Diverse Structural Design Strategies of MXene-Based Macrostructure for High-Performance Electromagnetic Interference Shielding

Highlights MXene-based macrostructure development and EMI shielding mechanisms are reviewed. Various structural design strategies for MXene-based EMI shielding materials are highlighted and discussed. Current challenges and future directions for MXenes in electromagnetic interference shielding are outlined.


Introduction
The complications associated with electromagnetic interference (EMI), which is caused by adverse electromagnetic waves (EMWs) or radiation, are becoming more severe as high-tech industries continue to expand.EMI adversely affects electrical devices and equipment, interferes with their functioning, contaminates the environment, and jeopardizes human health [1][2][3].EMI shielding inhibits or attenuates EMWs transmission between the protected region and surrounding environment.In theory, EMWs are reflected and absorbed by shielding materials [4][5][6][7].Therefore, the purpose of EMI shields is to eliminate EMI, which has significant implications for the development of next-generation electronics, communication technology, Internet of Things, and aerospace technology.Although conventional metal materials, characterized by great electrical conductivity, perform well as EMI shields, their inherently grreat density, bad corrosion stability, and demanding processability severely restrict their usage in greatly integrated modern mobile electronics [8][9][10].Thus, composites containing various fillers [11], magnetic fillers [12], and dielectric fillers, have been created as substitutes for metals in EMI shielding applications [13][14][15][16].Although these composites are lightweight and have anticorrosive nature, their restricted shielding capacities and complex processability restrict their widespread utilization [17].
MXenes are 2D transition metal carbides and/or nitrides with the generic formula M n+1 X n T x (n = 1-3) [18][19][20].The selective etching of a layer, typically comprising a group IIIA or group IVA factor, is often performed to match the MAX phase precursors (M n+1 AX n ) and create layered MXene materials.The distinctive 2D layered structure and rich surface functional groups give MXenes remarkable features, including high conductivity, surface hydrophilicity, and mechanical steadiness [21].Owing to their exceptional qualities, MXenes can be adopted in a broad range of usage, including supercapacitors, alkali metal ion storage devices and sensor platforms.Moreover, MXenes show significant potential for the growth of EMI shielding materials because they possess the necessary fundamental properties for constructing effective EMI shielding macrostructures, including excellent mechanical properties, remarkable electrical conductivity, big given surface areas and aspect ratios, and, most importantly, simple processability in aqueous media [22][23][24][25].Because the first report on the exceptional EMI shielding capabilities of Ti 3 C 2 T x MXenes in 2016, research in this field has proliferated exponentially (Fig. 1).Therefore, reviews centered on the development and future of EMI shielding materials on basis of MXene are highly desirable.Although there are some reviews of electromagnetic shielding materials based on MXene, these articles mainly explore MXene components, rather than the structure of MXene-based electromagnetic shielding composites.This review pays attention to the progress in the assembly of MXene-based EMI shielding macrostructures, as well as the associated EMI shielding mechanisms.Meanwhile, diverse structural design strategies for MXenebased EMI shielding materials are emphasized on basis of their inherent properties.In the end, the difficulties and views accompanying the development of MXene-based EMI shields are discussed.We hope that this material will serve as guidance for developing high-performance MXene-based EMI shielding macrostructures on basis of the rational design of components and structures and contribute to the high-efficiency utilization of emerging MXene nanomaterials.

EMI Shielding Mechanisms
Electromagnetic shielding is an important strategy for suppressing EMI and protecting against electromagnetic radiation.Electromagnetic shielding means the application of conductive or magnetically permeable materials as Fig. 1 The number of studies concerning "MXene" and "Electromagnetic shielding" published from 2016 to 2023.Source: Web of Science (Search time: March 2023) 1 3 shields to block the propagation EMWs and weaken the electromagnetic field [26].For understanding EMI shielding intrinsically, different shielding systems have been put forward, including the eddying role, electromagnetic field, and transmission line theories.The transmission line theory has been extensively implemented owing to the advantages of simplicity, and convenient and accurate calculation.The transmission line theory is often used to illustrate electromagnetic shielding mechanisms [27][28][29] that comprise three distinct processes, namely, reflection, absorption, and multiple reflection [30].Specifically, incident EMWs reaching the surface of a shielding material are partially shown as a result of the mismatch between the shielding material and air.The non-shown EMWs enter the shielding material where they are reflected numerous times and absorbed.The remaining small part of EMWs pass by the shielding material as transmitted waves.Figure 2 describes the EMI shielding system [31].

EMI Shielding Performance
The degree of incident EMWs attenuation is a key indicator for evaluating the shielding ability of a material.EMI shielding efficacy (EMI SE, unit: dB) is employed for quantitatively expressing the shielding capacity of a material [32].It is represented by the proportion of the electric field strength, magnetic field strength, or effect of EMWs before and after they pass by the shielding material, as shown in Eq. ( 1) [33,34]: where the subscripts i and t show incident and transmitted EMWs.

Reflection Loss (SE R )
SE R is brought by an impedance mismatch between the propagation medium of the incident EMWs and the surface of the shielding material.The SE R magnitude from the front to the back surface of the shield can be shown below [40]: where Z and Z 0 impede the shield material and air; and stand for the electrical electroconductibility and the magnetic penetrability; and f stands for the frequency of the incident EMWs.According to the formula, SE R is associated with the electroconductibility and magnetic penetrability of the material and the frequency of the EMWs.

Absorption Loss (SEA)
SE A is mainly derived from the dielectric and magnetic losses of a material [41].To achieve great absorption loss, the conditions below are required: high electrical conductivity for ohmic loss, which increases interactions between the electrons and (1) incident EMWs [42]; high dielectric and magnetic permeabilities increase the eddy current loss and magnetic hysteresis loss [43].The absorbed electromagnetic energy is dissipated as heat.The absorption loss (SE A ) of a shielding material can be shown as follows [44][45][46]: where d means the thickness of the shielding material, and stands for the skin or penetration depth.For conductive shields, the skin depth is shown as Here, means the EMWs attenuation constant of the shielding material and is expressed as , where stands for the angular frequency ( 2 f ) and is the dielectric permittivity.Hence, SE A depends on the controllable thickness and electrical conductivity and on the inherent electromagnetic nature of the material.

Multiple Reflections (SEM)
Various reflections of EMWs between two boundaries of a thin shield result in their attenuation.This process can be repeated until the electromagnetic energy dissipates completely.Multireflection effectiveness is calculated as follows [47,48]: SE M is majorly dependent on the thickness of the material.This parameter can be neglected when the shield is thicker than the skin depth, or in case of the SE T of above 15 dB [50,51].Nevertheless, if the thickness is significantly thinner than the skin depth, various reflections must be regarded while evaluating shield efficacy.

Internal Scattering (Internal Multiple Reflections)
In addition to the macroscopic reflections occurring between the two boundaries of an EMI shield, reflections and scattering inside the microstructure of the EMI shielding material can also occur.Such internal scattering (internal multiple reflections) may additionally prolong the propagation pathway of EMWs, thereby enhancing absorption loss and the total shielding effect.Therefore, the microstructures comprising a shielding material exert an important effect on EMI shielding.

Calculation of EMI Shielding Performance
For practical calculating EMI SE, the calculation theory on basis of either absorption or reflection loss is favored, depending on which property can be directly calculated from the scattering coefficients (S-parameters).Here, absorption loss and reflection loss are represented by SE A' and SE R' , respectively, to distinguish them from the concepts with the same name in the Schelkunoff theory: It is worth noting that macroscopic multiple reflection losses are encompassed by SE A' and SE R' ; thus, SE is defined as follows [49]: In addition, taking into account the density and thickness of the material, the feasible shielding effect of a material was defined by introducing the absolute shielding efficiency (SSE/t), which is calculated below: where and t denote the density and thickness of the shielding material, respectively.A great SSE/t proportion is required for lightweight shielding usage.

EMI Shielding Mechanism of MXenes
MXenes are metal carbide or nitride materials characterized by a 2D layered construction, great electrical conductivity, big given surface area, and rich functional groups [52].The favorable EMI shielding nature of these materials can be partly attributed to their great electrical electroconductibility [53] (10,000 S cm −1 ) and layered structure.When incident EMWs reach the MXene surface, a portion is shown because of the rich free electrons on the surface of the greatly conductive MXene [54].The EMWs enter the MXene lattice construction and make interaction with the dense electron to generate an electric current, resulting in ohmic losses, which attenuate EMWs.Moreover, layered structures can effectively enhance internal multiple scattering and reflection of EMWs; therefore, lamellar MXenes have been proven to be superior internal multiple reflection filler materials for EMI shielding [55].
3 MXenes as EMI Shielding Materials

MXene-Based Porous Materials
Lightweight design is becoming increasingly important in EMI shielding applications [44].In addition to effectively reducing the weight of composite materials, porous structures also promote multiple reflections of EMWs inside the material, thereby enhancing EMWs absorption and improving the shielding effect.

Foams and Aerogels
MXenes generally agglomerate readily, which limits the establishment of an effective conductive network.The introduction of porous structures can decrease the MXene agglomeration and improve the overall conductivity and electromagnetic shielding capacity of the material.Additionally, the weak interactions between MXene nanosheets preclude the construction of a three-dimensional structure with excellent mechanical properties using MXene alone; therefore, it is necessary to prepare MXene-based composites.MXene-based porous foams and aerogels have been widely studied as they are light-weight, highly porous, lowdensity, and adequately conductive.Liu et al. produced freestanding, flexible, reasonably strong, and hydrophobic MXene foams through fitting MXene sheets into thin films [56].By comparing with famous hydrophilic MXene materials, the MXene foam exhibited a startlingly hydrophobic surface, and excellent water resistance and durability.The MXene film was 6 μm thick, and its EMI SE was 53 dB, whereas that of the MXene porous foam grew to 60 μm and its EMI SE grew to 70 dB (Fig. 3a-g).The porous structure promoted EMWs scattering and reflection, effectively dissipating the EMWs energy.Notably, the EMI shielding system of the foam and film was absorption loss, which greatly reduced secondary electromagnetic pollution (Fig. 3h-k).Increasing the hydrazine dose resulted in increased thickness of the material and reduced density and conductivity.However, because the MXene foam formed a solid conductive network, the shielding properties of the material did not change significantly (Fig. 3l).The MXene foam showed comparable, high SE values and dependence on the expansion rate in both the experimental and calculated outcomes (Fig. 3m).
Using highly thermally conductive copper plates, Wu et al. constructed unidirectional aerogels coated with polydimethylsiloxane (PDMS) via directional freezing of MXene/ sodium alginate (SA).These lightweight, compressible aerogels with a honeycomb-like structure showed excellent conductivities of up to 2211 S m −1 and impressive EMI SEs of above 72 dB (Fig. 4) [57].The MXene/SA aerogels exhibited high conductivities of up to 644 S m −1 and great EMI SEs.The PDMS coating imparts considerable compressibility and durability to 3D conductive networks, broadening the potential applicability of composite foams to wearable devices and sensors.The foam coated with 6.1 wt% PDMS maintained the shielding efficiency at 48.2 dB.As MXene content increases, the SE T , and SE A increased significantly, while the SE R remained below 5 dB, suggesting that the electromagnetic shielding capacity of the foam was ruled by absorption loss, and that the internal conductive network facilitated EMWs absorption.
Zhao et al. constructed porous and conductive 3D MXene sheet structures via graphene oxide (GO)-helped hydrothermal assembly (Fig. 5a-c) [58].The MXene/RGO hybrid aerogel (MGA) presented a uniform cellular microstructure comprising intact MXene and exhibited an ultra-high electroconductibility of 1085 S m −1 .After compositing with epoxy resin, the composite aerogel displayed a great electroconductibility of 23.3 S m −1 and an EMI SE of 29.7 dB.When the fraction of MXene reached 0.74 vol%, the electroconductibility and EMI SE of the composites grew to 695.9 S m −1 and 56.4 dB (Fig. 5e-g).
Bian et al. prepared large-sized honeycomb-structured ultralight MXene aerogels comprising freeze-dried singlelayered MXene (Fig. 5d) [59].An MXene dispersion was first frozen, leading to the generation of ice crystals along the MXene sheets; the sheets were repelled by the ice crystal borders to build a steady network of connections.Subsequent freeze-drying sublimated the ice crystals while the MXene sheets maintained their original structure, thereby generating a large number of holes.The MXene aerogels showed great EMI shielding performances.The given shielding effect reached 9904 dB cm 3 g −1 (Fig. 5h-j).The great conductivity and electromagnetic shielding performances of the above two types of aerogels are largely attributed to their intricate 3D conductive network and porous structure.The size of the internal micropores was determined by the ice crystal volume, and could thus be regulated by adjusting the concentration of MXene in the aqueous dispersion.

Hydrogels
Abundant pores within a porous aerogel impede the penetration of EMWs; however, the air inside the pores limits further EMWs attenuation.Hydrogels contain water in their pores, thereby retaining the advantages of a porous structure, while being capable of further attenuating incident EMWs.Hydrogels have received widespread attention because of their favorable biocompatibility and robustness [130].
Yang et al. prepared MXene/polyvinyl alcohol biomimetic hydrogels using an ice-templated freeze salting-out method (Fig. 6a) [60].Except their great conductivity, mechanical strength, and ultraflexibility, the porous structures exhibited a honeycomb arrangement.The EMI SE of thin MXene/PVA hydrogels reached 57 dB in the X-band when the MXene content was only 0.86 vol% (Fig. 6b-g).The outstanding EMI shielding performance can be attributed to the synergistic mutual effect among MXene, PVA, water, and the biomimetic porous construction.The MXene nanosheets provided ample mobile charge carriers, which increased the conductivity of the hydrogel, leading to significant reflection losses of incident EMWs.The porous construction extended the propagation path of the EMWs, thereby ensuring extensive interactions between them and the cell walls to realize efficient EMWs depletion.Finally, the polarization relaxation of water molecules under an electromagnetic field and changes in the hydrogen bond network consumed EMWs energy.In addition, a strong dipole formed at the interface between PVA and the surface functional groups of the MXene nanosheets.
Bai et al. prepared a cellulose/MXene hydrogel that exhibited great electrical conductivity and good mechanical nature by adding MXene to a preprepared cellulose solution.First, a cellulose solution (4 wt%) was prepared by dissolving cellulose powder in an alkali (NaOH)/urea (7 wt%:12 wt%) aqueous solution, followed by freezing [61].The great electrical electroconductibility and uniform dispersion of MXene, in the cellulose hydrogel matrix, as well as the polarization loss of water resulted in efficient EMI shielding.Meanwhile, the internal 3D porous structure provided channels for the incident wave, which further increased internal multiplereflection attenuation and improved the shielding performance.Ultimately, the cellulose/MXene hydrogel displayed a remarkable EMI shielding performance with a EMI SE of 30 dB at 8.2 GHz (Fig. 6h-j).In addition to their excellent EMI shielding capacities, the hydrogels also exhibited impressive mechanical properties owing to the cellulosederived 3D support framework.The rich surface functional groups of the MXene nanosheets effectively cross-link the hydroxyl groups of cellulose, delivering a cellulose/MXene hydrogel with a tensile strain of 144.4%, compressive strain of 68.7%, and Young's modulus of 9.46 kPa.
Although MXene-based hydrogel EMI shielding materials have progressed considerably, studies on the influence of pore structure regulation and the effects of individual pore components on the shielding performance are seldom reported.Thus, elucidating these mechanisms can inspire future developments in excellent hydrogel-based EMI shielding systems.

Laminate and Composite-Structured MXene Films
MXene laminate films comprising three distinct forms have been reported [62][63][64][65].First, the MXene nanosheets are separately produced from their MAX phases with a chemical etching technique [42].Subsequent vacuum-assisted filtering of the aqueous MXene dispersions creates uniformly aligned MXene laminate sheets with the thicknesses of several microns.
The hydrophilicity of MXenes allows for the development of a biocompatible laminar MXene-SA composite film (Fig. 7a).A SEM figure of an MXene flake was displayed in Fig. 7b; the MXene flakes were almost transparent to the electron beam.The cross-sectional SEM image of the 50 wt% MXene-SA film was shown in Fig. 7c; nacre-like layered MXene stacking, resembling that of pristine MXene films, was observed for all composite ratios.Cross-sectional transmission electron microscopy figures of the MXene-SA composite films confirmed the intercalation of SA layers among the MXene flakes.In addition, at greater MXene contents, the MXene flakes were predominantly stacked, and only a few were observed to be separated from SA (Fig. 7d).MXene exhibited an extraordinary EMI shielding efficacy because of its exceptional electrical electroconductibility of ≈ 5000 S cm −1 , which was considerably higher than those of Mo 2 TiC 2 T x and Mo 2 Ti 2 C 3 T x (Fig. 7e).This research proved that electrical electroconductibility is a significant element in shielding (Fig. 7f).MXene demonstrated a great EMI 1 3 SE of 48-92 dB (8.2-12.4GHz), despite an increase in the mean thickness from 1.5 to 45 μm (Fig. 7g).Overall, MXene was shown to be an exceptionally suited material for EMI shielding usage.The MXene-SA composite films exhibited great EMI SE because of the great electrical conductivity induced by MXene and the laminate architecture constructed by the standardization of 2D MXene flakes.The portion of EMWs that entered the MXene-layered structure were attenuated in the form of eddy currents, ohmic losses, etc., which is due to the extensive contact between incident waves and high-electron-density MXene layers (Fig. 7j).A previous study corroborated the excellent EMI shielding properties of MXenes by presenting theoretical calculations based on the Fresnel formula and the attenuation rule.Thus, the tremendous potential of MXene as an EMI shielding material was demonstrated by the agreement between the theoretical calculations and experimental results (Fig. 7f-i).
Except reflection and absorption losses, various EMWs reflections also make contributions to the EMI shielding effect.To elucidate the roles of various reflections in the shielding capability of nanometer-thick MXene laminate sheets, Yun et al. prepared a big-area monolayer MXene film via interfacial self-assembly [44]; meanwhile, a multilayered film was created via the successive stacking of monolayer films.The monolayer MXene film demonstrated a EMW transmittance of over 90%, and exceptional flexibility.The absorbance grew, and the sheet resistance declined as the number of MXene layers grew; however, the EMI shielding effect steadily grew.Specifically, the monolayer MXene film (2.3 nm) had an EMI SE of 1 dB.The annealed sheet had SSE/t of 3.89 × 10 6 dB cm 2 g −1 maximumly.A detailed study of the shielding process was performed applying two distinct models.Simon's formula only occupies reflection and absorption, whereas the transfer matrix technique takes into account all possible shielding processes, such as SE M , SE R , and SE A .According to Simon's formula, μm-thick MXene films demonstrated a linear growth in SE T if the film thickness was greater than 1.5 μm.Nevertheless, when the film thickness was smaller than the skin depth (7.86 μm for MXene), Simon's theory failed to predict the acquired data, demonstrating the significant impact of repeated EMWs reflection in thinner films.The non-reflected waves undergo reflection and attenuation repeatedly inside the shielding material until they are either transmitted or completely attenuated, resulting in reduced SE T , higher SE A , and lower SE R contributions.Vacuum filtering techniques or interfacial assembly of 2D MXene flakes can be applied to generate tailored architectures inside the MXene laminates, resulting in enhanced attenuation of incoming EMWs within the structure.Electrically conductive MXene laminate nanofilms operate via the same absorption-dominating shielding mechanism as electrically conductive films with micrometer-scale thicknesses (SE A > SE R ).The repeated EMWs reflections induced by electrically conductive films and the efficient shielding performance at nanoscale thickness offer promise for shielding undesirable EMWs in sophisticated, highly integrated, and lightweight intelligent electronic systems.
Depending on different etching process, MXene nanosheet layers with dissimilar thicknesses can be obtained, which may also influence the EMI shielding performance.Figure 8 shows a comparison of two distinct preparation methods [66].Both protocols took part in the etching of Ti 3 AlC 2 MAX powder, the first one adopted 40% hydrofluoric acid to produce an accordion-like multilayered (M-MXene) morphology, and the second one adopted LiF and HCl for 16 h at 40 °C to produce delaminated ultrathin MXene sheets (U-MXene).The M-MXene composite contained more F terminations, whereas the U-MXene composite had more = O terminations.Both MXenes were cold pressed at 5 MPa after being combined with SiO 2 nanoparticles as an EMWs-transparent matrix at various mass proportions (20, 40, 60, and 80 wt%).As shown in Fig. 8g, the corresponding conductivities (σ) of the 60 wt% M-Ti 3 C 2 T x and U-Ti 3 C 2 T x composites were 6.3 × 10 −3 S m −1 and 0.42 S m −1 , respectively.In the 8.2-12.4GHz frequency scope, the 1 mm-thick 80 wt% U-MXene composite attained an EMI SE of 58 dB (Fig. 8h, i).With their better electrical conductivity, bigger surface area, and more extensive conductive network, the U-MXene composites outperformed M-MXene in terms of EMI shielding.Additionally, the exposed surface areas of the U-MXene composites exhibited copious surface terminations and point deficiencies.and EMI SE of composite films.Under strain, nanofibers and nanowires may operate, while polymers induce the formation of brick-and-mortar structures to provide flexible, robust, and mechanically strong structures.Moreover, the addition of polymeric chains can also enhance the oxidation resistance of composites, making MXene-polymer composites a promising choice.Cao et al. fabricated MXene-cellulose nanofiber composites with nacre-like structures and tested them using a simple vacuum-assisted filtering process [67].The dispersion of the 1D nanofibers led to fewer insulated connections between the 2D MXene nanosheets.At 12.4 GHz, a nanocomposite containing 80 wt% MXene displayed an electrical electroconductibility of 1.155 S cm −1 and an EMI SE of 25.8 dB.The robust nanofibers enhanced the mechanical nature of the composite films, which were superior to those of pure MXene and CNF paper.At a MXene content of 50%, the ultimate tensile strength was 135.4 MPa and fracture appeared at 16.7% strain.The mother-of-pearl construction of the composite film originated from great hydrogen bonding among the hydroxyl groups on the CNF and MXene surfaces, which also contributed to its excellent strength.Hydrogen bonding enables the composite to withstand higher stresses as it maintains a well-stacked and compact morphology.Therefore, MXene composites are promising candidates for use in foldable and wearable electronics.Xie et al. capitalized on the favorable mechanical properties of polymers to develop an ultrathin MXene-aramid nanofiber (ANF) composite for EMI shielding [68].The final tensile strength and fracture strain of the ANF paper increased to 197 MPa and 9.8%, at low MXene concentrations of < 10 wt%.The electrical electroconductibility and EMI SE MXene composite film were 170 S cm −1 and 33 dB.He et al. researched the EMI shielding efficiency of Ti 3 C 2 T x /hydroxyethyl cellulose nanocomposites [69], in which the confined organic HEC chains increased the mechanical strength of the composite by generating hydrogen bonds with the hydroxyl termini of MXene.In the observed X-band frequency scope, MXene/ HEC composite of 100 μm thickness revealed an EMI SE of 24 dB.Wang et al. adopted a solution casting process to build low-temperature annealed MXene/epoxy composites [70].At 2 mm thickness, the electrical electroconductibility of the insulating epoxy was increased to 0.38 S cm −1 by unannealed MXene, and 1.05 S cm −1 by MXene, which resulted in EMI SEs of 30 and 41 dB, respectively.
The introduction of insulating polymers may affect the total electrical conductivity of the material and diminish the EMI shielding ability; therefore, conductive polymers have attracted increasing attention.The use of conductive polymers preserves electrical conductivity.Conductive chains among MXene layers provides a conductive route for electron transport.Liu et al. prepared vacuum-screened MXene and PEDOT [71].The mother-of-pearl-type composite exhibited high electrical conductivity owing to its brickand-mortar construction, where 2D MXene sheets could be taken as bricks and the conductive organic polymer chains as mortar.The conductivity of the composite with an MXene/ PEDOT: PSS proportion of 7:1 (340.5 S cm −1 ) was lower than that of pure MXene, while the EMI SE values for both materials were 42 dB, and the composite was 1.94 g cm −3  dense.The composite construction preserved the electrical properties of MXene, allowing for the attenuation of EMWs by different polarization processes, which showed relatively poor conductivity.Similarly, Zhang et al. examined the EMI shielding nature of ultrathin MXene/polyaniline (MXene/ PANI) composites [72].Sufficient electrical electroconductibility was realized because of the conductive polymeric chains among the MXene layers.Consequently, an EMI SE of 36 dB was obtained at 40 μm thickness.
Wang et al. prepared core-shell Fe 3 O 4 @PANI composites, and then flexible lightweight Ti 3 C 2 T x /Fe 3 O 4 @PANI composite membranes with intercalated intercalation construction by vacuum-helped filtration applying Ti 3 C 2 T x MXene as the matrix material [131].When the Ti 3 C 2 T x nanosheets have a 12:5 weight-to-Fe 3 O 4 @PANI ratio, EMI shielding efficiency of 58.8 dB maximumly can be achieved with a thickness of only 12.1 μm, which is greater than the SE of MXene/PANI films of the same thickness.After modifying the film thickness by growing the concentration of Ti 3 C 2 T x , a SE of 62 dB can be realized at a thickness of 16.7 μm.Magnetic Fe 3 O 4 particles bring about the favorable magnetic loss, thus the electromagnetic wave absorption effect of the composite is enhanced through natural resonance and exchange resonance.Meanwhile, the multiple reflection and attenuation of internal electromagnetic waves are also increased through structural design.Therefore, the addition of semiconductor metal oxides and the design of the structure exert an important influence on improving the electromagnetic shielding effect of the material.

3
MXene hybrid films can be formed to improve the EMI shielding efficiency [91,92].Li et al. manufactured lightweight, thin, large-area, and ultra-flexible bicontinuous chemically cross-linked MXene/superaligned carbon nanotube composite sheets (Fig. 9a-c) [93].The films exhibited great mechanical strength, strong electrical electroconductibility (Fig. 9f), hydrophobicity, oxidation steadiness (Fig. 9i), wearable multifunctionality, EMI shielding (Fig. 9f-h), electrothermal conversion (Fig. 9d), and photothermal antibacterial properties (Fig. 9e).The X-band EMI SE ranged from 24 to 70 dB as the thickness increased from 8 to 28 μm in the ultrabroadband frequency scope of 8.2-40 GHz.An SSE/t of 122,368 dB cm 2 g −1 was obtained, greatly exceeding those of other reported shields.The excellent electro/photothermal effect of the films resulted in effective de-icing and antibacterial characteristics.Integrated with an economical and scalable production process, the multifunctional wearable bicontinuous films display enormous promise for usage in wearable equipment, defense systems, antibacterial devices, and the Internet of Things.
Cao et al. created a CNT/MXene/CNF composite film [94].They examined the synergistic role of conductive CNTs and CNFs in the EMI shielding and mechanical characteristics of the composite films.The resulting composite film exhibited remarkable mechanical characteristics.Because of the synergistic role of conductive CNT-MXene and nonconductive CNFs, the CNT/MXene/CNF hybrid film displayed a great electrical electroconductibility.
Xin et al. developed a MXene/CNF/Ag composite material for EMI shielding usage [95].A vacuum filtration process was used to create the MXene/CNF/Ag composite film, in which MXene yielded silver nanoparticles.The composite material displayed a high electrical electroconductibility of 588.2 S m −1 and an excellent EMI SE of approximately 50.7 dB, which was considerably greater than that of a MXene/CNF layer of similar thickness.
Wang et al. developed a PVDF/MXene/Ni composite film and studied the synergistic impact of MXene and Ni chains on the EMI SE [96].A PVDF/MXene/Ni composite film of 0.3 mm thick displayed an electrical electroconductibility of 892 S m −1 and an EMI SE of 34.4 dB, both of which were higher than those of pure MXene or pure Ni chains with the same loading.The mechanical properties were also examined.The Young's modulus, tensile strength, and toughness of the PVDF/MXene/Ni chain composite films were approximately 1.18 GPa, 41.9 MPa, and 2.9 MJ m −3 .
Xiang et al. [97] generated a TiO 2 -MXene/graphene film for EMI shielding via vacuum screening and pyrolysis.First, the fabrication of MXene/graphene film was made via vacuum filtration, followed by heat treatment for the partial transformation of MXene to TiO 2 to generate a TiO 2 -MXene/graphene film.The composite material showed a low surface resistance of 7.5 V (sq) −1 and an outstanding EMI SE of > 27 dB.Furthermore, while taking into account the density and thickness of the shielding film, the TiO 2 -MXene/graphene film exhibited an astounding shielding effect 1 .
Liu et al. manufactured GO-enhanced MXene films with outstanding electrical conductivities and mechanical strength using vacuum-helped filtering [98].The acquired MXene/GO film exhibited an exceptional tensile strength of 209 MPa, which is approximately nine-fold greater than that of the pure MXene film.In the meantime, the composite film exhibited an electrical electroconductibility of 2.64 × 10 5 S m −1 , which was comparable to that of the MXene film.The superior electrical electroconductibility of the MXene/GO film resulted in an exceptional EMI SE of 50.5 dB at a film thickness of 7 mm.Besides, the comparison of MXene-GO films were made with analogous shielding films described in the literatures with respect to SE vs. strength.
Miao et al. fabricated an AgNW/nanocellulose/MXene composite film using a pressure extrusion film-forming method [99].In this technique, NC was first disseminated across 2D MXene nanosheets through hydrogen bonding.Subsequently, the intercalation of the AgNWs formed a greatly interpenetrating 1D/2D comprehensive conductive network.The composite film demonstrated a phenomenal electroconductibility of 30,000 S m −1 and an exceptional EMI SE of 16,724 dB.The tensile stress of the AgNW/NC/ MXene composite film was 63.80 MPa, which was approximately 49.5-fold higher than that of the pure MXene film.Besides, after 10,000 bending cycles at 135 °C, the electroconductibility and EMI SE of the composite film remained stable.

Layer-by-Layer (LBL)-Structured MXene Film
The term "LBL-constructed film" means a film comprising alternating nanometer-thick monolayers of oppositely varied substances assembled via successive absorption.LBL films constructed using two phases with differing impedances may trigger significant internal scattering at the internal interfaces.Spin coating [73], spray coating [74], dip coating [75], solution casting [76], and interfacial assembly are common solution processing methods used to build LBL structures [77].The hydrophilic surfaces of exfoliated MXene sheets allow for the preparation of steady dispersions in aqueous and organic solvents, allowing solution treatment of a variety of nanostructures and polymers [78].Mechanical strength can also be increased by employing an LBL structure.
For instance, Li et al. produced big, high-strength, ultraflexible hybrid films using graphene oxide to promote the physical and chemical cross-linking of MXene sheets and cellulose (Fig. 10a) [79].The hydrophobicity, water/solvent resistance, and oxidative steadiness of MXene-based films were significantly enhanced (Fig. 10c, h).Favorable conductivities (Fig. 10d) and EMI shielding performances were achieved (Fig. 10e-g).An X-band SSE/t of 18,837.5 dB cm 2 g −1 and an EMI SE exceeding 60 dB were attained, which is equivalent to the best performances reported to date (Fig. 10h).Additionally, the photothermal, antibacterial, and electrothermal de-icing capabilities of the composite films were shown.Consequently, such effective MXenebased films prepared by simple and scalable manufacturing approaches offer significant application possibilities.
In addition to graphene, highly conductive carbon nanotubes (NTs) can also be applied for constructing LBLstructured composite films with excellent EMI shielding capabilities.Weng et al. developed a cross-functional semi-transparent Ti 3 C 2 T x -carbon nanotube (MXene/ CNT) composite film with an LBL structure using the spin-spray approach and investigated its EMI shielding ability [80].The developed MXene/CNT composite film showed a high degree of transparency and is applicable in various industries.The electrical electroconductibility of the 300-bilayer composite film was 130 S cm −1 and the SSE/t was 58,187 dB cm 2 g −1 .These were among the greatest values observed in flexible and semi-transparent composite thin films.Surprisingly, EMWs absorption was the primary shielding system of the as-prepared MXene/ CNT composite films.The excellent shielding properties were largely derived from the LBL structure of the film.
The mismatched impedance of the multilayered stacked LBL architecture with alternating conducting and nonconducting layers improved the internal scattering and absorption of EMWs.Jin et al. created a PVA/MXene composite film using a simple liquid casting process and LBL assembly of Ti 3 C 2 T x MXene and polyvinyl alcohol (PVA) [81].The initial layer is constructed by the application of an aqueous PVA solution to a clean iron substrate, next to drying at 45 °C.Under the same conditions, MXene layers of differing concentrations were deposited on the PVA layer and cured.This procedure was repeated until the desired thickness was achieved, after which, a final PVA coating was deposited.Varying the number of stacking cycles yielded various Ti 3 C 2 T x MXene contents (7.5, 13.9, and 19.5 wt%).Owing to the combination of PVA and Ti 3 C 2 T x MXene, the multilayered compacted films with single-layer thicknesses of 1-3 μm demonstrated outstanding mechanical flexibility.The electrical electroconductibility of the composite films increased with increasing Ti 3 C 2 T x MXene concentration, reaching 7.16 S cm −1 .The EMI SE followed a similar trend, attaining 44.4 dB maximumly at the highest Ti 3 C 2 T x MXene content and a thickness of 25 μm.
CNFs are also suitable for LBL assembly because their functional groups can bond to MXene to form a stable connection.Zhou et al. adopted a simple and effective alternating vacuum filtration approach to manufacture MXene/CNF composite films with an LBL construction [82].Because of the mechanical frame role exerted by the CNF layers, this alternating multilayered film outperformed both freestanding MXene and homogeneous CNF/MXene films in terms of mechanical strength and toughness.Moreover, the LBL MXene/CNF films displayed great electrical conductivities of 82-621 S m −1 .Surprisingly, the in-plane electrical electroconductibility was almost nine orders of magnitude greater than that in the through-plane orientation.This anisotropic electrical electroconductibility implies promising potential for insulation-requiring EMI shielding applications.Most impressively, the LBL MXene/CNF film showed a remarkable EMI SE, as well as a high SSE/t of 7029 dB cm 2 g −1 at just 35 μm thickness.The LBL construction comprising conductive and non-conductive layers induced extensive "reflection-absorption zigzag" reflection, thereby considerably enhancing the EMI SE.
LBL structures with tailored chemical, mechanical, and electrical properties can be applied in a broad range of fields.Moreover, the shape of the conducting material is critical for lowering the skin effect [80,83] and enhancing EMWs interactions within the layers via internal scattering, thereby significantly affecting EMI shielding properties.The advantages of MXene-based LBL composites include their adaptable density, and favorable electrical characteristics as well as mechanical strength, allowing large-scale regulation of EMI SE. allowing for EMI SE.

Fabric-Structured MXene Films
Flexible fabrics with conductive and EMI-shielding properties have drawn increasing interest in wearable and portable electronics.Except providing electrical electroconductibility, thermal electroconductibility, and EMI shielding nature, the integration of conductive fillers and fabric retains the stretchability, flexibility, and breathability of the fabric.MXenes, which are highly conductive and contain abundant functional groups, are ideal conductive fillers for electrical fabrics [84][85][86][87].
Using commercial cellulose filter paper as the substrate, Hu et al. employed a simple dip-coating approach to generate greatly lectrically and thermally conductive, flexible, and robust MXene/cellulose films (Fig. 11a) [88].The linked MXenes provide strong electrical and thermal electroconductibility to the composite sheets.Because of the inherent metallic conductivity of Ti 3 C 2 T x nanosheets and their linked network, the resulting composite film showed an exceptional electrical electroconductibility of 2756 S m −1 (Fig. 11b).Furthermore, the EMI SEs of the MXene/cellulose films reached 43 dB in the X-and Ku-bands (Fig. 11d,  e).Notably, the composite material was mechanically stable.Moreover, the composite sheet showed an in-plane thermal electroconductibility of 3.89 W m −1 K −1 (Fig. 11c).
Several kinds of textile materials have been manufactured using solvent-based processes including dip, spray, vacuum filtering, and screen printing.Two-dimensional MXenes exhibit good physicochemical characteristics and are regarded as appropriate nanomaterials for the fabrication of multi-functional flexible textiles.The findings showed that the synthesized MXene composite textiles have good shielding characteristics.The textiles also showcase multiple functionalities, such as hydrophobicity, heat dissipation, and so on, significantly expanding the application range of MXene fabrics.
Liu et al. employed vacuum-assisted LBL spray coating to develop MXene and silver nanowire -doped silk textiles, which displayed excellent EMI shielding, superhydrophilicity, and a greatly sensitive humidity reaction [89].The leaflike construction of the composite film consisted of MXene and AgNWs.This multifunctional film had a low sheet resistance of 0.8 V (sq) −1 , an excellent EMI SE of 54 dB in the X-band, and a thickness of 120 μm, while maintaining acceptable porosity and penetrability.Similarly, Zhang et al. applied a simple spray-drying coating process to create MXene-decorated woven cotton textiles [87].By modifying the spray-drying cycle, the degree of conductive connections in the fabric could be accurately changed; thus, the conductivity and EMI SE were readily controllable.Owing to its interwoven conductive architecture, M-CF exhibited a decent resistance of 5 V (sq) −1 at a modest loading of 6 wt%.Furthermore, the obtained MXene-decorated textiles exhibited satisfactory EMI SEs of above 36 dB at a low MXene loading (6 wt%).In addition, M-CF exhibited an excellent Joule heating capacity and kept the natural air penetrability and elasticity of the fabric.
Ma et al. used a simple "dipping and drying" process to yield a MXene-decorated air-laid paper with a superb folding endurance and EMI shielding effect [90].In the "dipping and drying" process, the air-laid papers are coated by MXene as a result of van der Waals forces and hydrogen bonding between the MXene nanosheets and cellulose.The MXene-decorated paper showed a great electrical electroconductibility of 173.0 S m −1 , excellent EMI shielding efficiency, substantial mechanical flexibility (it could be folded 9.8 × 10 4 times), and breathability.

MXene-Based Materials with a Segregated Structure
For conductive polymer composites with a unified construction, a high filler content is often required because inefficient lapping of the conductive filler inhibits the formation of a conductive network.To construct a more complete conductive network with a low proportion of conductive filler, an internal conductive network has been designed as a segregated construction.The preparation of conductive composites with a segregated structure generally entails the attachment of conductive fillers to the surface of polymer particles (similar to a core-shell structure), and then combining the materials under pressure to form a material with a segregated structure.The selective distribution of conductive fillers is made between the microinterfaces of the polymers, increasing the probability of lapping between the conductive fillers.
Zhang et al. made a greatly conductive MXene@polystyrene (PS) nanocomposite material (Fig. 12) [100].Due to the great electroconductibility of MXene and the continuous and effective conductive network formed inside the PS matrix, the obtained nanomaterials showed a low permeability threshold of 0.26 vol% and great electroconductibility of 1081 S m −1 , and achieved an excellent EMI SE of > 54 dB over the entire X-band.At a low MXene loading of 1.90 vol%, the EMI shielding effect of a 2 mmthick nanocomposite was 62 dB.The elasticity modulus of the material was 54% and 56% greater than those of pure PS and traditional MXene@PAA nanocomposites.By adjusting the PS diameter, the conductivity of the MXene@ PS nanocomposite material could be controlled; under the same load, MXene nanosheets favored the assembly on the surface of large microspheres to form a more continuous network, which was also conducive to load transfer and improved conductivity and the elastic modulus.Eventually, the continuous 3D conductive network formed at the interface of the hexagonal PS substrate, facilitated the dissipation of EMWs.
Such a structural design can also reduce the density of the system and impart other favorable properties, such as heat insulation, sound absorption, and high elasticity, by prefabricating the matrix, using methods such as supercritical CO 2 foaming, or by introducing a cell structure after the isolation structure is completed.Therefore, shielding materials with segregated structures are widely used.However, the conductive filler content in the isolation structure should generally not exceed 10 wt%, otherwise the dispersion of the filler at the interface becomes difficult.

3 4 Overview and Perspectives
The emergence of MXenes in EMI shielding in 2016 has had a transformative effect on this field.Since then, a slew of reports on "2D MXene and EMI shields" have been published.Several structural forms have been examined in terms of various performance indicators including thickness, density, and EMI SE.This review presented notable research achievements in the development of EMI shielding macrostructures based on MXene and emphasized the relevant structure-property relationships.Table 1 sums up the EMI SEs of MXene-based shields with various structures and the corresponding composition, thickness, density, and SSE/t.The data indicate that the structures of the materials have a profound effect on various performance indicators.
(1) Porous foams and aerogels provide robust and ultralightweight characters as well satisfactory EMI shielding without sacrificing thickness, which is favorable for aerospace and military applications [2,9,105,121,129].To reaching efficient EMI shielding, a compromise between the density and thickness is unavoidable, although an appropriate combination of both may yield an outstanding SSE/t.
(2) Compact MXene laminates and related composites are suitable for ultrathin shielding materials that require superior mechanical qualities, such as in miniaturized electronics [9,103,114,[125][126][127][128].MXene laminates deliver excellent EMI SEs at minimal thicknesses and can be fabricated at the nanoscale to fulfill commercial product needs.(3) Segregated constructions with exceptionally low MXene loadings are economical.
Owing to its superior metallic conductivity, MXenes provide state-of-the-art EMI shielding performances, surpassing numerous other conducting materials and their composites at equivalent thicknesses.MXene systems face several  (3) Owing to the hydrophilic properties of MXenes, MXene/ polymer composites and hybrids with other nanomaterials can only be fabricated under aqueous conditions.To expand the structural design scope, MXenes shall be synthesized and investigated with hydrophobic surfaces and appropriate organic dispersants.
Moreover, MXenes have significant potential for further investigation into its structure, properties, and integration with other materials, aiming to enhance its EMI shielding capabilities and broaden its use in related fields.Additional investigation is required to optimize the inherent properties and explore possible applications in many domains.Finally, although the reported MXene-based macrostructures exhibit satisfactory EMI shielding performances, research on MXenes is still in its infancy.Thus, there is crucial range for the development of new MXenes and investigating their shielding capabilities.We believe that subsequent research can overcome the various difficulties to achieve all-encompassing performance improvements and hope that this comprehensive assessment will provide new insights and guidelines for academia to propel the growth of next-generation EMI shielding materials.

Fig. 3 a
Fig. 3 a Graphical illustration showing the generation of MXene foams; digital figures of the MXene, b film, and c foam.Cross-sectional scanning electron microscopy images of the MXene d film and e foam.Contact angle measurements of the MXene f film and g foam.EMI SEs of MXene h films and i foams of different thicknesses.Contrast of the mean SE T , SE R , and SE A of the MXene j films and k foams of varying thicknesses over the X-band.l Thicknesses, densities, and electrical conductivities of the MXene foams using varying doses of hydrazine.m Roles of the expansion proportion in the EMI SEs of the MXene foams.Reproduced with consent from Ref. [56].Copyright 2017, WILEY-VCH

Fig. 4 a
Fig. 4 a Graphical description depicting the generation of MXene/SA hybrid aerogels and PDMS-coated MS foam.SEM figures of MS74 (mass proportion of MXene was 74%), b aerogel side figure and c top figure.d EMI SEs of the MS aerogels, and e plots of EMI SEs of the MS aerogels vs. the MXene content.Reproduced with consent from Ref. [57].Copyright 2020, Elsevier

Fig. 5 a
Fig. 5 a Schematically describing the generation of MXene/RGO hybrid aerogels.b SEM figure of GA (graphene aerogel).c Side figure SEM image of MGA-4 (MGA-4 contains 80 wt% Ti 3 C 2 T x ).d Digital figures of MGA-4 (100 mg) resting on a flower (left) and supporting a weight of 500 g (right).d MXene aerogel (35 cm 3 g −1 ) resting on foxtail grass.e Conductivities of the MXene/RGO hybrid aerogels.f EMI SE of EP/ MGA nanocomposites.g Role of sample thickness in the EMI SE of EP/MGA-4 nanocomposite (0.74 vol%).Total, reflection, and absorption EMI SEs of MXene aerogels with varying densities h 6.26 mg cm −3 , i 12.5 mg cm −3 , j 20.7 mg cm −3 .a-c and e-g Reproduced with consent from Ref. [58].Copyright 2018, American Chemical Society.d and h-j Reproduced with consent from Ref. [59].Copyright 2019, Royal Society of Chemistry

Fig. 6 aFig. 7 a 3
Fig. 6 a Graphical description displaying the generation of MXene/ PVA hydrogels.b X-band EMI SE and c SE R , SE A , and SE T .d Power parameters of hydrogels with different MXene contents.e EMI SE and f SE R , SE A , and SE T for varying solid contents of 0.86 vol% MXene/PVA hydrogels.g Role of sample thickness in the EMI SEs of 0.86 vol% MXene/PVA hydrogels.h EMI SEs of C/M hydrogels with varying MXene loading in the frequency scope of 8.2-12.4GHz, i SE T , SE A , and SE R of hydrogels with varying MXene loading at 8.2 GHz.j EMI SEs of hydrogels with varying thicknesses.a-g Reproduced with consent from Ref. [60].Copyright 2022, American Chemical Society.h-j Reproduced with consent from Ref. [61].Copyright 2022, Taylor & Francis Group ◂

Fig. 8 a
Fig. 8 a M-Ti 3 C 2 T x and b U-Ti 3 C 2 T x microstructures.c M-Ti 3 C 2 T x and d U-Ti 3 C 2 T x local conductive networks.Microwave publicity model in e M-Ti 3 C 2 T x and f U-Ti 3 C 2 T x composites.g DC electroconductibility (σ) vs. mass proportion of M-Ti 3 C 2 T x /SiO 2 and U-Ti 3 C 2 T x /SiO 2 composites; inset displays log 10 DC electroconductibility (σ) vs. mass proportion.Local conductive network and shielding effect regulation of h M-Ti 3 C 2 T x and i U-Ti 3 C 2 T x .Reproduced with consent from Ref. [66].Copyright 2019, Royal Society of Chemistry

Fig. 9 a
Fig. 9 a Schematic showing the generation of C-MXene/SA-CNT films.b Figure of big freestanding C-MXene/SA-CNT films.c Figure of a 200 g weight suspended from a 15-mg C-MXene/SA-CNT film (inset displays an origami plane).d Electrothermal and e photothermal nature of C-MXene/SA-CNT films.EMI shielding effect of the C-MXene/SA-CNT films.f EMI SE and electrical electroconductibility of SA-CNT films of different thicknesses in perpendicularly and parallelly.EMI SE in the X-band of C-MXene/SA-CNT films with different MXene contents g perpendicularly and h parallelly.i X-band EMI SEs of the films after 7-day soaking in different solvents or after 5000-cycle bending at a bending speed of 0.5 Hz and rolling.Reproduced with consent from Ref. [93].Copyright 2020, American Chemical Society

Fig. 10 a
Fig. 10 a Schematically showing the producing process of C-CMG films.b Cross-sectional SEM figure of the C-CMG film.c Figure of a C-CMG film showing ultra-flexibility.d Electrical conductivities of C-CMG films with varying MXene contents.EMI shielding performances of the C-CMG films.EMI SEs in the X-band of e cellulose, CM, CMG, C-CMG, and cellulose@GO films and f C-CMG films with MXene contents.g EMI shielding performances (SE T , SE A , and SE R ) at 10 GHz and SSEs of the C-CMG films with varying MXene contents.h EMI SE values of the 30 μm-thick C-CMG films.i X-band EMI SE of the films after 7-day soaking in various solvents.Reproduced with consent from Ref. [79].Copyright 2022, Wiley-VCH

Fig. 11 a
Fig. 11 a Schematic description of the production process of freestanding nanocomposites.b Electrical electroconductibility of M-filter.c Thermal electroconductibility of M-filter.d EMI SE of the filter paper and PDMS-coated M-filter.e Contrast of SE T , SE R, and SE A of PDMS-coated M-filters with varying dip-coating cycles at 12.4 GHz.f EMI SE of PM-7 after 2000 bending-releasing cycles and EMI SE retention.Reproduced with consent from Ref. [88].Copyright 2020, Elsevier

Fig. 12 a
Fig. 12 a Schematically describing the generation of Ti 3 C 2 T x @PS nanocomposites.b, c SEM figures of cross section of Ti 3 C 2 T x @PS-570 hybrid made at ambient temperature.d, e TEM figures of Ti 3 C 2 T x @PS-570 nanocomposites with 1.90 vol% of Ti 3 C 2 T x ; dark gray lines and white arrows mean electrical conduction paths.f Electrical conductivity, g EMI SE and h SE T , SE A , and SE R of Ti 3 C 2 T x @PS-570 nanocomposites.Reproduced with consent from Ref. [100].Copyright 2017, WILEY-VCH

Table 1
EMI shielding performances of different structural forms on basis of MXene obstacles that must be addressed in the future: (1) although synthesis techniques for more than 30 distinct MXenes have been described, only a few, including Ti 3 C 2 , Ti 2 C, Mo 2 TiC 2 , Mo 2 TiC 3 , and Ti 3 CN, have been studied.To elucidate the roles of basic composition, layer construction, and transition metal arrangement in the EMI shielding nature of MXenes, it is necessary to investigate other MXenes.It is also necessary to explore an efficient, green and scalable MXene preparation method for industrialization.(2) Typically, highly conductive MXenes contribute substantially to EMI shielding, which may result in secondary pollution.Porous foams, aerogels, and segregated constructions have been proposed to address these issues.Nevertheless, the generation of MXene-based shielding materials with varied structural factors, such as metastructures, remains necessary to significantly increase the absorption of incoming EMWs.