Growth of an Ag3Sn Intermetallic Compound Layer Within Photovoltaic Module Ribbon Solder Joints

In this study, the characteristics of growing an intermetallic compound(IMC) layer at solder joint in photovoltaic (PV) ribbon solder joint were investigated through the thermal ageing test. Also, the growth rate of IMC in the ribbon solder joint, which depend on the temperature and time, was predicted through the ageing test. That the ageing test were performed under three different conditions: 90 °C, 120 °C and 150 °C. Also, we prepare the two type solder composition(60Sn40Pb, 62Sn2Ag36Pb) to analyze Ag addition effect in solder to forming IMC layer. Following testing, the IMC layer formed Ag3Sn in Ag sintered layer by Sn diffusion phenomena at high temperature. The thickness of Ag3Sn in solder joint was measured by cross-section images during the thermal ageing test. The Ag3Sn IMC layer was filled in sintered Ag layer in 70 h under the harshest conditions of 150 °C and 750 h at 120 °C. The Ag3Sn thicknesses were calculated to activation energies forming IMC layer in solder joints. The results, the Ag3Sn growth rates under the various temperatures were predicted for long-term reliability of PV modules.


Introduction
The generation of power from renewable sources has been expected to bridge the gap between global power demands and the current supply of power. Direct conversion technologies based on solar photovoltaics possess several positive attributes and appear to be very promising [1,2,5,11,21,28,30]. Photovoltaic industries and related research have been growing rapidly. Photovoltaic (PV) modules generally consist of many solar cells that are connected to supply a required terminal voltage and current rating. In the field, solar arrays exhibit faults such as their power output being less than the sum of the output power of the constituent solar cells [19]. This drop in power has been attributed to solar ribbon disconnects [4,15,17,18,20], thermal loading [25], EVA yellowing [26,27] and other defects. Among the potential source of defects, the intermetallic compound (IMC) layer in solar ribbon solder joints has contributed to serious damage with regard to PV modules. Because the IMCs exhibit low toughness and brittle mechanical behavior, solar ribbon solder joints are weak to external forces. Damage due to cracks and solar ribbon disconnection play a crucial role with regard to the reliability and electrical performance of PV modules. Also, the formed IMCs within solder joint interfaces the affect increasing of series resistance, and the increased series resistance could be degrade the electric performance of PV modules [3,14]. IMCs form in solder joints due to diffusion processes when PV modules are exposed to high temperatures. IMCs form within solder joints due to interfacial reactions between the Cu/solder and solder/Ag interface. During the packaging of microelectronics, studies have investigated interfacial reactions between Cu pads/solder [13,32]. However, solar ribbon solder joints bonded onto 1 3 sintered Ag possess porous structures and exhibit different tendencies from microelectronic systems with regard to interfacial mechanisms and composition. Within microelectronics packaging, electrical connections between solder and Ag electrodes are not recommended for long-term applications due to Ag leaching phenomena [16]. For these atomic diffusions and forming IMCs layer, the various method have being tested. PV ribbon solder joints should thus be evaluated by various tests for long-term reliability. We focused on solder properties about addition materials such as Ag. The added Ag in SnPb solder could make the fine solder grain size, it also cause the reinforcement mechanical properties of solder joints.
In this study, solar ribbon solder joints were tested for analyze Ag 3 Sn suppression effect by added of silver (Ag). The solar ribbon joints were bonded by SnPb and SnAgPb solders, and exposed to high temperatures, the formation and growth of Ag 3 Sn via diffusion in the solder-sintered Ag interface was investigated to analyze thermal degradation within the PV module. Additionally, activation energies with regard to the growth and formation of Ag 3 Sn were calculated by measuring the growth gradient of Ag 3 Sn via temperature test levels. The growth rates of Ag 3 Sn in various temperature within solder joint were predicted for secure the long-term reliability of PV module.

Experiments
Mini PV modules, which were used to construct a PV module array, were manufactured to facilitate in dealing with thermal aging as shown in Fig. 1. To manufacture the mini PV modules, solar ribbons were bonded to the front electrodes of mono-crystalline silicon wafers that were 238.95 in area; the wafers were indurated to yield the following device layer structure: back sheet/ethylene vinyl acetate (EVA)/wafer/EVA/glass through a lamination process. The lamination process was performed at 150 °C, with 360 s spent under vacuum, 30 s under pressure and 540 s of curing. Two different compositions of solder were used for the tabbing process, which bonded the solar ribbon to the sintered Ag front electrodes. One solder composition consisted of 60Sn40Pb, while the other was 62Sn2Ag36Pb, which were supplemented with tin (Sn) and lead (Pb) leaching defects. Recently, Pb will be regulating by restriction of the use of Hazardous Substances in EEE(RoHS) in EU, it have been still used widely in industries. In this study, the basic SnPb systems were considered for analyze Ag addition effect. The addition of 2% silver (Ag) to the Sn-Pb solder had the effect of controlling the tin (Sn) and lead (Pb) leaching phenomenon in solder during thermal aging while also enhancing its mechanical properties [7,24]. Two different solder compositions were selected as shown in Table 1.
The general PV module ribbon solder joint is a sandwich structure consisting of the following layers: solder/ copper (Cu) core/solder/sintered silver (Ag)/silicon (Si) wafer. A thermal aging test was performed to analyze thermal degradation effects such as solid-state diffusion, coarsening and metallography changes with regard to the PV ribbon solder joints. Thermal aging was performed by following the JESD22-A103C test method with various test levels (A condition: 90 °C, B condition: 120 °C, G condition: 150 °C) within a 1000-h period. The thermal aging testing conditions were selected to be higher than 85 °C because the Ag 3 Sn intermetallic compounds (IMC) would be activated and would grow rapidly at 85 °C or higher [9,22]. After thermal aging, the PV ribbon solder joint was cut, mounted in epoxy resin, and polished to yield clear cross-sectional images. These images were obtained via optical microscopy and scanning electron microscopy (SEM); the thickness of the Ag 3 Sn IMC was measured via energy dispersive X-ray (EDX) spectrometry.

Results and discussion
In this study, Sn diffusion phenomena [8,10] was verified; the Ag 3 Sn IMC was formed via Sn diffusion from the solder and sintered Ag interface toward the inside of the sintered Ag layer when the PV ribbon solder joint was exposed to high temperatures. The Ag 3 Sn microstructure exhibited spheroidized and needle-like structures [6,12,23], yielding implications with regard to strengthening mechanisms as dislocations climbed over the Ag 3 Sn particles [29]. Joints with small spherical Ag 3 Sn particles were stronger than those exhibiting needle-shapes. However, the Ag 3 Sn layer would become weak due to thermal fatigue and cracks from coarsening phenomena when grown at the solder interface [31]. The growth of Ag 3 Sn should thus be analyzed to ensure the reliability of PV modules exposed to high temperatures. Figure 2  The results thus showed the addition of 2% silver (Ag) hardened the mechanical properties of solder, but had no effect with regard to suppressing tin (Sn) diffusion and controlling IMC growth at the solder and sintered Ag interface.
The activation energy of Ag 3 Sn growth was subsequently calculated using the IMC growth rate data, which was obtained in this study. The results showed that the growth of Ag 3 Sn IMC was both time-and temperature-dependent. The growth thickness was proportional to time, while the growth rate depended on temperature. Also, the IMC layers were believed to be sufficiently thick and it was assumed that control over growth kinetics of the IMC layer thickness was solely via diffusion [9,24]. We substitute Eq. (1), which was a modified Arrhenius equation. Y represents the diffusion product, Y 0 is the initial diffusion product, and t is time: Y 0 is the initial thickness of Ag 3 Sn and D is the diffusion coefficient to form Ag 3 Sn, which is time-dependent. Equation (2) was obtained by modifying Eq. (1) to be a function of the diffusion coefficient (D): D 0 is a temperature-independent constant, Q is the activation energy for diffusion, R is a gas constant, and T is the absolute temperature. To calculate Q, the natural logarithm of Eq. (2) was taken to yield Eq. (3): Equation (3) consists of ln D as a dependent variable with a linear form and 1/T as an independent variable. The activation energy could be calculated as a gradient from a reciprocal of the temperature and diffusion coefficient (D). In this study, the activation energies for SnPb and SAP solder were calculated to be 85.85 kJ/mol and 81.24 kJ/mol, respectively. The activation energies were similar regardless of solder composition because the addition of 2 wt% silver (Ag) did not suppress the diffusion of tin (Sn) in solder (Fig. 5).
When the PV module was exposed to heat, the duration at which the Ag 3 Sn layer was observed to grow until reaching a thickness of 18 um in the sintered Ag of the PV ribbon solder joint, was predicted from the calculated activation energy value in this study. The experimental values of the IMC growth rates at all temperatures (150 °C, 120 °C, 90 °C) were assumed to be linear for ease of analysis; trend lines for each temperature were derived from the experimental data with natural logarithm substitution. The prediction value (time), which was the growth of Ag 3 Sn in sintered Ag, was calculated from the trend lines shown in Figs. 6 and 7. It was thus predicted that the time required for Ag 3 Sn to fill the sintered Ag was 24 h (1 day) when exposing the PV ribbon solder joint to a temperature of 180 °C, 238 h (10 days) at 135 °C, 1482 h (62 days) at 105 °C, and 42,754 (1781 days) hours at 60 °C for the SnPb solder joint.  Future studies on degradation related to IMCs and thermal effects should be performed. Also, the correlations between Ag 3 Sn IMC and efficiency of PV module must be investigated to ensure the reliability of PV ribbon solder joints.  OpenAccess This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creat iveco mmons .org/licen ses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.