Optimization of the regioselective synthesis of mixed cellulose 3,5-dimethylphenyl and α-phenylethyl carbamate selectors as separation phases for chiral HPLC

Regioselective tritylation and carbonate aminolysis were employed in this work to synthesize cellulose 2,3-bis(3,5-dimethylphenyl carbamate)-6-(α-phenylethyl carbamate)-type chiral selectors. We evaluated and optimized the critical aspects of regioselective tritylation and detritylation at C6 of the glucopyranose units of the polysaccharide backbone. The advantage of using cellulose II in comparison to cellulose I for tritylation was analyzed and the detritylation time was determined by a fast and simple thin-layer chromatography method. Optimization of both tritylation and detritylation was accompanied by a combination of analytical techniques. Oxycarbonylation with phenyl chloroformate was used to introduce a reactive phenyl carbonate moiety at C6 of the intermediate cellulose 2,3-bis(3,5-dimethylphenyl carbamate), which was subsequently converted to the respective cellulose 6-(α-phenylethyl carbamate) derivative by aminolysis with enantiopure (R)- or (S)-α-phenylethylamine. The starting material, intermediates, and target cellulose derivatives were comprehensively analytically characterized by ATR-FTIR, solid- and liquid-state 13C NMR, GPC, and elemental analysis. With the optimized protocol, it became possible to obtain cellulose carbamate-type chiral selectors through carbonate aminolysis with simple and commercially available primary amines instead of reaction with isocyanate reagents. The enantioseparation performance of the obtained chiral selectors was evaluated against cellulose tris(3,5-dimethylphenyl carbamate) as a reference selector with a selection of chiral analytes.


Introduction
High-performance liquid chromatography (HPLC) on chiral stationary phases (CSPs) is one of the most powerful techniques for the direct separation of enantiomeric compounds, or generally, stereoisomers, both on analytical and preparative scales (Ahuja 1997;Subramanian 2008). Polysaccharide derivatives are the most versatile chiral selectors (CSs) due to their superior chiral recognition ability in comparison to other macromolecular selectors, such as proteins, macrocyclic polyethers, macrocyclic antibiotics, etc. (Teixeira et al. 2019). In the 1980s, Okamoto et al. successfully introduced polysaccharide derivatives for enantioseparation by HPLC and a number of polysaccharide derivatives carrying different substituents have been screened since then Chankvetadze 2020;Wang et al. 2021), e.g., aryl and alkyl carbamates, alkyl esters, benzoates, and cycloalkyl substituents (Chankvetadze 2012). Among them, polysaccharide phenyl carbamates and benzoates were shown to be the most powerful (Minguillón et al. 1996;Fanali et al. 2019). Up to 90% of the tested enantiomeric compounds could be separated by these polysaccharide derivative-based CSs (Ikai and Okamoto 2009;Shen and Okamoto 2016;Yin et al. 2019a). Amylose and cellulose are the most common polysaccharide matrices for CSs (Okamoto et al. 1986;Okamoto et al. 1998;Okamoto 2009;Ali et al. 2009;Shen and Okamoto 2016), but also chitosan and chitin are being used (Ribeiro et al. 2017). Hetero-substituted polysaccharides (such with different moieties) were shown to possess, in certain cases, even higher chiral discrimination than their homosubstituted counterparts (Acemoglu et al. 1998;Felix 2001;Katoh et al. 2011;Yin et al. 2019b).
One central part of the regioselective synthesis of such hetero-substituted cellulose derivatives is the use of, e.g., trityl protecting groups for C6-OH (Kaida and Okamoto 1993) as it allows regioselective distinction of this hydroxy group from those in C2-and C3-positions. This strategy has been applied to generate a series of hetero-substituted polysaccharide derivatives as CSs (Chassaing et al. 1996;Chassaing et al. 1997;Zheng et al. 2009;Shen et al. 2018). Heterogeneous tritylation of regenerated cellulose (= cellulose II) obtained by deacetylation of cellulose acetate (Hearon et al. 1943b) or homogenous tritylation of celluloses in a mixture of N,N-dimethylacetamide (DMAc)/LiCl/pyridine at 80 °C have been used to yield cellulose derivatives with high DS (Gömez et al. 1996;Shen et al. 2018;Ganske and Heinze 2018). The degradation of cellulose in the mixture of DMAc/LiCl at elevated temperatures needs to be considered here (Potthast et al. 2002;Chrapava et al. 2003).
Tritylation of mercerized and regenerated celluloses in pyridine as a reaction medium has also been described (Kern et al. 2000;Li et al. 2008). Recently, also ionic liquids were exploited as the reaction media for homogeneous tritylation (Erdmenger et al. 2007;Granström et al. 2008). With regard to later deprotection, treatment with concentrated aqueous HCl (Kaida and Okamoto 1993;Kern et al. 2000;Li et al. 2008;Shen et al. 2018) or gaseous HCl (Acemoglu et al. 1998) are the most common methods to cleave off the protecting group. Also here, cellulose degradation by hydrolytic cleavage of the glycosidic bonds under strongly acidic conditions has to be taken into account (Kontturi et al. 2016).
The substituent at C6 of the glucopyranose units of the polysaccharide backbone was shown to have a significant influence on the overall chiral recognition (Kaida and Okamoto 1993;Chassaing et al. 1996;Acemoglu et al. 1998;Felix 2001). Besides the substituents and their pattern, the enantioseparation performance of a certain CS significantly depends on the nature of the polysaccharide, its degree of polymerization (DP) (Okada et al. 2016;Zhang et al. 2020), the amount of selector coated onto the silica support, and the used coating/immobilization procedures (Yashima et al. 1996;Wei et al. 2019). Evidently, there is also an influence of the dimensions of the silica gel (Yashima et al. 1996;Qin et al. 2010;Bezhitashvili et al. 2017;Kohout et al. 2019), the analytes, and of course the HPLC conditions (Yashima et al. 1996;Bui et al. 2021) as it is also in non-chiral separations.
Carbonate aminolysis was shown to be an efficient path towards the introduction of carbamate functionalities onto cellulose (Elschner et al. 2013;Ganske and Heinze 2018;Bui et al. 2022c), besides the routinely used isocyanate chemistry (Hearon et al. 1943a;Hearon et al. 1943c;Heard and Suedee 1996;Khan et al. 2008;Labafzadeh et al. 2014). However, the former way offers higher flexibility due to the greater availability of amines compared to the rather limited choice of available isocyanates. Different phenyl chloroformates have been evaluated as reagents for cellulose aryl carbonate synthesis (Ganske and Heinze 2018;Bui et al. 2022c), which were shown to be more reactive than the respective alkyl carbonates (Elschner and Heinze 2015). For details on carbonate aminolysis for obtaining cellulose carbamates see the comprehensive studies by Heinze et al. and others (Pourjavadi et al. 2011;Elschner et al. 2013;Elschner and Heinze 2015;Ganske and Heinze 2018;Bui et al. 2022c).
In the present work, we describe the regioselective synthesis and testing of hetero-substituted mixed cellulose 3,5-dimethylphenyl and α-phenylethyl carbamate chiral selectors with a special focus on the critical aspects of tritylation and detritylation.

Instrumentation
Solid-state 13 C CP/MAS (12 kHz) and liquid-state 13 C NMR experiments were carried out on Avance III HD and Avance II 400 instruments (Bruker, Rheinstetten, Germany) with resonance frequencies of 100.68 MHz and 100.62 MHz, respectively. Data processing was performed with TopSpin 3.6.2 and ACD/ NMR Processor Academic Edition 12.01 software. Chemical shifts (δ) are given in ppm. ATR-FTIR spectra were recorded on a Frontier IR Single-Range spectrometer (PerkinElmer, Waltham, Massachusetts, US) equipped with a diamond/ZnSe crystal, LiTaO 3 detector, and KBr windows. FTIR spectra were evaluated using SpectraGryph software (version v1.2.15). UV/Vis measurements were carried out on a Perki-nElmer Lambda 35 spectrophotometer (PerkinElmer, Waltham, Massachusetts, US). GPC analyses were performed according to a standard procedure (Henniges et al. 2011;Jusner et al. 2022).
An Agilent Technologies, Inc. (Santa Clara, CA, USA) 1100 HPLC apparatus equipped with a quaternary pump (G1311A), autosampler (G1313A), TCC (G1316A), and DAD (G1315A) was used to evaluate the enantioseparation performance of the chiral columns. OpenLab CDS software (Agilent) was used for chromatographic data processing and evaluation.
Elemental analyses were carried out at the microanalytical laboratory of the University of Vienna on a EURO EA 3000 CHNS-O instrument (HEKAtech, Wegberg, Germany) with halide contents being determined by argentometry.

General information
In the case of the homogeneous reactions, the reactants were slowly added after the cellulose derivatives have been intensively mixed with the respective organic solvent mixtures at room temperature (RT) until a clear solution was formed. All reactions were performed under an inert atmosphere of dry nitrogen at the specified conditions. The precipitation of the crude products, vacuum filtration, and washing steps were repeated several times. Deionized water was used for washing. The purified cellulose derivatives were dried in a vacuum oven at 40 °C for at least 2 days before use. Any further variations or additional steps are described below.

Synthesis of the CSs 6R and 6S
Cellulose II preparation The cellulose II allomorph was prepared based on the protocols of Li et al. (2008), Kern et al. (2000) with modifications. MCC (10 g) was dispersed and vigorously stirred in 25% aq. NaOH (180 mL) in a closed vessel at RT for 48 h. The mixture was then added to EtOH (240 mL) and stirred for 1 h. Cellulose II was collected by vacuum filtration and washed with a large excess of EtOH. Immersion in EtOH and filtration/washing were repeated. Cellulose II was collected by vacuum filtration, washed with a large excess of distilled water for quantitative removal of residual NaOH until neutral and dried in a vacuum oven at 40 °C for 2 days.

Synthesis of cellulose 6-(4-methoxytrityl ether)
2 Dried cellulose II (7 g) was immersed and vigorously stirred in anhydrous pyridine (140 mL). The suspension was stirred at 100 °C for 8 h. A solution of 4-methoxytrityl chloride (2.5 molar eq. relative to the glucopyranose repeating units of cellulose) in anhydrous pyridine (112 mL) was slowly added. The mixture was stirred at 100 °C for 14 h, and the clear, yellowish solution was allowed to cool to RT. A large excess of EtOH was used to precipitate crude cellulose derivative 2, which was collected by vacuum filtration, washed with a large excess of EtOH, and distilled water (two times each) and dried at 40 °C in a vacuum oven for 2 days. The crude product was purified by redissolution in pyridine, reprecipitation, filtration, and washing as described above. Yield: 18.07 g, 96 wt%.

Synthesis of cellulose 2,3-bis(3,5-dimethylphenyl carbamate)-6-(4-methoxytrityl ether) 3
Cellulose derivative 2 (15 g) was dissolved in anhydrous pyridine (150 mL). 3,5-Dimethylphenyl isocyanate (4 molar eq. relative to the repeating units of cellulose derivative 2) was added dropwise and the mixture was stirred at 110 °C for 18 h. The solution was allowed to cool to RT. The crude cellulose derivative 3 was precipitated in a large excess of EtOH and collected by vacuum filtration. The filter cake was washed with a large excess of EtOH and distilled water (two times each). The material was dried at 40 °C in a vacuum oven for 2 days and further purified by redissolution in pyridine, reprecipitation, filtration, and washing as described above. Yield: 24.54 g, 98 wt%.

Synthesis of cellulose 2,3-bis(3,5-dimethylphenyl carbamate) 4
Homogeneous detritylation was performed according to the protocols of Li et al. (2008) and Kern et al. (2000) with modifications. Cellulose derivative 3 (14 g) was dissolved in THF (280 mL). A mixture of concentrated aq. HCl (37 wt%, 63 mL) and THF (980 mL) was slowly added and the mixture was stirred at RT for 4 h. The reaction was then quenched by the addition of solid Na 2 CO 3 /K 2 CO 3 until pH 7. Any formed salt was separated by vacuum filtration through a sintered glass frit. The THF in the filtrate was evaporated for the most part by rotary evaporation under reduced pressure. The crude cellulose derivative 4 was precipitated in a large excess of EtOH and collected by vacuum filtration, washed with a large excess of EtOH and distilled water (two times each), and dried at 40 °C in a vacuum oven for 2 days. The purification procedure was repeated after redissolution in THF. Yield: 8.34 g, 95 wt%.
Synthesis of cellulose 2,3-bis(3,5-dimethylphenyl carbamate)-6-(phenyl carbonate) 5 Cellulose derivative 4 (7 g) was dissolved in a mixture of anhydrous DMAc and pyridine (140 mL, 9:1, v/v). The solution was cooled to 0 °C by an ice/water bath. Phenyl chloroformate (2 molar eq. relative to the repeating units of cellulose derivative 4) was added dropwise. The reaction mixture was stirred for 12 h at 0 °C. A large excess of EtOH was employed to precipitate crude compound 5, which was collected by vacuum filtration, washed with a large excess of EtOH and distilled water (two times each), and dried at 40 °C in a vacuum oven for 2 days. Further purification of cellulose derivative 5 was carried out by repeating the above sequence after redissolution in DMAc. Yield: 8.74 g, 99 wt%.
Synthesis of cellulose 2,3-bis(3,5-dimethylphenyl carbamate)-6-(R/S-α-phenylethyl carbamate) 6R and 6S The cellulose derivative 5 (2.5 g) was dissolved in anhydrous DMF (50 mL). Either (R)-(+)-αmethylbenzylamine or (S)-(−)-α-methylbenzylamine (5 molar eq. relative to the repeating units of cellulose derivative 5) was added dropwise, and the mixture was stirred at 50 °C for 24 h. The reaction mixture was allowed to cool to RT, and a large excess of EtOH was used to precipitate crude cellulose derivative 6R or 6S, which was then collected by vacuum filtration, washed with a large excess of EtOH and distilled water (two times each), and dried in a vacuum oven at 40 °C for 2 days. Purification of cellulose derivatives 6R and 6S was carried out by redissolution in DMF and repetition of the sequence above. Yields: 6R: 2.45 g, 94 wt%; 6S: 2.36 g, 90 wt%.

Synthesis of 3-aminopropyl-functionalized silica gel APS
Previously published procedures were adapted to synthesize 3-aminopropyl-functionalized silica gel (APS) as an inert carrier for the CSs (Engelhardt and Orth 1987;Yashima et al. 1996;Okada et al. 2016;Bui et al. 2022a). Silica gel (10 g) was immersed in toluene (200 mL) during mechanical stirring, and the mixture was dried by azeotropic distillation in a dry nitrogen atmosphere. After distilling off about half of the volume of toluene, the temperature of the suspension was reduced to 80 °C, and triethylamine (1 mL) was added as a catalyst, followed by the addition of (3-aminopropyl)triethoxysilane (APTES, 10 mL). The reaction mixture was mechanically stirred for 48 h. The suspension was then cooled to RT and the crude APS was collected by vacuum filtration through a sintered glass frit (DURAN®, porosity 4), washed with hot toluene (100 mL), EtOH (100 mL), and with distilled water (two times each with 200 mL). APS was then dried at 40 °C in a vacuum oven for 2 days. Yield: 9.96 g.
Vol:. (1234567890) Silica coating and column packing The coating amount of each CS (1, 6R, and 6S) on APS was 20 wt% (Zhang and Francotte 1995). The coating was performed according to a previously published protocol (Bui et al. 2022a). Column packing was carried out as described in Bui et al. (2022a, b).

Cellulose tris(3,5-dimethylphenyl carbamate) 1
The reference CS, i.e., cellulose tris(3,5-dimethylphenyl carbamate), was synthesized (see Fig. 1A) and analytically characterized by ATR-FTIR, solid-state 13 C NMR, GPC, and EA. The solid-state 13 C NMR spectra of cellulose derivative 1 versus the starting material (MCC) are shown in Fig. 2, the EA results of all reported cellulose derivatives are summarized in Table 1. The FTIR and solid-state 13 C NMR spectra of cellulose derivative 1 were in full agreement with literature data (Liu et al. 2013;Wei et al. 2019;Bui et al. 2022a;Bui et al. 2022b). Cellulose derivative 1 is a well-known CS in chiral HPLC column materials and has been commercialized by several companies. However, we had to synthesize this reference CS in-house to compensate for differences in silica gel dimensions, cellulose starting material, column dimensions, coating procedure, and packing procedure-allowing for a fairer comparison between this reference and the novel CSs 6R and 6S described in this work. The DS of 3,5-dimethylphenyl carbamate

Influence of the cellulose allomorph on the tritylation reaction
In preliminary experiments, we observed that the heterogeneous tritylation of microcrystalline cellulose (= cellulose I) was less successful due to the high crystallinity of the starting material. Therefore, either the crystallinity had to be significantly reduced, or a homogeneous reaction was needed. For decreasing crystallinity and increasing accessibility, we chose mercerization and the resulting formation of cellulose II over extensive milling, to avoid tribochemical side reactions and cellulose degradation (Revol et al. 1987). Instead of dissolving cellulose I (MCC) in DMAc/LiCl at high temperature and accompanying degradation issues during heating (Potthast et al. 2002;Chrapava et al. 2003), the obtained cellulose II allomorph was used as the alternative starting material for tritylation. Cellulose II was prepared according to the protocols of Li et al. (2008) and Kern et al. (2000) with adjustments towards the complete removal of NaOH. The material was characterized by solid-state 13 C NMR (see Fig. S1). In the solid-state 13 C NMR spectrum of cellulose II, the decrease in intensity of the resonance at 88.8 ppm assigned to the crystalline region at C4 indicated that the degree of crystallinity was significantly lower compared to the starting material (Park et al. 2009;Kim et al. 2013;Halonen et al. 2013;El-Kott et al. 2019).

Cellulose 6-(4-methoxytrityl ether) 2
Several tritylating reagents can be used to protect C6-OH of cellulose: 4,4′-dimethoxytriphenylmethyl chloride, 4-methoxytrityl chloride, and trityl chloride. The methoxy-substituted trityl chlorides were shown to have a higher reactivity in comparison to unsubstituted trityl chloride. Under otherwise similar reaction conditions, a DS of 0.96 was achieved during 4 h of reaction time with 4-methoxytrityl chloride as a reactant, whereas 24 h were required in the case of trityl chloride. Furthermore, the detritylation time in the case of the methoxy-substituted trityl ether groups was only 5.5 h, while about 100 h were required for unsubstituted trityl ether groups. 4,4′-Dimethoxytriphenylmethyl chloride was less regioselective than the other two other trityl chlorides (Heinze et al. 1994;Gömez et al. 1996).
For tritylation, any residual NaOH from mercerization needed to be removed to ensure a high yield of tritylation, fewer by-products, and a short reaction time. A treatment of cellulose II in pyridine at 100 °C for 8 h was applied to additionally swell the starting material before its reaction with 4-methoxytrityl chloride (Mantanis et al. 1995). Through this pretreatment, a comparably short reaction time (14 h) and high DS (0.98 by mean of UV/Vis measurement and 0.99 by EA, see also Supplementary Information) was achieved, which is an improvement compared to previously reported protocols (about 70-100 h) with DS of 0.97 and 0.93 (Kern et al. 2000;Li et al. 2008). The UV/Vis method to determine the DS of 4-methoxytrityl ether was modified based on the protocol of (Gömez et al. 1996) (see Method S1 in the Supplementary Information).
The FTIR and solid-state 13 C NMR spectra of cellulose derivative 2 versus cellulose II are shown in Figs. S2 and S3. The FTIR spectrum of cellulose derivative 2 was consistent with literature data (Kern et al. 2000;Erdmenger et al. 2007) showing a decrease in the intensity of OH bands at 3467 cm − 1 and the presence of bands assigned to the aromatic ring, especially the vibrations of CH 3 -O-Ph at 1507 and 1251 cm − 1 . In the solid-state 13 C NMR spectrum of cellulose derivative 2, the resonances of the aromatic ring at 158.5, 147.8, 141.2, 127.5, 113.6, the quaternary carbon (C7) at 86.1, and the O-CH 3 groups (C12) at 54.7 ppm confirmed successful tritylation. Cellulose derivative 2 was soluble in DMAc, DMF, 1,4-dioxane, THF, and acetone, which was also in agreement with the report of Gömez et al. (1996).

Cellulose 2,3-bis(3,5-dimethylphenyl carbamate)-6-(4-methoxytrityl ether) 3
Carbamoylation with isocyanates was employed to introduce 3,5-dimethylphenyl carbamate substituents at the free C2-and C3-OH groups of the glucopyranose units after tritylation/protection of C6-OH. The FTIR and solid-state 13 C NMR spectra of the corresponding cellulose derivative 3 versus 2 are shown in Figs. S4 and S5. The absence of OH bands around 3467 and the presence of amide (N-H) vibrations at 3395, carbonyl (C=O) vibrations at 1723, aromatic ring signals at 1613,1539,1447,836, and the C-O band at 1249 cm − 1 in the FTIR spectrum of cellulose derivative 3 indicated a successful reaction, supported by the solid-state 13 C NMR spectrum with the carbonyl group resonance (C17) at 151.9, CH 3 -Ph peak (C22) at 20.8, and aromatic carbon signals of 3,5-dimethylphenyl carbamate at 137.6 and 115.1 ppm. The DS of 3,5-dimethylphenyl carbamate calculated based on the N content of the EA results was 1.84 (92%).

Cellulose 2,3-bis(3,5-dimethylphenyl carbamate) 4
For subsequent detritylation, to liberate the protected C6-OH, different concentrations of HCl were suggested in the literature. The detritylation time had to be optimized and kept to a minimum, in order to limit cellulose degradation by acidic hydrolysis (Kontturi et al. 2016), and also (minor) decarbamoylation (Acemoglu et al. 1998). A homogeneous detritylation approach was used and the minimum reaction timewhich has not been specified in previous works-was determined by a simple and fast thin-layer chromatography (TLC) method based on a protocol by Gömez et al. (1996) (Method S2). The TLC chromatograms are shown in Fig. S6. After 4 h of detritylation, the yellow color of the 4-methoxytrityl cations disappeared at the starting point of the TLC plate, indicating that the detritylation has been completed.
The FTIR and solid-state 13 C NMR spectra of cellulose derivative 4 versus 3 are shown in Figs. S7 and S8, respectively. The absence of bands assigned to CH 3 -O-Ph of the 4-methoxytrityl ether at 1510, 1248, and the recurrence of OH bands at 3467 cm − 1 in the FTIR spectrum of cellulose derivative 4 supported the success of the detritylation. Also, the solid-state 13 C NMR spectrum of compound 4 showed a nearly complete absence of the 4-methoxytrityl group resonances (C11 at 158.8, C7 at 86.1, and C12 at 54.5 ppm), even though a minute peak of the O-CH 3 groups (C12 at 54.5 ppm) remained still visible (see Fig. S8), which indicated a minor number of 4-methoxytrityl groups still to be present. Therefore, a quantitative UV/Vis method was applied to determine the exact detritylation yield (Method S3), which was 96%, in agreement with the solid-state 13 C NMR result. The DS of 3,5-dimethylphenyl carbamate based on the N content was still 1.84 (92%) -so the homogeneous detritylation during 4 h evidently did not affect the carbamate substituents at C2 and C3.

Cellulose 2,3-bis(3,5-dimethyl phenyl carbamate)-6-(phenyl carbonate) 5
Cellulose derivative 5 was synthesized by oxycarbonylation of C6-OH of cellulose derivative 4 with phenyl chloroformate to prepare a precursor, which subsequently was to be converted into cellulose derivatives 6R and 6S by carbonate aminolysis. Phenyl chloroformate was chosen as a reagent due to its higher reactivity compared to p-nitrophenyl chloroformate (Bui et al. 2022c;Bui et al. 2022a). FTIR and solid-state 13 C NMR spectra of cellulose derivatives 5 versus 4 are shown in Fig. S9 and Fig. S10, respectively. The FTIR spectrum of cellulose derivative 5 again shows the absence of OH bands indicating full conversion of C6-OH. Also, the shift of the C=O band from 1723 (only carbamate vibrations) to 1747 (mixture of carbamate and carbonate), and an increase in the intensity of the C-O vibration at 1208 cm − 1 (carbamate and carbonate) indicated that oxycarbonylation was successful. In solid-state 13 C NMR, the additional resonances of C25 at 120.7 and C26 at 129.4 ppm, and the chemical shift of C6 moving from 61.4 to 67.2 ppm in the carbonate derivative are supportive as well (Bui et al. 2022a). The DS of phenyl carbonate was 0.97 (see Supplementary Information for the calculation).
Aromatic amines cannot be used for the aminolysis of the carbonates due to their insufficient nucleophilicity (Elschner et al. 2013). However, primary and even secondary alkyl amines, being bulkier but usually also more nucleophilic, can be used in this way for obtaining carbamates by aminolysis, instead of the limited array of conventional, commercially available isocyanates.
The FTIR spectra of cellulose derivatives 6R and 6S versus 5 are shown in Fig. S11 and Fig.  S12, respectively, and the corresponding solid-state 13 C NMR spectra in Fig. 3 and Fig. S13. The presence of a new band assigned to the N-H group at approx. 3390, the chemical shift of the C=O signal from 1747 (overlay of carbamate and carbonate vibrations) to approx. 1710 cm − 1 (only carbamate band), the decrease in the intensity of the C-O band at 1218 cm − 1 due to the loss of the phenyl carbonate moiety in the FTIR spectra of cellulose derivatives 6R and 6S support the expected structure, as do the additional resonances in the 13 C solid-state NMR spectra, assigned to C23 at 154.8, C30 at 144.4, C32 at 127.5, C28 at 50.8 + 43.9, and C29 at 26.0 ppm. Liquid-state 13 C NMR in pyridine-d5 as NMR solvent was also further employed to evaluate the chemical structure of cellulose derivatives 6R and 6S (see Figs. S14 and S15). Due to rotational isomerism at the amide bond, C28 appeared at two resonances at approx. 52 and 44 ppm in the solid-state 13 C NMR spectra, while there was only one signal at 52.0 ppm in the solution-state 13 C NMR spectra. Apparently, the rotational barrier was already overcome in solution at the measurement temperature (28.1 °C). The  Fig. 4) were used to exemplarily showcase the enantioseparation performance of the newly developed column materials (CSP6R and CSP6S) in comparison to a reference column (CSP1) and a commercial stationary phase (CHIRALCEL® OD). The last two were based on cellulose tris(3,5-dimethylphenyl carbamate) as a CS. The chromatographic retention index (k 1 ), selectivity (α), and resolution (R s ) data of the chiral analytes for all tested CSPs are summarized in Fig. 5 and Table S1. Exemplary HPLC chromatograms of the analytes b and d are shown in Fig. 6. All of the selected chiral analytes were (at least partially) separated on both CSP1 and CHIRAL-CEL® OD. Especially, the chiral analytes d, e, and f were baseline-separated with R s > 1.5, while the analytes a, b, and c were partly separated. The selectivity of CSP1 was higher than that of CHIRALCEL® OD for the chiral analytes a, b, c, e, and f, while the resolution on CHIRALCEL® OD was higher for analytes d and f. Overall, the resolution values of the reference CSP1 and the commercial column were quite comparable. The CHIRALCEL® OD column was used in this study as a benchmark column. However, differences in silica gel dimensions (10 vs. 7 μm) and column dimensions (250 × 4.6 vs. 150 × 4 mm) with respect to the in-house prepared material have to be considered, especially in terms of column efficiency.
Regarding the overall enantioseparation performance of CSP6R and CSP6S, all of the selected chiral analytes were at least partially separated with R s < 1.5 (see Fig. 5 and Table S1) except analyte f on CSP6S. Though the selectivity values (α) for all chiral analytes were rather similar, the resolution values of CSP6R were always higher than those of CSP6S. A somewhat higher resolution on CSP6R than on CSP1 was observed for chiral analytes a and b.

Conclusions and outlook
The critical synthetic aspects of tritylation and detritylation for obtaining hetero-substituted cellulose derivatives to be used as chiral selectors in HPLC after coating onto silica gel were thoroughly optimized. The benefit of using cellulose II as a starting material was also elaborated. In general, the newly developed CSPs have shown medium enantioseparation performance, although no clear trends can be identified at the moment and further evaluation with a bigger set of chiral analytes is necessary. Also, further tests with smaller silica particles and pore sizes for enhancing the column efficiency and overall resolution are needed (ongoing work) as well as the preparation of other CSs by using different chiral amines. The present work has laid the foundation for this endeavor, by providing an optimized synthesis methodology and improved protocols for tritylation/detritylation and cellulose carbonate aminolysis, which we hope will be found useful.