use of Image Analysis in Tablet Microstructure Description
As mentioned in the corresponding part of the "Materials and Methods" section, the image analysis was put together in a way that the excipient, CaHPO 4 •2H 2 O, is the primary source of tablet microstructural information.Besides the phase contrast advantage, the use of this particular excipient as a primary microstructural tablet descriptor is sensible also from a mechanical point of view since it does keep some structure inside the tablet in contrast with well-deformable ibuprofen, which creates a more or less uniform mass after being subjected to compression and does not leave significant space for pores, cracks etc.The model tablet characteristics presented in this paper arose from the nature of used materials and their preparation process, which ultimately result in an atypical behaviour of such model tablets -fairly low or absent disintegration.This is another reason why to evaluate the microstructure based on the used excipient.Since it is insoluble, there is a certain correspondence with constitutional excipients used in matrix tablet production, where the insoluble matrix structure can be of great significance; hence, the evaluation of tablet microstructure in the form of a quadratic mean of the equivalent diameter (d Avg ) of CaHPO 4 •2H 2 O particles/ aggregates present on the tablet cross-section area.The quadratic mean was chosen to provide representative information about the mean excipient size while taking the relationship between the particle/aggregate size and its area visible on the cross-section into account.Moreover, using d Avg of CaHPO 4 •2H 2 O stems from the fact that the well-deformable API forms continuous domains when subjected to compression, in which the crystalline areas of excipient are spread.API domain characteristics are then dependent only on the mixture composition and homogeneity, and not on initial particle properties.

Process Setup Influence on Tablet Microstructure
Besides the input API particle size and morphology, the process parameter setup influence on the resulting tablet microstructure was evaluated.Compaction pressure was chosen as the independent variable here with the predetermined values of 62.5 MPa, 125 MPa and 250 MPa.The objective of this part was mostly about whether the presence of some amount of the ductile material (API) in the formulation will have the ability to suppress the excipient brittle fraction propensity and to what extent (to how high compression pressure values).
For the formulations where there is a high amount of ibuprofen present (Table II), its somehow fractureprotective function seems to manifest quite well.The values of the mean quadratic equivalent diameter of the CaHPO 4 •2H 2 O particles in prepared tablets are close to its raw powder value of 127.6 ± 87.2 μm.There are two outliers between the values obtained from tablets (EmC-IbuII 15-85 250 MPa and EmC-IbuI 15-85 125 MPa) which can be caused by the span of the size distribution (as can also be observed with all of the other formulations and the pure excipient evaluated from the SEM pictures) and relatively lower number of evaluated particles.However, the protection from the brittle fracture works here, at least to some extent.With the decreasing amount of the API in the formulation, the formation of excipient aggregates within the tablet begins to complicate drawing definite conclusions about the brittle fracture protection provided by the ibuprofen particles.However, the differences in excipient particle/aggregate size within tablets prepared from certain formulations with differing compaction loads are rather low when the ibuprofen content in the formulation is higher than 15 wt.%, which suggests that the fracture-protective function might be possible even at loads between 15 and 85 wt.% of the deformable material in the tablet.For a complete data table, please see Supplementary Table III.

Formulation and Process Impact on Microstructure
The resulting tablet microstructure was eventually evaluated as a function of tablet composition and compression pressure.In Fig. 8, there is the mean size of CaHPO 4 •2H 2 O particles/aggregates on the tablet cross-section plotted against tablet composition.The particle size of raw excipient powder, evaluated in the same manner as in the tablet crosssection analysis, is depicted in the graph for comparison (cross mark).The measured excipient size increases with its increasing amount in the formulation which is connected with the used evaluation method.Size is evaluated based on excipient regions observable on tablet cross-section, so the higher the amount of excipient, the higher the propensity to evaluate aggregates, preferably to individual particles and the higher the variance of resulting size between different used compression loads.As for the different ibuprofen batches (different point mark shapes) with different particle characteristics used for tablet preparation, there do not seem to be major differences in the resulting tablet microstructure evaluated from the excipient point of view.It corresponds with the previous findings about the initial API particle size influence on tablet microstructure ("API Particle Properties and Their Influence on Tablet Microstructure") and the observed phenomenon of ibuprofen's well deformability and creation of larger domains with non-distinguishable primary particles after submission to pressure.Moreover, a larger drop between the resulting sizes is observable between the formulations having 40 vol.% and 50 vol.%amount of ibuprofen which can be pointing to a certain threshold-like behaviour of this particular material combination, which is associated with the steep change of the system characteristics as the percolating (continuous) phase of the microstructure changes from excipient to the drug.The compression pressure used for tablet production (as the key process parameter) was found not to have a significant influence (shown in Fig. 8 via different point mark fillings on the tablet microstructure evaluated by the methodology used in this article).This corresponds to and confirms the earlier discussed high deformable propensity of ibuprofen during tablet compression, where nearly maximum deformation is obtained even for low compression pressure.

Formulation and Process Impact on Dissolution
As for microstructure, the atypical behaviour of the resulting tablets (low or no disintegration) also leads to the description of the API release in a non-standard way.The resulting parameter obtained from dissolution is, for the purposes of this work, the value of the limit release rate (r lim ) of ibuprofen.The use of r lim arose from the API plastic character and also from the fact that the used excipient creates nondisintegrable compacts.Thanks to these tablet properties, the dissolution of the drug can be considered comparable to intrinsic dissolution [34,35] in its early-developed forms [36].
Firstly, the limit release rate (r lim ) was, analogous to the tablet microstructure, evaluated as a function of tablet composition and compression pressure (Fig. 9).The overlook of the experimental data plot is quite similar to the dependency of tablet microstructure on composition.It suggests that the lower the amount of API in the formulation, the faster the dissolution.It can be thanks to the general nature of the tested model tablets.As only model binary mixtures were used (instead of the complex tablet formulation), there was not any extensive disintegration happening during the performed tests.This phenomenon thus can be explained by the higher relative surface area for ibuprofen available for dissolution in formulations having higher amounts of CaHPO 4 •2H 2 O, thanks to lower ibuprofen domain size within the tablet and possibly also higher structural porosity created by the excipient.The limit release rate is significantly more dependent on tablet composition in these faster-dissolving formulations (with an ibuprofen amount lower than 50 vol.%)than in the formulations where API is the major component, which can also be presented as some form of threshold-like behaviour as seen by the microstructural characterisation of model tablets.In correspondence with the previous results for excipient mean size, the used compression load or ibuprofen initial particle characteristics are not significantly influencing the release rate of the API from model tablets either.

Microstructure to Dissolution Correlation (MDC)
Eventually, both the tablet microstructural characteristic in the form of CaHPO 4 •2H 2 O d Avg and ibuprofen r lim were correlated (MDC, Fig. 10).The idea was to collect the combined influences of the mechanical properties of the input materials (particle size and viscoelastic behaviour) into the tablet microstructure parametrization (d Avg of CaHPO 4 •2H 2 O, MMC) and see its subsequent relationship with the tablet performance (API dissolution r lim , MDC).Here, the tendencies for threshold-like behaviour described in "Mechanical Properties to Microstructure Correlation (MMC)" and "Formulation and Process Impact on Dissolution" sections are mutually compensated, and the drug release rate proves to be a strong function of the given tablet microstructure.It can be well characterised merely by the CaHPO 4 •2H 2 O d Avg parameter irrespective of the tablet composition (ibuprofen amount in the formulation and initial particle size and morphology) and preparation method (applied compression load) in the form of linear dependency (Fig. 10c; Eq. ( 2)).
It can be argued that microstructure, which is determined by the material properties, is not the only or the most important factor affecting dissolution since physicochemical properties, such as hydrophilicity, pKa and the (2) r lim = 5.54 ⋅ d Avg + 9.99 (R 2 = 0.8881) physical form of the API, also significantly impact the dissolution behaviour.However, the effect of those parameters could be captured via an experiment involving pure API, such as the intrinsic dissolution rate test.When such an experiment precedes the use of the proposed methodology, the simplifications made can be seen as reasonable within the tested system.
In practice, the MMC to MDC approach can work together with the traditional methods used for a better understanding of dissolution behaviour, such as disintegration tests and different types of tablet imaging and input material imaging (Raman, SEM, SEM-EDS).The major area of application would probably be in the scope of new formulation development (especially for complicated systems containing, i.e.API in the form of an amorphous dispersion system), as well as troubleshooting and dissolution profile fine-tuning.Considering the poor disintegration of tested tablets, the application of the obtained results could lie in the area of disintegrated tablet fragments more likely than in the tablets as whole dosage forms.More specifically, the surface of the model tablets, when compared with the surface of disintegrated tablet fragments of the corresponding composition, can lead to the prediction of the drug release from such fragments and, subsequently, of the whole disintegrating tablet in question.
The additional directing parameter of the drug release from the whole tablet would then be the amount of disintegrant used for tablet preparation and its different modes of incorporation into the tablet microstructure [37].

Conclusions
The studied system of plastic API (ibuprofen) and brittle excipient (CaHPO 4 •2H 2 O) was used as a model to illustrate the potential of separating a formulation study into MMC and MDC parts.The direct relationship between the ibuprofen variant used, tablet composition and tablet compression parameters was difficult to analyse due to the mutually combined effects of those parameters.The MMC approach allows documenting the tablet microstructure through the excipient particle/aggregate size.This approach revealed that different combinations of the parameters can lead to similar microstructure and a threshold-like behaviour was observed when tablet microstructure (CaHPO 4 •2H 2 O d Avg ) and drug release rate (ibuprofen r lim ) were evaluated separately.MDC approach, which considers the drug release rate to be a function of the tablet microstructure, successfully described the drug release rate only as a function of excipient particle/aggregate size in the tablet as a single microstructure descriptor and the influence of input particle size and other parameters on the dissolution beyond their effects already identified by MMC proved rather insignificant.The used system can thus provide a general understanding of compressed solid dosage forms in which the plastic API component is formulated with a hard excipient with a propensity to brittle fracture under higher compression pressures.For example, solid dispersions prepared from poorly soluble drugs with polymers can belong to the plastic API component category, and their formulation can benefit from the presented results and proposed methodology.

Fig. 3 Fig. 4
Fig. 3 Illustrative workflow of image analysis performed on tablet cross-section areas (tablet from formulation EmC-IbuII 50-50 250 MPa).45× mag. a Original SEM picture (lighter areas on the tablet cross-section indicate the regions where the excipient is present, which are measured during the image analysis, the darker areas belong to the API), b three vertical bands after low-pass filtering

Fig. 8 Fig. 9
Fig. 8 CaHPO 4 •2H 2 O quadratic mean equivalent diameter as a function of tablet composition.Used ibuprofen batch: ■ Ibu II, • Ibu I, ▲ Ibu Im.Used compression pressure: white -62.5 MPa, grey -125 MPa, black -250 MPa (data points for tablets containing ibuprofen batch Ibu II compressed with 62.5 MPa may not be visible as they are overlapped by data points obtained at higher tabletting pressures)

Table I
Summary of All Prepared Tablet Variants and Their Respective Compositions,