Surface Segregation in Solid Oxide Cell Oxygen Electrodes: Phenomena, Mitigation Strategies and Electrochemical Properties

Solid oxide cells (SOCs) are highly efficient and environmentally benign devices that can be used to store renewable electrical energy in the form of fuels such as hydrogen in the solid oxide electrolysis cell mode and regenerate electrical power using stored fuels in the solid oxide fuel cell mode. Despite this, insufficient long-term durability over 5–10 years in terms of lifespan remains a critical issue in the development of reliable SOC technologies in which the surface segregation of cations, particularly strontium (Sr) on oxygen electrodes, plays a critical role in the surface chemistry of oxygen electrodes and is integral to the overall performance and durability of SOCs. Due to this, this review will provide a critical overview of the surface segregation phenomenon, including influential factors, driving forces, reactivity with volatile impurities such as chromium, boron, sulphur and carbon dioxide, interactions at electrode/electrolyte interfaces and influences on the electrochemical performance and stability of SOCs with an emphasis on Sr segregation in widely investigated (La,Sr)MnO3 and (La,Sr)(Co,Fe)O3−δ. In addition, this review will present strategies for the mitigation of Sr surface segregation.


Introduction
Solid oxide cells (SOCs) are electrochemical devices capable of both energy storage and regeneration in an intermediate temperature range of 600-800 °C with remarkably high efficiencies and low greenhouse emissions. Of different operating modes of SOCs, solid oxide fuel cells (SOFCs) can directly convert the chemical energy of fuels such as hydrogen, natural gas, ammonia, fossil fuel and biomass fuel into electrical power with high-quality heat being produced as a by-product of the overall power generation process [1][2][3][4][5]. Here, the overall efficiency of SOFCs in terms of combined heat and power (CHP) can reach 65%-85%, which is the highest among the fuel cell family. Alternatively, solid oxide electrolysis cells (SOECs) operate reversibly from SOFCs and are able to store surplus renewable electrical power from solar and wind in the form of useful fuels such as hydrogen, syngas and methane [6][7][8][9][10]. And because the electrical energy demand of electrolysis at high temperatures can partially be compensated by low-cost thermal energy, the electricity to fuel conversion efficiency of SOECs can exceed 100%.
One critical issue in the development of reliable SOC technologies involves poor long-term durability over 5-10 years as required for commercialization. Although SOC performance degradation can be caused by structural, thermal, chemical and mechanical sources from various cell components, one major contributor to performance degradation comes from the oxygen electrode. Here, oxygen electrode degradation can be divided into several categories, including microstructural coarsening, thermal mismatching, cation surface segregation, interfacial reactions as well as deposition and poisoning by volatile impurities such as CrO 3 , SO 2 , BO 2 , CO 2 and H 2 O in SOC stacks [45][46][47][48][49]. Among these, surface segregation plays a key role in the chemical instability of oxide surfaces and the performance degradation of SOC electrodes and is a phenomenon generally associated with the redistribution and accumulation of specific cations at oxide surfaces due to a loss of symmetry at the surface relative to the bulk. A typical example involves A-site cation segregation, particularly Sr, which is frequently observed in Sr-containing perovskite-based electrodes such as LSM and LSCF annealed under oxidizing atmospheres and/or at SOC operating conditions and can occupy active surface sites and degrade electrochemical activities for oxygen reactions [33,[50][51][52][53][54]. Surface-segregated SrO is also highly mobile and can migrate across GDC barrier layers to form SrZrO 3 insulating layers on YSZ electrolytes [55,56]. In addition, segregated SrO can interact with volatile impurities to form inert and nonreactive reaction products such as SrCrO 4 , SrSO 4 and SrCO 3 , causing the drastic poisoning of the electrocatalytic activities of oxygen electrodes [48,49,57,58]. Based on all of this, the fundamental understanding of cation surface segregation is vital in the development of reliable and durable SOC technologies.
Because numerous comprehensive reviews on cation segregation and its origin in perovskite oxide-based electrodes have been published [50-52, 59, 60], this review will focus on the segregation phenomenon, including influential factors, driving forces, reactivity with volatile impurities, mobility and interaction at the electrode/electrolyte interface and the influence of electrochemical polarization on Sr-doped perovskite oxide electrode materials. In particular, the latest developments in the understanding of the intrinsic relationship between surface segregation, interfaces and the activity of common and widely investigated electronic conducting LSM and mixed ionic and electronic conducting (MIEC) LSCF electrodes will be reviewed in detail. The latest developments in the mitigation of SrO surface segregation will also be discussed.

Lanthanum Strontium Manganite (LSM)
SrO surface segregation has been extensively reported on LSM-based electrodes [53,[61][62][63][64][65]. For example, Dulli et al. [61] annealed La 0.65 Sr 0.35 MnO 3 film at 900 °C in oxygen for 10 h and probed appreciable SrO segregation on the film surface using surface sensitive angle resolved X-ray photoelectron spectroscopy (XPS). In another study, de Jong et al. [62] deposited an LSM film at 750-800 °C in low vacuum followed by annealing at 450 °C in high vacuum and used XPS and ultraviolet photoelectron spectroscopy (UPS) analyses to reveal the presence of SrO and SrCO 3 a few angstroms in thickness on the film surface. Jiang et al. [53] used inductive coupled plasma optical Fig. 1 Operational principles of SOCs in the SOEC mode to store renewable energy in fuels such as H 2 and SOFC mode to generate electricity using stored H 2 emission spectroscopy (ICP-OES) analysis to show that the concentrations of Sr and Mn in the solution collected after the acid treatment of freshly prepared LSM electrodes after annealing at 1150 °C in air were one order of magnitude higher than that of La. Furthermore, Huber et al. [66] reported that a high Sr content was an indication of Sr enrichment or segregation on LSM surfaces based on observations of Sr segregation on LSM thin-film electrodes using in situ XPS and quasi-static secondary ion mass spectroscopy (ToF-SIMS).
In addition to Sr segregation, the surface segregation of B-site Mn cations in LSM and subsequent migration to YSZ electrolyte surfaces have also been observed under low oxygen partial pressures and cathodic polarization conditions [67][68][69][70][71]. For example, de Jong et al. [71] annealed an LSM film in varied oxygen partial pressures and reported based on X-ray adsorption spectroscopy (XAS) that annealing in ultra-high vacuum conditions can result in strong increases in the peak assigned to Mn 2+ and that this peak intensity decreased in oxygen-rich environments due to the increased valence state of Mn cations. Davis et al. [72] deposited an LSM film onto lattice matched LaAlO 3 and NdGaO 3 substrates and reported that total reflection X-ray fluorescence (TXRF) measurements showed the surface segregation of Mn cations during annealing at 800 °C in air accompanied by the increase in the Mn valence state to +4 at the surface as revealed using X-ray absorption near edge spectroscopy (XANES).
In further examples, Backhaus-Ricoult et al. [67] observed the rapid migration of Mn 2+ from an LSM film to a YSZ electrolyte surface using in situ photoelectron microscopy under polarization conditions and Jiang et al. [49] confirmed the segregation and subsequent diffusion of Mn cations at LSM surfaces through the systematic study of Cr deposition on LSM electrode systems (this will be discussed in following sections).

Lanthanum Strontium Cobalt (LSC)-Based Electrodes
Sr segregation is also well known in LSC-based electrodes [33,[73][74][75][76]. For example, Niania et al. [76] in situ investigated the microstructural and elemental evolution of LSCF pellets using high-temperature environmental scanning electron microscopy (HT-ESEM) and reported that the extent of SrO surface segregation increased with increasing annealing temperatures in the range of 750-1000 °C (Fig. 2). Here, the evolution of surface-segregated SrO can be divided into three distinct stages: (1) the rapid growth of segregated particles on grain boundaries, defect points and at the centre of grains; (2) the agglomeration of segregated particles; and (3) the continuous coarsening of segregated particles during annealing. Detailed elemental information concerning LSC-based electrode surfaces can further be obtained using high surface sensitive techniques such as low-energy ion scattering (LEIS). For example, Druce et al. [77,78] used LEIS to probe the surface chemistry of LSCF pellets after annealing at 400, 600 and 800 °C in air for 8 h as well as at 1000 °C in oxygen for 12 h and found that the onset temperature of SrO surface segregation occurred at as low as 400 °C and that the extent of segregation increased with increasing temperatures (Fig. 3a). Alternatively, these researchers also found that transition metals in B-sites disappeared on the surface at  [76]. Copyright 2016, WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim temperatures above 600 °C (Fig. 3b). Similar to segregated Sr species on LSM surfaces [53], segregated SrO can also be removed from LSC and LSCF electrode surfaces and films using acid etching [79][80][81][82]. For example, Kubicek et al. [79] etched the LSC film in 0.12 mol L −1 HCl solution for 5 s and reported a significantly reduced Sr surface content. Despite this, Sr tends to re-segregate on etched surfaces quickly at elevated temperatures [81,82].
SrO surface segregation can occur on porous LSCF electrodes after long-term operation. For example, Simner et al. [55] observed the significant performance degradation of an anode-supported YSZ film|GDC barrier layer LSCF cell after operation at 750 °C for 500 h and XPS analysis revealed that Sr segregated on both the outer and inner surfaces of the LSCF electrode and that the thickness of the Srsegregated layer was 35-75 nm. In addition, these researchers reported the formation of a SrZrO 3 reaction layer at the YSZ/GDC interface. In the case of the annealing of LSCF electrodes in the GDC electrolyte at 800 °C in air for 800 h, Wang et al. [83] found evidence of SrO surface segregation by detecting Sr species in the etched LSCF.
SrO surface segregation is usually accompanied by variations in electrode lattice parameters. For example, Hardy et al. [84] measured the X-ray diffraction (XRD) patterns of a cell with an anode-supported YSZ film|GDC barrier layer|LSCF electrode operating under constant current conditions at 750 °C and found that the diffraction patterns of LSCF continually changed during operation under load for more than 60 h in air in which the cubic lattice parameter of their LSCF was 3.92502 Å in the initial stage of operation and increased to 3.92650 Å after 60 h. This lattice expansion was also observed by Chang et al. [85] on an LSCF thinfilm electrode under cathodic polarization using synchrotron X-ray techniques.
B-site Co cation surface segregation can also occur on LSC and LSCF electrodes. For example, Zhao et al. [86,87] annealed LSCF pellets at 800 °C in air for 96 h and observed the segregation of both Sr and Co on the LSCF surface to form separated SrO and CoO x oxide particles (Fig. 4). As shown in Fig. 4, the surface of the freshly prepared LSCF sample before testing was dense, smooth and clean without pinholes, whereas the surface morphology of the LSCF sample after annealing changed significantly. Here, the formation of submicron-sized particles (less than 1 µm) and dark coloured particles (as large as ~ 5 µm) on the surface of the LSCF sample was detected and EDS element mapping identified the fine particles as SrO and the large particles as CoO x . In addition, Ni et al. [75] observed the generation of a CoFeO 3.5 phase after annealing an LSCF electrode at  after heat treatment at 800 °C in air for 96 h; c, d enlarged images of the segregated micron-sized particles and e EDS element mapping of Sr and Co. Arrows indicate segregated and isolated submicron-sized particles and large particles, modified based on Ref. [86]. Reproduced with permission from Ref. [86]. Copyright 2014, Royal Society of Chemistry 1 3 900 °C in air for 5 h. Co segregation has also been observed on LSC and LSCF electrodes after electrochemical polarization. As examples, Mutoro et al. [88] observed the segregation of Co on the LSC film after anodic polarization and Chang et al. [89] reported that Co segregated uniformly on LSCF film surfaces based on in situ synchrotron-based TXRF analysis and that this segregation responded sensitively and reversibly to electrochemical polarization. Baumann et al. [90] further observed the surface segregation of both Sr and Co on LSCF films as induced by cathodic polarization. And in the case of the reversible operation of a La 0.57 Sr 0.38 Co 0.18 Fe 0.72 Nb 0.1 O 3−δ (LSCFN) electrode directly assembled on the YSZ electrolyte, He et al. [91] found that Co-rich particles were generated in the vicinity of the LSCFN/YSZ interface at 750 °C under 0.5 A cm −2 for 240 h and that the number of particles increased in proportion to the degree of Sr accumulation at the interface, indicating the close correlation between Sr and Co segregation.

Other oxygen Electrode Materials
In addition to LSM and LSC-based electrodes, cation surface segregation also occurs on various perovskite oxides, layered perovskite oxides and RP oxides. For example, Norman and Leach [92] carried out the in situ and quasi in situ hightemperature XPS analysis of BSCF pellets in vacuum and found that although Co (and Fe) ions were predominant on the surface at intermediate temperatures (300 and 500 °C), Ba and Sr segregated to the surface at a higher temperature of 800 °C. Jung and Tuller [36] also detected an appreciable degree of Sr-excess at the surface of as-deposited STF films using XPS. In addition, Chen et al. [41] analysed the surface chemistry of (001) and (100) faceted RP oxide (La 1-x Sr x ) 2 CoO 4 (LSC214, x = 0.25 and 0.50) films using LEIS and XPS and reported that in the as-prepared films, the top surface was Sr-rich, whereas the subsurface was Co-rich. These researchers also reported that after annealing at elevated temperatures, the extent of SrO segregation increased and that the segregated SrO clustered into Sr-rich secondary phase particles. Burriel et al. [93] also characterized the surface of a La 1.67 Sr 0.33 NiO 4+δ (LSN) film using surface sensitive techniques including the crystal truncation rod, LEIS and angle-resolved XPS (ARXPS) and reported that both La and Sr can segregate onto the outer surface of LSN, whereas Ni was located in the subsurface region. Furthermore, researchers reported dominant La surface segregation in Sr-free LNO [78] and LaCoO 3−δ [94]. Moreover, Kilner's group [78,95,96] investigated the surface chemistry of double-perovskite GdBaCo 2 O 5+δ (GBC) and PrBaCo 2 O 5+δ (PBC) pellets annealed at 400-800 °C using LEIS and reported that Ba cations can rapidly segregate to the surface and that segregation started from 400 °C. Wei et al. [97] also observed that the extent of Ba surface segregation on PBC was affected by electrochemical polarization in which the level of Ba segregation increased through anodic polarization and decreased through cathodic polarization.

Influential Factors of Cation Surface Segregation
The extent of cation surface segregation, particularly Sr, is affected by various factors, including stoichiometric composition, strain, temperature, oxygen partial pressure, the nature of oxide samples, the type of cations in B-sites and electrochemical polarization condition.  [101]. In STF films, Chen et al. [102] reported that SrO segregation increased with increasing the Fe content and first principle calculations conducted by Ding et al. [103] suggested that the substitution of Fe with Co in LSCF can increase SrO segregation. Kwon et al. [104] also compared the effects of B-site cations on SrO surface segregation in Sr-doped LaBO 3 (001) (B = Cr 0.50 Mn 0.50 , Mn, Fe, Co 0.25 Fe 0.75 , Co and Ni) using DFT calculations and suggested that the minimization of elastic energy was the main driving force of SrO segregation in which these researchers predicted that larger B-site cations can lead to greater compressive strain on dopant cations and thereby increased SrO surface segregation.

Strain
In terms of the effects of strain on Sr surface segregation, Lussier et al. [105] deposited a La 1/2 Sr 1/2 MnO 3 film with a lattice constant of 0.3866 nm and a La 2/3 Ca 1/3 MnO 3 (LCM) film with a lattice constant of 0.3867 nm onto (100) faceted SrRuO 3 (SRO), SrTiO 3 (STO), NdGaO 3 (NGO) and LaAlO 3 (LAO) substrates with lattice constants of 0.3940 nm, 0.3905 nm, 0.3864 nm and 0.3793 nm, respectively, in which these substrates can provide a broad range of in-plane biaxial stress ranging from tensile (+ 1.91% for SRO and + 1.01% for STO) to relaxed (for NGO) and to compressive stress (− 1.89% for LAO). The results showed that compressive or tensile interfacial strain can modify the relative concentrations of La and Sr in the interfacial region to achieve better lattice matching. Estrade et al. [106,107] also deposited a 20-nm-thick LCM film onto STO (001) and (110) substrates to generate relaxed and tensile strained surfaces, respectively, and their electron energy loss spectroscopy (EELS) results showed that tensile strain can lead to La depletion at the free film surface and La enrichment at the LCM/STO interface, whereas relaxed films were chemically homogeneous. In addition, Jalili et al. [108] grew a 10-nm-thick LSM film onto (001) STO and (001) LAO substrates using PLD to generate in-plane tensile strain and in-plane compression strain, respectively, and observed a higher tendency for SrO segregation and higher concentrations of surface oxygen vacancies on the tensile strained LSM surface due to the larger spacing available for Sr cation accommodation and the reduced elastic energy on the surface as compared with the bulk. This positive effect of tensile strain on increasing oxygen diffusivity has also been reported on Au dispersed Pr 1. 9 Ni 0.71 Cu 0.41 Ga 0.05 O 4+δ [109] and La 0.8 Ce 0.1 Ni 0.4 Ti 0.6 O 3 with embedded metal nanoparticles [110], demonstrating that high concentrations of surface oxygen vacancies can play a key role in accelerating SrO segregation.
The accelerating effects of tensile strain on SrO surface segregation have also been observed on LSC and LSCF samples. For example, Cai et al. [111] deposited an LSC film onto STO and LAO substrates to generate tensile and compressive strain and found that although both tensile and compressive strain can induce Sr-rich surfaces, SrO segregation was slightly more pronounced in the case of tensile strain. In the case of LSCF films, Yu et al. [99] deposited LSCF films onto NGO, STO and GdScO 3 (GSO) substrates and found that SrO surface segregation increased with tensile strain and decreased with compressive strain. To gain a better understanding of the effects of strain on surface segregation, Liu et al. [112] further conducted experimental and DFT studies and found that tensile strain tended to create greater oxygen deficiencies on LSC surfaces than compressive strain due to the smaller oxygen vacancy formation energy associated with tensile strain.

Temperature
Sr surface segregation is also sensitive to temperature [113][114][115]. For example, Katsiev et al. [114] in situ probed the surface chemistry of polycrystalline LSM films as a function of temperature using Auger electron spectroscopy (AES) and observed Sr segregation on LSM surfaces at temperatures above of 400 °C and that the extent of segregation increased with increasing temperature. The onset temperature of surface segregation is further dependent on the dopant type. For example, Lee et al. [116] annealed 20 mol% Ba-, Sr-and Ca-doped LaMnO 3 films and probed the corresponding surfaces using atomic force microscopy (AFM) and ARXPS. Here, these researchers reported that surface-segregated Ba and Sr dopant particles appeared at 430 and 630 °C, respectively, and grew larger upon annealing at higher temperatures but that no structural changes were found on the film surfaces with Ca dopant up to 830 °C (Fig. 5).
In another study, Oh et al. [113] annealed LSCF pellets in temperatures ranging from 600 to 900 °C in air for 50-100 h and found that the amount of surface-segregated SrO increased with increasing temperature. Mutoro et al. [88] in situ investigated the surface composition of LSC films at varying temperatures of 25-650 °C at a low oxygen partial pressure of 1 × 10 −6 mbar and observed that Sr-containing secondary components on film surfaces increased with increasing temperature. Chen et al. [41] further reported that the surface roughness of an LSC214 film and its coverage by SrO particles increased with increasing annealing temperature at 400 and 500 °C.
The stability of segregated SrO appears to be also related to treatment temperature. For example, Caillol et al. [65] reported that an as-prepared LSM electrode sintered at 1200 °C was characterized by a SrO-segregated surface but that the SrO segregation disappeared after annealing at 800 °C for 1 week with no microstructural change. Chang et al. [117] also showed that Sr-rich nanoparticles can slowly be reincorporated into LSM films if annealed at 700 °C.

Oxygen Partial Pressure
The amount of SrO surface segregation on LSM is further dependent on oxygen partial pressure (P O 2 ) . For example, Fister et al. [118] probed the surface composition of LSM films using in situ synchrotron-based TXRF and observed that the concentration of surface Sr decreased with increasing P O 2 . Caillol et al. [65] observed a similar trend by exposing LSM powder to different P O 2 at 900 °C in which the Sr/La ratio on the LSM surface probed by XPS was 0.38 in 1% O 2 and decreased to 0.24 in 20% O 2 . Alternatively, Rohnke et al. [119] reported that the annealing of LSCrM in a P O 2 of 10 −9 mbar at 550 °C led to the gradual deletion of surface Sr and that as P O 2 increased to 10 −6 mbar, more Sr diffused from the LSCrM film to the YSZ surface. Lee et al. [116] also observed increased Sr segregation on LSM films at higher oxygen partial pressures. Similar increases in Sr segregation in O 2 rich atmospheres were reported by Oh et al. [113] on LSCF pellets annealed in pure N 2 , 0.1% O 2 and 21% O 2 at 800 and 890 °C for 50 h.

Microstructure or Morphology of Perovskite Oxides
The microstructure or morphology of perovskite oxides such as single-crystal films, polycrystalline pellets, powders and porous electrodes plays a vital role in determining SrO surface segregation [17,74,115]. For example, Plonczak et al. [120]. reported that the columnar grain boundaries of LSCF can increase surface areas by approximately 25 times as compared with dense flat films. Alternatively, la O' et al. [121] reported that LSC films can exhibit enhanced surface oxygen exchange kinetics and O 2 reduction reaction (ORR) activities as compared with bulk samples. Decorse et al. [98] further compared the surface composition of fine LSM powders and pellets and concluded that grain boundaries had a vital effect on surface composition. As-deposited LSC and LSCF thin films that are epitaxially grown using pulsed laser deposition (PLD) initially show Sr-rich and Co-poor termination surface layers [41,80,81,122,123] in which the extent of surface segregation on these films is dependent on deposition temperature. For example, Cai et al. [80] used PLD to grow 200-nm-thick LSC films on YSZ (100) electrolytes at 450 and 650 °C and created poor and well crystalline films. The LSC film grown at 650 °C underwent surface structural change from a Sr-rich state to a SrO/Sr(OH) 2 -rich phase-separated state, whereas the LSC film grown at 450 °C showed no surface segregation or phase separation. A recent study on LSCF thin-film electrodes prepared using PLD on GDC-buffered YSZ single-crystal substrates indicated significant differences between as-grown LSCF thin films in terms of the apparent surface exchange coefficient and surface segregation, indicating the dependence of oxygen exchange properties and surface segregation on the surface chemistry and nanostructure of film electrodes [124].
Crumlin et al. [125] also compared the temperaturedependent surface chemistry and behaviour of LSC pellets and LSC (001) films and reported that during annealing at elevated temperatures, the coverage of surface secondary phases on LSC films became smaller and Sr surface segregation increased with increasing temperature, whereas LSC pellets underwent no detectable change, suggesting that careful consideration is required in the comparison of findings published by different groups. Reproduced with permission from Ref. [116]. Copyright 2013, American Chemical Society 1 3

LSM
Early studies on LSM electrodes show that the electrocatalytic performance of LSM for ORR is highly sensitive to electrochemical polarization in which the electrocatalytic performance of freshly prepared LSM electrodes can be significantly enhanced by cathodic polarization but reduced by anodic polarization [53,[126][127][128]. Here, oxygen vacancies are generated at the LSM electrode/YSZ electrolyte interface under cathodic polarization and the subsequent positive charge of the oxygen vacancies can be compensated by the reduction of B-site Mn ions. This can be represented as follows in Kröger-Vink notation [129,130]:  [131]. Thus, the charge compensation through the reduction of B-site cations (and/or) will cause the increase in average cation size, e.g. the increase is 15.5% and 28.7% for Mn 3+ to Mn 2+ in LS and HS, respectively, and 9.4% for Mn 4+ to Mn 3+ in LS. Cation size increase leads to lattice expansion and would in turn increase the internal stress, which would drive the substituted Sr cations and/or B-site Mn cations to the surface, similar to the elastic interaction due to the size mismatch between the Sr dopant and the La host. Experimentally, B-site Mn cation segregation to the LSM surface under cathodic polarization has been observed by Backhaus-Ricoult et al. [67] using photoelectron microscopy techniques. The segregation and subsequent migration of Mn species to the TPB region of the LSM/YSZ interface have been well documented by deposition and poisoning of Cr studies and formation of (Cr,Mn) 3 O 4 spinels [49,132,133]. On the other hand, A-site Sr segregation to the LSM surface under cathodic polarization is inconsistent with the significant reduction of segregated SrO on LSM surface as shown by in situ studies on the surface chemistry of LSM using XPS and time-of-flight secondary ion mass spectrometry (ToF-SIMS) [66] and with significant enhancement of the electrochemical activity of LSM under cathodic polarization [53,[126][127][128]. This indicates that the charge compensation mechanism for the oxygen vacancy formation under cathodic polarization conditions through valence change of B-site Mn ions cannot explain the removal and disappearance of segregated Sr under cathodic polarization conditions. Another viable charge compensation mechanism is through incorporating SrO into La lattice sites, forming negatively charged defect, Sr ′ La . This is possible as the positively charged oxygen vacancies induced by cathodic polarization are essentially on the surface of LSM in the TPB regions. In this case, the incorporation of segregated SrO is driven by the electrostatic interaction and we will discuss this in more details later. Under anodic polarization, LSM experiences oxidation conditions with oxygen excess nonstoichiometry, similar to that at high oxygen partial pressure [134]. The negatively charged oxygen excess could push the already exited negatively charged defect, Sr ′ La , to the surface through the electrostatic repulsive force. The segregated SrO species occupy the active sites and deteriorate the electrochemical activity of LSM for ORR, consistent with the deactivation effect of LSM under anodic polarization conditions [128].
The phenomena of Sr incorporation and segregation in LSM under cathodic and anodic polarization have been validated by numerous in situ characterization techniques. For example, Chang et al. [117] used grazing incidence XRD (GIXRD) to in situ probe the cation concentration of LSM films during annealing and under applied cathodic potential at 800 °C and observed that after annealing, SrO segregation was found to occur uniformly over the LSM surface, whereas after applying a cathodic potential, Sr amounts were reduced on ~ 70% of the LSM surface. Huber et al. [66,135] also in situ studied the surface chemistry of LSM and LSCrM films under polarization using XPS and ToF-SIMS and observed that cathodic polarization led to the depletion (or incorporation) of Sr on surfaces, whereas anodic polarization led to Sr surface segregation (Fig. 6). The Sr incorporation on the LSCrM is relatively a faster process under cathodic polarization as compared to the Sr segregation under anodic polarization conditions. A similar phenomenon was also reported on LSCrM films by Rohnke et al. [119]. Sr surface segregation driven by anodic polarization under SOEC mode was also confirmed through observations of SrCrO 4 formation under Cr poisoning conditions [136] in contrast to the formation of a (Cr,Mn) 3 O 4 spinel phase by cathodic polarization under the SOFC mode on LSM electrodes [132]. The effects of polarization current on the performance and surface chemistry of LSM electrodes reported in the literature are listed in Table 1.

LSC-Based Electrodes
Electrochemical polarization also has a remarkable impact on cation segregation on the surface of LSC-based electrodes. Different from that observed on LSM electrodes, however, cathodic polarization generally increases cations, 1 3 particularly Sr segregation. For example, Vovk et al. [137] studied the surface chemistry of LSC film surfaces under polarization using in situ XPS and found that under cathodic polarization, the Sr/(La + Co) ratio at the LSC surface increased irreversibly by 5%, whereas the La/Co ratio remained constant. Baumann et al. [90] also observed that cathodic polarization led to increases in surface Sr and Co on LSCF films but that surface compositions remained unchanged by anodic polarization. Mutoro et al. [88] further probed the surface composition of LSC films using synchrotron XPS and observed SrO surface segregation by applying cathodic polarization as well as Sr incorporation and Co segregation by applying anodic polarization. A similar reversible change in surface Sr content was reported on LSC/LSC214 bi-layer films as well [88]. Alternatively, Choi et al. [138] tested LSCF films on GDC at 600 °C for 540 h and observed decreased R P after cathodic polarization and increased R P after anodic polarization.
The redistribution of cations induced by polarization may have a correlation with the change in cell volume or surface oxygen vacancy concentration. For example, Kivi et al. [139] in situ investigated the lattice parameters of porous LSC and LSCF electrodes under different atmospheres and polarization conditions using high-temperature XRD and reported that under open-circuit conditions, cell volumes increased slightly with decreasing oxygen partial pressures, but that the effects of oxygen partial pressure on cell volume became more significant if a cathodic potential was applied, in which cell volumes increased with increasing cathodic potential and the degree of volume expansion was more significant at lower oxygen partial pressures. These researchers also

Accelerated degradation by anodic
Increased by anodic Ex situ SEM-EDS [136] showed that the effects of cathodic potential on the change in lattice parameters were reversible by switching the potential between 0 and − 0.9 V [140]. Here, the increase in cell volume by applying a cathodic potential is possibly due to the increase in oxygen vacancies or the decrease in the effective oxidation state of Co ions. Table 2 lists the effects of polarization current on the performance and surface chemistry of selected LSC and LSCF electrodes reported in the literature.

Reversible Polarization
Surface segregation, particularly Sr species in YSZ electrolyte-based SOCs, is a complex issue due to the high activity of segregated Sr species with YSZ electrolyte and its significant dependence on the direction of polarization current. In the case of LSCF electrodes, although a GDC barrier layer is generally applied on YSZ electrolytes to function as a barrier layer, segregated Sr cations can readily diffuse through the pores or grain boundaries of the GDC layer to form a resistive SrZrO 3 phase at the GDC/YSZ interface region, in which the amount of formed SrZrO 3 is a good indication of the extent of Sr surface segregation. For example, Matsui et al. [141] reported that after an LSCF electrode was polarized in the cathodic mode at 0.3 A cm −2 and 1000 °C for 400 h, the volume of SrZrO 3 at the YSZ/GDC interface increased by 6 times as compared with that before polarization. Khan et al. [142] also prepared half cells with LSCF-GDC electrodes sintered on (Sc 2 O 3 ) 0.10 (CeO 2 ) 0.01 (ZrO 2 ) 0.89 (ScCeSZ) electrolytes at 1150 °C without a GDC barrier layer and reported that electrode activities decreased as polarization current densities increased in the range of 0-1.5 A cm −2 at 900 °C for 1000 h and that the Sr content at the LSCF-GDC /ScCeSZ interface increased with increasing current density. In the case of flat tubular single cells with co-sintered YSZ film/GDC barrier layers, Khan et al. [143] reported that performance degradation greatly increased with increasing current densities at 800 °C for 1000 h.
Recently developed direct assembly techniques provide an effective approach to study the intrinsic relationship between Sr segregation, interfacial formation and reaction of LSC-based electrodes on YSZ electrolytes [144,145]. With the directly assembled electrodes, it has been found that cathodic polarization can not only in situ induce the  [157,158] formation of electrode (LSM and LSCF)/electrolyte (YSZ and GDC) interfaces, but also lead to Sr segregation and diffusion, forming a Sr-rich layer and eventually a SrZrO 3 secondary phase at the YSZ surface in the case of LSCbased electrode/YSZ electrolyte interfaces [146][147][148]. In addition, further polarization can accelerate Sr segregation and SrZrO 3 reaction layer formation, which will lead to the disintegration of LSCF structures at the electrode/electrolyte interface (Fig. 7) [146]. These findings indicate that cathodic polarization can accelerate SrO surface segregation and kinetically promote the chemical reaction between LSCF and YSZ at 750 °C under polarization conditions. Alternatively, The et al. [149] studied LSCF electrodes in the anodic mode at 1 A cm −2 and 780 °C for 9000 h and detected the growth of a SrZrO 3 layer at the YSZ/GDC interface and the partial de-mixing of LSCF [149][150][151]. Choi et al. [138] further observed the significant degradation of an LSCF-GDC electrode after anodic polarization at a high current density of 2 A cm −2 under 700 °C for 1300 h, in which the electrode/electrolyte interface partly delaminated and Co and Sr accumulated at the electrode/electrolyte interface near the delaminated region.
To clarify the effects of polarization current direction on the activity of LSC-based electrodes, Shimura et al. [152] studied symmetric LSCF-SDC composite electrodes on YSZ electrolytes with dense SDC barrier layers under polarization at 900 °C and 0.5 A cm −2 for 5500 h. Here, these researchers reported that the overpotentials under anodic and cathodic modes remained constant over the operational duration in which the cell ohmic resistance increased from 0.5 to 0.8 Ω cm 2 after cathodic polarization, whereas the increase after anodic polarization was very small. Elemental analysis further showed significant Sr accumulation at the YSZ/SDC interlayer interface after cathodic polarization, which was consistent with cell ohmic resistance increases under cathodic polarization. Finsterbusch et al. [153] also prepared symmetric LSCF electrodes on GDC electrolytes and applied a constant DC voltage at 800 °C for 48 h in which gaseous Cr was fed as a tracer to catch segregated Sr cations at the surface through the formation of SrCrO 4 . Here, these researchers reported that Sr surface segregation can be inhibited by anodic polarization but that the inhibition effect became less evident as anodic overpotentials increased. Sr surface segregation increased at lower cathodic overpotentials, but decreased at higher cathodic overpotentials. Different results were reported on typical Ni-YSZ/YSZ/LSCF-GDC cells with high degradation rates in the electrolysis mode than in fuel cell mode [154].
Our group also investigated the effects of polarization current direction on Sr segregation in LSCF oxygen electrodes directly assembled on Ni-YSZ hydrogen electrodesupported YSZ electrolytes [146,155,156]. The LSCF/YSZ interfaces were in situ formed in the early stage of polarization at 750 °C as evidenced by decreased cell ohmic resistance and formation of contact marks on the YSZ electrolyte. And with two identical cells operating at 0.5 A cm −2 and 750 °C for 100 h, it was found that the operating stability of the cell under cathodic polarization deteriorated drastically, whereas significant performance enhancements were observed for the cell under anodic polarization (Fig. 8) [156]. And although a Sr-rich layer formed on both YSZ surfaces, the Sr-rich layer was ~ 30 nm after cathodic polarization and was much thicker than the 10-nm layer observed after anodic polarization. Similarly, Pan et al. [157,158] directly sintered LSCF electrodes onto a barrier layer-free YSZ electrolyte at 900 °C and observed enhanced electrode operating stability under anodic polarization at 1 A cm −2 and 800 °C for 158 h as compared with the performance decay under open-circuit conditions. He et al. [91] further investigated the effects of cyclic cathodic and anodic polarization on Sr segregation using a 10% Nb-doped LSCF (LSCFN) electrode assembled on a YSZ electrolyte and reported that although electrode performances severely degraded through cathodic polarization at 0.5 A cm −2 and 750 °C, it can largely be recovered by subsequently switching to the anodic polarization mode. This suggests that Sr surface segregation and accumulation at electrode/electrolyte interfaces as induced by cathodic polarization can be significantly mitigated through subsequent operation in the anodic polarization mode. However, the degree of performance reversibility and Sr segregation was dependent on the time duration of cycles. LSCFN electrode performances were largely reversible in the case of 12-h cathodic polarization/12-h anodic polarization cycles, whereas performance degradation occurred in the case of cyclic polarization with a shorter time period of 4-h cathodic polarization/4-h anodic polarization. Here, FIB-SEM and elemental mapping results indicated that for cyclic polarization using 4-h cathodic polarization/4-h anodic polarization cycles, significant Sr segregation and deposition at the electrode/electrolyte interface occurred after 224 h, whereas for cyclic polarization using 12-h cathodic polarization/12-h anodic polarization cycles, Sr accumulation at the interface was negligible (Fig. 9) [91].
In another study, Barnett et al. [82,159] investigated the effects of current switching on surface segregation and performance stability in symmetrical LSCF electrodes on GDC electrolytes. Here, these researchers performed current switching at 700 °C for 1000 h under varied current densities (0.7, 1.0 and 1.5 A cm −2 ) and observed that performance degradation was proportional to the level of current density [159]. To estimate the level of SrO surface segregation, these researchers also stirred the tested LSCF electrodes in ultrapure water for 10 min to seize the watersoluble Sr cations and used ICP-OES to analyse the solution. The results indicate that after current switching, the amount of surface-segregated Sr was higher than that of the as-prepared electrode and the electrode annealed under identical conditions without polarization. It has also been found that the effects of current density were dependent on operating temperature [82] in which at lower temperatures (650-700 °C), the performance degradation of LSCF electrodes increased with increasing current densities, whereas at a higher temperature of 750 °C, operating stability improved with increasing current densities.
Overall, the discrepancies in the effects of influential factors on Sr segregation as reported by different groups may be related to the fact that because Sr segregation is critically influenced by a variety of factors, the differences in sample preparation processes, surface chemistry, surface strains, surface morphology, atmospheres, impurities and polarizations can have a critical effect on observed Sr surface segregation. Therefore, it is important to conduct surface segregation studies under carefully controlled conditions.

Open-Circuit and Annealing Conditions
Although numerous theories exist regarding the mechanism or the driving force of Sr surface segregation in perovskite oxides under open-circuit and/or annealing conditions, the most accepted ones involve electrostatic and elastic interactions [52,103,116,160]. In this review, only the main points are briefly summarized.
Because Sr 2+ dopant possesses a 5.9% larger ionic radius than the host cation La 3+ , Sr 2+ cations experience compressive strain in LSM lattices that can be relaxed through surface migration. As a result, elastic interactions have been proposed as a driving force for SrO surface segregation in LSM [31,53,126,128] and have proved useful in the explanation of many segregation related phenomena. For example, Jalili et al. [108] reported a higher tendency of Sr segregation on tensile strained LSM surfaces due to the larger spacing available for the accommodation of Sr cations with reduced elastic energy on the surface than in the bulk. Lee et al. [116] also reported that the extent of dopant segregation was proportionally dependent on the size of dopants. Observed increases in Sr surface segregation at higher oxygen partial pressures can also be explained by elastic interaction, in which higher oxygen pressures can incorporate oxygen into lattices and contract lattices, whereas lower oxygen pressures can expand lattices upon oxygen loss. Because of this, the shrinkage of LSM lattices under high oxygen partial pressures can lead to increased dopant strain energy and accelerated Sr surface segregation. This was further confirmed by calculations using first-principles thermodynamics [161].
Surface oxygen vacancy concentrations tend to increase with decreasing oxygen partial pressures [162,163]. Because of this, Fister [118] proposed that electrostatic interactions are the driving force for SrO segregation in LSM and are related to the interactions between positively charged oxygen vacancies and net negative charges due to the substitution of Sr 2+ for La 3+ in LSM lattices. Large concentrations of positively charged surface oxygen vacancies (+2) can drive substituted Sr cations from the bulk to the surface through electrostatic interaction to maintain local electroneutrality. Electrostatic interactions between surface oxygen vacancies and Sr cations can also be used to explain the Sr surface segregation phenomenon of LSC and LSCF [125,164,165]. For example, Kuyyalil et al. [164] applied the electrostatic interaction mechanism to explain the formation of SrO layers on LSCF (100) film surfaces at a very low annealing temperature of 150 °C in which prior to annealing, surface oxygen vacancies were created by sputtering the LSCF film with low-energy Ar + ions.
Lee et al. [116] further identified both elastic and electrostatic interactions as driving forces for surface segregation, using (La,D)MnO 3 (D = Ca, Sr and Ba) as a model system (Fig. 10). The tendency to segregate to the surface increases with increased dopant sizes (the radii of Ca 2+ , Sr 2+ , Ba 2+ and La 3+ with CN = 12 are 1.34, 1.44, 1.61 and 1.36 Å, respectively [131]). Here, a smaller size mismatch between the host and dopant cations can suppress dopant segregation due to reduced elastic interactions. D 2+ substitution of A-site La 3+ in perovskites produces negatively charged D ′ La defects, which can be compensated by the formation of positively charged oxygen vacancies, V ⋅⋅ O on the surface. The electrostatic interaction between D ′ La and V ⋅⋅ O can then drive the substitutional D 2+ cations towards the surface. In another study, Ding et al. [103] took into account both strain relaxation and surface charge minimization as driving forces for Sr surface segregation on LSCF, in which DFT calculations indicated that the net effect of surface oxygen vacancies enhanced Sr surface segregation because the increase in surface charge overrode the induction of compressive strain. Sr surface segregation also depends on the type of B-site cations. For example, the substitution of Fe with Co can induce tensile strain and increase surface charge, thus increasing Sr surface segregation. Because of this, the application of compressive strain and the reduction in surface charge are effective strategies to suppress Sr surface segregation. This also indicates that electrostatic interactions play a dominant role in Sr segregation in LSCF [125,164,165].

Polarization Conditions
Sr surface segregation behaves differently under cathodic and anodic polarization conditions. In the case of LSM electrodes, cathodic polarization inhibits Sr segregation, whereas anodic polarization promotes Sr segregation in which incorporation and segregation of Sr species on LSM surfaces are supported by the activation/deactivation of LSM electrodes for ORR under the influence of cathodic/anodic polarization [53,126,127]. Here, the significant redistribution of segregated Sr species on LSM and LSCrM electrode surfaces can be studied by using in situ probing techniques [66,135,166].
The effects of polarization on Sr segregation/incorporation induced by cathodic/anodic polarization are complicated, as indicated by the activation and deactivation process of oxygen reduction reaction on LSM [126,128]. LSM-based materials are predominantly electronic conductors with negligible oxygen ion conductivities [167]. In fact, in the case of Sr-doped LaMnO 3 , Sr substitution of A-site La leads to the formation of electron holes, and at SOFC operating temperatures, the electron holes are localized onto specific Mn ions, forming Mn 4+ ions, Mn ⋅ Mn or electron holes, h ⋅ [168]. This is consistent with the p-type electronic conductivity of LSM-based materials [169]. The neutrality condition can be simply described as: Under cathodic polarization conditions, the generation of positively charged oxygen vacancies, V ⋅⋅ O,LSM,surface , is a dominant process in LSM electrodes for ORR. The subscript surface indicates that the positively charged oxygen vacancies generated under cathodic polarization are primarily on the LSM surface in the vicinities of the three-phase boundary (TPB). Cathodic polarization substantially reduced the formation energy of oxygen vacancies, and thus, the formed oxygen vacancies significantly enhance the ORR [130,170]. Considering the high concentration of positively charged oxygen vacancies on the LSM surface, the electroneutrality can also be established by incorporating the segregated SrO into the La lattice, forming negatively charged Sr ′ La . Such incorporation of SrO through the electrostatic attractive interaction can be expressed as: In this case, oxygen vacancies are formed under the influence of cathodic polarization and not due to the Sr substitution. As discussed above, the charge compensation through the oxidation of B-site Mn ions (Eqs. 1 and 2) would mainly drive the B-site Mn cations to the surface via the elastic interaction, while incorporation of segregated SrO into La lattice sites would be the alternative charge compensation mechanism for the oxygen vacancy formed under cathodic polarization conditions. The incorporation of segregated SrO species can be a fast process due to the strong electrostatic attractive force between the positively charged V ⋅⋅ O,LSM,surface and negatively charged Sr ′ La . Fast incorporation reaction of segregated Sr into LSM lattices is consistent with the observed activation effect and reduced Sr species at LSM electrode surfaces [53,66,117,135].
Under anodic polarization conditions, oxygen excess occurs, similar to the oxygen excess of LSM materials at high oxygen partial pressures [130,169]. The presence of oxygen excess in the form of negatively charged O ′′ excess ions (note: the oxygen excess could exist as negatively charged cation vacancies such as V ′′′ La due to the compact nature of LSM perovskite structure. Nevertheless, electronically O ′′ excess and V ′′′ La would function similarly due to the fact that both are negatively charged point defects) would push the negatively charged Sr ′ La out of the lattice to the surface by the repulsive electrostatic interaction. The Sr segregation due to the excess oxygen in LSM under anodic polarization can be expressed as follows: This anodic polarization-induced electrostatic interaction can subsequently drive Sr segregation to the LSM surface. Therefore, the driving force for Sr segregation at LSM electrode surfaces under polarization is most likely the result of oxygen nonstoichiometry modulated electrostatic interaction on the LSM surface induced by cathodic/anodic polarization. The observed Sr incorporation rather than Sr segregation under cathodic polarization implies that elastic interactions due to the size mismatch between the substitute Sr and host La cations are compensated by the electrostatic interactions of the generated oxygen vacancies and are not key factors dominating Sr surface segregation/incorporation in LSM under polarization conditions. The Sr segregation/ incorporation processes on LSM under polarization conditions are schematically shown in Fig. 11.
The effects of polarization on Sr segregation in LSCbased electrodes are the opposite of those observed in LSM electrodes. Cathodic polarization promotes Sr segregation, whereas anodic polarization inhibits Sr segregation [91,146,147]. These polarization effects can be explained based on the nature of LSC-based electrodes such as LSCF. LSCF electrode materials are well-known MIECs with high oxygen ion conductivity [171,172], which results in significant differences in electrode behaviours between LSCF and LSM. Cathodic polarization will cause the excess in oxygen vacancies on the electrode surface of LSCF. As a result, the increased accumulation of positively charged oxygen vacancies at the electrode surface would enhance electrostatic  Here, the results suggested that the high content of Sr on the LSM surface was an indication of Sr segregation and enrichment on the LSM surface. The electrochemical activity of freshly prepared LSM electrodes for O 2 reduction can be enhanced significantly through cathodic polarization (i.e. activation), and such activation phenomenon is much less pronounced after the acid treatment of the electrode (Fig. 13) [53]. The electrode polarization resistance for the reaction on the acid-treated LSM in 1 M HCl solution was 0.84 Ω cm 2 , which was much smaller than 6.2 Ω cm 2 for the reaction on LSM without acid treatment.

Surface Segregation and Activation
In addition, the reduction in polarization resistance under cathodic polarization treatment was also much smaller. La O' et al. [174] also observed significantly enriched La on annealed and quenched LSM and reported that cathodic polarization considerably decreased electrode impedance as associated with the reduction of surface La and increase in surface Sr and Mn species on LSM adjacent to the threephase boundary. Because segregated dopant cations such as SrO and BaO are electrically insulated as revealed by scanning tunnelling microscopy and spectroscopy (STM/ STS) [114,116], their occupation on electrode surfaces can have detrimental effects on electrocatalytic activity. For example, Wang et al. [83] reported that the surface segregation of SrO on annealed LSCF electrodes led to decreased surface exchange rates (k) by ∼ 50% and oxygen diffusion coefficients (D*) by 50%. Yokokawa et al. [175] recently also reported that Sr deficiencies in the LSCF bulk can lead to decreased k and D* due to positively charge oxygen vacancy can also be compensated by incorporating the surface-segregated SrO into the La lattice, forming negatively charged Sr ′ La and decrease in oxygen vacancy concentrations. Chen et al. [102] further proposed deterioration mechanisms of SrO segregation on the ORR kinetics of STF electrodes involving: (1) the inhibition of electron transfer from the bulk of STF to the oxygen species adsorbed on the surface and (2) the decrease in surface oxygen vacancy concentrations for the incorporation of oxygen into STF lattices. Lu et al. [82] suggested that the removal of surfacesegregated SrO through etching in diluted acid or water can significantly enhance the electrocatalytic activity of LSCF electrodes for ORR.
The initial state of LSM lattices can be examined to explain the activation phenomenon. The segregated SrO species on LSM surface occupies the active sites and significantly inhibits the dissociation and diffusion of oxygen, leading to the very high electrode polarization resistance. Here, the removal of SrO species can be achieved through chemical processes such as weak acid etching as well as with the application of cathodic polarization/current passage through the incorporation of segregated SrO species into LSM perovskite lattices due to the charge compensation between the positively charged oxygen vacancies formed and the incorporated negatively charged Sr ′ La defects (Fig. 11). The incorporation of SrO under cathodic polarization conditions is kinetically favourable and a fast process due to the strong oxygen vacancy modulated electrostatic interactions.
To clearly elucidate the effects of segregated cations on the electrocatalytic activity of LSC films, Rupp et al. [176] developed a combined PLD and electrochemical measurement approach to monitor electrochemical performance changes during surface decoration in a PLD chamber. Here, these researchers intentionally deposited a 4% Sr monolayer onto an LSC surface using PLD to achieve severe performance deactivation and found that this result was in good agreement with the aforementioned performance degradation as induced by in situ SrO surface segregation at elevated temperatures. The deposition of Co using PLD caused performance activation in LSC films. The dominant role of B-site cations as active sites for ORR has also been reported in the case of LSM [114,177].
Researchers have also reported the promotional effects of SrO decoration on electrode activity [34,178,179]. For example, Mutoro et al. [178] deposited 50%-80% of an LSC film surface with SrO nanoparticles using PLD and found that the surface exchange coefficient was remarkably enhanced by an order of magnitude. Here, these researchers attributed the enhancement of the Sr-decorated surface to the generation of a catalytically active LSC214 RP phase at the interface between SrO particles and the LSC film [42]. The positive effects of SrO and BaO nanoparticle infiltration into porous electrodes have also been reported [179][180][181][182][183]. For example, Hong et al. [179]   that the in situ formation of a highly active nanostructured barium cobaltite was critical to ORR activity and durability. Recently, Li et al. [34] also investigated SrO decoration on LSC film surfaces through infiltration and obtained polarization resistances ~ 30 times lower than that of pristine LSC films in which after annealing at 600 °C, the infiltrated SrO phase evolved into isolated islands and possessed a Srrich perovskite structure. Here, these researchers combined their experimental observations with DFT calculations and hypothesized that the surface infiltrated Sr 2+ cations had a high tendency to seize surface defective sites and inhibit intrinsic Sr flux, thereby suppressing SrO segregation. Despite this, excessive SrO infiltration can still lead to surface passivation. Therefore, the promotional effects of SrO surface decoration [34,178,179] may be related to interactions at the interface between SrO and perovskite oxides, forming a highly active Sr-containing perovskite phase. Nevertheless, the use of infiltration to study the effects of decorated SrO needs to be cautioned because infiltration can not only introduce nanoparticles but also clean the surface of infiltrated electrodes, meaning that the careful control of infiltrated electrodes/systems is required [185,186].

Cr
Although  [49,132,206]. For example, Zhao et al. [86] annealed LSCF pellets at 800 °C for 96 h in the presence of Cr 2 O 3 powder in dry air and observed the significant growth of surface-segregated SrO particles. LSCF pellets were also annealed in the presence of Cr 2 O 3 in wet air, which led to greatly accelerated Sr segregation with roughened LSCF grain surfaces and the formation of nanopores or pinholes. Here, this was attributed to the combined effects of the high volatility of CrO 2 (OH) 2 formed in humid air [207] and the acceleration effect of moisture on Sr surface segregation [195][196][197]. Wang et al. [208] also reported that the amount of SrCrO 4 generated on LSCF pellet surfaces decreased with decreasing temperature in the range of 700-900 °C and that decreases in temperature can significantly reduce the amount of surface-segregated SrO and partial pressure of CrO 3 , leading to significant reductions in Cr deposition. Wei et al. [209] further studied cation segregation and Cr deposition on double-perovskite oxide PrBaCo 2 O 5+δ (PBCO) and observed that after high-temperature annealing in O 2 atmosphere, both Ba and Co diffused out of the lattice to form BaO and Co 3 O 4 precipitates on the surface. It was found that in the presence of volatile Cr species, BaCrO 4 , but not CoCr 2 O 4 , was observed on PBCO electrode surfaces, indicating that Cr deposition preferentially occurred on segregated BaO rather than on Co 3 O 4 precipitates. The interactions between segregated species and Cr at cathodes under the SOFC operation mode can be described with a generalized nucleation deposition theory in which Cr deposition is essentially a chemical process in nature that is initiated by the nucleation reaction between high valence Cr species and a nucleation agent as follows [49]: in which N (s) represents a nucleation agent. Here, nucleation agents include Mn,Sr and Ba species generated under hightemperature annealing and/or polarization conditions on perovskite-based electrode surfaces and can be on electrode and electrolyte surfaces or at electrode/electrolyte interfaces. Further reactions between the Cr-N-O nuclei, gaseous Cr For LSCF electrodes exposed to CrO 3 environments, Cr preferentially deposits onto outermost electrode surfaces to form dense SrCrO 4 layers [188,206,[210][211][212] and to a lesser extent at the interface between LSCF electrodes and GDC barrier layers [213,214]. This is evidenced by Cr distribution in LSCF electrodes after operation for 10000 h (Fig. 14) [211]. Here, the preferential formation of SrCrO 4 on electrode surface layers can drive the diffusion of segregated SrO from electrode/electrolyte interfaces to electrode surfaces and therefore cause Sr deficiency in LSCF electrodes in interfacial regions [188,206,[210][211][212].

SO 2
Sulphur in air streams can significantly affect the performance and durability of SOFCs [191,215,216]. For example, Wang et al. [217] studied the mechanism and kinetics of sulphur deposition on LSM electrodes at 700 °C and 800 °C in 1 ppm and 10 ppm SO 2 and reported that the deposition of SO 2 was likely controlled by the nucleation reaction between surface-segregated SrO and SO 2 to form SrSO 4 on LSM electrode surfaces. Here, segregated SrO species act as both the nucleation agent and the reactant and the formation of SrSO 4 in turn can promote Sr segregation, leading to LSM Sr deficiency and driving the chemical reaction to the LSM/ YSZ interface. High oxygen activities and SrO segregation can also lead to the formation of Sr/La zirconate at electrode/electrolyte interfaces.
Xiong et al. [191] also investigated the sulphur poisoning of LSM electrodes in highly concentrated 0.01% SO 2 in air and reported that the LSM electrode was relatively stable during cathodic polarization at 800 °C for 5 h. On the other hand, Liu et al. [190] tested a double-layer oxygen electrode with an LSM-ScSZ inner layer and an LSM outer layer in 20 ppm SO 2 and reported that after cathodic polarization at 800 °C for 1000 h, SrSO 4 particles were observed around the LSM particles in both layers of the electrode. Wang et al. [218] further reported that the deposition of sulphur and formation of SrSO 4 were at the LSM/YSZ interface in the presence of 1 ppm SO 2 at 800 °C under anodic polarization conditions and attributed this to the fact that anodic polarization can promote SrO segregation at the LSM close to the YSZ electrolyte, promoting the formation of SrSO 4 and interfacial delamination.
Compared with LSM, cobaltite oxygen electrodes such as LSC, Sm 0.5 Sr 0.5 CoO 3 (SSC) and LSCF have much higher tendencies to react with SO 2 . For example, Schuler et al. [58,219] exposed a double-layer oxygen electrode consisting of a LSM-YSZ inner layer and an LSC outer layer to ~ 12 ppb SO 2 and reported that after operation at 800 °C for 1900 h, SrSO 4 preferentially deposited onto the LSC layer, in which the formation of more SrSO 4 on the cobaltite electrodes as compared with that on LSM electrodes was believed to be due to the higher activity of SrO in cobaltite electrodes [58,190,191]. Here, the reaction between SO 2 and LSC is favourable under oxygen-rich atmospheres and can be described by: In another study, Bucher et al. [220] exposed LSC pellets in air with SO 2 concentrations ranging from a few ppb (10) [191] reported that the testing of SSC electrodes under cathodic polarization conditions in 0.01% SO 2 -concentrated air at 800 °C for 8 h led to the formation of SrSO 4 and Sm 2 O 2 SO 4 at the electrode surface. Wang et al. [215,221] further exposed LSCF electrodes in 0.1, 1, 10 and 100 ppm SO 2 at 800 °C and reported that degradation became critical with increasing SO 2 concentrations due to the increasing generation of SrSO 4 and CoFe 2 O 4 . In addition, sulphur deposition preferentially occurred in the vicinity of the LSCF electrode/GDC electrolyte interface in 0.1 ppm SO 2 . The creation of high oxygen vacancy concentrations in electrochemically active regions under polarization conditions is believed to be able to promote SO 2 adsorption and accelerate SrSO 4 formation at electrode/electrolyte interfaces [222]. Alternatively, Kushi [223] reported that after exposure in 0.2 ppm SO 2 at 700 °C, sulphur deposition mainly occurred at the electrolyte/electrode interface after anodic polarization, whereas deposited sulphur was widely distributed across the entire electrode after cathodic polarization.
The formation of SrSO 4 on LSCF is critically dependent on operating temperature. For example, Wang et al. [224] annealed LSCF pellets in 20 ppm SO 2 at temperatures ranging from 400 to 900 °C and found that SrSO 4 formed on LSCF surfaces at high temperatures ⩾ 700 °C, whereas SrS formed at low temperatures < 700 °C. In addition, the surface segregation of Sr and/or Co on LSCF decreased significantly with temperature, whereas sulphur deposition on LSCF surfaces showed a volcano-type dependency on temperature, in which the reaction and formation of SrSO 4 were most kinetically active at 700 °C. Wang et al. [225] also reported that LSCF can exhibit severe performance degradation in 1 ppm SO 2 at low temperatures of 650 °C and 700 °C but that degradation was reduced at a high temperature of 800 °C. The results suggest that the severe performance loss at lower temperatures is due to the adsorption of SO 2 on the entire LSCF surface without the formation of sulphates, whereas the less severe performance loss at higher temperatures was attributed to the formation and accumulation of SrSO 4 , which left some active surface sites available for electrochemical reduction reactions.
The sulphur poisoning behaviour of LSCF electrodes is also dependent on composition. For example, De Vero [226] compared the sulphur poisoning of LSCF films with an A-site excess composition (La 0.75 Sr 0.42 Co 0.15 Fe 0.68 O 3−δ ) and a stoichiometric composition (La 0.60 Sr 0.39 Co 0.20 Fe 0.81 O 3−δ ) by annealing at 800 °C for 100 h in trace amounts of SO 2 (in the ppb level) and reported that the A-site excess LSCF film exhibited significant SrSO 4 formation with severe porosity, whereas only isolated SrSO 4 formation was observed in the stoichiometric LSCF film. Here, the partial poisoning by sulphur minimized excessive porosity and enhanced Co-rich oxide precipitation.

Boron
The main source of volatile boron species originates from the use of boron-containing sealing glass in SOCs, such as BO 2 under dry conditions and B 3 H 3 O 6 under wet reducing conditions [227]. To investigate this, Chen et al. [228] annealed LSM and LSCF pellets at 800 °C for 7 and 30 days using borosilicate glass as a boron source and found that the reaction between boron and surface-segregated SrO resulted in the formation of a SrB 2 O 4 layer on the outermost surface of the pellets. LaBO 3 was also observed underneath the SrB 2 O 4 surface layer. Chen et al. [203] further annealed BSCF pellets in gaseous boron at 800 °C for 7 days and observed a Ba-and Sr-rich layer on the surface.
Polarization can significantly affect the distribution of deposited boron. Chen et al. [229,230] conducted the in situ electrochemical study of boron poisoning in LSM electrodes under cathodic and anodic polarization at 800 °C in which borosilicate glass pellets were placed on top of an LSM electrode as a boron source without direct contact by using a Pt mesh buffer layer. Here, it was found that boron deposition occurred randomly on the LSM electrode surface under open circuit conditions but was driven to the electrode/electrolyte interface region under cathodic polarization, resulted in the formation of LaBO 3 and Mn 2 O 3 and the disintegration of the LSM perovskite structure (Fig. 15a, b). A LaBO 3 layer was also observed at the electrode/electrolyte interface under anodic polarization that led to electrode delamination and failure (Fig. 15c, d). Here, preferential boron deposition at the electrode/electrolyte interface can be attributed to the increased activity of highly energetic La at the LSM lattice sites of the three-phase boundary region under polarization conditions, which can accelerate the reaction rate between boron and energetic La. The in situ boron poisoning of LSCF electrodes under cathodic polarization was also investigated [231]. After cathodic polarization at 700 °C for 20 h, ohmic and polarization resistances were found to have increased by 4 and 12 times, respectively, and significant microstructure changes were observed in the vicinity of the electrode/ electrolyte interface (Fig. 15e, f). Here, the thickness of the reaction layer was found to be dependent on the overall electrode thickness, which was 6 μm thick for a 28 μm-thick electrode and 2.5 μm thick for a 6 μm-thick electrode. These microstructural changes can be attributed to the preferential deposition of boron and formation of LaBO 3 at the electrode/ electrolyte interface of LSCF electrodes.

CO 2
The effects of CO 2 on the distribution of surface cations are generally conducted under accelerated conditions. For example, Hu et al. [232] tested LSM electrodes in 0-10% CO 2 containing air in temperatures ranging from 750 to 850 °C and reported the formation of SrCO 3 on LSM surfaces based on AES and attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR). Ponce et al. [233] also observed the tendency of CO 2 reacting with SrO at LSM surfaces to form SrCO 3 . In addition, researchers have reported the minor poisoning effect of CO 2 on the operating stability of LSM electrodes [232,234]. On the other hand, the poisoning effect of the reaction between CO 2 and SrO on LSCF is severer. For example, Yu et al. [192] annealed LSCF at 800 °C under a CO 2 containing atmosphere for 9 h and observed the formation of a secondary phase on the surface, which consisted of SrO covered with a capping layer of SrCO 3 and Co-rich phases. Chen et al. [39] exposed LSCF electrodes to 1% and 10% CO 2 in air and reported that the impedance of the LSCF electrodes increased significantly with time and that the degree of degradation increased with increasing CO 2 concentrations (Fig. 16a). To gain a deeper understanding of the causes of this degradation, these researchers further exposed LSCF films to 10% CO 2 atmosphere at 500 °C and in situ Raman spectroscopy results showed drastic increases in peaks related to strontium carbonate with increasing exposure times (Fig. 16b). After exposure to CO 2 , the LSCF film surface became much rougher (Fig. 16c). DFT calculations also indicated that the growth of SrCO 3 resulted from carbonate formation through the strong interaction between CO 2 and Sr cations segregated from the LSCF electrode. In another study, Darvish et al. [234] carried out thermodynamic predictions regarding phase formations in LSCF and suggested the higher tendency of SrCO 3 formation at higher P CO 2 , lower P O 2 and lower temperatures.
Compared with LSCF, BSCF is more vulnerable to attack by CO 2 [235][236][237][238]. This is due to the higher tendency of CO 2 adsorption on BSCF surfaces and the formation of Ba-rich carbonates, particularly at higher temperatures, higher CO 2 concentrations and higher Ba doping levels in BSCF [235,236]. For example, Arnold et al. [239] showed that BSCF bulk samples can be affected down to a depth of 50 μm if exposed to pure CO 2 at 875 °C for 72 h in which two distinctive layers within the reaction zone existed. Here, the outer layer was ~ 5 μm thick and consisted mainly of (Ba,Sr) CO 3 , whereas the second layer underneath was ~ 40 μm thick and exhibited plate-like morphology with a mixture of carbonates and Co-/Fe-enriched oxides. Schmale et al. [240] exposed BSCF specimens to 99.9% CO 2 atmosphere at 900 °C and reported the formation of a (Ba,Sr)CO 3 carbonate top layer 1.4-3.0 μm in thickness after annealing for 24 h. The reaction layer increased to 5-7 μm in thickness after prolonging the annealing period to 240 h. In both cases, the Ba/Sr ratio remained at 1.25-1.50.

H 2 O
Moisture in air has a detrimental effect on the surface exchange rate and electrocatalytic performance of LSM, LSC and LSCF oxygen electrodes due to the structural damage caused by interactions between surface-segregated cations and moisture [193][194][195][196][197]. For example, moisture can accelerate SrO segregation on LSM. Sharma et al. [241] reported that exposure to 20% moisture enhanced SrO segregation on LSM after annealing at 800 °C for 50 h. Hu et al. [242] also observed SrO particle segregation on LSM Fig. 16 [243] observed La 2 O 3 segregation on LSM surfaces annealed at 800 °C for 5 h in 20% and 40% humidified air that was different as compared with annealing in dry air. Liu et al. [197] also reported that exposure to 20% moisture at 800 °C for 200 h led to the partial decomposition of LSM into La 2 O 3 and MnO x . Here, these researchers reported that decomposition was severer at a reduced temperature of 700 °C and was possibly due to the preferential combination of La cations from LSM with steam to form La 2 O 3 , particularly at reduced temperatures.
Moisture can severely accelerate Sr surface segregation in LSC and LSCF. For example, Bucher et al. [195,196] annealed LSC and LSCF pellet samples in humid atmosphere in a Si reactor and reported that after annealing at 600 °C for 5000 h with 30% and 75% relative humidity, LSC surface roughness increased by approximately one order of magnitude. Silicon poisoning and strong Sr segregation at depths of 10-90 nm were also found based on XPS depth profiles as compared with Sr segregation at a depth of 2 nm in dry conditions. Similarly, significant Sr segregation and silicon poisoning were also detected on LSCF after annealing at 600 and 700 °C in 30% humidity in which the reaction between volatile Si species and surface-segregated SrO may be the driving force for Sr surface accumulation. Liu et al. [197] also reported that after testing LSCF oxygen electrodes at 800 °C for 1000 h in 5% moisture the generation of a Sr-rich layer on the oxygen electrode surface was observed, and at a reduced temperature of 700 °C with 10% moisture, more Sr-rich oxides were detected.

Sr Segregation and Reaction at YSZ/GDC Interfaces
LSCF readily reacts with YSZ. Chen et al. [155] reported that the solid reaction of LSCF-YSZ mixtures starts at a calcining temperature of 800 °C to form a secondary phase of SrZrO 3 . SrZrO 3 possesses an orthorhombic structure at room temperature [244] and is an electrical insulator with a poor ionic conductivity of 1.87 × 10 −6 S cm −1 at 800 °C [245,246], which is more than four orders of magnitude lower than 8.70 × 10 −2 S cm −1 of GDC and 5.40 × 10 −2 S cm −1 of YSZ [247]. In addition, the generated SrZrO 3 phase at the electrode/electrolyte interface can block ion migration [248] and the diffusion of Sr to YSZ surfaces can cause Sr depletion in LSCF, leading to the further formation of Sr-free La(Co,Fe)O 3 with significantly reduced electrocatalytic activities for ORR [249,250]. Because of this, GDC or SDC barrier layers between LSCF and YSZ are essential for conventionally sintered LSCF electrodes at high temperatures of 1000-1200 °C to avoid chemical reactions at the LSCF/YSZ interface. Despite this, numerous reports have shown that even in the presence of doped ceria barrier layers, SrZrO 3 phases can still form at the YSZ interface after high-temperature electrode sintering [84,100,246,249]. The diffusion of Sr across the GDC layer is mainly caused by the high reactivity of segregated Sr species. Thermodynamically, surface-segregated Sr species exist mainly in the form of Sr(OH) 2 in humid air that is volatile under SOFC operating conditions [251]. Because of this, volatile Sr species can easily diffuse across the pores or grain boundaries of GDC barrier layers through gas-or solid-phase diffusion to reach the YSZ surface and form SrZrO 3 [56,252]. For example, Lu et al. [56] reported that after the sintering of a YSZ electrolyte close to an LSCF pellet without physical contact at 1200 °C for 50 h, SrZrO 3 was observed at the grain boundary of the YSZ electrolyte surface, indicating the volatility of surfacesegregated Sr species. Yin et al. [251] also compared the SrO activity of SrO powder with LSCF powder through annealing at 1000 °C in air for 200 h in which a YSZ sheet was placed on top of the powders without direct contact during annealing. It was reported that after annealing with SrO powder, Sr deposition was observed on the YSZ surface, whereas after annealing with LSCF powder, no Sr deposition was observed on the YSZ surface, indicating the higher SrO activity of SrO powder as compared with LSCF powder at 1000 °C.
Lu et al. [56] further investigated the effects of sintering temperature on LSCF electrodes and observed the formation of a SrZrO 3 layer on the SDC/YSZ interface at sintering temperatures of 1150 °C and above. At a lower sintering temperature of 1050 °C, EDS analysis revealed the presence of significant amounts of Sr at the SDC/YSZ interface. On the other hand, Gao and Barnett [253] did not detect Sr diffusion to GDC/YSZ interfacial regions after sintering LSCF-GDC composite oxygen electrodes at 1100 °C for 2 h. This discrepancy may be due to variable surface chemistry of LSCF and the physical states of GDC barrier layers.
Because the pores of doped ceria barrier layers can facilitate the diffusion of volatile Sr, the adoption of a dense, pore-free doped ceria barrier layer is useful in blocking Sr diffusion [56,254]. For example, Lu et al. [56] reported that in contrast to significant Sr diffusion to YSZ and porous SDC layer interfaces, the deposition of a dense SDC layer through PLD led to undetectable amounts of Srat YSZ electrolyte surfaces after sintering at 1200 °C for 2 h. The suppression of Sr diffusion led to the increase in PPD from 0.7 W cm −2 for the porous SDC barrier layer to 1.2 W cm −2 for the densified SDC layer. Despite this, dense GDC barrier layers cannot completely eliminate Sr diffusion during extended sintering and under long-term operating conditions and segregated Sr diffusion can proceed through grain boundary or surface diffusion pathways in GDC layers [100,254].

Composition Manipulation and Doping
One effective strategy to suppress Sr segregation and migration is to introduce A-site deficiencies in LSCF [56,103]. For example, Lu et al. [56] reported that a 5% A-site-deficient LSCF oxygen electrode, (La  [38,258] reported that Ca doping in the A-sites of double-perovskite structures to form NdBa 1−x Ca x Co 2 O 5+δ (NBCC) and PrBa 0.5 Sr 0.5−x Ca x Co 2 O 5+δ (PBSCC) can significantly enhance the electrochemical performance and operating stability of electrodes under air and CO 2 -containing atmospheres. Chen et al. [39] also demonstrated the excellent ORR activity and remarkable CO 2 tolerance of Cadoped PrBa 0.8 Ca 0.2 Co 2 O 5+δ (PBCC). When exposed to ~ 1 vol% CO 2 at 750 °C, the initial R P of the PBCC electrode was 0.024 Ω cm 2 and slightly increased to 0.028 Ω cm 2 after operation for 1000 h, which is ~ 1/24 that of an LSCF oxygen electrode under the same conditions. Here, the enhanced stability was attributed to both the increased electron affinity of mobile oxygen species with Ca as determined through DFT calculations and the increased redox stability from coulometric titration [38]. Impedance spectroscopy and in situ surface-enhanced Raman spectroscopy analyses indicated that the surface of PBCC was much more active for oxygen exchange and more robust against CO 2 poisoning than that of LSCF as confirmed by DFT calculations [39].
B-site doping with high valence cations such as Nb [259][260][261][262][263][264], Sb [265,266], Mo [267], Ta [268], Y [269][270][271][272], Sc [273] and W [274,275] has also been shown to be effective in enhancing the structural and compositional stability of cobalt-containing perovskite oxygen electrode materials such as LSCF, BSCF, SrCoO 3−δ and BaCoO 3−δ . For example, Li et al. [268] reported that Nb-and Ta-co-doped SrCoO 3−δ (SrCo 0.8 Nb 0.1 Ta 0.1 O 3−δ ) significantly stabilized the perovskite structure, which led to enhanced ORR activities. Duan et al. [271,276] also studied a Zr-and Y-co-doped BaCo 0. 4  at 600 °C) and better electrochemical activities for ORR as compared with those of LSCF or BCFN in temperatures ranging from 600 to 900 °C. In addition, the surface of the prepared LSBCFN was clean after polarization in the presence of a Fe-Cr metallic interconnect in contrast to the significant deposition of Cr compounds observed on LSCF and BCFN electrode surfaces (Fig. 17). Here, Cr deposits on BCFN surfaces were mainly composed of Ba and Cr (Fig. 17d) and can be attributed to the formation of BaCr 2 O 4 and/or BaCrO 4 [277]. The high resistance of LSBCFN electrodes to Cr deposition is due to the significantly reduced surface segregation of Sr and Ba (Fig. 17g).
One positive effect of high valence cation doping is the control of Co valences as the structural stability of Co-based perovskite oxides is mainly affected by the oxidation state of Coin perovskites [266,273,278]. Based on this, Wang et al. [264,279] systematically studied the chemical stability of BSCF in a wide range of oxygen partial pressures from 1 to 10 −22 bar from room temperature to 1000 °C and found that the cubic phase of BSCF decomposed if trivalent Co ions were oxidized to higher oxidation states in high oxygen partial pressures or if divalent Co ions were reduced to lower oxidation states in low oxygen partial pressures [279]. Usiskin et al. [278] also reported that both BSCF and SrCo 0.9 Nb 0.1 O 3−δ (SCN) can experience oxidative partial decomposition, which is thermodynamically preferred if the average valence of Co is greater than ~ 3.0. The doping of high valence cations can also effectively tune Co valences and therefore tailor the chemical stability of Cobased electrode materials. For example, Sc doping led to the absence of Co 4+ in SrSc 0.2 Co 0.8 O 3−δ [273]. Wang et al. [264,266] reported that the doping of high valence Nb or Sb into B-sites lowered the average valence of Co and consequently improved the chemical stability of BSCF under high oxygen partial pressures.
However, there is a balance that exists between structural stability and electrocatalytic activity in the doping of high valence cations in perovskite oxygen electrode B-sites. For example, Fan et al. [280] reported that in the case of Nbdoped BSCF, Nb doping can enhance the structural stability of BSCF but at the expense of reduced oxygen permeation activity. The doping of 10% Nb in BSCFB-sites led to a 10% lowering in oxygen flux, whereas the doping of 20% Nb drastically increased performance losses to 65%. Similarly, Chen et al. [189] reported that Nb doping in LSCF B-sites significantly reduced SrO surface segregation and enhanced the stability of oxygen electrodes but also decreased electrode activity, whereas Pd doping promoted ORR activities due to the exsolution of catalytically active Pd/PdO nanoparticles under the influence of cathodic polarization. As a result, the synergistic effects of Nb and Pd co-doping can lead to increased electrocatalytic activities and operating stability for LSCF electrodes.

Surface Modification
The modification of cobaltite-based perovskite oxides with intentionally selected catalysts/materials has been extensively adopted to improve the electrocatalytic activity of oxygen electrodes [281][282][283][284][285]. In addition, these modifications can potentially suppress SrO surface segregation and enhance operating stability. For example, Choi et al. [17] developed a facile infiltration approach to modify LSCF electrodes with a dense and conformal LSM film coating in which the LSM film was epitaxially grown on LSCF grains after annealing at 800 °C due to their structural similarities. This approach took advantage of the fast ionic and electronic transport of the LSCF backbone and the facile surface kinetics of the LSM thin film, and as a result, the LSM film coating significantly enhanced the electrocatalytic activity and stability of LSCF during operations at 750 °C for 500 h (Fig. 18) [286]. It has also been reported that LSM infiltration can enhance the operational stability of BSCF in CO 2 [287].
In another study, Chen et al. [288] reported that the infiltration of multi-phase catalyst coatings composed of BaCoO 3−x (BCO) and PrCoO 3−x (PCO) nanoparticles and conformal PBCC thin films on LSCF led to much better performances with excellent durability as compared with bare LSCF cells within 250 h. The coating of BCO on LSCF can significantly suppress Sr surface segregation and enhance operating stability during exposure to Cr contamination [289].
Researchers have also reported that alkaline earth metal-free oxides such as LNO, LaCoO 3−δ (LC) and PrNi 0.5 Mn 0.5 O 3 (PNM) can act as effective surface protective layers and LNO coatings can not only enhance electrode electrocatalytic activities, but also increase the operational stability LSCF and La 0.8 Sr 0.2 Co 0.8 Ni 0.2 O 3−δ [290,291]. In addition, PNM, LNO and LC coatings can enhance the tolerance of LSCF, BSCF and PBSCF to CO 2 and CrO 3 [189,238,[292][293][294]. Moreover, Chen et al. [295] studied the effects of PrO 2 , CeO 2 and Pr 0.2 Ce 0.8 O 2 (PDC) coatings on LSCF film surfaces and found that PrO 2 coatings can induce higher oxygen vacancy concentrations as compared with bare LSCF, greatly enhancing the rate of oxygen dissociation and ORR activity. In addition, PDC and CeO 2 coatings can suppress SrO surface segregation, thus enhancing durability. These results were also in good agreement with the positive effects of GDC nanoparticle decoration on the suppression of SrO surface segregation in LSCF and SSC electrodes [296][297][298]. Furthermore, Li et al. [290] reported that SDC infiltration can significantly enhance the CO 2 tolerance of SrCo 0.85 Ta 0.15 O 3 electrodes.
In another study, Gong et al. [299] investigated the effects of nanoscale ZrO 2 films on the cation stability of nanostructured LSC electrodes in which LSC was first infiltrated into an LSGM scaffold and coated with a conformal layer of the nanoscale ZrO 2 film through atomic layer deposition (ALD). And as a result of this ZrO 2 coating, reductions in R P and degradation rates as compared with the pristine sample by factors of 19 and 18 during stability testing at 700 °C for 4000 h, respectively, were observed. Here, the improved ORR activity retention was attributed to the suppression of Sr enrichment through the exchange of Zr M • for Co(III) and the creation of space charge layers across the oxygen electrode/ZrO 2 interface according to a defect chemistry model. Gong et al. [300] also used ZrO 2 coatings to enhance the cation stability of LSCF-GDC oxygen electrodes. Yildiz et al. [165] modified LSC film surfaces by infiltrating cations more and less reducible than Co into LSC B-sites and found that the infiltration of less reducible cations can significantly suppress Sr segregation and phase separation and reduce surface oxygen vacancy concentrations as well as increase LSC surface oxidation. Here, the reduction in surface oxygen vacancy concentrations led to decreased electrostatic interactions between oxygen vacancies and Sr cations, meaning that the infiltration of less reducible cations can significantly improve stability. These researchers further reported that the addition of Hf led to up to 30 times faster oxygen exchange kinetics after annealing at 530 °C for 54 h in air.

Phase Migration and In Situ Formation of Protective Layers
More recently, Ai et al. [301,302] [303]. Here, these results indicate the redistribution and migration of the ESB phase in the ESB-LSCFNb composite towards the YSZ electrolyte under the influence of cathodic polarization and the formation of a thin ESB layer at the cathode/YSZ electrolyte interface (Fig. 19). And aside from individual and isolated Sr-rich areas/particles in the size range of 10-40 nm, La and other elements of LSCFNb were uniformly distributed, indicating the significant suppression of Sr segregation and diffusion in LSCFNb electrodes under polarization conditions by ESB decoration. The in situ formed ESB layer can not only prevent direct contact and subsequent reaction between segregated SrO and the YSZ electrolyte, but also significantly promote oxygen migration/ diffusion at the interface for O 2 reduction reactions, resulting in remarkable increases in power output and decreases in activation energy. And overall, these results clearly demonstrate the benefits of the in situ formation of highly functional and active ESB protective layers on LSC-based cathode and YSZ electrolyte interfaces through ESB-decorated composite cathodes under SOFC operation conditions. Despite this, more work is required to optimize the polarization conditions for these phase migrations and distributions for the electrode/electrolyte interface of SOCs.

Concluding Remarks
Cation surface segregation, particularly Sr, is thermodynamically favourable under SOC operating conditions. Segregated Sr cations are uniformly dispersed on electrode surfaces and can gradually agglomerate to form Sr-rich secondary phases in the form of SrO, SrCO 3 or Sr(OH) 2 . These Sr-rich secondary phases are electrochemically inert, and their occupation on active surface sites can drastically deteriorate ORR/OER electrocatalytic activity. The excess surface segregation of Sr can also lead to the deficiency of Sr cations at the A-site of perovskite oxides, resulting in the deterioration in the electronic as well as ionic conductivity properties of the oxygen electrodes. And the major driving forces of surface segregation include elastic and/or electrostatic interactions. However, under polarization conditions, oxygen nonstoichiometry, i.e. the oxygen vacancy formation and termination processes on the surface of the perovskite electrodes, induced by the cathodic and anodic polarization Fig. 19 a STEM-EDS element mapping and b HRTEM and FFT images of the ESB-LSCFNb/YSZ interface of an anode-supported YSZ electrolyte cell with a directly assembled ESB-LSCFNb electrode after polarization at 250 mA cm −2 and 750 °C for 100 h. Red arrows indicate lattice distortion. Reproduced with permission from Ref. [303]. Copyright 2018, American Chemical Society could substantially modulate and change nature of the electrostatic interactions, accelerating or incorporating surfacesegregated Sr species. The dominant role of oxygen vacancy generation/termination under polarization conditions is evidently illustrated by the opposite effects of polarization on Sr surface segregation and incorporation or inhibition on LSM and LSCF electrodes. Because of this, the role of polarization in surface segregation is particularly important for the fundamental understanding of the performance and stability of SOCs under cyclic polarization or reversible operating conditions. Segregated cations, particularly Sr and Mn species, can further interact chemically with volatile impurities such as Cr, S and B in SOC stacks, leading to contaminant deposition and poisoning as well as significant performance degradation. Because of this, inhibition and significant reduction of surface cation segregation are critical in the enhancement of SOC electrochemical performance and durability. Here, the manipulation of operating regimes as well as the modification of stoichiometric compositions and oxygen electrode surfaces is effective approaches to mitigate the detrimental effects of surface segregation on operational stability. In addition, recent developments in the phase migration and in situ deposition and formation of highly active and protective layers on electrode/electrolyte interfaces have shown particular potential in the mitigation and inhibition of the detrimental effects of surface segregation in cobaltite-based electrodes of SOCs. Figure 20 summarizes the phenomena, electrochemical properties and mitigation strategies of cation surface segregation of SOC cathodes.
Overall, more insightful and fundamental knowledge concerning cation segregation, particularly in Sr-containing perovskite oxygen electrodes, is needed to foster the development of commercially viable SOC technologies. Here, key questions that need to be addressed include surface chemistry (e.g. segregation, diffusion, surface termination), and changes in surface chemistry with environment such as volatile species, microstructural features under static annealing conditions; oxygen nonstoichiometry and its associated surface chemistry under dynamic polarization conditions; cation segregation, distribution and phase changes at electrode surfaces and electrode/electrolyte interfaces; and the fundamental effects of segregation on electrochemical activity and long-term durability. And to address these interrelated and complex scientific questions, a combination of in situ and ex situ surface and microstructural characterization techniques such as synchrotron XAS, XPS, EELS, SIMS, high-temperature scanning probe microscopy and FIB-STEM as well as computational and thermodynamic modelling need to be applied to obtain model electrodes under well-controlled and defined test conditions to provide critical insights into the mechanisms of cation segregation that can further be used to predict the long-term activity and durability of SOC oxygen electrodes. Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creat iveco mmons .org/licen ses/by/4.0/.