Abstract
Using a flexible bis (triazole) ligand BBPTZ, where BBPTZ = 4,4'- bis (1,2,4-triazol-1-ylmethyl) biphenyl, a novel compound of [Ni2(BBPTZ)4][β-Mo8O26] (1) based on [NiN4O2]2+ secondary building unit (SBU) and [β-Mo8O26]4– cluster was synthesized by hydrothermal method. In compound 1, the [NiN4O2]2+ SBUs serving as 2-connected joints were directly connected [β-Mo8O26]4– clusters forming 1D inorganic strips. The adjacent strips were assembled through two types of BBPTZ ligands along the c axis, giving rise to 2D layers. It exhibits not only good thermal stability but also bifunctional electrocatalytic activity. When using it as the electrocatalyst for the electrochemical sensing for bromate, it shows a broad sensor range (1.35–4.75 mM) and comparable sensitivity of 62.39 µA cm−2 mM−1. Moreover, it also exhibits a remarkable activity towards the hydrogen evolution reaction, with a 248 mV onset potential, a Tafel slope of 131 mV dec−1, and a η10 of 386 mV.
Similar content being viewed by others
References
X. H. Wang, Q. Han, L. J. Chen, and J. W. Zhao (2016). Inorg. Chem. Commun. 63, 24–29.
S. B. Li, L. Zhang, H. Y. Ma, and H. J. Pang (2016). J. Chem. Sci. 128, 825–830.
Q. Chen, M. M. Wang, X. Hu, X. W. Chen, and J. H. Wang (2016). J. Mater. Chem. B 4, 6812–6819.
N. I. Gumerova and A. Rompel (2018). Nat. Rev. Chem. 2, 1–20.
L. Chen, W. L. Chen, X. L. Wang, Y. G. Li, Z. M. Su, and E. B. Wang (2019). Chem. Soc. Rev. 48, 260–284.
P. T. Ma, F. Hu, J. P. Wang, and J. Y. Niu (2019). Coordin. Chem. Rev. 378, 281–309.
Y. C. Ji, L. J. Huang, J. Hu, C. Streb, and Y. F. Song (2015). Energy Environ. Sci. 8, 776–789.
N. V. Izarova, M. T. Pope, and U. Kortz (2012). Angew. Chem. Int. Ed. 51, 9492–9510.
X. L. Wang, Y. Tian, Z. H. Chang, and H. Y. Lin (2020). ACS Sustainable Chem. Eng. 8 (41), 15696–15702.
J. Li, J. C. He, C. Si, M. X. Li, Q. X. Han, Z. L. Wang, and J. W. Zhao (2020). J. Catal. 392, 244–253.
W. Wang, J. Yang, W. Q. Kan, and J. F. Ma (2013). CrystEngComm 15, 5844–5852.
J. X. Liu, X. B. Zhang, Y. L. Lia, S. L. Huang, and G. Y. Yang (2020). Coord. Chem. Rev. 414, 213260.
P. F. Wu, Q. Xue, X. B. Dong, Y. J. Zhang, B. Liu, H. M. Hu, and G. L. Xue (2016). CrystEngComm 18, 5320–5326.
J. X. Meng, Y. Lu, Y. G. Li, H. Fu, and E. B. Wang (2009). Cryst. Growth Des. 9, 4116–4126.
H. Y. Zang, Y. Q. Lan, G. S. Yang, X. L. Wang, K. Z. Shao, G. J. Xu, and Z. M. Su (2010). CrystEngComm 12, 434–445.
H. Y. Liu, H. Wu, J. Yang, Y. Y. Liu, B. Liu, Y. Y. Liu, and J. F. Ma (2011). Cryst. Growth Des. 11, 2920–2927.
A. X. Tian, X. J. Liu, G. Y. Liu, J. Ying, and X. L. Wang (2012). Z. Anorg. Allg. Chem. 638, 141–145.
L. Yang, Y. Shen, Y. Z. Chen, X. Pan, X. L. Wang, and X. Wang (2019). Inorg. Chem. Commun. 108, 107493.
H. J. Du, C. H. Wang, Y. Li, Y. Y. Niu, and H. W. Hou (2015). RSC Adv. 5, 74065–74074.
H. L. Li, B. Shao, Y. Y. Li, L. J. Chen, and J. W. Zhao (2015). Inorg. Chem. Commun. 61, 68–72.
C. J. Zhang, H. J. Pang, Q. Tang, H. Y. Wang, and Y. G. Chen (2010). Dalton Trans. 39, 7993–7999.
X. Xu, W. W. Ju, W. T. Hou, D. R. Zhu, and Y. Xu (2014). CrystEngComm 16, 82–88.
H. Y. Liu, H. Wu, J. F. Ma, Y. Y. Liu, J. Yang, and J. C. Ma (2011). Dalton Trans. 40, 602–613.
A. X. Tian, J. N. Liu, X. B. Ji, G. Y. Liu, T. T. Li, Y. Tian, H. P. Ni, G. C. Liu, and J. Ying (2018). J. Mol. Struct. 1155, 371–379.
X. Pan, X. Wang, X. L. Wang, G. C. Liu, H. Y. Lin, and Y. Li (2019). Inorg. Chim. Acta 495, 118998.
X. L. Wang, X. Pan, X. Wang, G. C. Liu, H. Y. Lin, and S. Zhang (2019). Transit. Met. Chem. 44, 207–217.
G. M. Sheldrick, SHELXTL NT Version 5.1. Program for Solution and Refinement of Crystal Structures (University of Göttingen, Germany, 1997).
I. D. Brown and D. Altermatt (1985). Acta Crystallogr. B 41, 244–247.
X. L. Hao, Y. Y. Ma, H. Y. Zang, Y. H. Wang, Y. G. Li, and E. B. Wang (2015). Chem. Eur. J. 21, 3778–3784.
D. Dutta, M. Dolai, S. Biswas, A. Dutta, and M. Ali (2020). Polyhedron 176, 114204.
X. L. Hao, Y. Y. Ma, W. Z. Zhou, H. Y. Zang, Y. H. Wang, and Y. G. Li (2014). Chem. Asian J. 9, 3633–3640.
X. L. Wang, D. N. Liu, H. Y. Lin, G. C. Liu, N. Han, J. Luan, and Z. H. Chang (2015). RSC Adv. 5, 56687–56696.
X. L. Wang, N. Han, H. Y. Lin, J. Luan, A. X. Tian, and D. N. Liu (2014). Inorg. Chim. Acta 421, 342–348.
Q. Li, Q. Zhang, L. Ding, D. D. Zhou, H. Cui, Z. B. Wei, and J. P. Zhai (2013). Chem. Eng. J. 217, 28–33.
D. D. Zhou, L. Ding, H. Cui, H. An, J. P. Zhai, and Q. Li (2012). Chem. Eng. J. 200–202, 32–38.
A. X. Tian, M. L. Yang, N. Sun, Y. B. Fu, and J. Ying (2018). Polyhedron 155, 337–350.
Z. F. Li, J. H. Chen, D. W. Pan, W. Y. Tao, L. H. Nie, and S. Z. Yao (2006). Electrochim. Acta 51, 4255–4261.
A. X. Tian, J. N. Liu, T. T. Li, Y. Tian, G. Y. Liu, and J. Ying (2018). CrystEngComm 20, 2940–2951.
B. X. Dong, F. Y. Bu, Y. C. Wu, J. Zhao, Y. L. Teng, W. L. Liu, and Z. W. Li (2017). Cryst. Growth Des. 17, 5309–5317.
B. X. Dong, H. B. Chen, Y. C. Wu, J. Zhao, Y. L. Teng, W. L. Liu, and Z. W. Li (2017). Dalton Trans. 46, 14286–14292.
A. Balamurugan and S. M. Chen (2007). Electroanal. 19, 1616–1622.
S. S. Hassan, Y. P. Liu, Sirajuddin, A. R. Solangi, A. M. Bond, and J. Zhang (2013). Anal. Chim. Acta 803, 41–46.
M. Skunik and P. J. Kulesza (2009). Anal. Chim. Acta 631, 153–160.
M. R. Gao, M. K. Y. Chan, and Y. G. Sun (2015). Nat. Commun. 6, 7493–7500.
Z. H. Wei, Y. Liu, Z. K. Peng, H. Q. Song, Z. Y. Liu, B. Z. Liu, B. J. Li, B. Yang, and S. Y. Lu (2019). ACS Sustainable Chem. Eng. 7, 7014–7023.
J. S. Qin, D. Y. Du, W. Guan, X. J. Bo, Y. F. Li, L. P. Guo, Z. M. Su, Y. Y. Wang, Y. Q. Lan, and H. C. Zhou (2015). J. Am. Chem. Soc. 137, 7169–7177.
L. Zhang, S. B. Li, C. J. Gomez-García, H. Y. Ma, C. J. Zhang, H. J. Pang, and B. N. Li (2018). ACS Appl. Mater. Interfaces 10, 31498–31504.
A. A. Ensafi, E. Heydari-Soureshjani, and B. Rezaei (2017). Int. J. Hydrogen Energy 42, 5026–5034.
R. N. Biboum, B. Keita, S. Franger, C. P. Nanseu Njiki, G. J. Zhang, J. Zhang, T. B. Liu, I. M. Mbomekalle, and L. Nadjo (2010). Materials 3, 741−754.
Q. B. Shen, C. J. Zhang, M. Wang, H. J. Pang, H. Y. Ma, X. M. Wang, L. C. Tan, D. F. Chai, Y. Hou, and B. N. Li (2019). Inorg. Chem. Commun. 99, 64–69.
F. Y. Yu, Y. Gao, Z. L. Lang, Y. Y. Ma, L. Y. Yin, J. Du, H. Q. Tan, Y. H. Wang, and Y. G. Li (2018). Nanoscale 10, 6080–6087.
Acknowledgements
The work is supported by the National Natural Science Foundation of China (21671169), Six Talent Peaks Project in Jiangsu Province (No. 2017-XNY-043), and the projects funded by the High-Level Personnel Support Program of Yang-Zhou University, and the Priority Academic Program Development of Jiangsu Higher Education Institutions.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Zheng, QH., Ding, YX., Chen, C. et al. Synthesis, Structure, and Electrocatalysis of a Novel Compound Based on [β-Mo8O26]4− Cluster and [NiN4O2]2+ Secondary Building Unit. J Clust Sci 33, 1613–1621 (2022). https://doi.org/10.1007/s10876-021-02082-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10876-021-02082-9