Abstract
Nanocrystalline single-phase alloys with the nominal compositions (at%) of Nd12.3−x Dy x Fe79.7Zr0.8Nb0.8Cu0.4B6.0 (x=0, 0.5, 1.5, and 2.5) were prepared by melt-spinning and subsequent annealing. X-ray diffraction analysis shows that the as-spun ribbons were mainly composed of the amorphous phase. A slight content of Dy stabilizes the amorphous phase during annealing treatment. The grain size becomes smaller and the coercivity of the annealed ribbon is gradually improved with the increase of Dy content. Excessive Dy is harmful to the remanence. It is found that no intergranular phase exists between the grains by high-resolution transmission electron microscopy, and the grain boundaries are crystallographically coherent in the optimally annealed sample. The optimum magnetic properties of remanence (J r=1.09 T), coercivity (H ci=1048 kA/m), and maximum magnetic energy product ((BH)m=169.5 kJ/m3) are obtained from the x=0.5 ribbon in a post heat-treated state (700°C, 10 min).
Similar content being viewed by others
References
M. Ghidini, G. Asti, R. Pellicelli, et al., Hard-soft composite magnets, J. Magn. Magn. Mater., 316(2007), No.2, p.159.
H. Chiriac, N. Lupu, L. Stoleriu, et al., Experimental and micromagnetic first-order reversal curves analysis in NdFeB-based bulk “exchange spring”-type permanent magnets, J. Magn. Magn. Mater., 316(2007), No.2, p.177.
D.N. Brown, Z. Chen, P. Guschl, and P. Campbell, Developments with melt spun RE-Fe-B powder for bonded magnets, J. Magn. Magn. Mater., 303(2006), No.2, p.371.
H.W. Kwon and G.C. Hadjipanayis, Magnetic and microstructural study of hybrid magnet consisting of R-rich and R-lean Nd-Fe-B alloys, J. Magn. Magn. Mater., 310(2007), No.2, p.2575.
W.F. Miao, J. Ding, P.G. McCormick, and R. Street, Magnetic behaviour of mechanically milled (Nd1−x Dyx)8Fe88B4, J. Magn. Magn. Mater., 175(1997), No.3, p.304.
X. Fang, Y. Shi, and D.C. Jiles, Modeling of magnetic properties of heat treated Dy-doped NdFeB particles bonded in isotropic and anisotropic arrangements, IEEE Trans. Magn., 34(1998), No.4, p.1291.
S.G. Kim, M.J. Kim, K.S. Ryu, et al., Effect of Dy on magnetic properties of α-Fe/Nd2Fe14B type alloy, IEEE Trans. Magn., 36(1999), No.5, p.3316.
Z.W. Liu and H.A. Davies, Elevated temperature study of nanocrystalline (Nd/Pr)-Fe-B hard magnetic alloys with Co and Dy additions, J. Magn. Magn. Mater., 290(2005), No.2, p.1230.
L.M. Liu, Y.L. Shi, and X.M. Zhao, Magnetic properties and curie temperature of nanocomposite (Nd0.7Dy0.3)8Fe87B5, J. Hebei Norm Univ. Nat. Sci. Ed., 29(2005), No.4, p.261.
T. Jang and Y.S. Kim, Effect of small dysprosium additions on the coercivity of melt-spun Nd-Fe-C alloys, IEEE Trans. Magn., 36(1999), No.5, p.3310.
Y.H. Gao, J.H. Zhu, Y.Q. Weng, et al., The enhanced exchange coupled interaction in nanocrystalline Nd2Fe14B/Fe3B+ α-Fe alloys with improved microstructure, J. Magn. Magn. Mater., 191(1999), No.1, p.146.
R.J.I. Betancourt and H.A. Davies, Effect of grain size on the magnetic properties of nanophase REFeB alloys, J. Magn. Magn. Mater., 246(2002), No.1–2, p.6.
A. Manaf, R.A. Buckley, H.A. Davies, and M. Leonowicz, Enhanced magnetic properties in rapidly solidified Nd-Fe-B based alloys, J. Magn. Magn. Mater., 101(1991), No.1, p.360.
M. Sagawa, S. Fujimura, and H.Y. Yamamoto, Magnetic properties and microstructure of rare Earth-Iron-Boron permanent magnet materials, [in] Proceeding of the 4th International Symposium on Anisotropy and Coercivity in Rare Earth-Transition Metal Alloys, Ohio Dayton, 1985, p.587.
K.H.J. Buschow, New developments in hard magnetic materials, Rep. Prog. Phys., 54(1991), No.9, p.1123.
Z.W. Liu, Y. Liu, P.K. Deheri, et al., Improving permanent magnetic properties of rapid solidified nanophase RE-TM-B alloys by compositional modification, J. Magn. Magn. Mater., 321(2009), No.15, p.2290.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, Za., Luo, J. & Guo, Zm. Effect of Dy substitution on the microstructure and magnetic properties of nanograin Nd-Fe-B single-phase alloys. Int J Miner Metall Mater 17, 335–339 (2010). https://doi.org/10.1007/s12613-010-0315-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-010-0315-7