Recent Advances and Perspectives of Lewis Acidic Etching Route: An Emerging Preparation Strategy for MXenes

Highlights As an emerging preparation strategy for MXenes, Lewis acidic etching has attracted increasing attention in the past few years benefiting from a series of merits. Lewis acidic etching method is mainly presented from etching mechanism, terminations regulation, in-situ formed metals and delamination of multi-layered MXenes. The applications of MXenes and MXene-based composites obtained by Lewis acidic etching route in energy storage and conversion, sensors and microwave absorption are carefully summarized.


Introduction
The great success of graphene triggers enormous exploration in other two-dimensional (2D) materials, such as transition metal dichalcogenides, hexagonal boron nitride, layered double hydroxides (LDHs), graphitic carbon nitride, germanene, and black phosphorus [1][2][3][4][5][6][7][8][9][10].In 2011, multi-layered Ti 3 C 2 T x was first reported by Gogotsi and Barsoum's group, which announces the birth of a brand-new and large family of 2D materials, namely transition metal carbides, nitrides and carbonitrides termed as MXenes [11][12][13].They are generally derived from MAX precursors which possess a formula of M n+1 AX n (n = 1-4), where M stands for early transition metals (e.g., Ti, Ta, V, Mo, Nb, and Cr), A is mainly group 13 or 14 elements, such as Al, Si and Ga, and X refers to carbon or nitrogen (Fig. 1a) [14][15][16].So far, 155 MAX phases have been successfully synthesized [17].It is worth mentioning that some non-MAX ternary layered compounds such as Mo 2 Ga 2 C, Zr 3 Al 3 C 5 and Hf 3 Al 3 C 5 can also be used as precursors to prepare MXenes [18][19][20][21].Structurally, MAX precursors possess typical hexagonal closely packed crystal structure with a P6 3 /mmc space group, and they are established by stacking of M n+1 X n building blocks that are interleaved with A-site atom layer along the c direction, leading to strong M-X covalent/metallic/ionic mixed bond and weak M-A metallic bond [21][22][23].The difference in bond strength allows the A-site atoms to be selectively removed from MAX phase by a top-down method, and the remaining loosely stacked M n+1 X n architectures terminated with mixed surface groups T (e.g., -O, -OH, and -F) are named as MXenes, leading to a general chemical formula of M n+1 X n T x (n = 1-4, x ≤ 2) (Fig. 1b) [24][25][26].
The publications of MXenes have increased significantly in the past eight years and reach around 2600 in 2021 (Fig. 1c).It is noteworthy that the majority of reported articles are focused on Ti 3 C 2 T x MXene owing to its superior electronic conductivity (24,000 S cm −1 ) and large interlayer spacing [27][28][29][30].Correspondingly, great progress has been achieved in the development of MXenes, especially in compositional and structural diversity.First, there are four kinds of MXenes with different stoichiometries including M 2 XT x , M 3 X 2 T x , M 4 X 3 T x and M 5 X 4 T x [27,[31][32][33].Then, when the number of elements at the M-site exceeds two, MXenes can be categorized into three types according to the distribution of M-site atoms, namely s-MXenes with disordered arrangement, i-MXenes with in-plane ordering and o-MXenes with out-of-plane ordering (Fig. 1d) [15,[34][35][36].Additionally, X-site atoms can be occupied by carbon, nitrogen or both [37][38][39].Furthermore, the surface groups of MXenes mainly comprise of -O, -OH, -F, -Cl, -Br, -I, -S, -Se, -Te, -NH, etc., and can also be adjusted by etchants, termination substitution reaction and storage environment [40][41][42][43].To date, nearly 50 various MXenes have been experimentally fabricated [44].Considering the great tunability of M-site atoms, X-site atoms and surface terminations as well as the structural diversity of MXenes (Fig. 2), the number of MXenes will increase dramatically in the near future, eventually developing into a huge family [45].
MXenes generally exhibit a series of unique properties, including superior electronic conductivity, large and tunable gallery spacing, low ion diffusion barrier, rich surface chemistry, outstanding redox activity, hydrophilicity and wonderful mechanical strength (Fig. 2), making MXenes promising candidates for various fields [34,[45][46][47][48]. Specifically, large gallery spacing and rapid ion migration kinetics allow their use in high-performance metal-ion batteries and supercapacitors (SCs) [28,39,49,50].Flexibility, rich surface chemistry, adjustable interlayer spacing and high mechanical strength of MXenes enable them to be utilized as advanced separation membranes [51].Excellent electronic conductivity and light weight of MXenes permit their apply in electromagnetic interference shielding, and ample redox centers endow them with superior catalysis capability [52][53][54].Additionally, MXenes colloidal solution can be readily processed into freestanding papers and additive-free inks owing to the superior hydrophilicity [55,56].More importantly, the large compositional space, structural diversity and rich interlayer environment of MXenes offer great possibilities for unique combination and adjustability of properties (Fig. 2).For example, nitride MXenes display stronger polarity, higher electronic conductivity and more active sites compared with carbide counterparts, which renders them promising materials for secondary batteries [57].Besides, high entropy MXenes such as (Ti 1/5 V 1/5 Zr 1/5 Nb 1/5 Ta 1/5 ) 2 CT x offers high mechanical strain owing to the distinct lattice distortions, which can effectively induce the uniform nucleation and deposition of Li metal [58].Last but not least, the terminations play a key role in tuning the physicochemical characteristics of MXenes, especially in electronic properties.For example, MXenes without surface group possess high electron density near the Fermi level, while surface groups can generally alter the density of states and shift the Fermi level, finally resulting in semiconductor-like characteristics [59][60][61].Furthermore, Nb 2 C MXene with -Cl, -S or -Se surface groups demonstrated superconductivity, whereas the O or F-terminated Nb 2 C fail to enter the superconducting state in the low-temperature region [42,62].In summary, MXenes have been widely explored in various fields up to now and the great tunability of electronic, optical, magnetic, mechanical and thermal properties would gradually expand their applications in the future [45,63].
The effective synthesis strategy is able to adjust the properties of MXenes and make large-scale manufacturing possible [43,64].Until now, various preparation approaches for MXenes have been proposed.HF aqueous solution was first exploited to etch MAX precursors in 2011, which endows MXenes with distinct accordion-like morphology and mixed terminations of -OH, -O and -F [11].However, the strong corrosiveness of HF prevents some researchers from participating in the research of MXenes.In 2014, Ghidiu et al. reported the in-situ formation of HF etchant by simply mixing LiF and HCl, which is able to achieve the etching of MAX precursor and improve the safety of experimental operation simultaneously [65].Nevertheless, it is extremely challenging to prepare MXenes with uniform surface terminations by HF or LiF/HCl etching.Very recently, ZnCl 2 Lewis acidic salt was employed to etch Ti 3 AlC 2 MAX, which was based on the replacement reaction between Zn 2+ cations and zero-valence Al of Ti 3 AlC 2 MAX, finally leading to Zn metal-decorated multi-layered Ti 3 C 2 Cl 2 MXene [66].This strategy was further developed into a general route by using various Lewis acidic molten salts etchants to synthesize MXenes [67].Compared with HF or LiF/HCl etching, Lewis acidic molten salts etching strategy demonstrates a series of advantages, such as greatly enhanced safety because of avoiding the direct or indirect use of hazardous HF, great universality to etch non-Al MAX precursors, the ability to endow MXenes with controllable surface terminations, easy accessibility to in-situ formed metals-modified MXenes and the potential for large-scale application.
The Lewis acidic molten salts etching approach has received considerable attention since 2019 [66,67], which can be proved by the increasing article numbers (Fig. 3a).In summary, the MXenes and MXene-based composites prepared by Lewis acidic etching route have been applied by researchers from different fields, and significant progress has been achieved in the development of Lewis acidic etching (Fig. 3b-c), showing great utilization potential.Therefore, it is highly required to summarize these advances timely.Nevertheless, to the best of our knowledge, there has been no review discussing the research progress of Lewis acidic molten salts etching approach.Herein, we systematically summarize the recent advances of Lewis acidic etching strategy.First, we briefly introduce the traditional synthesis techniques of MXenes based on non-Lewis acidic etching route, mainly including HF etching, in-situ HF etching, bifluoride salts etching, electrochemical etching, alkali etching, common molten salts etching, etc.Then, Lewis acidic etching strategy are mainly presented from the following four aspects: etching mechanism, terminations regulation, in-situ formed metals and delamination of multi-layered MXenes (Fig. 4).Subsequently, the applications of MXenes and MXene-based composites produced by Lewis acidic molten salts etching route in energy storage and conversion, sensors and microwave absorption have been comprehensively discussed.Finally, we also propose some perspectives for the challenges and opportunities of Lewis acidic etching.This review aims to provide some help in the future development of Lewis acidic molten salts etching strategy and enable more researchers to fully understand this emerging method, thereby promoting its widespread utilization.

HF Etching
It is well known that graphene can be obtained by mechanical exfoliation of graphite because there is only weak van der Waals interaction between the layers [68,69].However, the metallic bond between M and A atoms in MAX precursors is stronger than van der Waals force, which makes it impossible to obtain MXenes via mechanical stripping of MAX precursors [21,26].Therefore, researchers have to explore other methods to prepare MXenes.In 2011, Gogotsi and Naguib et al. immersed Ti 3 AlC 2 MAX precursor in HF aqueous solution at room temperature and the Al layers can be selectively removed owing to the large difference between Ti-C and Ti-Al bond strength, thus leading to the successful preparation of multi-layered Ti 3 C 2 T x MXene with obvious accordion-like morphology (Fig. 5a-b) [11,[70][71][72].For the HF etchant, H + cations serve as oxidant and F − anions act as ligand to combine with by-product of the reaction.The etching process is presented as follows: (1) Ti 3 AlC 2 + 3HF = Ti 3 C 2 + AlF 3 + 3∕2H 2 Specifically, the almost zero-valence Al atoms in Ti 3 AlC 2 precursor lose electrons to become Al 3+ cations and then combine with F − anions ligand to form soluble AlF 3 [70,71].Simultaneously, the multi-layered Ti 3 C 2 MXene is generally modified with -O, -OH and -F groups based on Eqs.(2)(3)(4).The introduction of surface functional groups results in the shift of (002) peak to lower angle, which can effectively confirm the successful preparation of MXenes [70,73].Since then, a series of MXenes such as Ti 2 CT x , Nb 2 CT x , V 2 CT x , Ti 3 CNT x and Nb 4 C 3 T x have been successfully prepared by HF etching [13,[74][75][76][77]. Additionally, the obtained multi-layered MXenes can be intercalated by large organic molecules such as dimethyl sulfoxide (DMSO), urea, tetramethylammonium hydroxide (TMAOH), isopropanol (IPA), isopropyl amine (i-PrA), tetrabutylammonium hydroxide (TBAOH), which further expands the gallery spacing and weakens the interlayer  [66] Copyright 2019, American Chemical Society.Image published in 2020.04:Reproduced with permission from [67] Copyright 2020, The Authors, published by Springer Nature.Image published in 2020.06:Reproduced with permission from [157] Copyright 2020, Wiley-VCH.Image published in 2020.07:Reproduced with permission from [42] Copyright 2020, The American Association for the Advancement of Science.Image published in 2021.08:Reproduced with permission from [112] Copyright 2021, The Authors, published by Springer Nature.Image published in 2021.09:Reproduced with permission from [122] Copyright 2021, Wiley-VCH.Image published in 2022.08:Reproduced with permission from [147] Copyright 2022, Wiley-VCH.Image published in 2022.11:Reproduced with permission from [126] Copyright 2022, The Authors, published by Wiley-VCH interaction [78][79][80][81], finally enabling the multi-layered MXenes to be delaminated into few-layered or singlelayered MXenes (Fig. 5c) [82].
MAX precursors with different M-site atoms, A-site atoms, X-site atoms and n values usually require different HF concentration, etching time and reaction temperature.Generally, Mo-based and Nb-based MAX require higher HF concentration than Ti-based MAX to prepare corresponding MXenes [83,84].In addition, the etching of Sibased MAX including Ti 3 SiC 2 requires HF and other strong oxidants (H 2 O 2 , KMnO 4 , etc.) to complete together [85].Besides, compared with carbide MXenes, nitride MXenes require more precise adjustment of etching parameters during the preparation process, because the M-N bond may be broken under the attack of HF etchant [57].However, harsh reaction environment could result in the formation of defects, such as Ti vacancy, which can adversely affect the electronic conductivity of MXenes [86].Furthermore, some non-MAX precursors such as Zr 3 Al 3 C 5 , Hf 3 Al 4 C 6 and Mo 2 Ga 2 C can also be etched by HF to obtain Zr 3 C 2 T x , Hf 3 C 2 T x and Mo 2 CT x MXene, respectively, which greatly expands the scope of precursors and is of great significance to the development of MXenes [18][19][20].In general, HF etching method with excellent universality plays a crucial role in the rapid development of MXenes and some researchers still adopt this approach to prepare MXenes until now.Nevertheless, the strong corrosiveness of HF greatly increases the experimental risk and deteriorates its industrialization prospect.The development of a greener, safer and milder etchant is still the focus in the field of MXenes.

In-Situ HF Etching
In 2014, a relatively safe etching route by mixing HCl and LiF was proposed by Ghidiu et al. to prepare Ti 3 C 2 T x MXene [65].In this approach, HF can be in-situ generated to initiate the etching process based on Eq. ( 5) and Li + cations spontaneously intercalate into the interlayer of Ti 3 C 2 T x MXene.
The c-lattice parameter of MXenes obtained by LiF/HCl etching is greatly larger than that of MXenes prepared by HF etching, which is mainly owing to the intercalation of Li + cations and water molecules.Benefiting from the hydrophilic nature, the prepared Ti 3 C 2 T x MXene demonstrates claylike behavior and can be processed into different desired shapes such as rolled film.Additionally, clay-like Ti 3 C 2 T x MXene can be shaped into the letter "M" and exhibit a high electrical conductivity of 1500 S cm −1 .More importantly, thanks to the insertion of Li + ions and water, the van der Waals forces between the layers are weakened and multilayered MXenes can be directly centrifuged after sonication to obtain few-layered MXenes.It is worth mentioning that the molar ratio of LiF and Ti 3 AlC 2 MAX has a great influence on the lateral size of the final Ti 3 C 2 T x MXene, and higher LiF concentration favors the complete etching of Ti 3 AlC 2 MAX and intercalation of more Li + ions into the MXene interlayers.
Therefore, in-situ HF etching is further upgraded to the "minimally intensive layer delamination" (MILD) method in 2017 by increasing the molar ratio of LiF and Ti 3 AlC 2 MAX to 7.5:1.0,which can achieve the delamination of multi-layered MXenes via simple hand-shaking process rather than ultrasonication [87].The obtained Ti 3 C 2 T x MXene nanosheets demonstrate large lateral size and high quality, resulting in a high electronic conductivity of 4600 ± 1100 S cm −1 .So far, other fluoride salts including NaF, KF, FeF 3 , etc., and acids such as H 2 SO 4 have also been used by researchers [88][89][90][91].For example, Soundiraraju et al. reported the successful preparation of Ti 2 NT x MXene by immersing Ti 2 AlN MAX in a mixture of KF and HCl [89].Generally, the in-situ HF etching method based on LiF/HCl etchant has appeared the most in (5) HCl + LiF = HF + LiCl Fig. 4 An overview demonstrating the Lewis acidic etching method 1 3 the recently published articles on MXenes.The biggest advantage of in-situ HF etching route is the improvement of experimental safety and the ability to prepare MXenes nanosheets with larger lateral sizes and fewer defects.However, cations (Li + , Na + , K + , etc.) will intercalate into MXenes interlayers during the preparation process and it is difficult to eliminate them from MXenes, which may have an adverse impact on the further application of MXenes in some fields.The relationship between structure and properties should be further investigated.

Bifluoride Salts Etching
In 2014, bifluoride NH 4 HF 2 was used to etch the Ti 3 AlC 2 MAX precursor to obtain Ti 3 C 2 T x MXene [92].The reaction mechanism is summarized as follows: In this method, the selective etching of Al layers from Ti 3 AlC 2 MAX and the intercalation of NH 3 and NH 4 + into the interlayer of Ti 3 C 2 T x MXene occur simultaneously.The intercalation of ammonium species effectively increases the interlayer spacing.Further, NaHF 2 and KHF 2 were also utilized as etchants to prepare Ti 3 C 2 T x MXene by Feng et al. in 2017 and the etching mechanisms are similar to that of NH 4 HF 2 [93] (Fig. 5d).In 2020, Natu et al. used NH 4 HF 2 to etch Ti 3 AlC 2 MAX with polar organic solvents as the reaction medium instead of water, successfully realizing the water-free synthesis of Ti 3 C 2 T x MXene [94].The NH 4 HF 2 can be decomposed into HF and NH 4 F, and HF plays the role of etching the Al atomic layers.It is noteworthy that the as-prepared Ti 3 C 2 T x MXene is highly fluorinated and the ammonium cations surrounded by organic solvent molecules can intercalate into the layers, which endows MXene with the largest interlayer spacing of 5.07 nm up to now.Overall, the bifluoride salts etching is safer relative to HF etching.However, bifluoride salts are currently only used to etch Ti 3 AlC 2 MAX and the universality of the method requires to be further improved.

Electrochemical Etching
During the etching process of MAX precursors by using the three methods mentioned above, the researchers may be directly or indirectly exposed to hazardous HF, which reduces the safety of the experimental process.Moreover, high content of -F surface group may reduce the electronic conductivity of obtained MXenes and block ion transport, which is not conducive to their application in metal-ion batteries [59].Therefore, it is urgent to explore fluorinefree etching method.In 2014, Gogotsi et from Ti 2 SC MAX to obtain carbon/sulfur nanolaminates through electrochemical etching [96].It can be observed that the above two works failed to obtain MXenes by electrochemical etching method.In 2017, Sun et al. firstly synthesized Ti 2 CT x MXene without -F termination in diluted HCl aqueous electrolyte at 0.6 V for 5 days via electrochemical etching [97], and the mechanism can be exhibited as follows: At first, only the surface of Ti 2 AlC MAX that is in contact with the electrolyte can be etched and the generated Ti 2 CT x MXene is coated on the surface of MAX, which prevents electrolyte from entering the interior and makes it difficult for the inner MAX to be further etched.Subsequently, the Ti 2 CT x MXene on the surface will be transformed into a carbon layer.Finally, a three-layered structure including carbide-derived carbon, Ti 2 CT x MXene and unetched Ti 2 AlC MAX are obtained, thus leading to a low yield of MXenes.Some key parameters such as electrolyte concentration, etching potential and time have been proven to have a direct impact on the final etching products.
In 2018, Feng et al. prepared Ti 3 C 2 T x MXene with a large lateral size of 18.6 μm in a binary aqueous electrolyte containing NH 4 Cl and TMAOH (Fig. 5e) [98].In this method, the weak Ti-Al bond is broken and then Al 3+ cations combine with Cl − anions to form AlCl 3 .The obtained Ti 3 C 2 can be terminated by -OH group and the etching process is illustrated as follows: It is noteworthy that the intercalation of ammonium species and TMAOH can expand the interlayer spacing of Ti 3 C 2 T x MXene and expose more active sites, greatly promoting the etching of inner MAX phase and thus resulting in a relatively high etching yield of at least 60%.Later, a general strategy based on thermal-assisted electrochemical etching route was proposed by Hao's group to synthesize various MXene (Ti 2 CT x , Cr 2 CT x and V 2 CT x ) [99].In this approach, 1 M HCl solution is chosen as electrolyte and the heating facilitates the etching of MAX precursor.Specifically, when the etching time and temperature is increased to 9 h and 50 °C, respectively, the obvious accordion-like morphology can be observed for Ti 2 CT x MXene.In general, the electrochemical etching enables the preparation of fluorine-free MXenes for the first time and is safer and milder than conventional HF etching method.However, over-etching and low etching yield are unavoidable issues, which greatly hinders the largescale utilization of electrochemical etching method.

Alkali Etching
In addition to acids, alkalis can also be utilized to selectively etch MAX precursors.The earliest attempt to prepare MXenes via alkali etching was to immerse Ti 3 AlC 2 MAX in dilute aqueous NaOH solution at 80 °C by Xie et al. in 2014 [100].However, only the outermost MAX can be etched owing to the low NaOH concentration.Further, Zhang et al. proposed a NaOH-assisted hydrothermal process in 2018 to prepare Ti 3 C 2 T x MXene with a high yield of 92% (Fig. 5f) [101].In this method, the OH − anions attack Al-atom layers in Ti greatly increases the experimental risk, which makes alkali etching unsuitable for large-scale preparation of MXenes.

Common Molten Salts Etching
The above-mentioned methods for preparing MXenes are all based on the wet chemical etching route.However,  [89,103,105], which is mainly due to the difficulty in preparation.Firstly, the number of nitride MAX precursor is relatively limited due to the high formation energy.Then, M-A bond in nitride MAX exhibits high strength compared with that of carbide MAX, indicating that larger exfoliation energy is needed for nitride MAX.Finally, nitride MXene is prone to dissolve in HF solution and exhibits poor structural stability owing to the low cohesive energy [38,71].Therefore, great efforts should be made to explore the suitable etching route for nitride MAX.
In general, molten salts etching, as the first method to prepare nitride MXenes, is of great significance.However, this method is only applicable to the preparation of Ti 4 N 3 T x and Ti 2 NT x MXene at present, and the obtained MXene exhibits high content of -F surface group.The above two key points greatly limit the development of common molten salts etching method.

Other Etching Methods
In addition to the etching methods described above, there are other methods that can also be used to prepare MXenes.In 2017, Gogotsi's group presented an ammoniation strategy to transform Mo 2 C and V 2 C MXene to corresponding Mo 2 N and V 2 N at 600 °C by using NH 3 as nitrogen source (Fig. 5g) [105] Compared with above-mentioned top-down methods, the bottom-up approaches are usually able to synthesize defectfree 2D materials, which can also be utilized to obtain highquality MXenes.In 2015, Ren et al. developed chemical vapor deposition method to fabricate large-area high-quality ultrathin α-Mo 2 C nanosheets, which possess a thickness of few nanometers and a lateral size of around 100 µm [111].Moreover, the prepared α-Mo 2 C MXene exhibits superior stability under various environments including water, HCl or annealing at 200 °C in air.More importantly, this method reveals excellent generality and can also be used to construct WC and TaC crystals.In conclusion, many various methods have been proposed to prepare MXenes until now.However, each etching route has its own shortcomings and is unlikely for large-scale utilization in the future.As we all know, exploring a safe, green, non-hazardous, low-cost and easily scalable preparation method is the biggest challenge for the researchers in the fields of MXenes, which plays a crucial role in the development of MXenes in the next decades.

MXene Synthesis: Lewis Acidic Etching Method
In 2019, Huang's group proposed a brand-new, safe and green method, namely Lewis acidic molten salts etching, to prepare Cl-terminated MXene [66].Owing to a series of advantages, Lewis acidic etching has attracted intensive attention since it was presented, greatly promoting the development of MXenes in the past three years.The introduction of Lewis acidic molten salts etching approach is mainly classified into following four aspects: etching mechanism, terminations regulation, in-situ formed metals and delamination of multi-layered MXenes.

Etching Mechanism
The mechanism of Lewis acidic molten salts etching method is based on the replacement reaction between Lewis acidic molten salts and A-site atoms in MAX precursor.Taking the etching of Ti 3 AlC 2 MAX precursor by the firstly used Lewis acidic salt ZnCl 2 as an example, Huang et al. thoroughly mixed the Ti 3 AlC 2 and ZnCl 2 with a molar ratio of 1:1.5 in a glovebox and the mixture was placed in alumina crucible, which is then heated at 550 °C for 5 h in a tube furnace under Ar atmosphere (Fig. 6a) [66].It can be observed that main peaks of final product shift to lower angles relative to those of Ti 3 AlC 2 MAX in the X-ray diffraction (XRD) patterns (Fig. 6b), revealing an enlarged lattice parameter.Additionally, the densely-packed structure can still be kept, and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image in Fig. 6c [66] Copyright 2019, American Chemical Society.h Schematic demonstrating the preparation of Ti 3 C 2 T x MXene by CuCl 2 etching.i Schematic showing the relationship between redox potential of A-site elements, redox potential of Lewis acidic salts and Gibbs free energy.Reproduced with permission from [67] Copyright 2020, The Authors, published by Springer Nature.j Schematic illustration of the one-pot synthesis of Ti 3 C 2 T x MXene under air atmosphere.Reproduced with permission from [112] Copyright 2021, The Authors, published by Springer Nature.k Phase diagram of NaCl/ZnCl 2 mixture.Reproduced with permission from [113] Copyright 2021, Wiley-VCH atoms can diffuse into the interlayer of Ti 3 C 2 and occupy the position originally belonging to Al atoms, thereby leading to the generation of new MAX phase Ti 3 ZnC 2 .It is worth mentioning that the removal of AlCl 3 from the system considerably accelerates the element replacement reaction.
When the molar ratio of Ti 3 AlC 2 and ZnCl 2 further increases to 1:6, Ti 3 C 2 MXene with -Cl termination instead of Ti 3 ZnC 2 MAX can be successfully obtained.Firstly, the classical multi-layered structure is observed for Ti 3 C 2 Cl 2 MXene (Fig. 6d).Then, the XRD pattern of as reacted product indicates that the strongest (104) peak at around 39° of Ti 3 AlC 2 MAX almost vanishes and the (002) peak moves to a lower angle of 7.94° (Fig. 6e), suggesting an expanded interlayer spacing.Additionally, the characteristic XRD peaks of Zn metal can also be observed.Further, Ti-Cl chemical bond in Ti 3 C 2 Cl 2 MXene can be confirmed by Cl 2p X-ray photoelectron spectroscopy (XPS) spectra (Fig. 6f) [66].Above discussions effectively confirm the formation of Ti 3 C 2 Cl 2 MXene and the reaction process can be described by following equations: As exhibited in Fig. 6a, the formation of Ti 3 C 2 Cl 2 MXene can be divided into two stages including the initial formation of Ti 3 ZnC 2 MAX shown in Eqs.(15)(16) and the subsequent reaction of Ti 3 ZnC 2 MAX with excessive ZnCl 2 to obtain Ti 3 C 2 Cl 2 exhibited in Eqs.(17)(18)(19).Specifically, the Zn atoms in Ti 3 ZnC 2 MAX can be separated from interlayer and react with excessive Zn 2+ to generate Zn 2 2+ cations, and the Cl − anions can easily intercalate into the interlayer of Ti 3 C 2 , forming Ti-Cl chemical bond (Fig. 6g).Meanwhile, the Zn 2 2+ cations gain electron to form Zn metal.In general, Zn 2+ cations and Cl − anions in ZnCl 2 act as H + and F − in HF etchant, respectively.Later in 2020, Prof. Huang and coworkers generalized the previously proposed Lewis acidic etching method, which greatly expands the family of Lewis acidic molten salts (FeCl 2 , CoCl 2 , NiCl 2 , CuCl 2 , CdCl 2 , CuI, CuBr 2 , etc.) and can prepare various MXenes from Al, Si and Ga-based MAX precursors [67].They immersed Ti 3 SiC 2 MAX in CuCl 2 /NaCl/KCl mixed molten salts at 750 °C (Fig. 6h), ( 17) and NaCl and KCl play a role in providing molten salts environment.The etching process is illustrated as follows: Specifically, the zero-valence Si atoms in the interlayer lose electrons to become Si 4+ cations and then combine with Cl − anions to form SiCl 4 , which can readily escape as gas at around 57 °C.Subsequently, the Cu 2+ cations can obtain electrons to transform into Cu metal.Finally, excessive Cl − anions can be grafted onto exposed Ti atoms, resulting in the formation of Ti 3 C 2 Cl 2 MXene.It is worth mentioning that individual HF is difficult to etch Ti 3 SiC 2 [85], while Lewis acidic salts can readily complete the above etching process, which reflects the superiority of Lewis acidic etching.After the etching process, NaCl, KCl and excessive CuCl 2 can be eliminated by washing the etching products with deionized water.
Further, Huang et al. proposed an effective criterion to determine whether the A-site atoms in MAX can react with metal ions in the Lewis acidic salts.They found that the metal ions in the Lewis acidic salts with high electrochemical redox potential can etch the MAX precursor with low redox potential A-site atoms.The relationship between redox potential of A-site elements, redox potential of Lewis acidic salts and Gibbs free energy is illustrated in Fig. 6i.For example, CuCl 2 molten salt can easily remove the Si atoms from Ti 3 SiC 2 MAX as mentioned above, which is ascribed to the higher redox potential of Cu 2+ /Cu pair (−0.43 V versus Cl 2 /Cl − ) compared with that of Si 4+ /Si pair (−1.38 V versus Cl 2 /Cl − ).The general etching reaction between A-site elements in MAX phase and Lewis acidic molten salts MQ y (Q = Cl, Br or I) can be described as follows: It can be inferred that the difficulty degree of etching M n+1 AX n precursors by Lewis acidic molten salts is independent of M, X and n values, and only depends on the redox potential of A-site element.Therefore, based on Lewis acidic etching criterion, a large number of MAX phases (Ti 3 AlC 2 , Ti 3 ZnC 2 , Ti 3 SiC 2 , Ti 3 AlCN, Ti 2 GaC, Ti 2 AlC, Ta 2 AlC, Nb 2 AlC, etc.) can be etched by using different Lewis acidic salts (FeCl 2 , CoCl 2 , NiCl 2 , CuCl 2 , CdCl 2 , AgCl, CuI, CuBr 2 , etc.).
The reaction mechanism of Lewis acidic etching method is basically clear now, but the understanding of Lewis acidic (20) etching method can still be further deepened by optimizing etching parameters such as reaction atmosphere and etchant compositions.For example, in order to prevent the oxidation of the prepared MXenes, the inert gas such as Ar is generally used for protection in the process of Lewis acidic etching.However, Lin et al. proposed a simple one-pot synthesis method, containing molten salts shielded strategy for MAX preparation and subsequent in-situ Lewis acidic etching, to achieve the preparation of MXenes under air atmosphere (Fig. 6j) [112].Specifically, they thoroughly mixed Ti, Al and C powders with NaCl and KCl salts, and the mixture was then pressed into a pellet.Subsequently, the pellet was further placed in a salt bed composed of NaCl and KCl which can melt at around 650 °C to insulate the air, and the Ti 3 AlC 2 MAX can be obtained by heating at 1300 °C for 1 h in muffle furnace without Ar protection.Finally, CuCl 2 was introduced to the reaction system at 700 °C to achieve the in-situ etching of Ti 3 AlC 2 MAX for 10 min, thus leading to the quick formation of Cl-terminated Ti 3 C 2 T x MXene.Therefore, with the assistance of the molten salts shielding strategy, Lewis acidic molten salts can directly etch MAX precursor in air atmosphere, which greatly promotes the development of Lewis acidic etching method.In addition, Zhang et al. demonstrated one-step eutectic etching strategy for the synthesis of in-plane porous Ti 3 C 2 Cl 2 MXene by regulating the etchant composition from ZnCl 2 to NaCl/ZnCl 2 mixture [113].When ZnCl 2 is used to etch the MAX phase, the volatilization of generated AlCl 3 at high temperature will cause structural/crystal defects in the precursor, which will then evolve into void space.However, the generated pores will gradually collapse owing to the absence of temporary physical support during cooling process.Further, they found that when the etchant is changed into a mixture of ZnCl 2 and NaCl in a molar ratio of 4:6, the NaCl mole percent will gradually increase to 72% with the progress of etching process, which makes the salt melt shift across the phase boundary and leads to the precipitation of NaCl particles at 550 °C based on the phase diagram (Fig. 6k).The formation of NaCl particles can occupy void space to prevent the shrinkage and collapse of pores, finally resulting in a large increase in mesoporous volume and specific surface area.Therefore, the pore structure of the prepared MXenes can be greatly adjusted by the manipulation of etchant composition.The above-mentioned two works indicate that the Lewis acidic etching method still possesses broad development space and can be further improved from different aspects in the future.

Terminations Regulation
A large number of theoretical calculations and experiments have proved that the composition of surface groups can considerably influence the physical and chemical properties of MXenes, such as electronic property, mechanical property, magnetic property, optical property, chemical stability, dispersibility and redox activity [15,26,55,61,63,[114][115][116].Therefore, in order to accurately explore that how surface functional groups affect the properties of MXenes, it is pretty important to synthesize MXenes with controllable surface chemistry.However, preparing MXenes with single and uniform surface groups has been a huge challenge for researchers.Taking HF etching as an example, MXenes exhibits mixed surface terminations including -O, -OH and -F [31,43].Firstly, the complex and uncontrollable surface termination greatly affect the properties of MXenes, which is not conducive to the management of experimental variables and the large-scale preparation of MXenes.Additionally, functional groups like -F can irreversibly react with Li + or Na + cations and block their transport, which negatively affects the electrochemical performance of MXenes electrodes [117,118].Therefore, preparing MXenes with fluorine-free surface groups should be the best choice for researchers in the fields of lithium-ion batteries (LIBs) or sodium-ion batteries (SIBs).However, it is difficult to obtain MXenes with homogeneous and fluorine-free terminations before 2019.Fortunately, the fabrication of MXenes with totally controllable surface chemistry is realized by the propose of Lewis acidic molten salts etching strategy.The functional groups of MXenes prepared by Lewis acidic etching mainly depends on the Lewis acidic salts anions.For example, Ti 3 C 2 MXene terminated by -Cl functional group can be synthesized by Cl − anions-containing Lewis acidic salts etching.However, a small part of -Cl terminations may be replaced by -O groups during the washing process, and the content of -O surface group mainly depends on the competition between -O and -Cl terminations [67,119].Lin et al. proved that -O surface group in Nb 2 C MXene prepared by CuCl 2 etching demonstrates stronger competitiveness compared with -Cl surface groups, thus leading to Nb 2 CT x MXene rich in -O termination, while the competition between -O and -Cl for Ti 3 C 2 MXene is relatively weak [119].Since the -O functional groups are conducive to the electrochemical process of metal-ion batteries and SCs [120,121], it is necessary to further increase the content of -O termination in Ti 3 C 2 T x MXene.Pang [122], the additional introduction of six water molecules can effectively raise the number of -O functional groups and the etching process can be described as follows: Due to the wide variety of halogen elements in the Lewis acidic molten salts, MXene can also be terminated by other halogen anions.For example, Ti 3 C 2 MXene with -Br or -I functional groups can be obtained via CuBr 2 or CuI etching, respectively (Fig. 7a-b).Further, Ti 3 C 2 MXene can be endowed with -BrI, -ClI and -ClBr binary terminals as well as -ClBrI ternary halogen terminations.It is gratifying to note that Ti 3 C 2 MXene with -Cl, -Br or -I functional groups all exhibit metallic-level conductivity (Fig. 7c), while F or OH-terminated Ti 3 C 2 MXene often demonstrates semiconductor behavior [11,66,123,124].More importantly, due to the strong electrochemical reactivity, Br or I-terminated Ti 3 C 2 MXene demonstrates excellent zinc storage performance.However, Ti 3 C 2 MXene with -O, -F, -OH and -Cl functional groups exhibit low discharge specific capacity and oblique charge discharge curve when used as cathode for zinc-ion batteries (ZIBs) [123].The above discussion reveals that the electrochemical performance of MXene electrodes can be greatly enhanced by adjusting the type of functional groups.Additionally, the halogen terminations of MXenes can be used as halogen sources and nucleation sites to prepare MXene/halide heterostructures.For example, Cui et al. synthesized intimate contact Bi 12 O 17 Cl 2 /Ti 3 C 2 MXene 2D/2D heterojunctions by the in-situ growth of Bi 12 O 17 Cl 2 nanosheets on the surface of Cl-terminated Ti 3 C 2 MXene that was obtained via CuCl 2 etching [125].
Since the bond dissociation energies of Ti-Br and Ti-Cl bond are smaller than that of Ti-O, Ti-OH and Ti-F bonds [126], it is possible to chemically modify the surface of MXenes originally terminated with -Br or -Cl functional groups at a relatively low temperature.Based on this point, Kamysbayev et al. proposed a universal strategy to successfully prepare O, S, Se, Te and NH-terminated Ti 3 C 2 MXene and non-terminated Ti 3 C 2 via Lewis acidic etching and subsequent termination substitution/elimination reactions in molten inorganic salts (Fig. 7d) [42].Firstly, Ti 3 C 2 Br 2 MXene was prepared by mixing Ti 3 AlC 2 MAX with CdBr 2 Lewis acidic salt.As followed, Ti 3 C 2 Br 2 MXene was dispersed in CsBr/KBr/LiBr eutectic salt at 300 °C and then reacted with NaNH 2 , Li 2 O, Li 2 S, Li 2 Se or Li 2 Te at around 500-600 °C in an Ar-filled glove box to synthesize Ti 3 C 2 (NH), Ti 3 C 2 O, Ti 3 C 2 S, Ti 3 C 2 Se, Ti 3 C 2 Te MXene, respectively.Moreover, when treated with LiH at 300 °C, the surface groups of Ti 3 C 2 Br 2 MXene can be completely eliminated, thus leading to the formation of bare Ti 3 C 2 MXene.This strategy realizes the controllable chemical transformation of functional groups for the first time.The surface groups can significantly regulate the interatomic spacings of MXenes lattice and their electronic properties.For example, the Ti 3 C 2 Te lattice exhibits a greater in-plane lattice expansion (18%) (Fig. 7e).More importantly, Cl, S and Se-terminated Nb 2 C MXene prepared by the above-mentioned strategy exhibits unprecedented superconductivity behavior (Fig. 7f), while Nb 2 C MXene with -F and -O terminations synthesized by HF etching fails to demonstrate superconducting state, which is also proved by theoretical calculations [62].The discovery of superconductivity phenomenon is mainly attributed to the influence of functional groups including -Cl, -S and -Se on MXenes structure, such as lattice strain, carrier localization, phonon frequency, and electron-phonon coupling [127], which greatly promotes the research of MXenes in the field of physics.
Very recently, Zhang et al. reported the synthesis of Ti 3 C 2 Br x MXene through CuCl 2 etching of Ti 3 AlC 2 precursor and subsequent termination substitution in AlBr 3 /NaBr/KBr eutectic molten salts [128].When the molar ratio of AlBr 3 is lower than 50%, the AlBr 3 /NaBr/ KBr molten system with plenty of naked Na + , K + and Br − demonstrates strong Lewis basicity.The Na + and K + cations can intercalate into the interlayer of MXene and the previous -Cl termination can be replaced by the Br − anions via nucleophilic reaction, which simultaneously achieves the increase of interlayer spacing and the substitution of surface groups.The enlarged interlayer spacing leads to an expanded multi-layered morphology of Ti 3 C 2 Br x MXene, which may be conducive to the following delamination process to obtain few-layered nanosheets.In addition, Liu et al. synthesized N-containing Ti 3 C 2 T x MXene via FeCl 2 1 3 Lewis acidic etching, subsequent magnet cleaning and final thermal treatment in Li 3 N/LiCl/KCl molten salts (Fig. 7g) [126].The magnet cleaning process can not only effectively remove Fe nanoparticles, but also prevent the -Cl surface group from being largely replaced by -O, which is beneficial for following termination substitution reaction.The dramatic decrease in Cl L2,3-edge intensity and appearance of N-K edge in electron energy-loss spectroscopy (EELS) confirm that the -Cl functional groups can be transformed to -N terminations in Li 3 N/LiCl/KCl Lewis basic molten salts (Fig. 7h), thus leading to the N-containing Ti 3 C 2 T x MXene.
In short, combined with Lewis acidic etching, termination exchange reactions in Lewis basic molten salts medium can endow MXenes with unconventional terminations, which have never appeared before and are hard to be directly obtained by individual Lewis acidic etching.By selecting various Lewis bases with different anions such as S 2− , Se 2− , Te 2− , N  X elements as well as various surface groups mentioned above, there are a large number of new MXenes that can be explored, which may show some excellent properties.Up to now, the regulation of MXene surface groups through chemical transformation is still in its infancy and plenty of theoretical calculations and experiments are required to further explore the effect of these new functional groups on the properties of different MXenes, such as electrical conductivity, ion diffusion kinetics, thermal conductivity, work function, optical conductivity, mechanical property, hydrophilicity, chemical and thermal stability.

In-Situ Formed Metals
According to the etching mechanism shown in Eq. ( 22), metal ions in the Lewis acidic molten salts can be in-situ reduced to various metals during the etching process of MAX precursors, thus leading to the formation of MXenes/ metals composites.Taking CuCl 2 etching of Ti 3 SiC 2 MAX as an example, Cu nanoparticles can be uniformly anchored among the multi-layered Ti 3 C 2 T x MXene matrix and the Ti 3 C 2 T x /Cu hybrids can be successfully obtained [67].It is worth mentioning that Cu nanoparticles are able to be loaded in the Ti 3 C 2 T x MXene matrix through one-step insitu growth process, so the interaction between them is stronger than that of Ti  8a), respectively [122].The strong interaction between Cu nanoparticles and -O surface group of Ti 3 C 2 T x MXene can be proved by X-ray absorption (XAS) spectrum (Fig. 8b), effectively preventing the detachment of Cu from the Ti 3 C 2 T x MXene matrix.Furthermore, owing to the diversity of MXene compositions and the large family of Lewis acidic molten salts, various metal nanoparticles (Fe, Co, Ni, Zn, Ag, Cd, Sn, etc.) can be distributed among the different MXenes (Ti 3 C 2 , Ti 3 CN, Ti 2 C, Ta 2 C, Nb 2 C, etc.), which greatly enriches the choice of researchers.In the early development stage of the Lewis acidic etching strategy, researchers generally remove the in-situ generated metal nanoparticles from MXenes/metals composites in order to obtain pure MXenes, which almost becomes a custom.However, metal or metal compounds have been intensively investigated in energy storage and conversion, electromagnetic interference shielding and other fields in the past few decades [129][130][131][132][133]. Consequently, rational and effective application of various metals in MXenes/ metals composites obtained by Lewis acidic etching is worth investigating.Additionally, MXenes have been widely utilized to support metal or metal compounds.Based on the excellent synergistic effect between MXenes and metals or metal compounds, MXenes/metals hybrids and MXenes/metal compounds composites exhibit better performance than their individual components and have been widely investigated in various fields [54,73,[134][135][136][137][138].Nevertheless, the traditional fabrication process of MXenes/ metals hybrids or MXenes/metal compounds composites usually requires the synthesis of MXenes and the subsequent introduction of additional metal sources, which makes the preparation process complicated [117,[139][140][141][142][143][144].As mentioned above, Lewis acidic salts can achieve the etching of MAX precursor and the introduction of metal sources simultaneously.Therefore, if Lewis acidic molten salts are used to etch MAX phases, the obtained MXenes/metals composites can be applied directly, and then the MXenes/ metal compounds composites can be prepared by one-step sulfurization, phosphorization, tellurization or selenization treatment of MXenes/metals composites, which opens a new window for the universal construction of MXene-based hybrids through Lewis acidic etching route, showing great research potential.
In general, MXenes/metals or MXenes/metal compounds composites can be obtained quickly and easily by taking full advantage of Lewis acidic etching products.As expected, the MXenes/metals and MXenes/metal compounds composites prepared by Lewis acidic etching route have been rationally applied in some fields due to the superior structural stability.For example, the reported Ti 3 C 2 -Cu composites via CuCl 2 •2H 2 O molten salts etching exhibit superior electrochemical performance in SCs when used as electrode material [122].Additionally, Snnanoconfined Ti 3 C 2 T x MXene was synthesized by onestep SnCl 2 molten salt etching (Fig. 8c-d), and demonstrated excellent cyclic stability as anode for LIBs [145].Further, CoCl 2 etching and in-situ sulfidation process were used to prepare strongly coupled N-doped MXene-CoS 2 composites, which can effectively alleviate the shuttle effect of lithium polysulfides (LiPSs) in lithium-sulfur 1 3 (Li-S) batteries [146].Recently, our group presented a general method to fabricate a series of Ti 3 C 2 T x MXene/ transition metal sulfides (MS y , M = Fe, Co, Ni or Cu) composites via Lewis acidic etching and subsequent sulfurization treatment (Fig. 8e-f) [147,148].When served as anodes for SIBs, the readily produced hybrids can show greatly boosted sodium storage performance owing to the interfacial electronic coupling.Until now, the applications of Lewis acidic molten salts etching products, especially the in-situ formed metals, have been relatively rare and concentrated in the field of energy storage.More rational utilization of etching products in other fields, such as electromagnetic interference shielding, demonstrates great potential and deserves further exploration.

Delamination of Multi-Layered MXenes
The MXenes prepared by Lewis acidic etching strategy exhibit obvious multi-layered accordion morphology.In order to demonstrate true 2D morphology, it is necessary to implement intercalation and delamination process to obtain single-layered or few-layered MXene nanosheets, which can expose more active sites and possess higher surface area [71].In general, MXenes prepared by HF etching are terminated with -O and -OH functional groups and therefore show excellent hydrophilicity [81], which makes it easy to disperse MXenes in water.The well-dispersed MXenes can then be intercalated by organic molecules (urea, amine, DMSO, TMAOH, TBAOH, IPA, etc.) and inorganic substances (LiCl, NaCl, KCl), which increases the gallery spacing and weakens the van der Waals force and hydrogen bond between MXene layers [43, 78-80, 149, 150].Finally, the few-layered MXenes nanosheets can be obtained by ultrasonic and centrifugation processing [151,152].Nevertheless, MXenes prepared by Lewis acidic etching method fail to be terminated by -OH functional group, which greatly decreases their hydrophilicity [153][154][155].Therefore, it is difficult to uniformly disperse the obtained MXenes in water to form stable colloidal solution, which greatly reduces the delamination efficiency, thus exhibiting a low yield of few-layered and single-layered nanosheets.In order to enhance the delamination efficiency, researchers often considerably extend the sonication time, which tends to endow MXenes with small lateral size and poor quality.In general, most of the MXenes synthesized by Lewis acidic etching is at the multi-layered state according to the published articles, and only a few of them are at the fewlayered state.
For example, Ti 3 C 2 Cl x nanosheets with lateral dimensions of 0.4-2.0μm were prepared by 10 h ultrasonication treatment of multi-layered MXene obtained by ZnCl 2 etching [156].Yang  MXene by CdCl 2 molten salt etching, and the multi-layered MXene was intercalated by IPA molecule followed by 25 h ultrasonication process to obtain few-layered nanosheets with lateral size of hundreds of nanometers [159].Furthermore, Liu et al. used large organic base molecule TBAOH to intercalate into Ti 3 C 2 T x MXene produced by CuCl 2 etching, followed by ultrasonication bath for 6 h at low temperature to separate the layers, leading to the few-layered nanosheets with a lateral size of around 600 nm [153].It is worth mentioning that TMAOH intercalated Lewis acidic salts etched-Ti 3 C 2 T x MXene suspension can be stably stored for 2 weeks without obvious precipitation.Finally, DMSO molecule intercalation and ultrasonication process can also be used to delaminate the Cl-terminated Ti 3 C 2 MXene prepared by CuCl 2 etching to obtain few-layered samples [125].To sum up, due to the poor hydrophilicity of MXenes prepared by Lewis acidic etching, the delamination usually requires large organic molecules and long-time sonication, which leads to low yields of few-layered MXenes and small lateral sizes of nanosheets.
In order to solve the above-mentioned issues, two viable and effective methods have been proposed.The first method is to enhance the hydrophilicity of MXenes, and the other method is to disperse MXenes in organic solvents instead of water for intercalation and delamination.For example, Arole et al. presented a method to produce water-dispersible Ti 3 C 2 T x nanosheets via SnF 2 molten salt etching, KOH washing, DMSO intercalation and bath sonication for 1 h (Fig. 9a) [154].The KOH washing facilitates the introduction of -OH terminal groups on Ti 3 C 2 T x MXene and thus greatly boosts the formation of stable Ti 3 C 2 T x suspension with a zeta potential of −31.7 mV.The few-layered or singlelayered Ti 3 C 2 T x nanosheets can be prepared by DMSO intercalation and sonication for only 1 h (Fig. 9b), which is conducive to reduce the required energy during the sonication process.Finally, the Ti 3 C 2 T x film produced by vacuum filtration exhibits an electronic conductivity of 706 S cm −1 , In addition, Kamysbayev et al. immersed multi-layered Ti 3 C 2 T x (T = -Cl, -S or -NH) MXene obtained by Lewis acidic etching and surface functionalization in n-butyllithium (n-BuLi) hexanes solution to complete the Li + intercalation process (Fig. 9c).Then, the lithium-intercalated Ti 3 C 2 T x MXene was added to the polar organic solvent N-methyl formamide (NMF) rather than water, leading to the stable colloidal solution with a zeta potential of −29.3 mV after bath sonication for 1 h (Fig. 9d) [42].The as-prepared Ti 3 C 2 T x suspension of single-layered nanosheets exhibit obvious Tyndall effect and superior crystallinity (Fig. 9e-g), showing the advantage and potential of delamination in polar organic solvents.However, n-BuLi is difficult to be widely used as intercalator due to its high risk.In conclusion, although some progress has been made in the delamination of multi-layered MXenes obtained by Lewis acidic etching, there is still no simple, safe and effective method to prepare MXene nanosheets with high yield and large lateral size.
Table 1 compares non-Lewis acidic etching strategies with Lewis acidic etching in terms of some key indicators such as universality, scalability, safety and terminations.
It can be concluded that Lewis acidic etching exhibits good universality, scalability and safety relative to other methods.Table 2 comprehensively summarizes the parameters for the preparation of various MXenes by Lewis acidic etching, which includes the molar ratio of MAX precursor and Lewis acidic salts, reaction temperature, time and 1 3 atmosphere.Additionally, delamination parameters such as the type of intercalators and sonication time are also presented.

Applications
Benefiting from the unique layered structure, superior electronic conductivity, low ion diffusion barrier, uniform and  1 3 tunable surface functional groups and large interlayer spacing, the obtained MXenes and MXene-based composites via Lewis acidic molten salts etching route have been intensively investigated in various fields, such as energy storage, energy conversion, sensors and microwave absorption.

Energy Storage
Due to the rapid consumption of fossil fuels and gradually serious environmental pollution, the development of clean renewable energy has become more and more important [160,161].However, the intermittency and instability of renewable energy makes it necessary to store the generated electricity [162].In recent years, electrochemical energy storage devices have received increasing research interests because of their fast response speed, versatility and application flexibility [163].Among the various electrochemical energy storage devices, LIBs currently occupy an absolute dominant position.Other technologies such as SIBs, ZIBs, Li-S batteries and SCs are in a rapid development period [164].In particular, SIBs are promising for large-scale energy storage in the following few years owing to the low price and abundant sodium resources [165].

Lithium-Ion Batteries
In the past three decades, significant progress has been made in the development of LIBs technology.Derived from the high power and energy density, long cycle life, high energy conversion efficiency and low discharge rate, LIBs system has now been widely used in consumer devices, electric vehicles and large-scale energy storage [166,167].Layered materials have been intensively studied as electrode materials for LIBs due to their unique structural stability.As early as 2012, Tang et al. confirmed that Ti 3 C 2 MXene possesses low Li + diffusion barrier, superior electronic conductivity, low discharge voltage and high lithium storage capacity via theoretical computation, making it a promising LIBs anode [59].Since then, a large number of works have experimentally proved that MXene-based anodes can deliver relatively high discharge capacity, stable long-term cyclic performance and outstanding rate performance [72,[168][169][170][171].The theoretical capacities of MXene electrodes depends on formula weight, interlayer spacing as well as the type of transition metals and surface groups.MXenes with low formula weights such as V 2 C and Ti 2 C can afford large gravimetric capacities [88,172,173].In addition, large interlayer spacing can allow more Li + ions to intercalate into the MXenes, accordingly leading to higher specific capacities [30,174].Surface functional groups such as -F and -OH has been proved to impede Li + transportation via theoretical calculations, which is unfavorable for realization of theoretical specific capacity [59,172].However, O-terminated Ti 3 C 2 MXene can absorb two Li layers, confirming the lithium affinity of -O functional groups and thus contributing to the enhanced lithium storage capacity (Fig. 10a) [120].
It is worth mentioning MXenes obtained by Lewis acidic etching method may exhibit better electrochemical performance due to the absence of -F and -OH surface groups and the introduction of -O termination.In 2020, Li et al. prepared multi-layered Ti 3 C 2 T x MXene (T = -O and -Cl) via CuCl 2 etching of Ti 3 SiC 2 precursor [67].When used as anode for LIBs, the obtained Ti 3 C 2 T x MXene exhibit a distinct pseudocapacitive-shaped cyclic voltammetry (CV) curves without redox peaks in organic electrolyte.In comparison, MXene anodes synthesized by HF etching generally show obvious redox peaks in CV profiles [168,171].In addition, Ti 3 C 2 T x MXene delivers a discharge capacity of 205 mAh g −1 at 0.6C rate, corresponding to the fact that per Ti atom can transfer around 0.4 electrons.Further, superior long-term cyclic stability up to 2400 cycles can be obtained for multi-layered Ti 3 C 2 T x MXene electrode.The superior lithium storage performance can be attributed to the strong adsorption ability of -O surface group on Li + cations [120].Moreover, the Li + insertion/deinsertion storage mechanism can be confirmed by the enlarged/decreased interlayer spacing through in-situ XRD measurement.In 2021, the Nb 2 CT x MXene (T = -O and -Cl) with obvious accordionlike morphology was prepared by CuCl 2 molten salt etching of Nb 2 AlC precursor [119].The theoretical calculations indicate that -O surface groups can obtain more electrons from Nb atoms than -Cl termination for Nb 2 CT x MXene, thus resulting in the substitution of -O for -Cl functional groups during ammonium persulfate solution washing process, which is conducive to its lithium storage performance.Nb 2 CT x MXene anode delivers a high discharge capacity of 330 mAh g −1 at 50 mA g −1 (Fig. 10b), which is larger than the theoretical specific capacities of Nb 2 C (305 mAh g −1 ) and Nb 2 CO 2 (292 mAh g −1 ).Additionally, capacity rising phenomenon can be clearly observed for Nb 2 CT x MXene at 1000 mA g −1 (Fig. 10c), which can be attributed to the electrochemical activation and common pillaring effect.
In 2022, Lin et al. prepared Ti 2 CT x and Ti 3 C 2 T x MXene by one-pot method in an air atmosphere with Ti, C, and Al powders as precursor, simultaneously achieving the synthesis of MAX and in-situ CuCl 2 etching in molten salts system [112].When served as anodes for LIBs, Ti 2 CT x and Ti 3 C 2 T x electrode both exhibit rectangular and symmetric CV curves in a voltage range of 0.1-2 V (Fig. 10d), which is similar to those of previously reported MXene electrodes prepared by Lewis acidic etching [67].Furthermore, Ti 2 CT x anode shows discharge capacities of 256 and 164 mAh g −1 at 0.5 and 10 mV s −1 , respectively.In comparison, specific capacities of 164 and 113 mAh g −1 can be obtained for Ti 3 C 2 T x electrode at the same scan rate.The superior rate performance of these two MXene electrodes is mainly due to the pseudocapacitive-controlled charge storage mechanism.Later, Chen et al. reported the synthesis of Ti 3 C 2 T x , Ti 2 CT x , Ti 3 CNT x and Ti 4 N 3 T x MXene via molten salts-shielded synthesis strategy in air atmosphere with MAX phases as precursor and CuCl 2 molten salt as etchant [175].The low-melting eutectic salt reaction medium can effectively restrain the oxidation of MXenes at high temperature.More importantly, the proposed method can be used to prepare Ti 3 C 2 T x MXene on a relatively large scale.The distinct accordion-like structure can still be obtained for Ti 3 C 2 T x MXene prepared from 60 g batch of Ti 3 AlC 2 MAX (Fig. 10e), demonstrating superior scalability.Among the Ti 3 C 2 T x , Ti 2 CT x and Ti 3 CNT x MXene electrodes, Ti 2 CT x anode delivers the largest discharge capacity, and the three electrodes all exhibit excellent rate performance (Fig. 10f).
Recently, Cao et al. demonstrated the successful preparation of multi-layered Ti 2 NT x MXene (T = -O and vCl) via CuCl 2 etching at 450 °C for 1 h [176].The existence of Ti-Cl and Ti-O bonds can be confirmed by XPS and XAS measurement.Theoretical calculations indicate that the Gibbs energy change of -O substituting -Cl termination is −2.3 eV, while the value of -O replacing -F surface group is 0.07 eV, demonstrating that -Cl can be readily substituted by -O.The obtained Ti 2 NT x MXene can deliver high discharge capacities of 303.4 and 158.4 mAh g −1 at 0.1 and 5 A g −1 , respectively.More importantly, a large capacity of 350 mAh g −1 after 1,200 cycles at 1 A g −1 can be obtained for Ti 2 NT x electrode, revealing outstanding cycling stability.A hybrid capacitor by pairing Ti 2 NT x anode and super activated carbon cathode can demonstrate an energy density of 45.36 Wh kg −1 at 123.32 W kg −1 .It is noteworthy that the MXene electrodes mentioned above are all at multilayered state, and few-layered MXene electrodes may show better electrochemical performance.Liu et al. reported the synthesis of exfoliated Ti 3 C 2 T x MXene (termed as e-MS-Ti 3 C 2 T x ) via CuCl 2 molten salts etching and subsequent TBAOH intercalation [153].The e-MS-Ti 3 C 2 T x electrode delivers discharge capacities of 225 and 95 mAh g −1 at 0.2 and 16 A g −1 , respectively, which is higher than that of unexfoliated Ti 3 C 2 T x anode.The boosted rate performance of e-MS-Ti 3 C 2 T x electrode is mainly assigned to the enhanced contact area between electrode and electrolyte after exfoliation.Additionally, the increased content of -O termination after TBAOH treatment will also benefit the lithium storage performance [177].
The type of halogen terminations may have an influence on the electrochemical performance of MXene.Liu et al. synthesized Ti 3 C 2 T x MXene with -F, -Cl or -Br functional groups via HF, NiCl 2 or NiBr 2 etching, respectively [178].The typical accordion morphology can be afforded for three halogenated MXenes.The element composition analysis shows that Ti 3 C 2 Br x MXene possesses the highest content of -O surface group among the Ti 3 C 2 F x , Ti 3 C 2 Cl x and Ti 3 C 2 Br x MXene (Fig. 10g).This phenomenon is mainly assigned to the fact that the formation energy of Ti-Br bond is the lowest compared with that of Ti-Cl and Ti-F bonds according to theoretical calculations.Consequently, -O can easily replace the -Br surface group when the prepared Ti 3 C 2 Br x MXene is exposed to air, and the highest content of -O functional group contributes to the largest discharge capacity of 189 mAh g −1 for Ti 3 C 2 Br x anode.Finally, the Ti 3 C 2 Br x electrode exhibits the best rate performance and cyclic performance relative to Ti 3 C 2 F x and Ti 3 C 2 Cl x anode (Fig. 10h).The electrode materials mentioned above are all individual MXenes, while the MXene/active metal composites can also be utilized as anodes for LIBs.Wu et al. reported the preparation of Sn-nanoconfined Ti 3 C 2 T x MXene hybrids via SnCl 2 molten salt etching of Ti 3 AlC 2 [145].The Sn nanoparticles are in-situ grown and confined between the Ti 3 C 2 T x MXene during the etching process.It is noteworthy that the confined effect of MXene can effectively prevent the aggregation of Sn nanoparticles at high temperature and accommodate its large volume variation upon cycling.As a result, Ti 3 C 2 T x /Sn anode remains a reversible capacity of 226.2 mAh g −1 after 1000 cycles at 0.2 A g −1 , which is higher than that of pure Ti 3 C 2 T x and Sn electrode.The volume expansion of Sn nanoparticles can gradually enlarge the interlayer spacing of MXene from 1.17 to 1.34 nm after 2200 cycles (Fig. 10i), which greatly exposes more active sites upon cycling and contributes to the obvious capacity rising phenomenon.

Sodium-Ion Batteries
SIBs possess a similar working mechanism to LIBs.It is well known that the working voltage of SIBs is lower than that of LIBs, thus resulting in a relatively low energy density of SIBs [179,180].However, due to the abundance of sodium resources and attractive cost-effectiveness [181], SIBs are promising to be utilized in some fields that do not require high energy density, such as large-scale energy storage [182,183].As a type of negative electrode for SIBs, transition metal sulfides exhibit high theoretical specific capacities and safe discharge voltage [184].Nevertheless, large volume expansion and inferior charge transfer kinetics of transition metal sulfides greatly deteriorate their sodium storage performance [185].Our group has been working on improving the electrochemical performance of transition metal compounds in the past few years [73,117].Recently, we proposed a general strategy for constructing Ti 3 C 2 T x MXene/transition metal sulfides (Ti 3 C 2 T x /MS y , T = -O and -Cl, M = Fe, Co and Ni) heterostructures as SIBs anodes through directly sulfurizing Lewis acidic etching products (MXenes/metal composites) (Fig. 11a-b) [147].Different from the traditional construction process of preparing MXene first, then adsorbing transition metal ions and finally vulcanizing, this strategy simplifies the preparation procedure of MXene/transition metal sulfides hybrids via rationally utilizing Lewis acidic etching products.Additionally, this fabrication process avoids the use of HF as etchant and water as reaction medium, which effectively improves the experimental safety and alleviates the oxidation of MXene, respectively.For the fabricated Ti 3 C 2 T x /FeS 2 heterostructures, FeS 2 nanoparticles are in-situ grown and tightly fixed on the Ti 3 C 2 T x MXene substrate (Fig. 11c-d), demonstrating a stable framework for continuous Na + insertion/extraction. Furthermore, O 1 s XPS spectrum and theoretical calculations confirm that Ti 3 C 2 T x MXene and FeS 2 nanoparticles demonstrate interfacial electronic coupling effect via Ti-O-Fe bonds (Fig. 11e-f), facilitating the rapid interfacial electron transfer from MXene to FeS 2 .Additionally, Ti 3 C 2 T x /FeS 2 hybrids also exhibit rapid Na + diffusion kinetics and mechanical strain release channels.Consequently, derived from the above advantages, the Ti 3 C 2 T x /FeS 2 anode delivers a reversible capacity of 474.9 mAh g −1 after 600 cycles at 5 A g −1 (Fig. 11g), and reveals a high capacity of 456.6 mAh g −1 at 10 A g −1 , suggesting outstanding long-term cyclic performance and rate capability.In addition, the full-cell device assembled with Ti 3 C 2 T x /FeS 2 anode and Na 3 V 2 (PO 4 ) 3 cathode can demonstrate a discharge capacity of 431.6 mAh g −1 after 1000 cycles at 3 A g −1 and an energy density of around 130 Wh kg −1 at a power density of 415 W kg −1 , indicating superior application prospect of Ti 3 C 2 T x / FeS 2 heterostructures.
Copper sulfide (CuS), as another common transition metal sulfide, also possesses high theoretical capacity and low price, and has been widely studied as anode for SIBs.However, electrode pulverization and inferior electrochemical reaction kinetics have an adverse effect on its performance In order to improve the sodium storage performance of CuS, our group readily fabricated Ti 3 C 2 T x /CuS hybrids (T = -O and -Cl) via CuCl 2 •2H 2 O etching and following in-situ sulfurization treatment [148].The construction process also achieves the effective application of Lewis acidic molten salts etching products.Plenty of CuS nanoparticles are distributed among the Ti 3 C 2 T x MXene substrate, and they are connected by Ti-O-Cu covalent bonds.Benefiting from the extremely boosted electron transfer and Na + migration, enhanced sodium adsorption and structural integrity, the obtained Ti 3 C 2 T x /CuS anode delivers stable long-term cyclic performance with a discharge capacity of 347 mAh g −1 after 800 cycles at 3 A g −1 and wonderful rate performance with a high capacity of 346.3 mAh g −1 at 8 A g −1 .More importantly, the constructed SIBs full cell with Na 3 V 2 (PO 4 ) 3 cathode and Ti 3 C 2 T x /CuS anode reveals a capacity of 189.6 mAh g −1 after 800 cycles at 2 A g −1 .In the above-mentioned two works, MXene/transition metal sulfide heterostructures are efficiently constructed by rationally utilizing Lewis acidic etching products, namely MXenes/ metal composites, which fully reflects the great advantages of Lewis acidic etching relative to other etching methods.

Zinc-Ion Batteries
Due to the flammability of organic electrolyte, LIBs and SIBs systems possess inevitable potential safety hazards, resulting in the combustion of electric vehicles and largescale energy storage devices from time to time in the past few years [187].Therefore, ZIBs system has recently attracted considerable attention owing to the use of aqueous electrolyte, which possesses high safety and low price [188,189].Additionally, ZIBs also demonstrate other important merits, such as high eco-efficiency and ionic conductivity of approximately 1 S cm −1 [190].The halogen electrodes including Br 2 and I 2 exhibit conversion reaction mechanism and high theoretical specific capacities, and have been widely investigated as cathode materials for ZIBs [191][192][193].Fortunately, the MXenes obtained by Lewis acidic etching can be endowed with -Br or -I functional groups, so it is necessary to investigate their zinc storage performance (Fig. 12a).In 2021, Li et al. prepared Ti 3 C 2 MXene with -Cl, -Br and -I functional groups through CuCl 2 , CuBr 2 and CuI etching, respectively [123].When applied as cathodes for ZIBs, the Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXenes exhibit obvious redox peaks in CV profiles and flat discharge-charge plateaus in galvanostatic charge-discharge curves, while Ti 3 C 2 Cl 2 MXene shows no redox peaks and oblique charge-discharge curves.The conversion reaction process of Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene is illustrated as follows: In contrast, the Cl − anions in Ti 3 C 2 Cl 2 MXene will loss electrons and turn into Cl 2 gas, which may escape from the MXene interlayer, making this conversion reaction irreversible.Consequently, Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene demonstrate energy densities of 129 and 135.6 Wh kg −1 , respectively, which is significantly higher than that of Ti 3 C 2 Cl 2 MXene.This work realizes the application of halogen terminations for the first time, and also suggests that the electrochemical performance of MXenes can be greatly improved by regulating the surface groups.
It is worth mentioning that the reaction mechanism of above-mentioned Ti 3 C 2 I 2 MXene is still stopping at individual I − /I 0 redox pair, thus resulting in a low discharge voltage of around 1.3 V when used as ZIBs cathode.If the I 0 /I + redox pair can be activated, the discharge voltage can be further increased.However, I + cations are unstable in common electrolytes such as ZnSO 4 solution.In order to solve this issue, Li et al. first synthesized Ti 3 C 2 I 2 MXene via CuI etching and then chose electrolyte system that contains electronegative F − or Cl − anions, which can considerably stabilize the I + cations during the cycling process [194].Specifically, once I + cations are generated, F − or Cl − anions can combine with them, making I + cations exist stably, which can be effectively confirmed by the peak at 200 cm −1 in the in-situ Raman spectra of the Ti 3 C 2 I 2 MXene (Fig. 12b).Therefore, the I 0 /I + redox pair are successfully activated in ZnCl 2 + KCl electrolyte and a higher reduction peak at 1.66 V can be observed (Fig. 12c).As expected, Ti 3 C 2 I 2 MXene in ZnCl 2 + KCl electrolyte affords a large discharge capacity of 207 and 126 mAh g −1 at a current density of 0.5 and 5 A g −1 , respectively, showing superior rate performance.Additionally, outstanding cyclic stability can be delivered for Ti 3 C 2 I 2 MXene with ( 27) approximately 80% capacity retention after 2800 cycles.The excellent zinc storage performance is attributed to the rapid electron/Zn 2+ transfer kinetics and strong confinement effect of MXene that prevents interlayer iodine active species from escaping to the outside.In short, the additional high discharge plateau at 1.65 V endows Ti 3 C 2 I 2 MXene with a large energy density of 280 Wh kg −1 .The above two works indicate that MXenes prepared by Lewis acidic molten salts etching has broad development space in aqueous ZIBs.

Lithium-Sulfur Batteries
Li-S batteries have received extensive attention since its birth in 1962.Compared with LIBs, SIBs and ZIBs systems, Li-S batteries demonstrate a very high theoretical energy density of 2600 Wh kg −1 and have been regarded as one of the most promising energy storage devices in the future [195,196].However, ultralow electronic conductivity of sulfur (10 -30 S cm −1 ) and Li 2 S, sluggish reaction kinetics, severe shuttle effect of LiPSs and low utilization rate of sulfur result in inferior rate performance and cyclic durability [197].Luckily, MXenes are expected to improve the electrochemical performance of Li-S batteries owing to their metallic conductivity, chemical adsorption ability, catalytic effect and structural diversity [198,199].In 2020, single atom zinc implanted Ti 3 C 2 T x MXene (SA-Zn-MXene) as sulfur host was successfully fabricated via ZnCl 2 etching of Ti 3 AlC 2 MAX [157].They found that Zn 2+ cations in ZnCl 2 molten salt can not only react with the interlayer Al atoms, but also replace a few Ti species in MXene lattice during the etching process, which can be further confirmed by the bright dots corresponding to Zn atoms in HAADF-STEM image (Fig. 12d).On one hand, the SA-Zn-MXene exhibits strong interaction with Li 2 S 4 polysulfides (Fig. 12e), and can catalyze the polysulfides transformation by decreasing the reaction barriers.On the other hand, the nucleation of Li 2 S 2 / Li 2 S can be significantly boosted by Zn atoms in MXene lattice.Additionally, the large volume variation of sulfur upon cycling can be accommodated by flexible Ti 3 C 2 T x MXene.Consequently, the S@SA-Zn-MXene electrode exhibits the lowest overpotential of 23 mV and superior rate performance with a high capacity of 517 mAh g −1 at 6C (Fig. 12f).More importantly, the enhanced cyclic stability can be obtained for S@SA-Zn-MXene, which delivers a discharge capacity of 706 mAh g −1 after 400 cycles at 1C.
Polar metal compounds including metal oxides, metal sulfides, metal selenides, metal nitrides, metal borides and metal phosphides have been considered as effective electrocatalysts to accelerate reaction kinetics of LiPSs [200][201][202].In 2022, Yang et al. obtained N-doped Ti 3 C 2 T x MXene-CoS 2 heterostructure (N-MX-CoS 2 ) via CoCl 2 etching and subsequent in-situ sulfidation treatment with thiourea as sulfur source (Fig. 12g), and then utilized N-MX-CoS 2 as a bifunctional catalyst to modify the commercial separator [146].The N element can be doped into the hybrids during the process of thiourea pyrolysis, which can be proved by the existence of N-C and Ti-N peaks in XPS spectra.This strategy enables CoS 2 nanoparticles to be tightly anchored among the MXene substrate.In the N-MX-CoS 2 hybrids, the N atoms and polar CoS 2 nanoparticles can form strong chemical interaction with LiPSs and provide rich catalytic sites to facilitate LiPSs conversion reaction.The Ti 3 C 2 T x MXene with metallic-level conductivity can further promote sulfur redox reaction kinetics.Since N-MX-CoS 2 heterostructure possesses dual functions of adsorption and catalysis, the shuttle effect of LiPSs can be effectively inhibited and polarization can be greatly decreased (Fig. 12h-i).Finally, the batteries with modified separator deliver superior rate performance (775 mAh g −1 at 4C) and excellent long-term cycling stability with a low decay rate of 0.052% per cycle (651 mAh g −1 after 700 cycles at 1C and 721.6 mAh g −1 after 400 cycles at 2C) (Fig. 12j).To our relief, a series of MXenes/metal compound composites with strong binding energy can also be synthesized via Lewis acidic etching route, which is worthy of in-depth exploration and may provide new inspiration to the further development of Li-S batteries.

Metal Anodes-Based Batteries
Metal anodes including Li, Na, K, Al, Mg and Zn have been intensively investigated in high-performance secondary metal batteries in the past few decades owing to their low plating/stripping potentials and high theoretical specific capacities, thus leading to high energy densities [203][204][205][206]. Nevertheless, there are some key factors that deteriorate the electrochemical performance of metal anodes.First, the uneven deposition of metals during the discharge process will contribute to the uncontrolled growth of dendrites, which can pierce the separator and result in the shortcircuit of cells.Then, the nearly infinite volume expansion leads to the rupture of solid electrolyte interphase (SEI) layer.In addition, the side reactions and the formation of "dead metal" will continuously consume the electrolyte and metal sources.Consequently, metal anodes generally demonstrate low coulombic efficiency, short cycle life and serious safety hazards [207,208].Some common strategies such as optimizing electrolyte composition, building artificial SEI film and fabricating three-dimensional robust frameworks have been utilized to enhance the performance of metal anodes [209].Fortunately, MXenes with high electronic conductivity, low ion migration barrier, unique layered structure and sufficient functional groups can greatly facilitate the plating/stripping kinetics, effectively preventing the dendrite growth [15,210].
For example, single zinc atoms immobilized Ti 3 C 2 Cl x MXene (Zn-MXene) as a host for lithium metal was reported through ZnCl 2 molten salts etching (Fig. 13a-b), and the content of Zn monoatoms is around 0.87 at% [156].It is worth mentioning that sufficient reaction time is conducive to the substitution of Zn for Ti.Due to the lithiophilic nature of Zn, the lithium metal can preferentially nucleate around the single atom Zn sites on the surface of Ti 3 C 2 Cl x MXene.When the plating level increases to 5 μAh cm −2 , a flat and smooth morphology can be obtained (Fig. 13c).Furthermore, Li metal grows vertically along the nucleation site to form a bowl-shaped lithium at higher deposition amounts (Fig. 13d-e), finally achieving dendrite-free Li metal anode.Therefore, Zn-MXene films can exhibit a low nucleation overpotential of 11.3 mV for half battery and a long cycle life of 1200 h for symmetric cells at 1 mA cm −2 with a fixed capacity of 1 mAh cm −2 .In addition, the Zn-MXene//LiFePO 4 full cell delivers a high capacity of 150 mAh g −1 at 0.5C and superior cyclic stability with a capacity of about 100 mAh g −1 after 500 cycles at 10C.
In recent years, MXenes have attracted extensive attention in inhibiting the growth of Zn dendrites due to their superior lattice matching [211].More importantly, the surface groups of MXenes are considered to affect the adsorption energy and migration kinetics of Zn 2+ ions.Based on this point, Li et al. reported the synthesis of various halogenated MXenes including Ti 3 C 2 Cl 2 , Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene as interface layers via corresponding Lewis acidic molten salts etching to regulate the Zn deposition [212].They found that above-mentioned halogenated MXenes possess metallic-level conductivities and good affinity to Zn metal via theoretical simulation (Fig. 13f), which is conducive to the deposition of Zn 2+ ions.Consequently, Zn 2+ ions tend to grow horizontally rather than vertically under the regulation of outermost halogen surface groups, which effectively inhibits the disordered growth of Zn metal at the beginning.Subsequently, the constructed coherent heterogeneous interface induces the uniform deposition of Zn metal (Fig. 13i).As expected, the obtained halogenated MXene-Zn anode exhibits better electrochemical performance than bare Zn metal anode.Among the MXenes with -Cl, -Br or -I terminations, the -Cl functionalized Ti 3 C 2 MXene-Zn anode possesses the strongest ability to inhibit the growth of Zn dendrites derived from its medium adsorption and diffusion for Zn 2+ .Consequently, Ti 3 C 2 Cl 2 -Zn electrode exhibits a flat and smooth surface after cycling, and a cycle life of 840 h at 2 mA cm −2 with a fixed capacity of 1 mAh cm −2 for symmetric cells (Fig. 13g-h).Finally, the Ti 3 C 2 Cl 2 -Zn//Ti 3 C 2 I 2 full cell demonstrates superior long-term cyclic stability up to 9,000 cycles, which is better than that of Zn//Ti 3 C 2 I 2 battery.The above two works indicate that MXenes obtained by Lewis acidic etching have a good induction effect on the uniform growth of metal anodes.

Dual-Ion Batteries
As a novel battery concept, the dual-ion batteries (DIBs) demonstrate a brand-new working mechanism, which is realized by intercalating the anions and cations of electrolyte into respective electrodes.In general, DIBs possess some advantages such as high theoretical energy density, low cost and long cycle life [213].Nevertheless, low anode specific capacity of DIBs still remains a big problem.MXenes, as a type of 2D layered material, have abundant nano-level channels to allow the insertion and de-insertion of ions and can be regarded as electrodes for DIBs.In 2022, Ti 3 C 2 Cl 2 MXene with adjustable in-plane porosity was obtained by eutectic molten salts (NaCl/ZnCl 2 ) etching (Fig. 14a) [113].The formation mechanism of in-plane pore has been discussed previously in detail.Specifically, the surface area and mesoporous volume of Ti 3 C 2 Cl 2 MXene increase gradually with the rise of NaCl content in ZnCl 2 /NaCl mixture (Fig. 14b-e), which can create more active sites and benefit the Li + migration.For example, when the mole percent of NaCl in ZnCl 2 /NaCl mixture is 60%, the obtained Ti 3 C 2 Cl 2 -60 MXene delivers a specific surface area of 85 m 2 g −1 and pore size concentrates on 3-4 nm.Additionally, Ti 3 C 2 Cl 2 -60 demonstrates superior TiC 6 octahedral core symmetry and low Li + migration kinetics.Consequently, the Ti 3 C 2 Cl 2 -60 MXene as LIBs anode delivers a discharge capacity of 382 mAh g −1 at 0.1 A g −1 .Further, when paired with graphite cathode, Ti 3 C 2 Cl 2 -60/graphite DIBs afford a high discharge capacity of 242 mAh g −1 at 0.1 A g −1 (Fig. 14f), and the superior cyclic stability with 83% capacity retention can also be obtained (141 mAh g −1 after 1000 cycles at 1 A g −1 ), demonstrating excellent electrochemical performance.The in-plane porous MXene produced by Lewis acidic molten salts etching can also be utilized in other fields such as catalysis.

Supercapacitors
SCs store and release energy through the physical adsorption and desorption of electrolyte ions on the electrode surface, and show higher energy density compared with common capacitors [214].Up to now, SCs have been regarded as a reliable and promising energy storage device due to high power density, environmental friendliness and high safety [215].MXenes become one of the best electrodes for SCs owing to the moderate specific area, high electronic conductivity, rich ion diffusion channels and large faradaic pseudocapacitance [28,216].MXene was first used as electrode material for SCs in 2013 [217].Yury et al. reported the synthesis of a series of cations (Li + , Na + , K + , NH 4 + and Mg 2+ )-intercalated Ti 3 C 2 T x MXene, and a volumetric capacitance of 350 F cm −3 can be obtained in KOH electrolyte, which is better than that of traditional porous carbon.Later, freestanding Ti 3 C 2 T x films prepared by LiF/HCl etching exhibit a high volumetric capacitance of 900 F cm −3 at 2 mV s −1 in H 2 SO 4 electrolyte [65].Recently, MXenes synthesized by Lewis acidic etching have also been investigated as electrode materials for SCs.For example, Ti 3 C 2 -Cu composites was prepared by CuCl 2 •2H 2 O Lewis acidic salts etching in 2021, and the Cu nanoparticles are tightly anchored on the Ti 3 C 2 T x MXene via Ti-O-Cu interfacial bond [122].Previous studies have shown that O-terminated MXenes exhibit high capacitance due to the easy absorption of H + by -O functional group.The Ti 3 C 2 -Cu electrode is able to deliver a capacitance of 885 F g −1 at 0.5 A g −1 in H 2 SO 4 electrolyte.Additionally, the symmetric SCs based on Ti 3 C 2 -Cu achieve a high areal energy density of 103.3 μWh cm −2 at 0.8 mW cm −2 .The superior electrochemical performance of Ti 3 C 2 -Cu electrode is mainly attributed to high content of -O termination, high pseudocapacitive contribution of Cu nanoparticles, boosted charge/mass transfer kinetics and strong interaction between MXene and Cu.
Later, Khan et al. synthesized Ti 3 C 2 Cl 2 , Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene via CuCl 2 , CuBr 2 and CuI molten salts etching, respectively [218].When used as electrode materials for SCs in 3 M H 2 SO 4 electrolyte, typical pseudocapacitiveshaped CV curves can be obtained and a specific capacity of 92, 29 and 63C g −1 can be afforded for Ti 3 C 2 Cl 2 , Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene at 5 mV s −1 .Further, the capacity retention ratio can reach as high as 85.22% after 10,000 cycles at 1.4 A g −1 for Ti 3 C 2 I 2 electrode, suggesting outstanding long-term cyclic stability.The excellent electrochemical performance of -F, -Br or -I functionalized MXene mainly benefits from the high electrochemical activity of corresponding halogen surface groups.In order to further improve the performance of MXenes produced by Lewis acidic etching, several common and effective strategies such as tuning the interlayer spacing and compositing MXene with other electroactive materials have been proposed by researchers.For example, Zhang et al. reported the synthesis of Ti 3 C 2 Cl 2 MXene via CdCl 2 etching in 2022 and then increased the interlayer spacing of MXene by the intercalation of NaCl and cetyltrimethylammonium bromide (CTAB), respectively (Fig. 14g) [219].As expected, large organic cation CTA + can greatly enlarge the interlayer spacing to 1.16 nm, while the small Na + cation-intercalated MXene shows a value of 1.14 nm (Fig. 14h).The large interlayer spacing of MXene-CTAB can increase the contact area between MXene and electrolyte, boost the ion diffusion kinetics and decrease the charge transfer resistance.Additionally, the CTA + cations can react with the ions between MXene layers, and effectively adsorb counter ions in the electrolyte to deliver additional specific capacitance.Consequently, the Ti 3 C 2 Cl 2 MXene-CTAB electrode can provide a higher capacitance of 258.28 F g −1 in (NH 4 ) 2 SO 4 electrolyte than MXene-NaCl.The highest energy density of MXene-CTAB electrode can reach 11.48 Wh kg −1 at a power density of 200 W kg −1 .More importantly, Ti 3 C 2 Cl 2 MXene-CTAB exhibits superior cyclic durability with only 7% capacitance loss after 3000 cycles at 1.0 A g −1 , which is superior to that of Ti 3 C 2 Cl 2 MXene and Ti 3 C 2 Cl 2 MXene-NaCl.
LDHs have been regarded as promising electrode materials for SCs owing to their high specific capacitance and energy density [220].However, low electronic conductivity of LDHs results in inferior rate capability and cyclic performance [221].Hybridizing LDHs with highly conductive MXenes may lead to great improvement in electrode performance.In 2022, Zhao et al. firstly prepared Ti 3 C 2 Cl 2 MXene nanodots (QD-Ti 3 C 2 Cl 2 ) via CdCl 2 etching and subsequent hydrothermal reaction, and the nanodots are distributed on the surface of MXene nanosheets [222].Then, the negatively-charged QD-Ti 3 C 2 Cl 2 can integrate with positively-charged NiAl-LDHs to electrostatically fabricate QD-Ti 3 C 2 Cl 2 @NiAl-LDHs composites, where the NiAl-LDHs nanosheets are dispersed on MXene nanosheets (Fig. 14i).Derived from the superior charge transfer kinetics of QD-Ti 3 C 2 Cl 2 , a small band gap of 0.52 eV can be obtained for QD-Ti 3 C 2 Cl 2 @NiAl-LDHs, which is lower than that of NiAl-LDHs (1.51 eV), demonstrating enhanced electronic conductivity.Additionally, compared with NiAl-LDHs, QD-Ti 3 C 2 Cl 2 @NiAl-LDHs hybrids possess a higher specific area of 658.74 m 2 g −1 and lower Gibbs free energy of redox reaction (−0.355 eV) (Fig. 14j), greatly accelerating the mass transport and adsorption of active species.Therefore, the obtained QD-Ti 3 C 2 Cl 2 @NiAl-LDHs electrode achieves a pretty high capacitance of 2010.8F g −1 at 1.0 A g −1 (Fig. 14k), and excellent long-term cyclic performance with 94.1% capacitance retention after 10,000 cycles, which is better than those of NiAl-LDHs electrode.Additionally, a large energy density of 100.5 Wh kg −1 can be delivered for QD-Ti 3 C 2 Cl 2 @NiAl-LDHs at a power density of 299.8 W kg −1 .The above examples reveal that MXenes prepared by Lewis acidic etching are promising anodes for electrochemical energy storage systems.

Energy Conversion
Exploring renewable energy is one of the greatest challenges for the sustainable development of contemporary society.Advanced energy conversion systems such as photovoltaic electrodes, catalysis, and fuel cell, will play a crucial role in the future [223].For example, photovoltaic devices such as silicon solar cells have been commercialized on a large scale and dominate the market in China, and perovskite solar cells (PSCs) are attracting increasing attention.Additionally, several common and classical catalysis reactions including hydrogen evolution reaction (HER), oxygen evolution reaction (OER), carbon dioxide reduction reaction (CO 2 RR) and nitrogen reduction reaction (NRR) have also been widely investigated in the past decades [224].

Perovskite Solar Cells
Compared with silicon solar cells, PSCs possess the advantages of low cost, high absorption coefficient, easy preparation and high theoretical photoelectric conversion efficiency (PCE).In recent years, a high PCE value of 25.7% can be obtained for PSCs, which makes PSCs become one of the most promising photovoltaic devices in the near future [225].However, defective interfaces and grain boundaries of PSCs greatly deteriorate device performance [226].Recently, MXenes have been intensively researched in PSCs as additive, electrode or hole/electron transport layer owing to their high electrical conductivity and carrier mobility, adjustable work function, abundant surface functional groups and excellent mechanical property [227].In 2021, Zhou et al. synthesized Ti 3 C 2 Cl x MXene suspension via CdCl 2 etching and following IPA intercalation, and the Ti 3 C 2 Cl x MXene as addictive is then incorporated into the bulk and surface of perovskite film (Fig. 15a-b) [159].The peak shift in Pb 4f XPS spectrum indicates that the -Cl surface group with strong electron-withdrawing ability in Ti 3 C 2 Cl x MXene and the unsaturated Pb 2+ in CsPbBr 3 can form Pb-Cl bond along the interface (Fig. 15c).The strong interaction between Ti 3 C 2 Cl x MXene and CsPbBr 3 can effectively relieve the lattice strain of perovskite (Fig. 15d), and the defects situated at the interface and grain boundaries can be healed.Therefore, a high PCE of 11.08% and open-circuit voltage of 1.702 V can be obtained for the fabricated all-inorganic CsPbBr 3 PSCs.More importantly, the Ti 3 C 2 Cl x -functionalized CsPbBr 3 devices exhibit outstanding long-term stability of 100 days under 80% relative humidity and 25 °C (Fig. 15e), demonstrating the high-quality of perovskite films.
Later, Ti 3 C 2 Cl x quantum dots (Ti 3 C 2 Cl x QDs) with an average size of around 8 nm were prepared through CuCl 2 etching, subsequent hydrothermal reaction and ultrasonication treatment (Fig. 15f) [228].As followed, the Ti 3 C 2 Cl x QDs is introduced into the precursor solution to fabricate perovskite layer via one-step processing.Similarly, the -Cl functional groups in Ti 3 C 2 Cl x QDs can generate chemical bond with Pb 2+ cations in Rb 0.05 Cs 0.05 (FA 0.83 MA 0.17 ) 0.90 Pb(I 0.83 Br 0.17 ) 3 perovskite compound, which can also be confirmed by the peaks move in Pb 4f and Cl 2p XPS spectra.Additionally, scanning electron microscopy (SEM) images demonstrate that the perovskite grain size can be enlarged from 273 to 453 nm after the addition of Ti 3 C 2 Cl x QDs (Fig. 15g), reducing the number of grain boundary.The introduction of Ti 3 C 2 Cl x QDs acting as nucleation sites can effectively slow down the growth of perovskite crystal and the film crystallinity can be greatly enhanced with an optimized orientation, thus leading to fewer crystal distortion.Moreover, the interfacial charge transfer resistance between perovskite layer and SnO 2 electron transport layer can be greatly reduced owing to the highly conductive Ti 3 C 2 Cl x , and the energy level alignment can be further improved (Fig. 15h).Consequently, the Ti 3 C 2 Cl x QDs-modified device can deliver a high PCE value of 21.31% and an open-circuit voltage of 1.19 V (Fig. 15i).Furthermore, the extraordinary long-term stability with 84% PCE retention after 1000 h storage time under 40% relative humidity can be afforded for Ti 3 C 2 Cl x QDs-modified device (Fig. 15j).The two works indicate that the Cl-terminated MXenes prepared by Lewis acidic etching has great potential to enhance the performance of PSCs devices.

Hydrogen Evolution Reaction
H 2 is regarded as a clean and renewable energy source that can replace fossil fuels in the future owing to its high heat value and pollution-free combustion product.The HER is an effective method to produce high-purity H 2 via water splitting [229].Some noble catalysts such as Au, Pt and Pd have been widely used to accelerate the H 2 evolution kinetics and decrease overpotentials because of their high activities [230].Nevertheless, high price and low reserve greatly impede the large-scale application of noble catalysts.In recent years, MXenes have been considerably researched as catalyst derived from their 2D layered structure, tailorable surface chemistry, diverse composition, high electrical conductivity and superior mechanical stability [231,232].Particularly, the polar terminations of MXenes can strongly interact with other materials to form high-performance catalysts.For example, Jiang et al. firstly synthesized Ti 3 CNCl 2 MXene via NiCl 2 molten salt etching of Ti 3 AlCN MAX.Then, Ti 3 CNCl 2 @CoS 2 core-shell architecture as efficient HER catalyst can be obtained by hydrothermal reaction [233].Theoretical calculations reveal that electron can transfer from Ti 3 CNCl 2 MXene to CoS 2 through -Cl functional group, demonstrating strong interaction between them.Additionally, the Gibbs free energy of H 2 adsorption of Ti 3 CNCl 2 @CoS 2 hybrids is close to zero, indicating a strong catalytic activity.It is noteworthy that the electrons of Ti 3 CNCl 2 @CoS 2 become more delocalized, which suggests that H + cations are easy to combine with electrons.As a result, benefiting from the synergistic effect of CoS 2 and highly-conductive Ti 3 CNCl 2 , the constructed Ti 3 CNCl 2 @ CoS 2 hybrids deliver a low Tafel slope of 89 mV dec −1 and small charge transfer resistance in 0.5 M H 2 SO 4 electrolyte.Moreover, boosted long-term stability can be obtained for Ti 3 CNCl 2 @CoS 2 , which can sustain catalytic activity for 10 h and the current density shows almost no attenuation.

Overall Water Splitting
Water splitting provides a simple, effective and promising method for H 2 and O 2 production, which can effectively solve the energy crisis [234].In general, electrolysis of water is composed of HER at the cathode and the OER at the anode and requires a theoretical voltage of 1.23 V [235].Nevertheless, the multi-electron reaction results in sluggish kinetics, which greatly limits the H 2 and O 2 production and increases the drive voltage [236].Exploring high-performance electrocatalysts can effectively solve the above-mentioned issues.For example, Sarfraz et al. reported the synthesis of Clterminated Ti 3 C 2 Cl 2 MXene via CuCl 2 etching of Ti 3 AlC 2 precursor in 2022, and Ti 3 C 2 Cl 2 MXene with obvious lamellar structure is then used as catalyst for water splitting in 1 M KOH solution [237].Compared with Ti 3 C 2 T x MXene obtained by HF etching (HF-Ti 3 C 2 T x MXene), Ti 3 C 2 Cl 2 MXene possesses an enlarged interlayer spacing, more active sites and stable architecture.Therefore, Ti 3 C 2 Cl 2 electrode shows a smaller overpotential of 330 mV than HF-Ti 3 C 2 T x MXene (390 mV) at 30 mA cm −2 for OER.Similarly, a lower HER overpotential of 259 mV can be obtained for Ti 3 C 2 Cl 2 at 10 mA cm −2 , while HF-Ti 3 C 2 T x MXene demonstrates a large overpotential of 444 mV at the same current density.Notably, Ti 3 C 2 Cl 2 electrode exhibits a low Tafel slope of 48 and 92 mV dec −1 for OER and HER, respectively, indicating excellent catalytic activity for water splitting.

Carbon Dioxide Reduction Reaction
In recent years, the depletion of fossil fuels has produced a large amount of CO 2 , leading to a huge impact on the environment, such as greenhouse effect and the extinction of some species [238].Therefore, it is necessary to reduce CO 2 emission or find effective ways to use it.The CO 2 RR is an effective and green method to convert CO 2 into high-value chemicals or fuels [239].However, CO 2 RR suffers from sluggish kinetics owing to the good stability of CO 2 , and efficient catalysts are therefore required [240].In 2021, Zhao et al. synthesized single atom Cu immobilized Ti 3 C 2 Cl x MXene (SA-Cu-MXene) as CO 2 RR electrocatalyst via ZnCl 2 molten salt etching of Ti 3 (Al 1−x Cu x )C 2 MAX (Fig. 16a) [158].It is worth mentioning that the Cu atoms can be well preserved during the selective etching process.The content of Cu single atoms is approximately to be 1.0 wt% and many bright dots representing Cu atoms can be observed in HAADF-STEM image (Fig. 16b).Additionally, XAS measurement indicates that Cu atoms are coordinated by -O surface groups of Ti 3 C 2 Cl x MXene via Cu-O bond (Fig. 16c).Owing to the superior charge transfer kinetics of MXene and unsaturated electronic structure of Cu atoms, the obtained catalyst can greatly reduce the energy barrier from CO 2 to CH 3 OH and deliver a maximum Faradaic efficiency value of 59.1% at −1.4 V (Fig. 16d-e), demonstrating outstanding catalytic capability.More importantly, a high Faradaic efficiency of over 58% can still be obtained after 30 h, which indicates enhanced stability.Haber-Bosch process, which requires to be carried out under high temperature and pressure (300-500 °C and 150-200 atm) [241].In short, Haber-Bosch process not only consumes huge energy but also releases plenty of greenhouse gases into the atmosphere.The electrocatalytic NRR has attracted intensive attention as a green method to produce NH 3 at room temperature and atmospheric pressure [242].Nevertheless, promising electrocatalysts with superior stability and high activity are also required to promote the NRR process, which suffers from a large overpotential and low yield of NH 3 owing to the strong N≡N bond in N 2 [243].For example, Wang et al. prepared highly dispersed Fe immobilized in fluorine-free Ti 3 C 2 T x MXene (HD-Fe-MXene) as NRR electrocatalyst in 0.1 M Na 2 SO 4 electrolyte through FeCl 2 etching and HCl washing (Fig. 16f) [244].The XRD pattern indicates that the formed Fe nanoparticles can be eliminated by HCl, and energy-dispersive spectroscopy and XPS analysis demonstrate that the remaining Fe atoms with a content of 3.12 wt% are highly anchored on the surface of Ti 3 C 2 T x MXene via Fe-O bond.Benefiting from the rich active sites and outstanding electrical conductivity of Fe atoms and fluorine-free Ti 3 C 2 T x MXene, the adsorption and activation of N 2 as well as charge transfer kinetics can be considerably improved.Consequently, the obtained electrocatalyst can afford a high NH 3 yield of 18.25 µg h −1 mg −1 and a Faradaic efficiency of 21.8% (Fig. 16g).Additionally, boosted stability with almost unchanged current density after 24 h testing can be obtained for HD-Fe-MXene electrode.

Sensors
In modern society, sensors play an increasingly significant role in environmental protection, disease detection and industrial production, etc.Currently, there are different types of sensors, such as gas sensors, biosensors and sound sensors [245].Owing to the medium specific surface area, layered structure, rich active sites and superior electronic conductivity, MXenes have been regarded as promising sensitive materials in recent years [44].For example, Wu et al. synthesized Ti 3 C 2 Cl 2 MXene via ZnCl 2 etching in 2021 and investigated its gas-sensing performance [246].They found that Ti 3 C 2 Cl 2 MXene exhibits a response value of 13.2% to NH 3 , indicating the potential of Ti 3 C 2 Cl 2 MXene in gas sensors.In addition, Au/Pt/Ti 3 C 2 Cl 2 hybrids as sensors were fabricated by ZnCl 2 etching and subsequent self-reduction process (Fig. 17a) [247].The Ti species with low-valence can effectively reduce Au 3+ and Pt 4+ cations to Au and Pt nanoparticles, respectively, which are then distributed on the surface of Ti 3 C 2 Cl 2 nanosheets (Fig. 17b).By virtue of the superior catalytic activity of obtained Au/Pt/Ti 3 C 2 Cl 2 composites, a colorimetric sensing platform is constructed to in-situ detect the H 2 O 2 from HeLa cells.The fabricated sensor possesses a wide detection range of 50-10,000 μM and detection limit of 10.24 μM (Fig. 17c), demonstrating promising application in intracellular biosensing.

Microwave Absorption
With the rapid development of information technology in recent years, smart devices based on electromagnetic wave have been utilized more and more frequently, thus resulting in increasingly serious electromagnetic pollution [248,249].Therefore, exploring advanced microwave absorption materials is becoming increasingly important.MXenes demonstrate great potential in the fields of microwave absorption based on the following aspects: (1) The layered architecture can realize multiple reflection and scattering of electromagnetic wave; (2) The high electronic conductivity endows MXenes with high dielectric loss; (3) The surface groups of MXenes will produce dipole under electromagnetic field, which further strengthens the dielectric loss [52].It is noteworthy that MXenes/metal hybrids obtained by one-step Lewis acidic etching can exhibit good microwave absorption performance due to the addition of ferromagnetic metals.For example, Wang et al. firstly prepared Ti 3 CNCl 2 (Co) hybrids via CoCl 2 etching, and Ti 3 CNCl 2 (Co) composites were then distributed on the surface of reduced graphene oxide (RGO) nanosheets to form Ti 3 CNCl 2 -decorated RGO aerogel via the crosslinking effect of dopamine hydrochloride (Fig. 17d) [250].Benefiting from the conductivity loss of 3D interconnecting conductive network, improved polarization loss of abundant heterogeneous interfaces and surface functional groups as well as magnetic loss of Co nanoparticles, the Ti 3 CNCl 2 /RGO aerogel can deliver a minimum reflection loss intensity of -62.62 dB at 17.2 GHz with a thickness of 2.5 mm (Fig. 17e), indicating its boosted microwave absorbing ability.
Table 3 provides an overall summary of the performance of MXenes and MXene-based materials in the fields of LIBs, SIBs, ZIBs, Li-S batteries, metal anodes, DIBs, SCs, PSCs, HER, overall water splitting, CO 2 RR, NRR, sensors and microwave absorption.

Summary and Perspectives
In the past eleven years, great progress has been achieved in the development of MXenes, which can be effectively confirmed by the increasing publications.Notably, the compositional and structural diversity of MXenes have been considerably expanded.In terms of composition, M-site atoms, X-site atoms and surface groups all exhibit rich selection space.Structurally, i-MXenes, o-MXenes and high-entropy MXenes have also been extensively explored.It can be anticipated that if an efficient and general preparation method is applied, plenty of new MXenes with various compositions and structures can be successfully obtained, and they may demonstrate some fascinating properties.Therefore, exploring a safe, green, non-hazardous, low-cost and easily scalable synthesis method has always been the research focus in the MXene community.Up to now, many preparation strategies for MXenes have been proposed, such as HF etching, in-situ HF etching, bifluoride salts etching, electrochemical etching, alkali etching, common molten salts etching, ionic liquids etching, halogen etching and chemical vapor deposition.Nevertheless, they all have their own shortcomings and are unsuitable for large-scale application (Table 1).For example, HF etching, in-situ HF etching and alkali etching all exhibit high or medium experimental risk.Additionally, bifluoride salts etching, alkali etching, common molten salts etching, ionic liquids etching and halogen etching demonstrate poor universality.More importantly, the MXenes prepared by above-mentioned methods fail to demonstrate controllable and uniform terminations.Lewis acidic etching, as an emerging preparation strategy for MXenes, has attracted increasing attention in the past three years owing to a series of merits, such as significantly boosted safety, superior generality, the ability to endow MXenes with uniform surface groups and the potential for large-scale application.In this review, we have systematically introduced the Lewis acidic molten salts etching strategy from four aspects: etching mechanism, terminations regulation, in-situ formed metals and delamination of multi-layered MXenes.Briefly, the etching mechanism is mainly based on the replacement reaction between metal cations in Lewis acidic molten salts and zero-valence A-site atoms in MAX precursor.The difficulty degree of etching reaction mainly depends on the redox potentials of molten cations and A-site atoms, but has nothing to do with the M, X-site atoms and n value in MAX phase.A simple criterion is that the metal cations in Lewis acidic salts with high redox potentials can readily etch the MAX phases with low redox potential A-site atoms.Accordingly, some nitride MAX including Ti 2 AlN and Ti 4 AlN 3 and non-Al MAX such as Ti 3 SiC 2 and Ta 2 GaC with high exfoliation energy can be successfully etched by various Lewis acidic molten salts.Additionally, uniform Cl, Br or I-terminated MXenes is able to be obtained by Lewis acidic etching, and they all exhibit metallic-level conductivities and even superconductivity in the low-temperature summarized.Up to now, most applications are concentrated in the fields of energy storage and conversion.However, the development of Lewis acidic etching is still in its infancy, and more efforts are required to fully understand this method and promote its widespread application.Some main challenges and opportunities are listed as follows: (1) At present, there are still some details to be researched during the Lewis acidic etching process.For example, the reaction between metal cations in Lewis acidic molten salts and M species in MAX phase during the etching process has been confirmed, which generally results in the formation of single atom-implanted MXenes.However, the specific mechanism and the difficulty degree of above reaction still require further exploration through a lot of experiments and theoretical calculations, which is conducive to the controlled preparation of single atom-implanted MXenes.In addition, a recent study has proved that NaCl can not only provide molten salts environment during the etching process, but also act as pore-forming agent to form Ti 3 C 2 Cl 2 MXene with in-plane porosity.In the future, more attention should be paid to investigate the universality of NaCl as pore-forming agent, which can greatly promote the preparation of other in-plane porous MXenes through Lewis acidic etching.Notably, the in-situ formed metal nanoparticles are usually aggregated during the cooling process and then anchor on the surface of MXenes.It is unclear whether there are some metal clusters in the interlayer of MXenes.Furthermore, preventing the agglomeration of metal nanoparticles is also worth investigating.(2) In the future, more researches should be carried out to synthesize nitride MXenes via Lewis acidic etching.
It can be expected that more nitride MXenes will be successfully prepared due to the superior universality of Lewis acidic etching.Currently, Lewis acidic molten salts are mainly used to etch MAX phase precursors.
The future studies are needed to investigate that whether non-MAX ternary layered compounds such as Mo 2 Ga 2 C can be etched by Lewis acidic salts.Further, transition metal borides (MAB) such as MoAlB and Cr 2 AlB 2 , which is similar to MAX phase, have attracted intensive interests in the past few years.Therefore, the universal preparation of MBene by etching MAB precursors with Lewis acidic molten salts is worthy of in-depth investigation.Finally, the parameters of Lewis acidic etching reaction, including the molar ratio of MAX precursor and Lewis acidic salts, reaction temperature, time and atmosphere, are widely different in reported literatures (Table 2).More efforts are still required to optimize the etching parameters on the premise of ensuring the successful preparation of MXenes, such as selecting low-cost Lewis acidic salts, decreasing the amount of Lewis acidic salts and reaction temperature and changing the reaction atmosphere from protective gas to air, which is beneficial for the large-scale preparation of MXenes via Lewis acidic etching.(3) Although MXenes prepared by Lewis acidic etching can be theoretically terminated by uniform halogen groups, some halogen terminations will inevitably be replaced by -O in air atmosphere or during the washing process.
In addition, the surface group substitution/elimination reactions in molten inorganic salts are carried out in Ar-filled glovebox in order to avoid the competition between -O functional group and other terminations.
In the future, it is an urgent issue to maintain uniform termination for MXenes obtained by Lewis acidic etching under air atmosphere.All in all, combined with Lewis acidic etching, termination exchange reaction in Lewis bases molten salts medium can indeed endow MXenes with unconventional terminations.Therefore, much work should be needed to explore the influence of new terminations (S, Se, Te, N, NH, etc.) on the properties of various MXenes, such as electronic, optical and mechanical, magnetic properties as well as ion migration kinetics, hydrophilicity, chemical and thermal stability, etc.
1 3 (4) So far, MXenes/metals hybrids prepared by Lewis acidic etching have been successfully applied in LIBs and SCs.In the future, MXenes/metals composites exhibit great research potential in catalysis, metal anodes and other fields.For example, benefiting from the unique layered structure and superior charge/mass transfer kinetics of MXenes as well as nucleation induction effect of some metals (Co, Sn, etc.), MXenes/metals hybrids can be utilized as threedimensional frameworks to suppress the dendrite growth of metal anodes (Li, Na, K, Zn, etc.).Furthermore, the obtained MXenes/metals hybrids can be transformed to MXenes/metal compounds composites via one-step sulfurization, phosphorization, selenization or tellurization treatment.Currently, most of the research was concentrated in MXenes/metal sulfides hybrids, such as N-MX-CoS 2 and Ti 3 C 2 T x /FeS 2 .In the future, more studies should be performed to prepare MXenes/metal phosphides, MXenes/metal selenides or MXenes/metal tellurides hybrids via Lewis acidic etching route, which can be rationally and effectively applied in LIBs, SIBs, potassium-ion batteries and so on.(5) Up to now, most of MXenes prepared by Lewis acidic etching are still at multi-layered state (Table 2).The absence of hydrophilic terminations such as -OH makes it difficult for the obtained multi-layered MXenes to be dispersed in water and then intercalated by large organic molecules, thus reducing the delamination efficiency and exhibiting a low yield of few-layered and single-layered nanosheets.Although some attempts have been made, such as improving the hydrophilicity of MXenes by KOH treatment, or intercalating MXenes by n-BuLi in organic solvent NMF, there is still no safe, green, efficient and easily scalable method to delaminate the Lewis acidic molten salts-etched multi-layered MXenes.In the future, great efforts should be made to explore other appropriate delamination methods, such as high-energy ball milling and electrochemical delamination.
In conclusion, although some progress has been made in the development of Lewis acidic etching, it is still in the early stage.In order to solve the above-mentioned challenges, much more work should still be done in the near future.It can be anticipated that Lewis acidic etching will experience a rapid development period, which can attract more and more researchers in MXene community to widely utilize this emerging preparation strategy.

Fig. 1 a
Fig. 1 a Element composition of MAX phase.Reproduced with permission from [16] Copyright 2022, Elsevier.b Schematic illustration of the preparation of various MXenes from corresponding MAX phases.Reproduced with permission from [26] Copyright 2021, Wiley-VCH.c The annual published article numbers of MXenes.d Schematic of s-MXenes, i-MXenes and o-MXenes

Fig. 2
Fig. 2 Schematic illustration of the structural, compositional and property diversity of MXenes

Fig. 3 a
Fig. 3 a Annual publications of Lewis acidic etching method.b Application ratio of MXenes and MXene-based composites prepared by Lewis acidic etching route in different fields.c A timeline showing the development progress of Lewis acidic etching route.Image published in 2019.03:Reproduced with permission from [66] Copyright 2019, American Chemical Society.Image published in 2020.04:Reproduced with permission from [67] Copyright 2020, The Authors, published by Springer Nature.Image published in 2020.06:Reproduced with permission from [157] Copyright 2020, Wiley-VCH.Image published in 2020.07:Reproduced with permission from [42] Copyright 2020, The American Association for the Advancement of Science.Image published in 2021.08:Reproduced with permission from [112] Copyright 2021, The Authors, published by Springer Nature.Image published in 2021.09:Reproduced with permission from [122] Copyright 2021, Wiley-VCH.Image published in 2022.08:Reproduced with permission from [147] Copyright 2022, Wiley-VCH.Image published in 2022.11:Reproduced with permission from [126] Copyright 2022, The Authors, published by Wiley-VCH

Fig. 5 a
Fig. 5 a Schematic showing the preparation of multi-layered Ti 3 C 2 T x MXene by HF etching.Reproduced with permission from [70] Copyright 2022, American Chemical Society.b SEM image of multi-layered Ti 3 C 2 T x MXene.Reproduced with permission from [72] Copyright 2020, Springer Nature.c SEM image of single-layered Ti 3 C 2 T x MXene.Reproduced with permission from [82] Copyright 2021, American Chemical Society.d Schematic exhibiting the reaction mechanism between Ti 3 AlC 2 and bifluorides.Reproduced with permission from [93] Copyright 2016, Elsevier.e Schematic of the electrochemical etching of Ti 3 AlC 2 MAX in a binary aqueous electrolyte.Reproduced with permission from [98] Copyright 2018, Wiley-VCH.f Schematic of synthesis of Ti 3 C 2 T x MXene by NaOH-assisted hydrothermal method.Reproduced with permission from [101] Copyright 2018, Wiley-VCH.g Synthesis of Mo 2 N and V 2 N MXene via ammoniation strategy.Reproduced with permission from [105] Copyright 2017, Royal Society of Chemistry.h Schematic diagram showing the preparation of Ti 3 C 2 T x MXene via iodine-assisted etching.Reproduced with permission from [108] Copyright 2021, The Authors, published by Wiley-VCH

Fig. 6 a
Fig. 6 a Schematic showing the preparation of Ti 3 C 2 Cl 2 MXene by ZnCl 2 Lewis acidic salt etching.b XRD patterns of Ti 3 AlC 2 and Ti 3 ZnC 2 MAX.c HAADF-STEM image of Ti 3 ZnC 2 MAX and corresponding energy-dispersive spectroscopy (EDS) mapping.d SEM image of multilayered Ti 3 C 2 Cl 2 MXene.e XRD patterns of Ti 3 C 2 Cl 2 MXene and Ti 3 C 2 Cl 2 /Zn hybrids.f Cl 2p XPS spectra of Ti 3 C 2 Cl 2 MXene.g EDS mapping analysis showing the Lewis acidic etching of Ti 3 AlC 2 MAX.Reproduced with permission from [66] Copyright 2019, American Chemical Society.h Schematic demonstrating the preparation of Ti 3 C 2 T x MXene by CuCl 2 etching.i Schematic showing the relationship between redox potential of A-site elements, redox potential of Lewis acidic salts and Gibbs free energy.Reproduced with permission from [67] Copyright 2020, The Authors, published by Springer Nature.j Schematic illustration of the one-pot synthesis of Ti 3 C 2 T x MXene under air atmosphere.Reproduced with permission from [112] Copyright 2021, The Authors, published by Springer Nature.k Phase diagram of NaCl/ZnCl 2 mixture.Reproduced with permission from [113] Copyright 2021, Wiley-VCH

Fig. 7 a
Fig. 7 a-b HAADF-STEM images and corresponding EDS mapping of Ti 3 C 2 Br 2 and Ti 3 C 2 I 2 MXene, respectively.c Electronic structure of Ti 3 C 2 Br 2 MXene.Reproduced with permission from [123] Copyright 2021, American Chemical Society.d Schematic showing the preparation of Ti 3 C 2 T x MXene via Lewis acidic etching and subsequent termination substitution in molten inorganic salts as well as corresponding HAADF-STEM images and EDS analysis.e Biaxial straining of Ti 3 C 2 T x MXene lattice induced by the terminations.f Temperature-dependent resistivity of Nb 2 CT x MXenes.Reproduced with permission from [42] Copyright 2020, The American Association for the Advancement of Science.g Schematic of the preparation of N-containing Ti 3 C 2 T x MXene via FeCl 2 Lewis acidic salt etching.h EELS analysis of pristine Ti 3 C 2 T x and N-containing Ti 3 C 2 T x MXene.Reproduced with permission from [126] Copyright 2022, The Authors, published by Wiley-VCH

Fig. 8 a
Fig. 8 a Schematic illustration of the synthesis of Ti 3 C 2 -Cu/Co composites.b XAS spectra of Ti 3 C 2 -Cu hybrids.Reproduced with permission from [122] Copyright 2021, Wiley-VCH.c Schematic showing the preparation of Ti 3 C 2 T x /Sn composites by SnCl 2 Lewis acidic salt etching.d SEM image of Ti 3 C 2 T x /Sn hybrids.Reproduced with permission from [145] Copyright 2022, Elsevier.e Schematic diagram of the preparation of Ti 3 C 2 T x /CuS composites.f High-resolution transmission electron microscope (HRTEM) image of Ti 3 C 2 T x /CuS.Reproduced with permission from [148] Copyright 2022, Royal Society of Chemistry

Fig. 9 a
Fig. 9 a Schematic of the synthesis of KOH-treated few-layered Ti 3 C 2 T x MXene nanosheets.b Transmission electron microscope (TEM) image of Ti 3 C 2 T x nanosheets.Reproduced with permission from [154] Copyright 2021, The Authors.c Schematic of the intercalation and delamination process.d Zeta potential of Ti 3 C 2 Cl 2 MXene in NMF and inset representing the high concentrated MXene inks in NMF and N 2 H 4 .e Digital photographs of stable colloidal solutions of Ti 3 C 2 T x MXenes (T = -Cl, -NH and -S) in NMF showing Tyndall effect.f TEM image of Ti 3 C 2 Cl 2 MXene nanosheets and inset showing its selected area electron diffraction (SAED) pattern.g XRD patterns of multi-layered and delaminated Ti 3 C 2 Cl 2 MXene.Reproduced with permission from [42] Copyright 2020, The American Association for the Advancement of Science

Fig. 10 a
Fig. 10 a Valence electron localization function of Ti 3 C 2 O 2 Li 2 with or without an extra Li layer.Reproduced with permission from [120] Copyright 2014, American Chemical Society.b Rate performance of Nb 2 CT x MXene.c Long-term cyclic performance of Nb 2 CT x MXene.Reproduced with permission from [119] Copyright 2021, Wiley-VCH.d CV curves of Ti 2 CT x and Ti 3 C 2 T x MXene.Reproduced with permission from [112] Copyright 2021, The Authors, published by Springer Nature.e SEM image of Ti 3 C 2 T x MXene prepared from 60 batch of Ti 3 AlC 2 MAX.f Specific capacities of Ti 3 C 2 T x , Ti 2 CT x and Ti 3 CNT x MXene at various C-rates.Reproduced with permission from [175] Copyright 2022, Zhengzhou University.g Elemental composition comparison of Ti 3 C 2 F x , Ti 3 C 2 Cl x and Ti 3 C 2 Br x MXenes.h Long-term cyclic performance of Ti 3 C 2 F x , Ti 3 C 2 Cl x and Ti 3 C 2 Br x MXenes at 1 A g −1 .Reproduced with permission from [178] Copyright 2022, Elsevier.i TEM image of Ti 3 C 2 T x /Sn anode after 2200 cycles.Reproduced with permission from [145] Copyright 2022, Elsevier

Fig. 11 a
Fig. 11 a Schematic of the fabrication process of Ti 3 C 2 T x /MS y hybrids.b XRD pattern of Ti 3 C 2 T x /FeS 2 composites.c SEM image of Ti 3 C 2 T x / FeS 2 hybrids.d HRTEM image of Ti 3 C 2 T x /FeS 2 .e O 1 s XPS spectra of Ti 3 C 2 T x /FeS 2 .f Charge density difference of Ti 3 C 2 T x /FeS 2 composites.g Cyclic performance of Ti 3 C 2 T x MXene and Ti 3 C 2 T x /FeS 2 hybrids at various current densities.Reproduced with permission from [147] Copyright 2022, Wiley-VCH

Fig. 12 a
Fig. 12 a Schematic diagram of the working mechanism of Zn/halogenated Ti 3 C 2 MXene cells.Reproduced with permission from [123] Copyright 2021, American Chemical Society.b In-situ Raman spectra of the Ti 3 C 2 I 2 cathode around 200 cm −1 .c CV curves of Ti 3 C 2 I 2 cathode in ZnCl 2 + KCl electrolyte or conventional ZnSO 4 electrolyte.Reproduced with permission from [194] Copyright 2021, Royal Society of Chemistry.d HAADF-STEM image of SA-Zn-MXene.e Charge density difference for Li 2 S 4 polysulfides adsorbed on SA-Zn-MXene and MXene.f Rate capabilities of S, S@MXene and S@SA-Zn-MXene.Reproduced with permission from [157] Copyright 2020, Wiley-VCH.g Schematic of the preparation process of N-MX-CoS 2 hybrids.h Adsorption test of MX-Co, MX-CoS 2 and N-MX-CoS 2 .i Galvanostatic charge-discharge curves of Li-S batteries with various materials-modified separator at 0.2C.j Long-term cyclic stability of Li-S batteries with various materialstreated separators at 1 C. Reproduced with permission from [146] Copyright 2021, Elsevier

Fig. 13 a
Fig. 13 a Schematic showing the preparation of Zn-MXene for Li nucleation and growth.b HAADF-STEM image of Zn-MXene nanosheets.c-e SEM images of Zn-MXene nanosheets after Li plating with capacities of 5, 20 and 60 μAh cm −2 , respectively.Reproduced with permission [156] Copyright 2020, American Chemical Society.f Calculated atomic distance between Zn atom and neighboring halogen termination as well as Zn adsorption energies of different MXene surfaces.g SEM image and EDS mapping of the Ti 3 C 2 Cl 2 -Zn electrode after cycling.h Longterm cyclic performance of various symmetric cells.i Schematic diagram of the Zn deposition process on the MXene substrate.Reproduced with permission from [212] Copyright 2021, American Chemical Society

Fig. 14 a
Fig. 14 a Schematic showing the preparation of in-plane porous Ti 3 C 2 Cl 2 MXene via eutectic etching.b N 2 adsorption-desorption isotherms of various MXenes.TEM images of Ti 3 C 2 Cl 2 MXene obtained by eutectic etching with c 0%, d 33% and e 60% NaCl mole percent in the NaCl/ ZnCl 2 mixture.f Rate performance of Ti 3 C 2 Cl 2 -60/graphite DIBs.Reproduced with permission from [113] Copyright 2021, Wiley-VCH.g Schematic demonstrating the preparation of MXene-NaCl and MXene-CTAB.h XRD patterns of MXene, MXene-NaCl and MXene-CTAB.Reproduced with permission from [219] Copyright 2021, Elsevier.i HRTEM image of QD-Ti 3 C 2 Cl 2 @NiAl-LDHs composites.j The free energy diagram of pseudocapacitive process on the QD-Ti 3 C 2 Cl 2 @NiAl-LDHs.k Specific capacities of the various electrodes at different current densities.Reproduced with permission from [222] Copyright 2021, Elsevier

Fig. 15 a
Fig. 15 a Schematic showing the preparation of Ti 3 C 2 Cl x MXene.b Cross-sectional SEM image of all-inorganic PSCs.c Pb 4f XPS spectra of CsPbBr 3 perovskite film.d Schematic of released strain in the CsPbBr 3 grains with Ti 3 C 2 Cl x MXene.e Long-term stability of the devices in air under 80% relative humidity and 25 °C.Reproduced with permission from [159] Copyright 2021, The Authors, published by Wiley-VCH.f Schematic demonstrating the preparation of Ti 3 C 2 Cl x QDs.g SEM images of pristine and Ti 3 C 2 Cl x QDs-modified perovskite films.h Schematic illustration of the perovskite-Ti 3 C 2 Cl x QDs-SnO 2 heterojunction.i Reverse and forward scans for the pristine and Ti 3 C 2 Cl x QDs-modified devices.j Normalized PCEs against storage time for the pristine and Ti 3 C 2 Cl x QDs-treated devices.Reproduced with permission from [228] Copyright 2021, Elsevier

NH 3 ,Fig. 16 a
Fig. 16 a Schematic of the synthesis of SA-Cu-MXene.b HAADF-STEM image of SA-Cu-MXene.c XAS spectra of SA-Cu-MXene.d Free energy diagram of CO 2 to CH 3 OH.e Faradaic efficiency of SA-Cu-MXene at various potentials.Reproduced with permission from [158] Copyright 2021, American Chemical Society.f Schematic of the preparation of HD-Fe-MXene.g Faradaic efficiency of different materials at various potentials.Reproduced with permission from [244] Copyright 2022, The Authors, published by Wiley-VCH

Fig. 17 a
Fig. 17 a Schematic demonstrating the synthesis of Au/Pt/Ti 3 C 2 Cl 2 hybrids for in-situ detection of H 2 O 2 and colorimetric detection of glutathione.b EDS element mapping of Au/Pt/Ti 3 C 2 Cl 2 composites.c Absorption spectra of Au/Pt/Ti 3 C 2 Cl 2 nanocomposites system with increasing concentrations of H 2 O 2 .Reproduced with permission from [247] Copyright 2022, Elsevier.d Schematic representing the preparation of Ti 3 CNCl 2 /RGO aerogel.e Reflection loss of Ti 3 CNCl 2 /RGO.Reproduced with permission from [250] Copyright 2021, Elsevier al. removed M-atom and A-atom layers from Ti 3 AlC 2 , Ti 2 AlC and Ti 3 SiC 2 MAX precursors to prepare carbide-derived carbons via electrochemical etching approach [95].In 2015, Zhao et al. selectively extracted Ti atom layers (6) Ti 3 AlC 2 + 3NH 4 HF 2 = NH 4 3 AlF 6 + Ti 3 C 2 + 1.5 H 2 , which further enriches the family of nitride MXenes.
et al. etched Ti 3 AlC 2 by CuCl 2 •2H 2 O or CoCl 2 •6H 2 O Lewis acidic salts 3− and NH 2 − , researchers can obtain the desired surface groups-terminated MXenes.The above discussions fully reveal the great potential of the halogenated MXenes synthesized by Lewis acidic etching method in various fields.Taking consideration of the rich selection of M and 3 C 2 T x /Cu composites prepared by mechanical mixing, which is another key advantage of Lewis acidic etching method relative to traditional etching route.Recently, it has been reported that when the Ti 3 AlC 2 MAX precursor is etched by CuCl 2 •2H 2 O or CoCl 2 •6H 2 O, the obtained Ti 3 C 2 T x MXene can be decorated with Cu or Co nanoparticles (Fig.

Table 1
Comparison of non-Lewis acidic etching techniques and Lewis acidic etching routes

Table 2
The specific parameters for the preparation of various MXenes via Lewis acidic etching

Table 3
Summary of the performance of MXenes and MXene-based materials prepared by Lewis acidic etching route .These redox-active groups-terminated MXenes have been investigated in SCs and advanced batteries.More importantly, halogen groups such as -Cl and -Br can be substituted by S 2− , Se 2− , Te 2− , N 3− and NH 2 − anions from Lewis bases molten salts via nucleophilic reaction owing to the low dissociation energies of Ti-Br and Ti-Cl bond, really realizing the controllable terminations.Further, the in-situ generated metal nanoparticles can be tightly anchored among the MXenes substrate during the etching process.The rational and effective application of MXenes/metals and onestep sulfidation treatment-obtained MXenes/metal sulfides composites in LIBs, SIBs, Li-S batteries, SCs and HER have been demonstrated.Subsequently, the multi-layered MXenes obtained by Lewis acidic etching have been delaminated into few-layered nanosheets via n-BuLi, IPA, TBAOH, DMSO or i-PrA intercalation.Finally, the application of obtained MXenes and MXene-based hybrids via Lewis acidic etching route in LIBs, SIBs, ZIBs, Li-S batteries, metal anodes, DIBs, SCs, PSCs, HER, overall water splitting, CO 2 RR, NRR, sensors and microwave absorption have been carefully region