Low-temperature synthesis of doped MnO2–carbon dots nanocomposite: an analysis of nanostructure and electrical properties

The synthesis of δ-MnO2, δ-MnO2 carbon dots nanocomposite, and Fe/Cu-doped δ-MnO2 carbon dots nanocomposite has been successfully carried out through a stirring process at room temperature and 80 °C. The synthesized powder shows a low crystallization determined through XRD and TEM analysis. Furthermore, the carbon dots are well attached to MnO2 performing a core–shell composite material, while the doping ions Fe and Cu were incorporated into the matrix substitute Mn in the MnO6 octahedron, although potassium ions were also detected. The manganese possess an oxidation state of + 3 and + 4, which promotes the oxygen vacancy creation VO··\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$${V}_{\mathrm{O}}^{\cdot\cdot}$$\end{document} denoting the conductivity decrease.


Introduction
The use of fossil energy nowadays is being worked on to minimize its utilization due to causing a problem, i.e., is a limited source and the root of an environmental issue.The use of alternate energy becomes intriguing.Correspondingly, the need for adequate energy storage in the sense of highly possessing power and energy density becomes imperative, such as batteries and supercapacitors.In supercapacitors, the charge-discharge cycle mechanism and charge stored are reversible.Metallic oxide is an alternative for an electrode material that holds high specific capacitance and low resistivity.Typical metal oxide materials were reported, RuO 2 , MnO 2 , NiO, Co 3 O 4 , and NiCo 2 O 4 [1].Manganese oxide is among the most interesting due to its high theoretical specific capacitance (1370 F gr −1 ), low cost, and environmentally friendly [2].
Given the structure, manganese oxide behaves in polymorph structures α, β, γ, δ, and λ-type MnO 2 .The polymorphism can be described by the number of octahedral sub-units (n × m), where n and m stand for the dimensions of the tunnels in the two directions perpendicular to the chains of the edge-sharing octahedral MnO 6 .The α-type structure is characteristic of (2 × 2) and (1 × 1) of MnO 6 octahedra units aligned along the c-axis.The β-MnO 2 is characterized by one-dimensional chains of MnO 6 octahedra aligned along the c-axis to form (1 × 1) size vacant tunnels.γ-MnO 2 type structure is an intergrowth structure consisting of (2 × 1) and (1 × 1) tunnels.The δ-type MnO 2 has a layered structure; each layer is composed of edge-sharing MnO 6 octahedra.Finally, the λ-type MnO 2 has a defective spinel structure [3].It was reported that these structures possess thermal stability order β > α > γ > δ ≈ λ [4].
The use of MnO 2 as charge storage was involved in the capability of the manganese oxidation state alteration Mn 3+  and Mn 4+ inside the octahedron MnO 6 presenting defect [5], and hence, the storage capacity can be improved through doping creating defects.Metallic ions, such as V, Ru, Ag, Co, Ni, Sn, Cu, and Fe, were reported as successful dopants for Mn [16,17,22,23].Previous studies revealed that Feand Cu-doped α-MnO 2 [6,7], both Fe and Cu present a mixed oxidation state Fe +3 , Fe 4+ , and Cu 2+ , Cu 3+ , while Mn 3+ , Mn 4+ .This creates defects Fe � Mn , Cu � Mn , Mn � Mn , and The Cu 2+ has large size, may filled tunnel (2 × 2) otherwise substitute Mn creating Cu �� Mn .Given the dopant percentage, 5% of dopant Cu and Fe is the plausible characteristics in view of conductivity and permittivity.Moreover, decreases in the average crystallite size have two effects, reduce the appearance of lattice strain, increase the effective surface area, and finally facilitate the charge transfer during the charging and discharging processes.In parallel, to increase the conductivity, carbon-based material was usually used as an improver [8].Several types of supercapacitors were reported, among them was a carbon base supercapacitor developed through an electric doublelayer capacitor (EDLC) to include carbon nanotubes (CNTs), activated carbon, carbon black, and carbon fiber [9][10][11].On the other hand, carbon dots (CDs) have a small dimension (≈ 10 nm) which is considerable attribute including enhanced electron transferability, long-term chemical stability, negligible toxicity, and acquaintance of large effective surface areato-volume ratio [12].Nanostructures and composite material engineering are effective methods for improving electrode capacitive performance.The core-shell structure has been shown to be an effective technique for improving the electrochemical performances of nanocomposites, resulting in improved electrical conductivity, shorter ionic transport, and stronger bonds [13].Given the good sense above, the material composed of MnO 2 -doped containing carbon should be expected to give an exceptional characteristic.
Various synthesis methods have been reported, i.e., sol-gel [14], coprecipitation [15], electrodeposition [16], hydrothermal reaction [17], and oxidation-reduction (Redox) method [18].The redox reaction is a simple method for producing selective MnO 2 with high specific capacitance.The production of MnO 2 by such a process has the benefit of being a very rapid, one-pot reaction that is performed at a low temperature and takes shorter, and the technique is fulfilled by basic laboratory equipment [19].Given the previous synthesis methods, it is intriguing to pursue the synthesis of doped MnO 2 /CDs nanocomposites at low temperatures to simplify synthesis suitable to electrochemical storage such as supercapacitors.To discover the description of the synthesized powder, MnO 2 /CDs' nanocomposite that will be synthesized based on a redox reaction between Mn 2+ and Mn 4+ , mixed with CDs and further 5% of the metal transition Fe 3+ and Cu 2+ as dopants.

Synthesis of carbon dots (CDs)
The CDs were completed using a one-step hydrothermal process with glucose, and 6 g of glucose were dissolved in 60 ml of deionized water by stirring for 30 min.The solution was then transferred to a 100-ml stainless-steel autoclave with a Teflon lining, which was subsequently put in a 180 °C oven for 2 h.The autoclave was naturally cooled to room temperature, and the CD solvent was acquired.After the hydrothermal treatment, the translucent suspension turns brown.The produced brown suspension was centrifuged at 4500 rpm for 15 min and filtered through a 0.22-μm filter.

Synthesis of δ-MnO 2
In this study, we applied a mixed oxidation-reduction process using MnCl 2 and KMnO 4 to synthesize δ-MnO 2 , following the redox reaction: In a typical MnO 2 synthesis, 0.712 g of MnCl 2 .4H 2 O was ultrasonically dissolved in 60 ml of distilled water for 1 h.Following that, 0.948 g of KMnO 4 was added to this solution, which was then stirred for about 10 min at room temperature and continued for 1 h at 80 °C, and the pink color of permanganate changed to brownish-black.The product was washed several times with deionized water and ethanol until the filtrate became neutral, then dried at 80 °C for 2 h.The sample δ-MnO 2 was referred to as M-0 and MS for stirring at room temperature and 80 °C, respectively.

Synthesis of δ-MnO 2 /CDs nanocomposites and doped samples
Because of the thin-layered structure of graphene [20], almost all of the carbon atoms are reactive; thus, it can be oxidized by MnO 4  − ions in an acid solution via the following chemical reaction: Given the thin carbon dot (CDs) size, it is expected that the above reaction will occur in the case of MnO 2 /CDs (MnO 2 + xC).In this procedure, 7.12 ml CDs solution was added to a solution of MnCl 2 .4H 2 O, followed by a similar preparation as above.MnO 2 /CDs nanocomposites were made using the stirring method at low temperatures (room temperature and 80 °C).The products are abbreviated as MC-0 and MCS.The schematic of this process is shown in Fig. 1.To synthesize Fe-and Cu-doped nanocomposite samples, FeCl 3 •6H 2 O and CuCl 2 •2H 2 O (5 mol%) were used as dopant reagents and added to the above solution and proceeded similarly.

Characterization
The phase and crystal structure of MnO 2 were investigated using X-ray diffraction (XRD Philips X'Pert) with Cu-K (1) (2) radiation at 30 mA and 40 kV, step scan 0.02°, and Bragg angle range of 5°-60°.Through the match, phase identification was accomplished!Software.Fast Fourier transform infrared (FTIR) measurements were used to determine the chemical structure of MnO 2 and nanocomposites.
Field emission scanning electron microscope (FESEM) images and other element maps involving energy-dispersive X-ray (EDX) analysis were used to determine the morphology.Using ImageJ software, the numerical dimension of each sample was obtained by averaging the diameters of nanorods from different samples.
X-ray photoelectron spectroscopy (XPS) analysis data were obtained with an Axis Ultra DLD system equipped with an Al monochromatic was carried out to analyze the oxidation state of Mn and other elements in the sample.
Electrical measurements were taken on powder that was inserted between two copper electrodes and then uniaxially pressed with a 13 mm diameter.The data were collected using a Solartron Impedance Analyzer SI 1260 at room temperature with a frequency range of 0.1 Hz to 32 MHz and an applied voltage of 1 V.

Results and discussion
Powder assessment using X-ray diffraction and FTIR X-ray diffraction (XRD) studies have been used to identify the presence of the different phases/purity of synthesized MnO 2 and MnO 2 /CD nanocomposites.The X-ray diffraction spectra of the MnO 2 and MnO 2 /CDs composite mixed at room temperature are presented in Fig. 2a.It is noted that diffraction peaks show broad peaks at 2θ around 37°, which can be indexed to δ-type MnO 2 (JCPDS 42-1317).Further analysis, the γ-type MnO 2 (JCPDS 14-0644) [21] seems to be matched with the spectra MC0.It was reported that in processing at low temperatures [3], either γ-phase or δ-phase was formed.Therefore, it can be considered as a mixed phase of δ and γ-MnO 2 .Broad peaks are related to a coincidence of diffraction peaks of (110) of the δ phase and (131) of the γ phase, besides, a poorly crystallized compound originating from the small grain size and approximately amorphous state of the powder.The δ-phased MnO 2 is a 2D layered structure with an interlayer separation of ~ 7 Å between the MnO 6 octahedra, in which a large number of stabilizing cations, such as K + and H + , were considered to fill those spaces.While the γ-MnO 2 contains octahedrons chain corner and edge-sharing producing (2 × 1) and (1 × 1) tunnel.In another disparity treatment, the sample was then stirred at a temperature of 80 °C for an hour.The spectra of X-ray diffraction on MnO 2 samples, MnO 2 /CDs' nanocomposites, and Cu-and Fe-doped samples are shown.
XRD patterns confirm MnO 2 /CDs with mixed crystalline and amorphous parts, δ-MnO 2 and γ-MnO 2 exhibited low intensity and broad diffraction peaks at 37°, which is typical of hexagonal randomly stacked and single-phased Birnessite-type MnO 2 [23].The diffraction peaks of MCS had not changed when compared to MnO 2 .The MnO 2 /CDs were no longer pure MnO 2 phases, but the contours of the peaks were nearly identical.Therefore, it can be concluded that the presence of CDs does not change the crystal structure of MnO 2 .
Further investigation was conducted by FTIR measurements to characterize the chemical structure of MnO 2 and nanocomposites.Figure 2b shows the FTIR spectra of MnO 2 and MnO 2 /CDs with different methods of preparation, i.e., stirred at room temperature and 80 °C.The peaks presented at 518 cm −1 and 524 cm −1 are attributed to the stretching vibrations of Mn-O-Mn.A broad peak centered at 3444 cm −1 and a shoulder peak at 1645 cm −1 reveal the existence of hydroxyl groups on the surfaces of materials.The existence of CDs was demonstrated by the characteristic absorption at 1200 cm −1 in which the former was signed to the C=C vibrational stretch.The undetected signal of Cu and Fig. 1 The schematic of the synthesis procedure for MnO 2 and MnO 2 /CDs' nanocomposites Fe dopants should be considered that its low concentration and substitute Mn in BO 6 octahedron makes it signal covered by Mn-O-Mn-stretching vibration.

Microstructure and structure analysis through FESEM/TEM
Field emission scanning electron microscope (FESEM) analysis is used to decipher the surface morphology of the as-obtained δ-MnO 2 and composites material (Fig. 3a).All sample shows spherical morphology with a flower-like type of nanostructures, with a diameter of about 300 nm.The addition of CDs to MnO 2 causes the surface of the nanocomposite's appearance to be smoother, which indicates the presence of CDs attached to the surface of MnO 2 .
Further analysis using EDX, Fig. 3b shows the MCS-Fe sample for representatives, and the similar fashion for other samples should be referred to supplement Fig. 1S.It was observed the K + ion residue on all synthesized materials, which may fill in between layers due to its ionic size makes K + not substitute Mn 4+ in MnO 6 octahedron.Dopants Fe and Cu were detected which indicates that dopants were incorporated in the MnO 2 matrix a priori substitute Mn in MO 6 octahedron.Furthermore, carbon was also detected, which confirmed the FTIR and FESEM analysis given previously.
Further detailed analysis insight into the morphology, TEM analysis, and SAED were used in MC's samples.Figure 4 shows the shape of the morphology of MCs that flower type which is similar to that of FESEM.Furthermore, at higher magnifications up to 300.000 × (Fig. 4b), the grains are observed as typically elongated nanorods of the dimension ≈ 2 nm (width) and ≈100 nm (length) and shortened in Fe/Cu-doped sample.It is also the core cell type grains shown by the MCS sample (Fig. 4b inset) that signifies MnO 2 grains are covered by CDs, while noncarbonated sample MS are absent from carbon cells.This occurrence reinforces the analysis given by FESEM and EDX previously.
The SAED pictures show a circles fringe indicating polycrystal diffraction and are indexed as (110) and (020) reflection planes of δ-MnO 2 (Table 1); however, a wide fringe is presented which is an indication of low crystalline arrangement; otherwise, the coincidence of the reflection plane owing to γ-MnO 2 as described in XRD analysis previously and CDs coated grains.

XPS analysis
The elemental composition and surface functional group types of δ-MnO 2 (MS), δ-MnO 2 /CDs composite (MCS), and Fe/Cu-doped MnO 2 /CDs (MCS-Fe, MCS-Cu), as well as the state of Mn and O in the materials were studied using XPS. Figure 5 shows the MCS-Fe sample of the XPS survey spectrum and the deconvolution of selected peaks highresolution spectrum of Mn3s, C1s, O1s, Mn2p, and Fe2p.Further data should be referred to in Fig. 2S.It demonstrates that the composite is primarily made up of the elements Mn, C, and O.The high-resolution XPS of Mn2p is shown in Fig. 5e (so did for other samples depicted in Fig. 2S); there are three distinct characteristic peaks at 641.92 eV, 643.75 eV, 653.52 eV, and 654.35 eV which are indexed to Mn2p 3/2 and Mn2p 1/2 , respectively (Table 2).While the  energy difference between Mn2p 3/2 and Mn2p 1/2 characteristic peaks is 11.80 eV, it proves the presence of Mn in the form of + 3 and + 4 valence in the composite material.Based on high-resolution XPS spectra of Mn2p and O1s, it can be decided that the Mn element in the composite is in the form of MnO 2 .The Mn 3 s is used to calculate the average oxidation state of Mn, with reducing energy separation among the 7 S and 5 S multiplet associated with an increasing oxidation state [24].From the deconvolution process using Gaussian function, Mn3s spectrum analysis (Fig. 5b), possessing a spin-energy splitting of 4.77, 4.57, and 5.03 eV and using Beyreuther equation [25], revealed the average oxidation state of Mn are 2.832, 3.594, 2.009, and 2.648 5.384, 4.784, 6,032 and 5.529 for MS, MCS, MCS-Fe, and MCS-Cu, respectively.This demonstrates that the average oxidation states (AOS) of Mn are Mn 3+ and Mn 4+ .All deconvolution of Mn 2p peaks as well as the AOS are presented in Table 2.
The deconvoluted O1s spectrum (Fig. 5d) can be fitted with the presence of an Mn-O-Mn bond (cantered at 529.49 eV), and an Mn-O-H bond (531.1 eV) belonging to defect oxide or hydroxyl-like groups [26].The lattice oxygen Mn-O-Mn content was gradually decreased with the carbon and dopant (Fe, Cu), with the areal of Mn-O-Mn over MS, MCS, MCS-Fe, and MCS-Cu summarized in Table 2. Another important difference in the O 1 s spectra of MCS nanocomposites compared to that of doping samples is the decrease in the relative intensity of peak, which can suggest a decrease in the number of Mn-O bonds.This may be due to the existence of Mn 3+ , Fe 2+ , Fe 3+ , or Cu 2+ species on the surface, indicating the possibility of oxygen vacancies in the sample.Additionally, to study the structural configuration of carbon dots and their defects (such as vacancies and disorder) in MnO 2 /CDs' nanocomposites, the C1s peak of MCS-Fe was deconvoluted into three peaks with binding energies of 284.73 eV is related to C = C/C-C graphitic structure (sp 2 ), 286.26 eV attributed to C-O in hydroxyls, epoxy groups, and phenols, and 288.09 eV associated with C=O/C-OOH in ketones, aldehydes, and quinones [27].An addition of CDs has a significant effect on the composition of the C-C/ C=C functional group.Meanwhile, Fe and Cu doping caused a level shift of binding energy that tend to interact between dopant and carbon and confirms the presence of defects and vacancies in this sample.The FWHM of nanocomposites varies in the range of 1-2.5 eV.
Deconvolution of Fe2p revealed the energy characteristic Fe 3+ at 710.82 eV and 712.58 eV 2p 3/2 , while the 2p 1/2 indicated Fe 3+ at 724.71 eV.Furthermore, Cu 2p peaks, which include Cu 2p 3/2 peak at 935.34 eV to satellite peaks at 947 eV, and the Cu 2p 1/2 peak at 956.81 eV.In general, the presence of the Cu 2 O phase is confirmed.The lack of this phase in the XRD pattern, on the other hand, suggests that its presence is limited to the surface layer and the creation of exposure to air and oxygen.Regardless, the most common oxidation state in this material is Cu 2+ .Presumably, Fe 2+ , Fe 3+ and Cu 2+ substitute Mn 4+ in MO 6 octahedron creating defect Fe �� Mn Fe � Mn , Cu �� Mn , and

Electrical properties
The electrical circuit model of the arrangement described in paragraph 2.2.includes a wiring circuit, material response, and electrodes.However, given the attained data, the wiring and electrode response should be insignificant comparing the material response, and hence, the circuit model approach should become the serial of a parallel circuit of resistance and capacitance of grain and grain boundary.The electrical analysis therefore should be conducted using two methods: the Nyquist plot and the Debye plot based on the circuit model given in Fig. 6 (inset) of the material then deduced to the equation as depicted in Eqs.
in MCS-Fe and MCS-Cu samples, indicating that doping Fe and Cu results in the formation of defects that inhibit electron mobility, increasing resistance.Figure 7a depicts the real impedance Z′ component versus frequency.The amplitude of Z′ is greater in the lowfrequency region, decreases monotonically with increasing frequency, and then drops significantly above f ≈ 10 4 Hz.Furthermore, the magnitude of Z′ increases with the addition of CD and dopant, and its value for all samples combine in the higher frequency region.This could be due to the release of space charge polarization caused by the material's decreased barrier properties at high frequencies.Cu and Fe doping increases oxygen vacancies caused by the possibility of substitution of Fe 3+ , Fe 2+ , Cu 2+ , and Cu + on Mn 4+ .
Figure 7b shows the frequency dependence of imaginary impedance Z″ at different composite, with a typical Debye relaxation curve at f ≈ 10 3 Hz and f ≈ 10 5 Hz, as well as the detailed numerical values of R 1 and R 2 determined by relaxation frequency.As shown in the graph, the Z″ value rises initially, reaches a peak Z″ max, and then falls with frequency.With the addition of CDs and dopants, the position of the Z″ peak increases and regularly shifts to a lower frequency, indicating a gathering of relaxation times in the system.Table 3 summarizes the numerical values of material resistance (R 1 and R 2 ) concluded by the Nyquist plot and Debye relaxation frequency, with a focus on the grain response of the Z′ and Z″.
The permittivity of the material is related to the capacitance.The relative permittivity and phase as a function of frequency are depicted in Fig. 8 for various samples.All samples showed that dielectric constants reduced with increasing frequency before achieving constant values in the high-frequency region.
At low frequencies, space charge determines relative permittivity, whereas dipole polarization determines it at high frequencies.The unbounded electrons produced during defect reactions caused by unusually high relative permittivity are referred to as space charges.The presence of multiple defects in the material causes the formation of defect  dipoles, which leap to face the high frequency of the external electric field, resulting in low permittivity.
Figure 9 depicts the relationship between area capacitance and frequency.All samples had MnO 2 areal capacitances with CDs, and the doping with Fe and Cu varies slightly between samples, with the MS sample having the highest values.The high areal capacitance at low frequencies is predominantly the response of space charges and drops quickly with increasing frequency.

Conclusion
The synthesis of MnO 2 carbon dots was successfully carried out at low temperatures; no significantly different results are presented by treatment at room temperature and 80 °C.The powder was a poorly crystallized compound resulting from the small grain size.Carbon dots are well adhered to the MnO 2 surface making the core-shell type grains.Mn poses an oxidation state of + 3 and 4 + .The K + ionic residue has a large size; it is rather filled between two layers of MnO 6 octahedron chains.The Fe and Cu dopant present in a mixed oxidation state, incorporated in the MnO 2 matrix generating defects Fe � Mn , Cu �� Mn , and V ⋅⋅ O .The presence of the oxygen vacancy disrupts the charge mobility resulting in a decrease in the conductivity of doped material.

Figure 6
Figure 6 depicts a Nyquist plot of real impedance Z′ versus imaginary impedance Z′′ for all samples, demonstrating the formation of negative Z′ which signifies a capacitive response.Focusing on the material aspect, two semicircles are composed of grain resistance and capacitance, and grain boundary resistance and capacitance responses.The addition of CDs in the sample results in larger radius semicircles.The small semicircle observed in MS suggests that the electrical processes in the material arise because of grain material contribution.The semicircle radius increased dramatically

Fig. 7
Fig. 7 Frequency dependence of a real impedance Z ′ and b imaginary impedance Z ′′

Fig. 8
Fig. 8 Frequency dependence of a relative real permittivity ′ and b relative imaginary permittivity ′′

Fig. 9
Fig.9The dependency frequency on the areal capacitance of samples

Table 2
The XPS dates of Mn 2p and Mn 3 s values of MS, MCS, MCS-Fe, and MCS-Cu Fig. 6 Nyquist plot of real impedance Z′ versus imaginary impedance Z″ of samples

Table 3
Grains resistance R 1 and R 2 of samples derived from Nyquist and Debye plots