Exploring Miniaturized HVOF Systems for the Deposition of Ti-6Al-4V

The exceptional properties of Ti-6Al-4V of high strength, lightweight, corrosion resistance and machinability make it one of the most widely used alloys in in the aerospace industry. Significant efforts are underway to establish powder bed additive manufacturing technologies for Ti-6Al-4V. There are also increasing attempts to use thermal and cold spray to build near-net-shaped parts with buildup rates orders of magnitude higher than powder bed. Thermal spraying, such as HVOF, can oxidize and degrade the alloy due to the high processing temperature. Lowering the flame temperature through inert gas addition in full-size HVOF systems is a possible approach to retain solid-state deposition of the feedstock particles, thereby limiting oxidation and detrimental α-case formation, while providing sufficient heat input for particle softening and plastic deformation at impact. Novel miniaturized HVOF systems, with spray jets of only a few millimeters in width, may further offer the possibility to improve the spatial resolution of the buildup for near-net shape forming. The process parameter range for solid-state deposition of Ti-6A-4V using the liquid-fuelled TAFA Model 825 JPid and the novel hydrogen-fuelled Spraywerx ID-NOVA MK-6 with the addition of nitrogen is shown. Buildups at over 80% deposition efficiency generally yield as-sprayed porosities below 3% and hardness above 200 HV100gf. Attainable microstructures and oxygen content as a function of spray parameters are delineated. Recrystallization and beta-annealing of selected samples lower the residual porosity and can create equiaxed α and intergranular ß-phases. Ultimate tensile strengths of up to 1100 MPa were attained; however, the residual oxygen content of above 0.7% was found to limit β-phase formation, which contributes to a limited elongation to failure.


Introduction
Application of titanium alloys in the aerospace industry is driven by their superior properties such as high strength, fatigue resistance and creep resistance at low-to-moderate temperatures in combination with low density and low modulus (high flexibility). Because of difficulties in casting and welding of titanium alloys due to the high affinity to oxygen and the high solid solubility of oxygen (about 14.5%) (Ref 1), there is a demand for direct fabrication of metal parts in near-net shapes (NNS), which can produce complex components with minimal waste of material (Ref 2). Various processing techniques like plasma spraying, selective laser melting and electron beam melting have previously been used to deposit Ti and its alloys as coatings (  or near-net-shaped parts. These techniques involve high working temperatures resulting in phase transformations, tensile residual stresses and high-temperature oxidation. One of the techniques that have been explored is low-pressure plasma spray (LPPS). It suppresses the oxidation of the feedstock powder through operation in an inert atmosphere under low-pressure conditions ( Ref 6). The LPPS equipment costs are rather high, and this investment can only be justified in exceptional cases. An alternative approach is to use cold spray technology to deposit the material well below the melting point and attaining deposition through plastic deformation of impacting particles, minimizing or eliminating the deleterious effects of high-temperature oxidation, phase transformations and/or tensile residual stresses (Ref [7][8][9]. Furthermore, the cold spray process is highly conducive in building a high-resolution, near-net-shaped feature not only   by virtue of its spatially restricted spray jet of a few millimeters, but also because its sensitivity to the angle of particle impact, which can be exploited to control the deposit shape. , modifying a high-velocity oxy-fuel (HVOF) spraying process to produce Ti-6Al-4V coatings in a process referred to as warm spraying (WS). In this process, the temperature of a supersonic gas flow generated by combustion of a fuel and oxygen is controlled by diluting the combustion flame with an inert gas such as nitrogen. Such approach raises the processing temperature only slightly above the cold spray process to attain enhanced material softening, while achieving similar or better particle deformation through gas velocities comparable to the cold spray process. Fine tuning of the spray process parameter and post-heat treatment, in particular through beta-and recrystallization annealing, is the wide spray jet and lack of spatial resolution of the deposit. To allow high-resolution near-net-shape forming as relevant for aerospace components, spray jets in the order of a few millimeters would be far more suitable. Novel initiatives to design miniaturized spray systems could be adopted to address this gap. This study explores miniaturized inner diameter TAFA Model 825 JPid and the Spraywerx ID-Nova MK-6 HVOF systems, which were modified to allow nitrogen addition to create a miniaturized warm spray apparatus. The goals are to tune the Ti-6Al-4V powder softening and acceleration for solid-state deposition of dense coatings, while maintaining a high-resolution jet and minimizing in-flight oxidation. Alternatively, highvelocity air-fuel system HVAF, as miniaturized in the Uniquecoat i7 for example, is based on the principle of using air instead of oxygen as the oxidant, thereby creating a combustion environment containing fuel, oxygen and nitrogen, similar to warm spraying. HVAF solid-state deposition of Ti6Al4V is detailed by P. Khamsepour

Materials and Processes
Two distinctly different miniaturized HVOF systems were employed in this study: the TAFA Model 825 JPid (Praxair Surface Technologies Inc.), a kerosene-fuelled HP/HVOF gun with power levels in the range of 140 kW, originally designed for tight confines of ''Francise'' turbine vanes or inner diameters as small as 8 00 /204 mm, and the smaller ID-Nova MK-6 (Spraywerx Technologies Inc, Vancouver), a hydrogen-fuelled HVOF gun designed for inner diameters as small as 4 00 /102 mm with powder levels in the range of 60-80 kW. For both systems, nitrogen was added to the combustion in an attempt to reduce the combustion temperature and increase the gas velocity avoiding particle melting and fostering a solid-state deposition of Ti-6Al-4V. Further, these systems feature a narrow particle jet of less than 8 or less than 6 mm width, conducive to a finer special resolution than attainable in conventional HVOF systems for the creation of near-net shapes. Key parameter ranges are summarized in Table 1 and 2 for the TAFA Model 825 JPid and ID-Nova MK-6, respectively. Limiting the heat input to promote solid-state deposition, the 825 JPid kerosene system was operated only up to a net power of 70 kW. The effects of power input, nitrogen addition and standoff distance on the resulting coating characteristics are investigated. The ID-Nova MK-6 was operated at net power levels not exceeding 52 kW. The effect of power input on the coating characteristics was studied. Figure 1 shows photographs of the TAFA Model 825 JPid and ID-Nova MK-6 during Ti-6A-4 V spraying, respectively, featuring highly luminous spray jets. The brightness of the jet is attributed to in-flight combustion of some portion of the titanium powder fines. All coatings were produced on grit basted (60 grit alumina) mild steel coupons or tube substrates. Forced air and nitrogen cooling was used to limit the surface temperature during deposition to below 200°C.
Spherical Ti-6Al-4V grade 5 powders from AP&C (Boisbriand, Canada) were used in this study. Particle sizes, as measured with a Coulter LS (Hialeah, FL) particle size analyzer, show a wide distribution around the D 50 of 10.4 lm with all particles below 20 lm (Fig. 2). The SEM micrographs in Fig. 3 show that the particles are fully dense and feature a smooth surface, facilitating powder flow. The oxygen content in the powder of 0.25% was measured with a LECO 836 Series Elemental Analyzer. Phase analysis was carried out by x-ray diffraction (XRD) using a Bruker D8-Discovery diffractometer (Bruker AXS Inc.,Madison, WI) with Cu K a radiation at an acquisition of rate of 0.01°/s and confirms an exclusive a/a' phase composition of the starting powders, while no other phases could be detected.
The resulting spray coatings were analyzed by optical microscopy and SEM. Porosity was estimated by image analysis at 200x. Vickers hardness was measured at 100 g force (HV 100gf ).
Selected coating samples were removed from the substrate by EDM machining and subjected to vacuum heat treatment. Recrystallization annealing was conducted at a heating rate of 10°C/min up to 925°C, a temperature slightly lower than the a ? ß transition of 995°C. At the same heating rate, beta-annealing was implemented up to 1025°C, slightly above the a ? ß transition temperature. The maximum temperature was maintained for 1 h, followed by oven cooling at a rate slower than 350°C/min.
Tensile testing (MTS 810, MTS Systems Corp., Eden Prairie, USA) was performed with specimens based on smallscale testing using gage dimensions of 14 9 1 mm, which have a length-to-width ratio similar to sheet-type specimens in ASTM E8/E8M-22 (Ref 24). In-plane specimens with a tensile direction perpendicular to the traverse direction were produced by machining the tensile geometry using EDM followed by milling and cutting 1-mm-thick sections. The rate of the actuator (i.e., grip) movement was 0.21 mm/min with the specimen elongation based on the change in extensometer position at 12.5 mm. Tensile specimen sizes for freestanding Ti-6Al-4V coupons are shown in Fig. 4.

Results and Discussion
Process Parameter (TAFA 825 JPid) Figure 5 shows optical micrographs of typical Ti-6Al-4V coatings produced at low (360 slpm) and high (575 slpm) nitrogen flows for varying combustion powers, as imposed by increasing amount of kerosene flow. Instead of a splat structure typically found in thermal spray coatings, the microstructures show compaction of partially deformed particles with different degrees for interface bonding, suggesting a solid-state deposition. Coating thickness was maintained at approximately 350 lm at a deposition efficiency of 80-95%. Increasing the kerosene flow induces a decrease in coating porosity, as summarized in Fig. 6(a). The evolution of the microstructures in Fig. 5 suggests closer particle packing and increased particle deformation at higher input power possibly due to a combined effect of increased particle impact velocity and particle softening. At the moderate nitrogen flows (360 slpm), the particle boundaries are well visible in the optical micrographs, possibly due to the formation of an oxide layer on the particle surfaces. The SEM micrograph inserts of the etched cross section (using Kroll reagent) at higher magnifications emphasize the preferentially etched oxide layers on the boundaries. These interfaces become slightly less apparent at higher nitrogen flow (575 slpm) (Fig. 5d and e), and the etchant attack between the particles is less severe, suggesting less oxide formation and improved bonding. Figure 6(a) further shows slightly higher hardness values (* 370 HV 100gf ) for the coatings produced at higher nitrogen flows, at similar porosities than obtained at the lower flows, which may confirm improved metallurgical bonding. Preferential bonding is generally attributed to increased particle impact velocity ( Ref 22). The higher nitrogen flows likely impart higher gas and particle velocities, thereby lowering the particle residence time in the flame and cool the flame to balance the particle temperatures, thereby mediating in-flight oxide scale formation. Figure 6(b) shows the porosity and oxide content evolution with increasing standoff distance. A slight densification is observed, which may be related to an increased residence time of the particles in the flame available for particle heating and softening. At the same time, an increase in oxygen pickup in the coating from 0.62 to 0.76% is found. While differences in hardness of * 345-360 HV 300gf in these coatings could not be found, the increase in oxygen content suggests that the particle residence time may indeed directly affect oxide scale formation and particle bonding.
Process Scale-up and Heat Treatment (TAFA 825 JPid) Preferential spray conditions using high power at 9 lph kerosene/300 slpm oxygen in conjunction with an elevated nitrogen flow of 575 slpm to improve particle bonding were chosen to scale the thin 350 lm coatings to thicker buildups. Balancing porosity and oxygen pickup, a spray distance of 38.1 mm was used. Figure 8(a) shows micrographs of a * 5-mm-thick Ti-6A-4 V as-sprayed coating produced on a 114-mm-diameter steel mandrel, as depicted in Fig. 7. Cross sections of the full coating width (optical) along with representative SEM images after etching are depicted. While a thin porous layer is seen at approximately one mm thickness, which is attributed to a non-intended process shutdown and subsequent start-up, the bulk of the coating is rather dense with a slightly more porosity region toward the top 600 microns of the coating.
In the bulk of the deposit, the etched cross section shows rather good particle contact and bonding. Table 3 summarizes the measured coating characteristics. While the values of oxygen content of 0.76% and deposition efficiency of 94.3% are expected from the previous tests, it is interesting to note that the as-sprayed porosity of 2.7% and hardness of 261 ± 27 HV100gf are somewhat lower than in the thinner coatings described earlier. The densification for the thicker coating with respect to the thinner coupons may be caused by an extended compacting effect of the impacting particle on the underlying coating during the longer coating process, as commonly seen in cold spraying. The slightly higher porosity in the top region of the coating, visible in the optical image in Fig. 8(a), may also suggest that the underlying layers are more compacted than the top layers, driving down the overall porosity in thicker solid-state buildups. A sintering effect due to the extended exposure of the coating to 120-150°C for the duration of the deposition may also be possible.
To investigate the potential of such coating for near-net shape forming, the Ti-6Al-4V buildup was removed from the underlying substrate and subjected to vacuum heat treatment for recrystallization and beta-annealing. Figure 8 summarizes the microstructural evolution of the coatings as a function of annealing temperature. Porosity, hardness and oxygen content are given in Table 3. Both annealing temperatures induced a significant densification of the coatings down to 0.7% porosity. Zones of porosity in the as-sprayed coating such as in the top layers and a mid-layer (caused by a spray process upset) are fully homogenized and distributed uniformly throughout the coating. Further, the original particle boundaries became largely fused, resulting in an increase in hardness. The material appears fully reconstructed and transformed into equiaxial a grains with intergranular ß, which is expected to impart beneficial mechanical properties. Similar densification of coldsprayed Ti6Al4V deposits was observed by Bhowmik et al., reporting metallurgical bonding and the disappearance of all spat interfaces at vacuum heat treatment temperature of 950°C ( Ref 19). In particular, a high ß-phase content contributes to formability of the alloy, which may result in higher elongation to failure in tensile testing, as discussed in a later section. For the heat-treated samples, the lighter phase in the SEM micrographs represents the ß phase component. The presence of the ß phase in the betaannealed sample was confirmed by XRD though a small diffraction signal at the ß (110) line, as shown in Fig. 9. It is interesting to note the a-grain grown at 1025°C (betaannealing) over the 925°recrystallization. No interlamellar a could be discerned, possibly because of the high oxygen content in the coating stabilizing the a-phase.
Process Parameters (ID-Nova MK6) Figure 10 shows optical micrographs (500x) of approximately 400-lm-thick Ti-6Al-4V coatings produced with the ID-Nova MK-6 system at increasing torch power from Increasing the input power drastically reduces the porosity from 16% in (a) to 8% in (b) down to 0.2% in (c) at the highest power and drives the deposition efficiency from * 70% to close to 100%, as summarized in Table 4. It is interesting to note that at the lower powers, the particles are barely deformed and exhibit a significant oxide scale, as indicated by the gray particle boundaries visible in the micrographs even without etching. These oxide scales possibly further impeding particle bonding and contribute  to the high porosity. The denser regions in (b) appear to be formed by oxides and small fines filling the gaps. The oxide content in coating (b) is 1.74 ± 0.07% with a coating hardness of 300 ± 61 HV 100gf . In contrast, the coating produced at the highest power (c) shows a lower oxide content of 1.06 ± 0.1% and a lower hardness of 210 ± 20 HV 100gf , suggesting a superior degree of particle bonding with less oxide scale. The XRD spectra in Fig. 11 suggest the presence of a-case (oxide scale) at the lower-power conditions. It is possible that at the highest gas flow rates, although at higher power, the higher particle velocity and lower residence time limit in-flight oxidation of the particles and create the superior coating. Since the higher power condition is associated with the higher gas flow rates, it is possible that the resulting higher particle velocity and shorter residence time limit the in-flight oxidation and create a superior coating.

Process Scale-up and Heat Treatment (ID-Nova MK6)
The preferential spray conditions at the higher net powers were scaled to a coating thickness of * 2 mm. Figure 12 shows the SEM microstructures of the as-sprayed coatings at 49 and 52 kW net power. Deposition efficiencies, oxygen content and hardness was preserved by the scaling. However, for the 49 kW condition the overall porosity is reduced from * 8% (Fig. 10b) to below 3.5% (Fig. 12a) and the residual porosity is primarily found in the top layers of the coating. This feature was consistent for all coatings produced with the ID-Nova MK6 and maybe an indication that there is a compaction effect on the underlying layers by the impinging solid-state particles, similar to the observations made for the JPid 825 coatings above. These thicker coatings were subsequently removed from the underlying substrate and subjected to vacuum heat treatment for beta-annealing at 1025°C. Optical and SEM micrographs in Fig. 13 show that the heat treatment fully fused and reconstructed the original particle boundaries, leading to increase in hardness, and ultimately transforming the material into equiaxial a grains with intergranular ß. Material characteristics of the as-sprayed and heat-treated samples are summarized in Table 5. The porosity gradients of coating a), as produced at lower power, fully disappear. Any residual porosity is homogenously disturbed throughout the layer. It is interesting to note that the remaining porosity after heat treatment does not correlate with the as-sprayed porosity and that the coating produced at higher power exhibits significantly more b-phase than the lower-power coating in Fig. 13. This is attributed to its lower oxygen content of approximately 1%, stabilizing the a-phase to a lesser extent and thereby allowing more b-phase formation. The small

Tensile Testing and Mechanical Properties
The mechanical properties of selected coatings were evaluated by tensile testing following the ASTM standard E8/ E8M-22 (Ref 24). For these test, freestanding and heat-treated sections of the coating were machined into tensile test coupons, as described above. Due to an oxygen content of 1% and above in multiple samples, only the samples with the lowest oxygen content, as produced by the JPid-825 system, are considered at this stage of the study. An average of five specimen per conditions were recorded. Figure 14 shows representative stress-strain curves for recrystallization and bannealed coupons. Two replicates are shown for the b-annealed coupons. Table 6 summarizes the mechanical properties of the HVOF-sprayed Ti-6Al-4V buildups.
The attained ultimate tensile strength of * 890 MPa after recrystallization and in particular 1126 MPa after beta-annealing compares highly favorable to the values reported in the literature, which are generally below 900 MPa for coatings produced by low-and high-pressure HVOF warm spraying, cold spraying, low-pressure plasma spraying or bulk material. However, the elongation at failure of * 1% is low in comparison with the literature data. The formability of Ti-6Al-4V and, by consequence, its elongation at failure is related to both the microstructure of the material and the amount of b-phase. The limited elongation here is likely due to high level of a-phase stabilization, thereby suppressing the b-phase, by the residual oxygen content in the buildup of approximately 0.7%. Further reduction in this oxygen content both from the feedstock and processing side would be required to further improve these properties.

Conclusion
This study illustrates the potential viability of using novel miniaturized HVOF systems for the production of near-netshaped Ti-6Al-4V materials. In particular, the addition of nitrogen into the combustion was implemented in these smaller systems to improve as-sprayed coating porosity by increasing the gas and particle velocity and mediate the particle heating to limit oxide scale formation. Both the kerosene-and hydrogen-fuelled systems demonstrated very high deposition efficiencies above 80% for coatings or parts reaching multiple millimeters in thickness. As-spayed coatings can attain porosities well below 3%. Post-treatment through recrystallization and beta-annealing fuses the as-sprayed coating structure into nearly fully dense buildups and transforms the material into equiaxial a grains with intergranular ß. The amount of beta phase increases with both increasing annealing temperature and decreasing oxygen content. For these HVOF buildups, beta-annealing can generate exceptional ultimate tensile strength with UTS over 1100 MPa. To further improve the mechanical  properties, a key challenge is the reduction in the residual oxygen content in the coating to improve particle bonding and to avoid a-phase stabilization, thereby allowing for b-phase creation for higher elongation at failure and formability.
Funding Open Access provided by National Research Council Canada.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons. org/licenses/by/4.0/.