Structural, optical, dielectric, and surface properties of polyimide hybrid nanocomposites films embedded mesoporous silica nanoparticles synthesized from rice husk ash for optoelectronic applications

In this study, mesoporous silica nanoparticles previously prepared from the rice husk ash were utilized as nanofillers to fabricate thin films of polyimide/silica hybrid nanocomposites with different ratios (0, 6, 8, 10, and 12%). Subsequently, all hybrid films were further subjected to comprehensive characterization using XRD, SEM, AFM, and contact angle analyzers. The films exhibited a variety of optoelectronic properties depending on the silica nanoparticles' content. Where the silica nanofillers affected the optical clarity of polyimide films and increasing the silica ratio resulted in decreasing in films transmittance which led to reducing the transparency and enhanced the absorption coefficient of films in the UV range. Besides, the dielectric constant value and free charge carrier concentrations have increased which promoted the optical conductivity of the films. Moreover, increasing silica content resulted in converting the films from hydrophobic to hydrophilic surfaces, and has improved their wettability at all pH values.

of silica nanoparticles. In addition, this study was expanded to investigate the suitability of the prepared nanocomposites films for optoelectronic applications.

Materials
RH was collected from agricultural fields, in Giza, Egypt. Hydrochloric acid (HCl), extra pure with 35% purity and molecular weight of 36.46 g/mol was obtained from Loba Chemie. Sodium hydroxide pellets (NaOH), ACS reagent with assay ≥ 97%, and molecular weight of 39.99 g/mol were obtained from Fisher Scientific. Ammonia solution (NH 4 OH), AR with 18-20% purity, and molecular weight of 35.05 g/mol were obtained from Loba Chemie. Ethanol solution (C 2 H 5 OH), with a purity of 96% and molecular weight of 46.07 was purchased from the Merck group.

Raw material analysis
Rice waste is an agricultural waste with a high content of amorphous silica. However, the presence of metal ion impurities and unburned carbon may present an adverse effect on product color and purity. In this regard, different extraction techniques were applied to produce high-quality SiO 2 NPs. The silica extraction process was carried out under diverse conditions to evaluate the effect of different pretreatments on produced silica; these conditions include different types of acid with varying concentrations and various calcination temperatures. In the present study, silica was produced by the sol-gel method. In the case of the combustion method, the best conditions for pretreatment of rice wastes to produce silica were using HCl in the demineralization process at room temperature and a concentration range of 3 M for rice husk under the temperature of calcination was 800 °C for 1 h. The lower temperatures were found to contain unburned carbon as it was clear from the gray color. The yield of resulted silica was 13%. Table 1 shows the chemical analysis of rice husk. The results of lignin, holocellulose, α-Cellulose, lignin, and hemicelluloses are based on extract-free raw materials.

Preparation of mesoporous silica nanoparticles
Mesoporous silica nanoparticles were obtained from the rice husk ash through the following steps; firstly, the rice husk ash was soaked and washed in distilled water to remove the dust and other soluble organic and inorganic materials. Then, the washed rice husk ash was dried in an oven at 120 °C for 24 h. To remove the carbonate materials from the rice husk ash, the dried rice husk ash was soaked in an acidic solution for 24 h. Afterward, it was washed with distilled water several times to remove the excess acid and then was air-dried for 24 h. The purified rice husk ash was burned in a muffle furnace at 800 °C for 1 h. Following, 2.5 M of NaOH was mixed with 10 g of the burned rice husk ash and was boiled for 4 h followed by a filtration step. Thereafter, 1 g of the filtrate was dissolved in a mixture of (ethanol, H 2 O, and ammonia solution), and was stirred for 1 h at room temperature. A cationic quaternary ammonium surfactant was added to the above mixture with continuous stirring for 4 h at room temperature. Subsequently, the mixture was left for 48 h to evaporate the solvent and form a gel. Finally, the gel was dried at 600 °C for 2 h to obtain mesoporous silica nanoparticles.
To further check the chemical composition of purified rice husk and the produced mesoporous silica nanoparticles, an ICP analysis was conducted to examine the purity of silica nanoparticles extracted from the rice husk. The analysis of heavy metal species was performed using the inductively coupled plasma-mass spectrometer (X-Series 2 ICP-MS, Thermo Scientific). The contents of metal species in the treated biomass and the yielded silica nanoparticles were given in Table 2. The obtained results showed that the acid treatment helps in reducing the impurities, and has resulted in more pure mesoporous silica nanoparticles.
1 g of PAA-PM in NMP solution was added to 1 gm of DMF. The mixture was stirred for 1 h, and then they were sonicated for 30 min. Finally, the solution was cast onto sodalime glass plates and was cured in an oven under the air atmosphere. Imidization was achieved by placing the films in an air oven for three successive 1 h durations, at 100, 200, and 300 °C, respectively.
To prepare polyimide/mesoporous silica hybrid nanocomposites films, 1 g of PAA-PM in NMP solution was added to 1 g of DMF. An appropriate amount of the prepared mesoporous silica nanoparticles according to different molar ratios based on 0, 6, 8, 10, and 12 wt.% was dissolved in 1 g of DMF and mixed with the dissolved PAA-PM in DMF, respectively. The mixture was stirred for 1 h, and then they were sonicated for 30 min. Finally, the solution was cast onto soda-lime glass plates and was cured in an oven under the air atmosphere. Imidization was achieved by placing the films in an air oven for three successive 1 h duration at 100, 200, and 300 °C, respectively. Meanwhile, the silica network formation simultaneously took place with the imidization process. Figure 1 presents a schematic diagram for the preparation process of the polyimide/mesoporous silica hybrid nanocomposites films.

Characterization of polyimide/mesoporous silica hybrid nanocomposites films
X-ray diffraction analyses were performed on the prepared polyimide/mesoporous silica hybrid nanocomposites films using the Bruker D8 Discover instrument. The X-ray measurements were performed using grazing incidence diffraction (GID) geometry. The Fig. 1 Schematic illustration for the mechanism of preparation of polyimide/mesoporous silica hybrid nanocomposites films prepared films were scanned in a range of 2θ = 5°-80° with a scan speed of 2°/min. Where, the Cu radiation source provided a high-intensity Cu-Kα1 parallel beam with a wavelength of 1.54060 Å and resolution of 1.5 Å under an applied voltage of 40 kV and a current of 40 mA. The morphological structures of prepared film surfaces were investigated for different ratios at various magnifications and acceleration voltage using a scanning electron microscopy (JEOL JXA-840A, Japan) analyzer. The Raman spectroscopy (Horiba labRAM HR evolution visible single spectrometer) was used to obtain the Raman shift spectrum of prepared polyimide/ mesoporous silica hybrid nanocomposites films at room temperature. The instrument was equipped with a He-Cd edge green laser line with a wavelength of 532 nm and a diffraction grating of 1800 gr/mm (450-850 nm) supported by a 25% ND filter and an objective of 50X offering a high throughput diffraction-limited lateral spatial resolution of 0.5 µm and spectral resolution of 1 cm −1 . Atomic Force Microscope (AFM, 5600LS, Agilent) was used in non-contact mode to provide 2D and 3D topographic images besides the surface roughness profiles of the prepared polyimide/ mesoporous silica hybrid nanocomposites films. The analysis of AFM images and data was carried out using Pico image basics software version 6.2. The optical properties of prepared polyimide/mesoporous silica hybrid nanocomposite films with different silica ratios were obtained using a computerized double-beam ultraviolet-visible spectrophotometer SPECORD 200 PLUS Analytik Jena with 1 nm steps. Attension Theta Topography analyzer by Biolin Scientific, model T200 under the condition of sessile drop recipe, distilled water droplet volume of 4 μm, and measurement time of 10 s was used to study the effect of surface roughness on the contact angle, wettability, and the hydrophilic properties of the prepared polyimide/ mesoporous silica hybrid nanocomposites films. The analyzer was equipped with a manual fine focusing on optics, and software-controlled autofocus. The results were analyzed using OneAttension software including all measurement modes.

X-Ray analysis
The XRD patterns for the prepared hybrid nanocomposites films were shown in Fig. 2. The XRD pattern for the pure polyimide sample is characterized by a significant barrow. According to the obtained XRD patterns, the prepared silica nanoparticles revealed a partial crystallinity with a predominantly amorphous phase. As silica nanoparticles with different ratios (6-12 wt.%) were incorporated into the polymer matrixes, an amorphous broad peak with Bragg angle at 2θ = 19-21° was obtained for all prepared nanocomposites films, which attributed to the presence of silica nanoparticles. Moreover, another small hump was observed at about 46° probably assigned to the silica nanoparticles. These results are in accordance with the standard pattern of silica in the Standards Joint Committee on Powder Diffraction (JCPDS) database with card number COD#9,000,520. In addition, the corresponding silica pattern confirmed the formation of tridymite silica with monoclinic crystal lattice structure and space group C1c1. These obtained results are in good agreement with other previous studies (Prasetyo et al. 2022;abualnoun et al. 2020;Sun et al. 2017). The different ratios of mesoporous silica nanoparticles added to the polymer matrixes caused a shift in the positions of both peaks and small humps in the XRD patterns of prepared polyimide/mesoporous silica hybrid nanocomposites films as shown in Fig. 3a, b. Accordingly, the discrepancy between these diffraction angles at 2θ = 19-21° and 2θ = 46° for the differently prepared nanocomposites films with silica ratios (0-12 wt.%) might be ascribed to the difference in the degree of imidization process of the polyimide/mesoporous silica hybrid nanocomposites films blend during the processing of the samples. It could observe that the diffraction peaks of produced films are broadened. This could be described as during the formation of the blend films; a partial rearrangement of the crystalline parts occurs inside the polymer. Thus, when a different ratio of SiO 2 nanoparticles is added to polyimide blends, a little shift occurs in the prepared nanocomposites films diffractograms resulting due to masking effect of polyimide films blend matrixes for the small contents of the SiO 2 nanoparticles. These results are in good match with the literature (Gaabour 2019;Lee et al. 2009). Moreover, Joly et al. (1999) mentioned that X-ray diffraction shows that the presence of silicon species induces modifications in the microstructure of the polyimide chains. These As above-mentioned, the position of the peaks and humps observed in patterns of films were shifted. This is due to the presence of mesoporous silica nanoparticles within the polyimide matrix. Lorentz function fitting was used to obtain information about the presented full width at half maximum (FWHM) of the barrow. Figure 4 depicts the relationship between the FWHM values of polyimide/mesoporous silica hybrid nanocomposites films and different ratios of mesoporous silica nanoparticles. The increases in mesoporous silica nanoparticles ratios from 0 to 10 wt.% causes the gradually decreasing FWHM values. While increasing the silica ratio to 12 wt.%, a rapid increase in the FWHM value occurred. Thus, it could conclude that the XRD peaks of nanocomposite films became narrower indicating that at lower ratios of SiO 2 nanoparticles, the SiO 2 nanoparticles were covered by polyimide polymer blends and the polymer vacancies did not fully occupy by the SiO 2 nanoparticles during the film deposition. Therefore, a probable decrease in the FWHM occurred. On contrary, an increase in FWHM value and peak intensity at the highest ratio of SiO 2 nanoparticles indicates that smaller crystallite sizes were formed, which increased the disordered phase inside the obtained hybrid nanocomposites films and indicated a distortion of crystalline structures due to the crosslinking. In general, the peak broadening of the XRD line width could be caused by a variety of factors, including crystallite size, non-uniform strain, and stacking defects. As a result, the distinguishing crystallization process in the structure is thought to be responsible for the increase in XRD line width. Previous studies in the literature mentioned similar results (Kadhim et al. 2015;Al-Hardan et al. 2010). Figure 5 showed the SEM images of prepared films that depict the divergences in the surface morphologies of polyimide/mesoporous silica hybrid nanocomposites films including different SiO 2 nanoparticle ratios. It could be observed that for 6 wt.% of silica ratios, a small amount of mesoporous SiO 2 nanoparticles were sprinkled inconsistently in the polyimide matrix. However, there was some interlinkage between mesoporous SiO 2 nanoparticles in interrupted regions. On the other hand, with the further increasing addition of mesoporous SiO 2 nanoparticles with ratios of 6, 8, 10, and 12 wt.%, it could be seen an intensive distribution of mesoporous SiO 2 nanoparticles over the polyimide matrix, and these distributions were homogeneity spread to most regions. In addition, the mesoporous SiO 2 nanoparticles became more in contact with each other, which resulted in more efficient optical and electrical properties and decreases in the dielectric constant of the hybrid nanocomposite films. Meanwhile, it could be observed that as the silica content in the polyimide matrix increased, slight agglomeration among the nanoparticles occurred, while the overall dispersion of SiO 2 nanoparticles in the polyimide matrix was still better. Moreover, in the SEM image of 12 wt.% films, the silica nanoparticles are entirely aggregate, leading to phase separation between the nanoparticles and the polyimide matrix, resulting in the generation of pores in the film and, subsequently, producing a deterioration in the mechanical properties of the film (Huang et al. 2022). In addition, the corresponding EDS spectrum of 12 wt.% ratios confirmed the chemical composition of the prepared films, where the spectrum demonstrated the major presence of Si and O elements in the prepared film.

Raman analysis
The Raman spectra of polyimide and hybrid composite films are displayed in Fig. 6a and the related enlarged graph (Fig. 6b). The characteristic absorption bands and the corresponding chemical bonds are present in Table 3. Both hybrid samples and polyimide films exhibit the distinctive imide group peaks at 1780 and 1711 cm −1 (asymmetric and symmetric C=O stretching vibrations, imide I), 1460 cm −1 (aromatic C=C stretch), 1368 cm −1 (C-N-C axial vibration, imide II), 1092, and 730 cm −1 (C-N-C transverse vibration, imide III). The peak at 1711 cm −1 is attributed to the imide group, and the peak at 1780 cm −1 represents the cyclic five-membered ring that confirmed the imide formation. While the bands at 1368, 1092, and 730 cm −1 are assigned to the C-N-C bond and the imide ring deformation. The bands at 1502 and 830 cm −1 represented C 6 H 4 and Si-O-Si, respectively. The band at 1173 cm −1 refers to C 6 H 4 or C 6 H 2 . The peak at 677 cm −1 originated from C-C=O in-plane swing vibration. Raman spectra confirmed the succeeded imidization of polyimide films via disappearing the band at 1650 cm −1 and the expansion of the imide group at 1711 cm −1 . This observation showed a good agreement with the earlier studies (Ma et al. 2016;Gao and Holmes 2004). The sharp band near 1080 cm −1 and the appearance of peaks at 633, 541, 500, and 475 cm −1 induced by the existence of the Si-O-Si bond indicate that the mesoporous silica nanoparticles have been successfully incorporated into the hybrid composites films. As can be observed in the enlarged spectra, these peaks became much stronger and increased with increasing ratios of the mesoporous silica. While the peaks in the range of 50-200 cm −1 reflect the absence of the imide II and aromatic C=C stretch bands suggesting the cleavage of C-N and C=C bonds and the polyimide molecules were disintegrated in friction. The variation in relative intensity of these bands reflects their re-orientation concerning the phenyl ring in the imide structure, which is related to polyimide friction and wear. These observations showed a good agreement with the earlier studies (Martínez-Gómez et al. 2015;Yang et al. 2013).

Polyimide/mesoporous silica films surface morphology
The AFM was used to investigate the effects of mesoporous silica nanoparticles incorporation on polyimide surface morphology. In comparison to pure polyimide, the typical peakand-valley structure of polyimide morphology was smoothened by the incorporation of mesoporous silica nanoparticles, as shown in Fig. 7. Mesoporous silica nanoparticles were  Cyclic five-membered ring also observed on the surface of polyimide films. The AFM images show that the fluorinated silica nanoparticles were thoroughly embedded in the polyimide layers. Moreover, the surface morphology of the polyimide film with 0 wt.% of SiO 2 NPs has the same homogeneity with flakes-like bumps. While for the hybrid polyimide nanocomposites with 6, 8, 10, and 12% wt.% SiO 2 NPs, the surface morphology of prepared films began to vary. Where the films seemed smoother with little gulfs and meander on the surface. In addition, gradually increasing of ratios silica nanoparticles helped fill the gaps and gave a more crowded surface with regular stacking. Where the embedded silica nanoparticles appeared clearly on the surface of films at the ratios of 10 and 12 wt.%. Generally, the AFM results demonstrated that the surface of polyimide films has improved with the addition of silica nanoparticles, which can be due to charge accumulation, as well as the surface partial charge. The 3D AFM images of the prepared films are presented in Fig. 8. The images further showed the homogenous distribution of silica nanoparticles throughout the polyimide films and could easily observe the little agglomeration of silica nanoparticles with increasing silica ratios.
The surface roughness of polyimide/mesoporous silica hybrid nanocomposites films was also assessed (Fig. 9). It was found that the total height roughness (Rt) of polyimide film with 0.12% (w/v) silica nanoparticles decreased from 86.5 to 2.14 nm. Accordingly, could conclude that the addition of silica nanoparticles smoothed the peak-and-valley structure of the surface morphology, and subsequently, the surface area dropped as the roughness decreased.
These results are well-matched with the previous study by Chang and Chen (2002). Where they reported that for the SP system, the mean square roughness ranged from 0.26 to 0.34 nm, while for the SF hybrid thin films, it was between 0.28 and 0.30 nm. The mean square roughness of these systems is less than that of the model polyimide thin films (0.63 Fig. 7 AFM images of the prepared polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles for PMDA-ODA and 0.41 for 6FDA-ODA), which confirms the excellent planarity of the prepared hybrid thin films. Consequently, the produced polyimide-silica hybrid thin films are expected to produce good optical waveguides because low roughness reduces the surface scattering loss at the waveguide surface. Figure 10a shows the absorbance of polyimide/mesoporous silica hybrid nanocomposites films as a function of the wavelength (λ). It is worth noting that as the silica ratio rises, the absorbance rises because of the increased number of light-absorbing molecules. A wide absorption peak may see in the wavelength range of 430-450 nm. The surface plasmon resonance (SPR) of silica nanoparticles causes the oscillation of free conduction electrons to increase under the influence of the electromagnetic field, resulting in this broad peak. Besides, Fig. 10a demonstrates how the absorption edge in the visible region shifts towards longer wavelengths (red shift) as silica nanoparticles are added to thin films. Where the shift in absorption edge was increased from (λ ≈ 636 nm) to (λ ≈ 744 nm) for 0 wt.% (SiO 2 NPs) and 10 wt.% (SiO 2 NPs), respectively. This could be attributed to several parameters including the increase in vacancies, an increase in disorder, an increase in grain size and atom agglomerations, and the rearrangement of film constituents. Furthermore, the absorption coefficient should be studied to investigate the occurrence of any alterations in the band structure. The absorption coefficient (α) expresses the quantified absorption of light by the optical medium. This is defined as the fraction of energy absorbed (1) α (λ) = (2.303∕d) * A Fig. 9 Roughness profiles of the prepared polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles where (A) is absorbance and (d) is the thickness of thin films. The absorption coefficient (α (λ) ) of produced films with different SiO 2 nanoparticle ratios (0, 6, 8, 10, 12 wt.%) as a function of photon energy (hυ) is shown in Fig. 10b. It could observe that the increasing addition of silica nanoparticle ratios shifted the absorption edge of polyimide/mesoporous silica hybrid nanocomposites films to lower photon energy. This shift in photon energy from 1.76 to 1.22 eV suggests the shrinking of optical band gaps of the nanocomposite films. Likewise, in a previous study, Alsaad et al. (2020) reported that by the addition of 2%, 4%, and 8% SiO 2 NPs concentrations to the polymer solution, α increase to 0.00032, 0.00033, and 0.000355, respectively. Interestingly, α increase considerably to 0.00038, as SiO 2 NPs concentration increases to 16%. It retains almost constant value in the visible spectrum region as the content of SiO 2 NPs increase constantly. As a result, (PMMA-PVA)/SiO 2 NPs nanocomposite thin films may act as light filters for the entire range of visible regions with constant partial absorption depending on the concentration of SiO 2 NPs.

UV-Vis absorption
However, the produced nanocomposite films had a maximum absorption coefficient in the UV range with photonic energy of 3.1 eV. The strong ability to absorb all UV subtypes (UVA, UVB, and UVC) was confirmed by the sharp absorption coefficient for polyimide/ mesoporous silica hybrid nanocomposites films at photon energy 3.1 eV, which opens the door for using our prepared hybrid nanocomposites films in many optoelectronic applications such as UV shielding films. Whereas Knežević et al. (2018) studied the ability of mesoporous silica and organosilica nanomaterials as UV-blocking materials and they concluded that the MSN and PMO materials concerning their potential for skin protection from the UVA/UVB sun irradiation exhibited to be promising sunscreen agents.

Optical energy band gap
Tauc's relation was used to calculate the direct optical band gap (Mir et al. 2014): . 10 a Absorbance spectra as a function of the wavelength (λ), and b Absorption coefficients (α) as a function of photon energy (hυ) for polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles where A is a constant, E g is the material band gap, and n is the transition type's exponent. Direct transitions are allowed; n = 1/2, indirect transitions are allowed; n = 2, direct transitions are forbidden; n = 3/2, and indirect transitions are forbidden; n = 3. Figure 11 depicted the relationship between (αhv) 2 and (hv) for all prepared hybrid nanocomposites films and Table 4 shows the E g values that were calculated.
The data clearly shows that raising the silica percentage inside the hybrid nanocomposites films lowers the E g values. The energy states between the valence and conduction bands altered due to changing the silica ratios. Additionally, increasing the silica ratios aids in the integration of mesoporous silica nanoparticles into the polymer matrix, resulting in the development of localized electronic states in the optical band gap, which acts as trapping centers.

Optical transmittance and reflectance
Figures 12 a, b demonstrate the optical transmittance T percent and reflectance R percent of the developed hybrid nanocomposites films . As shown in Fig. 12a, the optical clarity of polyimide films is affected by silica nanofillers. Subsequently, increasing the ratio of mesoporous silica nanoparticles leads to a decrease in the transmittance of polyimide films. This is because Fig. 11 Plots of (αhν) 2 versus (hν) for the polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles silica nanofillers increase the density of localized states, which reduces transmittance. While the reflectance of the developed hybrid nanocomposites films increases as the wavelength range increases, as shown in Fig. 12b.

Refractive indices and extinction coefficient
The refractive index (n) and the extinction coefficient are the most essential factors in optoelectronics (k). Figures 13 and 14 show the fluctuations of n and k for polyimide/ mesoporous silica hybrid nanocomposites films as a function of photon energy (a, b). Based on the following relationship, the refractive index (n) could be calculated from the reflectance (R) and absorption coefficient (Hassanien and Akl 2018;Mistrik et al. 2017): The refractive index of all samples increases with photon energy, as shown in Fig. 13a. Furthermore, as the silica ratio increases, the refractive index increases. This is due to a decrease in the polymer matrix's interatomic spacing, which leads to an increase in the density of hybrid nanocomposite film as the silica ratio increases. In addition, the formation of new energy states is evidenced by the increase in refractive index, and consequently, a decrease in the energy bandgap of polyimide blends is observed with the addition of various silica nanoparticle ratios. The following equation could be used to compute the extinction coefficient (k), which relates to the amount of energy lost inside the material (Nofal et al. 2021): The value of k is decreased by photon energy, and the k value is increased by raising the silica ratio, as shown in Fig. 13b. This is owing to an increase in the density of the hybrid nanocomposite film due to higher silica ratios, which enhances the absorption coefficient.
The capacity of the generated hybrid nanocomposite films for UV shielding applications is confirmed by raising k values in the UV range, as their transparency in the UV range is lowered and the absorption coefficient is increased by increasing the silica ratio.
Moreover, it could observe the appearance of two peaks at wavelengths of λ ≈ 370 nm and λ ≈ 810 nm in Figs. 10 and 12 for all prepared polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles. It is expected that these peaks are mainly designated to the polyimide blend, which was found in the polymer film in the absence of silica nanoparticles (0 wt.%), however, the addition of silica nanoparticles may be contributed to appearing of these peaks. This may be attributed to that the optical transparency and colorlessness of the polyimides are influenced by intramolecular conjugation and intermolecular charge transfer (CT) complex formation. It is expected that the incorporation of the aliphatic unit in the polyimide backbone results in reduced conjugation and CT complex formation (Yu et al. 2015). Thus, it was expected that the iso-propylidene group and phthalic ether groups present in dianhydride and diamine moieties were effective in decreasing the charge-transfer complex between polymer backbone chains through steric hindrance leading to an increase in the intermolecular distance and thus decreased the interaction between the polyimide chains resulting in a fluctuated transparency (Dhakshnamoorthy et al. 2012). Consequently, the two absorption peaks may be correlated with the electronic transition occurring in the imide group (NC = O). It is well known that the compounds with oxygen and nitrogen, containing non-bonding electrons can show these types of characteristic absorptions (Virk et al. 2001).
On the other hand, the increasing feed ratio of SiO 2 NPs resulted in films with higher transparency. This is probably because the bulky SiO 2 NPs are helpful for the disruption of charge transfer between polyimide chains, which is assumed responsible for the usually deep color of polyimide film. Where the polyimide film has an intrinsically yellowish coloration problem related to the diimide fragment conjugation as a liquid crystal alignment layer (Ju et al. 2017). Besides, the silane group of SiO 2 NPs cage is strongly electron-withdrawing because the silanes group easily forms covalent bonds making SiO 2 NPs weaken the electron-donating ability of the diamines and suppressing the intermolecular chargetransfer complexing (CTC) between alternating electron donor (diamine residue) and electron acceptor (dianhydride residue) moieties (Deng et al. 2018).
Another reason is due to the strong intermolecular interactions and charge transfer complex (CTC) of aromatic polyimides, aromatic polyimides exhibited strong absorption between the UV and visible area (Deng et al. 2018). However, the introduction of SiO 2 (4) k = 4 NPs increased the steric hindrance, thereby reducing the formation of transfer complexes and disrupting the structural integrity of the chain. Consequently, the introduction of SiO 2 NPs improved the transparency of the polyimide. Where the electron-withdrawing effect of SiO 2 NPs slightly influences the charge transfer of imide groups.

Optical dielectric constant
Because the optical dielectric constant is so crucial in real-world applications like optical device design and optical communications. Therefore, based on the following relationships, we will use the acquired values of n and k to research and analyze the complex dielectric constant (ε* = ε r + ε i ) for all created hybrid nanocomposites films (Ren et al. 2000): where ε r and ε i represented the real and imaginary dielectric constants, respectively. Figures 14a, b illustrate the ε r and ε i as a function of photon energy.
As demonstrated in the picture, raising the silica ratio raises the r and I values. These findings show that raising the silica ratio increases the energy density of stats, which leads to an increase in the polarization process and a greater dielectric constant. The direct relationship between the I and k spectra is revealed by their form constancy. As can be observed in the image, I spectra in the UV region are moved to lower photon energy, indicating that increasing charge carrier concentration reduces optical relaxation time.
Accordingly, the longer absorption bands for the polyimide copolymer systems could attribute to the intramolecular charge transfer between donors and acceptor moieties in the polymer network. Therefore, the polyimide copolymer of pyromellitic dianhydride absorbs and emits light with different energies exhibiting multiple absorption bands. These multi bands absorption and emission peaks may be due to the presence of many aryl substituents (Hariharan et al. 2018). In general, pyromellitic dianhydride-co-4, 4´-oxydianiline, Fig. 14 a Real dielectric constants and b Imaginary dielectric constants of polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles and N-methyl-2-pyrrolidone-based systems show a strong multi-absorption band due to conjugation of poly aryl molecule π-π* transition, thus the corresponding polyimide also possess a strong multi absorption and a red-shift due to the influence of aryl-substituted. Nevertheless, these polymers have a small absorption n-π* transition for the carbonyl (C=O) and imine (N=C) groups. Consequently, this may explain the appearance of signals at 1.5 eV and 3.2 eV in the spectrums of Figs. 13, 14, and 17.

Optical dispersion constants
The refractive index dispersion is one of the most significant parameters to consider when designing optical devices and optical communications applications. As a result, in this section, we will utilize the Wemple-DiDomenico (W-D), single oscillator model, to find the dispersion parameters according to the following relationship (Yakuphanoglu et al. 2004): where E 0 is the oscillator energy and E d is the dispersion energy. The E o and E d can be calculated from the slope and intercept of the relationship between (n 2 −1) −1 and (hυ) 2 , as illustrated in Fig. 15a. Table 4 shows that E o has the same dependence as E g , which can be determined using Tauc's relation. As indicated in the table, raising the gelatin ratio increases E o , whereas increasing the silica ratio decreases it. This could be because increasing γ-dose causes a rise in the HOMO-LUMO gap's localized electronic states, which enhances the low energy transition and lowers the value of E o .
The relation between the lattice dielectric constant ε L and the refractive index n is given by Gadallah and El-Nahass (2013): The carrier concentration to effective mass ratio is N/m*, c is the speed of light, and e is the electron charge. The value of ε L is calculated by extrapolating n 2 −λ 2 plots to λ 2 = 0 and N/m* from the slope (Fig. 15b). Table 4 shows that increasing the silica ratio increases ε L . 15 a Plots of (n 2 −1) −1 versus (hυ) 2 and b n 2 versus λ 2 for polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles and N/m*. This means that as the silica ratio is increased, the number of free charge carriers in the polyimide/mesoporous silica hybrid nanocomposites films increases.

Optical conductivity
Using the provided values of α and n, the optical conductivity of polyimide/mesoporous silica hybrid nanocomposites films can be calculated (Al-Ghamdi et al. 2021): where c is the light velocity in space. Figure 16 shows the optical conductivity as a function of photon energy. The figure shows that as the photon energy is raised, σ opt increases for all samples due to increased electron excitation. It's also worth noting that increasing the γ-dose raises the optical conductivity. Thus, increasing the number of free charge carriers in the generated polyimide/ mesoporous silica hybrid nanocomposites films by increasing mesoporous silica nanoparticles causes an increase in σ opt with increasing silica ratio.
Quantitative optical parameter measurements for polyimide/mesoporous silica hybrid nanocomposite films could be useful in the future.

Volume and surface energy loss function
The real and imaginary components 1 and 2 of the complex dielectric constant are related to the volume energy loss function (VELF) and the surface energy loss function (SELF). The SELF and VELF dropped as the incident photon energy increased, as shown in Fig. 17a, b. Furthermore, at any incident photon energies, the volume energy loss is greater than the surface energy loss, showing that the excitation of plasma oscillation in the bulk of polyimide nanocomposite films is greater than that on its surface. The absorption coefficient, extinction coefficient, optical reflectance, dielectric constant, SELF, VELF, and refractive index of the polyimide/mesoporous silica hybrid nanocomposite films indicate that they are appropriate for the development of various photonic devices.

Surface energy properties
Due to their benefits in various applications, industrial engineering materials attract a lot of scientific and industrial interest. For optics, tribology, and corrosion/wear applications, high compactness and low porosity are the most important microstructure features. The interaction of the employed materials with water is thought to be the most important cause of the mechanical and electrical properties of industrial engineering materials becoming compromised. Because of its fundamental importance in various domains and practical value in biological and high-tech applications such as coatings, cleaning, drying, and adhesion, the wetting phenomena of a water droplet on a rough surface has been intensively investigated for a long time. At the macroscopic scale, wetting phenomena are well recognized, but they can also occur at the nanoscale. The use of oblique angle deposition (OAD) thin films incorporated into ultrasonic devices or complicated photonic structures generated by stacking thin film layers with varied refractive indices have also aided detection in liquid media. The surface tensions between the three phases (solid, liquid, and gas) could be explained in the case of three phases (solid, liquid, and gas) (see Fig. 18): The angle at which the liquid-vapor interface meets the solid-liquid interface is known as the contact angle (θ C ). A drop will assume a wide range of contact angles, from the so-called advancing contact angle (θ A ) to the so-called receding contact angle (θ R ), even on a completely smooth surface. The equilibrium contact angle (θ C ) can be computed using the following formula (Thabet and  The pH value affects the contact angle of polyimide/mesoporous silica hybrid nanocomposites films, as shown in Fig. 19a. The concentration of the utilized nanofillers also affects the contact angle of polyimide/mesoporous silica hybrid nanocomposite films. When silica nanoparticles are inserted into the polyimide matrix, the surface changes from hydrophobic to hydrophilic for all pH values. Figure 19b shows how the concentrations of nanofillers affect the wetting energy of polyimide/mesoporous silica hybrid nanocomposites films. The wettability of polyimide/mesoporous silica hybrid nanocomposite films is improved by increasing the ratio of silica nanofillers for all pH values. The acquired results are because including silica nanofillers into the polyimide matrix causes the formation of many hydrophilic species, which improves the wettability of polyimide nanocomposites films. Furthermore, increasing pH values improve the wettability of polyimide/mesoporous silica hybrid nanocomposites films by forming more hydrogen bonds between the used water and the polyimide/mesoporous silica hybrid nanocomposites films, resulting in increased dipole/dipole interactions and thus improved wettability. Figures 19 and 20 show the relationship between the spreading coefficient and work of adhesion for polyimide/mesoporous silica hybrid nanocomposites films (c, d). The silica nanofillers improved the spreading coefficient and adhesion work of polyimide/ mesoporous silica hybrid nanocomposites films, as indicated in the figures. The key causes for these outcomes were surface roughness and molecular interactions.
Based on the above-mentioned results, it is possible to conclude that using nanotechnology to improve the surface energy attributes for polyimide materials is a viable option. The contact angles, energy, and attraction forces of nanocomposite surfaces were all controlled by the concentrations of mesoporous silica nanoparticles. As a result, the polyimide/mesoporous silica hybrid nanocomposite films could be beneficial

Fig. 18
Forces acting along the boundary line of a liquid droplet for electrical plastic gloves, safety shoes, water pipelines, underground electrical cable sheathing, cable ducts, and other electrical components.

Conclusion
Optoelectronic properties of a set of hybrid nanocomposite films of polyimide polymer (matrix) and mesoporous silica nanoparticles (filler) that were prepared via a green sol-gel process were investigated. The films were fabricated with different ratios of mesoporous silica nanoparticle content concentrations; (0, 6, 8, 10, and 12%). Several characterization instruments were used to inspect the crystalline, morphological, spectroscopic, and surface properties of the prepared films. It was found that the prepared films exhibited photonic energy ≥ 3.1 eV in the UV region. Moreover, many optical parameters have been affected by the ratio of included mesoporous silica nanoparticles, where the band gap (E g ), transmittance, and transparency values of prepared films were decreased with increases in nanosilica ratios. On contrary, the increase of nano-silica content enhanced the refractive index, extinction coefficient dielectric, imaginary dielectric constants values, and free charge carrier concentrations for the prepared films, which subsequently resulted in improvements in their optical conductivity. Moreover, the different content of nano-silica has modified the (a) (b) (c) (d) Fig. 19 Dependence of a contact angle, b wetting energy, c spreading coefficient, and d work of adhesion on silica ratio of polyimide/mesoporous silica hybrid nanocomposites films with 0, 6, 8, 10, and 12 wt.% ratios of silica nanoparticles surface structure of the prepared polyimide/mesoporous silica hybrid nanocomposite films giving the prepared films many different properties. Where the prepared films became more hydrophilic surface. Accordingly, the wettability, spreading coefficient, and adhesion work at a wide range of pH values was boosted for all the prepared polyimide/mesoporous silica hybrid nanocomposites films.