High entropy alloys (HEAs) attract more and more attention due to their simple structure, high strength and hardness, good ductility, and excellent softening, oxidation, corrosion, and wear resistance properties. Among the known HEA systems, the AlCoCrFeNi alloy exhibits complicated microstructure and excellent mechanical properties. In this study, the AlCoCrFeNi/TiB2 composites were prepared via power metallurgy route in combination with spark plasma sintering (SPS) technology. At first, the AlCoCrFeNi HEA powders were prepared by gas-atomization technology under Ar atmosphere with the high purity of raw elemental materials. The commercial TiB2 powders with average particle size of about 2 Îźm were used as the reinforcing agent to prepare the AlCoCrFeNi/TiB2 composites. The effect of TiB2 content on the phase, microstructure, and tribological properties of the synthesized AlCoCrFeNi/TiB2 composites were investigated by XRD, SEM, and EPMA, whereas also through friction and wear tests. The results show that phase transformation occurs with Ď phase formation after sintering. The TiB2 particles tend to agglomerate and grow up with increased TiB2 content. The effect of TiB2 on the tribological behavior of the composites was studied through measuring the coefficient of friction (COF) and wear rate (W). The resulting values of COF and W show that the wear resistance of AlCoCrFeNi/TiB2 composites is improved with increasing the TiB2 content.
Similar content being viewed by others
References
J.W. Yeh, S.K. Chen, S.J. Lin, J.Y. Gan, T.S. Chin, T.T. Shun, C.H. Tsau, and S.Y. Chang, âNanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes,â Adv. Eng. Mater., 6, 299â303 (2004).
Y. Zhang, T.T. Zuo, Z. Tang, M.C. Gao, K.A. Dahmen, P.K. Liaw, and Z.P. Lu, âMicrostructures and properties of high-entropy alloys,â Prog. Mater. Sci., 61, 1â93 (2014).
Y. Yu, J. Wang, J.S. Li, J. Yang, H.C. Kou, and W.M. Liu, âTribological behavior of AlCoCrFeNi(Ti0.5) high entropy alloys under oil and MACs lubrication,â J. Mater. Sci. Tech., 32, 470â476 (2016).
S.J. Chen, H.S. Oh, B. Gludovatz, S.J. Kim, E.S. Park, Z. Zhang, R.O. Ritchie, and Q. Yu, âReal-time observations of Trip-induced ultrahigh strain hardening in a dual-phase CrMnFeCoNi high-entropy alloy,â Nat. Commun., 11, 826 (2020).
T.F. Yang, W. Guo, J.D. Poplawsky, D.Y. Li, L. Wang, Y. Li, W.Y. Hu, M.L. Crespillo, Z.F. Yan, Y. Zhang, and Y.G. Wang, âStructural damage and phase stability of Al0.3CoCrFeNi high entropy alloyunder high temperature ion irradiation,â J. Alloys Compd., 188, 1â15 (2020).
Y.Z. Shi, L. Collins, R. Feng, C. Zhang, N. Balke, P.K. Liaw, and B. Yang, âHomogenization of AlCoCrFeNi high-entropy alloys with improved corrosion resistance,â Corros. Sci., 133, 120â131 (2018).
V.F. Gorban, M.I. Danylenko, M.A. Krapivka, and S.A. Firstov, âStructural and chemical microinhomogeneity of the high-entropy TiVZrNbHfTa coating,â Powder. Metall. Met. Ceram., 58 469â473 (2019).
A. Munitz, S. Salhov, S. Hayun, and N. Frage, âHeat treatment impacts the micro-structure and mechanical properties of AlCoCrFeNi high entropy alloy,â J. Alloys Compd., 683, 221â230 (2016).
P.F. Zhou, D.H. Xiao, Z. Wu, and M. Song, âMicrostructure and mechanical properties of AlCoCrFeNi high entropy alloys produced by spark plasma sintering,â Mater. Res. Express., 6, 0865e7 (2019).
K.S. Li, K.H. Kang, K.R. Lim, and Y.S. Na, âInfluence of compressive strain on the microstructural evolution of an AlCoCrFeNi high entropy alloy,â Mater. Charact., 132, 162â168 (2017).
K.P. Kumara, M.G. Krishna, J.B. Rao, and N.R.M.R. Bhargava, âFabrication and characterization of 2024 aluminium-high entropy alloy composites,â J. Alloys Compd., 640, 421â427 (2015).
J. Chen, P.Y. Niu, T. Wei, L. Hao, Y.Z. Liu, X.H. Wang, and Y.L. Peng, âFabrication and mechanical properties of AlCoNiCrFe high-entropy alloy particle reinforced Cu matrix composites,â J. Alloys Compd., 649, 630â634 (2015).
G.H. Meng, X. Lin, H. Xie, C. Wang, S.Q. Wang, and X. Ding, âReinforcement and substrate interaction in laser surface forming of AlCoCrCuFeNi particle reinforced AZ91D matrix composites,â J. Alloys Compd., 672, 660â667 (2016).
P.F. Zhou, D.H. Xiao, and T.C. Yuan, âComparison between ultrafine-grained WCâCo and WCâHEAâcemented carbides,â Powder Metall., 60, 1â6 (2016).
G. Zhu, Y. Liu, and J.W. Ye, âEarly high-temperature oxidation behavior of Ti(C, N)-based cermets with multi-component AlCoCrFeNi high-entropy alloy binder,â Int. J. Refract. Met. H., 44, 35â41 (2014).
Y.L. Li, H.Y. Xu, B.R. Ke, Y.C. Sun, K. Yang, W. Ji, W.M. Wang, and Z.Y. Fu, âTEM characterization of a Supra-Nano-Dual-Phase binder phase in spark plasma sintered TiB2â5 wt.% HEAs cermet,â Ceram. Int. 45, 9401â9405 (2019).
Z. Fu and R. Koc, âTiNiFeCrCoAl high-entropy alloys as novel metallic binders for TiB2âTiC based composites,â Mater. Sci. Eng. A, 735, 302â309 (2018).
E. Colombini, M.L. Gualtieri, R. Rosa, F. Tarterini, M. Zadra, A. Casagrande, and P. Veronesi, âSPSassisted Synthesis of SiCp reinforced high entropy alloys: reactivity of SiC and effects of pre-mechanical alloying and post-annealing treatment,â Powder Metall., 61, 64â72 (2017).
A.S. Sharma, K. Biswas, and B. Basu, âMicrostructure-hardness-fretting wear resistance correlation in ultrafine grained CuâTiB2âPb composites,â Wear, 319, 160â171 (2014).
Z.Z. Fu and R. Koc, âUltrafine TiB2âTiNiFeCrCoAl high-entropy alloy composite with enhanced mechanical properties,â Mater. Sci. Eng. A, 702, 184â188 (2017).
S. Yadav, A. Aggrawal, A. Kumar, and K. Biswas, âEffect of TiB2 addition on wear behavior of (AlCrFeMnV)90Bi10 high entropy alloy composite,â Tribol. Int., 132, 62â74 (2019).
D. Medved, J. Balko, R. SedlĂĄk, A. KovalÄĂkovĂĄ, I. Shepa, A. Naughton-DuszovĂĄb, E. Baczek, M. Podsiadlo, and J. Dusza, âWear resistance of ZrB2 based ceramic composites,â Int. J. Refract. Met. H, 81, 214â224 (2019).
J.T. Liang, K.C. Cheng, and S.H. Chen, âEffect of heat treatment on the phase evolution and mechanical properties of atomized AlCoCrFeNi high-entropy alloy powders,â J. Alloys Compd., 803, 484â490 (2019).
S.Y. Xie, R.D. Li, T.C. Yuan, L.B. Zhou, M. Zhang, M.B. Wang, P.D. Niu, P. Cao, and C. Chen, âEffect of heating rate on microstructure and mechanical properties of AlCoCrFeNi high entropy alloy produced by spark plasma sintering,â Mater. Charact., 154, 169â180 (2019).
J.C. Rao, H.Y. Diao, V. OcelĂk, D. Vainchtein, C. Zhang C. , Kuo, Z. Tang, W. Guo, J.D. Poplawsky, Y. Zhou, P.K. Liaw, and J.Th.M. De Hosson, âSecondary phases in AlxCoCrFeNi high-entropy alloys: An in-situ TEM heating study and thermodynamic appraisal,â Acta Mater., 131, 206â220 (2017).
S. Sing, N. Wanderka, K. Kiefer, K. Siemensmeyer, and J Banhart, âEffect of decomposition of the CrâFâCo rich phase of AlCoCrCuFeNi high entropy alloy on magnetic properties,â Ultramicroscopy, 111, 619â622 (2011).
Z. Wu, M.C. Troparevsky, Y.F. Gao, J.R. Morris, G.M. Stocks, and H. Bei, âPhase stability, physical properties and strengthening mechanisms of concentrated solid solution alloys,â Curr. Opin. Solid State Mater. Sci., 21, 267â284 (2017).
Quantitative EDS X-ray microanalysis using SEM, Australian Microscopy and Microanalysis Research Facility (2014).
M. Chen, L.W. Lan, X.H. Shi, H.J. Yang, M. Zhang, and J.W. Qiao, âThe tribological properties of Al0.6CoCrFeNi high-entropy alloy with the Ď phase precipitation at elevated temperature,â J. Alloys Compd., 777, 180â189 (2019).
I.A. Podchernyaeva, S.A. Klimenko, V.M. Beresnev, V.M. Panashenko, I.N. Toryanik, S.An. Klimenko, and M.Yu. Kopeikina, âFormation of a tribofilm in the surface layer of AlâTiâCrâNâB magnetron coating on boron nitride during turning of hardened steel,â Metall. Met. C+, 54, 140â150 (2015).
C.Y. Hsu, T.S. Sheu, J.W. Yeh, and S.K. Chen, âEffect of iron content on wear behavior of AlCoCrFexMo0.5Ni high-entropy alloys,â Wear, 268, 653â659 (2010).
Author information
Authors and Affiliations
Corresponding author
Additional information
Published in Poroshkova Metallurgiya, Vol. 59, Nos. 9â10 (535), pp. 68â78, 2020.
Rights and permissions
About this article
Cite this article
Kang, J.G., Yang, B.T. & Wei, J.C. Effect of TiB2 on the Phase Composition, Microstructure, and Tribological Properties of AlCoCrFeNi/TiB2 Composites. Powder Metall Met Ceram 59, 537â545 (2021). https://doi.org/10.1007/s11106-021-00195-4
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11106-021-00195-4