Investigating Periodic Table Interpolation for the Rational Design of Nanoalloy Catalysts for Green Hydrogen Production from Ammonia Decomposition

Developing highly active catalysts for the decomposition of ammonia to produce hydrogen is an important goal in the context of renewable energy. Allied with this is a need for identification strategies to efficiently design novel catalysts integral to ensuring rapid progress in this research field. We investigated the efficacy of N–binding energy and periodic table interpolation to predict active bimetallic nanoparticle catalysts. Supported iron-platinum and iron-palladium were identified and experimentally shown to be more active than their monometallic analogues. Atomic resolution electron microscopy indicated that the most active catalyst (5 wt% Fe 80 Pt 20 /γ-Al 2 O 3 ) was principally formed of alloyed nanoparticles. It restructured during testing, yet no activity loss was noted at 20 h time-on-line. While these findings show that periodic table interpolation may be a viable tool for identifying active combinations of metals, the activity of the catalysts in the current work were not able to outperform the Ru/Al 2 O 3 benchmark. Further catalyst optimization or refinement of reaction descriptors may facilitate the development of catalysts with higher intrinsic activity than the current state-of-the-art catalysts. Graphical Abstract


Introduction
Climate change is one of the greatest challenges of our time.It is directly responsible for numerous ecological disasters, such as coral bleaching and the melting of the polar ice caps.A significant contributor to climate change is the CO 2 emitted from burning fossil fuels, which has motivated research into a clean "hydrogen economy," as H 2 combustion will produce only clean water as a by-product.A recent Intergovernmental panel on climate change (IPCC) study reported that the environmental situation is far worse than previously thought; radical changes are required immediately to stop global temperatures increasing by 2 °C, accelerating the need for clean fuels [1].
Proton exchange membrane fuel cells (PEMFCs) can be an alternative to combustion technology.The use of hydrogen in PEMFCs produces no CO x by-products, yielding significantly cleaner energy than combustion sources [2].However, hydrogen fuel is limited by storage and transportation issues, requiring large storage tanks at pressures in excess of 200 bar.Thus, alternative hydrogen sources have been widely investigated [3][4][5][6].Methanol and methane are two traditional examples of hydrogen-storing molecules; however, both produce CO x products upon utilization.This by-product poisons the membranes of PEMFCs, and, therefore, cannot be used as a fuel source in this particular application [7,8].Alternatively, ammonia has been recognized as a suitable hydrogen carrier and is now being investigated as a source of H 2 for fuel cells [8][9][10][11].Ammonia can also be liquefied at moderate pressures and ambient temperature, enabling it to be stored and transported easily, making it compatible with the current liquid fuel infrastructure [12].However, ammonia is also a poison for PEMFCs (with tolerances of 0.1 ppm) [13], although it can be effectively removed by the use of an absorber or membrane reactor [14,15].Ammonia decomposition is considered a critical reaction in the search for a feasible source of hydrogen for fuel cell technology.At the point of use, ammonia can be broken down into hydrogen for fuel, with the only by-product being harmless nitrogen.However, current catalysts are often based on scarce metals such as Ru or contain complex supports unsuitable for scale-up, such as carbon nanotubes [16].The NH 3 decomposition reaction proceeds through sequential dehydrogenation steps followed by the combinative desorption of H 2 and N 2 [17].The rate-determining step (RDS) depends on the nitrogen binding energy, where a strong binding facilitates the N-H bond scission and a weak one facilitates the combinative desorption of nitrogen [18].As a result, a volcano plot of activity as a function of binding energy can be produced [18,19].Due to its high intrinsic activity, Ru has been widely studied, with many studies investigating the optimal particle size and active sites [20][21][22].Even as a single catalyst, Ru has been shown to be the most active [23][24][25].
However, Ru is scarce, making it undesirable as a massmarket catalyst [26].Periodic table interpolation theory posits that the N-binding energy of an alloy is a linear combination of that of the parent metals [19,27].Therefore, an optimized intermediate binding energy could be formed by alloying abundant metals with high and low N-binding energy.For the ammonia synthesis reaction, which can also be described using N-binding energy, the bio-inspired CoMo catalyst was predicted through periodic table interpolation and demonstrated to be more active than Ru [19].CoMo is also active in the decomposition reaction [28].It has been noted that under reaction conditions, alloys can undergo surface segregation.As such, the N-binding energy on the pristine CoMo per se can become an ineffective descriptor to predict the catalyst's activity [27].Metal multilayer surfaces where Ni, Fe, or Co are added to Pt(111) have also been predicted and demonstrated to be active at < 300 °C while the sub-surface configurations of the same metals (e.g.Pt-Co-Pt or Pt-Fe-Pt) were not, indicating the importance of nanostructure [27,29].

Wet Impregnation
Monometallic (Ru, Fe, Ni, Co, Fe, Pt and Pd) catalysts were prepared by wet impregnation.The appropriate mass of metal chloride precursor was measured to give a 5 wt% loading.These were dissolved in de-ionised water and added to 0.95 g of dried γ-Al 2 O 3 support.The mixture was stirred at 80 °C until the excess solvent was removed and the catalyst resembled a thick paste.The Co, Fe, Ni, Pd, and Ru catalysts were dried in a vacuum oven at 60 °C for 2 h.Due to safety issues with the use of chloroplatinates, the Pt catalyst was dried in a specific oven at 110 °C for 16 h.The catalysts were then reduced under a flow of 5% H 2 /Ar at 550 °C with a temperature ramp rate of 10 °C min −1 for 3 h.

Chemical Vapour Impregnation (CVI)
Monometallic (Ru, Fe and Pt) and bimetallic catalysts (FePt and FePd) with various molar ratios were prepared by chemical vapour impregnation (CVI) to prepare catalysts with a total metal loading of 5 wt%.Appropriate metal precursors (Pt(acac) 2 , Pd(acac) 2 , Ru(acac) 3 , and/or Fe(acac) 3 ) were mixed with γ-Al 2 O 3 in a Schlenk flask and heated to 140 °C for 1 h under vacuum.The as-prepared catalyst was reduced at 550 °C for 3 h in a flow of 5% H 2 / Ar.As all catalysts in this study are 5 wt% loading and supported on γ-Al 2 O 3 , they will henceforth be referred to only by their molar metal ratio (i.e., Pt or Fe 80 Pt 20 ).

Ammonia Decomposition Reaction
Ammonia decomposition was carried out on pelleted and sieved catalyst samples (300-425 µm) in a quartz, fixedbed flow reactor (i.d., 7 mm; catalyst mass, 100 mg) under a flow of dilute NH 3 (5000 ppm NH 3 /Ar, 100 ml/min) at 500 °C.The resultant GHSV through the catalyst bed was 60,000 h −1 , which was representative of the high space velocity expected to be used in catalytic NH 3 -dissociation reactors.Before the reaction, the catalyst was pre-treated under a flow of Ar (100 ml/min) at 500 °C for 1 h to remove any surface contaminants.On-line analysis of the effluent gas stream was carried out using a Gasmet DX4000 Fourier-Transform Infra-red spectrometer (FT-IR) and the H 2 formation rate was calculated after steady-state was achieved.Each reaction was carried out three times and an average used in the reaction data presented, where the error bars represent the standard deviation of each of the triplicate tests.
Equation 1 was used to calculate the ammonia conversion (C NH3 ) based on the difference between the moles of ammonia fed into the reactor, m NH3i , and that detected at the outlet, m NH3o : From this the H 2 formation rate was calculated according to Eq. 2: where the formation rate of H 2 (mmol H2 g −1 s −1 ) is given by the moles of ammonia fed, m NH3i (mmol s −1 ) into the reactor as a function of NH 3 conversion, adjusted to the moles of H 2 evolved in the reaction (1.5) over 1 g of catalyst (Catalyst mass factor = 10 for 100 mg of catalyst as used in this study).

Characterisation
Samples for examination by (S)TEM were prepared by dry dispersing the catalyst powder onto a holey carbon film supported by a 300 mesh copper TEM grid.Bright field (BF) TEM images were taken using a JEOL 2100FX microscope operating at 200 kV.Bright field (BF) and high angle annular

× Catalyst mass factor
Scheme 1 Elementary steps of the ammonia decomposition reaction; * indicates surface adsorption dark field (HAADF) STEM images of Fe-Pt catalysts were taken using an aberration-corrected JEM ARM-200CF microscope operating at 200 kV.This instrument was also equipped with a JEOL Centurio silicon drift detector for X-ray energy dispersive spectroscopy (XEDS).Particle size distribution analysis was performed from analysis of the HAADF electron micrographs using ImageJ.CO-DRIFTS studies were carried out on a Bruker Tensor 27 spectrometer using a Harrick in-situ cell equipped with 2 mm CaF 2 windows.The cell was connected to a water chiller, Harrick cell heater and thermocouple to regulate the temperature.A 2% CO/N 2 mixture was flowed over the catalyst at room temperature at a rate of 20 ml min −1 until saturated (approx.20 min) whereupon the gas flow was switched to N 2 to purge any gas phase and physisorbed CO species.After the removal of gas-phase CO, a spectrum was recorded.
Samples were placed in metal sample holders and patterns were measured using a Panalytical X'Pert diffractometer with a Cu X-ray source operating at 40 kV and 40 mA.Patterns were attained by 40 min scans over a 2ϴ angular range of 5-80°.Phase identification was performed by matching experimental patterns against entries from the international centre for diffraction data (ICDD) database.

Relationship Between N-Binding Energy and Catalyst Activity
The interaction of atomic nitrogen with the catalysts (N-binding energy) is a suitable descriptor of catalytic activity for NH 3 synthesis and decomposition reactions [25].Materials with N-binding energy that is not too weak or too strong are good catalyst candidates.The rationale for this statement can be rationalized from the reaction mechanism of select elementary reactions presented in Scheme 1.
Ammonia initially adsorbs onto the catalyst's surface through the N atom (step 1).Three consecutive N-H bond scissions occur, leading to H adsorbed on the catalyst's surface (steps 2 to 4).The reaction proceeds through the associative desorption of adsorbed H and N atoms (steps 5a and b).The rate-determining step (RDS) in this mechanism is widely accepted to be either the first dehydrogenation (step 2) or the N 2 desorption (step 5b) [24], which is dependent on the N-binding energy.When the N-binding energy indicates a weak interaction, the first N-H bond is difficult to cleave, and step 2 in Scheme 1 is the RDS.As the N-binding energy increases, the electron back-donation into the N-H antibonding orbital increases, facilitating N-H bond cleavage (steps 2-4).However, strong N-binding hinders the N 2 associative desorption (5b), which becomes the RDS [37].Such a dependence of the RDS on a physical property results in a volcano plot of activity, as introduced by Sabatier in the early 1900s, explaining the reasons behind optimum catalyst performance and design [30].
We have explored the relationship between N-binding energy and NH 3 decomposition by preparing six monometallic transition metal catalysts (Fe, Co, Ni, Ru, Pd, and Pt) supported on γ-Al 2 O 3 by wet impregnation.The H 2 formation rate from NH 3 decomposition, expressed as the mmol of H 2 formed over a gram of catalyst per second, was plotted as a function of the N-binding energy values extracted from density function theory (DFT) calculations by Nørskov and co-workers [30] resulting in the volcano plot presented in Fig. 1a.The H 2 formation rates achieved in this work (Fig. 1a and b) over the monometallic catalysts are comparable to those reported in the comprehensive review by Lucentini et al. [38].The correlation between catalytic activity and N-binding energy also follows the expected trend; Ru is the most active catalyst achieving 100% conversion at 500 °C (0.072 mmol H2 g −1 s −1 ) (Fig. 1).For example, a 5% Ru/Al 2 O 3 catalyst promoted with potassium (100% NH 3 inlet flow, 30,000 h −1 GHSV, 400 °C) achieved an H 2 formation rate of 0.07 mmol g −1 s −1 [39].In contrast, an H 2 formation rate of 0.88 mmol g −1 s −1 was achieved over a K-promoted 4.85% Ru supported on magnesia-carbon nanotube catalyst (100% NH 3 inlet flow, 60,000 h −1 GHSV, 400 °C) [40].The other metals with stronger/weaker N-binding energies are on either side of the highest catalyst activity.Co is an outlier; the N-binding energy implies that the NH 3 decomposition rate should be higher (Fig. 1a).We consider that this discrepancy may be due to the dispersion of the metal or possible differences between the structure of the prepared catalyst and the structure used to calculate the value of N-binding energy.It was also noted that a similar correlation was found when the catalytic activity was plotted against N-H scission activation energy as calculated by Masel and co-workers [24] (Fig. 1b).
Despite the previous monometallic results, this study focuses on influencing the decomposition rate through rational bimetallic catalyst design [24,30].In both correlations, i.e.N-binding and N-H scission energies, Fe was on the opposite side of the volcano to Pd and Pt and, hence, according to periodic table interpolation, nanoalloys formed from Pt-Fe and Pd-Fe could be good candidates for NH 3 decomposition.We extend Hansgen's et al. investigation on Fe-Pt-Pt(111) surface active at low temperatures [29] to conventional nanoparticulate catalyst design.The H 2 formation rate over Fe-based catalysts indicates that it is typically low, in the order of 0.002-0.09mmol H2 g −1 s −1 [38].Pt-based catalysts alloyed with Ni or Sn were reported to achieve H 2 formation rates in a range of 0.009-0.103mmol H2 g −1 s −1 .However, a rate of 0.103 mmol H2 g −1 s −1 was achieved at 500 °C over a PtSn/MCM-41 catalyst with an NH 3 flow rate of 250 ml min −1 [41].Higher rates were reported; however, higher temperatures were required to reach these (T 50 of ca.600 °C, the temperature at which 50% conversion occurs).

Enhancing Catalyst Activity Using Chemical Vapour Impregnation as a Preparative Technique
CVI has emerged as a promising method to prepare active catalysts containing metals such as Fe and Cu [42,43] and has also been demonstrated to be effective in preparing alloy catalysts such as PdZn [44].The small (< 5 nm) nanoparticles typically prepared by CVI and their narrow particle size distribution suggest that it may be a viable route to preparing highly active ammonia decomposition catalysts.
To validate this proposition, the activity of two Ru/Al 2 O 3 catalysts, one prepared by wet impregnation and the other by CVI, were tested between 200 and 500 °C (Fig. 2).Both catalysts show ammonia decomposition activity at temperatures as low as 300 °C with the catalyst prepared by CVI showing activity at temperatures as low as 200 °C (< 10% conversion).These reaction temperatures also agree with modelled micro-kinetic simulations [45].The CVI catalyst was more active and had a T 20 (the temperature at which 20% conversion occurs) of ca.260 °C (H 2 formation rate of 0.0144 mmol g −1 s −1 ), which is roughly 40 °C lower than the T 20 value for the wet impregnation catalyst.The active site for Ru catalysts has previously been identified as a B 5 -type site [46].These B 5 sites are important for ammonia synthesis and decomposition, and have also been shown to be the active site for Fischer-Tropsch synthesis and π-bond cleavage in diatomic molecules [47,48].Therefore, preparing Ru nanoparticles with a high concentration of B 5 sites is significant within catalysis.It has also been shown that the optimum particle size for B 5 site formation is 3-5 nm [21].This difference in reactivity between CVI and wet impregnation routes may be related to the number of B 5 sites and the crystal structure of the nano-catalysts, as shown previously [45,49].Representative bright field TEM images of both Ru/Al 2 O 3 catalysts are shown in Figure S1.Both methods produce Ru particles that are well-dispersed.The mean Ru particle size was 2.47 nm (average from 100 nanoparticles) when prepared by wet impregnation and 2.62 nm (average from 101 nanoparticles) when prepared by CVI.Although the difference in average particle size is small, it is consistent with the catalytic activity comparison (Fig. 2) of the 5 wt% Ru/Al 2 O 3 catalysts prepared by CVI and IWI.Hence, CVI is chosen to be the main catalyst preparation method used throughout the paper as it can lead to well-dispersed supported nanoparticles and it is solvent-free.

Evaluation of Nanoalloys with Different Rate-Determining Steps
As illustrated in Fig. 1, monometallic Fe, Pd, and Pt catalysts are relatively inactive (< 0.01 mmol H2 g −1 h −1 ).The ratedetermining step is the N 2 associative desorption over Fe, whereas it is the N-H bond scission over Pt and Pd.We prepared a systematic set of Fe-Pt and Fe-Pd catalysts Initially, the catalyst synthesis via CVI was performed sequentially with an impregnation of Fe(acac) 3 followed by a reduction step and a subsequent impregnation with Pt(acac) 2 before a final reduction step.Analysis of powder XRD patterns (Fig. S3) and TEM images (Fig. S4) suggested that this led to a considerable amount of unalloyed Pt, which formed large nanoparticles, the diameter of which progressively decreased as the Pt content of the alloy decreased.The evidence for the Pt nanoparticles being alloyed is based on the sharp reflections in Figure S4 of the seq-CVI catalysts assigned to Pt(111), where the Fe 3 Pt(111) reflection would be found at 40.3°.Therefore, all subsequent preparations were carried out by a co-CVI method whereby both metals were impregnated simultaneously, followed by a single reduction step under flowing 5% H 2 /Ar at 550 °C.
The powder XRD patterns of the supported series of co-CVI FePt catalysts with varying compositions, shown in Fig. 3a, display six broad reflections at 2θ values of 32°, 37°, 39°, 47°, 62° and 68°, which correspond to the (220), (311), ( 222), ( 400), ( 333) and (440) planes respectively of the γ-Al 2 O 3 support [50].As the Pt content of the catalyst increases, an overlapping reflection at 2θ = 39° appears due to Pt(111), suggesting that some large, unalloyed Pt particles may still be present [51].See Figure S3 for XRD of the support only.DRIFTS spectra with carbon monoxide (CO-DRIFTS) as probe molecule were recorded on the Fe, Pt, and FePt samples to assess the structure of the metal surface (Fig. 3c).In the Pt-only catalyst, two peaks with centers at 2052 and 2076 cm −1 are noted and attributed to CO adsorbed An additional HAADF-STEM image and the corresponding X-ray Energy Dispersive Spectra from areas 1 and 2 highlighted in d demonstrate that the particle labeled 2 contains both Fe Pt on Pt atoms associated with edge and kink sites, respectively [52].These are consistent with the presence of small Pt particles as analyzed from the XRD data.The intensity of these two peaks decreased dramatically upon the introduction of Fe, suggesting that fewer of these sites are available for the binding of CO.At Fe-rich compositions (i.e., > Fe 40 ), these peaks become lower in intensity and indistinguishable from the background profile.These observations indicate that most Pt was now alloyed with Fe, with only a lower concentration of isolated Pt sites remaining to bind CO.
The fresh Fe 80 Pt 20 sample was analyzed using STEM.Representative images are displayed in Fig. 4a and c, and S5, with the corresponding particle size distribution in Fig. 4b.The XEDS results in Fig. 4d confirm that the prepared particles are indeed nano-alloys and that they are small and well-dispersed with a mean particle diameter of 1.75 nm (average from 536 particles).The larger (> 5 nm) particles present have a low population, and the overall population is dominated by particles with a diameter of < 3 nm.The HAADF-STEM image in Fig. 4a (inset) suggests some limited atomic ordering of the Fe and Pt in the nano-alloys may be occurring with this particle exposing the {100} and {110} facets of tetragonal FePt.EDS data in Fig. 4c and d, where the background region (red box) shows a Fe:Pt composition ratio of 82:18 and the particle (blue box) shows a Fe:Pt ratio of 83:17, confirmed that the molar ratio of Fe:Pt in the nanoparticle was close to that of the nominal ratio.This confirms the particles contain both Fe and Pt, and also suggests that Fe and Pt are likely to be present across the support surface, possibly atomically dispersed (a proposition supported by CO-DRIFTS measurements).These measurements indicate the potential to improve the nanoalloy formation's efficiency further.
The catalytic activity over the series of Fe-Pt catalysts is shown in Fig. 5a.As previously indicated, the parent metals were both relatively inactive at 500 °C where respective H 2 formation rates over Fe and Pt were 0.002 and 0.007 mmol g −1 s −1 .However, a synergistic effect can be seen for the nano-alloy catalysts, which all outperformed the parent metals.The most active catalyst was Fe 80 Pt 20 , which achieved ca.82% conversion (H 2 formation rate 0.06 mmol g −1 s −1 ) under the same reaction conditions.As discussed earlier, the alloy composition influences the efficiency of alloy formation; as the Fe content of the catalysts increases, the extent of alloying increases, resulting in a higher number of active nano-alloy sites and fewer, less active, unalloyed metal particles.However, it is recognized that metal dispersion and the efficiency of alloying present additional complexities, particularly when preparing supported nanoparticle catalysts.Furthermore, while the alloyed catalysts did not achieve the same activity level as the Ru catalyst, it demonstrates that two inactive metals can be used to form active NH 3 decomposition catalysts, and further optimization of the catalyst may reduce the activity gap between FePt and Ru.Indeed, Hansgen et al. demonstrated through both theoretical and NH 3 -TPD experiments that Fe-Pt-Pt(111) was a highly active bimetallic composition, capable of decomposing NH 3 at < 77 °C [29], highlighting the importance of nanostructure.
The stability of the most active (Fe 80 Pt 20 ) catalyst was also assessed by running the ammonia decomposition reaction at 500 °C continuously for 20 h (Fig. 5b).During that time, no significant deactivation was observed, and the  and S6) and XEDS analysis (Fig. 6c, d). Figure 6b shows that after 20 h testing, the mean particle diameter was 1.85 nm, an insignificant increase from the fresh catalyst (1.75 nm).This test indicated that Fe-Pt nano-alloys prepared by CVI are not only small and well-dispersed when prepared but also resistant to sintering under reaction conditions and any other deactivation mechanism.However, we note that the nanoparticles underwent structural changes during the reaction, transforming from well-faceted, structured particles to random alloys.This restructuring could be responsible for the modest improvement in NH 3 conversion from 1 to 4 h time-on-line.Pd has a similar calculated N-binding energy to Pt, meaning that the rate-determining step over Pd should also be N-H bond scission.It was expected that FePd nanoalloy catalysts would show similar results to these of FePt catalysts, namely a synergistic effect resulting in a higher conversion of ammonia.Four FePd catalysts were prepared similarly to the FePt catalysts and were characterized by powder XRD as shown in Fig. 3b.Five characteristic reflections due to γ-Al 2 O 3 were observed.However, there were also two reflections at 2θ values of 39.9 0 and 46.6° attributed to Pd 0 (100) and (200), respectively [53].These signals indicate that the conditions of the preparation method were not ideal for the FePd catalysts and resulted in larger crystallites of Pd.The intensity of these peaks decreases as the Fe-content increases, suggesting that the extent of alloying increases or that the size of the Pd nanoparticles decreases.
CO-DRIFTS of the FePd series was performed to elucidate further the effect of the metal composition on the properties of the metal.The monometallic Pd sample exhibits two bands centered at 1979 and 1940 cm −1 (Fig. 3d).These are attributed to the bridging modes of CO on metallic Pd [54,55].Interestingly, no linearly bound CO was observed, expected at > 2000 cm −1 , suggesting that surface Pd atoms were present in the catalyst or, more likely, that alloying with Fe caused a significant electronic modification of the metal nanoparticle that inhibited CO adsorption.After the introduction of Fe, the band at 1979 cm −1 observed in monometallic Pd disappeared, and the overall intensity of the adsorbed CO decreased by an order of magnitude.The lower stability of the bridged species at 1970 cm −1 has been previously reported [54].Furthermore, as the Fe-content of the FePd alloy catalysts increased, the band at 1940 cm −1 decreased and was not visible in the Fe 60 Pd 40 and Fe 80 Pd 20 samples.It is thought that, as the Fe content of the catalyst increased, the extent of the alloying increased, and these bands decreased due to a lack of neighbouring Pd sites on the surface, similar to that observed with the FePt series (Fig. 3c).
From the FePd catalytic activity (Fig. 3a), it is evident that all the FePd samples were less active than their FePt analogues.However, there are some similarities between the two sets of testing data, which indicates that there may be a critical compositional-related synergistic effect of alloyed metals with differing rate-determining steps.Firstly, all the nano-alloy catalysts show synergy compared to the monometallic catalysts.Secondly, the most active nanoalloy catalyst was Fe 80 Pd 20 , achieving a conversion of 23% (H 2 formation rate 0.016 mmol g −1 s −1 ).The origin of this effect may be due to the formation of catalysts with a more optimized N-binding energy, but this might not have been achieved as efficiently as with the counterpart FePt catalyst series despite the comparable N-binding energies of Pd and Pt.This suggests that other factors affect the catalytic activity, such as Fe-Pd mixing or nanoparticle size, which were not optimized in relation to Fe 80 Pt 20 .It is also significant that in both nano-alloy catalysts, the activity was not as high as Ru, which illustrates the complexity of catalyst design comprised of multiple metals.

Conclusions
Using the CVI preparation method, we have demonstrated a simple, solvent-free route for preparing mono-and bi-metallic nanoparticles and show that it leads to a narrow distribution of nanoparticle diameter.By considering the N-binding energy as an activity descriptor for NH 3 decomposition, we identified FePt and FePd as promising bimetallic catalysts, which exhibited higher activity than the parent metals.Although the FePt catalyst was not as active as a monometallic Ru catalyst, we have shown that two inactive metals can be combined to form active NH 3 decomposition catalysts.Furthermore, there is scope to improve the efficiency of alloy formation, which could close the activity gap to Ru catalysts.While necessary for the potential hydrogen economy through their application in ammonia decomposition, these results have a broad appeal to the general catalysis field.The methods utilized apply to many reactions governed by scaling relationships to design novel nano-alloy catalysts with the potential to outperform current benchmarks.

Fig. 1 Fig. 2
Fig. 1 Relationship between initial H 2 formation rate and N-binding energy a or N-H scission activation energy b over 5 wt% M/Al 2 O 3 (M = Fe, Co, Ni, Ru, Pd or Pt), Ru at 100% conversion; Error bars represent average activity of three reactions.Reaction conditions:

Fig. 3
Fig. 3 Powder XRD patterns of four compositions of FePt a and FePd b, and the two-parent mono-metals supported on γ-Al 2 O 3 ; reflections labeled (filled circle) originate from γ-Al 2 O 3 .The labeled (filled square) corresponds to where Pt(111) or Pd(111) and

Fig. 4
Fig. 4 Representative HAADF-STEM image of the unused Fe 80 Pt 20 / Al 2 O 3 catalyst a and its corresponding particle size distribution (diameter) b The higher magnification image shown inset in a displays some atomic columns highlighted in red with relatively lower contrast and are considered Fe-rich columns in the FePt particle.c

Fig. 5 H
Fig. 5 H 2 formation rate as a function of nominal Pt/(Pt + Fe) (black square) and Pd/(Pd + Fe) (red circle) ratio at 2 h time-on-line a Error bars represent average activity of three reactions.Time-on-line (20 h)

Fig. 6
Fig. 6 Representative HAADF-STEM images of the used Fe 80 Pt 20 / Al 2 O 3 catalyst a and its corresponding particle size distribution (diameter) b A higher magnification HAADF image is shown as an inset in a, and some atomic columns with relatively lower contrast