Sequence effects on the life estimation of thin-walled welded tubular structures made of HSS + UHSS under bending

Welded hollow sections are typical in different industries. A database of fatigue life data of welded hollow section joints covering sequence effects and the accuracy of the linear damage accumulation is presented. The effects of the shape of the applied load spectra, sequence effects of different amplitudes have been investigated using two high-strength steels. This document covers thin-walled tubes of 2-mm thickness made of low-carbon or mild steel 1.8849 (S460MH) and austenitic TWIP-steel 1.4678 + CP700 (X30MnCrN16-14). Constant amplitude and two-level load spectra are presented to check the linear damage accumulation. Using stress concentration factors from finite element analysis, typical FAT classes for the structural and the effective notch stress concepts are checked as well. Both structures show much higher strength compared IIW recommendations by structural stress approach and DVS 0905 by effective notch stress approach. Typical maximum linear damage sums taken from recommendations and codes of 0.2 or 0.5 are exceeded for all spectra investigated and in some of the cases even significantly above 1.0. Transferability of the recommendations to component type structures like those tubular joints made of high-strength steel needs revision to lift its lightweight potential but this will require additional data.


Introduction
Hollow sections for lightweight structures are common use in many industrial sectors like crane industry, agricultural and transportation industry, and steel bridge constructions. In general, these tubular structures represent truss or frame like topologies. To lift lightweight potentials in modern designs, use of high-and ultra-high-strength steel grades for an economical design becomes increasingly relevant. Many codes or recommendations are lacking data for designing with high-strength steel. The enormous efforts made by the steel industry in recent years to continuously increase strength and ductility in the form of pareto-optimal new grades (advanced high-strength steels AHSS, ultrahigh-strength steels UHSS) and to make this material available to the industry are not yet visible in the codes and recommendation. Typically, such tubular structures have to be designed for variable amplitude loading to avoid fatigue damage by the use of linear damage accumulation. Limits of the allowable linear damage sums below 1.0 are used in many of those design rules to compensate somewhat the systematic inaccuracy of the linear damage accumulation. When determining the damage sums, the effects of important influencing factors are not taken into account. Among those are the shape of the amplitude spectrum applied, the influence of rare overloads like misuse, welding residual stresses and their relaxation by service loads, and possible sequence effects by varying load levels in time.
It is well known that an analytical damage sum as obtained by using the linear accumulation by Palmgren [1] and Miner [2] in relation to experimental results of life can scatter very widely and that the specified or recommended allowable limits which might lead to uneconomical or even unsafe designs. Many researchers addressed the topic of the prediction capabilities of the linear damage rule [3][4][5][6]. One very large study was done in the 1990's by a German group [7]. Generations of researches are trying to improve the damage accumulation theories for better predictability [8][9][10][11][12][13][14][15]. A comprehensive overview by Fatemi and Yang from 1998 is still a good summary for modifications of the linear damage accumulation theory covering the last century [16].
Among the objectives of this research project as presented in this paper was to verify the application of linear damage accumulation by providing a broad test base of different load sequences for different welded hollow sections made of different steel grades and having different sections to cover the size effect. Here, only thin-walled tubular joints under bending are covered. In a second publication, an investigation of thick-walled welded tubular structures can be found [17].
By using welded hollow sections for testing constant amplitude SN curves as well as experimental fatigue life for a variety of test scenarios, this project provides new data on tested components. It will be shown that the transferability of recommendations from technical rules to components is still an open issue. Rules, standards, and recommendations are usually referring to small specimens for specific welded joints. Size effects due to the size of the weld throats and also size effects due to the length of highly stressed weld toes and roots are not covered sufficiently. This will be demonstrated by the experimental findings in the following.  [21]. This makes this material especially important in case of high-strength requirements for static or crash loading, lightweight design in transportation industry or moving structures for capital goods. See Tables 1 and 2 for monotonic material data for steel sheet and tubes used in the project as well as the range of chemical composition as given by the steel supplier for this type of steel.
In the following text, the low-carbon or mild steel will be referred to as 1.8849 and the austenitic TWIP steel will be referred to as 1.4678.
All tests are carried out on a three-point bending test, the schematic diagram of which can be seen in Fig. 1. The distance between the simple supports is 800 mm.
The dimensions for this type of specimen and test remain constant for all tests performed. The nominal dimensions of the square tubes are all 50 × 50 × 2 mm.
Welding was performed manually for 1.8849 and automatically for 1.4678. For 1.4678, SN curves also have been obtained for a small number of manually welded specimens. No weld preparation has been performed prior to welding. The manual and automated welding processes were performed according to specifications of the industrial partner from bus industry involved. The comparison of manual and automated welding was in the interest of industrial partners. Tack welding of filler rods to the belt  After welding the cover layers, the seams were mechanically cleaned using a wire brush. All weld seams start and end in the corners. Because the corners also face maximum stresses for those joints, this specification is usually not recommended from the durability point of view but refers to practical aspects in manufacturing of complex bus frames. Therefore, this weld sequence was used for all specimens. See Fig. 2.
All specimens made of 1.8849 were delivered electrocoated for corrosion protection. 1.4678 specimens have been left uncoated. Figure 3 shows examples of micrographs at two different positions of specimens made of the higher-strength material.
A typical failure pattern at the location of maximum bending moment can be seen in Fig. 4. Two crack locations can be seen. The crack started at the section corners due to the maximum structural stress at such joints and maybe additional notch effect due to the transition of two fusion lines. The crack shown in the figure shows the crack length after 0.2, 1.0, 5.0 mm increase of displacement at the load intake of the load-controlled fatigue tests. All fatigue life values as given in this paper reflect load cycles for an increment of 0.2 mm.

Test equipment
Tests were performed using a hydraulic as well as a resonance testing machine, both from Schenck. The hydraulic cylinder was selected for very short high blocks due to shorter start-up times. Longer blocks, especially at the  low level, were then performed with the resonance testing machine. In contrast to the hydraulic cylinder, this required about 100-300 cycles to reach the desired test level. To ensure that cycles required for start-up do not distort the calculation of the total damage or are not taken into account at all, only longer blocks were run on the resonance testing machine.
Both testing machines have a maximum test load of approx. 63 kN and are equipped with a corresponding load cell up to 63 kN. Before the tests were carried out, the load cells were calibrated to a deviation of 0.002 kN using Spi-der8 PC measurement electronics and a suitable calibration load cell up to 10 kN.
The test frequency of the hydraulic cylinder is in the range of approx. 5-9 Hz. The frequency of the resonance testing machine is about 12 Hz.

SN-curves
Using specimen from the same production lot as the later variable amplitude tests, at first, SN-curves for the structure were obtained: 12 tests of 1.8849 and 7 tests for 1.4678, both manually welded and 16 tests of 1.4678 robot welded specimen. The resulting raw data can be found in Table 13 in the Appendix. The parameters of the SN-curves are given in Table 3. Figure 5 shows the resulting curves for both materials in manually welded condition for nominal bending stress in the critical weld section as well as the test results. Nominal stress was calculated by a linear transfer coefficient for the applied load DF of c N = 33.13 MPa/kN and covers the bending stress only. Nominal stresses, at the location as given in Fig. 1, can be derived for dimensions used and a section modulus of W = 5660 mm 3 by Due to the large support spacing of 800 mm, transverse shear forces are about 4% of bending stress and can be neglected. Regression of the SN-curves were done using the equations from DIN 50100 [22] since the project is focused on steel construction and crane design which usually use this procedure. According to this rule, especially for small sample numbers (n < 10) the logarithmic standard deviation s lgN tends to underestimate and must therefore be corrected according to: As shown in the figure, curves from regression and valid for P A = 2.3%, 10%, 50%, 90%, and 97.7% are shown in black color.
The scatter bands are reasonable low due to the use of specimens from the same production lot.
In addition to the free slope from regression, the regression line with fixed slope m = 5 is also shown in blue, which represents a common value for SN curves for such thin-walled welded components.
The increase of the slope exponent especially of m = 8.4 for 1.8849 and less pronounced by m = 5.6 for 1.4678 show a significant effect of the material strength of the base material as well the effect of the thin-walled welded structures in these results.
MPa kN (2) s lg,N,corr = s lg,N 1 − 1.74 n − 2 In Fig. 6, the difference between the manually welded and the robot welded specimens made of 1.4678 can be seen. A significant increase of the fatigue strength of the manually welded specimen compared to the robot welded ones is due to the material pile up in the highly stresses corner for the latter, which creates additional notch effect which can be seen in Fig. 2. We currently have no explanation for the lower strength, which can be seen for the robot welded specimens for very high stress ranges. Those fatigue life values should be less prone to stress concentration. Geometrical differences in the local cross section might be responsible for this effect. Using image analyzing software in order to quantify the local weld geometry could help to quantify the local notch severity. Such investigation has not been in the scope of the research project.

Load spectra for variable amplitude testing
The SN-curves have been taken to define the subsequent variable amplitude spectra using analytical damage accumulation by the Miner's rule. Except for reversed loading conditions, all cycles are applied using a stress ratio R = 0.1. For reversed loading, R = 10 is used for compression cycles.

1.8849
Maximum stress ranges are fixed to ΔS h = 250 MPa for all spectra which corresponds to a fatigue life according to the SN-curve from regression of 5555 cycles. This is well above 5000 cycles which defines the transitions between high and low-cycle fatigue ranges according to DIN 50100 [22]. The minimum load levels are defined by the ratio or load factor LF of upper to lower stress ranges by LF =|ΔS h |/|ΔS l |. The maximum load factor used was 1.8 which corresponds to a minimum stress cycle of 139 MPa and a cycle to failure of 778,243 cycles. The defined cycles thus are well within the range of the SN-curve. For the variable amplitude testing, different spectra have been defined. The naming of the tests for variable amplitude loading was done using the naming convention according to Fig. 7. Using the SN-curves the following spectra has been defined using analytical linear damage accumulation for an allowable damage of 1.0 for the respective material.

High-low spectra
The test scenarios result from a variation of the ratio of high load (overload) ∆S h to low load (base load) ∆S l on one hand, and from a variation of the ratios of the partial damage sums of high load D h and low load D l on the other hand. The damage proportions for the 4 high-low-spectra in Fig. 8 are estimated with the damage accumulation rule according to Palmgren-Miner using the SN-curves as obtained for the respective material. The maximum damage according to Palmgren-Miner of 80% due to the overload ensures that a fracture should not already occur during the initial overload block. The maximum and minimum load levels have been defined to be safely within the range of the SN-curve for high-cycle fatigue.

Low-high spectra
Using just the worst-case from the high-low spectra the levels for a reversed sequence low-high was derived. The spectrum according to Fig. 9 is resulting from this approach.

Opposite phase high-low spectrum
For transportation systems, in-phase spectrum levels are usual loading conditions, especially in the direction of the acceleration due to gravity. Therefore, those spectra have been tested with higher effort. UL1.8-80/20 test spectrum was also used to investigate overloads occurring in opposite phases as shown in Fig. 10. The R-ratio of the foregoing high-block in compression amounts R = 10.

Repeated loads in-phase
Block-type spectra of repeated overloads have been defined according to Fig. 11. Each of those in-phase high-low spectra was designed for a repetition of each block 8 times to analytical failure. Such spectra represent also the occurrence of rare overloads like misuse or pot-hole driving.

Test results from variable amplitude testing
The results from variable amplitude testing as raw data can be seen in Table 14 (1.8849) and  Tables 14 and 15 given by D V = D test /D calc reflect the prognosis quality of the linear damage accumulation as calculated against the corresponding SN-curves. D calc , which is the expected theoretical damage for sizing the spectra before testing, is 1.0 for all cases. D V > 1.0 refers to an experimental damage higher than theoretically and indicates a very conservative value for using the Miner rule for such cases. Vice versa, values below 1.0 result in an underestimation of the analytical fatigue life using the Miner rule if compared to the experiments.
In the left column, those tables also contain an equivalent cycle to failure number N äq as calculated for a constant amplitude spectrum at the maximum stress cycle ΔS h for the corresponding material. This reflects a Gassner-type evaluation.
Apart from the reversed loading case UL-1.8-80/20, no mean stress correction is necessary, since the two-level tests and the component SN curve were performed at the same load ratio. For UL-1.8-80/20, a correction factor for medium level 1 residual stresses of f(R) = 1.3 according to [24,25] was applied for the cycle in compression. Due to the thin-walled design, this should be a reasonable assumption but need to be taken with caution. There is too little knowledge about mean stress effects of hollow sections in general. Table 14 contains both evaluations with and without the mean stress correction.
Marked in the tables are a few tests which have been identified as outliers for the test series of the respective stress spectrum. The procedure of the outlier detection was simply done by visible inspection of the test series in probability paper. An example is shown in Fig. 12 where the test marked in green is identified. Using log-normal or normal distributions for D V does not give different results. Outliers are not contained in the regression curve to get values for different probabilities to calculate the scatter factor T from the 90% and 10% quantiles as well as the standard deviation s lg according to the equation The resulting statistical values can be seen in Tables 4 and  5. Important findings are.
• High-low spectra only show outliers, but only for the manually welded 1.8849. • Especially spectra with high damage content (80%) in the high block show more than one outlier. • Low-high spectrum shows largest scatter.
• Median values of all relative damage sums are above 0.84 up to 1.5, all 10% values above 0.51 up to 1.0 (except UL1.8-80/20 with mean stress correction. See "Discussion" section).
The boxplots in Fig. 13 shows the dispersion of relative damage sums. Each box covers 50% of data, the black whiskers represent 1.5 times the distance between mean value (in red) and blue box boundaries. However, the whiskers are cut to the next data point inside, which is why whiskers of unequal length can also be seen. The collective form UL1,8-80/20-korr represents the damage sums calculated considering mean stress correction.
The individual points are enumerated consecutively for this purpose and match the numbering above or below the individual boxplots. 3. Damage prognosis tends to the unsafe side when there is higher partial damage at lower amplitudes.
4. If the damage fraction of large amplitudes increases, then scatter is reduced.  5. In repetitive block programs there are hardly any differences in the distribution of the partial damages of the two load levels. 6. High content of cycles in the low load range leads to an unsafe evaluation. 7. High overloads in the high-low spectra theoretically leads to deceleration of cracks, which can be seen in high relative damage sums. Rare overloads at the very beginning for this sequence type has a larger effect towards underestimating life than repeated high-low blocks. Figure 14 shows the damage totals of the test series HL1.5-80/20 of the high-strength steel 1.4678. In direct comparison with the same test series for the material 1.8849, it is noticeable that the linear damage accumulation leads to a more conservative result. In the median, the total of the individual tests is D V = 1.5.

Residual stress measurement
To get first impression about residual stresses, measurements have been taken on one specimen of 1.4678. Since the samples made of 1.8849 have all been electrocoated, residual stress measurements could not be performed for those. A proper removal of the electrocoat was not possible.
For measurement, X-ray diffraction was used. See parameters in Table 6. This work was performed by University Kassel, Germany. The following distributions show stresses in lateral and longitudinal direction of the horizontal tube. Path coordinates can be taken from Fig. 15. The paths in the following figures are along the horizontal tube in web center and tube edge through the weld and 150 mm away from the weld along a lateral path on the web. Since the TWIP steel was hardened by cold forming, stresses at the remote position 150 mm away from the weld and HAZ were also taken.
Longitudinal and transverse residual stresses measured at this distance over the transverse section can be taken from Fig. 16. Both the longitudinal and the transverse residual stresses seem to be distributed relatively constant over the transverse section and change only in the edge areas shortly before the beginning of the bending radii of the tube, which  Since the residual stresses were measured both on the right and on the left of the weld seam, these curves differ due to the different positions of the respective tubes. Nevertheless, it can be observed that higher tensile residual stresses occur in the longitudinal direction in the edge region of the tubes than in the center of the tube. This observation also agrees with the measurements far away from the HAZ. Similar findings can be obtained when considering the transverse residual stresses. Here, however, in agreement with the measurements in the unaffected zone, the residual stresses are in the compression. In summary, it can be stated that the heat input from the welding process only affects the residual stresses in the immediate vicinity of the weld seam.

Stress concentration factors
Finite element analysis is state of the art for analytical assessment of deformation, stresses, and strains also for welded structures [26]. Besides the experiments, notch factors to evaluate structural and notch stresses were determined for the geometry of the thin-walled square hollow joint by finite element analysis in this project as well. Using those stress concentration factors, the SN-curves based on nominal stresses can be transferred to structural stresses and effective notch stresses. For finite element analysis, ANSYS Workbench 2021 R2 2 was used.
Structural stresses are derived by linear and quadratic extrapolation according to the IIW Recommendations [27], effective notch stresses based on a fictitious radius in the notch root and weld toe of r = 0,3 mm as suggested by the DVS 0905 [25]. For such thin-walled structures the reference radii 1.0 mm as suggested by [27] weakens the weld throat too much and should not be used. Therefore, this reference radius should not be used for this structure.
The nominal dimensions of the tubular joint as described in chapter 2 have been used to model the geometry. Due to symmetry, 1/4 of the total structure was modeling applying symmetry boundary conditions. At the bearing rolls, the structure is simply supported. Loading is applied by the compressive force on the top face of the vertical tube.
To reduce computational effort, submodeling was used. The domain of the submodel can be seen in Fig. 18 (right). This model included the stiffening effect of the weld seam with angular, i.e., discontinuous transitions for the analysis of structural stresses and in case of notch stress analysis the fictitious radii at weld root and weld toe. The flank angle is set to 45° (Fig. 19).
Only solid elements with quadratic shape functions have been used. For mesh refinement in weld root and weld toes for the effective notch stress concept, the DVS 0905 code of practice recommends at least 24 elements along a 360° arc in the notch radius and also the corresponding element edge length normal to the notch surface for quadratic approach functions of the finite elements. A convergence study on our model confirms this recommendation as seen in Fig. 20 (right). To determine the structural stresses, the methods according to Haibach (1 mm and 2 mm stresses) [], as well as the linear and quadratic extrapolation methods according to [27], were applied. For this purpose, the notch area was modeled without filleting the seam runout.
To determine the stress curves, the required evaluation points were defined by means of several evaluation paths and sections perpendicular to the notch on the component surface, see Fig. 19 (right). The path with the highest resulting stress was used for further evaluation. See It can be seen from this figure that the Haibach structural stress underestimates very much and thus this definition cannot be taken for such thin-walled structures. This pragmatic method performs much better for thicker welds.
Notch stress analysis results in maximum stresses in the weld toe at the section corners only.
Stresses in the weld root are approximately a factor of 4 lower than at the location of maximum weld toe. Therefore, they can be excluded as failure critical locations. This was also confirmed in the tests with the same geometry for both materials.
Stress concentration factors SCF represent the ratio between the determined structural or notch stresses and the previously defined nominal stresses (Fig. 22). Nominal, structural, and notch stress concepts always refer to linearelastically determined stresses. For this reason, structural and notch stresses can be obtained simply by linear scaling as shown in Table 7.
The SCF derived for the two Haibach methods show the strong underestimation of the structural stress method for such thin-walled structures. For stress fields showing nonlinear distributions in front of the hot spot the quadratic extrapolation should be used for hot-spot stress evaluation.
According to DVS 0905 [25,28], checking against a SN curve for the base material in addition to the check with respect to the SN curve according to the FAT class is mandatory for mild notches having low stress concentration factors. To exclude such cases, minimum values of the seam shape (4) K t = k or hs S Fig. 21 Structural stress evaluation for path with maximum principal structural stress

Fig. 22
Notch stress distribution, maximum principal structural stress and at the weld toe of maximum stress factor K w must be achieved, which is defined by the ratio of notch stress to structural stress and is depending on the reference radius. The minimum value of K w for r = 0.3 mm to use the FAT class-based SN curve for the fatigue assessment only is K w,min = 2.13 [25]. In our case, the ratio from finite element analysis gives K w = 2.19 which is close but larger. The small distance from the limit in this use case with a high localized stress concentration and flank angle of 45° is remarkable.

Constant amplitude testing
First, the SN curves are compared to FAT classes taken from DVS 0905 for the effective notch stress concept and from the IIW recommendations for structural stresses, both applied to maximum principal stress. For load carrying welds, FAT90 is recommended for structural stresses and FAT300 is recommended for r = 0.3 mm for the effective notch stress concept, both using a slope exponent of m = 5 for thin-walled structures. FAT classes are given for a low probability of failure as typical in many standards of 2.3% (about equal to a probability of survival of 95% of the mean together with either a two-sided 75% or a one-sided 95% confidence limit or alternatively mean minus two times standard deviation [27]). Transferring the FAT classes to a failure probability of 50%, multiplication by 1.3 as a pragmatic approach is used. IIW recommendations suggest a value of less than 2.3 for the number of specimens to obtain the SN-curve. Also, FAT classes are valid for a stress ratio R = 0.5. According to DVS 0905 [25], transformation to R = 0.1 requires an additional factor f(R) = 1.073 in the case of conservatively assuming residual stresses. We consider this value as a theoretical upper bound when looking on the residual stresses for the TWIP steel as seen in Fig. 17 (right). For comparison of the most probable mean values from regression ΔS 2E6,50% , the FAT class in total needs to be multiplied by an assumed 1.4 to obtain comparable characteristic values. We consider this as an upper bound value for the code-based SN data for 50% probability. The modified FAT classes and the stress ranges from constant amplitude testing multiplied by the corresponding stress concentration factors can be seen in Table 8 for characteristic values of structural stress Δσ hs,2E6 and Table 9 for the effective notch stresses Δσ ns,2E6 , both valid for a probability of 50%. A significant difference can be seen in both tables. For structural stresses, the stress concentration factor from quadratic extrapolation only is used for this evaluation.
To get a better view on the full range of the SN-curves, the ratios of characteristic values can be seen in Tables 10  and 11. The values for 10 4 cycles have been calculated using the respective slope exponents for each approach from Tables 8 and 9. Also, the K t -values are applied with the same magnitudes as for 2·10 6 cycles. The ratios between characteristic values from the experimental SN-curves and the code-based values are given for 10 4 and 2·10 6 cycles in the last two columns of these tables. The results demonstrate a massive increased fatigue strength of for both materials and both welding processes if we compare the data to the transferred FAT classes and standardized slope exponents from the codes. This gives an indication that -due to high-strength material, thinwalled structures and tested components, not just weld details -the application of the cited technical recommendations is much too conservative for such cases.
The higher difference in strength between experiment and code-based strength by using the structural stress is even higher compared to the notch stresses. Because the experimental obtained characteristic values are based on the same nominal stress but different stress concentration factors, this difference can only be due to one or two wrong FAT classes. The FAT classes from IIW recommendations apply to any load-carrying weld geometry and thus those FAT values might be more conservative than the corresponding FAT class for the effective notch stress concept. A single master SN-curve is used by the effective stress concept as well, but very local stress concentrations at the critical section corners are captured by this concept only. We assume, this might be the reason for this difference.
Since the increase of the strength of the manually welded specimens for both materials are about the same for the lower stress ranges, the strength increase at 2·10 6 cycles might be less due to the material but the high stress concentration of a component type structure and the thinwalled dimensions.
The strength increase of the TWIP steel is much more significant for 10 4 cycles though. This reflects the higher monotonic material strength of this advanced steel. The TWIP-steel has a steeper SN-curve due to the higher strength for monotonic loading.
The results from the constant amplitude testing have shown that by using the TWIP steel, not only massive weight reductions for monotonic loadings but also for variable amplitude loading can be achieved for such structures. The higher the loads of rare events or the higher the maximum stress of an applied spectrum loading, the higher the advantage of the TWIP steel.

Variable amplitude loading
Tests for CAL and VAL were all done using specimens of the same lot to apply the SN-curves on life estimation with reasonable accuracy. Although each of the variable amplitude spectra have been repeated seven times for most of the spectra defined, the resulting data can only give an indication of tendencies. A final conclusion for an improvement of the linear damage accumulation cannot be drawn by these tests alone.
The variable amplitude spectra as defined in chapter 4 and resulting relative damage sums D V in chapter 5 based on the raw data in Tables 14 and 15 in the Appendix. The resulting statistical values can be seen in Tables 4 and 5. Important findings are as follows.
The effects as observed by fracture mechanics on speed up or slow down of crack propagation due to varying mean stress and varying amplitudes in two-step loadings [29] can be seen for the fatigue of welded specimens investigated here as well. Change from high to low in phase slows down crack propagation temporarily and speeds up from low to high stress cycles. Change from negative high stress cycles to positive low ones (reversed mean stress) also yields a speed up. This can be seen in the experimental results obtained. Since the linear damage accumulation does not consider those physical based sequence effects, this -besides other reasons -is reflected by the relative damage sums D V > 1.0 or D V < 1.0.
Median values of all relative damage sums (except UL1.8-80/20 with mean stress correction, see below) are in general well above 0.84 up to 1.5, all 10% values are above 0.51 up to 1.0.
Having a larger fraction of damage at low stress cycles compared to the large stress cycles increases scatter. This is comparable to the different scattering behavior of SNcurves at high and low load amplitudes. Vice versa, spectra with high damage content for large stress ranges show lower scatter of the estimated life by liner damage accumulation.
IIW recommendations [27] suggest a critical damage sum of 0.2 for fluctuating mean stresses. As can be seen in Tables 4 and 5, this criterion is fulfilled by all tests performed. Median relative damage sums of most of the tests performed are safely above 0.5. However, it is difficult to differentiate the load sequences to be used for this purpose.
In the case of in-phase tensional loadings, i.e., mean stress remains positive for all stress ranges, the critical damage sum could be modified to higher values. An allowable value of 0.5 seems reasonable as recommended by DVS 0905 [25]. If the load spectra comply with the ones used in this program, even higher values could be taken but require additional tests for qualification. In the following, a few more comments about the specific spectra are summarized.

High-low spectra
Trivial but referred to for plausibility: with a lower load factor LF = 1.5, the low stress level following the high level is higher as compared to LF = 1.8. Accordingly, the tests break down earlier than with a load factor of 1.8. Also, a theoretical damage fraction of D h = 80% in the high block leads to earlier failure compared to setting D h = 20%.
Scatter for high-low spectra increases for a high amount of partial damage for low stress ranges. It is largest for spectra having 80% damage for the minimum stress ranges at low level.
The high-low spectrum (HL1.5-80/20) applied to specimens made of TWIP steel (robot welded) yields significant higher underestimation of fatigue life compared to the mild steel (manually welded).

Low-high spectra
The visible theoretical overestimation of life can be explained by the speed up of crack propagation for simple step loading on crack type specimens.

Opposite phase high-low spectrum
This spectrum yields a remarkable low scatter of life even though 7 specimens have been tested. Even without mean stress correction, the relative damage sum for median of D V = 0.9. UL1.8-80/20 with mean stress correction for medium level residual stresses in the welds to calculate the relative damage sum D V leads to the worst case for the relative damage sum D V = 0.1 for all spectra tested in the program. Under these assumptions, the theoretical linear damage accumulation is overestimating fatigue life significantly. Speed up of the crack propagation for this load sequence not considered in the linear damage accumulation on one hand and a mean stress correction differing from the recommendations might explain this. Therefore, this correction seems not to be valid for this type of structure. This effect requires more comprehensive tests on the effect of mean stress on this type of component like structures.

Repeated loads in-phase
The visible theoretical overestimation of life can be explained by the speed up of crack propagation for simple step loading from low to high levels on crack type specimens. This effect seems not to be compensated by the slowdown of crack propagation vice versa for repeated block loading. Compared to the tested simple two-step loadings high-low and low-high the scatter is smaller and the prognosis quality better for such block loadings.
The two block program test series do not show big differences for the two damage ratios D h and D l defining the spectra. Mixing the high and low stress cycles instead of two-step loading increases the damage. This correlates with observations for block loading vs. random loading [17].

Plausibility checks according to ISO 14347
ISO 14347 [30] is a specific standard for the design of joints made of welded hollow section. Although this code is limited to a minimum of 4 mm, it was used to check plausibility of the experimental results from constant amplitude testing. Based on the stress resultants acting on each branch of a welded joint, this method uses stress concentration factors for many different designs to estimate fatigue life as a structural stress concept at different critical positions along the welds. ISO 14347 provides SN-curves with different "FAT classes" and different slope exponents m ISO dependent on the wall thickness of the tubes. Table 12 summarizes the results for comparing the experimentally obtained life for the characteristic values at 2·10 6 cycles and 50% probability, ΔS 2E6,50% . Remarkable are the still highly different slope exponents m ISO and m Exp . The following check thus is only valid for the stress range used. Due to the steeper SN-curves of the ISO, the results for higher stress ranges are different.
The fatigue strength as given in ISO 14347 are valid for low failure probability. For comparison with the mean values from the constant amplitude testing, a factor of 1.3 was applied also for this analysis. D V,1 relates the 2·10 6 cycles from the experimental tests to the cycle to failure number as obtained using the modified characteristic value from the ISO. A high additional safety distance of about a magnitude in life for these materials and wall thickness can be observed for this stress level. Since ISO is not focusing on high-strength steels either, this might be an additional reason for this result.
No factor of mean stress correction is included in D V,1 , because ISO 14347 does not contain a procedure for it. D V, 2 gives an idea about this effect by using an assumed correction factor of 1.15 to increase the fatigue strength towards R = 0.1. Looking at the different results from D V,1 and D V,2 a potential for improving the ISO by adding a correction function for mean stress effects can be concluded.
Finally, the ISO is also checked with the given SN-curves taken from this code without modification, i.e., low failure probability and no mean stress correction. D V,3 represents this number.
Because the fatigue strength of the manually welded TWIP steel joints is about the same as for 1.8849, this analysis is restricted to manually welded mild steel and robot welded TWIP steel only.

Conclusions
Welded thin-walled X-type square hollow section joints (50 × 50 × 2) made of a manually welded low alloy mild steel 1.8849 (S460MH) and robot/manually welded high strength/ high ductility TWIP steel 1.4678 in cold hardened condition have been tested under bending loading with a stress ratio R = 0.1. SN-curves as well as fatigue lives for different twostep variable amplitude spectra were obtained by the experiments. A comparison of manually and robot welded specimens has been drawn based on the interest of participation industry partners. All raw test data can be found in the appendix.
Fatigue strength of the fully austenitic TWIP steel joints in robot welded condition at 2·10 6 cycles is about 12% less than for the mild steel manually welded. The SN-curve is steeper thus which leads to higher strength for higher stress ranges towards LCF. The fatigue strength of the manually welded TWIP specimens is about the same as of the mild steel specimens at 2·10 6 cycles but they yield a steeper slope leading to a higher fatigue strength for high stress cycles. For lightweight constructions this material bears improved strength and ductility not only for static loading or plastic collapse but also for fatigue strength. These first results for R = 0.1 indicate the lightweight potential of this new material.
Finite element analyses have been performed to calculate stress concentration factors of the components for structural and notch stress concept. Applying those stress concentration factors to FAT values from the IIW recommendations and DVS 0905 gave a significant underestimation of the code-based fatigue strengths. The difference is higher for the structural concept. Thin-walled design and component characteristics by a strong local stress concentration in the welds at the section corners might be responsible, that the two stress-based concepts differ.
Variable amplitude testing was done for different twolevel block spectra. Those spectra have been designed for a total damage sum of D = 1.0 using the experimental obtained SN-curves and a maximum stress cycle yielding about 5500 cycles on the SN-curve of the material used. A maximum factor between minimum and maximum stress cycle of 1.8 was selected. High-low, low-high, reversed high-low, and high-low sequences with 8 blocks have been tested using different fractions of partial damage for the high and the low blocks. Constant and variable amplitude testing was performed for specimens taken from the same manufacturing lots. The effects obtained from the experiments thus can be considered as of high quality. Most of the test have been performed using 7 specimens for statistical purpose. The results are on a sound basis but will require further tests on different materials, test scenarios to get enough data to improve rules for damage accumulation. Alternatively, such high experimental effort could be reduced by combining experimental with high level analytical means based on computational fracture mechanics. From the results obtained the following findings can be summarized: • DVS 0905 recommends not to exceed a partial damage sum of 0.5 for variable amplitude loading. This is fulfilled by all tests except the case with reversed mean stresses and considering this mean stress effect. • IIW-recommendations suggest a critical damage sum of 0.2 for fluctuating mean stresses. As can be seen in Tables 4 and 5, these recommendations are fulfilled by all tests performed. • Median relative damage sums of most of the tests performed are above 1.0. However, it is difficult to differentiate the load sequences to be used for this purpose. • In case of in-phase tensional loadings, i.e., mean stress remains positive for all stress ranges, the critical damage sum could be modified to higher values. A value of 0.5 seems reasonable. • If the load spectra comply with the ones used in this program, even higher values could be taken but require additional tests for qualification.
This paper covers a contribution to a database of tests on welded hollow sections using constant amplitude testing and variable amplitude testing using different block-type spectra. It has been demonstrated, that applying selected codes leads highly safe results for the SN curves of the welded hollow sections and materials tested. Further research and modification of the technical rules is recommended.