Facile preparation of glycine-based mesoporous graphitic carbons with embedded cobalt nanoparticles

A simple route has been developed for the preparation of mesoporous graphitic carbons with embedded cobalt nanoparticles just using glycine as a nitrogen source, cobalt nitrate and distilled water. After heating the mixture to 300 °C under magnetic stirring, a dry solid product was obtained, which was then carbonized at 900 ºC under argon atmosphere. Changing the glycine/Co molar ratio allowed controlling the size of the cobalt particles and their dispersion in the carbon matrix, the porosity of the carbon and its graphitic character. The carbon–metal composites obtained were tested as oxygen cathodes in Li–O2 batteries. Cells assembled exhibited a full discharge capacity up to 2.19 mAh cm−2 at a current of 0.05 mA cm−2 and over 39 cycles at a cutoff capacity of 0.5 mAh cm−2. This work provides a green, feasible and simple way to prepare mesoporous graphitic carbons with embedded cobalt nanoparticles without involving templates.


GRAPHICAL ABSTRACT Introduction
In the global challenge of developing more efficient and ecofriendly energy systems, lithium-ion batteries have historically attracted the greatest interest, but today searching for higher energy density, a series of batteries known as ''new generation batteries'' are emerging. Among them lithium-oxygen battery  ) stands out in terms of its energy density [1,2]. In recent years, the study of various aspects of the nonaqueous Li-O 2 battery has been intensified, covering the stability of the electrolytes, solvents, cathode materials used and the problems derived from the charge/discharge reversibility of the battery (specially the oxidation of ORR products). During the discharge process, O 2 is reduced by a series of mechanisms strongly dependent on current density [3], solvent [4] and nature of the cathode [5] until it forms (mainly) insoluble and insulating Li 2 O 2 [6]. However, the loss of capacity and the low cyclability that these batteries present is due to the oxygen species [7,8] produced in the oxygen reduction and evolution reactions, which are highly reactive and produce parasitic reactions, which decompose the components of the cell [9] such as the cathode [10] and the electrolyte [11].
Without any doubt, one of the most important aspects to developing a Li-O 2 battery is the oxygen cathode. For a Li-O 2 battery, this must fulfill a series of requirements, such as high oxygen permeability, excellent conductivity and catalysis of the oxygen redox reaction. Several non-carbonaceous materials are currently being studied to be used as cathodes [12,13]. Nonetheless, carbon-based materials remain the most studied materials for cathode application in Li-O 2 batteries, in spite of having many known issues [5].
The known catalytic effect of cobalt has been introduced in Li-O 2 batteries as redox mediators [14,15], carbon-free cathodes [16,17] and carbon cathodes [18,19]. Among the latter, porous carbons with embedded cobalt and cobalt oxide nanoparticles have been widely investigated in the field of energy conversion and storage: lithium-ion batteries [20,21] lithium-sulfur batteries [22,23] and Li-O 2 batteries [24,25]; these last were mainly motivated by their ORR and OER catalytic activity [26]. In fact, it has been reported that Co nanoparticles embedded in carbon nanostructures can reduce the charge and discharge polarization of Li-O 2 batteries extending its lifetime [27]. Indeed, it can also reduce the charge overvoltage by forming easily decomposable amorphous Li 2 O 2 [27].
Several methods have been already proposed for synthesizing Co/porous carbons composites employing numerous carbon precursors, cobalt sources and experimental methods (see Table S1 in Supplementary material). Most of these methods suffer from need of expensive organic precursors (such as cobalt acetylacetonate and potassium hexacyanocobaltate), complicated processing (such as silica, or carbonates as templates) and careful washing. The table below summarizes the strategies used to obtain the Co-carbon composites used for oxygen redox.
Taking into account all the above, in search of a simpler and more sustainable route, we report herein a synthesis process to prepare mesoporous graphitic carbons with embedded cobalt particles to be used as cathodes in Li-O 2 batteries. The synthesis involved the use of commercial glycine, cobalt nitrate and distilled water. Glycine has been used elsewhere as a reducing fuel for the synthesis of ultraporous metals by a simple combustion reaction [28]. We performed an extensive composition and morphology characterization of these materials, named GX-Co-T (where X represents the glycine amount in the molar ratio G/CoN), and we studied the electrochemical properties. Both the morphological characteristics and the electrochemical behavior of the materials strongly varied depending on the preparation conditions and the amount of Co added. Cells assembled with G6-Co-T delivered a full discharge capacity up to 2.19 mAh cm -2 at a current of 0.05 mAh cm -2 over 39 cycles without any capacity loss at a cutoff capacity of 0.5 mAh cm -2 .

Synthesis of MGC-Co
Mesoporous graphitic carbons with embedded cobalt nanoparticles (MGC-Co) were prepared by using a two-step simple method with commercial powdered glycine (glycine for synthesis, CAS number 56-40-6, Sigma-Aldrich) and cobalt (II) nitrate hexahydrate (CoN, Co(NO 3 ) 2 Á 6H 2 O, ACS reagent, C 98%, CAS 10026-22-9, Sigma-Aldrich). The schematic illustration of the synthesis is shown in Scheme 1. Briefly, glycine powder was dissolved in deionized water under stirring using a PYREXÒ beaker. Subsequently, an amount of CoN was added to the previous solution until it was completely dissolved. Glycine/CoN molar ratios employed are shown in Table S2. Then, the solution was heated up to 300°C within the same beaker on a digital hot plate stirrer until a brown dark residue was developed, and the release of vapors ended. This step ensured a good dispersion of nitrates in the matrix of the carbon precursor. The nitrogen-rich, thermally decomposed glycine (N-rich TDG) obtained was cooled at room temperature and subsequently carbonized in a tubular furnace at 900°C under Ar atmosphere for 1 h using a heating rate of 10°C/min. Before characterization, the carbonized products were grinded in an agate mortar and sieved through a 180-mesh. The average carbon yield was around 15 wt.% MGC-Co and was labeled as GX-Co-T, where X represents the glycine amount in the molar ratio G/CoN. For comparison purposes, carbonized glycine (G-T) at 900 8C was also prepared as a bare sample. An overview of the samples prepared is provided in Table S2, which also includes the respective Co contents calculated from the ash residues of thermal gravimetry in air (see below for conditions).

Materials characterization
Thermogravimetric analysis (TGA) was carried out with a simultaneous thermogravimetric analysis (TG)-differential scanning calorimetry/differential thermal analysis (heat flow DSC /DTA) system NETZSCH-STA 449 F1 Jupiter. The amount of cobalt incorporated in the carbon materials was analyzed by thermogravimetry from 25 to 900°C at a heating rate of 5 8C/min under flowing air (80 mL/min). N 2 adsorption/desorption experiments were performed at -196°C using a Micromeritics ASAP 2020 equipment. Specific surface areas, S BET , were determined by the Brunauer-Emmett-Teller (BET) method. Micropore volumes (V mi ) and external surface areas (S ext ) were determined by the t-plot method. Total pore volume (V T ) was estimated by the Gurvitsch's rule as the amount adsorbed at a relative pressure of P/P 0 = 0.995. Pore size distributions (PSDs) were estimated from the adsorption branches of the isotherms by the Barrett-Joyner-Halenda (BJH) model. TEM studies were performed with a JEOL (JEM1210) instrument, operating at 100 keV. Before examination, the samples were dispersed in anhydrous ethanol and deposited on a holey carbon film on a copper grid. X-ray diffraction (XRD) patterns at small and wide angles were obtained on a Siemens D5000 instrument operating at 40 kV and 20 mA, using Cu-Ka radiation (l = 0.15406 nm). X-ray photoelectron spectroscopy (XPS) measurements were carried out using a SPECS EA10P hemispherical analyzer using a 300 W non-monochromatic X-ray source (Al Ka line with a photon energy of 1486.6 eV).

Electrochemical measurements
As carbon powders, the different MGC-Co samples synthesized here were used after grinding in a mortar and sieving through a 180-mesh. The method used for the preparation of carbonbinder composite electrodes was based on the common procedure in which a carbon powder is mixed with polyvinylidene fluoride (PVDF, Sigma-Aldrich) as a binder and carbon black (Super P, TIMCAL) in the mass ratio of 4:4:2 in N-methyl-2-pyrrolidone (NMP, Sigma-Aldrich, C 99.0%). The slurry obtained was used to impregnate a 10-mm-diameter carbon paper (Freudenberg H2315/H23) and finally dried at 80°C for 25 h. The electrode loading was of the order of 1 mg (* 1.3 mg cm -2 ). Li-O 2 battery used consisted of a Teflon homemade cell based on the Giessen battery design [29]. The electrolyte was prepared in a glovebox without exposure to air: 1 M lithium triflate (LiTf, Sigma-Aldrich, 99.995%) dissolved in diethylene glycol dimethyl ether (DEGDME, Sigma-Aldrich, 99.5%). The separator was a 12-mm-diameter glass fiber filter (filterLab MFV1, 260 lm thick) soaked with * 100 ll of electrolyte, the anode a 11-mm-diameter Li metal foil (Rockwood Lithium, 0.4 mm thick). All Li-O 2 cells were assembled in an argon-filled glove box. Once assembled, the cell was purged with dry pure oxygen for 60 s. Electrochemical tests, such as cyclic voltammetry and galvanostatic charge-discharge measurements, were performed using a MTI BST8-WA battery tester Biologic VMP3. All the tests were done at 25 8C.

Results and discussion
The literature data [30] indicate that glycine decomposes at temperatures between 220 and 280 8C into glycylglycine (dipeptide) and 2,5-piperazinedione. Among others, NH 3 , H 2 O and CO 2 gases evolve during the decomposition [30,31]. At the same time, cobalt nitrate can be reduced to CoO, N 2 O and H 2 O at around 242°C [30,32]. According to that, after this first heating step, the dark product obtained presumably is composed of a complex mixture of glycylglycine (dipeptide), 2,5-piperazinedione and CoO. On the other hand, during the carbonization up to 900 8C, the obtained solid product can decompose releasing CO 2 , HCNO, HCN [30] and NH 3 leading to a N-rich carbonaceous product at the end of the process. At the same time, the carbothermal reduction reaction of CoO to elemental metal occurs at temperatures higher than 800°C [33] resulting in particles of cobalt embedded in the N-rich carbon matrix. Additionally, these metal particles that emerged could act as catalysts for the conversion of amorphous carbon into more ordered or graphitic carbon [34]. The morphology and structure of samples observed by TEM analysis are shown in Fig. 1. TEM image of carbonized glycine (G-T) revealed a carbonaceous material with a dense structure with low porosity. GX-Co-T samples showed clearly embedded cobalt particles within carbon matrix, the sizes and distributions of which are function of G/CoN molar ratio. In addition, all these samples revealed to have certain porosity which are also dependent on cobalt nitrate loading employed during synthesis. For lower G/CoN molar ratios (samples G144-Co-T and G72-Co-T), cobalt particles showed good dispersion and poor agglomeration in the carbon matrix, being the mean Co particle diameter in the range of 50-200 nm. On the other hand, TEM images of samples G36-Co-T, G16-Co-T and G6-Co-T revealed that an increase in the cobalt loading to values higher than 16 wt.% induced the formation of larger cobalt particles (up to about 500 nm) that did not disperse uniformly on the carbon matrix due to a clear agglomeration. Figure 2a-b shows the N 2 sorption isotherms and the corresponding BJH pore size distributions (PSDs) of GX-Co-T samples. Pristine carbon obtained directly from the carbonization of glycine (G-T) was mainly a microporous carbon that shows a type I isotherm. Nevertheless, the addition of CoN influenced the mesostructuration of final products changing their isotherms shape to type II with associated H3-type hysteresis loop that according to the IUPAC classification indicates the presence of non-rigid aggregates of plate-like particles or assemblies of slit-shaped mesopores [35].
According to textural data calculated from N 2 isotherms (see Table S3), a total pore volume (V T ) maximum is observed with the G36-Co-T (16 wt.% Co), with a V T 2.3 times compared to pristine carbon G-T. For higher amounts of the experimentally determined Co (and thus of the porogen nitrate precursor), V T gradually decreased, possibly associated with the high density of Co content and structural degradation (see Fig. 2c). Samples G6-Co-T and G36-Co-T showed clear mesoporous structures compared to pristine carbon. Ordered mesoporous carbons with embedded cobalt nanoparticles made by a novel one-pot laser-assisted approach were reported recently by Chimbeau et al. [35].
The structures of the pristine carbon (G-T) and Codoped carbons were analyzed by XRD. XRD patterns of samples are shown in Fig. 2d. Sample G-T only presents a weak and broad reflection at around 24°c orresponding to the (0 0 2) plane of carbon [36,37], which indicates a still highly amorphous nature after the thermal treatment. On the other hand, samples prepared using cobalt nitrate showed a diffraction peak at 2h = 44.28 and 51.58 corresponding to (1 1 1) and (2 0 0) crystal planes of metallic cubic cobalt, respectively. On the other hand, traces of CoO can be also observed due to the oxidation of cobalt particles upon to exposure of air at room temperature [38]. In Fig. 2d, it can be appreciated how the (0 0 2) carbon peak becomes increasingly sharper even when the proportion of cobalt in the sample is small. These facts corroborate that, as previously reported [34], the formation of metal particles (e.g., Fe, Co and Ni) during carbonization can act as graphitization catalysts at relatively low temperatures. Note that in an uncatalyzed reaction the graphitization process occurs at temperatures above 2000 8C [39].
The XPS spectra in Figure S1 and Fig. 3 show the surface composition of representative samples, which can be qualitatively related to their bulk composition. GT pristine carbon presents a set of peaks corresponding to C 1s (285 eV), N 1s (401 eV) and O 1s (532 eV). Thus, the product obtained directly from the carbonization of glycine (at 900 8C) appears particularly N enriched. C 1 s spectrum can be mainly divided into C-C/C= C (284 eV), C-N (285 eV), C-O (286 eV) and O-C =O (289 eV) [40], which confirms that the carbon is bonded to nitrogen and some oxygen groups. Similarly, the high-resolution N 1 s spectrum can be deconvoluted into pyridinic-N (398 eV), Co-N x (399 eV), pyrrolic N (400 eV), graphitic N (401 eV) and oxidized N (402 eV) [41,42]. It is known that pyridinic N and Co-N x species play an important role for ORR and OER [43]. The total of pyridinic N and Co-N x of G6-Co-T (37%) is higher than that of G-T (21%) or G36-Co-T (26%) (Table S4). Meanwhile, XPS spectra of samples obtained using cobalt nitrate exhibit in addition new peaks, corresponding to Co(0), Co(II), Co-N x and the shakeup satellite peaks [44]. In addition, the O 1s spectra also prove the existence of cobalt oxide. The dominant existence of surface Co 2? oxides in the XPS analysis can be attributed to the thin CoO layer shell formed by the exposure of cobalt particles to ambient air [38] given the XPS surface sensitivity.
Cyclic voltammetry (CV) was applied to investigate the electrocatalytic activities of selected Cobased carbons and G-T within the voltage range of 2.0-4.5 V (Fig. 4a). All cathodes exhibit a reduction and an oxidation peak, respectively, ascribed to the formation of Li 2 O 2 and the decomposition of Li 2 O 2, respectively [45]. It is worth noticing that G6-Co-T shows larger ORR and OER peak current than G-T and G36-Co-T, implying its superior ORR and OER activity. Figure 6b shows discharge curves of Li-O 2 batteries at 0.05 mA cm -2 . The discharge capacity of G6-Co-T electrode (2.19 mAh cm -2 ) is much higher than that of G-T electrode (1.38 mAh cm -2 ) and G36-Co-T electrode (1.42 mAh cm -2 ) consistent with what is expected from the results of the CV. The excellent performance of G6-Co-T electrode can be attributed to its higher pyridinic N and Co-N x content, providing more active sites for ORR [43], facilitating the formation and better distribution of the discharge products [46].   The cycling performance of the cathode with G-6, G6-Co-T and G36-Co-T was evaluated with the limited capacity of 0.5 mAh cm -2 at the current density 0.05 mA cm -2 (Fig. 4c). G6-Co-T cathode presents an improved cycle stability, proving once again the benefit of this over the other tested materials. There is an evident improvement on the discharge potential between GT and G36-Co-T. Here, the 2.3 times larger total pore volume may allow maintaining electrochemically active surface area, even though clogging occurs finally after discharging a similar capacity. However, when the percentage of Co increases to 67%, the increase in discharge capacity obtained is very evident (more than 50%). Note that in this case, the pore volume is approximately the same (0.13*0.14 cm 3 g -1 ), which justifies that the catalytic effect of the cobalt, together with pyridine nitrogen content added to the increase in the carbon graphitic character, has a more positive effect on the battery discharge than the total pore volume. This catalytic effect could imply a modified discharge mechanism that promotes a more homogeneous distribution of precipitate, which at the same time improves its removal, as confirmed by the enhanced anodic current above 3.2 V vs. Li (Fig. 4a), and by the improved cycle life. The discharge capacity and cycle life of G6-Co-T are comparable to several recently reported cathodes for Li-O 2 batteries (Table S5).

Conclusions
A novel and straightforward synthetic procedure is presented here allowing to produce N-enriched mesoporous graphitic carbon materials embedded with cobalt nanoparticles. This material makes use of the porous structure of a carbon with a high degree of graphitization and also takes the advantage of both catalytic effects of the N and the Co. Li-O 2 cells assembled with G6-Co-T electrode (Co = 67%) exhibited a full discharge capacity up to 2.19 mAh cm -2 at a current of 0.05 mAh cm -2 and cycle stability for over 39 cycles without capacity loss at a cutoff capacity of 0.5 mAh cm -2 .
The reported route is very simple and avoids the problem of residual templates after the reaction, consequently, eliminates the use of strong acids (i.e., HF) to remove the template. For the fact of not using even a wash of the final product, the waste generation is almost absent. In addition, glycine is an abundant and inexpensive raw material in the chemical industry. Carbon obtained directly from the carbonization of glycine was mainly a microporous carbon with low degree of graphitization but significant N content. However, the addition of cobalt nitrate influenced significantly the structure of final products turning it mesoporous. It is important to mention that even with a low proportion of cobalt a high degree of graphitization at low temperature could be reached. Both the porosity and the Co content could be adjusted with the initial ratio of the reagent concentration. For these reasons, this synthetic route can be considered not only economic but also green and eco-friendly. EXP, RTI2018-096273-B-I00, RTI2018-3097753-B-I00, with FEDER co-funding, the CSIC program for the Spanish Recovery, Transformation and Resilience Plan ''Plataforma Temática Interdisciplinar Transició n Energética Sostenible? (PTI-TRANSENER ?)'' funded by the Recovery and Resilience Facility of the European Union, established by the Regulation (EU) 2020/2094. The authors also acknowledge the Generalitat de Catalunya (2017SGR1687). W.W. gratefully acknowledges the support from the China Scholarship Council (CSC No.:201808340076). This work has been performed within the framework of the doctoral program in materials science of UAB (W. W.).

Funding
Open Access funding provided thanks to the CRUE-CSIC agreement with Springer Nature.

Declarations
Conflict of interest The authors declared that they have no conflict of interest.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licen ses/by/4.0/.