Review of Water-Assisted Crystallization for TiO2 Nanotubes

TiO2 nanotubes (TNTs) have drawn tremendous attention owing to their unique architectural and physical properties. Anodizing of titanium foil has proven to be the most efficient method to fabricate well-aligned TNTs, which, however, usually produces amorphous TNTs and needs further thermal annealing. Recently, a water-assisted crystallization strategy has been proposed and investigated by both science and engineering communities. This method is very efficient and energy saving, and it circumvents the drawbacks of thermal sintering approach. In this paper, we review the recent research progress in this kind of low-temperature crystallization approach. Here, various synthetic methods are summarized, and the mechanisms of the amorphous–crystalline transformation are analyzed. The fundamental properties and applications of the low-temperature products are also discussed. Furthermore, it is proved that the water-assisted crystallization approach is not only applicable to TNTs but also to crystallizing other metal oxides.


Introduction
Over the past few decades, titanium dioxide (TiO 2 ) has drawn ever-increasing interest for its application to energy and environmental areas, such as photocatalysis [1,2], dyesensitized solar cells (DSSCs) [3,4], Li-ion batteries [5,6], supercapacitors [7,8], gas sensors, and water splitting, because of its low cost, high abundance, high chemical stability, and lack of toxicity [9][10][11][12][13][14]. In particular, onedimensional (1-D) TiO 2 nanotubes (TNTs) are widely investigated because they possess the advantages of both high surface area and direct carrier transport pathways, which make them a promising candidate for various fields [15][16][17]. Four main routes have been proposed to synthesize TNTs, including sol-gel, hydrothermal, templating, and anodic oxidation methods [18][19][20][21]. The TNTs prepared through sol-gel or hydrothermal methods are generally randomly oriented, and the templating method is limited because of its complicated fabrication process and high cost [22]. Anodic oxidation not only offers the advantages of being facile and easily scaled up but also can yield highly ordered oriented nanotube (NT) arrays, resulting in markedly enhanced performance [23][24][25]. In addition, such NT characteristics as the tube diameter and thickness of the tube wall can be readily manipulated by changing the experimental parameters of the anodization process [26,27]. Therefore, anodic oxidation is expected to be a superior method for fabricating oriented TNTs.
However, the as-anodized TNTs are generally amorphous after anodization, which is not useful for many applications such as DSSCs, where the anatase phase and higher crystallinity have been proved to be essential for enhanced performance [28]. To address this issue, thermal annealing is always carried out to obtain the desired crystalline TNTs. Specifically, the conversion of amorphous TiO 2 NTs to the anatase phase occurs at above 300°C, and mixture of anatase and rutile appears when the annealing temperature is above 550°C [29][30][31]. Although thermal annealing is an effective method to crystallize amorphous TNTs, there are some drawbacks: (1) the annealing method requires additional energy consumption and is costly; (2) this process may facilitate the formation of a thick barrier layer that separates the NT arrays from the substrate, resulting in deterioration of electron transport; (3) the hightemperature annealing process impedes the integration of NT arrays on temperature-sensitive polymeric substrates, hindering the development of lightweight TNTs-based devices [32][33][34]. Consequently, exploring a low-temperature method for the crystallization of TNTs is significant in broadening their applications.
In fact, there are some reports concerning the fabrication of crystallized TNTs at low temperatures without annealing [35,36]. Su et al. found that a crystalline structure formed when the anodization was carried out at a high voltage (120 V) [37]. However, the crystallinity was so low that only a weak and broad (101) peak of anatase appeared. Ali et al. fabricated crystalline TNTs with the assistance of perchloric acid electrolytes, but the TNTs fell into the electrolyte, leading to an extra centrifugation procedure [38]. Therefore, it is urgent to find a facile strategy to crystallize the as-anodized TNTs with considerable crystallinity without involvement of any hazardous substances. In 2011, Liao et al. and Wang et al. proposed a novel water-assisted crystallization (WAC) approach to crystallize the amorphous as-anodized TNTs [39,40]. In short, after the conventional anodization (electrolyte: ethylene glycol solution containing H 2 O and NH 4 F), the as-anodized foils were simply soaked in water for a certain time, and the amorphous TNTs arrays transformed into the anatase phase. It is truly amazing that this transformation occurred with the help of only water and without any annealing treatment or additives. Because of its facile and green chemistry features, the WAC strategy arouses people's interest, and much effort has been devoted to it [41].
Although many papers based on the WAC route have been published since 2011, no review of this field is available. Therefore, a comprehensive review could not only provide timely information for researchers but also motivate the development of TNTs. As shown in Fig. 1, this review mainly summarizes aspects of WAC for TNTs, including methods and mechanisms, fundamental properties, applications, and other materials. First, various WAC methods and the corresponding mechanisms are introduced. Second, we investigate the fundamental properties of the products after WAC treatment. Third, we introduce the main applications, including photocatalysis, DSSCs, and supercapacitors. The fourth section is mainly about other materials generated employing the WAC strategy, namely TiO 2 -based nanostructured materials and other metal oxides.

Methods and Mechanisms
It is well known that crystallization strategy plays a key role in fabricating nanomaterials significantly influencing the structure and morphology of the products. In this section, we cover the various WAC-based crystallization methods used for synthesizing TNTs. We first introduce the water-only WAC method, in which water is the only substance employed in the crystallization process. Then, some modifications are presented, such as doping with metal ions. Finally, some ingenious methods inspired by the WAC mechanism are proposed for the preparation of TNTs. The mechanisms of the abovementioned methods are also discussed.

Water-Only WAC Method
With respect to the water-only WAC method, the amorphous as-anodized TNTs are treated only with water without any other additives for crystallization. According to the different forms of water, it can be classified as a solid-liquid method or a solid-gas method. As the crystallization process involves only water, it is considered a green and cost-effective approach.
In 2011, Wang et al. prepared amorphous TNTs by anodization (electrolyte: ethylene glycol solution containing NH 4 F and H 2 O) and then immersed them in water at RT (* 25°C) [40]. As a result, the amorphous TNTs transformed into pure anatase phase after 3 days without occurrence of rutile or brookite phases (Fig. 3a, b). In addition, the obtained anatase TNTs were stable, and no discernible changes were observed when the immersion time was prolonged to 30 days. The amorphous TNTs transformed into the anatase phase not only by annealing but also through the water-assisted strategy at RT. Based on systematic studies, a dissolution-precipitation mechanism was proposed to explain this type of WAC phenomenon. The building blocks of the amorphous materials are randomly distributed, while the crystallized materials are long-range ordered [50]. As TiO 6 octahedra are the building blocks for both amorphous TNTs and anatase TNTs, it is assumed that the amorphous-anatase transformation is a process that rearranges the TiO 6 octahedra with the assistance of water. As schematically shown in Fig. 3c, two different TiO 6 octahedra, which share one common vertex, first absorb a water molecule forming a bridge between the surface hydroxyl groups through the lone electrons on the oxygen (step 1). In step 2, dehydration of the abovementioned complex occurs. Two water molecules are ejected and one oxygen atom is taken away by forming a new water molecule, resulting in the linkage of octahedra by sharing one common edge. Subsequently, third octahedra proceeds in a similar hydration-dehydration process and the three octahedra become linked together by sharing their edges at a right angle (step 3). Finally, the right-angle assembly connects with another identical assembly, leading to the basic unit cell of anatase TiO 2 (step 4). The reason why the rearrangement of TiO 6 octahedra leads to the formation of the anatase phase and not the rutile phase can be explained as follows. It is believed that the Gibbs free energy of anatase clusters is lower than that of rutile clusters; therefore, the anatase phase is more thermodynamically stable [51]. It is concluded that the amorphousanatase transformation is achieved through a dissolutionprecipitation process, in which randomly distributed TiO 6 octahedra are rearranged with the assistance of water. Owing to the dissolution and reprecipitation processes, the morphology of TNTs cannot stay the same as before, and numerous pores are formed, which will be discussed in the next chapter.
Although the dissolution-precipitation process has been developed, there are still many scientific issues to be explored. In 2016, we further investigated the amorphousanatase transformation and supplemented the dissolutionprecipitation mechanism by immersing the as-anodized TNTs in hot water (90°C) for a certain time [52]. We named it the WAC strategy because water is the only Fig. 2 Schematic illustration of the crystallization process in water substance involved in this crystallization process. Could any other substance also lead to this amazing amorphousanatase transformation under the same conditions? In addition to immersing the amorphous TNTs in hot water, we also immersed them in ethanol and ethylene glycol solutions. However, no distinct anatase peaks were detected except for the Ti substrate peaks, as shown in Fig. 4b, c. We inferred that water is an essential factor in the crystallization process, confirming the water-assisted mechanism. In addition, we not only focused on the TNTs but also paid attention to the byproducts leading to deeper insight into the WAC mechanism. Specifically, after the samples were immersed for 2 h at 90°C, the water became turbid owing to the existence of white precipitate byproducts. When the immersion time was prolonged to 20 h, white products settled to the bottom, and the water became transparent again, as shown in Fig. 4d, e. The selected area electron diffraction (SAED) results in Fig. 4f reveal that the white byproducts are composed of nanoparticles (NPs) possessing an anatase crystalline structure in line with that of the TNTs on Ti substrate. Based on this result, a supplementary dissolution-recrystallization-precipitation mechanism was proposed; its schematic diagram is presented in Fig. 4g. First, TiO 6 octahedra dissolve in water forming Ti(OH) 6 2species. Then, the Ti(OH) 6 2species spontaneously recrystallize and precipitate in situ into TNTs, maintaining the mechanical nanotubular structure. However, a fraction of Ti(OH) 6 2species recrystallize and precipitate into anatase TiO 2 NPs, which are apart from the TNTs and suspended in water. In other words, the overall reactions of the amorphous-anatase transformation can be described as follows: Here, TiO 2(am) represents the amorphous TNTs, and TiO 2(an) represents the anatase TNTs. These findings corroborate and enrich the water-assisted dissolution-precipitation mechanism and provide deeper insight into the WAC strategy. It is worth noting that experimental parameters, such as water temperature and immersion time, have a significant influence on the properties of the obtained anatase TNTs. For example, Karine et al. employed the solid-liquid method to crystallize amorphous TNTs for various time periods at different temperatures (RT, 80, 100, and 120°C). They found that the crystallographic properties and morphological features are distinctive under different experimental conditions [46]. Actually, the solid-liquid as-anodized in water for 3 days (b) (a) ( method to crystallize amorphous TNTs is widely recognized as a fundamental and convenient strategy. The dissolution-precipitation mechanism is not only applicable to the solid-liquid method but also serves as the theoretical basis of other derived synthetic strategies.

Solid-Gas Method
Although the solid-liquid WAC method is cost-effective and convenient, the full-of-water condition results in a disadvantage: TNT films may detach because of the dissolution of the bottom layer under the NTs. To circumvent this problem, a solid-gas method, in which water is gaseous, is proposed [44,53,54]. As schematically shown in Fig. 5a, the amorphous TNTs are put into a Teflon-lined stainless autoclave containing a small amount of water. With increasing temperature, the liquid water turns into water vapor surrounding the TNTs and crystallizes them. Liu et al. employed the solid-gas method to crystallize the amorphous TNTs at temperatures of 130-180°C, and only 0.3 mL water was added to the autoclave [54]. The dissolution-precipitation process proceeded at the TNT/vapor interfaces leading to the crystallization of amorphous TNTs. X-ray diffraction (XRD) results showed this amorphous-anatase transformation, and the effects of vapor temperature and crystallization duration were also investigated. For comparison, they also used the solid-liquid method to crystallize amorphous TNTs by immersing them in water (maintaining other conditions the same). At temperatures of 130 or 160°C, the nanotubular structure of the solid-gas samples was preserved, and only some NPs appeared on tube walls (Fig. 5b), which is a common morphology feature resulting from the WAC method. In contrast, the solid-liquid samples exhibited a serious collapse of TNTs, and the nanotubular architecture was destroyed (Fig. 5c), which is consistent with previous reports. These results indicate that the solid-gas method can alleviate the collapse of NTs,   To compare with the abovementioned example, a facile solid-gas method at a low temperature of 50°C was proposed by Andrea et al. [55]. In this case, the temperature of the TNT arrays was not the same as that of the water vapor because they were not sealed in an enclosed space. Specifically, the as-anodized samples were fixed into a clamping system and exposed to water vapor that had been previously heated to 90°C. No intentional heating was provided to the TNTs, and their temperature reached 50°C (measured by a Pt100 temperature detector) resulting from contact with the heated vapor. The researchers demonstrated that a thin water layer emerges in this situation and subsequently forms part of a solid/liquid/vapor interface system where the water-assisted dissolution-precipitation occurred. After exposure for only 20 min, (101) peaks belonging to the TiO 2 anatase phase were detected in the XRD results, in contrast with the prior amorphous nature. This result shows that amorphous TiO 2 can transform into the anatase phase even at a low temperature of 50°C. Considering the presence of water vapor in air at RT, we may wonder if the amorphous-anatase transformation would occur when the amorphous TiO 2 is exposed to air. Su et al. prepared amorphous TiO 2 and placed it in air to observe the changes [56]. As a result, the amorphous TiO 2 transformed into the anatase phase within 90 days. They attributed this phenomenon to the rearrangement of TiO 6 octahedra with assistance from the water from moisture. Although the crystallization period was extremely long, this result still indicates that the amorphous-anatase transformation occurs in air at RT and normal atmosphere pressure without any solvent or additive.
The water-only WAC method can effectively crystallize amorphous TNTs. The dissolution-precipitation process plays an important role in this amorphous-anatase transformation in which TiO 6 octahedra are rearranged with the assistance of water.

Modified WAC Method
In addition to the water-only WAC method, much effort has been devoted to investigating other modified methods that employ aqueous solutions containing various ions. In this section, we introduce the modified WAC methods involving aqueous solutions containing metal ions and nonmetal ions [57][58][59][60].

Aqueous Solution Containing Metal Ions
Since the first report of TNTs, many efforts have been devoted to doping TNTs with metal ions [61][62][63][64][65][66]. Although the doped TNTs exhibit satisfying performances, the complicated procedures of generating them limit their development. Inspired by the WAC strategy, researchers used aqueous solutions containing metal ions to crystallize the amorphous TNTs and dope the metal elements into TiO 2 at the same time. For example, Zhang et al. fabricated MTiO 3 (M = Zn, Co, Ni) NTs by a hydrothermal treatment that immersed the amorphous TNTs into aqueous solutions containing different metal acetates [67]. Considering the participation of metal acetates, the reactions in the autoclave can be described as follows: Here, M represents the metal ions, and Ac represents acetate (CH 3 COO -). As mentioned above, the amorphousanatase transformation is highly dependent on the reaction between Ti(OH) 6 2and H ? (Eq. 2). From Eqs. 3 and 4, however, we can see that H ? is consumed because of the presence of Ac -. Consequently, the reaction in Eq. 2 is hindered, and the combining of Ti(OH) 6 2and M 2? occurs and is promoted. As shown in Fig. 6a, the XRD results confirm the existence of ZnTiO 3 when the metal acetate is Zn(Ac) 2 . Actually, the employment of an aqueous solution of Zn(Ac) 2 not only causes the formation of ZnTiO 3 but also influences the morphology of NTs. Some NPs emerge during the dissolution-precipitation process when the water-only WAC method is used because of the reaction in Eq. 2. These NPs are usually adhered on tube walls and form a NP/TNT morphological feature. In Zhang's work, the NP/TNT structure appeared when the concentration of Zn(Ac) 2 was low (0.05 M), as shown in Fig. 6b. In contrast, the nanotubular architecture remained intact, and few NPs were observed when the concentration was increased to 0.5 M (Fig. 6c). These results confirm that the addition of M(Ac) 2 hinders the combining of Ti(OH) 6 2and H ? and, subsequently, alleviates the collapse of NTs. To further investigate the reactions and obtain deep insights, additional experiments were carried out. On the one hand, crystalline anatase TNTs, instead of the amorphous TNTs, were hydrothermally treated with 0.2 M Zn(Ac) 2 . As expected, ZnTiO 3 was not detected in this case. Because the stability of anatase TiO 2 is relatively high, the TiO 6 octahedra do not absorb water molecules and form Ti(OH) 6 2groups [68][69][70]. Therefore, the reactions in Eq. 5 are restricted, and ZnTiO 3 is not obtained. On the other hand, ZnTiO 3 was also not obtained when Zn(Ac) 2 was replaced by ZnCl 2 and the other conditions were maintained, which could be attributed to the fact that strong acid radicals would not proceed the reactions, as in Eq. 4. This result demonstrates that both the amorphous nature and weak acid radicals are essential in the preparation of MTiO 3 . In addition, the morphology of the anatase TNTs was nearly unchanged after hydrothermal treatment in 0.2 M Zn(Ac) 2 solution (Fig. 6d). Based on the above results, a schematic illustration of the reactions in the presence of anatase or amorphous TNTs is displayed in Fig. 6e.
In contrast to the metal elements used for doping, some metal ions in the solution nucleate and crystallize simultaneously with the recrystallization of amorphous TNTs. For instance, Zhao et al. fabricated Ag-TiO 2 nanocomposites by immersing amorphous TNTs in an aqueous solution containing AgNO 3 , glucose, and ethanol at 180°C [71]. After 2 h, the sample contained three phases, including silver, anatase TiO 2 , and titanium (substrate). In this reaction, Ag ? ions diffused into the amorphous TNTs and transformed into Ag NPs. The WAC of amorphous TNTs proceeded at the same time, eventually resulting in Ag-TNT nanocomposites.

Aqueous Solutions Containing Nonmetal Ions
As for TNTs with nonmetal ions, we mainly discuss nitrogen-doped TNTs (N-TNTs), which have many advantages in various fields [72][73][74][75]. A variety of strategies, such as ammonolysis and ion implantation methods, have been developed to implant nitrogen into TNTs [76,77]. Unfortunately, high temperature is usually an inevitable experimental condition for obtaining N-TNTs limiting their development for many applications. Consequently, it is important to develop a convenient low-temperature method to prepare N-TNTs. Wang et al. fabricated N-TNTs by immersing the as-anodized amorphous TNTs into an aqueous solution of ammonia at 90°C, as shown in Fig. 7a [78]. Because of the weak alkaline environment of the solution, the reactions in Eqs. 1 and 2 were accelerated. As expected, the amorphous TNTs transformed into the anatase phase after immersion, and the crystallinity increased with increasing immersion time. As shown in Fig. 7b, X-ray photoelectron spectroscopy (XPS) was carried out to investigate the influence of ammonia. Sharp peaks for Ti, O, and C were detected in both the as-anodized and ammonia-treated samples, while the N 1s peak was also observed in the latter. The N 1s peak located at approximately 399.8 eV was assigned to interstitial nitrogen with a Ti-O-N structure, which is consistent with other studies [79,80]. The normalized Ti 2p core-level XPS spectra of the as-anodized and ammonia-treated samples are presented in Fig. 7c. The peak of the ammonia-treated sample is clearly shifted compared with that of the as-anodized sample, indicating that their Ti ions have different bonding environments. The researchers demonstrated that this redshift could be attributed to an increase in electron cloud density on Ti owing to the presence of nitrogen. The XPS results also confirm that there were more Ti 3? ions in the ammonia-treated sample, and we can conclude that oxygen vacancies (Ti 3? ) emerge during the ammonia solution immersion. Moreover, the N-TNTs exhibit an elevated conductivity, as shown in Fig. 7d. The conductivity of the as-anodized TNTs was only  b Low-resolution XPS spectra of as-anodized TNAs and ammonia-treated TNAs (10 h). The inset shows the corresponding N 1s core-level XPS spectra with high resolution. c The corresponding normalized Ti 2p core-level XPS spectra with high resolution together with their difference spectrum ('ammonia-treated TNAs' minus 'as-anodized TNAs'). d I-V characteristics of the as-anodized TNAs and ammonia-treated TNTs annealed for 5, 8, 10, and 15 h, respectively. The inset: a simplified sketch of the two-point measurement arrangement [78]. Copyright Ó 2014 Elsevier B.V 8.96 9 10 -9 S m -1 , while this value of the ammoniatreated sample reached as high as 7.42 9 10 -6 S m -1 . The researchers demonstrated that the variation in conductivity could be attributed to the enhanced crystallinity and oxygen vacancies introduced in the ammonia-treated products.
In addition, Cui et al. immersed the as-anodized TNTs into an aqueous solution of various concentrations of (NH 4 ) 2 TiF 6 (0.005, 0.01 and 0.02 M) [81]. Although water molecules were considered to be the main agents in the crystallization of TNTs because of the very low concentrations of (NH 4 ) 2 TiF 6 , the presence of [NH 4 ] ? and [TiF 6 ] 2markedly influenced the products, especially their morphology. When these materials were employed in supercapacitors, the specific capacitance of the (NH 4 ) 2-TiF 6 -treated sample was three times that of the sample without (NH 4 ) 2 TiF 6 treatment.

Other Methods
We have introduced the main WAC methods, and a dissolution-precipitation mechanism has been adopted to explain the amorphous-anatase transformation. However, this transformation process usually requires a relatively long crystallization time, especially for the solid-liquid method. At RT, days are needed to achieve the transformation because of the low dissolution-precipitation rate. Therefore, accelerating the WAC process becomes a challenging issue. In 2017, Aijo et al. reported a very efficient technique for RT crystallization of as-anodized TNTs, which is quite different from the methods above [82]. The most attractive feature of this method is the very fast amorphous-anatase transformation, which only requires 5 min. As shown in Fig. 8a, the preparation process comprises the following steps: (1) titanium foil is anodized in an ethylene glycol solution containing ammonium fluoride and water; (2) the sample is crystallized using a two-electrode system, where the as-anodized sample is used as the working electrode and platinum acts as the counter electrode. An alternating square voltage pulse with a pulse width of 100 ms is employed, and the electrolyte used in this step is a 1 M KCl aqueous solution. The addition of KCl improves the conductivity, and this species does not participate in the reactions on either the anode or the cathode. After a pulse treatment of only 5 min, a sharp (101) XRD peak of the anatase phase was observed, suggesting successful amorphous-anatase transformation in a short time. In addition, the nanotubular structure was well maintained after pulse treatment, and few NPs were detected, in contrast with the water immersion samples, in which many NPs adhered to tube walls. As shown in Fig. 8b, an electrophilic-nucleophilic mechanism is proposed to explain the crystallization process. In the first stage, a positive pulse (? 5 V) is applied to the amorphous TNT electrode, making it electrophilic and leading to the accumulation of OHions on the surface. These OHions act as 'bridges' bonding the two adjacent Ti(OH) 6 2octahedra together. In the second stage, a negative pulse (-5 V) is applied to the amorphous TNT electrode, making it nucleophilic and causing the attraction of H ? ions. These H ? ions 'attack' the 'bridges,' resulting in the formation of edge-shared octahedra. With the increase in pulse treatment time, this process continues until a basic unit of anatase TiO 2 is formed.
In summary, there are many ways to accomplish the WAC of amorphous TNTs. The dissolution-precipitation mechanism is appropriate for most of the methods; some other mechanisms were also proposed. Finding a green, efficient, and low-cost method for crystallizing amorphous TNTs not only promote the further investigation of TiO 2 but also have great significance for the exploration of crystallography.

Fundamental Properties
After the WAC process, some properties of the products are quite different from those of the as-anodized and hightemperature-annealed samples. In this section, we mainly introduce fundamental properties, including the morphology, surface area, crystallinity, and bandgap, of the products prepared by WAC methods.

Morphology Evolution
It is well known that the morphology of nanomaterials is the most important factor affecting their properties. Although the 1-D structure usually does not collapse completely during the WAC, there are still many changes that cannot be ignored. In the following, these new morphological features and the corresponding influence factors are summarized.

NT-NP/NT-NR Evolution
Treatment time Figure 9a-d shows the scanning electron microscopy (SEM) images of the morphological evolution of a sample as a function of water immersion time. From  Fig. 9a, it can be seen that the as-anodized TNTs have smooth tube walls. However, when the sample is immersed in water at RT for 30 h, some NPs with a mean diameter of approximately 10 nm appear on the tube walls forming an NP/NT structure. With increasing immersion time, more NPs emerge on both the inner side and outer side of the tube walls. It should be noted that the NP/NT structure is still maintained, because the inside of the tube is not completely filled with NPs. If we further prolong the   immersion time to over 72 h, the original tubular structure is no longer visible, and only the solid nanorods (NRs) are detected (Fig. 9d). The NT-NP/NT-NR evolution can be attributed to the dissolution-precipitation, in which TiO 6 octahedra from the original NTs dissolve, rearrange, and precipitate as anatase TiO 2 NPs on tube walls. In Fig. 9e, a scheme illustrating the transformation from amorphous NTs to anatase NRs is presented. In addition, Wang et al.
found that a double-walled NT structure forms before the formation of NPs/NTs (Fig. 9b) [40]. It is believed that the large space inside the NTs facilitates water molecules to access the inner surfaces of the tubes, while the narrow space between the adjacent NTs limits the transport of water molecules. Therefore, the dissolution-precipitation process occurring on the outer surfaces of the NTs is dramatically slow compared with that on the inner side, finally forming the double-walled structure. This type of NT-NP/NT-NR evolution has also been discovered in most experiments using WAC methods. For example, Cao et al. immersed the as-anodized TNTs into water for different duration times (up to 7 days) and investigated the morphology transformation [83]. Figure 10 shows SEM and transmission electron microscopy (TEM) images of the samples with different immersion times. For the as-anodized TNTs (Fig. 10a), the tube wall is smooth, and no lattice fringes or diffraction rings can be detected from the high-resolution TEM and SAED images, confirming the amorphous nature. After immersion for 24 h (Fig. 10b), an NP/NT architecture appears, and the diffraction rings assigned to anatase TiO 2 are observed. Within 3 days (Fig. 10c), the NPs/NTs transforms into NRs composed of NPs. Both the lattice fringes and diffraction rings are clearly observed, indicating the good crystallinity of the prepared anatase TNTs. It can be noted that a higher surface area can always be obtained after WAC treatment, resulting from the formation of pores and nanoparticles during the morphology evolution process. On the other hand, losing the tubular structure also causes some drawbacks listed as follows: (1) numerous boundaries between nanoparticles lead to a slow diffusion of electrons; (2) the structure may be not as robust as before. In short, there are advantages and disadvantages of the morphology evolution, and it can be controlled to meet different requirements.
Treatment temperature Regarding the solid-liquid method, its high temperature ([ 100°C) can easily lead to the collapse of TNT films [53]. In contrast, the TNT films are relatively robust under solid-gas treatment. Additionally, the treatment time plays a key role in the NT-NP/NT-NR transformation. Liu et al. demonstrated that high temperature accelerates the dissolution-precipitation rate and, subsequently, facilitates the formation of NP/NT structures [54]. After exposure of the sample to water vapor for 4 h at 130°C, only a small number of NPs appeared, and the nanotubular structure was well preserved. Nevertheless, the nanotubular structure of the 180°C sample started collapsing, and the NR structure was about to form. NT lengths Although many researchers have studied the influences of treatment time and temperature, little attention has been paid to the effect of NT length. In 2013, Wang et al. used the solid-liquid WAC method to crystallize the amorphous TNTs and investigated the influence of NT lengths on the morphology [84]. When as-anodized TNTs with lengths of 3.5 lm were immersed in water for 45 min, only a few NPs were observed on surfaces, and the tube walls were still smooth. For the 6.5 lm samples, many more NPs were generated, and the tube walls became extremely rough forming a typical NP/NT structure. For the longest tubes (16.5 lm), solid NRs composed of NPs appeared. This result shows that the long NTs are more prone to NT-NP/NT-NR evolution than the short NTs, which may be attributed to the abundant titania source allowing the dissolution-precipitation process to occur. Furthermore, it was also found that the morphology near the tube bottom was different from that of the tube top. Specifically, the bottom NTs were filled with NPs and became NRs, while the top NTs still exhibited an NP/NT structure. The solid NR structure of the bottom part of NTs limits the attachment and transportation of dye molecules, which is the reason why the amount of dye loading does not increase dramatically with longer NTs.
pH effect From Eq. 2, we can see that the concentration of H ? ions plays a key role in the dissolution-precipitation and, subsequently, affects the formation of TiO 2 NPs. Zhang et al. investigated the influence of pH on morphology transformation and found that the NP size is strongly related to the pH value [67]. In HCl solution (pH = 3), the NTs transformed into NRs composed of compact NPs with a diameter of approximately 80 nm. In contrast, the NRs formed in deionized water (pH = 6.5) were composed of NPs with a diameter of approximately 40 nm. When the pH was 11 (NaOH solution), smaller NPs of 20-30 nm in diameter were observed on both the top surface and tube walls. It can be concluded that the NP size decreases with increasing pH value; in other words, the NPs grow larger with a higher concentration of H ? . This phenomenon can be explained by the fact that the presence of more H ? ions at low pH accelerates the reaction in Eq. 2, thus, forming larger anatase TiO 2 NPs. This theory also applies to the condition when the amorphous TNTs are immersed in a solution containing weak acid radicals such as acetate (CH 3 COO -). CH 3 COOcan combine with H ? to restrict the reaction in Eq. 2; therefore, the formation of NPs is hindered, and the nanotubular structure is usually maintained.
Besides, there are many other factors influencing the NT-NP/NT-NR morphology evolution. For example, Huo et al. reported that the dissolved oxygen in water remarkably affects the tubular structure of TNTs. When the dissolved oxygen was eliminated by purging with N 2 , and then the WAC procedure was conducted while maintaining other conditions the same, the nanotubular architecture was well kept and the NT-NP/NT-NR evolution did not occur [43]. In addition, the residual fluorine on TNTs after anodization also affects the morphology transformation. The existence of fluorine accelerates the NT-NP/NT-NR evolution because the titanium fluoride compounds can create anatase TiO 2 by hydrolysis [83,85,86] In summary, NP/NT and NR structures are commonly observed because of the dissolution-precipitation process during crystallization. There is no doubt that the participation of NPs would greatly increase the surface areas of products, which is beneficial for many applications.

Other Morphologies
Advanced NPs/NTs As the crystallization using the WAC method is always accompanied with the formation of particles, it is considered as a convenient way to decorate NPs on NTs, in contrast with the presynthesized NP method [87][88][89][90]. However, the generation of NPs is due to the sacrifice of NTs, which makes the tube walls become gradually thinner during the treatment. With this sacrifice, the nanotubular structure may completely collapse and transform into NRs. Therefore, it is a challenge to decorate NPs on tube walls without the destruction of NTs. Kurian et al. proposed a strategy of coating a secondary thin amorphous TiO 2 layer on previously crystallized TNTs and then immersing them in water [45]. As illustrated in Fig. 11a, crystallized TNTs were first obtained by anodization and annealing and then transferred onto the fluorine-doped tin oxide (FTO) substrate. Second, a thin amorphous TiO 2 layer (approximately 15 nm in thickness) was deposited on the TNT film by the atomic layer deposition (ALD) technique. Finally, the resultant sample was immersed in water for different durations. The primary crystallized anatase TNTs are quite stable when immersed in water [91]. Therefore, when the ALD-treated sample was immersed in water, the outer amorphous layer transformed into anatase TiO 2 NPs through the dissolutionprecipitation process, while the inner crystallized NTs remained unchanged. As shown in Fig. 11b, c, some crystalline NPs are decorated on the tube walls. Because the NTs are not destroyed at all, we define this type of NPdecorated structure as advanced NPs/NTs. The prepared products were employed in DSSCs, and they showed a better performance than the sample without water treatment (Fig. 11d). There are two reasons that explain this promotion: (1) the participation of NPs dramatically increases the surface area and is beneficial for higher dye loading; and (2) the primary crystallized NTs serve as backbones for electron transport. It is believed that this strategy can be applied to various 3-D structures to both increase the surface area and promote the dye loading amount without destroying the geometric architecture.
Nanoworms/NTs The water-only method usually causes NP/NT and NR structures to form, as mentioned above. Some novel morphological features appear when other ions are involved in the solution. For example, a nanoworm/NT structure was obtained when the as-anodized TNTs were immersed in the aqueous solution of ammonia at 90°C [75]. Compared with the normal nanotubular structure of the as-anodized sample (Fig. 11e), many NPs appear on the top surface of the sample immersed in hot water (Fig. 11f), in line with previous reports. However, when the as-anodized TNTs were immersed in an aqueous solution of ammonia, many worm-like titania structures with a length of approximately 100 nm form on both the top surfaces and tube walls of TNTs, as shown in Fig. 11g. From the crosssectional SEM image, it is clear that the diameter of the NTs decreases substantially after immersion. When the concentration of ammonia increased, the worm-like morphological feature was maintained and became denser. Researchers found that this type of nanoworm/NT structure exhibits a better performance for degrading methyl orange (MO) than the high-temperature-annealed sample.

Surface Area
One of the reasons why TiO 2 NTs have been widely studied is their relatively high surface area [92]. For example, high surface area is beneficial for absorbing more dye molecules in DSSCs and, subsequently, it promotes efficiency [93]. Although the nanotubular structure contributes to a surface area that is considerably larger than that of bulk TiO 2 , there is still much room for improvement. On the one hand, much effort has been dedicated to increasing the surface area of TNTs by adjusting the NT length, diameter, and tube wall thickness. However, the average surface area of TNTs prepared by anodization and annealing processes is only approximately 30-40 m 2 g -1 according to a Brunauer-Emmett-Teller (BET) analysis using N 2 adsorption/desorption [25,94,95]. On the other hand, some modifications of the NT geometry, such as the fabrication of bamboo-type architecture and decoration of NTs with NPs, have been performed to improve the surface area [96][97][98]. Using the WAC method to decorate TiO 2 NPs on TNTs is clearly more convenient and environmentally friendly than these methods. As shown in Table 1, some experimental parameters and their influences on TNTs properties, such as morphology and specific surface areas, are listed. As the morphology of the as-anodized NTs barely changes after annealing, the specific surface area of the annealed products is close to that of the as-anodized ones (approximately 30 m 2 g -1 ). When the solid-liquid method is employed for crystallization, the specific surface area of the sample after water immersion remarkably increases to 104.76 m 2 g -1 , which is nearly four times that of the as-anodized sample. The emergence of TiO 2 NPs makes a major contribution to the high specific surface area. Moreover, the specific surface area of a sample possessing a NR morphology (Ref. [40]) reaches as high as 203.3 m 2 g -1 . Although the long treatment time (72 h) plays a key role in forming a large specific surface area, the length and diameter of the original NTs are also important factors. In addition, the products prepared by the solid-gas method also exhibit a relatively high specific surface area.

Crystallinity
The amorphous TNTs can transform into the anatase phase through the dissolution-precipitation process with the assistance of water. There are two main factors influencing the crystallinity of the products: treatment duration and treatment temperature. Generally, the crystallinity is enhanced with increasing treatment time or treatment temperature; however, it should be noted that this upward trend is not unlimited. For example, a distinct (101) peak assigned to anatase TiO 2 appeared after the sample was immersed in water for 2 days at RT. When the immersion time was prolonged to 4 days, the intensity of the (101) peak had almost no enhancement compared with that of the 2-day sample [47]. At the same time, the average crystalline size indeed decreased with the longer water treatment. Although the anatase phase can be obtained using the WAC method, the crystallinity is not as high as that of the annealed products. Fan et al. first crystallized amorphous TNTs by the solid-gas method, and then the prepared products were further annealed at 450°C [53]. The intensity of the dominant (101) peak was significantly larger after annealing, indicating that the previously obtained TNTs were partially crystallized. As we expected, the structure and morphology were not clearly different after annealing. Therefore, some researchers first prepare rough NPs/NTs using the WAC method and then anneal them at high temperature; thus, the final products possess both high surface area and good crystallinity.

Bandgap
As TNTs are semiconductors, their bandgap is an important characteristic that can highly influence their properties and applications. Among the normal crystalline phases of TiO 2 (anatase, rutile, brookite), anatase TiO 2 is widely investigated because it has a better photocatalytic activity due to its relatively low charge carrier recombination rate [99]. In a conventional manner, the amorphous as-anodized NTs are annealed to obtain anatase TiO 2 NTs, which usually possess a bandgap of approximately 3.2 eV [100][101][102]. Therefore, we wonder if the bandgap differs when the anatase TiO 2 products are fabricated by the WAC method at low temperatures.
To assess the bandgap of the WAC-treated products, ultraviolet-visible (UV-Vis) absorption spectra of the samples were measured. Liao used a solid-liquid method to crystallize the amorphous TNTs, and Andrea used a solidgas method. They found that the bandgap of the anatase TiO 2 products was close to 3.2 eV (Fig. 12a) [39,55]. Similar bandgap values indicate that the WAC-treated samples absorb similar numbers of photons as the annealed samples. However, in Andrea's work, the TNTs prepared by the solid-gas method exhibited higher efficiency in degrading methylene blue than the annealed TNTs. As the abilities of these materials to absorb photons were very similar, this improvement could be attributed to a high surface area, as discussed above. In addition, the bandgap changed remarkably and was no longer 3.2 eV when the amorphous TNTs were immersed in a solution containing specific ions. For example, the as-anodized TNTs were immersed in DI water and an aqueous solution of ammonia for crystallization [75]. The absorption spectra of the water-treated and the ammonia-treated samples are shown in Fig. 12b. The estimated bandgap of the water-treated sample is approximately 3.2 eV, which is in agreement with previous reports. However, all samples immersed in ammonia solution have higher absorption intensity than the watertreated samples. The bandgap decreased gradually with increasing ammonia concentration, indicating that more light was absorbed. When the ammonia: water concentration ratio was 1:1, the bandgap decreased to 2.84 eV, which could be attributed to an isolated localized state of N 2p (Fig. 12c). It is well known that the annealed anatase TNTs are only activated under UV light (wavelength \ 387 nm), which is only a small fraction (4%) of the solar spectrum. Hence, the narrower bandgap (2.84 eV) leads to a broader absorption spectrum that includes visible light and, subsequently, enhances the material's photocatalytic properties.

Degradation of Pollutants
Recently, various photocatalytic semiconductor materials have been widely investigated [103][104][105]. Among them, TiO 2 has received increasing attention because of its excellent photocatalytic performance in degrading organic   [39,55]. Copyright Ó 2011 American Chemical Society pollutants [106][107][108]. A schematic illustration of the degradation process of TiO 2 is shown in Fig. 13a. First, UV irradiation promotes electrons from the valence band (VB) to the conduction band (CB), and the corresponding electrons (e -) and holes (h ? ) reach the TiO 2 -environment interfaces. In the CB, the electrons on the surface of TiO 2 are easily captured by oxygen dissolved in the solution, forming O2 Áspecies. O2 Áhas a high oxidizing power and, thus, plays a vital oxidative role in the degradation process [109,110]. At the VB, a fraction of photogenerated holes can directly oxidize the pollutants adsorbed on the surface of TiO 2 , and the other holes can react with water molecules to form the hydroxyl radical (OH Á ). Because O 2

Á-
and OH Á possess high oxidative activities, the pollutants are effectively degraded to harmless substances. The related reactions are shown as follows: Liao et al. crystallized amorphous TNTs by immersing them in hot water, and their photocatalytic properties were investigated through the degradation of MO aqueous solution, as shown in Fig. 13b, c [39]. The results showed that the TNTs that received hot water treatment for 6 h exhibited a slightly higher performance than the annealed (450°C) products. Because the crystallinity of the hot water-treated TNTs was not as high as that of the annealed samples, the approximately equal degradation efficiency was attributed to their elevated surface area. With increasing immersion time, the degradation efficiency remarkably increased. The efficiency of a 35-h-immersed sample was nearly four times that of an annealed sample. Hou et al. fabricated anatase TiO 2 by immersing amorphous TNTs in an aqueous solution of ammonia [75]. As expected, the ammonia-treated products also presented a significant improvement over the annealed sample. Although a high surface area is an important factor that notably promotes the contact of TiO 2 and MO aqueous solution, the narrower bandgap of the ammonia-treated products also plays a key role. Such bandgap allows the ammonia-treated products to absorb visible light more efficiently than the annealed sample and, consequently, contributes to their excellent degradation performance.

DSSCs
In recent years, DSSCs have attracted worldwide attention as promising candidates for next-generation photovoltaics [111][112][113]. For conventional DSSCs, the photoanode is usually a mesoporous thin film composed of randomly distributed TiO 2 NPs [114]. Unfortunately, the numerous boundaries between NPs cause a slow diffusion of photogenerated electrons in this system. To circumvent this issue, a variety of 1-D structures, including NTs, nanowires, and nanofibers, have been investigated to optimize the electron transport [115][116][117]. In particular, vertically oriented TNTs have been widely studied as an alternative because of the fast transport of electrons and ions through their TiO 2 layers [118][119][120]. However, the smooth tube walls often have insufficient surface area for dye adsorption and, hence, a relatively poor light harvesting ability, which limits the improvement of conversion efficiency [121,122]. Therefore, it is important to increase the surface area of TNTs and maintain the nanotubular structure at the same time [123,124]. Clearly, the WAC method introduced in this review is more convenient and efficient than other methods for obtaining NPs/NTs that both possess high surface area and exhibit rapid transport. In the following section, we will introduce the basic principles of DSSCs and discuss related studies employing WAC-treated products.
A schematic illustration of the configuration of DSSCs is presented in Fig. 14 [125]. Incident photons are absorbed by dye molecules adsorbed on the TiO 2 NT walls, and electrons are excited from the highest occupied molecular orbital (HOMO) to the lowest unoccupied molecular orbital (LUMO). The excited electrons are injected into the CB of TiO 2 and then travel through the NTs via diffusion toward the back contact, finally reaching the counter electrode through the circuit. Meanwhile, the oxidized dye on the surface accepts electrons from Iin the electrolyte, leading to the regeneration of the ground state of the dye and generation of I 3 -. Then, I 3 diffuses toward the counter electrode and reduces back to I -, completing the cycle [126,127].
A high surface area and nanotubular structure are important factors that ensure that more dye molecules can be absorbed and the recombination rate is restricted. Therefore, the products synthesized by WAC are considered suitable for DSSCs. For example, as-anodized TNTs were immersed in water for several days at RT, transferred, and then applied in DSSCs [47]. After 2 days of immersion, the amount of absorbed dye increased remarkably (by 38.9%) compared with that adsorbed by the as-anodized TNTs. Correspondingly, the DSSCs based on TNTs immersed in water for 2 days exhibited the excellent solar energy conversion efficiency (g) of 6.06%, which is a 33% improvement compared with that of a sample employing untreated TNTs. When the immersion time was prolonged to 3 days, the dye-adsorption ability of the products increased. However, the conversion efficiency of the 3-day sample decreased to 83.3% of the 2-day sample value. Similarly, Zeng et al. fabricated NP/NT products by the solid-gas method and employed them in DSSCs [44]. The samples synthesized at 180°C showed the highest conversion efficiency (up to 8.11%), while the efficiency of the 200°C sample was only 6.4%. This decline was attributed to the elevated recombination rate due to the relatively collapsed nanotubular architecture, which was generated using either a long immersion time or a high temperature. We can conclude that not only a high surface area but also a good architecture is beneficial for efficiency. In Table 2, some photovoltaic parameters of DSSCs based on various photoanodes are listed. Specifically, J sc , V oc , FF, and g represent the short-circuit current density, open-circuit voltage, fill factor, and solar energy conversion efficiency, respectively. SL, SG, and MW represent the solid-liquid, solid-gas, and modified WAC methods, respectively.

Supercapacitors
It is well known that TNT supercapacitors are a type of double-layer capacitors, where a large surface area corresponds to an excellent areal specific capacitance [128][129][130][131]. Therefore, enhancing the NT surface area is considered to be an effective approach to improve the capacitance, and numerous research efforts have been dedicated to it. Hybrid NPs/NTs possessing high surface areas prepared by the WAC method are clearly promising candidates for high-performance capacitors.
Fan et al. first used the hydrothermal solid-gas (HSG) method to crystallize the as-anodized TNTs and adjust their morphology; the HSG-treated sample was then annealed to yield fully crystallized products [53]. As shown in Fig. 15a, b, the as-anodized products had smooth tube walls, while the final HSG-treated products possessed a NP/NT structure, leading to a high surface area. For the supercapacitor performance, all the HSG-treated samples  [125]. Copyright Ó 2012 American Chemical Society exhibit larger integrated areas and higher current responses than the direct-annealed TNTs without HSG treatment, indicating a significant enhancement of capacitance by HSG treatment (Fig. 15c). From Fig. 15d, the calculated areal capacitance of the HSG-180 sample (180 lL water in a 50 mL Teflon liner) was highest, up to 41.04 mF cm -2 , which is 2.96 times that of the direct-annealed TNTs without HSG treatment. The surface area of the HSG-180 sample is 3.16 times that of the direct-annealed TNTs without HSG treatment. The high similarity of these values suggests that the improvement in capacitance could be fully attributed to the enlarged surface area. Furthermore, when the HSG-treated sample was annealed in argon atmosphere rather than air, the areal capacitance of the HSG-180 sample further increased to 50.39 mF cm -2 . It is believed that the oxygen vacancies (Ti 3? ) formed in argon atmosphere lead to superior electrical conductivity and thereby promote areal capacitance. In addition to using deionized water, immersing the as-anodized TNTs in the aqueous solution containing some ions is also an appealing approach. In Cui's work, the specific capacitance of the products prepared through immersion in (NH 4 ) 2 TiF 6 solution was 2 times higher than that of a sample treated in deionized water under the same conditions [81].  In summary, WAC-treated TNTs are suitable for many applications owing to their advantages of high surface area and structures that can be easily controlled by adjusting experimental parameters, such as immersion time and treatment temperature. In addition to the applications mentioned above, TNTs are also widely used in water splitting cells, gas sensors, biomedical coatings, drug delivery, etc. [132][133][134][135][136][137]. Thus, we foresee the WAC strategy to be employed in these fields in the future.

Other Materials
In the above sections, we have detailed the WAC strategy mainly as it regards TiO 2 NTs. The WAC method can be used for many other materials that can be classified as TiO 2 -based materials and other metal oxides.

TiO 2 -Based Materials
In addition to TiO 2 NTs, there are a variety of nanostructured TiO 2 materials, such as TiO 2 nanospheres (TNSs) and nanofibers (TNFs). Different from the TNTs usually prepared from Ti substrate by anodization, TNSs and TNFs can be synthesized by various methods, including sol-gel, solvothermal, hydrothermal, and electrospinning methods [138][139][140][141][142]. Despite the large differences in synthetic methods and morphologies, the WAC method is also considered suitable for crystallization and controlling the morphology of TNSs and TNFs.
TNSs As shown in Fig. 16a, Li et al. used the WAC method to fabricate porous anatase TNSs based on amorphous nanospheres prepared by the sol-gel technique [143]. Figure 16b shows a TEM image of pristine nanospheres just after the sol-gel process. The as-prepared nanospheres were sticky and tended to aggregate because of the presence of oligomers formed during hydrolysis. After the WAC, the original nanospheres became quite porous with the emergence of numerous NPs (Fig. 16c). When the water treatment time was prolonged, the nanospheres became more porous, and the aggregation tendency was notably relieved. In this transformation process, water mainly plays the following roles: (1) water dissolves the oligomers on the surface of as-prepared nanospheres restricting aggregation, and (2) water assists dissolutionprecipitation, which eventually causes the formation of anatase grains, which are responsible for the pores of the finally obtained TNSs. The crystallinity and surface area of the TNSs were controlled by adjusting either the water treatment time or temperature. With increasing water treatment time, the crystallinity enhanced (Fig. 16d). In particular, crystalline TNSs were highly porous, reaching a surface area of as high as 647 m 2 g -1 under appropriate conditions (treatment temperature: 75°C), which is remarkably higher than the values reported in previous reports (Fig. 16e). Because of their high surface area and good crystallinity, the porous TNSs show better performance in phosphoprotein enrichment than commercial anatase products.
Joo et al. reported that porous, hollow TNSs can also be synthesized employing the WAC strategy [144]. As shown in Fig. 16f, the synthetic procedure was as follows: (1) a SiO 2 @TiO 2 core-shell structure was first prepared by a sol-gel technique; (2) the as-prepared SiO 2 @TiO 2 nanospheres were crystallized in water, resulting in a porous and crystalline TiO 2 shell; and (3) the SiO 2 core was removed, resulting in the successful fabrication of porous hollow TNSs. The corresponding morphology transformation is presented in Fig. 16g, h; it shows that porous hollow nanospheres were successfully prepared. Moreover, XRD results confirmed the transition from an amorphous form to the anatase phase after water reflux treatment. In addition, many other relevant studies have also been reported, and the WAC method is considered to be cost-effective and convenient in preparing porous TiO 2 nanospheres [145][146][147][148].
TNFs TNFs, as one of the most important 1-D nanomaterials, have received extensive attention, and various methods have been developed for synthesizing them [149,150]. Among the methods, the electrospinning technique is considered to be very promising owing to its versatility and flexibility [151][152][153]. Although TNFs have been investigated systematically in many ways, there are few reports about the effects of water on electrospinning TNFs. As water plays an important role in adjusting the properties of TNTs and TNSs, it can be speculated that electrospinning TNFs would also be affected by the presence of water.
In 2017, Jin et al. fabricated porous and crystalline TNFs by a simple water steam treatment without any template agents [154]. Similar to the previous WAC results, the morphology of the nanofibers greatly changed after water steam treatment and was highly dependent on treatment temperature. SEM images of the TNFs under water steam treatment at various temperatures are presented in Fig. 17. When the precursor nanofibers were treated at 150°C for 2 h, the surface of the nanofibers became rough, and some pores emerged (Fig. 17a, b). With increasing temperature, the surface became rougher, and the diameter of the pores increased ( Fig. 17c-f). Specifically, the average pore sizes of the 150, 350, and 550°C samples were 3.63, 8.84, and 13.95 nm, respectively. After steam treatment, the original nanofibers became crystalline, and the crystallinity of the obtained TNFs increased with the temperature elevation (Fig. 17g), similar to the behavior of the TNTs mentioned above. Figure 17h, i presents TEM results of a sample prepared at 550°C; they show that the rough nanofibers were composed of anatase NPs with a diameter of 30 nm. Because the vapor-treated nanofibers were composed of NPs, the porous TNFs exhibited higher surface areas than the annealing sample (Fig. 17j). The highest surface area of the water steam-treated TNFs was 128.07 m 2 g -1 , while that of the TNFs that were annealed in air was only 9.85 m 2 g -1 . This large difference can be attributed to the dissolution-precipitation process under water steam. Sun et al. also prepared TiO 2 nanoflowers through the dissolution-precipitation mechanism [155]. It can be concluded that the WAC strategy is applicable to TiO 2 -based materials.

Other Metal Oxides
The as-anodized amorphous TNTs can be transformed into the anatase phase with water treatment through the dissolution-precipitation process, in which the TiO 6 octahedra rearrange and form the unit cell of anatase TiO 2 . Although this type of WAC mechanism can be extended to other TiO 2 nanomaterials, their basic building blocks are still TiO 6 octahedra. Therefore, we wondered whether the WAC mechanism is applicable to metal oxides that contain no TiO 6 octahedra.
Nanostructured tin oxides (SnO 2 ) synthesized by anodizing tin foils have been widely investigated in various areas [156][157][158] Fig. 16 a Schematic illustration of the water-assisted crystallization process for preparing porous anatase TiO 2 nanospheres from sol-gel derived amorphous particles. b TEM images of the original amorphous TiO 2 spheres. c TEM images of the samples after immersing in water at 75°C for 30 min. d XRD patterns of products obtained by immersing in water at 75°C for different time periods. e The change of surface area as a function of heating time period for samples treated at different temperatures. f Schematic illustration of the water-assisted crystallization strategy for conversion of amorphous TiO 2 layer to mesoporous crystalline shells. Typical TEM images of the samples at different preparation steps: g SiO 2 @TiO 2 core-shell structures prepared by sol-gel coating and h mesoporous TiO 2 hollow nanostructures after removing SiO 2 cores [141,142]. Copyright Ó 2011 Elsevier B.V. and 2006 American Chemical Society nanomaterials are amorphous and not suitable for many applications, such as gas sensing and energy storage [159,160]. Because the melting point of the Sn substrate is approximately 230°C, using the conventional annealing method (500°C) to crystallize the as-anodized SnO 2 is impracticable. Some researchers focused on the interesting amorphous-anatase transformation of the as-anodized TiO 2 NTs and developed a convenient way to obtain crystalline SnO 2 at low temperatures. In 2017, Bian et al. used the WAC method to crystallize as-anodized SnO 2 for the first time [161]. To be specific, the anodization of tin was first carried out with tin foil as the anode in an oxalic acid aqueous solution. Then, the amorphous as-anodized SnO 2 was immersed in deionized water at various temperatures (25, 40, 80, or 100°C) for different durations. Although no clear change was observed when the as-anodized sample was immersed at 25°C for the short time of 2 h (Fig. 18a,  b), prolonging the immersion time to 168 h effectively crystallized the amorphous sample. In addition, the higher treatment temperature accelerated the crystallization. Both digital photographs and SEM images of the products prepared at 60°C are quite different from those of the as-anodized and RT-treated samples. As the building blocks of SnO 2 (amorphous and rutile) are SnO 6 octahedra, similar to TiO 6 octahedra in TiO 2 , the Bian group proposed a mechanism explaining that the transformation from amorphous to rutile SnO 2 was assisted by water soaking (Fig. 18c). This mechanism also includes a hydration-dehydration process similar to that of TiO 2 , as discussed in Fig. 3c. As shown in Fig. 18e, TEM and SAED images reveal the porous structure and amorphous nature of the asanodized SnO 2 . After the samples were soaked in water at 60°C for 2 h, clear and strong diffraction rings assigned to rutile SnO 2 appear (Fig. 18f), indicating successful amorphous-crystalline transformation with the assistance of water. The WAC-treated SnO 2 products were applied in sodium-ion storage and delivered excellent performance, as shown in Fig. 18g.
In addition, the WAC method was also proven to be applicable to the as-anodized iron oxides in our previous work [162]. The facile WAC method is appropriate for the crystallization of not only TiO 2 NTs but also many other metal oxides at low temperatures.   and e, f 550°C. g XRD patterns of the samples heat-treated at different temperatures in water steam. h, i HRTEM and SAED images of the water steam-treated TiO 2 nanofibers prepared at 550°C. j Nitrogen adsorption-desorption isotherms of the samples heat-treated at different temperatures in water steam [152]. Copyright Ó 2009 Elsevier B.V

Conclusion and Outlook
The WAC strategy has been extensively studied and it is considered to be an efficient and convenient approach to crystallizing amorphous TiO 2 NTs at low temperatures. In this review, we have summarized various aspects of the recent progress in using this strategy. The basic WAC method is simply immersing as-anodized TNTs in water, during which the disordered TiO 6 octahedra are rearranged with the assistance of water. Although many modified methods have been developed, water molecules still play the most important role in causing the amorphous-anatase transformation. In addition, the WAC strategy can also be employed for doping metal or nonmetal elements into TNTs by using solutions containing different ions. Because of the dissolution-precipitation process, some crystalline TiO 2 NPs emerge on the tube walls, leaving a rough surface feature, which is quite different from the tube walls of the annealed products. Because of the numerous NPs, the WAC-treated products usually possess a high surface area. showing the transformation from amorphous to rutile SnO 2 assisted by water soaking. TEM images of the SnO 2 samples e as-anodized and f after water soaking at 60°C for 2 h; the insets show the corresponding SAED patterns. g Long-term stability profiles and Coulombic efficiency of the water-crystallized SnO 2 at 0.3 C for 500 cycles [159]. Copyright Ó 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim Furthermore, we can control the morphology of the samples by adjusting experimental parameters, such as the immersion time and treatment temperature. Combining the merits of 1-D architecture and high surface area, the WACtreated products show excellent performance in many applications, including photocatalysis, DSSCs, and supercapacitors. It should be noted that the WAC mechanism is not only applicable to amorphous as-anodized TNTs; it was proven that many other TiO 2 nanomaterials prepared by various techniques can also be crystallized through this type of WAC method. Despite many clear advantages of the WAC strategy for crystallization, there are still some drawbacks, such as the relatively long crystallization time and low degree of crystallinity. Therefore, optimizing the WAC method to overcome these challenges requires further study. Although we have shown that the WAC strategy is also applicable to as-anodized tin or iron oxides, there are still many metal oxides that have not been investigated in this sense. Hence, another topic that must be further studied is the expansion of the WAC method to other metal oxides. We hope that this review will motivate the development of WAC strategies in more fields and inspire researchers in lowtemperature crystallization.