Architecture Design and Interface Engineering of Self-assembly VS4/rGO Heterostructures for Ultrathin Absorbent

The employment of microwave absorbents is highly desirable to address the increasing threats of electromagnetic pollution. Importantly, developing ultrathin absorbent is acknowledged as a linchpin in the design of lightweight and flexible electronic devices, but there are remaining unprecedented challenges. Herein, the self-assembly VS4/rGO heterostructure is constructed to be engineered as ultrathin microwave absorbent through the strategies of architecture design and interface engineering. The microarchitecture and heterointerface of VS4/rGO heterostructure can be regulated by the generation of VS4 nanorods anchored on rGO, which can effectively modulate the impedance matching and attenuation constant. The maximum reflection loss of 2VS4/rGO40 heterostructure can reach − 43.5 dB at 14 GHz with the impedance matching and attenuation constant approaching 0.98 and 187, respectively. The effective absorption bandwidth of 4.8 GHz can be achieved with an ultrathin thickness of 1.4 mm. The far-reaching comprehension of the heterointerface on microwave absorption performance is explicitly unveiled by experimental results and theoretical calculations. Microarchitecture and heterointerface synergistically inspire multi-dimensional advantages to enhance dipole polarization, interfacial polarization, and multiple reflections and scatterings of microwaves. Overall, the strategies of architecture design and interface engineering pave the way for achieving ultrathin and enhanced microwave absorption materials.

14 16 18 1 Introduction With the advent of the 5G era, widespread applications of communication technologies and electronic devices have caused serious electromagnetic (EM) interference [1,2]. The ever-increasing demands for the elimination of EM radiation hazards have spurred significant concerns to develop microwave absorption materials [3,4]. Recently, amounts of traditional materials, such as ferrites [5], metallic magnets [6], and dielectric ceramics have been widely employed as microwave absorbents [7]. However, the inherent defects such as larger thickness, high density, and narrow effective absorption bandwidth (EAB) seriously hinder their extensive applications, which is far from fulfilling the ultrathin and enhanced goals of microwave absorbent. Additionally, the boom of flexible and miniaturized smart electronic devices is eagerly demanding ultrathin and enhanced microwave absorbent [8]. Thus, it is highly desired but remains a gigantic challenge to achieve high-performance microwave absorbent. Currently, considerable attention has been focused on the design of high-performance microwave absorbents to tackle the issues of ultra-thick thickness, high density, and imperfect absorption intensity and bandwidth [9,10]. Carbon nanostructures, including graphene [11], carbon nanotubes [12], fullerene [13], and so on, demonstrate great excellences to be designed as ultrathin and enhanced microwave absorbent because of their large specific surface area, remarkable thermal and electric conductivities, and exceptional dielectric properties [14]. Reduced oxide graphene (rGO) as a widely studied two-dimensional (2D) material possesses residual oxygen-containing functional groups and defects that can be acted as attachment sites or dipole polarization centers [15][16][17]. The pristine 2D rGO nanosheet has great potential to be designed as an ultrathin microwave absorbent but exhibits marginal microwave attenuation capability, which cannot bridge the gap of achieving enhanced microwave absorption. In order to cope with this issue, rGO microarchitectures with multiple winkles and microporous cavities are tailored and widely applied to promote microwave attenuation capability in virtue of the multiple reflections and scatterings of incident microwaves [18][19][20]. The elaborate rGO microarchitecture fully maintains the superior privileges of rGO by evading excessive stacks or agglomerations, which can greatly contribute to pursuing the ultrathin microwave absorbent [21]. For example, Pan et al. prepared hierarchical multi-dimensional carbon-based aerogels. The graphene layers were uniformly intercalated by three-dimensional (3D) helical carbon nanocoils, endowing the abundant microporous structure and better dielectric properties. The hierarchical multi-dimensional carbon-based aerogels showed the maximum reflection loss (RL) of − 55.1 dB and EAB of 5.6 GHz [18]. Gao et al. designed graphene microflowers with highly microporous architecture. The maximum RL and EAB of graphene microflowers were up to − 42.9 dB and 5.59 GHz, respectively, showing significant increment compared with the stacked graphene, which is primarily due to the ascendancy microarchitecture [22]. Dielectric losses, including dipole and interfacial polarization relaxations, are predominant in rGO microwave absorbent, whereas the pristine rGO possessing single dipole polarization relaxation is difficult to obtain multiple dielectric losses. Therefore, introducing a heterointerface to stimulate interfacial polarization relaxation of rGO-based absorbent is another smooth road to enhance microwave absorption performance. For instance, Ji et al. anchored metal oxide granular film on graphene with large surface area and high charge carrier concentrations to construct heterointerface. The prepared graphene/metal oxide exhibited the EAB of 7.0 GHz with a thickness of 2 mm because of the strong interfacial polarization relaxation [23]. He et al. successfully developed rGO/ MoS 2 nanosheets heterostructure. The prepared rGO/MoS 2 nanosheets heterostructure possessing multiple conductive networks and heterointerfaces demonstrated the EAB of 5.7 GHz and maximum RL of − 60 dB with a thickness of 2.5 mm [24]. Thence, the inspired interfacial polarization relaxation usually can endow rGO-based absorbent with enhanced microwave attenuation capability. VS 4 with a narrow bandgap of ≈1.0 eV stands out from the transition metal sulfides due to its Peierls distortions, good dielectric characteristics, and environmental benignities. Moreover, the unique chain-like VS 4 nanostructure formed by van der Waals force is easy to anchor on rGO to generate heterointerface (Fig. S1) [25]. Accordingly, motivated by the unparalleled merits of rGO microarchitecture and VS 4 nanostructure, the synergy of microarchitecture and heterointerface may provide exceptional feasibilities to achieve enhanced VS 4 /rGO microwave absorption materials.
Herein, architecture design and interface engineering strategies are implemented to prepare self-assembly VS 4 / 1 3 rGO heterostructure as ultrathin microwave absorbent. VS 4 nanorods are tightly and evenly anchored on rGO, generating abundant microarchitectures and rich heterointerfaces. The synergy of microarchitecture and heterointerface effectively modulates the impedance matching and attenuation constant of VS 4 /rGO heterostructure, thus achieving the ultrathin absorbent with enhanced microwave absorption performance. The maximum RL of 2VS 4 /rGO40 heterostructure can reach as strong as − 43.5 dB at 14 GHz and 1.5 mm with the impedance matching and attenuation constant approaching 0.98 and 187, respectively. Furthermore, the EAB of 4.8 GHz can be achieved with an ultrathin thickness of 1.4 mm. More importantly, architecture design and interface engineering significantly contribute to motivating the multi-dimensional advantages of VS 4 /rGO heterostructure. (i) The anisotropic one-dimensional (1D) VS 4 nanorods with high aspect ratio greatly facilitate dipole and interfacial polarization relaxations. (ii) 2D rGO nanosheets with VS 4 nanorods attached can effectively modulate the impedance matching and boost interfacial polarization. (iii) 3D reticulum-like microporous architecture of VS 4 /rGO heterostructure induces multiple reflections and scatterings of incident microwaves. Moreover, combining with density functional theory calculation, the effects of VS 4 /rGO heterointerface for polarization relaxation are also further investigated, inducing reinforcement in microwave absorption performance. Overall, the synergy of architecture design and interface engineering for the construction of self-assembly VS 4 /rGO heterostructure can extend the development of ultrathin microwave absorbent.

Synthesis of rGO Microarchitecture
Graphene oxide (GO) was prepared by the modified Hummers method from graphite powder. rGO architecture was synthesized by facile hydrothermal and freeze-dying methods. Typically, 80 mg of GO powder was uniformly dispersed in 60 mL deionized water by sonication of 90 min. Then, the prepared uniformly homogeneous GO dispersion was transferred into a Teflon-lined stainless autoclave and heated to 180 °C for 10 h. After cooling to room temperature and freezing in the refrigerator at − 20 °C, the frozen hydrogel was put into a vacuum freeze dryer to remove ice and acquire rGO architecture.

Synthesis of VS 4 /rGO Heterostructure
Typically, the VS 4 /rGO heterostructures were successfully performed by a facile one-step hydrothermal method. Initially, 5 mmol of Na 3 VO 4 and 25 mmol of CH 3 CSNH 2 were put into 60 mL dispersion containing 40 mg of GO under constant magnetic stirring until formed a homogeneous solution at 60 °C. Then, the mixed solution was transferred into 100 mL of Teflon-lined stainless autoclave and heated to 160 °C for 24 h. After cooling to room temperature, the product was collected and washed with deionized water three times and placed in the refrigerator at − 20 °C for 12 h. Subsequently, the frozen product was performed to remove the water of VS 4 / rGO heterostructures via a freeze-drying method. As Table S1 shows, the VS 4 /rGO heterostructures with different content of VS 4 nanorods and rGO marked as 1VS 4 /rGO40, 3VS 4 /rGO40, 2VS 4 /rGO20, and 2VS 4 /rGO60 were prepared by the same method.

Synthesis of VS 4 /rGO Nanocomposite
VS 4 nanorods were prepared via a hydrothermal method. In a typical process, 5 mmol of Na 3 VO 4 and 25 mmol of CH 3 CSNH 2 were dissolved in 60 mL of deionized water to obtain the mixed solution, and then 1 mol L −1 NaOH aqueous solution was added to manipulate the pH of 12. After magnetic stirring of 0.5 h at 60 °C, the solution was transferred into 100 mL of Teflon-lined stainless autoclave and heated to 160 °C for 24 h. After cooling to room temperature, the product was collected and washed with deionized water three times. Then, the purified product was dried in a vacuum oven at 60 °C for 12 h to obtain the pristine VS 4 nanorods. VS 4 /rGO nanocomposite was prepared by the ultrasonic dispersion method. Detailly, the VS 4 nanorods and rGO were dispersed into the absolute ethanol under ultrasound condition, and the molar ratio of VS 4 nanorods and rGO was about 3:1. Then, the prepared VS 4 /rGO nanocomposite was obtained by centrifugal separation and vacuum drying method.

Characterization and EM Parameters Measurement
The morphology and microstructure of the prepared VS 4 / rGO heterostructures were characterized by field emission scanning electron microscope (FESEM; FEI, Quanta3D FEG) and transmission electron microscope (TEM; TECNI G2 F20). The crystal structures were measured by X-ray diffraction (XRD; Rigaku DMAX-RB). Raman spectra were obtained by Jobin-Yvon Raman microprobe (JY-HR800) under 532 nm laser excitation. Chemical compositions and valence states were analyzed by X-ray photoelectron spectrometer (XPS; Thermo Fisher ESCALab250). Thermo-gravimetric analysis (TGA) was conducted in dry air by using a TA Q-600. The nitrogen adsorption/ desorption experiments were performed in Micromeritics ASAP2020. The specific surface area was obtained by using Brunauer-Emmett-Teller (BET) analysis. Pore size distributions were assessed by using the Barrett-Joyner-Halenda (BJH) method. The EM parameters, including permittivity and permeability, were measured by a vector network analyzer system (HP722ES) in the frequency range of 2-18 GHz. The VS 4 / rGO heterostructures were uniformly dispersed in paraffin with filler loadings of 20%, 30%, and 40%. Then, the asprepared mixture was pressed into a toroidal-shaped specimen with an inner diameter of 3.04 mm, an outer diameter of 7.0 mm, and a thickness of 2.0 mm. The EM parameter measurements of VS 4 nanorods, rGO architecture, and VS 4 / rGO nanocomposite were like VS 4 /rGO heterostructure. The complex permittivity and permeability of the as-prepared samples were further to be measured.

DFT Calculation
The Vienna Ab-initio Simulation Package (VASP) software was used to simulate computation based on density functional theory (DFT). The interaction between ions and electrons was described by the projector-augmented wave (PAW) method. The Generalized Gradient Approximation (GGA) with the Perdew Burke Ernzerhof (PBE) function was employed as the exchange associated functions.

Results and Discussion
Figure 1a schematically illustrates the synthetic process of self-assembly VS 4 /rGO heterostructure. The VS 4 /rGO heterostructure with abundant microarchitectures and rich heterointerfaces was fabricated through hydrothermal and freezedying methods. Similarly, the pristine VS 4 nanorods were fabricated without rGO by the same hydrothermal reaction.
Meanwhile, Fig. 1 also shows a series of SEM and TEM images of the VS 4 nanorods and self-assembly VS 4 /rGO heterostructure. Figure 1b reveals that the VS 4 nanorods are seriously agglomerated due to the absence of a growing template. In Fig. 1c, the rGO architecture demonstrates reticulum-like microarchitecture with lots of randomly distributed nano-walls formed by wrinkled nanosheets. Figures 1d and S2 exhibit that the self-assembly VS 4 /rGO heterostructure also possesses numerous wrinkles and microporous architecture originated from scrolling and folding of rGO. The crooked VS 4 nanorods are evenly anchored on the surface of rGO as Fig. 1e elucidated. Furthermore, the heterointerfaces between VS 4 nanorods and rGO are clearly shown in Fig. 1f, and the average lateral and longitudinal sizes of VS 4 nanorods are about 20-40 and 100-300 nm, respectively. High-resolution transmission electron microscopy (HRTEM) image of VS 4 /rGO heterostructure with distinct lattice is exhibited in Fig. 1g. The interlayer spacings of 0.56 nm and 0.37 nm correspond to (1 1 0) plane of VS 4 and (0 0 2) plane of rGO, respectively [25]. Therefore, the interface between VS 4 and rGO can be clearly observed, but the distinct voids and gaps at boundaries do not appear, exhibiting the tight combination of VS 4 nanorods and rGO.
The elemental compositions of VS 4 /rGO heterostructure are further measured by energy dispersive spectroscopy (EDS). Figure 2a presents the VS 4 nanorods are horizontally and evenly aligned on the rGO. Figure 2b shows that the elements of V, S, C, and O can be identified from the survey scan of EDS with the atomic proportions of 10.27, 42.66, 41.36, and 5.71 at%, respectively. The stoichiometric ratio of V and S atoms is around 1: 4, which proves the existence of VS 4 [25]. Further confirmed by the elemental mapping of Fig. 2c, the four elements of V, S, C, and O are detected on the surface of VS 4 /rGO heterostructure. The C element is derived from rGO, and the O element mainly originates from the residual oxygen-containing functional groups of rGO [26,27]. The crystalline phase of the prepared VS 4 / rGO heterostructure is revealed by X-ray diffraction (XRD). Figure 2d shows the two major peaks of 15.8° and 17.0° are assigned to the (1 1 0) and (0 2 0) planes of monoclinic VS 4 (JCPDS No. 072-1294) [28]. Figure 2e demonstrates the Raman spectra of VS 4 nanorods, rGO, and VS 4 /rGO heterostructure. The peaks located at 191.6 and 280 cm −1 are attributed to the stretching (A 1 ) and bending (B 1 ) modes of V-S chemical bands, respectively. The characteristic peaks located at 1342 and 1593 cm −1 correspond to the D and 1 3 G peaks of rGO. In addition, the peak intensity ratio of D and G for VS 4 /rGO heterostructure (1.1) is higher than rGO (0.96), revealing the formation of plentiful defects and distortions caused by structural imperfection and heterointerface [29].
The surface chemical state of VS 4 /rGO heterostructure is investigated by X-ray photoelectron spectroscopy (XPS) (Fig. S3). Figure 3a shows the high-resolution XPS spectrum of V 2p. The characteristic peaks of 516.5 and 524 eV are attributed to V 2p 3/2 and V 2p 1/2 , corresponding to the V 4+ of VS 4 [30,31]. The other two characteristic peaks of 513.9 and 521.8 eV derived from V-C chemical bonds can be clearly detected, confirming the strong bonding and abundant heterointerface between VS 4 and rGO [32]. In contrast, the high-resolution XPS spectra of VS 4 nanorods and VS 4 /rGO nanocomposite prepared by ultrasonic dispersion method are shown in Figs. S4 and S5, respectively. As shown in Fig. S5a, the high-resolution spectrum of V 2p lacks the V-C band peak, which is due to VS 4 nanorods fail to be fabricated and anchored on rGO. Figure S5b-c exhibits that the high-resolution spectra of S 2p and C 1s are the same as the VS 4 /rGO heterostructure. Compared with VS 4 nanorods and VS 4 /rGO nanocomposite, the V 2p 3/2 of VS 4 / rGO heterostructure demonstrates a positive shift, indicating the electrons transfer from VS 4 nanorods to rGO (Fig.  S6). As Fig. 3b shown, the corresponding peaks located at 162.7 and 163.8 eV originating from the S 2 2− ions can be indexed to S 2p 3/2 and S 2p 1/2 , respectively [32]. Figure 3c shows the fitted C 1s peaks approximately locate at 284.7, 285.7, 286.7, and 288.6 eV, respectively. These C 1s peaks are originated in the presences of C-C/C=C in the aromatic ring and the residual oxygen-containing functional groups such as -OH and -COOH [33]. The VS 4 /rGO heterostructures are analyzed by thermogravimetric analysis (TGA) to evaluate their thermal stability and content. As Fig. 3d shows, the small weight loss of VS 4  compounds, respectively. The oxidation decomposition of rGO is observed at 370-500 °C. After 600 °C, the slight weight gain is caused by the further oxidation of vanadium oxide [33,34]. The N 2 adsorption-desorption isotherm is obtained to measure the surface area and pore size distribution of VS 4 /rGO heterostructure. Figure 3e shows that the isotherms of VS 4 Fig. S7. The mesopores and macropores existing in the VS 4 /rGO heterostructure are associated with the content of GO in the hydrothermal reaction process. Additionally, 2VS 4 /rGO40 with the largest heterointerface area demonstrates more reticulum-like micropores that provide plentiful microporous networks [32][33][34].
To evaluate the microwave absorption performance, the EM parameters, including complex permittivity (ε r = ε′-jε") and complex permeability (μ r = μ′-jμ″), are measured by vector network analyzer system (HP722ES) in the frequency range of 2-18 GHz. According to the EM energy conversion principle, the real parts of complex permittivity (ε′) and permeability (μ′) are associated with electrical and magnetic energy storages, respectively. However, the imaginary parts of permittivity (ε″) and permeability (μ″) represent the dissipations of electric and magnetic energies, respectively [35]. As shown in Fig. 4a, the ε′ of VS 4 /rGO heterostructures with the different filler loadings exhibit a downward tendency in the frequency range of 2-18 GHz. When the frequency of the microwave is increasing, the dipoles existing in VS 4 /rGO heterostructure cannot reorient themselves quickly enough to respond to the applied alternating EM field. Therefore, the complex permittivity starts to decrease and generates typical frequency dispersion behaviors.
When the filler loadings of 2VS 4 /rGO20, 2VS 4 /rGO40, and 2VS 4 /rGO60 are fixed at 30 wt%, the ε′ of 2VS 4 / rGO40-30% demonstrates a decreasing tendency from 16.91 to 12.0, and the values of ε′ for 2VS 4 /rGO20-30% and 2VS 4 /rGO60-30% all display decreased trends. The ε′ value of 2VS 4 /rGO60-40% is higher than 2VS 4 /rGO60-30%, which is mainly due to the increase of dielectric media. The values of ε′ for 1VS 4 /rGO40 and 3VS 4 /rGO40 maintain a relatively lower level. Figure 4b demonstrates the changing trend of ε″ is different from ε′. In general, the values of ε″ increase with the filler loading of VS 4 /rGO heterostructures, which is related to the presence of abundant microarchitectures and heterointerfaces. Based on the analysis of TGA results and BET surface area, 2VS 4 / rGO40 possesses abundant microarchitectures and rich heterointerfaces, demonstrating the highest ε″ than other samples with the filler loading of 30 wt%. The ε″ of 2VS 4 / rGO40 is over 3.0 in the frequency range of 2-18 GHz, indicating the great EM energy attenuation ability. The other samples exhibit lower values of ε″, which are mainly due to the poor microarchitecture and insufficient heterointerface. Additionally, the multiple dielectric relaxation peaks exhibiting in the ε″-f curves are derived from nonlinear resonant behaviors of VS 4 /rGO heterointerfaces [36,37]. Correspondingly, 2VS 4 /rGO40 demonstrates obvious and corrugated resonance peaks in the ε″-f curves of 7-11 GHz and 13-16 GHz, further manifesting the promotion of abundant microarchitectures and rich heterointerfaces for dielectric loss.
In order to evaluate the dielectric loss capability, the values of tanδ ε (tanδ ε = ε″/ε′) are shown in Fig. 4c. The curves of tanδ ε display several fluctuations in the frequency range of 8-18 GHz, which are mainly due to the orientations of induced dipoles. Additionally, the dipole moments cannot match up with the alternating EM fields in high-frequency range. Furthermore, the weak magnetic properties of VS 4 / rGO heterostructure cause the values of μ′ and μ″ to fluctuate around 1 and 0, respectively. Therefore, the calculated tanδ μ (tanδ μ = μ″/μ′) of VS 4 /rGO heterostructure is closed to 0 (Fig. S8). According to Debye relaxation theory, the ε r can be indicated as Eq. 1 [38]: where f represents the frequency, τ is the polarization relaxation time, ε r and ε ∞ represent the stationary permittivity and the optical dielectric constant, respectively. Meanwhile, the ε′ and ε″ can be further demonstrated as Eqs. 2 and 3: Based on the aforementioned Eqs. 1-3, the relationship between ε′ and ε″ can be clearly expressed as Eq. 4: According to Eq. 4, the curve of ε′ versus ε″ exhibits a single semicircle denoted as Cole-Cole semicircle, which illustrates the process of Debye dipolar relaxation. Generally, the dielectric loss also can be obviously represented by Debye dipolar relaxation [39]. The curves of ε′ versus ε″ for VS 4 /rGO heterostructures are shown in Fig. 4d, in which the presence of semicircles demonstrates the multiple dielectric relaxation losses.
In order to evaluate the microwave absorption performance, the RL of VS 4 /rGO heterostructure usually can be calculated by the measured complex permittivity and permeability. The RL can be evaluated by Eqs. 5 and 6 based on the transmission line theory [40]: Z 0 and Z in represent the characteristic impedance of free space and the input impedance of absorbent, respectively. f is the frequency of the incident microwave; t is the thickness of the absorbent layer; c is the velocity of light. To reveal the influence of the frequency and thickness of absorbent, Fig. 5 outlines the RL curves and 3D presentations of the calculated RL of VS 4 /rGO heterostructures within the thickness of 1-6 mm and in the frequency range of 2-18 GHz.
The microwave absorption performance of VS 4 /rGO heterostructure can be modulated by manipulating the thickness   Figure 6a demonstrates the 3D RL presentations of rGO, VS 4 nanorods, VS 4 /rGO nanocomposite, and VS 4 /rGO heterostructure (2VS 4 /rGO40-30%). Specifically, the maximum RLs of rGO architecture and VS 4 nanorods are about − 7.5 and − 3.2 dB with a thickness of 1.5 mm, respectively. However, the maximum RL of 2VS 4 /rGO40-30% is up to − 43.5 dB at 14 GHz with a thickness of 1.5 mm, overwhelmingly outperforming the microwave absorption performances of rGO architecture and VS 4 nanorods. In contrast, the VS 4 /rGO nanocomposite prepared by the ultrasonic dispersion method shows the weak RL of − 6.9 dB with a thickness of 1.5 mm (Fig. S11a). The self-assembly VS 4 / rGO heterostructure holds the intimate contact heterointerface that is proved by the previous characterizations of TEM and XPS. However, the pristine VS 4 nanorods and rGO architecture are short of heterointerfaces, and the absence of interfacial polarization relaxation fails to promote microwave attenuation. So, it can be concluded that the VS 4 /rGO heterointerface benefits the enhancement of microwave absorption performance. Compared with the VS 4 /rGO nanocomposite, the VS 4 /rGO heterostructure with rich microporous architectures can greatly improve the multiple reflections and scatterings of microwaves, which exponentially boost microwave attenuation. The ε′, ε″, and tanδ ε of VS 4 nanorods, rGO architecture, VS 4 /rGO nanocomposite, and VS 4 /rGO heterostructure are shown in Fig. S11. As Fig.  S11b-c shown, rGO architecture demonstrates the highest ε′ and ε″. Undoubtedly, rGO possessing a significant dielectric property endows the self-assembly VS 4 /rGO heterostructure with greater permittivity. In contrast, VS 4 /rGO nanocomposite prepared by ultrasonic dispersion cannot effectively inspire the excellent dielectric property of rGO. The pristine VS 4 nanorods have limited dielectric properties because of their inherited attributes. The rGO architecture also has the highest tanδ ε , further manifesting its excellent dielectric loss. VS 4 /rGO nanocomposite displays a higher value of tanδ ε than the self-assembly VS 4 /rGO heterostructure, which is mainly originated in the independent rGO (Fig. S11d).
The tanδ ε of self-assembly VS 4 /rGO heterostructure is also higher than the agglomerated VS 4 nanorods, proving that the introduction of rGO plays a great role in boosting dielectric loss. Additionally, the permeabilities of VS 4 nanorods, rGO architecture, VS 4 /rGO nanocomposite, and VS 4 /rGO heterostructure are negligible due to the weak magnetic performances of VS 4 and rGO. The microwave absorption performances of rGO, VS 4 nanorods, and VS 4 /rGO nanocomposite with different thicknesses are shown in Fig. S12. Generally, the excellent microwave absorption performance not only comes from the higher attenuation capability but also attributes to the well-matched impedance matching. The attenuation capability of absorbent is evaluated by the concept of attenuation constant α, which can be calculated by Eq. 7 [41]: a. a.
c.  Figure 6b illustrates that rGO possesses the highest attenuation constant due to its excellent dielectric loss and conductive loss. VS 4 /rGO heterostructure and VS 4 / rGO nanocomposite exhibit a similar value of attenuation constant, proving the combination of VS 4 and rGO is good for achieving higher attenuation constant. The pristine VS 4 nanorods demonstrate the weak attenuation constant, which is negative to microwave absorption. Among them, the VS 4 /rGO heterostructure exhibits the best microwave absorption performance, which is mainly due to its well-matched impedance matching. The frequency dependences of impedance matching, attenuation constant, and RL for 2VS 4 /rGO40-30% with a thickness of 1.5 mm are shown in Fig. 6c. According to Eq. 5, the value of Z =|Z in /Z 0 | closed to 1 means that all microwaves propagate into the interior of absorbent without reflections [42]. Generally, the attenuation constant can attain a larger value in the high-frequency range. However, the maximum RL cannot be obtained after the 16 GHz due to the value of Z is far away 1. The lower value of impedance matching is attributed to the strong interfacial reflection of microwave. Taking impedance matching and attenuation constant into account, the maximum RL of 2VS 4 /rGO40-30% reaches − 43.5 dB in 14 GHz with the impedance matching approaching 1. The frequency dependences of impedance matching, attenuation constant, and RL for VS 4 nanorods, rGO architecture, and VS 4 /rGO nanocomposite at the matching thickness of 1.5 mm are shown in Fig. S13. As Fig. S13a shows, rGO architecture demonstrates the higher attenuation constant and poor impedance matching, leading to weak microwave absorption performance. Figure S13b shows that VS 4 nanorods possess the better impedance matching and lower attenuation constant, demonstrating limited microwave absorption performance. Figure S13c shows that the VS 4 /rGO nanocomposite prepared by the ultrasonic dispersion method also presents weak microwave absorption performance with a thickness of 1.5 mm, and the mismatched impedance matching significantly weakens microwave absorption performance even though the attenuation constant is at high level [43].
Except for the existence of heterointerface, the richness of heterointerface also exerts great influences on the microwave absorption performance. According to the above analysis of BET surface area and TGA results, the heterointerface and microarchitecture of VS 4 /rGO heterostructure can be modulated by the self-assembly generation of VS 4 nanorods anchored on rGO. Figure 6d shows [44]. Specifically, the selections of crystal structure models and calculation parameters are shown in Figs. S14 and S15. VS 4 can be grown on rGO along the (1 1 0) plane direction with the optimal lattice constant. The surface energy of VS 4 (1 1 0)/rGO (1 0 0) can be calculated to about 0.798 eV, which is lower than VS 4 (− 2 0 4)/rGO (1 0 0) of 6.657 eV and VS 4 (0 2 0)/rGO (1 0 0) of 3.124 eV. Additionally, the V-terminated surface is more preferred to construct a heterointerface with rGO (1 0 0) than S-terminated surface ( Fig S16). Therefore, the VS 4 /rGO heterointerface is prone to be bonded by V-C bands. As Fig. 6g shown, VS 4 employs the (− 2 0 4), (0 2 0), and (1 1 0) lattice planes to match the plane of rGO (1 0 0), respectively. Figure 6g(I) demonstrates the charge density of VS 4 (− 2 0 4)/rGO (1 0 0) interface with an imaginary line on the heterointerface, and the C atoms above the heterointerface are far away from the bottom V atoms. Figure 6g(II) displays the charge density of VS 4 (0 2 0)/rGO (1 0 0) interface, and the distance of V and C atoms is farther than the VS 4 (− 2 0 4)/rGO (1 0 0) interface. Therefore, V and C atoms are extremely difficult to bond together. Figure 6g(III) exhibits the charge density of VS 4 (1 1 0)/rGO (1 0 0) interface, and the shortest distance between V and C atoms is successfully realized. Due to the dislocation of the interface atom after relaxing, the V atoms are adjacent to C atoms with the formation of strong chemical bonds. Therefore, the 1 3 VS 4 (1 1 0)/rGO (1 0 0) interface is easy to bond, and the result is consistent with the analysis of the above interface energy. Overall, the interfaces of VS 4 (− 2 0 4)/rGO (1 0 0) and VS 4 (1 1 0)/rGO (1 0 0) have great potential to form chemical bonds [45].
The chemical bands further require to be analyzed by charge density difference of heterointerface. The charge density differences of VS 4 (− 2 0 4)/rGO (1 0 0) and VS 4 (1 1 0)/rGO (1 0 0) heterointerfaces are shown in Fig. 6h. Figure 6h(I) shows that the charges are increasing between V and C atoms significantly, proving the formation of the covalent bonds between V and C atoms. Figure 6h(II) displays that the charges are increased near C atoms obviously, while the charges are decreased near V atoms considerably, indicating part of the charges of V atoms is transferred to C atoms. So, the ionic bonds have formed between the V and C atoms. The calculated results of charge density difference exactly match the electronic binding energy shift measured by XPS, further proving the electrons migrate from the VS 4 to rGO (Fig. S6). Furthermore, the charge density difference in VS 4 /rGO heterointerface results in the enhancement of dipole and interfacial polarization relaxations, which greatly motivate microwave attenuation capability [46,47].
Based on the abovementioned analysis, the strategies of architecture design and interface engineering open a new door for the development of enhanced and ultrathin microwave absorbents. Figure 7 shows the schematic illustration of microwave absorption mechanism for VS 4 / rGO heterostructure. Architecture design and interface engineering inspire the synergy of multi-dimensional advantages, including the anisotropy of 1D nanorods, 2D interface polarizations, and multiple microwave reflections or scatterings of 3D microarchitecture, facilitating to modulate impedance matching and attenuation constant [6,10]. Firstly, 1D VS 4 nanorods are anchored on rGO by van der Wall force and V-C bonds. The shape anisotropy and high aspect ratio of nanorods endow them with rapid charge transportation rate along the axial. The defects of VS 4 nanorods and residual oxygen-containing functional groups of rGO break the balance of charge distributions in nanorods and interface [11,26]. Eventually, the induced multitudinous dipoles and interfacial polarization centers significantly facilitate polarization relaxations [39,48]. Secondly, the constructed 2D VS 4 /rGO heterointerfaces are joined together firmly. Numerous randomly distributed space charges accumulated at the heterointerface generate prominent dipole moments and logs. Therefore, the fine connections of VS 4 /rGO heterointerface effectively modulate the impedance matching and greatly improve the interfacial polarization relaxation [41]. Thirdly, the designed self-assembly 3D reticulum-like microporous VS 4 /rGO heterostructure provides a conductive paths for the electrons hopping and migrating between VS 4 nanorods and rGO. The foamed conductive networks remarkably prolong the transmission paths of microwaves, which encourage the transformation of EM energy into heat energy by the induced microcurrent in alternating EM fields [42,43]. In summary, the mixed-dimensional advantages originating from the synergy of architecture design and interface engineering can boost an appropriate balance of impedance matching and attenuation constant, eventually achieving high-performance microwave absorption materials.

Conclusions
In summary, the strategies of architecture design and interface engineering are proposed to construct the selfassembly VS 4 /rGO heterostructure for the ultrathin and enhanced microwave absorbent. The synergy of microarchitecture and heterointerface can effectively modulate the impedance matching and attenuation constant of VS 4 / rGO heterostructure, thereby achieving enhanced microwave absorption performance at ultrathin thickness. The maximum RL of 2VS 4 /rGO40 heterostructure can reach as strong as − 43.5 dB at 14 GHz and 1.5 mm with the impedance matching and attenuation constant approaching 0.98 and 187, respectively. Furthermore, the EAB of 4.8 GHz can be achieved with an ultrathin thickness of 1.4 mm. DFT calculations provide a platform to decipher the interfacial polarization originating from heterointerface. Architecture design and interface engineering inspire multi-dimensional advantages, including anisotropic dipole polarization, interfacial polarization, and multiple reflections or scatterings of microwaves, eventually facilitating to achieve enhanced microwave absorption performance at ultrathin thickness. Therefore, architecture design and interface engineering offer an instructive attempt for the development of highperformance microwave absorption materials.