Synergistic “Anchor-Capture” Enabled by Amino and Carboxyl for Constructing Robust Interface of Zn Anode

Highlights The synergistic “anchor-capture” mechanism of polar groups on Zn stripping/plating process is firstly proposed. The amino group firmly anchors on Zn surface and the carboxyl group strongly captures Zn2+, constructing a robust anode–electrolyte interface and inducing uniform Zn deposition. The ultra-stable cycle lifespan of Zn–Zn symmetric cell (over 2800 h) and high utilization rate of Zn anode (the depth of discharge up to 68% for 200 h) are achieved under the proposal of synergistic “anchor-capture.” Supplementary Information The online version contains supplementary material available at 10.1007/s40820-023-01171-w.

ABSTRACT While the rechargeable aqueous zinc-ion batteries (AZIBs) have been recognized as one of the most viable batteries for scale-up application, the instability on Zn anode-electrolyte interface bottleneck the further development dramatically.Herein, we utilize the amino acid glycine (Gly) as an electrolyte additive to stabilize the Zn anode-electrolyte interface.The unique interfacial chemistry is facilitated by the synergistic "anchor-capture" effect of polar groups in Gly molecule, manifested by simultaneously coupling the amino to anchor on the surface of Zn anode and the carboxyl to capture Zn 2+ in the local region.As such, this robust anode-electrolyte interface inhibits the disordered migration of Zn 2+ , and effectively suppresses both side reactions and dendrite growth.The reversibility of Zn anode achieves Zhen Luo and Yufan Xia contributed equally to this work.
The stability of Zn anode is largely determined by the diffusion and migration behavior of Zn 2+ at the interface [14,15].In general, Zn 2+ near the anode surface follows 2D diffusion mechanism, which aggregates at prior nucleation sites to capture electrons and then be reduced to form initial protrusion [16].To minimize the surface energy, such reduction of Zn 2+ tends to trigger the protrusion vertical growth and the formation of dendrites, leading to an increased surface area of Zn exposing to water molecules to accelerate the hydrogen evolution reaction (HER) [17].The OH − generated by hydrogen evolution elevates the local pH value near the anode and react with ZnSO 4 electrolyte to further deteriorate the interface by generating the inactive by-product of Zn 4 SO 4 (OH) 6 •xH 2 O (ZSH) on the anode [18], which exacerbates the dendrite growth and side reactions.
Up till now, many progress has been achieved in surface modification [19][20][21][22], structural design [23,24], and electrolyte modification [25][26][27][28] to address the above issues.Among them, electrolyte modification is one of the most effective strategies with wide applications.Natural biomolecules, such as amino acids and their derivatives, are attracting great attention for modifying the electrolytes.For instance, it was found that silk fibroin (SF) with mainly β-sheet conformation into ZnSO 4 electrolyte can adhere to the surface of Zn anode and regulate the uniform Zn deposition [27,29], while the one with the secondary structure transformation from α-helices to random coils in the aqueous electrolytes is inclined to participate in Zn 2+ solvation structure due to more exposed polar groups [30].Moreover, Xu et al. [31] proposed a lysozyme membrane constituted by β-configuration dominant amyloid aggregates to facilitate uniform Li + flux in lithium metal batteries.As for amino acids, positively charged ones such as arginine are confirmed to electrostatically adsorb on Zn anode surface and regulate the interface charge states [32].Cysteine, which possesses more complex configuration, contributing to the reconstruction of solvation structure and anode-electrolyte interface [33].These additives are rich in various polar groups such as amino (−NH 2 ), carboxyl (−COOH), sulfhydryl (−SH), etc.However, the efficacy of additives and the mechanism elucidation for specific polar group remain yet to be explored, which are especially critical for precisely designing functional additives applied into AZIBs.
Herein, the simplest amino acid, glycine (Gly), which consists of one amino and one carboxyl was selected as the electrolyte additive.The adsorption of amino promotes Gly with an anchoring effect on the surface of Zn metal, enabling a stable Zn anode-electrolyte interface and inhibiting the side reactions caused by water decomposition.In addition, Zn 2+ is captured owing to the strong coordination with carboxyl, thus alleviating its disordered diffusion.Under this synergistic "anchor-capture" effect, side reactions and dendrite growth at the Zn anode-electrolyte interface are significantly suppressed, realizing a long-lifespan and stable Zn anode with excellent rate performance and long-term cycling stability.

Material Characterizations
The surface morphology and phase structures were assessed by the scanning electron microscopy (SEM, Hitachi S-4800) and X-ray diffraction analyzer (XRD, Bruker D8 diffractometer, Co-Kα, λ = 1.789Å).Fourier transform infrared spectroscopy (FTIR) was carried out on Thermo Scientific Nicolet iS20.X-ray photoelectron spectroscopy (XPS) was performed by Thermo Scientific K-Alpha equipped with Al Kα X-ray source (12 kV, 6 mA).The O-H stretching of different electrolytes was collected by Raman spectroscopy (Raman, HORIBA Scientific LabRAM HR Evolution, 532 nm laser).The solvation structure of Zn 2+ was confirmed by nuclear magnetic resonance spectrometer ( 2 H NMR, Bruker 400 MHz), the solvent was D 2 O.

Electrochemical Measurements
The Zn-Zn symmetric cells, Zn-Ti half cells and Zn-MnO 2 full cells were assembled in atmosphere using CR2025 coin-type cell, which were tested by the Neware BTS-5 test system.Electrodes were cut into disks with a diameter of 16 mm with glass fiber filters (Whatman) used as separators.The cathode electrode was prepared by mixing MnO 2 , Ketjen black (KB) and polyvinylidene fluoride (PVDF) with a mass ratio of 7:2:1 in N-methyl-2-pyrrolidone (NMP) and casted onto Ti foils (10 μm).The electrode was dried at 120 °C for 12 h in vacuum.The mass loading of active material was around 2.5 mg.
The cyclic voltammetry (CV), linear sweep voltammetry (LSV), potentiodynamic scanning (Tafel), chronoamperometry (CA) measurements and electrochemical impedance spectroscopy (EIS) were carried out on the CHI760E electrochemical workstation.The average differential capacitance was derived from CV data with different scan rates (from 2 to 10 mV s −1 ) and a voltage range of − 15 to 15 mV.The hydrogen evolution performance was recorded by performing LSV test at 5 mV s −1 with Ti foil as the working electrode, Zn plate as the counter electrode and Ag/AgCl as the reference electrode, respectively.Tafel plots were performed at a scan rate of 0.01 V s −1 with Zn plate as the working electrode, Ti foil as the counter electrode and Ag/AgCl as the reference electrode.The CA curves were measured at a fixed overpotential of − 150 mV.The EIS measurement was finished with a frequency range of 0.01 ~ 1,000,000 Hz.The galvanostatic cycled Zn plates were obtained from twoelectrode systems using Zn plates (1 cm × 3 cm) as both working and counter electrodes soaked in 2 M ZnSO 4 and 2 M ZnSO 4 + 0.1 M Gly/Ac-Gly/Gly-NH 2 electrolytes.The soaking area of each electrode was 1 cm 2 .
The transfer number of Zn 2+ was calculated according to potentiostatic polarization method [34], which can be given by: where I SS and I 0 represent the steady-state current and initial current, R SS and R 0 are the charge transfer resistances of steady-state and initial state, and ΔV is the applied overpo- tential (5 mV).

Ab-initio Calculations
The surface adsorption calculation related to the interaction between Zn slab and molecules was performed by using the Vienna ab initio simulation package (VASP) [35,36] based on Density functional theory (DFT).The projector augmented-wave (PAW) method [37] was carried out to represent the interactions of electrons with ion cores.The generalized gradient approximation (GGA) parameterized by the Perdew-Burke-Ernzerhof (PBE) method [38] with D3 correction [39] that was used to describe the van der Waals corrections.The energy cutoff was set to be 420 eV.The Brillouin-zone integration was sampled with a Γ-centered k-point mesh of 2 × 2 × 1 for all adsorption calculations.The convergence criteria for forces and energy were set to 0.02 eV Å −1 and 10 -5 eV, respectively.On the Z direction, there is 15 Å vacuum to avoid the interaction between adjacent images for slab model.A 5 × 5 supercell with four-layer Zn (002) slab was used to represent the absorbed surface for molecules, and the bottom two layers were fixed to simulate the bulk property.Visualization of the crystal structures was performed using VESTA [40] and data post-processing were used by VASPKIT code [41].The adsorption energy between Zn slab and different molecules was defined as following equation: where E Zn−Slab+Molecules , E Zn−Slab and E Molecules represent the total energies of the Zn (002) Slab with adsorbed molecules, Zn (002) slab, and adsorbed molecules, respectively.

Molecular Dynamics (MD) Simulations
Classical MD simulations were carried out using GROMACS 2022.2 [42] to provide insights on the electrolytes designed in this work.The force field parameters of Zn 2+ ions and SPC/E [43] water model were obtained with Amber03 force field [44].The GAFF force field [45] parameters of glycine and sulfate ion were generated with Acpype program [46], and the corresponding atom charges were based on restrained electrostatic potential (RESP) charges generated by Multiwfn [47].Initially, 12 Gly, 40 Zn, 40 SO 4 and 671 H 2 O molecules were packed into a 30 × 30 × 30 Å 3 box using the packmol software [48].
For comparison, zinc sulfate solution was simulated by packing 40 Zn, 40 SO 4 and 703 H 2 O molecules in a 30 × 30 × 30 Å 3 box.All the systems were first submitted to energy minimization by using the steepest descent method.Then, they were heated from 10 to 298.15 K in 100 ps, followed by 200 ps equilibration under isothermal-isobaric ensemble (NPT) at 1 bar.For the production run, an additional 20 ns NPT simulation was performed.The integration time step was 1 fs.For NPT simulations, the temperature was controlled by coupling the system with a Nosé-Hoover thermostat [49] at a time constant of 2 ps, and the pressure was controlled using the Parrinello-Rahman pressure [50] coupled with a 5 ps time constant.Electrostatic interactions were treated using the Particle-Mesh-Ewald (PME) methods [51,52] with a 1.3 nm cutoff distance.VMD software [53] was used to visualize the systems and obtain the ion association state.

Quantum Chemistry (QC) Calculations
Quantum chemistry (QC) calculations were performed using the Gaussian 16 software [54] to calculate the structures and binding energies of Zn 2+ -Gly and Zn 2+ -H 2 O complexes.The structure optimization and frequency calculations were performed at B3LYP-D3(BJ)/def2-TZVP level [55,56].Then a single-point energy calculation of each optimized structure was performed at the same functional and basis set.The universal solvation model SMD [57] was used to simulate the aqueous environment.The binding energy (BE) is calculated as follows: where E AB , E A , and E B denote the total energies of the AB complexes, bare A, and bare B, respectively.E BSSE is the basis set superposition error (BSSE) correction energy [58], which is used to correct the energy of interaction in all the complexes.

"Anchor" Role of Amino Group for Anti-Corrosion
First of all, 2 M ZnSO 4 electrolytes with different concentrations of Gly (0.05/0.1/0.5 M) were used to assemble Zn-Zn symmetric cells.Under the galvanostatic condition of 1 mA cm −2 and 1 mAh cm −2 , the cell with 0.1 M Gly shows an ultra-stable cycling life over 1000 h (Fig. S1).Therefore, the concentration of 0.1 M was chosen for further study on Gly.To accurately compare the roles of different polar groups, N-acetylglycine (Ac-Gly) and glycinamide hydrochloride (Gly-NH 2 ) are selected as the other two additives, which are derived by the amidation of amino and carboxyl groups in Gly, respectively.The detailed molecular structures of Gly, Ac-Gly and Gly-NH 2 are shown in Fig. 1a.The amide group (-CO-NH-, highlighted by light gray translucent oval area) is usually less active [59], which has negligible effect on Zn anode during cycling.After adding 0.1 M Gly/Ac-Gly/Gly-NH 2 into 2 M ZnSO 4 solution, the pH values of electrolytes were first determined.As can be seen from Fig. S2, the pH value declines from 3.79 for bare ZnSO 4 to 2.94/1.37/2.52 for ZnSO 4 + Gly/Ac-Gly/Gly-NH 2 , © The authors respectively.To evade the effect of pH, dilute sulfuric acid (10 wt.%) was added to the ZnSO 4 and ZnSO 4 + Gly/Gly-NH 2 electrolytes to adjust the pH to 1.37.
Compared with the normal ZnSO 4 solution (pH = 3.79), after immersed in ZnSO 4 solution with lower pH for 7 days, the Zn plate presents the similar morphology with rough surface covered by a mass of irregular flake-like by-products (Fig. S3), which are confirmed by the X-ray diffraction (XRD) patterns as Zn 4 SO 4 (OH) 6 •xH 2 O (Fig. 1b), indicating that the decline in pH would not inhibit the formation of by-products.On the contrary, no undesired by-products and diffraction peaks appear for the Zn plate immersed in ZnSO 4 + Gly/Gly-NH 2 solutions (pH = 1.37), as well as the overall smooth surfaces display step-like or isolated Zn islands randomly distributed (highlighted by yellow solid line circles) morphology, respectively.Under the presence of Ac-Gly, large cavities (highlighted by yellow dash line circles) and a rugged morphology are discovered on the surface despite no by-products to be observed.Moreover, the pH values of these solutions following immersion with Zn plates were also determined.As shown in Fig. S4, the pH values of ZnSO 4 + Gly/Ac-Gly/Gly-NH 2 solutions vary smaller than that of ZnSO 4 solution, implying the better anti-corrosion property of these additives.Especially, the increase of pH for ZnSO 4 + Gly solution is only 0.65, further demonstrating that Gly molecules can effectively inhibit side reactions and stabilize the local pH.
To assess the corrosion behaviors of Zn anode, the Tafel plots of Zn-Zn symmetric cells using different electrolytes are recorded in Fig. 1c, with corresponding corrosion current density ( j cor )/corrosion potential ( V cor ) summarized in Table S1.The difference between each V cor is negligible.As expected, the Zn anode in ZnSO 4 + Gly electrolyte delivers the lowest j cor of 1.11 mA cm −2 , which indicates the prominent anti-corrosion.The decreases of j cor compared to bare ZnSO 4 electrolyte with the addition of Ac-Gly and Gly-NH 2 also demonstrate that they suppress the corrosion of Zn anode to some extent.Moreover, the HER performance is a critical indicator to evaluate the stability of Zn anode, which is reflected by the magnitude of cathodic current in linear sweep voltammetry (LSV) curves.To alleviate the electrochemical reduction of Zn 2+ on surface, the base electrolyte is changed from 2 M ZnSO 4 to 1 M Na 2 SO 4 solution.In Fig. 1d, the increased HER overpotential and decreased HER current further confirm the positive roles of Gly and Gly-NH 2 in blocking side reactions.However, only decreased HER current can be observed in Na 2 SO 4 + Ac-Gly electrolyte, which can be attributed to the de-solvation effect of carboxyl (as discussed in the following section).
In order to understand the anti-corrosion performance of Zn anode in different electrolytes, the differential capacitance tests were performed.The average differential capacitance ( C ) is closely relevant to the electric double-layer (EDL) structure near the electrode surface [60][61][62], which can be derived from the following equation: where i is the average current density and v is the corre- sponding scan rate of a cyclic voltammetry (CV) curve.
As shown in Figs.S5 and 1e, the C of Zn anode sig- nificantly decreases to 52 and 100 μF cm −2 with Gly and Gly-NH 2 additives, respectively.We conjecture that both Gly and Gly-NH 2 can participate into the EDL structure and interact with Zn anode surface.In contrast, after adding Ac-Gly, a prominent increase of C is observed from 195 to 275 μF cm −2 .This might be caused by the corrosion of Zn anode that leads to more exposure of surface area to electrolyte, as large cavities observed in SEM image in Fig. S3.To verify the hypothesis mentioned above, the Fourier transform infrared spectroscopy (FTIR) was performed.The soaked Zn plates from Gly/H 2 O and Gly-NH 2 /H 2 O solutions exhibit the similar spectra variation compared with bare Zn in the range of 600 ~ 1700 cm −1 , including the C=O stretching at 1597 cm −1 and O-H bending at 902 cm −1 , respectively (Figs. 1f, g).In addition, peaks at 3200 ~ 3500 cm −1 are observed which correspond to the -NH 2 stretching.
These results convincingly confirm that Gly and Gly-NH 2 can spontaneously adsorb on Zn surface in solution media.Nevertheless, for Zn plate soaked in Ac-Gly/H 2 O solution, weak signals of -NH 2 and C=O stretching are detected, indicating the poor adsorption of Ac-Gly (Fig. 1g).The energy-dispersive X-ray spectroscopy (EDS) mapping also verifies the uniform coverage of Gly on Zn surface (Fig. S6).Ab-initio calculations were also conducted to study the adsorption energies ( E ads ) of different molecules on the Zn (002) facet (Fig. 1h).Interestingly, the interaction between Zn surface and Gly molecule is much stronger than that of H 2 O molecule (− 0.241 eV), no matter the N-terminal from amino or the O-terminal in -C=O from carboxyl.Specifically, Gly molecule prefers to adsorb on Zn surface by amino since the E ads in N-terminal state is much larger than that in O-terminal state (− 0.736 vs. − 0.479 eV).The relatively larger E ads of Gly-NH 2 (− 0.942 eV) and smaller E ads of Ac- Gly (− 0.637 eV) on Zn surface also demonstrate the prior interplay between amino and Zn atoms.
To determine whether the amino is physically or chemically adsorbed on Zn surface, the charge density difference calculations and high-resolution X-ray photoelectron spectroscopy (XPS) spectra were carried out.In Fig. 1i, apparent overlapped electron cloud between Zn and N atoms is found, suggesting a stable affinity between Gly and Zn.Meanwhile, the characteristic peak of N-Zn is distinctly observed at 398.9 eV in the N 1s spectrum (Fig. S7).These results confirm that Gly and Gly-NH 2 chemically anchor on the Zn surface via amino group, which plays a dominant role in inhibiting side reactions.

"Capture" Role of Carboxyl Group for Uniform Deposition
Apart from the inhibition of side reactions, the effect of Gly, Ac-Gly and Gly-NH 2 on Zn 2+ deposition behavior was also explored.As shown in Fig. 2a, compared with bare ZnSO 4 electrolyte, the nucleation overpotentials of Zn 2+ in ZnSO 4 + Gly and ZnSO 4 + Ac-Gly electrolytes significantly increase by 46 and 38 mV, respectively, much larger than that in Gly-NH 2 -containing electrolyte (29 mV).It is well known that a higher nucleation energy barrier for Zn 2+ is conducive to the formation of finer nuclei and uniform deposition [32,63,64].Subsequently, the chronoamperometry (CA) measurements were utilized to assess the evolution of deposition and growth of Zn nuclei under an overpotential of − 150 mV with Zn-Zn symmetric cells (Fig. 2b).The growth rates of current density caused by polarization during 50-200 s were calculated and shown in Table S2.In general, the rapid increase of current density with time in bare ZnSO 4 electrolyte reflects that the surface of Zn anode is dominated by 2D diffusion mode, in which Zn 2+ migrates along the Zn surface and the consequent "tip effect" leads to the continuous accumulation of Zn nuclei, which brings about the severe dendrite issues [16,65,66].
In contrast, the addition of Ac-Gly and Gly-NH 2 can reduce the current growth rate, which is caused by the restricted 2D diffusion of Zn 2+ .For Gly-containing electrolyte, the disordered Zn 2+ flux is regulated and Zn 2+ is directly reduced on the surface, yielding a stable 3D diffusion mode with the lowest current density response.The transfer number of Zn 2+ ( t Zn 2+ ) in different electrolytes was tested by potentiostatic polarization method.Figures S8a  and c show the electrochemical impedance spectroscopy (EIS) spectra of Zn-Zn symmetric cells in bare ZnSO 4 and ZnSO 4 + Gly electrolytes and the corresponding CA curves under the applied overpotential of 5 mV are displayed in Figs.S8b, d.As evidenced in Fig. S8e, the symmetric cell delivers a higher t Zn 2+ with Gly-containing electrolyte, fur- ther indicating the more homogeneous Zn 2+ flux and concentration gradient at the interface [67].
The above results have proved that the additives can regulate the kinetics of Zn 2+ .Here, the interactions among Zn 2+ , H 2 O and Gly molecules were further analyzed using quantum chemistry (QC) calculations.The calculated binding energies suggest that Zn 2+ appears to be more favored to combine with Gly than H 2 O (Fig. 2c).Besides, the electrostatic potential value for Gly molecule significantly increases when Zn 2+ approaches the carboxyl group (Figs.2d and S9), implying the transfer of electrons from nucleophilic site (carboxyl group) to Zn 2+ , which in favor of building firm bond among them in an implicit solution environment.Molecular dynamics (MD) simulations were carried out to investigate the solvation structure of Zn 2+ in ZnSO 4 + Gly electrolyte.In Fig. 2e, the double bonded oxygen atom from carboxyl in one Gly molecule obviously participates into the solvation sheath and replaces one of the H 2 O molecules around Zn 2+ , indicating an explicit change in solvation structure.
The corresponding radial distribution functions (RDFs) and coordination number analysis in different electrolytes were also performed.In bare ZnSO 4 electrolyte, a sharp peak of Zn 2+ -O at around 1.9 Å away from Zn 2+ is observed, which should refer to the participation of H 2 O into the solvation sheath, and the average coordination number is simulated to be 5.5 (Fig. S10).In ZnSO 4 + Gly electrolyte, it is clear to see that the peak of Zn 2+ -O (Gly) appears at a closer distance and displays much stronger intensity than that of Zn 2+ -N (Gly), and the average coordination number of Zn 2+ -O (H 2 O) is reduced to be 5.3, demonstrating that Gly molecule mainly coordinates with Zn 2+ via the carboxyl group rather than the amino group and can partially de-solvate Zn 2+ with a new solvation structure (Figs.2f, g  and S11).For further verifying the de-solvation effect of carboxyl group, the Raman spectra and nuclear magnetic resonance (NMR) spectra of different electrolytes were conducted.As shown in Fig. S12a, b, the O-H   wavenumber after adding Gly and Ac-Gly, demonstrating that both the molecules with carboxyl group have stronger interaction with water molecules and could break the original hydrogen bonding network, which weaken the activity of water [68].On the contrary, the Gly-NH 2 molecules without carboxyl group do not cause shift of the O-H stretching compared with bare ZnSO 4 (Fig. S12c).As for the NMR results in Fig. 2h, the 2 H peak of D 2 O shifts from 4.719 to 4.716 ppm in ZnSO 4 + Gly electrolyte, implying that more free water is released, which further proves that Gly can change the solvation structure of Zn 2+ [69].Furthermore, the mean-squared displacement (MSD) versus time was performed to characterize the diffusion rate of Zn 2+ in different electrolytes (Fig. S13).By adding Gly, the plot slope for MSD versus time increases, which can be inferred that Zn 2+ diffuses faster to Zn surface in ZnSO 4 + Gly electrolyte.

Synergistic "Anchor-Capture" Mechanism
Based on the above results, a synergistic "anchor-capture" effect (Fig. 2i) of amino and carboxyl groups in Gly molecule emerges as the mechanism of stabilizing Zn anode.In details, Zn 2+ would solvate with H 2 O to form {Zn(H 2 O) 6 } 2+ in bare ZnSO 4 electrolyte and migrate to the surface of Zn anode under the internal electric field.On the one hand, the H 2 O molecule would decompose and generate H 2 after contacts with Zn metal, thus elevating the pH value of local regions and further promoting the formation of by-products (ZSH).On the other hand, Zn 2+ randomly diffuses along the rough metal surface and aggregates at the prior nucleation sites to form small prominence.The consecutively deteriorated surface conditions significantly induce the growth of Zn dendrites, eventually leading to the failure of battery system by piercing the separator and causing short circuit.
On the contrary, the introduction of Gly molecule can firmly anchor on the Zn anode surface via the N atom of amino, which prevents the contact between H 2 O and Zn metal, thus protecting Zn anode from side reactions.Meanwhile, the Zn 2+ is captured by Gly due to the strong nucleophilicity of carboxyl, effectively confining the disordered 2D diffusion and guiding the uniform deposition.At the case of Gly-NH 2 and Ac-Gly, amino or carboxyl groups alone cannot effectively stabilize the interface, thus eventually Zn anode would deteriorate and come to failure.

Synergistic "Anchor-Capture" Enabled Electrochemical Performance
First, the long-term CE performances in different electrolytes are compared by assembling Zn-Ti asymmetric cells.
As shown in Figs.3a and b, the introduction of Gly achieves an ultra-stable operation over 500 cycles and delivers a high average CE of 99.22% at 1 mA cm −2 and 0.5 mAh cm −2 , which illustrate that the Zn anode can maintain high reversibility under the synergistic effect of amino and carboxyl groups.For the bare ZnSO 4 electrolyte, the Zn-Ti cell displays a notable fluctuating CE at about the 214th cycle, and the cut-off voltage of charging (1.0 V) cannot be reached, primarily due to the deteriorating dendrite growth and severe side reactions.However, Zn-Ti cells with Ac-Gly and Gly-NH 2 exhibit more chaotic fluctuation of CE, mainly ascribed to the uneven stripping and the concentrated plating beyond cavities or near dendrites.Even under a much faster kinetics at 10 mA cm −2 and higher deposition capacity of 1 mAh cm −2 , the Zn anode with Gly can still keep stable cycling with a high average CE of 99.15% for 580 cycles, which significantly surpasses that of Ac-Gly and Gly-NH 2 (Fig. S14).These results demonstrate the effectiveness of synergistic "anchor-capture" mechanism in homogenizing Zn deposition and promoting the reversibility of Zn anode.The Zn-Zn symmetric cells using ZnSO 4 + Gly electrolyte can also deliver much better cycling stability under galvanostatic condition.The voltage profiles in Fig. 3c depict that the Zn-Zn cell with Gly additive exhibits an ultra-long cycle lifespan over 2800 h without obvious overpotential fluctuation at a current density of 1 mA cm −2 .On the contrary, the cell cycled in ZnSO 4 electrolyte maintains stable for merely 90 h and fails with a sudden voltage drop, as a result of the short circuit due to the formation of disordered Zn dendrites which penetrate through the separator [70].The stability of Zn anode last only for 190 and 310 h with amino (Gly-NH 2 ) or carboxyl (Ac-Gly) groups alone, respectively.Moreover, as shown in EIS results of Fig. S15, the Zn-Zn cell with Gly-containing electrolyte displays a similar charge transfer resistance ( R ct ) compared with that in bare ZnSO 4 electrolyte before cycling, indicating that the adsorption of Gly has no negative impact on the charge transfer process near Zn anode surface.Nevertheless, the symmetric cell with Gly-containing electrolyte shows a lower R ct than that with ZnSO 4 electrolyte after 20 cycles, due to the robust https://doi.org/10.1007/s40820-023-01171-w© The authors anode-electrolyte interface constructed by the assistance of amino and carboxyl groups in Gly.
When the current density is increased to 5 mA cm −2 , the symmetric cell with Gly also achieves an operation time of up to 800 h under the areal capacity of 5 mAh cm −2 , which is about 16 times of that in bare ZnSO 4 electrolyte (53 h, Fig. 3d).Interestingly, due to the regulated Zn 2+ flux enabled by carboxyl group, the addition of Ac-Gly realizes much longer cycle life and higher cycle stability than that of Gly-NH 2 in Zn-Zn symmetric cells, which is consistent with the results analyzed before.To evaluate the evolution of Zn deposition process, the electrodeposition of Zn 2+ at 5 mA cm −2 on Zn anode was conducted and characterized by SEM.As shown in Fig. 3e, after 1 h of electrodeposition, the deposits are smooth and dense for ZnSO 4 + Gly/Ac-Gly, whereas loose and full of dendrites for bare ZnSO 4 and ZnSO 4 + Gly-NH 2 .For longer time of electrodeposition (2 h, Fig. S16), unlike the highly dense and flat deposits in ZnSO 4 + Gly electrolyte, there are some large pores generated with the presence of Ac-Gly, which may cause the failure of batteries during the subsequent cycling.The SEM images and XRD patterns of cycled Zn anodes in Figs.3f and S17 also confirm the critical role of combined amino and carboxyl on stabilizing Zn anode.Even at a larger current density of 10 mA cm −2 , Gly can ensure a superior operation stability of 175 cycles (350 h) with no fluctuation of voltage (Fig. S18).
The depth of discharge of Zn anode (DOD Zn ) is one of the crucial criteria to evaluate the gravimetric energy density of ZIBs, referring to the fraction of Zn involved in the electrochemical redox reactions in Zn anode [71].Since the commercial Zn foil (with a thickness slightly over 100 μm) used as anode at a low areal capacity is far too excessive, the utilization rate of Zn anode is extremely low (DOD Zn < 1%).In order to evaluate the stability of Zn anode at a higher DOD Zn , the thickness of commercial Zn foil was reduced by repeated rolling with several times.As shown in Fig. S19, the texture of rolled Zn foil is in accordance with that of commercial Zn foil, with a thickness of about 20 μm.
Subsequently, the voltage profiles of symmetric cells assembled with rolled Zn foils at different DOD Zn were depicted in Figs.S20 and 3 g.At a DOD Zn of 43% (the areal capacity is 5 mAh cm −2 ), a steady cycle lifespan for 400 h with less than 50 mV overpotential is achieved with the addition of Gly, whereas the cell with bare ZnSO 4 electrolyte presents short circuit within 100 h.Even at a higher DOD Zn of 68% (the areal capacity is 8 mAh cm −2 ), the Zn-Zn cell with Gly delivers a remarkable cycle stability up to 200 h.In contrast, large voltage polarization after 50 h is observed in the bare ZnSO 4 electrolyte and the cell finally becomes open-circuited at 83 h.These results are strong proofs for ensuring AZIBs achieve practical application target (DOD Zn > 40%) with the synergistic effect of amino and carboxyl groups.

Validation of Stable Anode-Electrolyte Interface Enhanced Full Cells with MnO 2 Cathode
Accordingly, The Zn-MnO 2 full cells were assembled with β-MnO 2 cathode to further demonstrate the stable anode-electrolyte Interface enhanced AZIBs.The β-MnO 2 powder synthesized by hydrothermal method possesses fine needle-like morphology with an average length of 2 μm and excellent crystallinity (Fig. S21).Notably, 0.1 M MnSO 4 was added into both bare ZnSO 4 and ZnSO 4 + Gly electrolytes to alleviate the manganese dissolution during cycling [72].
Figure 4a shows the CV curves of Zn-MnO 2 full cells with/ without Gly.The similar redox peaks of both two curves suggest that Gly has no impact on the reaction mechanism of MnO 2 , which is supposed to be the H + and Zn 2+ co-insertion mechanism [73].Obviously, the anodic peak shifts to lower voltage (Δ 1 = 21 mV) and the cathodic peak shifts to higher voltage (Δ 2 = 18 mV) in ZnSO 4 + Gly electrolyte, demonstrating the diminished polarization and boosted reaction kinetics of MnO 2 cathode material.Under the synergistic "anchor-capture" effect, the Zn-MnO 2 full cell delivers a superior rate capability to that with bare ZnSO 4 electrolyte (Fig. 4b).After cycling from 0.2 to 1.0 A g −1 (5 cycles for each current density), the Zn-MnO 2 cell with Gly remains a high specific capacity of 309.4 mAh g −1 and preferable capacity retention of 82% when the current density returns to 0.2 A g −1 , much higher than that in bare ZnSO 4 electrolyte (269 mAh g −1 , 73% of the initial capacity).The charge-discharge profiles presented in Figs.4c, d unveil that both two voltage plateaus during discharge process show better repeatability with increasing current density, further revealing the positive role of Gly on reaction reversibility of MnO 2 cathode.Finally, the long-term cycling performance of Zn-MnO 2 full cells with/without Gly was tested.In Fig. 4e, it is clear to see that the cell maintains a flat and steady cycle performance for 200 cycles with a higher discharge capacity of 167.2 mAh g −1 at 0.5 A g −1 in the presence of Gly, while a quick loss of capacity within 80 cycles is observed for the cell using bare ZnSO 4 electrolyte, which delivers an inferior discharge capacity of 93 mAh g −1 (31% of the initial capacity) at 200th cycle.Furthermore, the specific capacity with bare ZnSO 4 electrolyte rapidly decays from 105.1 to 16.7 mAh g −1 within 200 cycles at a current density of 3 A g −1 (Fig. S22a).In comparison, the cell with Gly additive delivers higher discharge capacity over the whole 200 cycles.Even at a higher current density of 5 A g −1 , the Zn-MnO 2 full cell assembled with Gly electrolyte exhibits a capacity retention of 75% (58.4 vs. 77.8mAh g −1 ) after 200 cycles (Fig. S22b).

Conclusions
In this work, Gly was used as an electrolyte additive to stabilize the Zn anode interface.Benefited from the synergistic "anchor-capture" effect of amino and carboxyl, Gly can steadily anchor on the Zn anode surface and capture the Zn 2+ at the interface, therefore inhibiting HER process and the formation of by-products, which ensures uniformly deposition of Zn 2+ .This strategy achieves a stable long cycle life over 2800 h (at the condition of 1 mA cm −2 and 1 mAh cm −2 ) and high Zn utilization rate of 68% (areal capacity of 8 mAh cm −2 ) in Zn-Zn symmetric cells.Moreover, the reversibility of Zn stripping/plating process is significantly improved with a high average CE of 99.22%.Finally, the superior rate performance and long-term cycling stability of Zn-MnO 2 full cells further verify the potential of Gly in practical application.This work would bring new insight into the selection and design of additives for promising AZIBs in large-scale energy storage.

Fig. 1 a
Fig. 1 a Molecular structures of Gly, Ac-Gly and Gly-NH 2 .The blue, brown, red and pink balls represent N, C, O and H atoms, respectively.b XRD patterns of Zn plates soaked in different solutions for 7 days.The pH values of ZnSO 4 + Gly/Ac-Gly/Gly-NH 2 solutions were adjusted to 1.37.c Tafel plots of the Zn anode tested with three-electrode system in different electrolytes.d LSV curves of Zn plate tested with threeelectrode system in different electrolytes.e Average differential capacitance for Zn in different electrolytes.FTIR spectra of Zn plates soaked in different solutions for 7 days: f Gly/H 2 O solution; g Ac-Gly/H 2 O and Gly-NH 2 /H 2 O solutions.h Adsorption energies comparison of H 2 O, Gly, Ac-Gly and Gly-NH 2 molecules on the Zn (002) facet, insets are the corresponding adsorbed models for different situations.The gray balls represent Zn atoms.i The charge density difference of the Zn slab with Gly molecule along the c axis (iso-value = 6 × 10 -4 e Bohr −3 ).The yellow and cyan iso-surfaces represent the increase and decrease in electron density, respectively stretching vibration at around 3100 ~ 3680 cm −1 shifts to a higher https://doi.org/10.1007/s40820-023-01171-w© The authors

Fig. 2 a
Fig. 2 a CV curves for Zn nucleation in Zn-Ti cells using bare ZnSO 4 and ZnSO 4 + Gly/Ac-Gly/Gly-NH 2 electrolytes.b The CA curves of Zn anode tested in Zn-Zn symmetric cells using different electrolytes.c Binding energies for Zn 2+ with different molecules (H 2 O and Gly) under QC calculations.d Electrostatic potential mapping of the Gly-Zn 2+ compound.e 3D snapshot of MD simulations for ZnSO 4 + Gly electrolyte and partial enlarged snapshot representing Zn 2+ solvation structure.f Simulated radial distribution functions (RDFs) for Zn 2+ -N (Gly) and Zn 2+ -O (Gly) collected from MD simulations in ZnSO 4 + Gly electrolyte.g Simulated RDFs and coordination numbers analysis for Zn 2+ -O (Gly) in ZnSO 4 + Gly electrolyte.h NMR spectra for ZnSO 4 /ZnSO 4 + Gly electrolytes.i Schematic illustration of Zn deposition behaviors in ZnSO 4 electrolyte with/without Gly

Fig. 3 a
Fig. 3 a CE comparison of Zn-Ti cells in bare ZnSO 4 and ZnSO 4 + Gly/Ac-Gly/Gly-NH 2 electrolytes at 1 mA cm −2 and 0.5 mAh cm −2 and b corresponding voltage profiles at different cycles, respectively.The voltage profiles of Zn-Zn symmetric cells using different electrolytes performed at c the current density of 1 mA cm −2 with the areal capacity of 1 mAh cm −2 , the insets are detailed voltage profiles at different cycle time ranges; d the current density of 5 mA cm −2 with the areal capacity of 5 mAh cm −2 .e The SEM images of Zn electrodeposition on Zn anodes in different electrolytes for 1 h at 5 mA cm −2 .f Surface morphologies of Zn anode after 50 cycles in different electrolytes under the condition of 5 mA cm −2 and 5 mAh cm −2 .g The voltage profiles of Zn-Zn symmetric cells using ZnSO 4 and ZnSO 4 + Gly electrolytes performed at the current density of 10 mA cm −2 with the areal capacity of 8 mAh cm −2 (rolled Zn foil as anode with the DOD Zn of 68%)

Fig. 4 a
Fig. 4 a CV curves of Zn-MnO 2 full cells using ZnSO 4 and ZnSO 4 + Gly electrolytes.b Rate capability of Zn-MnO 2 full cells at various current densities from 0.2 to 1.0 A g −1 in different electrolytes and c, d corresponding charge/discharge profiles.e Cycling performance of Zn-MnO 2 full cells at the current density of 0.5 A g −1 with/without Gly.0.1 M MnSO 4 was added into each electrolyte

1 3 2 Experimental Procedures and Calculations 2.1 Electrolytes Preparation and Cathode Material Synthesis
4were dissolved in 30 mL deionized water separately.Then mixed these two solutions quickly and stirred for 30 min until the solution turned purplebrown.Next, the mixed solution was transferred to an autoclave and heated at 140 °C for 12 h.The obtained precipitates were washed with deionized water by several times and dried in air at 80 °C for 12 h.