Easy-Made Setup for High-Temperature (Up to 1100 °C) Electrochemical Impedance Spectroscopy

In the following communication, we report an easy-to-assemble Swagelok-like setup for high-temperature electrochemical impedance spectroscopy with good reproducibility based on robust 1.4114 steel 10M screws joined by non-conductive ceramics-Al2O3. We analyze the sample materials for electrochemical merits (activation energy, charge-carrier density and flatband potential) of well-known standards such as yttria-stabilized zirconia with 8 mol.% Y2O3 (8YSZ), CeO2 and In2O3. The material‘s data are compared with literature data performed on a standard impedance analyzer within a casual high-temperature commercial cells. The symmetrical cell consists of insulating material (Al2O3 screw) and two steel contacts, connected by PtRh wires of thermal resistance tolerating temperatures of 2300 °C. Our high-temperature electrochemical setup is able to withstand temperatures up to 1100 °C and can be easily and mildly cleaned for repetitive usage. In addition, we present a methodology for generation of a high-temperature sintered 8YSZ ceramics and evaluate them with our setup. We analyze the internal resistances within the setup and propose a simplified option for introduction of various gas atmospheres into the sample‘s interior, as well as evaluate the utilization of tube furnace for simplicity. We perform equivalent circuit fitting and present an easy to implement approach for reliable high-temperature electrochemistry.

One of the most interesting examples of high-temperature electrochemistry involves dielectric spectroscopy, in particular, electrochemical impedance spectroscopy (EIS) ( . EIS is a technique able to non-destructively investigate crucial material parameters at high temperature, such as conductivity, viscosity (acoustic impedance spectroscopy), activation energy of oxygen vacancy in, e.g., k-oxygen sensors, resistance of the ionic transport within, e.g., porous ceramics (Mac Mullin number for solid-state electrolytes) or even the evaluation of charge-carrier density in photovoltaic materials (Mott-Schottky junctions) (Ref [13][14][15][16]. The current development of hightemperature electrochemistry makes EIS therefore a lucrative and cost-effective method for evaluation of materialÕs behavior at elevated temperatures. The main drawback of the application of EIS at both laboratory and pilot scale is the need for a reliable system allowing to acquire the desired spectra in a dedicated span of alternating current (AC) frequencies ( Ref 17,18). Main parts of such a system are the signal analyzer (galvanostat for galvanostatic electrochemical impedance spectroscopy (GEIS) and potentiostat for potentio-electrochemical impedance spectroscopy (PEIS)). Most of the modern instruments (Gamry, BioLogic, Princeton Instruments, CHI, MetroOhm) utilize this bifunctionality in one setup. Another crucial part is obviously the cell containing the material for analysis, which is connected to the signal analyzer (Ref [19][20][21][22]. It needs to be chemically and temperature resistant and should not or minimally and in Fig. 1 Experimental cell setup based on M10 metric 1.4841 hightemperature resistant screws with Al 2 O 3 nut (96% pure, 30% apparent porosity for gas permeation). The thickness of the PtRh wire is exaggerated for clarity. The cell was placed inside the tube furnace with two inlets for feeding the PtRh wires through (Carbolite, operating temperature up to 1200°C). The crocodile clips ensure connection to the potentiostat outside the tube furnace ( Figure S1, Supporting Information). The cell can be operated up to 1100°C and is limited by the 1.4841 heat-resistant screws controlled fashion contribute to the internal resistance of the measurement, nor to the iR drop (Ref [23][24][25]. It should also be reliable, cost-effective and easy to assemble for multiple analysis of, e.g., batches during pilot or large-scale production ( Ref 26).
In order to fulfill those requirements, we propose an affordable, yet reliable and easy-to-assemble setup for hightemperature (up to 1100°C) electrochemistry with particular emphasis on EIS. The analysis cell depicted in Fig. 1 consists of three major parts: the 1.4841 steel M10 screws with flat electrical contacts, a ceramic non-conductive alumina nut and high-temperature resistant and conductive wire connections (PtRh) point-welded by an arc discharge (300 V) to the 1.4841 steel screws. The high-porosity of the alumina nut allows to vary the gas atmosphere (e.g., vacuum, synthetic air, argon, neon). The material of interest is placed within a nut of welldefined geometry and is brought to contact with 1.4841 hightemperature-resistant steel from both sides. This allows to avoid the necessity of conductive film deposition by DC sputtering or physical vapor deposition (PVD) on the, e.g., ceramic materials in order to create electric contact, which is often the case for laboratory-scale research. The so-prepared Swagelok-type cell may then be placed in a tube furnace with the desired gas type and flow (Fig. 2, inset A), which allows to perform electrochemical analysis.
This contribution investigates the obtained electrochemical merits on standard materials (8% yttria-stabilized zirconium oxide; 8YSZ oxygen gas sensor and catalytic RedOx-active oxide such as CeO 2 and In 2 O 3 ), as well as research-type sintered 8YSZ ceramics. The obtained results are compared with the literature, and the potential of using the simplified Swagelok-type cell approach is discussed.

Materials and Methods
Electrochemical measurements of staircase potentio-electrochemical impedance spectroscopy (SPEIS) were acquired with a BioLogic VSP potentiostat (France) equipped with PCcontrolled EC-Lab software (version 11.33) and were performed in single sine mode in a 1MHz-1mHz frequency range. Mott-Schottky analysis was acquired in À 1.5 to +1.5 V versus open circuit potential (OCP) range with 1500 potential steps (dE 2 mV), 10 mV sinus amplitude and 6 points per decade of frequency in logarithmic spacing with 2 measurements per set used for signal averaging. Each SPEIS spectrum was validated by Kramers-Kronig relations and numerically fitted by a Z-fit procedure with details emphasized in the text. The custommade standardized 10M screw threads were prepared according to the standard of ISO 10642 out of steel type 1.4841 (temperature inertness till 1150°C in air under standard conditions). PtRh wires (250 lm thick as confirmed by digital optical microscopy and of 99.9% purity, as confirmed by X-ray photoelectron spectroscopy, each 15 cm long) were pointwelded to the screws in house by an arc discharge. The PtRh contribution to the Nyquist plots were neutralized by the iR drop determination, as only the electrode resistance was affected during the measurement. Standard alligator-clips were placed at the end of the wires for connecting the signals to the  potentiostat. The internal resistance of the PtRh wire was established as less than 0.1 mOhm and is therefore excluded from the calculation of the electrochemical merits. The conductivity was calibrated using alomel (99.9% purity, inhouse source). The dihedral-width M10 nuts were purchased from Misumi, Japan (CA/NN-M10), which are composed of 96% alumina (with rest 4% of calcium oxide impurities, as established by X-Ray photoelectron spectroscopy in house) and are of 30% apparent porosity. The tube furnace from Carbolite Furnaces Ltd &02-3216P1 (Type MTF 12/25 A Figure S1) with internal controller was employed ( Figure S1, Supporting Information). The temperature within the nut was calibrated as opened (one side left unclosed with steel screw) after 45 minutes from reaching the measurement temperature by the Kthermocouple of +/À 1.1°C measurement certainty and 35 lV/ K Seebeck coefficient, to which all temperature measurements in text are referred (Fig. 2). CeO 2 , In 2 O 3 and the 8YSZ powders were purchased from Sigma-Aldrich/Merck, Germany. The 8YSZ scintillated pellet was prepared by pressing 100 mg material in a 10-mm piston under 10 tons of hydraulic pressure and subsequent scintillation at 1000°C for 24 hours under atmospheric air. The commercial 8YSZ pellet fitting 10M metric screw was purchased from Keramik GmbH, Germany. The gas flow into the cell was introduced by inserting the inlets and outlets to the Carbolite tube furnace ( Figure S1). The gas flow in sccm was controlled by a home-build Hg manometer.  At 560°C, pellet 5 At 560°C, pellet 6 Data not reported in the literature The point welding was performed by a direct current (DC) arc discharge at 300 V, without the use of any external metals.

Results and Discussion
We present a design of the measurement cell, calibration of the tube furnace temperature and results for impedance characterization of the materials 8YSZ, CeO 2 , In 2 O 3 and selfsintered experimental 8YSZ. We estimate the activation energies, flatband potentials and internal resistances of the cell based on equivalent circuit analysis according to the standardized Z-fit numerical procedure. We present the experimental measurement data up to 750°C and estimate the capability of measurements up to 1100°C in order to evaluate the cell stability.

Cell Design and its Validation
In the first step, the cell was assembled according to Fig. 1. PtRh wires were attached to crocodile clips and the measurement cell setup could be compared to the 2-probe measurement of a typical 2-electrode cell. The only contribution of the conductivity is the material under investigation, as Al 2 O 3 is not conductive also at elevated temperature. The potentially occurring perturbation arising from the wiring was removed by application of PtRh wire with minimal self-resistance. The quality of PtRh was carefully evaluated by means of XPS spectroscopy. The thermal resistance up to 2300°C and excellent electrical conductivity of this alloy have allowed for non-disturbed measurements.
The relatively large porosity of the alumina nut has allowed for introduction of various gaseous environments into the interior of the investigation area. An example of such a measurement under 20 sccm of oxygen flow at elevated temperatures is presented in Fig. 4,  . Here, the Ô means the negative charge, while . is the positive charge. V 0 is the vacancy replacing oxygen, and x stands for the charge-neutrality. The presence of oxygen vacancies is strongly suggested, as based on the activation energy, which was calculated to be 89.01 kJ/mol (0.92 eV) for the synthesized 8YSZ, 83.21 kJ/mol (0.86 eV) for the commercial 8YSZ ceramic ring (GmbH, Germany), 91.66 kJ/mol (0.92 eV) for CeO 2 and 136.98 kJ/mol (1.38 eV) for In 2 O 3 ( Table 1). Owing to the various concentrations of oxygen vacancies, which was additionally investigated by means of staircase potentiostatic-impedance spectroscopy (SPEIS) and the Mott-Schottky equation (Eq 2), the value of the activation energy was established to depend on the chemical environment ( Ref 27). The results of the activation energy, charge-carrier concentration and flatband potential calculations are gathered in Table 1. We note that the dielectric constants needed for the calculations of the concentrations of active species were calculated according to the procedures reported in the literature; in our case, we restrict ourselves to fixed temperatures with smallest values of resistance, as judged by a Z-fit of the equivalent circuits ( Ref 28,29). Figure 2 shows a representative plot for the Al 2 O 3 nut interior temperature calibration within the opened measurement cell placed within the tube furnace. Owing to the uniform thermal convection within the tube furnace, the nut interior measured with one side open (i.e., with one screw left out) has proven the accuracy of the temperature readout of the furnace display and of the K-element thermocouple temperature readout placed within the cellÕs interior.

Measurements of Standards
In order to assess the applicability of simple measurement cell in Fig. 1, we have performed a temperature-dependent determination of oxygen vacancies within CeO 2 , In 2 O 3 , commercial 8YSZ and self-made 8YSZ under various gas atmospheres. By applying the Arrhenius equation: and the Mott-Schottky equation: where r is the conductivity, A the Arrhenius constant, E a the activation energy, R the universal gas constant, T the temperature, and C is the capacitance, e and e 0 are the dielectric constant and permittivity in vacuum, k B is the Boltzmann constant, A the electrode surface area, e the number of electrons transferred (assumed as 1), N D the charge-carrier density (in cm À3 ), V is the measured potential against the normal hydrogen electrode (NHE, in Volt), and V FB is the flatband potential (in Volt). According to the proposed hoping mechanism of conductivity in the literature, which depends on the amount of available and addressable (at the given temperature) oxygen vacancies, the saturation of those by gas flow leads to differences in impedance spectra and is a well-known phenomenon (Ref 30). Our approach was to evaluate the Al 2 O 3 porosity in order to observe the effect of oxygen saturation. The experimental results for oxygen flow (20 sccm) are shown in Fig. 4, insets A/B.
The measurements of commercial standards are in agreement with the literature (Ref [31][32][33][34][35]. The equivalent circuit modeling is exemplary shown in the Fig. 3, inset A, as a magnified cut-out from the cumulative assembly of EIS spectra in the inset B. The spectra show good agreement with the theoretically obtainable results (error analysis of the Z-fit v 2 / Z = 0.35), as judged by the 6.7% error yielded by the Kramers-Kronig relations (KK relations). The KK analysis represents the mathematical dependence of the imaginary and real parts of the impedance, therefore proving the application potential of the proposed high-temperature measurement system (Ref 36. The conductivity of CeO 2 and In 2 O 3 owing to the hoping mechanism was evaluated and found to be in good comparison with the literature data ( Ref 38,39). We have observed the accessibility of oxygen vacancies to vary at different temperatures, but considered a temperature of 350°C for both CeO 2 and In 2 O 3 in order to compare the charge-carrier density with literature values (Ref 31-35). The respective Arrhenius plots for CeO 2 , In 2 O 3 and YSZ (both synthesized and commercial) can be found in the Supporting Information.
The substitution of Ce 4+ in ceria and In 3+ in indium oxide by foreign elements due to the implantation or respective sample preparation (e.g., electrospinning) results in an increased amount of oxygen vacancies, which are treated as the main source of the charge-carriers ( Ref 40). Many of the vacancies will nevertheless be intrinsically built into the structure as point defects, which consequently leads to an improved conductivity ( Ref 41). The different accessibility of oxygen vacancies is translated to charge-carrier densities and is not to be referred to structural changes, as, e.g., ceria exhibiting a fluorite Fm3m space group up to its melting point at 2477°C, but rather to the bulk activation energy needed per mol unit of the material under investigation ( Ref 42,43). For example, the chargecarrier density of In 2 O 3 can vary, as it depends on the amount of reduced material, which occurs due to the thermal RedOx reduction reaction: 2In 2 O 3 ! 4In 0 + 3O 2 , meaning that the materialÕs chemistry is involved in a large bundle of parameters influencing the conductivity. In the case of oxide materials, this may vary from batch to batch (Ref 43, 44).

Measurement of Experimental Research Samples
In order to investigate the potential of the proposed setup, we have performed a real-run test of the research-type prepared samples. The 8YSZ powder was sintered under air for 24 hours at 1000°C prior to pelletization as described in the materials and methods section. The translucent ceramic pellet was carefully placed inside the measurement cell and brought into the tube furnace. We have observed much higher temperature activity of the sample at 660°C, as manifested by the generation of the semi-circle in the Nyquist plot and therefore the observed temperature-dependent conductivity. The results aiming for a comparison of the merits obtained by our cell with literature values are gathered in Table 1. Figure 4 shows the applicability of the cell for measurements during respective gas treatments. The spectra in A and B show different temperatures, while only in the range of 560-566°C the peculiar generation of the second semi-circle was observed, which was attributed to the phase transition within the monoclinic 8YSZ system to the tetragonal system (Ref 54). Interestingly, this phase transition behavior was observed only under oxygen atmosphere. Further discussion of this effect is nevertheless outside of scope of this article and we refer to the reader to the comprehensive review of that matter in the literature ( Ref 54).
The peculiarity of ceramic solid and oxygen gas interaction is still a matter of research, as conductivity (both electrical and ionic) measurements at higher temperatures are considered to be challenging ( Ref 45). The dependence of the gas atmosphere on the 8YSZ conductivity (specified in this study by a gas pressure of 1 atm and a flow of 20 sccm) and especially on the oxygen vacancies saturation is manifested by the presence of the charges in the bulk of the material, which causes creation of holes within CeO 2 and In 2 O 3 . The exact character of holes and the creation of localized Frenkel exciton states within the 8YSZ, as well as their exact position and contribution to the final states of the Bloch-conduction band, are not fully understood yet and are currently a matter of intensive computational studies (Ref [46][47][48][49]. In case of the data presented in Table 1, the conductivity of 8YSZ varies strongly with the atmosphere, while the position of relative to the conduction band and easily obtainable flatband may provide additional merits explaining the accessibility of excitons and their influence on the conductivity ( Ref 50). The possibility of more careful temperature control should provide better insight into the quantum properties of ceramics under investigation within our system.

Conclusions
In this study, we have presented an easy method for reliable measurements of high-temperature impedance spectroscopy in a cell of well-defined geometry, easy availability of the assembly materials and high durability. The cell consists of 1.4841 10M steel screws with temperature resistance up to 1150°C, alumina (96% Al 2 O 3 ) and PtRh connectors. We have performed analysis of electrochemical merits like activation energy of oxygen vacancies in ceria, In 2 O 3 and yttria-stabilized zirconium oxide, their charge-carrier concentration and flatband potential. We have established that the amount of charge transfer concentration varies with temperature, which we refer to as the activation energy needed to successfully activate the active centers and we discussed the availability of Frenkel excitons potentially contributing to the conductivity. The theory of flatband was referred to the position of the Bloch-conduction band in order to demonstrate the possibility of performing investigations of quantum electronic structure of both powders and pellets. After characterization of the commercial standards, we have demonstrated a possibility of investigation of researchgrade materials, such as self-prepared 8YSZ. We also shown the influence of gas atmosphere on the impedance measurement due to the large 30% porosity of the alumina used as the powder/pellet vessel. In conclusion, our approach can be used in any tube furnace of adequate size and our normalized approach of the cell makes high-temperature impedance measurements a straightforward, reproducible and highly accurate task.

Funding
Open Access funding enabled and organized by Projekt DEAL. We acknowledge the funding provided by Deutsche Forschungsgemeinschaft (DFG, HA 6128/6-1).

Conflict of interest
The authors declare no conflict of interest.

Open Access
This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.