Oil/water separation and functionality of smart carbon nanotube–titania nanotube composite

Water treatment applications are in high demand recently. In this work, the titania nanotube (TNT) was successfully grown onto the outer surface of the carbon nanotubes (CNTs) via the hydrothermal method. The resultant prepared composite was doped with different ratios of nitrogen. The structural and morphological merits of the composites displayed the successful composition of the matrices, as well as the particle size of the composite within the nanoscale. The optical specifications of the composites demonstrate successful direct and indirect transitions with a high energy gap (> 3 eV). The testing of different oils in the water/oil separation exhibited a high rate of success to split oil and water (> 95%). In this regard, CNT-TNT 1.0 sample reflects the highest efficiency. Compared to other researchers that demonstrate the highest efficiency of their proposed structure, our membrane offers a decent separation efficiency. The proposed composite might provide a feasible and cost-effective method for water/oil separation application in the nanotechnological fields.


Introduction
The utilization of carbon nano-based materials in different applications acquired great attention in the last two decades, especially those related to environmental protection [1][2][3][4]. The water contaminated with oil not only affects all life being organisms, but also decelerates the industrial revolutions. The discharged water coming out from different factories contains multiple contaminants like dyes and oil [5]. The great challenges are not only separating oil from water but also removing other contaminants. The multifunction materials capable of performing multi-tasks are favored. The scientific society proposed different advanced techniques to clean up oil spills from water, Abstract Water treatment applications are in high demand recently. In this work, the titania nanotube (TNT) was successfully grown onto the outer surface of the carbon nanotubes (CNTs) via the hydrothermal method. The resultant prepared composite was doped with different ratios of nitrogen. The structural and morphological merits of the composites displayed the successful composition of the matrices, as well as the particle size of the composite within the nanoscale. The optical specifications of the composites demonstrate successful direct and indirect transitions with a high energy gap (> 3 eV). The testing of different Vol:. (1234567890) such as coagulation and fluctuation, chemical oxidation, adsorption, biological treatment, photocatalytic treatment, and membrane technology [6][7][8]. Among all of the separation techniques, membrane technology is favored. The membranes are durable and costeffective, consume less energy, are single-stage, have corrosive resistance, and are non-toxic, environmentally friendly, and efficient [9].
Due to their outstanding properties, sodium titanate nanotubes (TNTs) were subjected to massive research in past decades [10]. The application areas of TNT comprise energy storage [11][12][13], photocatalysis [14], sensors [14], dye removal [15][16][17], and fire protection [18]. Sodium titanate has a general Na 2 Ti n O 2n+1 (n = 3-8) formula, with numerous crystalline phases with different physicochemical properties. Specifically, Na 2 Ti 3 O 7 and Na 2 Ti 6 O 13 have been comprehensively studied because of their exceptional stability and outstanding ionic conductivity [10]. Several approaches like sol-gel, solidstate, and hydrothermal have been reported for TNT preparation [19]. The hydrothermal method is a single-step process that produces many TNTs with different morphologies [20]. Carbon nanotubes (CNTs) are promising 1D materials with splendid functionalities used in different fields [21][22][23]. It was applied as a sensitive material to various physical, chemical, and biological stimuli; however, some limitations related to its intrinsic characteristics hinder its practical applications [24][25][26][27][28][29]. It was reported that the incorporation of CNTs with some functional materials (e.g., metal oxides) resulted in enhancing the functionality of the resultant composite [30,31]. The incorporation of sodium titanate and CNTs was reported to have untraditional merits compared to their separate components. Payan et al., successfully synthesized TNT/SWCNT via a two-step hydrothermal route. The proposed composite was tested against 4-CP degradation under UV and solar irradiation [32]. Santos et al., have prepared TNT/MWCNTs through the hydrothermal method. They concluded that the modification of TNT with MWCNTs led to a remarkable enhancement in the oxidization of methyl yellow (MY) [33]. Mohamed et al., prepared MWCNTs/TNT nanocomposites loaded with platinum nanoparticles as methylene blue (MB) dye removal. Their research work demonstrated that the combination between TNT and MWCNT resulted in a superior photocatalytic activity in the degradation of MB [34]. Jiang et al., synthesized CNT/TNT composite to be applied as photocatalyst material for methyl orange (MO) dye. According to their results, the degradation rate reached 94% after irradiation for 40 min. Hongchao Li et al., successfully prepared carbon membranes by the mixing polyacrylonitrile and phenolic resin via the pyrolysis process. They approached an optimal rejection for oil with 94.2% [35]. Carbon membrane coated with polyethylene glutaraldehyde was prepared. The impacts of coating sorts and solutions used as well as the concentration for the structure and the separation efficiency for oily wastewater were explored while ~ 94% separation was affirmed in another report [36]. Herein, through this work, titanium dioxide nanoparticles (TiO 2 ) were grown on the external surface of CNTs, and then transformed into TNT via a hydrothermal route. The earlier obtained composite was doped with nitrogen using a solid-state reaction followed by calcination. The main target of this study is to acquire a smart material having oil/water separation properties. The prepared composites were studied using different techniques including XRD, FTIR, UV-Vis, SEM, and HR-TEM, to assess their properties, and then tested for the application mentioned earlier. The microstructural-related parameters such as microstrain, dislocation density, and crystallinity degree were calculated from the XRD diffractograms. The conducted optical study reveals an interaction between the doped TNT and CNT. This interaction alters the energy level of the conduction band. The studied membrane was prepared using a simple vacuum filtration method. The efficiency of the synthesized membranes was investigated initially against n-hexane. The obtained results confirmed the sample CNTs-TNT1.0 has the highest separation efficiency. The latter was tested versus different oils.

Synthesis of CNT-TiO 2 composite
The first step of grafting TiO 2 over CNTs is to modify their outer surface to get a functional group. Initially, 0.5 g of MWCNTs was treated with a mixture of HNO 3 and H 2 SO 4 (3:1, V:V) for 4 h to get a function group and eliminate the undesired impurities and catalyst particles. The MWCNTs were washed repeatedly with deionized water, followed by ethanol, and then deionized water, and finally dried at 60 °C until complete evaporation of the water.
The CNT-TiO 2 composite was synthesized as per procedures described in the literature [39]. Briefly, 5 mL of TTIP was dissolved in 30 mL of absolute ethanol to form a clear solution, followed by the dispersion of 30 mg of MWCNTs in the solution using an ultrasonic homogenizer. Another solution comprising 2 mL acetic acid and 30 mL deionized water was dropped slowly into the above solution under continuous stirring for 3 h. The resultant solution was allowed to rest overnight. The precipitates were separated from the liquor solution by centrifugation, and then washed and dried. The bright gray powder was calcined at 350 °C for 2 h.

Synthesis of Na 2 Ti 3 O 7 /MWCNT composite
The Na 2 Ti 3 O 7 /MWCNT composite was synthesized by hydrothermal route. Typically, 0.3 g of CNTs-TiO 2 was stirred in 30 mL of 10 M NaOH solution for 10 min. The slurry was poured into a 50-mL Teflon-lined stainless-steel autoclave and maintained at 180 °C for 24 h. The autoclave was cooled naturally; then, the precipitates were recovered by centrifugation. The precipitates were washed several times with deionized water followed by washing with 0.1 M HCl, and again with deionized water until they reached neutralization and finally dried.

Synthesis of nitrogen-doped Na 2 Ti 3 O 7 /MWCNT composite
The nitrogen-doped Na 2 Ti 3 O 7 /MWCNTs were executed by a simple solid-state reaction using urea as a nitrogen source. At the outset, about 3 mL of ethanol was added to a mixture of 0.3 g of Na 2 Ti 3 O 7 / MWCNT composite and different rations of urea, as represented in Table 1. Each slurry was grounded manually in an agate mortar for 10 min, and then heat-treated at 350 °C for 3 h. Finally, the obtained N-doped Na 2 Ti 3 O 7 /MWCNTs were labeled as CNT-TNT0.5, CNT-TNT1.0, and CNT-TNT1.5. Figure 1 represents a scheme of the preparation procedure.

Membrane preparation
The membranes were constructed by using a simple vacuum filtration apparatus. A certain amount (10 mg) of each composite was ultrasonically dispersed in 50 mL of deionized water for 30 min and stirred for an additional 1 h to get a homogeneous solution. The obtained composite was filtered through a nitrocellulose filter membrane for 10 min. The achieved membrane was dried at 50 °C for 24 h for further testing and characterization. The membrane preparation process is presented in Fig

Experimental setup
Oil separation was carried out with a designed setup in Figure 2b; the oil/water mixture (1: 1.6weight) was flowing past the composite membrane matrix due to suction towards gravity force and the separated liquid was eventually collected in a conical flask. Water and different types of oil (including n-hexane, vacuum oil pump, engine oil, petroleum ether, and toluene) were colored with methylene blue. The separation time for 200 mL mixture solution was about 60 s by a vacuum pressure of 15 Micron Hgs.

Characterization techniques
The phase composition was identified by XRD using Malvern Panalytical Empyrean 3 with Cu Kα radiation at a wavelength of 1.54 Å. The FTIR spectra were acquired using an FTIR spectrometer (Vertex 70, Bruker); the spectra were collected in a spectral range of 4000-400 cm −1 with a spectral resolution of 5 cm −1 . The microstructure was verified by scanning electron microscopy (SEM), Quattro S, Thermo Scientific. More details regarding the microstructure were verified by the high-resolution transmission electron microscope (HR-TEM) model JEOL JEM2100 electron microscope. The optical properties were performed at room temperature using a spectrophotometer (UV-Vis-NIR, JASCO V-570, Japan) equipped with an integrating sphere attachment (JASCO ISV) in the 200-2000 nm wavelength.
Oil/water separation experiment n-Hexane was used as an oil model; then, different types of oils were utilized and tested. The water/oil combination was executed by mixing 15 g of n-hexane and 25 g of water. The prepared membrane was wetted before starting the separation experiment. The separation efficiency was estimated using the following equation: where M r and M i are the mass of oil before and after separation respectively.

Results and discussion
Phase assessment This section explores the structural specifications of the synthesized composites via different apparatus. A powerful and standard device is the X-ray  . 1 The schematic illustration of the synthesis process diffraction which sheds light on the internal nature of the composite, the crystallite size, the observed microstrain, the dislocation density, and other significant parameters that unveil the structure's nature. Figure 3 represents the XRD diffractograms of the CNT-TiO 2 , CNT-TNT, CNT-TNT0.5, CNT-TNT1.0, and CNT-TNT1.5 as remarked above each diffraction pattern performed within 5° to 75° at ambient conditions. CNTs have two peaks at the diffraction angles of around 25° and 42°, which are indexed to the (002) and (100) planes correspondingly, while the former is the strongest one and the latter owes much lower intensity [40]. This coincides with ICDD card no. #01-077-7164, and preceding reports [41].    Fig. 3 The propagation of the diffraction peaks with the diffraction angles in the XRD diffraction pattern for the synthesized nanocomposites k represents the sample's shape factor, λ is the wavelength for the incident ray CuK α source with the value of 0.15406 nm, ∆ remarks the full width at the median of the highest value, and θ is the angle at which the diffraction occurs. Furthermore, the value of the microstrain could be determined as follows [49][50][51]: The value of the microstrain has a meaning; a negative one remarks the presence of compressive strain in the particles [52]. Conversely, the positive value represents tensile strain [53]. The enhancement of the strain magnitudes reflects the propagation of grain walls [54]. Knowing the crystallite size, the dislocation density is estimated as follows [49,50,55]: For further analysis of the composites, the degree of crystallinity might be produced based on the area under the peaks of the plot as follows [56][57][58]: While A C is the area under crystalline peaks, A T is the elaborated area under the crystalline and noncrystalline peaks of the pattern.
Calculated parameters for these composites are tabulated in Table 1.
As can be seen from Table 1, the average particle size decreases, while the positive value of the microstrain indicates the occurrence of tensile strain [51]. The reduced crystallinity degree is due to the occurring hydrothermal treatment.

FTIR
The FTIR was used mainly to characterize the formed bonding between constituents of composite. Figure 4 displays the FTIR spectra of the as-prepared CNT-TiO 2 nanoparticles, CNT-TNT, and nitrogen-doped CNT-TNT nanocomposite with doping ratios of 0.5, 1.0, and 1.5%. All the FTIR spectra revealed distinct peaks at about 3430, 681, and 487 cm −1 which are assigned to the stretching vibration bands of O-H, Ti-O-Ti groups of the TiO 2 nanoparticles, and TNT [59,60].
Furthermore, the peak that appeared at 1623 cm −1 is characteristic of the C = O group of the acid-treated CNT. A prominent peak appears at the spectra of CNT-TNT, and nitrogen-doped CNT-TNT nanocomposite appears at 901 cm −1 ; this peak is characteristic of the Ti-O-Na bond. This confirms the formation of TNT. Also, the spectra of nitrogen-doped CNT-TNT reveal a characteristic peak at 1365 cm −1 is assigned for the N-H vibration mode. It was observed that the peak intensity increases with increasing the doping ratio of nitrogen. This peak does not appear at the spectra of CNT-TiO 2 and CNT-TNT, which confirms the successful doping of the CNT-TNT with nitrogen [61][62][63][64][65].

Morphological evaluation
The FE-SEM and HR-TEM instruments were used to investigate the morphology of the prepared materials. The general overview of the structure of the materials was examined through FE-SEM, while more detailed morphology was recognized from HR-TEM images. The FE-SEM images of CNT-TNT are illustrated in Fig. 5.
The SEM images of CNTs-TNTs exhibit a fiberlike structure that covers the outer diameter of CNTs. The images indicate that the CNTs are fully covered with TNT with noticeable agglomeration. It seems that the TNT was grown perpendicular to the outer surface of CNTs. More details regarding the microstructure were deduced from the HR-TEM as presented in Fig. 6. The HR-TEM images of CNTs-TiO 2 indicated in Fig. 6a reveal that the CNTs have a tubular structure with a hollow cavity. The spherical TiO 2 nanoparticles are attached externally to the CNTs with good distribution and less agglomeration. However, some TiO 2 nanoparticles were grown out of the CNT surface, as indicated in Fig. 6b. The size of the spherical TiO 2 nanoparticles was measured to be around 6 nm. The measured particle size from XRD was found to be in good agreement as obtained from HR-TEM.
After hydrothermal treatment, the TiO 2 spherical particles were turned into nanotubes with an external diameter of about 7-9 nm as shown in Fig. 6c. The outer diameter of TNT is the same as the diameter of spherical TiO 2 nanoparticles, indicating the transformation of TiO 2 to TNT after hydrothermal treatment. The TNT seems to be agglomerated and covers the external surface of the CNTs. The TNT seems to be grown perpendicular to the outer surface of CNTs.

Optical studies
The electronic configuration of Ti 3 is 3d 1 4s 2 . It has five-fold degeneracy, and its ground state term symbol is 2D. The five-fold degeneracy is split into 2 T 2g and 2 E g states in an octahedral crystal field. Thus, only one electron transition, 2 T 2g → 2 E g , is expected in an octahedral crystal field. The separation between these energies is 10D q , which is crystal field energy. Normally, the ground 2T 2g state is split due to the Jahn-Teller effect, and hence, lowering of symmetry is expected for Ti(III) ion. This state splits into 2 B 2g and 2 E g states in tetragonal symmetry, and the exciting term 2 E g also splits into 2 B 1g and 2 A 1g levels. Thus, three bands are expected for tetragonal (C 4v ) symmetry. The energy level diagram in a tetragonal environment is shown in Fig. 7.
From the observed band positions, the crystal field parameter in the octahedral field is Dq (1205 cm −1 ), and tetragonal field parameters are Ds (1867 cm −1 ) and Dt (268 cm −1 ). The optical properties were investigated using a UV-Vis-NIR reflectance spectrophotometer with an integrating sphere attachment in the 200-2000 nm wavelength range. Figure 8 shows the absorbance and reflectance of TiO 2 , TiO 2 -CNT, and N-doped TiO 2 -CNT nanocomposite.
The diffuse reflectance spectrum of TiO 2 , TiO 2 / CNT, and N-doped TiO 2 -CNT nanocomposite is reported in Fig. 8a. A relatively moderated reflectivity characterized the sample since the reflectance was ~ 50% for wavelengths above 400 nm, and at 800 nm it was about ~ 40%. Figure 8b also reports the absorbance spectrum. As clearly visible, the spectrum unveils absorbance values of about 0.3-0.6 for wavelengths above 400 nm.
However, the total absorption spectra will depend on the phase of crystal and microstructure shape morphology and the distribution of holes among available sites at a given time after the photogeneration. Figure 8 reveals the positions of the bands on the wavelength scale (nm) rather than their relative intensities, and the bands' maxima are aligned. Ti(III) ion in anatase phase is characterized by three broad bands around 1440 nm (0.86 eV, 6945 cm −1 ), 830 nm (1.49 eV, 12,050 cm −1 ), and 550 nm (2.25 eV, 18,180 cm −1 ) which are due to the transitions from 2 B 2g → 2 E g , 2 B 2g → 2 B 1g , and 2 B 2g → 2 A 1g respectively. The inset in Fig. 8 illustrates two clear peaks near 216 and 263 nm related to GQDs of π → π* transition of sp 2 C hybridization of aromatic C = C bonds, which confirm the report for carbon materials such as graphene quantum dots [65,66].
The interaction between the CNT and pure and N-doped TiO 2 nanoparticles changes the energy level of the conduction band through the interaction of unpaired π electrons with the titanium atoms, causing a displacement of the conduction band edge toward the visible region, therefore a reduction in the composite band gap Fig. 6 The HR-TEM of the a CNTs-TiO 2 , b TiO 2 nanoparticles, and c CNT-TNT nanocomposite value. The band gap energies of the specimens are calculated using the Kubelka-Munk function [67,68]: F (R∞) is the so-called remission or Kubelka-Munk function. In the parabolic band structure, the band gap E g and absorption coefficient α of a direct band gap semiconductor are related through the well-known equation [69][70][71][72].
where α is the linear absorption coefficient of the material, hν is the photon energy, and A is the proportionality constant. When the material scatters in a perfectly diffuse manner (or when it is illuminated at 60 ± incidence), the K-M absorption coefficient K becomes equal to 2α (K = 2α). Considering the K-M scattering coefficient S as constant concerning wavelength, we obtain the following expression [73,74]: Therefore, obtaining plotting the [F (R∞)hν] 2 against hν, the band gap E g of a powder sample can be extracted easily. Figure 9 displays the band gap energy of CNTs and pure and N-doped TiO 2 nanoparticles after Kubelka-Munk treatment which the direct band gap energy of pure anatase structure TiO 2 nanoparticles was 3.45 eV. After the composite process, the band gap energy of the CNT-TiO 2 -doped N nanocomposite was shifted to 3.71 eV, which depended on the result of the larger crystallites into an agglomeration of the nanocomposites. However, this behavior can be attributed to the chemical bond between the CNTs and the anatase structure TiO 2 nanoparticles formed during the synthesis of the materials.

Water/oil separation evaluation
This study investigated the oil/water separation efficiency of the prepared composites using a simple vacuum filtration system. n-Hexane has been utilized as an oil model in all oil/water separation experiments. Different types of oils, including n-hexane, vacuum pump oil, engine oil, petroleum ether, and toluene, have been tested. Figure 10 represents the separation efficiency of the prepared samples using a mixture of water and n-hexane. Remarkably, all samples have an efficiency greater than 90%. The order of separation efficiency is CNTs-TNT1.0 ˃ CNTs-TNT0.5 ˃ CNTs-TiO 2 ˃ CNTs-TNT 1.5 ˃ CNTs-TNT. The CNT-TNT1.0 sample has the highest separation efficiency of 99%; the lowest separation rate was achieved by the CNT-TNT sample.
The CNT-TiO 2 sample performs better than the CNT-TNT sample. This situation was changed when titania was doped with nitrogen. This confirms that incorporating nitrogen atoms has a remarkable effect on enhancing the oil/water separation efficiency. Since sample No. 4 exhibited a remarkable separation efficiency over other prepared samples, it will be used for further separation experiments. Different oils were allowed to pass through sample No. 4 (CNTs-TNT1.0) to check the separation efficiency. The separation efficiency as a function of the oil type is represented in Fig. 10. Moreover, among all tested oils, the highest efficiency was achieved for n-hexane. Table 2 reveals close and recent structures directed towards water/oil separation and their efficiency and our structure. Comparing to the studied structure by different research groups, the proposed membrane reveals the highest efficiency.

Conclusion
The preparation of carbon nanotubes is delivered in this report where doped and undoped samples with nitrogen are acquired using a solid-state hydrothermal procedure. The obtained structural results verified the existence of the intended titania nanotubes as well as the carbon nanotubes. The morphological studies of the samples using HR-TEM and SEM support the XRD results. The effective incorporation of the starting constitutes into the composite's network is verified. The optical study further demonstrates a variation of the band gap energy due to the occurring interaction between the CNTs and TNTs with a raised band gap higher than 3 eV. Diverse oils of n-hexane, vacuum pump oil, engine oil, petroleum ether, and toluene were employed for the water/oil separation experiment. Among all the studied samples for the water/oil separation, sample 4 (CNTs-TNT1.0) achieved the highest successful separation efficiency (> 95% efficiency) compared to other composites. The proposed structure could function on industrial application for removing petroleum spill in nature.

Data availability
The presented data to regenerate these results are included in the manuscript.

Conflict of interest
The authors declare no competing interests.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.