Efficient Separation of Nd(III) and La(III) Via Supported Liquid Membrane Using EHEHPA (P507) as a Carrier

This work tested an effective and efficient Nd/La extraction and separation via flat-sheet supported liquid membrane. A microporous polypropylene film was used as the solid support for the liquid membrane and P507 as the extractant. The effect of Nd(III) and La(III) concentration in the feed, the concentration of P507, and acid solution concentration in the stripping phase on Nd and La extraction and separation were studied. The results suggest the extraction of La and Nd increases with the initial pH of the feed solution and P507 concentration. Maximum separation factor of 44.25 was obtained at the low P507 concentration of 5% (v/v).

Nowadays, the interest in neodymium extraction is increasingly significant due to the demand for commercial super magnets based on Nd 2 Fe 14 B permanent magnets and solid lasers used in the medical industry [10][11][12]. The primary resource of neodymium originates from the monazite ore. Monazite ore is an essential source of neodymium, typically containing 45% Ce, 23% La, and 17% Nd and minor amounts of Pr, Sm, Gd, and Y. Nd extraction for monazite processing requires La and Nd separation after removing thorium phosphate and insoluble CeO 2 products [13]. Another resource of Nd is the recycling of spent Nimetal hydride (Ni-MH) secondary batteries [14][15][16]. The Ni-MH batteries were subjected to acid leaching. After removing the Ni(II), Co(II), and Mn(II) either by electrodeposition or solvent extraction, La and Nd were left in the leaching solution subject to separation [17].
However, separating and purifying REEs can be difficult due to their similar chemical and physical properties [18]. In general, the separation of REEs is developed based on ion exchange and solvent extraction [19,20]. The solvent extraction method has been commercially employed as the principal technique for separating REEs, especially for handling large volumes of diluted pregnant liquors. The fundamental theory of light REEs lies in the lanthanide contraction effect [18]. The effect demonstrates the steady decrease in the size of the atoms and ions of the rare earth elements with increasing atomic number from lanthanum (atomic number 57) through lutetium (atomic number 71). The phenomena decide the trends in the stability constants of the complexes, allowing particular distinction for element separation [21].
The supported liquid membrane (SLM) separation techniques have been attracting more attention due to the superiority of low solvent inventory, ease of operation, and simultaneous extraction and stripping [17,[30][31][32][33][34]. REEs separation using SLM method can be straightforwardly seen as a simultaneous three-step process: (1) molecule extraction from feed phase to the SLM, (2) diffusion through SLM, and (3) stripping process to the received phase. The selective transport is based on the different permeability of cations. At the same time, the permeability is related to the driving force of feed to organic strips and the thickness of the membrane. Several reports have used SLM to extract and separate REEs [30,31,[33][34][35][36][37]. Ryan C. Smith et al. studied the REEs recovery from coal fly ash leachate using SLM [30]. They found that SLM process was more selective for heavy REEs, while the convention SX process favored the selectivity for light REEs. J. Martinez studied the factor influencing selectivity of a ternary mixture of REEs (yttrium-neodymium-dysprosium) using flat-sheet SLM (FSSLM) [33]. The results suggested that lower the pH of the stripping phase increased selectivity. Also, reducing the extractant concentration significantly improved the selectivity but increased the processing time. This work explores two typical light REEs (Nd and La) extraction and separation with flat-sheet SLM using extractant P507. The effect of feed concentration, feed pH, P507 concentration, strip solution composition, and strip acidity has been studied on the extraction and separation of La/Nd has been studied in detail. The optimal conditions determined will be used for pilot-scale research of REEs separation with hollow-fiber SLM technology.

Extraction Experiment
The FSSLM experiments were carried out in a two-compartment cell, as shown in Fig. 1. The hydrophobic polypropylene membrane was immersed in P507/D80 mixture with a predetermined % (v/v) and treated with an ultrasound bath for 10 min. The membrane pores were filled with carrier solution by capillary action. The membrane was then impregnated in the organic solutions and kept in the petri dish for 12 h before the extraction experiment. After removing from the carrier solution, the excess carrier solution on the surface of the membrane was then wiped out with tissue paper. Subsequently, the loaded membrane was clamped between the two compartments and was fixed firmly by using the gasket to avoid possible solution leakage from one compartment to the other. The feed and strip solutions were added into the two separate chambers. The feed solutions were 250 mL acidic solutions containing La(III) and Nd(III), and the strip solutions were acidic solutions with higher acidities.
The solutions were stirred at 350 rpm for 6 h at room temperature (20 ± 2 °C). Samples from both feed and strip solutions were taken at 0, 0.5, 1, 1.5, 2, 3, 4, 5, and 6 h for La(III) and Nd(III) concentration measurement. Amounts of 250-1000 µl solutions from both the feed and strip were withdrawn and diluted. Their concentrations were determined for both feed and strip solutions by ICP-OES (inductively coupled plasma-optical emission spectrometry) using a Perkin Elmer Optima 3000. Before and after the separation tests, the membranes were subjected to elemental analysis via PXRF (portable X-ray fluorescence spectroscopy). The P concentration from the PXRF measurement reflects the content of P507 loaded on the membranes. La and Nd extraction using P507 (abbreviated as H 2 A 2 ) is a cation exchange process. The extraction of REEs from feed solution is accompanied by the release of three hydrogen ions from the extractants, as shown in Eq. 1-2.
According to the equation, the high acidity in the feed phase has an adverse effect on La and Nd transport. In contrast, the stripping process is promoted by increasing the acidity of the aqueous stripping solution. Therefore, it is critical to determine the optimal initial pH of feed solutions and strip acidity. The amount of P507 on the membrane is also related to the REEs extraction process and the REEs concentration in the feed phase from the above equations.
The Nd and La extraction efficiency can be quantified as the extraction fraction for a single REE extraction, which illustrates the percentage of Nd(III) or La(III) transported into the strip solution from the initial feed solution. To simplify the process, the concentration at the membrane boundaries was neglected. The equations can be written as: where [La(III)] Feed;0 and [Nd(III)] Feed;0 represent the initial Nd(III) and La(III) concentration in the feed solution. To evaluate the feasibility of separating Nd(III)/La(III) using P507 in SLMs, the separation factor was introduced: A more significant value of α means a better separation effect.
The permeability coefficients La(III) and Nd(III) in the membrane were determined experimentally by plotting the linear relationship curve for ln (C f,t /C f,0 ) vs. t as the following equation: where C f,0 and C f,t are the REE ion concentration in the feed at t = 0 and time t, respectively, Q is the effective surface area (cm 2 ), which is the product of geometric surface areas (25 cm 2 ) and porosity (55%), V is the total feed volume (250 mL), and P is the permeability coefficient (cm/s).

Effect of Initial La(III)/Nd(III) Concentration
Extraction and separation of Nd/La were first investigated as the function of La(III) and Nd(III) concentrations at 100, 200, 500, and 1000 mg/L. The initial pH of the feed solution was 3. The strip solution was a 3 M HCl solution. The extractor was 20% (v/v) of P507 in D80 diluent. Figure 2a, b shows extraction% of Nd and La within 6 h, respectively. It is evident that the processing time increases with the increase of the initial ion concentration. When La(III) and Nd(III) concentrations were 100 and 200 mg/L, both La and Nd extraction exceeded 90% after 6 h but with limited selectivity. However, when the concentration of La(III) and Nd(III) was 500 and 1000 mg/L, selectivity increased although with decreased extraction. The Nd(III) extraction was 96.2% in the 500 mg/L test, while La(III) extraction was only 61.2%. By increasing the ions concentration to 1000 mg/L, the extraction% of Nd and La was calculated as 88.8 and 13.7, respectively. The separation selectivity for the binary Nd/La mixture was also studied. The separation factor at 6 h was calculated based on Eq. 5, as shown in Fig. 2c. It is apparent that with the increase of the Nd(III) and La(III) concentration from 100 to 1000 mg/L, the α(Nd/La) increased from 1.03 to 6.39. Apparently, at a low feed concentration (less than 500 mg/L), the saturation of P507 was present in the membrane phase. Thereby, the transport of both La and Nd wasn't restricted. When the ions concentration increased to > 500 mg/L, more Nd(III) was loaded on the membrane phase and recovered in the trip phase.

Effect of P507 Concentration on Nd/La Separation
The extractant concentration plays a significant role in metal ions' transportation for the SLM process. The effect of the phosphorus extractant (P507) concentration on separation of Nd from Nd-La mixed solution in P507-HCl system: 5, 10, 20, and 40% (v/v) of P507/D80 was used. The feed solution was at initial pH of 3, 1000 mg/L La(III) and Nd(III) containing HCl solution. The strip solution was a 3 M HCl solution. Figure 3a, b shows the extraction % of Nd and La within 6 h. Figure 3c shows the selectivity of Nd extraction.
In order to partially quantify the concentration of P507 loaded on the membrane, PXRF (portable X-ray fluorescence spectroscopy) scan was conducted to determine the P concentration on the loaded membrane. This is due to P507 being a phosphorus-based extractant. The results of P wt% from scanning the membrane are shown in Table 1. The table shows the P wt% increased from 0.54 at 5% (v/v) to 5.05 at 40% (v/v) P507 concentration. Moreover, the P wt% only slightly decreased for the membrane before and after the tests, which suggests negligible loss of the extractant in the acidic environment, especially the strip that had 3 M HCl. For example, the 20% P507 test had an initial P wt% of 2.81 and decreased to 2.62 wt% after REEs transport. From Fig. 3, the extraction of both Nd and La increased with higher P507 concentrations. When raised the P507 concentration from 5 to 40% (v/v), the extraction of Nd(III) and La (III) significantly increased from 51.83 to 94.11% and 1.17-28.18%, respectively, after 6-h tests. The selectivity analysis also found that the extractant concentration significantly affected the selective extraction of Nd. The separation factors, α(Nd/La), shown in Fig. 3c, depict the high dependence on the P507 concentration. The highest value of α(Nd/La) was found to be 44.25 at 5% (v/v) P507 and drastically reduced to only 6.39 and 3.23 for 20 and 40% (v/v) of P507. The phenomena provide an opportunity for the separation of Nd from La. As shown in Fig. 3d, the permeability coefficient value increased with extractant concentration for La(III) and Nd(III), respectively. Also, it was presented that the Nd(III) permeability values were higher than those of La(III) in the P507 concentration range from 5 to 40% (v/v), and the gap was widened with increasing P507 concentration. Moreover, the results indicated that the P507-Nd/La complex transport increased linearly when the P507 concentration ranged from 5 to 20% (v/v).

Effect of Feed Acidity on Nd/La Separation
According to the REEs extraction principle, the feed solution pH is another critical parameter to separate REEs using a cationic extractant. The extractant is loaded with REEs during the extraction process, and free protons are released into the feed phase, causing the pH to decrease. Based on Eqs.
(1) and (2), the decreasing H + concentration promotes the Nd(III) and La(III) to interact with the extractant in the first stage. To verify the effect of the initial feed solution pH, the SLM tests were designed with varied initial pH of 0, 1.5, 2, 3, and 4. The feed solutions contained 1000 mg/L of La(III) and Nd(III). The extractant was 20% (v/v) 507, and a 3 M HCl solution was used as the strip phase. The extraction% of Nd and La is shown in Fig. 4a and Fig. 4b, respectively. The separation factors diagram as per pH is shown in Fig. 4c.
The percentage of La and Nd extracted both increased with increasing pH. When pH is 0, no La and Nd extraction

Effect of Strip Acidity on Nd/La Separation
According to the cation exchange reaction above, the acid concentration solution is supposed to affect the REEs loaded  Fig. 5a, b. The Nd extraction rate has no noticeable change when the HCl ranges from 0.5 to 3 M from Fig. 6a, ranging between 88.80 and 93.29%. However, further increased the HCl concentration to 5 M, the Nd% extracted drastically decreased to 77.13%. As for the La extraction, with an increase of HCl concentration from 0.5 to 5 M, the La extracted% decreased from 22.30 to 6.11%. The separation factors in the extraction for different HCl concentrations are shown in Fig. 5c. As can be seen, with the increase of the acidity, the α (Nd/La) increased from 4.18 at 0.5 M HCl and reached the maximum value of 12.63 at 5 M HCl. As illustrated above, the cation ions transfer related to the H + concentration in the dispersed phase. However, the nature of the acid necessarily differs for variant acids. Thereby, the mass transfer power will be unequal. To explore the role of different trip agents on Nd/La separation, HCl, H 2 SO 4 and HNO 3 with the same H + concentration were used in the strip phase. The feed solution was a pH 3, 1000 mg/L La(III) and/Nd(III) containing HCl/H 2 SO 4 /HNO 3 solution. The strip phase was an acid as same as the feed solution with 3 M H + . The extractant was 20% (v/v) P507. The extraction and separation results are shown in Fig. 6. HCl is the most efficient agent for La(III) and Nd(III) extraction, presenting the above extraction curves. The percentage of La and Nd extracted has the following order: HCl > HNO 3 > H 2 SO 4 . As for the selectivity, it was found that α(Nd/La) was higher in HCl and H 2 SO 4 system, 6.49 and 6.80, than in HNO 3 , 4.30. HCl solution was proven to be the most effective stripping agent for Nd and La extraction, and HCl and H 2 SO 4 had superior effect of Nd/La separation.

Effect of Nd/La Ratio in the Feed Solution
The different mole ratio of Nd(III)/La(III) in the feed was also investigated, considering the practical application for all kinds of REEs sources, including the monazite ore and Ni-MH secondary batteries. The mole ratio was set to be Nd(III)/La(III) = 1/4, 1/2, 1, 2, 4. The extractant was 20% (v/v) P507/D80 mixture, and the strip solution was a 1 M HCl solution. The process time was 6 h for all the tests in this study. The results, including Nd, La extraction%, and the Nd selectivity, are shown in Fig. 7. As discussed above, Nd(III) is more prone to be transported through the SLM than La(III). Figure 7a indicates that the Nd extraction% has a narrow extraction percentage ranging between 87 and 95% with varied Nd(III)/La(III) mole ratios. However, the La(III) transport was retarded by the high ratio of Nd(III)/La(III). At the ratio of 4, the La(III) extraction was only 16.14%, while it increased to 45.70% at the ratio of 1/4. It can be concluded that the feed solution composition correlated with the selectivity of the Nd. Due to the faster transport of the Nd-P507 complex than La, the higher ratio of Nd/La in the feed, the higher α(Nd/La) would be obtained. The Nd selectivity shown in Fig. 7c demonstrates that the α(Nd/La) increases with the Nd(III)/La(III) mole ratio from 2.08 to 5.88.

Conclusions
The interest in neodymium (Nd) is increasing due to its vital role in high-tech sectors, such as permanent magnets (Nd 2 Fe 14 B alloys). The extraction of Nd from ores and recycling of Nd from the wastes demand effective and efficient Nd and La separation. This research used a supported liquid membrane with EHEHPA (P507) to extract and separate Nd(III) and La(III). The effect of Nd(III) and La(III) concentration in the feed, feed pH, P507 concentration, and the acidity stripping phases on Nd/La extraction and separation were discussed. The results show that the feed solution pH and P507 concentration play significant roles in Nd/La extraction and separation. When the initial concentration of La(III) and Nd(III) was 1000 mg/L, 20/80 (v/v)% P507, feed pH 3, and strip solution was 3 M HCl, 99.8% of Nd(III) was extracted after 6 h, while the extraction of La(III) was 22.2%. The tests at 5% (v/v) of P507 and feed pH of 1.5 showed the highest Nd(III)/La(III) separation factors of 44.25 and 19.25, respectively.