Abstract
The results concerning the synthesis, structure and thermal properties of V2O5-MoO3-Ag2O samples in the vanadium rich region of ternary system are presented in the form of quasi-binary phase diagrams in which at constant V2O5/MoO3 molar ratios, equal 9:1, 7:3 and 1:1, the content of Ag2O was variable. A new ternary phase isostructural with NaVMoO6 has been detected in the investigated system.
Similar content being viewed by others
References
L. Ya. Margolis, Okislenie uglevodorov na geterogennikh katalizatorakh. ’Khemia’, Moscow 1977, p. 96.
A. Bielański and J. Haber, Oxygen in Catalysis, Marcel Dekker, New York 1991, p. 137.
A. Bielański, J. Poźniczek and E. Wenda, Bull. Pol. Ac. Sci. Chem., 24 (1976) 415.
A. Bielański and J. Poźniczek, React. Kinet. Catal. Lett., 33 (1987) 417.
N. Strupler and A. Morette, Compt. Rend. Chim. Miner., 260 (1965) 1971.
A. Bielański, K. Dyrek, J. Poźniczek and E. Wenda, Bull. Pol. Ac. Sci. Chem., 19 (1971) 507.
A. Bielański and M. Najbar, Appl. Cat. A: General, 157 (1997) 223.
A. Bielański and M. Najbar, Pol. J. Chem., 52 (1978) 883.
R. H. Jarman, P. G. Dickens and A. J. Jacobson, Mater. Res. Bull., 17 (1982) 325.
R. H. Jarman and A. K. Cheetham, Mater. Res. Bull., 17 (1982) 1011.
R. Kohmüller and J. P. Fourie, Bull. Soc. Chim. Fr., 11 (1968) 4379.
E. Wenda, J. Thermal Anal., 36 (1990) 1417.
E. Wenda, J. Thermal Anal., 30 (1985) 879.
A. Casalot and P. Pouchard, Bull. Soc. Chim. Fr., 10 (1967) 3817.
J. Galy, J. Darriet and D. Canalis, C. R. Acad. Sc. Paris, 264, ser. C(7) (1967) 579.
Powder Diffraction File, International Centre for Diffraction Data, File Nos.: 04-002-4831.
D. Kobertz, M. Miller, U. Niemann, L. Singheiser and K. Hilpert, Thermochim. Acta, 430 (2005) 73.
M. Kurzawa and M. Bosacka, J. Therm. Anal. Cal., 56 (1999) 211.
M. Kurzawa and G. Dźbrowska, J. Therm. Anal Cal., 56 (1999) 217.
M. Kurzawa and M. Bosacka, J. Therm. Anal. Cal., 65 (2001) 451.
J. Walczak, M. Kurzawa and E. Filipek, Thermochim. Acta, 117 (1987) 9.
J. Walczak, M. Kurzawa and P. Tabero, Thermochim. Acta, 118 (1987) 1.
J. Walczak and E. Filipek, Thermochim. Acta, 150 (1989) 125.
J. Walczak and E. Filipek, Thermochim. Acta, 161 (1990) 239.
J. Walczak and E. Filipek, Thermochim. Acta, 173 (1990) 235.
J. Walczak and E. Filipek, Thermochim. Acta, 228 (1993) 127.
J. Walczak and E. Filipek, Thermochim. Acta, 246 (1994) 65.
M. Kurzawa and G. Dźbrowska, J. Phase Equilibria, 18 (1997) 147.
M. Kurzawa and G. Dźbrowska, Solid State Ionics, 101–103 (1997) 1189.
M. Kurzawa, M. Bosacka and P. Jakus, J. Mater. Sci., 38 (2003) 3137.
M. Bosacka and M. Kurzawa, Solid State Sci., 7 (2005) 1294.
A. Blonska-Tabero and M. Kurzawa, J. Therm. Anal. Cal., 88 (2007) 33.
P. Tabero, J. Therm. Anal. Cal., 88 (2007) 37.
M. Bosacka, J. Therm. Anal. Cal., 88 (2007) 43.
A. Blonska-Tabero, J. Therm. Anal. Cal., 88 (2007) 201.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wenda, E., Bielański, A. Phase diagram of V2O5-MoO3-Ag2O system. J Therm Anal Calorim 92, 921–929 (2008). https://doi.org/10.1007/s10973-007-8339-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-007-8339-6