Recent Advances in Various Starch Formulation for Wastewater Purification via Adsorption Technique: A Review

Water purification is considered one of the most essential issues in our lives. Therefore, the contamination of water surfaces owing to the hasty upsurge in industrialization has received great global attention because of its potential danger to human health and the eco-system. Particularly, the discharge of various non-biodegradable contaminants into the water body—heavy metal ions, organic dyes, pharmaceutical antibiotics, pesticides, and oils—causes these contaminants to accumulate on the water's surface and have harmful impacts on humans and the environment. Several conventional methods can be applied to solve this problem, including chemical oxidation, precipitation, coagulation, and so on. However, they suffer from serious limitations: high cost, limited functionality, prolonged and heavy energy use, and poor separation efficiency. Conversely, the adsorption technique has recently attracted a lot of attention for wastewater treatment thanks to its remarkable benefits of being a simple, highly selective, and low-cost technique. Recently, natural polysaccharides (especially starch)-based adsorbents have received great interest in water purification owing to their outstanding properties, including being easily available, non-toxic, low-cost, biodegradable, and biocompatible. However, it possesses notable drawbacks that prevent it from being used alone as an adsorbent for wastewater treatment, including low thermal stability, slight water solubility, and rapid degradability in water. Therefore, this review highlights a comprehensive presentation about various starch modifications: starch-based grafts, hydrogels, aerogels, beads, nanofibers, and nanocomposite formulations to remove several toxic contaminants, including toxic heavy metal ions, organic dyes, pharmaceutical antibiotics, pesticides, and oils.


Introduction
Water contamination is the most serious ecological concern because of the paucity of drinking water. Water pollution has fatal impact on human health and the health of other living organisms. Water purification is considered as a crucial topic in recent years. Rapid industrialization and significant growing population results in flowing of very dangerous industrial effluents and domestic sewage into water sources. They include many toxic materials that deteriorating and poisoning the water surfaces [1][2][3][4]. In this issue, there are different pollutants present in industrial effluents such as toxic heavy metals, synthetic dyes, residual antibiotic and pesticides, and different oil pollutants which are non-biodegradable materials and not degrade easily via conventional treatment techniques. As a result, they accumulate in living cells and cause fatal diseases [5][6][7].
To date, many scientific research groups worldwide are interested in preparing efficient adsorbent based on natural biopolymer polysaccharides for wastewater treatment to overcome the current challenges. Polysaccharides are natural carbohydrates which consist of different monosaccharide units (glycans), and/or sugar derivatives (heteroglycan) bonded together via glycosidic bonds [22]. They have remarkable features such as easily available and have excellent properties such as non-toxic, biodegradable, biocompatible, and amenable to modifications [23][24][25]. Therefore, they are harmless to human and eco-system and hence, they are widely applied for different essential fields such as wastewater treatment, food, textile, cosmetic, paper, and medicine fields [22,[26][27][28][29]. Particularly, starch-based adsorbent has been attracted a lot of attention in the field of wastewater treatment from different toxic pollutant due to its excellent properties, including non-toxicity, biodegradability, and low-cost material [30]. However, unmodified starch is rarely applied directly as adsorbent for wastewater treatment because it has certain notable drawbacks, including low surface area, poor water solubility, low molecular weight, limited thermal stability, and lack of reaction function groups. Therefore, several starch modifications have been fabricated to improve its adsorption efficiency toward different pollutants via adding functional groups on starch backbone and changing its chemical surface [20].
Many recent reviews have demonstrated explored the application of modified starch for wastewater treatment. Fang et al. [20], have studied the removal of dye, heavy metals, pharmaceutics, and oil by using starch-based magnetic adsorbents. While Haq et al. [31], have presented the use of starch-based hydrogels, composites and nanoparticles for removal of dyes and heavy metals. Moreover, Gupta et al. [32], have focused on the starch modification with different techniques: oxidation, irradiation, grafting, crosslinking and esterification techniques for removal of heavy metals. On the other hand, this review article highlights a comprehensive presentation about the recent advances in the fabrication of starch modifications such as starch-based grafted copolymers, hydrogels, polymer nanocomposite, aerogels, beads, and nanofibers, to remove various toxic pollutants: toxic heavy metal ions, synthetic dyes, pharmaceutical antibiotics, pesticides, and oils. It covers several starch formulations for removal of various toxic pollutants via adsorption technique.

Starch Structure
Starch, low-cost second abundant polysaccharide, is a homopolymer of Glucopyranose units with the molecular formula (C 6 H 10 O 5 ) n . Amylose and amylopectin are two different forms of polymer chains that make up starch as shown in Fig. 1. [33]. While amylopectin is a branching polymer consisting of -1,4-glycosodic with branched chain linked by -1,6-glycosidic bonds, amylose is a straight chain -1,4-glycosidic links. Each of these polymers receives unique features as a result of this conformational change. For instance, the crystalline area of the granules is caused by the short branching of amylopectin at the-1,6-glycosidic linkages [34,35]. About 20-30% of starch is amylose and 70-80% is amylopectin in its natural state. Starch is mainly synthesized in the Fig. 1 Chemical illustration of starch structure [38]. Copyright 2021. Adapted from MDPI 1 3 chloroplast of plant leaves and/ or in the amyloplast of the storage organs of plants. It contains some lipids and phosphate groups. There are various reported botanical sources of starch such as corn starch, rice starch, potato starch and Cassava Starch [36,37].

Physicochemical Properties of Starch
Indeed, starch has many wonderful benefits, like biocompatibility, safe usage, low-cost, biodegradability, and ease of availability. Moreover, it consists of several hydroxyl groups (Fig. 1). Starch has relatively poor water solubility and a relatively lower capacity to absorb water and oil due to its polymeric and branching structure. Additionally, it has an excellent swelling power, good gelatinization powers, and a relatively high viscosity. It may also create thin films and has good pasting qualities, including consistency, smoothness, and clarity. Starch is increasingly being used to remove water and environmental pollutants such colours, heavy metals, pesticides, antibiotics, and microbes [39]. The functional qualities of starch can be modified under the influence of numerous physical and chemical conditions to boost its nutritional, biomedical, and environmental relevance. However, it has some drawbacks that make it inappropriate to be utilised as an adsorbent for wastewater treatment without modification, including limited thermal stability, being damaged by several of microbes, and rapid degradability in water. The modification of starch to create highly effective adsorbents for wastewater treatment applications has thus been the subject of investigation by a number of scientists.

Chemical Modification of Starch
Due to the presence of several hydroxyl groups on the surface of starch, it is an ionic hydrophilic linear polymer with fabulous features such as non-toxicity, biodegradability, biocompatibility, and low-cost material. Nevertheless, native starch has certain notable drawbacks, including low surface area, poor water solubility, low molecular weight, limited thermal stability, and lack of reaction function groups, which represent obstacles to apply it directly as adsorbent for wastewater treatment [20]. In this review, several starch modifications have been fabricated such as starch-based grafts, hydrogels, polymer nanocomposites, beads, aerogels, and nanofibers to overcome its limitations to enhance its adsorption ability for wastewater treatment.

Grafted Starch
Grafting is the process of covalently bonding monomers to polymeric chains, which is followed by further polymerization of those chains to create the desired product [40,41]. Increasing the nonpolar nature of starch is a frequent technique [42,43]. Grafted co-polymers and starch biopolymers have a wide range of uses, including the treatment of waste water and the delivery of drugs and genes for tissue engineering and gene therapy [32,44]. Three more techniques can be used to produce starch-grafted synthetic polymers: grafting through, grafting to, and grafting from [42,43,45,46]. Copolymerization of macromonomers occurs during the grafting process. Grafting onto involves a reaction between two distinct functional groups on independent polymeric strands. In the grafting-onto approach, the interaction between the functional groups on the polymeric chains causes the polymerization of vinyl monomers to begin. [38,41]. The grafting from method is the most popular of these three methods because it gives access to the polymeric chains' reactive groups and produces a high yield of grafted starch (Fig. 2) [38,41,42]. In the grafting through (macromonomer) method the macromonomers are oligomeric or polymeric chains bearing a polymerizable end group. Copolymerization of preformed macromonomers with another monomer yields graft copolymers. Table 1 shows the advantage and disadvantage of different techniques of the grafted methods [47,48].
For example, varied irradiation doses and dosage rates were employed to create copolymers of starch-graft-polyacrylamide (St-g-PAM) using electron beam irradiation as the free radical initiator. Using an accelerated electron beam, St-g-PAM filled with freshly manufactured silver nanoparticles was also created. The results revealed that the level of grafting substantial viscosity and thermal behaviour (thermodynamic parameters) were influenced by the irradiation dose, dose rate and presence of silver nanoparticles. The coagulation-flocculation process of the synthesized copolymers in aqueous solutions showed good efficiency to improve different water quality indicators [49]. In order to meet the need for treating coal mine wastewater, acrylamide and legume starch were combined to create a novel, very effective flocculant. According to experimental findings, the classic polyacrylamide and polyaluminum chloride does not possess the same excellent flocculation effect as the graft copolymer of acrylamide and mung bean starch. The new flocculant has a number of advantages, including being inexpensive, quick to degrade, and especially appropriate for situations with strict environmental standards. It is also likely to have a wide range of potential applications for treating coal mine wastewater [44]. For example, in order to remove Pb 2+ ions from aqueous media using a batch approach, Ekebafe et al. [50] described the synthesis of hydrolyzed cassava starch-g-poly (acrylic acid) (St-g-PAA) and starch-g-poly (acrylonitrile) (St-g-PAN) copolymers that adsorbed Pb 2+ ions in aqueous solution via chelation mechanism. The prepared adsorbents showed maximum adsorption capacity of Pb 2+ ions reached 118.61 mg/g for St-g-PAA and 115.83 mg/g for St-g-PAN at optimized conditions, contact time (18.25 h), temperature (300.3 K), pH (7.85), 20 ppm of Pb 2+ concentration, and an adsorbent dose of 0.5 g/100 ml. The adsorption experimental data fitted very well with the Elovich equation and the intraparticle kinetic models.

Starch-Based Hydrogels & Beads
Hydrogels are a type of three-dimensional polymeric structure which has a significant water imbibing capacity. Hydrogels exhibit a large scale of flexibility in terms of fast swelling capacity, modifiable surface properties such as charge, functionality, fast dispersion process, large surface area, porous structure, permeability, catalysis, fast kinetics, thermal stability, wonderful acid/base properties and hydrophilicity [51]. When compared to other adsorbents, hydrogels are preferred in adsorption applications due to their quicker kinetics and greater capacity to remove a variety of pollutants [47]. Starch's structure  [48]. Copyright 2014. Reproduced with permission from Elsevier includes several hydroxyl groups that help hydrogel networking. Starch-based hydrogels (SHs) have drawn a lot of attention since they are widely available and have numerous applications [52]. Because hydrogels made of synthetic polymers and petrochemicals are not environmentally friendly, polysaccharides like starch are used to create biodegradable hydrogels. By cross-linking, hydrolyzing, and polymerizing the material's vinyl monomers that have been aggregated with one or more functional groups, hydrogels are created. Different components can be included within the polymeric matrix to lower costs and increase adsorption effectiveness [47]. The presence of hydrophilic groups as -COOH, -SO 3 H, -OH, and -NH 2 increases the hydrophilicity of hydrogel polymer. Starch hydrogels (SHs) gained huge attention in many fields due to the presence of a large number of hydroxyl groups. SHs also are non-toxic, biocompatible, and cheap. Due to these reasons, SHs can be an alternative to synthetic [52]. Starch hydrogels for wastewater treatment are modified by incorporation of functional groups such as primary amine, hydroxyl, carboxylic or sulfonic acid that enhancing its pollutants removal capacity [53].
For instance, modification by graft copolymerization is widely studied and used synthetic methods in HGs composed of polysaccharides [54]. Recently, Farag and co-workers synthesized bifunctional HG using radiationinduced grafting method. 2-Acrylamido propanesulphonic acid and dimethylaminoethyl methacrylate was copolymerised grafted onto starch and modified using benzyl chloride. These gels exhibited excellent removal efficiency for dye (astrazon red), cobalt, and phosphate with maximum adsorption capacities (Q max ) of 600 mg/g, 426 350 mg/g, and 650 mg/g, respectively [55]. In another work, to improve the water capacity of starch hydrogel, Kirti et al. prepared a starch hydrogel with enhanced water-absorbing capabilities by glutaraldehyde crosslinking of starch with PVA and blending with 1-Butyl-3-methylimidazolium tetrafluoroborate (BMIM-BF4) to enhance the plasticity and generate porosity within the hydrogel, leading to swelling capacity up to 300% [56]. Whereas, a poly(m-aminothiophenol) (MAP)/ potato starch hydrogel for the elimination of Hg 2+ ions from wastewater was reported by Fu et al. [57]. Following inverse vulcanization, sulfur interacts with MAP/potato starch to create crosslinked cp MAP-S-PS hydrogel for removal of Hg 2+ (Fig. 3a), the adsorption mechanism of cp MAP-S-PS could be attributed to the formation of a coordinated band or complex between Hg 2+ ions and various donor atoms (S, N, and O). The obtained hydrogel displayed excellent selectivity for Hg 2+ adsorption with Q max of 436.68 mg/g at conditions of pH (4.5), temperature (328 K), and contact time (180 min). While the regeneration study showed that the adsorption efficiency decreased to 197.77 mg/g after fifth cycle as shown in Fig. 3b.
On the other hand, starch beads are 3D crosslinked hydrogel in spherical shape structure. They have been favoured for industrial fields owing to its uniform size, low friction, and low pressure drop in the columns [58]. The uses for microand nanoscale beads and spheres are numerous, but they are particularly useful in the environmental and medical fields. As an illustration, nanobeads and spheres frequently have a high mechanical stability, a low weight, and a large specific surface area [59]. Most recently, amidoximated starch hydrogel beads were prepared by Diana et al. [60] with ionotropic gelation method in the presence of cationic chitosan ( Fig. 4a  and b). Batch experiments were used to test the hydrogel beads' capacity for solubilizing heavy metals such as Ni 2+ , and Zn 2+ and two organic dyes including direct blue 15 and congo red in simulated polluted water in relation to the characteristics of the beads. Figure 4c showed optical image of the prepared beads, and Fig. 4d exhibited spherical shape for modified starch beads.

Starch-Based Polymer Nanocomposites
It has been noted that polymer nanocomposites with inorganic reinforced fillers of nanoscale size are efficient reinforcing agents that considerably enhance the physical and chemical properties of the matrix [61]. Because of the reduction in the total free energy of mixing, nanofillers are known to have good compatibilization and miscibility with various polymer matrixes and exhibit high performance at low concentration. The dispersion and localization of nanofillers, which may be evenly distributed throughout the polymer matrix or concentrated at the interface, affect the characteristics of polymer nanocomposites. Several researches have been done on starch-based polymer nanocomposite materials that are filled with various nanofillers, carbon nanomaterials (such as graphene and its derivatives, and CNTs), metal/metal oxides, and silicate nanoclays [62]. The findings demonstrate that nanofillers enhance mechanical and thermal stability due to their superior dispersion inside the matrix polymer [62].According to earlier studies [43,44]. For example, Alperet al. [63], exfoliated graphene oxide (GO) nanosheets within hydroxyethyl starch (HES)/divinylsulfone nanocomposite to remove malachite green dye. The obtained findings showed maximum adsorption of the prepared nanocomposite of 89.3 mg/g. In another study, starch nanocomposites were created by Abdul-Raheimet al. [64], from modified starch, acrylic acid, and Fe 3 O 4 for removal toxic heavy metal ions such as Pb 2+ , Cu 2+ , and Ni 2+ ions. The findings showed that maximum adsorption reported as 100, 70 and 100 mg/g for Pb 2+ , Cu 2+ , and Ni 2+ ions, respectively. Moreover, Mohammed et al. [65], reported the preparation of Fe 2 O 3 NPs /starch nanocomposite using formaldehyde as a crosslinker (Fig. 5) for removal different toxic divalent cations: Pb 2+ , Hg 2+ , and Cd 2+ ions. The   [60]. Copyright 2022. Adapted from MDPI adsorption of metal ions was accomplished by starch-based iron oxide nanoparticles with many OH groups and the schematic diagram to represent the synthetic procedure of Fe 2 O 3 NPs-starch nanocomposite and the proposed core shell structure of Fe 2 O 3 NPs-starch nanocomposite. The results showed Q max of Hg 2+ , Pb 2+ , and Cd 2+ of 133.3 mg/g, 2000 mg/g, and 322.58 mg/g, respectively, at the optimal conditions for maximal adsorption: pH 7, 20 min of contact time, 0.2 mg/l of metal, and 20 mg of adsorbent. The findings showed that Pb 2+ exclusively obeyed the Freundlich isotherm model, while Hg 2+ and Cd 2+ were best fitted by all models.

Starch-Based Aerogels
Aerogel formulations are 3D porous materials and are considered one of the most promising adsorbed materials for water purification from various pollutants such as heavy metal ions, dyes, etc. [66]. They are classified into three categories: organic, inorganic, and hybrid forms whose porous micro-or nanostructure [67,68]. The physico-chemical characteristics of the prepared aerogels are primarily controlled by several parameters as starch supply, biopolymer content, amylose/amylopectin ratio, and degree of gelatinization [69]. They have outstanding features: low-cost, sustainable, and potential materials as well as high surface area, high porosity, and low density [70][71][72]. Starch-based aerogels are a class of advanced porous materials which are easily fabricated with different biopolymers, and/or synthetic polymers via freeze drying technique [73]. For example, recently, Li et al. [74], have fabricated rich 3D layered porous starch-based aerogel (starch/polyacrylamide/ CaCO 3 / TEMPO-oxidized nanocellulose) via freeze drying method for removal of MB and CR dyes from an aqueous solution (Fig. 6). The resultant starch aerogels had excellent swelling ability as well as potential adsorption capacity for MB and CR reached 101.01 mg/g and 277.76 mg/g, respectively, via electrostatic and H-bonding interactions. After four reusable cycles, the adsorption efficiency of the starch aerogels decreased to 74.56% and 65.75% for CR and MB, respectively.
In another study, Yun et al. [75] have prepared highly porous aerogels via combination of reduced graphene oxide (rGO) nanosheets with dialdehyde starch nanocrystals (DASNC) via freeze drying method (Fig. 7). After  [65]. Copyright 2019. Reproduced with permission from Elsevier modification of DASNC with rGO, the findings found that the prepared aerogel surface with high robust, which resulted in superior mechanical property, as well as excellent specific capacitance reached up to 316 F/g. Moreover, the obtained aerogels were applied as adsorbent for removal of rhodamine B (RB) and crystal violet (CV) with high Q max reached up to 539 mg/g and 318 mg/g for RB and CV, respectively, owing to the porous surface and high surface area of the examined starch aerogels.

Starch-Based Nanofibers
Polymeric nanofiber membranes can be designed to widely apply for removing various contaminants from polluted water owing to its significant features such as large surface area, high separation efficiency, high porosity, low-cost and easily functionalize with multifunctional materials to achieve potential wastewater treatment [76].The fabrication methods of polymeric membranes include electrospinning,  [75]. Copyright 2019. Reproduced with permission from American Chemical Society phase inversion, track -etching, sintering and stretching method [77]. However, electrospun nanofibers have received potential attention in wastewater treatment compared with other approaches because of its advanced advantages including simple modification technique, strong versatility, low-cost method, and broad selection of materials. In this approach, charged polymer melt of solution and high-voltage electric field are applied to design smooth and controllable morphology nanofibers [78,79]. Recently, for the removal of Cr 6+ ions from an aqueous solution, Sun et al. [80] have prepared electrospun Starch-graft-Polyacrylonitrile (St-g-PAN) nanofibers via electrospinning technique in in dimethyl sulfoxide (Fig. 8). In this study, the authors charged about 4.3 wt% of grafted starch under typical spinning voltage of 15 kV. The SEM image displays finer fibrous without any knobs. Moreover, the adsorption results demonstrated that the obtained St-g-PAN nanofiber achieved potential removal of Cr 6+ ions with Qmax of 533.4 mg/g, at pH 2.0. Table 2 showed the advantages and disadvantages of different mentioned starch modifications.

Modified Starch-Based Adsorbents for Wastewater Treatment
Excessive leakage of various contaminants into the water surfaces owing to rapid urbanization and industrialization as well has received a great interest worldwide. Among these contaminants, heavy metal ions, textile organic dyes, residual pharmaceutical antibiotics, pesticides, and oils, which are highly toxic, and non-biodegradable materials. As a result, they significantly reduce water quality, accumulate in living cells, and cause fatal diseases. Therefore, in recent years, wastewater purification has been received great attention from worldwide scholar researchers. Recent modified starch-based adsorbents possess many advantages including high adsorption selectivity, good thermal and mechanical stability, and low-cost materials, which increase its capability for water purification [88].

Removal of Heavy Metal Ions
Heavy metal ions (HMs) define as elements have an nuclear density more than 4 ± 1 g/cm 3 [13,17]. HMs such as, cadmium (Cd), chromium (Cr), iron (Fe), lead (Pb), cobalt (Co) and nickel (Ni) ions are commonly used in industrial applications whose industrial waste products are drained into water streams. However, they have many obstacles, like high toxicity, carcinogenicity, water-solubility, and non-biodegradability. Consequently, their effluents contaminate all water resources, and then accumulate in living cells and result in a dangerous influence on human health. They can also lead to Parkinson's and Alzheimer's illnesses and neurodegenerative disorders [17,[89][90][91][92][93].
Heavy metals enter the water sources from a diversity of industries, such as minerals extraction, water treatment, metal molding, metal coating, batteries, nuclear industry, Leather tanning, electroplating, fuel combustion, landfills, electronics, metal finishing, wood processing, enamelling and nuclear power generation [17,18,[94][95][96][97]. Adsorption technique isa considered as the most effective method for eliminating various HMs from contaminated water owing to its low-cost, ecological impact, excellent removal efficiency

References
Grafted copolymer Modifies the symmetry of the polymeric chain and modulates both intramolecular forces and properties such as glass transition temperature, crystallinity, solubility, elasticity, permeability and chemical reactivity can be tuned within wide limits Grafted product characterizations are being inherently difficult as it is further complicated by homopolymer which is amply generated during the reaction [20,81] Grafting results in retention of desirable properties of base polymer and incorporation of favorable properties in grafted polymer Production of by-products; consumption of chemicals; cause environmental pollution, etc.

Introduce various functional groups; alter physicochemical properties
Easy to scale up an extensive range of applications, etc

Renewable and sustainable
Extraction methods needed for the starting product [82,83] Greater swelling capacity in the saline solution, given that water preferably interacts with salt, therefore reducing the hydrogel swelling; Modifications required to create Superabsorbent hydrogels Poor mechanical strength, etc.
Desired absorption rate (particle size and porosity) depending on the application requirements; Lower content of soluble and residual monomers; Low production cost; Greater durability and stability in the swelling environment and during storage; High biodegradability without the formation of toxic byproducts; non-toxic; Photostability; Re-swelling capacity (if necessary) Viscoelasticity, high permeability, and adsorption kinetics, which favor the removal of contaminating species from wastewater Beads High mechanical stability, a low weight, and a large specific surface area Hardness, high relative crystallinity and reduced swelling ratios as the gelation time increased [84] Aerogels Ultrahigh porosity and ultralow density, very high surface area Complex fabrication process [85,86] Surface functionalization open porosity and hydrophobicity decide the absorption properties of aerogels High manufacturing costs, and high failure rates The sorption characteristics of aerogels are used to absorb heavy metal ions in water treatment and oil spills Aerogels made from starches with a lower amylose content such as potato starch had a lower specific surface area and a higher density  2+ , and Cr 3+ , respectively, at pH 5.0, and 12 h via coordination bonds between the adjacent amine groups in polymer chains and metal ions.in addition. The regeneration study showed excellent reusability, as the adsorption capacity remained stable after 10 reusable cycles.
While Aniagor and Hashem [103], described the preparation of polyacrylonitrile (PAN) grafted corn starch to remove Zn 2+ ions. Grafted PAN including polar CN groups provide entrenched stable network chains and enhanced both of water absorption capacity and cation binding interaction. The high adsorption capacity of Zn 2+ ions 508.85 mg/g was demonstrated at pH of 5.0, 20 min, and 0.3 g/l adsorbent concentrations.
In addition to grafted starch copolymers, the starch-based hydrogels including great attention to be an efficient adsorbent for elimination of toxic HMs from contaminated water. Farag et al. [55] used radiation method to graft copolymerize 2-acrylamido-2-methylpropane-1-sulphonic acid (AMPS) and dimethyl aminoethyl methacrylate (DMAEMA), for capturing of Co 2+ ions. The findings illustrated that Q max was observed of 350 mg/g at 25 °C, and pH 3. the Co 2+ ions adsorption of onto the obtained hydrogels is via coordination bond between NH 2 groups on hydrogel surface and lone pair of electrons of Co 2+ ions.
Moreover, Duquette and Dumont [104] demonstrated the preparation of grafted starch hydrogel in the presence of itaconic acid using acrylamide as a cross-linker. The obtained hydrogel had the ability to eliminate Cu 2+ from Higher separation performance, Lower energy requirements, High specific surface area Easier preparation methods High pore interconnectivity, relatively uniform pore size the aqueous solution by Q max of 1.36 mmol/g at pH 3.5. through electrostatic interaction between carboxylate anions and metal ions. Whereas, according to Schmidt et al. [105], cross-linked potato starches hydrogels (StMBA) and starch-grafted PAM copolymer hydrogels were synthesized by chemical crosslinking polymerization (Fig. 9a) using MBA as a crosslinker for the removal Cu 2+ and Fe 3+ ions from aqueous solutions. According to LSM image, alamellar morphology (Fig. 9b). The adsorption results demonstrated that StMBA had an adsorption efficiency of 14.0 mg/g (Fig. 9c) and 2.9 mg/g (Fig. 9d) for Cu 2+ and Fe 3+ , respectively, while grafted starch hydrogels reported higher efficiency reached 23.0 mg/g and 21.2 mg/g for Cu 2+ and Fe 3+ , respectively, via coordination bonds between metal ions and amine groups on the surface of starch hydrogels. In another study, Rahmanet al. [106] mentioned the preparation of a superabsorbent hydrogel based on potato starch and PAA via irradiation grafting approach to remove Cr 6+ ions from industrial wastewater. The as-prepared hydrogel showed excellent adsorption capacity of 10.13 mg/g after 3 h. In order to remove heavy metal ions like Pb 2+ , Zn 2+ , and Cu 2+ , Anghelet al. [107] described the production of potato starch/cellulose / toluene-diisocyanate via batch-adsorption technology. The obtained data showed the Q max of Pb 2+ , Zn 2+ , and Cu 2+ were 66.66, 58.82, and 47.61 mg/g, respectively at pH 5.0, and 120 min, which well-fitted Langmuir isotherm model.
Starch-based beads have been widely applied for removal of heavy metal ions from polluted water. For the elimination of Cu 2+ ions, Dragan et al. [108] reported the preparation of grafted starch/polyamidoxime/ chitosan beads by ionotropic gelation. The adsorption data showed that Q max estimated by the Langmuir model was 238.14 mg Cu 2+ /g for the fabricated beads at 25 °C. The adsorption mechanism exhibited that chemisorption is a mean mechanism of interaction between the chelating beads and the Cu 2+ ions. Moreover, the prepared beads reused up to 5 adsorption-desorption cycles without any decrease in Cu 2+ ions adsorption. While for the elimination of Pb 2+ ions from an aqueous solution, Chen et al. [109] mentioned the preparation of starch/humic acid beads via inverse phase suspension crosslinking. The findings showed that Q max was 50 mg/g at pH 5, and 298 k. The obtained beads showed good regeneration with little loss of adsorption capacity. The adsorption mechanism of Pb 2+ ions was with electrostatic interaction. Recently, Dragan and Loghin [110] have fabricated starch beads based on starch-g-PAN/chitosan for the elimination Cu 2+ , Ni 2+ , and Co 2+ ions from an aqueous solution. The adsorption findings showed that Q max of Cu 2+ , Ni 2+ , and Co 2+ ions onto the beads surface were 100.6 mg/g, 83.25 mg/g, and 74.01 mg/g, respectively via chemisorption mechanism (Fig. 10).
Starch polymer nanocomposites have great attention for purification the contaminated water from eluted industrial toxic heavy metal ions in recent years. The combination Fig. 9 a Schematic representation of formation of cross-linked starch-g-PAM hydrogels, b SEM image of the prepared hydrogel, and the adsorption efficiency of c Cu 2+ ions and d Fe 3+ ions against contact time (min) [105]. Copyright 2020. Adapted from MDPI 1 3 of starch and metals and /or metal oxides can provide new material with special mechanical and chemical properties as well as an improved metal ion adsorption capacity [111]. For instance, Saberiet al. [112], demonstrated the creation of starch/PEG-PAA hydrogel and AgNPs-base nanocomposite for removal of Hg 2+ ions. The Q max was achieved as 158.21 mg/g and 182.53 mg/g in pH 7 and 6, respectively. A new nanocomposite mixed made of molybdenum trioxide (MoO 3 ), waste mallow stem biochar, super magnetic spinel ferrite (MSB@CoFe 2 O 4 ), and gelatin-esterified starch was designed and fabricated by Mahmoud et al. [113]. The results show the Q max of Pb 2+ onto hydrogels were 2075, 4375, and 5000 μmol.g −1 , respectively, via electrostatic interaction mechanism. The reusability test showed a little loss (2%) after five continuous recycles.
In order to removal of Cu 2+ and Pb 2+ from wastewater, Saberiet al. [114] described the synthesis of the magnetic Fe 3 O 4 -based starch-PAA (Fe 3 O 4 @St-PAA) nanocomposite. The obtained Fe 3 O 4 @St-PAA showed the adsorption efficiency of 99.32% and 93.83% towards Cu 2+ , Pb 2+ , respectively, according to Langmuir isotherm model. The adsorption efficacy based on the electrostatic interaction between metal ions and various chelating groups in the magnetic nanocomposities such as carboxylic and hydroxyl groups.
In order to remove As 3+ ions from aqueous solution, Bisht and Neupane [115], demonstrated the green chemical production of Fe 3 O 4 @St nanocomposite by supercritical CO2-assisted. The results showed that the maximum As 3+ adsorption capacities on the obtained nanocomposite reached 124 mg/g via coordination covalent bond between As 3+ ions and surface anions on magnetic surface. While the results showed that a complete removal of arsenic from the ground water sample in 15 min the nanomaterials be regenerated in NaOH solutions and could retain more than 50% of the As 3+ removal capacity even in the fifth regeneration/ reuse cycle. Moreover, Xie et al. [116] mentioned the preparation of Fe 3 O 4 /starch /PAA/PAM nanocomposite via an inverse emulsion graft copolymerization for elimination of Cd 2+ ions from aqueous solution (Fig. 11). According to the findings, the maximum adsorption capacity of Cd 2+ on the obtained nanocomposites was 39.98 mg/g, well described by the pseudo-second-order kinetic and Langmuir isothermal adsorption models. The obtained nanocomposite exhibited a various active sites on the surface as -COOH,-OH, and-NH functional groups that increase the chelation ability with Cd 2+ ions.
Ahamad et al. [117] developed starch/salicylaldehyde/ Fe 3 O 4 nanocomposite for the elimination of Pb 2+ and Cd 2+ from pollutant water. According to the adsorption data, the highest adsorption capacity for Pb 2+ and Cd 2+ ions was found to be 265.4 and 247.2 mg/g, respectively. After seven cycles, the manufactured starch nanocomposite samples showed an outstanding reusability.
While, according to Chen et al. [118], a new modified calcium and starch-ferromanganese binary oxide (Ca-SFMBO) nanocomposite adsorbent for the removal of arsenic As 3+ and Cd 2+ ions from water has been developed. The Q max of % Ca-SFMBO for As 3+ and Cd 2+ of were 156.25 mg/g and 107.53 mg/g respectively at pH of 6. Moreover, Xu et al. [119] demonstrated the preparation of a new potato starch-FMBO with an Fe/Mn ratio of 1.00/2.00 and pH of 2 using starch for stabilization dispersion. The maximum As 3+ adsorption capacity of starch-FMBO was 161.29 mg/g at 24 h.
The synthesis of a silica-sand/anionized corn starch composite for the removal of Cu 2+ from water was reported by Li et al. [120]. The adsorption data showed that Qmax for Cu 2+ ions of 383 mg/g at 20 min. The adsorption data are well fitted with Langmuir isotherm model the pseudo-second order kinetic.
Carbon-based nanomaterials are considered as the most attractive nanofillers which are used widely to incorporate inside polymer chains to enhance the adsorption efficiency of the used polymer [121]. In order to remove Cr 6+ , Kumar athilaka et al. [122] created a new starch-stabilized nano zerovalent iron-GO nanocomposite. GO was prepared by the Hummer method. The findings showed that maximum adsorption capacity of the obtained nanocomposite was 143.28 mg/g at pH 3, within 20 min, fitted well with the Langmuir isotherm model. In another study, Hosseinzadeh and Ramin [123] created Fe 3 O 4 /starch-g-PAM/GO nanocomposite via in situ radical solution polymerization to effectively remove Hg 2+ from aqueous solution. The adsorption data found that nanocomposites had Q max of 277 mg/g at optimum pH7. The Hg +2 removal mechanism was a result of the electrostatic interaction between the negatively charged carboxamide fictional groups and Hg +2 ions, as well as mercury ion covalently bonded to -NH groups of acrylamide. Moreover, the oxygen containing hydroxyl groups were complexed with Hg +2 ions. By using a simple esterification technique, Wang et al. [124] created Fig. 10 Schematic adsorption mechanism of heavy metals on the prepared starch beads adsorbent [110]. Copyright 2018. Reproduced with permission from Elsevier starch/GO nanocomposite for elimination of Cd 2+ from the aqueous solution. GO and poly PVA were esterified to produce the polymeric modification of graphene. The findings showed that maximum Cd 2+ adsorption capacities were 43.20 mg/g well-fitted with the Langmuir isotherm model. Additionally, GO-starch nanocomposite was created by Bulin et al. [125] using a hydrothermal method to remove Cu 2+ ions. The adsorption efficiency reached 542.1 mg/g at optimum pH 8. In the third cycle, the Q max decreased to 372.19 mg/g. Also, in another study, starch/GO nanocomposite was fabricated by Guo et al. [126] to scavenge aqueous Pb 2+ ions. The adsorption results showed that the obtained nanocomposite had a capacity of 383.32 mg/g (95.83%) of Pb 2+ ions by Freundlich model. Moreover, the regeneration assay decreased the efficiency of the obtained nanocomposite to 189.69 mg/g in the fifth cycle. Moreover, by the same approach, A starch/GO nanocomposite membrane was designed by Beeviet al. [127] for removing Pb, Cd, Zn, and Mg ions from wastewater. The results showed that the maximum efficiency for heavy metal ions removal was 89.04%, 91.32%, 88.56%, and 89.76% for Pb, Cd, Zn, and Mg ions, respectively.
Starch nanocomposite-based on agricultural waste adsorbents are highly recommended in last few decades for water purification. Baghbadoran et al. [128] demonstrated the fabrication of cellulose nanofibers (CNFs) treated starch-g-PAA/MBA nanocomposites to remove Cu 2+ ions from aqueous solution. The results showed that the maximal adsorption capacity of the fabricated nanocomposite was 957 mg/g, via ion exchange and chelating of Cu +2 ions and ionized&deionized carboxyl groups on nanocomposite surface (Fig. 12). Furthermore, lately, Mohamed et al. [129] have mentioned the preparation of Pisumsativum pods (N-PSPB)/ starch/glycerol nanocomposite for the removal of Cr 6+ ions. The surface area and hole volume of the obtained nanocomposites were 226.94 m 2 /g and 9.88 cm 3 /g, respectively, using SEM and BET techniques. The as-prepared nanocomposites achieved  [116]. Copyright 2021. Reproduced with permission from Elsevier excellent adsorption efficiency up to 420.13 mg/g. They were able to maintain their adsorption efficiency even after 10 adsorption cycles.
On the other hand, silicate nanoclays are widely applied for removing toxic heavy metals from contaminated water. Silicate nanoclay which resulting from isomorphous substitution, and have the capacity to adsorb HMs via exchange of their counter cation [130]. For example, according to Chen et al. [131], Laponite RD/ corn starch/PVA nanocomposite was synthesized by freezing/thawing method for the removal of Cd 2+ ions from wastewater. The findings showed excellent cadmium ion adsorption efficiency of 63.46% was obtained when LRD was at 12.5% after 24 h. Moreover, the adsorption of Cd +2 ions was attributed to the electrostatic interaction between the negative charged surface of nanoclay and Cd +2 ions. The intercalation process was reported by Garca-Padilla et al. [132], to synthesize starch/MMT nanocomposites with varied starch-to-nanoclay ratios: 5:1, 10:1, and 10:3 in acetic acid solution to remove Ni 2+ and Co 2+ ions from aqueous solution. The results showed the highest removal of Ni 2+ and Co 2+ ions were 97.1%, and 78.7%, respectively, according to Langmuir model. Most recently, starch-based aerogels have been applied for removal of heavy metals from polluted water. For example, Camani H. and his team-work [133] have reported crosslinked corn starch adsorbent aerogels in the presence of citric acid as a crosslinking agent via freezedrying method for removal of Cd2 + and Zn2 + ions from an aqueous solution. The adsorption data showed good adsorption efficiency for the obtained starch aerogels owing to high porosity and pore density, large specific area, and good mechanical stability. The results reported that adsorption efficiency reached 30% at 12 h via ionexchange mechanism (Fig. 13 a and b). Several reported studies in recent years have been mentioned based on different starch formulations for removal of different toxic heavy metals ( Table 3).

Removal of Synthetic Dyes
Organic synthetic dyes are widely used in various industries including textile, paper, dying, and printing industries due to their inexpensive cost and easy availability-for example, crystal violet, methylene blue, and orange II dyes. The discharge of hazardous contaminants such as different synthetic dyes to waster surfaces makes it unfavourable for living organisms' usage [134][135][136][137]. The fabric industry sewages contain various sorts of dyes that cause a severe threat to the ecological system [138][139][140]. Furthermore, the adsorption of dye on adsorbent surface is achieved via various adsorption mechanisms, as schematically shown in Fig. 14. It should be noted that the adsorption of water pollutants on adsorbents is mainly guided by electrostatic attraction, π-π interactions, van der Waals forces, hydrogen bonding, acid-base reactions, and hydrophobic interaction [141].
Recently, Farag et al., have been reported radiation technique for grafting AMPS and DMAEMA onto starch for removal of basic dye (Astrazon Red 6B) from aqueous media. The maximal adsorption capacity reached 600 mg/g at pH 9 via electrostatic and H-bonding interactions [55]. While effective disposal of MG dye using potato starch grafted AA/AM hydrogel in the presence of MBA as crosslinker was studied at 60 mg/l of dye. The findings showed good adsorption efficiency of 94.2% at 120 min. The high removal percentage is due to the electrostatically interaction between the negative charged -CONH 2 , -COO − and -COOH functional groups and positively function groups of MG [142]. Lately, Guo et al., [143], have reported crosslinked starch hydrogels by quaternary ammonium terminals for adsorption of golden yellow (GY) dye. The Q max from Langmuir model was recorded 208.77 mg/g (99.59%) at 308.15 K, and 14.3 min [143]. A novel hydrogel beads based on gelatin and oxidised maize starch were examined by Dai et al., [144] and the utility and viability of using them to treat wastewater with colours was investigated.. Tartrazine was presented as a model substance. The data illustrated Qmax Fig. 12 Adsorption mechanism of Cu +2 ions on starch-g-PAA/ MBA/CNFs nanocomposites [128]. Copyright 2019. Reproduced with permission from Elsevier of 293 mg/g at 35 °C, a pH of 2.5, and stirring at 400 rpm via electrostatic and H-bonding interactions. Mahmoodi et al., [145] designed ethylenediamine/GA-modified starch (SEG/ positive charge) hydrogel for capture DR23 and Acid Blue 92 (AB92) dyes by adsorption technique. The adsorption capacity was growing from 8 mg/g (DR23) to 167 mg/g (AB92) via electrostatic interaction and H-bonding interaction. In another study, Loghin et al. [146], synthesised beads made from chitosan and potato starch, and PAN for removal of CR and DB15 from an aqueous solution. The prepared starch beads achieved good adsorption for CR with 170 mg/g and 75 mg/g for DB15.
Starch-based modified nanocomposites adsorbents are widely applied for removal of different dyes from contaminated water. Starch-g-PAM/GO/HAP nanocomposite adsorbent was prepared by Hossein et al. for removal of MG from an aqueous water. to be environmentally benign and effective at removing various cationic dyes from contaminated water.
The Qmax for MG dye was 297 mg/g at pH 10, and the adsorption isotherm data was well fitted with the Langmuir isotherm model. After five consecutive reusable cycles, the obtained nanocomposite demonstrated good regeneration capability without any reduction in adsorption efficiency [26]. According to Pourjavadi1 et al. prepared CaCO 3 / starch/PAM/PAMPS/GO nanocomposite adsorbent for detection of MB dye. The adsorption data demonstrated high adsorption capacity of up to 714.29 mg/g at pH 7. The high adsorption capacity of the nanocomposites as a result of presence of different functional groups as Sulfonate, hydroxyl and amide which facilitate the interaction between nanocomposites and MB via electrostatic interaction, hydrogen bonding interactions as well as π-π interactions [147].
Ismail et al. reported that poly(p-aminophenol) (PpAP), containing starch and GO nanocomposite was prepared via free radical polymerization to remove MB dye from an aqueous solution. The fabricated nanocomposite adsorbent Fig.13 Schematic of the adsorption of a Cd 2+ ions b Zn 2+ ions on crosslinked corn starch aerogels [133]. Copyright 2023. Reproduced with permission from Elsevier     [202] was able to remove MB dye by efficiency of 96.7% from water at pH 7. The numerous functional groups contained in the ternary composite, which promote electrostatic reactions, hydrogen bonding, and π-π interactions between the MB dye and the ternary composite. After six regenerated cycles, the synthesised adsorbent also shown good reusability without any decrease in adsorption efficiency of MB dye [148]. Moreover, recently, Hossein zadeh et al., reported the preparation of starch-g-PAM/GO nanosheets / n-HAP nanocomposite (Fig. 15a) for removal of MG dye. The MG dye adsorption maximum was recorded as 297 mg/g at basic pH solution (pH10). After 5 regenerated cycles, the synthesised adsorbent also shown good reusability without any decrease in adsorption efficiency of MG dye (Fig. 15b) [149].
On the other hand, starch-based nanoclay nanocomposites have been reported in several literature for removal of dyes. For instance, Lawchoochaisakul et al., mentioned the fabrication of cationic starch/MMT for removal of water-soluble cationic dyes including Basic Blue (BB66) and Basic Yellow Fig. 14 Adsorption processes and mechanisms for dye removal from bulk liquid [141]. Copyright 2021. Adapted from Royal Society of Chemistry   Fig. 15 a Schematic preparation of starch-g-PAM/GO nanosheets / n-HAP nanocomposite adsorbent for removal of MG dye, and b five adsorption-desorption cycles for the prepared nanocomposite [149]. Copyright 2018. Reproduced with permission from Elsevier (BY1) from solutions. The results showed good ability for the prepared nanocomposite adsorbent with adsorption efficiency up to 99.40% (49.7 mg/g) for BB66 and 99.7% (49.9 mg/g) for BY1, via intercalation of CST into the interlayer spacing of MMT. The adsorption mechanism showed that the existence of cationic starch may widen the MMT interlayer space, enhancing the adsorption on the surface of the prepared nanocomposite [150].
While the modified starch nanocomposite adsorbents based on metal/metal oxide nanoparticles have been reported for detection of various dyes as well. For instance, recently, El-Sheikh et al., [151], have been reported starch nanocomposite based on carboxy methyl starch copolymerized with PAM/ Ag NPs as an adsorbent for MB from aqueous solutions. The study displayed that removal % of MB reached up to 99.33%, at 343 K [151]. Under batch circumstances, Optilan Blue (OB) adsorption on starch-coated Fe 3 O 4 NPs was carried out. On the adsorption of OB on the prepared nanocomposite, the findings showed that the highst removal of OB wase 88.87% at pH 2 and 308 K [152]. Additionally, Yeamin et al., [153] have reported the preparation of poly (aniline), PANI, /starch/SiO2 nanocomposites for removal of MB and OG dyes via adsorption technique. The MB dye adsorption capacity is 6.8 × 10 6 mol/g, while the removal capacity of OG was 48 × 10 6 mol/g at pH 6.86 and 302 K. As a nanofiber membrane for the elimination of MB dye, Moradi et al., [154] fabricated a PVA/starch nanofiber membrane using an electrospinning technique. The findings illustrated that the highest adsorption capacity of MB is 400 mg/g. at pH 8.5, and 150 min. Furthermore, after five reusable cycles, the adsorption capacity remained at 92.1%. Several reported studies in recent years have been mentioned based on different starch formulations for removal of different toxic synthetic dyes ( Table 3).

Removal of Antibiotics
Pharmaceutical antibiotics have reported as dangerous water pollutant in recent years [155,156]. Every year, a massive number of antibiotics are manufactured and consumed. Antibiotics that have not been utilized or digested are discharged into the environment which introduces resistance into natural bacterial ecosystems [157][158][159]. For instance, according to water analysis data, ciprofloxacin and tetracycline have been found at high concentrations in surface water, groundwater, and sediment [160,161]. Various chemical and physical methods have been used to eliminate organic compounds, including adsorption, biodegradation, chemical oxidation, ion exchange, and membrane approaches [162][163][164][165][166][167]. But the adsorption technique has great attention in few past years due to its outstanding advantages that mentioned above.
Grafted starch has been applied widely for capture of antibiotic drugs from contaminated water. For example, Bouhedda et al. [168] mentioned the designing of an amphiphilic adsorbent system based on grafting of starch with octenyl succinic anhydride for the removal of cephalexin antibiotic with a batch adsorption method. They studied different factors, including octenyl succinic anhydride grafted starch dose, temperature, adsorption time, and pH. Q max reported as 0.92 mg/g at pH 6, via hydrophobic interaction. The results were well fitted to the Redlich-Peterson isotherm and second-order kinetic model. Most recently, Kang and his co-workers [169], have reported high-efficient modified corn starch-based hyperbranched brush architecture flocculant for removal of tetracycline. They mentioned that the as-prepared flocculant has remarkable advantages, including low-cost material, easy preparation, and eco-friendly. Hyperbranched brush architecture starch-based flocculant has been synthesised by grafting of PAMPS and PAM on the backbone of carboxymethyl corn starch. The obtained flocculant grafted copolymer starch achieved super removal ability for tetracycline reached up to 95.7% via electrostatic and H-bonding interactions.
To remove both tetracycline and ciprofloxacin from wastewater using hydrogel-based adsorbent, Itodo et al. [170] synthesised crosslinked starch/chitosan hydrogel with 2% glutaraldehyde using the casting method for removal of the tetracycline and ciprofloxacin. The results showed that the maximum removal efficiency was 99.4% using the batch adsorption method. The adsorption mechanism was controlled with chemisorption mechanism between adsorbent and adsorbate. On other hand, Fu et al. [171] are interested in preparing a highly efficient starch nanocomposite-based adsorbent for the removal of tetracycline in the presence of nanoscalezerovalent iron using a batch method. The removal efficiency reached up to 99%, which was obtained from the adsorption method (around 30%) and the degradation approach (around 69%) using 200 mg of modified starch and 500 ppm of antibiotic. They reported that both a neutral environment and a high ionic strength enhanced the sedimentation rate. In a recent study for the removal of tetracycline drug, Shen et al. [172] have prepared corn starch and carboxymethyl starch-modified magnetic bentonite clay nanocomposite-based adsorbents. They prepared magnetic bentonite clay with a solvothermal method. The asprepared carboxymethyl starch/magnetic bentonite showed better adsorption performance (Qmax = 169.7 mg/g) than corn starch nanocomposite (Qmax = 132.3 mg/g) via ionexchange mechanism, fitting into the Langmuir isotherm and pseudo-second order models. The obtained carboxymethyl starch nanocomposite had good adsorption efficiency and reached up to 59.4% after 3 reused cycles.
Zhang et al. [173] recently have utilized from a biological self-assembly manner for preparation of two starch porous carbon nanocomposites-based adsorbent for the removal of Tetracycline (Fig. 16a). They isolated quinoa starch from quinoa seeds via alkaline steeping technique. They prepared two hyphae/starch composites using fungal hypha of Aspergillusniger and Myrotheciumverrucaria with code number of PCCQS-AN and PCQS-MV, respectively. Surface area of the obtained two composites mentioned as 3050 m 2 /g and 2546 m 2 /g, respectively. The adsorption method of tetracycline illustrated superior adsorption capacity for PCCQS-MV (67.16%) than for PCCQS-AN (57.23%) that occurred through electrostatic, π-π, and H-bonding interactions (Fig. 16b). The regeneration studies showed that the as-obtained composites have the ability to maintained higher efficiency up to 43% after 5 cycles.
Additionally Mohamed et al. [174] reported the preparation of Pisumsativum pods biochar (PSPB) NPs / starch nanocomposite for the removal of naproxen drug with mass ratio of 2% (w/w) in the presence of glycerol as crosslinking agent at an elevated temperature. The as-prepared nanocomposites were employed for the removal of naproxen drug using adsorption method. The findings showed excellent adsorption efficiency, reaching up to 309.82 mg/g, fitted to Langmuir isotherm through electrostatic, π-π, and H-bonding interactions. They were able to maintain their efficiency after 10 reusable cycles. Moreover, metal organic frameworks (MOFs) have been considered one of the most attractive nanocomposite formulations in the past few years to capture antibiotic structures from contaminated water. For example, Mohamed and Mahmoud [175] designed starch nanocomposite adsorbent matric onto MOFs which were doped with nanomagnetite to remove fluvastatin antibiotic.
They synthesized MOFs based on malonic acid-grafted starch nanocomposites in the presence of zinc acetate/glutaric acid and nanomagnetite (NFe3O4) with microwave irradiation technique according to Fig. 17. The results recorded a high surface area of 528.4 m2/g; mesoporous structure with pore size of 2.9 nm, as well as high crystallinity. The adsorption data for the removal of antibiotic demonstrated a Q max of 782.1 mg/g via H-bonding interactions, fitting with Langmuir isotherm. The validity of as-prepared nanosorbent for the capture of fluvastatin from real water was proved in the range of 96.2-99.9%.
In the latter study, Jia and his colleagues reported a hierarchical porous adsorbent for sulfanilamide drug from wastewater [176]. They prepared a porous adsorbent based on starch (maize)/chitosan/UiO-66-COOH-type carboxylic zirconium MOF with a facile Ch-adhesive approach via electrostatic and H-bonding interactions. The results demonstrated that the porous nanocomposite offered a macroporous structure with high stability. The Q max recorded to be 46.64 mg/g via electrostatic and H-bonding interactions according to the Langmuir isotherm model, meaning the formation of a homogenous monolayer on the adsorbent surface. And, it was fitted to a pseudo-second-order model. The adsorption mechanism confirmed that the Zr-O moiety in carboxylic Zr-MOF had a high affinity for the sulfanilamide drug. Moreover, the adsorption of the as-obtained adsorbent affected with pH of the antibiotic solution, therefore, it decreased with an increase in pH from 3 to 11. Additionally, the recyclability test showed that the nanocomposite-based Fig.16 a Biological self-assembly manner for preparation of two starch porous carbon nanocomposites, b Adsorption of tetracycline on nanocomposite surface [173]. Copyright 2022. Reproduced with permission from Elsevier adsorbent has the ability to maintain its adsorption efficiency of 30.24 mg/g after 4 reused cycles. Table 3 shows different reported studies in recent years have been mentioned based on different starch formulations for removal of antibiotics.

Removal of Pesticides
Without using pesticides, modern farming is all but impossible. In spite of being first banned or restricted globally in the 1980s, organochlorine pesticides (OCPs) were found to be among the most resilient classes of organic pollutants [177]. Conversely, synthetic pyrethroids and organophosphates are two pesticides that are typically categorised as being substantially less persistent than OCPs and are therefore frequently used in pest management. However, the rising use of synthetic pyrethroids (SPs) and organophosphorus pesticides (OPPs) poses very high chronic and acute toxicity to some aquatic creatures, including fish, invertebrates, and mollusks [178]. Taking into account all of these variables, pesticide use does not ensure water safety. According to literature studies, rivers in agricultural catchments face major difficulties as a result of the pesticides' expanding use at an exponential rate [179,180]. To date, starch has been highlighted as an attractive natural material for designing high-efficient adsorbent to eliminate pesticides owing to its outstanding advantages, including low cost, biocompatibility, non-toxicity, and easy chemical modification. for example, Tang et al. [181] investigated pesticide removal from basil leaves using gelatinized corn starch (GS) using surfaceenhanced Raman scattering (SERS) mapping (Fig. 18). They studied the removal of different pesticide categories, such as organo-phosphorus pesticide like temephos, organo-nitrogen pesticide like acetamiprid, organo-chlorine pesticide like dicofol, and fenvalerate as pyrethroid pesticide. Results showed that the SERS mapping tool is a highly efficient tool to detect pesticide residues on vegetable leaves surface. Moreover, according to the findings, temephos, fenvalerate, dicofol, and acetamiprid can be effectively removed by washing with gelatinized corn starch of 40 g/l for 5 min. The best solution to eliminate pesticide from basil leaves in the absence of "secondary contamination" was gelatinized corn starch.
Moreover, Suo et al. [182] reported superior rapid removal of 11 pesticides using mesoporous activated  [175]. Copyright 2020. Reproduced with permission from Elsevier carbon/starch nanocomposites using an adsorption method. The adsorption data of as-prepared starch nanocomposites was recorded to be above 80%, higher than other reported adsorbents such as graphitised carbon black, commercial activated carbon. Findings fitted with the pseudosecond order and Langmuir isotherm models. Moreover, the adsorption mechanism for all tested pesticides enhanced by N atoms, π-π benzene bonds, and oxygen-containing functional groups through hydrophobic interactions and H-bonding interactions. The regeneration test results showed that, after 5 consecutive adsorption-desorption cycles as shown in Fig. 19, the as-obtained starch nanocomposites have good adsorption efficiency, which is still greater than 80% for all pesticides tested.

Removal of Oils
The repercussions of oil contamination on the environment are irreversible. As a result, the removal of oil pollutants has been one of the major environmental issues in the oil and petrochemical industries, where it is necessary to clean contaminated effluents of this contamination [183,184]. In general, wastewater that has combined with oil in a wide range of quantities is referred to as oily wastewater [185]. In addition to petroleum fractions, the oil molecules detected in oily effluent can also include lipids and hydrocarbons. Absorbents have lately been used as suitable alternatives to clean oil contaminants and waste oils since they are extremely selective, environmentally acceptable, chemically inert, have minimal operational costs as well as considerable absorption Fig. 18 Pesticide removal from basil leaves using gelatinized corn starch (GS) with SERS mapping [181]. Copyright 2021. Reproduced with permission from Elsevier   Fig. 19 a The adsorption capacity of 11 pesticides by ACS, GCB, AC, C18, and b PSA towards 11 pesticides., Adsorption efficiency of 11 pesticides by ACS after various cycles of regeneration [151]. Copyright 2019. Reproduced with permission from Elsevier capacity, and can be easily recovered [186]. The collection of oily effluent from various industrial sources may differ in terms of its physical properties and chemical content [187].
Currently, a variety of treatment techniques, including adsorption, flocculation, electrocoagulation, and flotation, have been developed for the removal of oil contaminants in order to reduce or prevent the harmful effects of oily wastewater on our ecosystems [188][189][190]. Adsorption has been identified as one of the most promising technology for extracting oil from wastewaters among them since it is one of the least expensive, most efficient methods, and easiest to adapt [190,191]. Free oil, dispersed oil, emulsified oil, and dissolved oil are the four subcategories of oil-contaminated water, sometimes known as oily wastewater. There are several surface characteristics for effective treatment of oily wastewater. Hydrophobic and oleophilic, hydrophilic and oleophobic, and superhydrophilic and superoleophobic surfaces are among these surface characteristics [192].
According to Wang et al. [193], porous starch-based materials have strong oil absorption capabilities, but their hydrophilicity prevents them from being used to mop up oil spills. By adding nanoparticles of Fe 3 O 4 and silylated SiO 2 to starch cryogel, a new superhydrophobic absorbent based on starch designated as (HMS-SiO 2 @MSC) was created (Fig. 20). The Fe 3 O 4 and silylated SiO 2 nanoparticles provided the adsorbent with magnetic (saturation magnetization: 4.36 emu/g) and superhydrophobicity (water contact angle: 154.4°) properties. The (HMS-SiO 2 @MSC) shown good practicability for cleaning up oil slick on the water's surface using magnets. The benefits of starch and magnetic Fig. 20 a, b Schematic synthesis of MSC and HMS-SiO 2 @MSC, and c adsorption capacity of chloroform and n0hexane by HMS-SiO 2 @MSC [193]. Copyright 2022. Reproduced with permission from Elsevier nanoparticles can be combined in magnetic starch-based adsorbents, which have distinct important characteristics such availability, affordability, size, form, crystallinity, stability, magnetic characteristics, adsorption abilities, and exceptional surface properties. Additionally, the adsorption capacity of HMS-SiO 2 @MSC toward chloroform and n-hexane is 7.78 and 2.72 g/g respectively.
By hydrolysing hexadecyltrimethoxysilane and tetraethyl orthosilicate in the presence of starch cryogel in a singlestep sol-gel procedure, Wang et al. [194] created a superhydrophobic starch-based adsorbent for the removal of oil from water. Starch cryogel is simultaneously given hierarchical micro/nanostructures and low surface energy throughout the process, resulting in a high water contact angle (> 153.0°) and a low sliding angle (< 8.0°). The as-obtained adsorbent has good mechanical and chemical durability, outstanding water repellent, self-cleaning, and anti-fouling capabilities. Furthermore, it demonstrated acceptable oil adsorption performance (2.6-7.5 g/g), which was dominated by its porosity and followed a pseudo-second-order model. Because of its preferential wettability towards water and oil, it was used to remove oil from the water's surface and when submerged. A significant class of smart coatings known as superhydrophobic coatings with large water contact angles (CA > 150) and small water sliding angles (SA 10) have drawn a lot of attention due to their potential applications in a variety of industries, incorporating water/oil separation [195]. Superhydrophobic and magnetic modular starch nanocomposites containing three starch-based modules, namely, a superhydrophobic nano-coating, a magnetic nanocomposite insertion, and a high-strength starch/polyvinyl alcohol composite substrate was prepared by Wang et al. [196] for potential removal of chloroform oil from water. The modular cryogel was exceptionally water-repellent, self-cleaning, and anti-fouling, with high water contact angles (152°) and low slide angles (9°). The adsorption efficiency of the prepared nanocomposite for removal of chloroform reported as 99.8%. After 25 reusable cycles, the adsorption efficiency showed that the prepared nanocomposite maintain its efficiency without any change.

Conclusion, Challenges, and Future Prospects
The adsorption technique is considered one of the most essential ones in recent years for wastewater treatment.
Recently, natural polymer such as starch has received great attention for the design of high-performance adsorbents to remove various non-biodegradable contaminants from wastewater, owing to its outstanding features: non-toxic, biodegradable, low-cost material, easily available, and biocompatible. However, it has some drawbacks that make it inappropriate to be used as an adsorbent for wastewater treatment without modification, including low adsorption efficiency and low thermal and mechanical stability. This review presented various starch modification-based adsorbents that can be designed in various formulations such as grafted copolymers, hydrogels, nanofibers, aerogels, and polymer nanocomposites. These modifications can be made in the presence of various synthetic polymers such as poly(acrylic acid), poly(acrylonitrile), and others, as well as natural polymers such as chitosan, gelatin, alginate, and others. In addition to different essential nanofillers, there are carbon-based nanomaterials (such as graphene oxide and carbon nanotube), metal and metal oxide nanoparticles (like Ag NPs and Fe 3 O 4 ), and nanoclay (such as bentonite and montmorillonite).
The above-mentioned modifications can overcome the limitations of starch to enhance its adsorption ability for wastewater treatment. In addition to enhancing mechanical characteristics, thermal stability, and removal efficiency. Therefore, the review showed the ability of the above-mentioned starch modifications to achieve excellent adsorption efficiency against different non-biodegradable pollutants such as toxic heavy metal ions (for example, Pb 2+ , Cu 2+ , Ni 2+ , Hg 2+ , and Cd 2+ ions), synthetic dyes (such as rhodamine B, crystal violet, malachite green, astrazon red 6B, reactive orange), pharmaceutical antibiotics (for instance, cephalexin, tetracycline, ciprofloxacin, fluvastatin, and sulfanilamide), pesticides (such as temephos, fenvalerate, dicofol, and acetamiprid), and oils and organic solvents (including motor oil, chloroform, hexane, and toluene). Furthermore, the adsorption results for most adsorbed pollutants were fitted to the Langmuir and Freundlich models and a pseudosecond-order kinetic model.
Although starch-based adsorbents have exhibited enormous potency to be employed in water purification, still numerous barriers limit their mercantile applications. The key challenges and recommendations for future work are highlighted below.
• There is a restricted literature on the use of starch based adsorbents in the real wastewater systems. It is crucial to assess the potential of these adsorbents under realistic circumstance and to evaluate the impact of other pollutants on the sorption potential and selectivity of manufactured adsorbents. • Researchers should likewise recognize new strategies to consolidate the adsorption capacity, stability, restoration potential and selectivity of starch-based adsorbents. • It is recommended to execute the cost analysis and economic viability to obtain judgment about the sustainable nature of the water treatment process utilizing these adsorbents. • Development and synthesis of porous starch using enzymolisation of starch or other methods to enhance its adsorption capacity needs to be inspected in the future.
• Irradiating starch can be used with other modification strategies, advancing the development of green technology and the economy. This would result in some synergistic effect by decreasing the amount of the agents used in starch modulation. • Reusability and renovation of the modified starches are the controlling factors in respect of cost reduction for any industrial and environmental application. Hence adequate selection of desorbing media exists a defiance for the future scientists and environmentalists. • Future research should take into account other natural starch supplies, environmentally friendly nanomaterial synthesis, recyclable materials, and the toxicity of nano-waste. For use in commercial applications, further research on biodegradable starch-based hybrids and nanomaterials is required. This research should concentrate on new functional materials, processing innovation, and cost reduction. • Future research ought to go into how these adsorbents perform in real water filtration systems with regard to their possible toxicity and environmental impact. Future research should also focus on assessing starch-based composites as potential materials for the manufacturing of membranes for water treatment processes.

Conflict of interest
The authors declare that they have no conflict of interest.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.