Composite fabrication and characterization of crosslinked polyaniline/Pterocladia capillacea-activated carbon for adsorption of direct blue-86 dye from water

The fabrication of crosslinked polyaniline/Pterocladia capillacea-activated carbon composite (CrossPANI/P-AC) at different ratios (1:0, 1:0.2, 1:0.6, and 1:1) was studied. CrossPANI/P-AC composites were fabricated by the in situ polymerization of aniline using hydrogen chloride as an acidic dopant, and ammonium persulfate as initiator, while Pterocladia capillacea-activated carbon was synthesized by the chemical activation method and incorporated into the polymer matrix. The samples were characterized by the terms such as Fourier transform infrared (FTIR) spectroscopy, Brunauer–Emmett–Teller, X-ray diffraction (XRD), thermogravimetric analysis, scanning electron microscopy, and energy-dispersive X-ray spectroscopy (EDX). FTIR spectroscopy showed the main characteristic peak positions of CrossPANI/P-AC; XRD showed low crystallinity of CrossPANI/P-AC. A high specific surface area for CrossPANI/P-AC was achieved at a ratio of 1:0.2 where Brunauer–Emmett–Teller surface area, total pore volume, and mean pore diameter values were 166.10 m2/g, 0.0141 cm3/g, and 3.40 nm, respectively. The capability of CrossPANI/P-AC (1:0.2) composite as adsorbent for Direct blue-86 (DB-86) dye from aqueous solution was investigated. The impact of initial dye concentration, temperature, pH, and contact time on the DB-86 dye adsorption from its water solution was examined. The equilibrium adsorption data were well represented by the Langmuir isotherm achieving maximum monolayer capacity (Qm) of 163.93 mg/g at a dose of 0.5 g/L. In contrast, the kinetic adsorption data were well fit by the pseudo-second-order model. Thermodynamic analysis demonstrated that DB-86 dye adsorption occurs spontaneously, endothermically, and physically in nature. The results demonstrated that these composites effectively removed DB-86 dye from aqueous solutions and could be recycled.


Introduction
Water is the most valuable human resource on the planet [1], and it necessitates continuous examination and adjustment of water resource policy at all levels. Water pollution has been identified as the most prominent global cause of mortality and disease [2][3][4], with water contamination responsible for the deaths of 1.8 million people in 2015 [5]. The introduction of numerous colored chemicals into diverse water bodies due to increasing industrialization and urbanization has recently caused a major imbalance in aquatic systems [6]. According to the number of workers, export prices, and local production costs, Egypt's textile industry is one of the country's most important [7]. The textile industry sector, in particular, produces a lot of dye-bearing effluents [8]. Anionic dyes, cationic dyes, and non-ionic dyes are the three types of dyes, and the majority of them are harmful, and some are cancerous [8,9]. Direct Blue 86 dye (Color Index No. 74180, CAS with solution of ZnCl 2 (5 g) for 24 h. After that the mixtures were dehydrated in 24 h at 110 °C and then pyrolysis in a quartz tube under N 2 atmosphere at carbonized temperature 600 °C, holding time 30 min. The activated carbon was chilled at ambient temperature before being washed with boiling water and dried in a 70 °C oven. The samples were then refluxed in a Soxhlet extractor for 2 h with 1 M HCl, then filtered and washed with distilled water until pH was neutral. The activated carbon was then dried at 70 °C, crushed, sieved smaller than 100 mm, and stored in a glass bottle until needed.

Synthesis crosslinked Polyaniline/Pterocladia capillacea-activated carbon composite (CrossPANI/P-AC)
Polyaniline (PANI) was synthesized on the surface of the P-AC with ratio (1:0, 1:0.2, 1:0.6, 1:1) as follows: aniline and Pterocladia capillacea-activated carbon were premixed in HCl (1 M) for 2 h under cooling the mixture below 5 °C using ice bath. A pre-cooled (NH 4 ) 2 S 2 O 8 (0.3 M) in HCl solution (1 M) was slowly added under stirring to the monomer (aniline) solution for 30 min. The reaction vessel was placed in an ice bath cooling system during oxidation cooling since the reaction is highly exothermic (ΔH = 372 kJ mol −1 ). After complete oxidation, the reaction mixture was stirred for two hours at low temperature (0-5 °C) and then left unstirred overnight at room temperature. The precipitated polymer (dark blue powder) was filtered, washed with copious amounts of distilled water, and then diluted with HCl solution until the washing liquid was colorless. Then, we washed with ethanol to remove oligomers and non-polymeric impurities and dried under vacuum at 50 °C to produce the aimed material. Heating PANI/P-AC produced CrossPANI/P-AC at 180 °C for 3 h [61]. Characterization X-ray diffraction (XRD) patterns were obtained using Bruker's X-ray diffractometer (model: 2D Phaser, Germany), in the range 2θ: 10°-80°, with CuKα radiation (λ = 1.540598 Ǻ). FTIR was studied using Bruker VERTEX70 Spectrometer connected with platinum ATR (model V-100, Germany) over the range of (400-4000 cm -1 ) to determine the chemical bonds and functional groups. Thermal stabilities studies were operated by Simultaneous Thermal Analyzer (model: SDT650, USA) instrument in the temperature range of room temperature to 900 °C, with a ramping temperature of 5 °C per minute under an atmosphere of nitrogen gas (100 mL/min). The Brunner-Emmett-Teller (BET) surface areas were determined by N 2 adsorption-desorption isotherm using (BELSORP -model: Mini II, BEL Japan). The morphological structure was performed using a scanning electron microscope (SEM) and energy-dispersive X-ray spectroscopy (EDX) using (JEOL-JSM-5300 LV, Tokyo, Japan). The point of zero charges (pH pzc ) was determined as described in [66] using pH meter JENCO (model 6173, USA). UV-visible spectra of direct blue 86 dye before and after adsorption were recorded on PG instrument (model T80, UK) spectrophotometer.

Removal of Direct Blue 86 dye by batch method
Direct Blue 86 dye stock solution (1000 mg/L) was prepared by dissolving 1.0 g of DB-86 dye in 1000 ml distilled water. All working solutions with various concentrations were obtained by successive dilution with distilled water. Measurement of DB-86 dye concentration was carried out by spectrophotometer at (λ max = 615 nm) using a standard curve. The removal of DB-86 dye was performed via batch equilibrium method. The removal % of DB-86 dye using CrossPANI/P-AC composites with different ratios was determined. The influence of pH, contact time, CrossPANI/P-AC dosage, initial DB-86 dye concentration and adsorption temperature were investigated.
The removal % of DB-86 dye on CrossPANI/P-AC with different ratios (1:0, 1:0.2, 1:0.6, 1:1) was tested by adding 50 mg of each composite to 100 mL of 50 mg/L DB-86 dye solution at pH 2.2, and shacking at 200 rpm for 180 min contact time. The adsorption capacity of CrossPANI/P-AC for DB-86 dye is calculated from equation: where q e is the adsorption capacity of DB-86 dye-loaded adsorbent (mg/g), C 0 and C e represent the initial and equilibrium concentrations of DB-86 dye (mg/L), m is the amount of CrossPANI/P-AC (mg), and V is the volume (L) of DB-86 dye solution.
The effect of solution pH on the adsorption was conducted by adding 0.05 g of CrossPANI/P-AC (1:0.2) composite to 100 mL of 50 mg/L DB-86 dye solution at pH range from 2.2 to 8.5 adjusted using JENCO pH meter and shaken in a shaker operated at 200 rpm at 27 ± 1 °C. After three hours, an appropriate amount of the reaction solution was taken out and then centrifuged, and the remained concentration were measured.
The effect of adsorbent mass on DB-86 dye adsorption was investigated by adding different amounts of CrossPANI/P-AC (1:0.2) (0.05, 0.075, 0.1, 0.125, and 0.150 g) into a number of flasks containing 100 mL known DB-86 dye solutions concentration and shaking at 200 rpm at 27 ± 1 °C to the equilibrium uptake (180 min) by determining the amount of DB-86 dye adsorption was.
At pH 2.2, shaking speed 200 rpm, and temperature 27 ± 1 °C, the effect of time and kinetics experiments was carried out in a series of flasks containing 0.05 g of adsorbent and 100 mL of DB-86 dye of various concentrations (50-150 mg/L) at time intervals of 5-180 min. At predetermined intervals, an appropriate amount of the solution was taken out and then centrifuged, and concentration was determined. The linear kinetic models such as pseudo-first-order, pseudo-second-order, Elovich, intraparticle diffusion, and film diffusion were used to generate the theoretical kinetics graphic (Table 1) [67][68][69][70][71].

Parameters
References Pseudo-first-order 1 2.303 t (2) q e (mg/g): adsorption capacity at equilibrium, q t (mg/g): adsorption capacity at time t, K 1 (L/mg): rate constant of pseudo-first-order adsorption [67] Pseudo-second-order  [69,70] Liquid film diffusion ln(1 − F: the fractional attainment of equilibrium (F = q t /q e ), K FD :the film diffusion rate constant [71] 1 3 The effect of initial concentrations was investigated at temperature 25 ± 1 °C and pH 2.2 by shaking (0.05, 0.075, 0.1, 0.125, 0.15) g of adsorbent CrossPANI/P-AC(5:1) with 100 mL of DB-86 solution of various concentrations from (50,75,100,125, 150 mg/L) and shaken in a shaker operated at 200 rpm. The adsorbent was removed by centrifugation after equilibrium, the supernatant was collected, and the concentration of DB-86 dye that remained was measured. Table 2 summarizes the adsorption isotherms for removing DB-86 dye using the Langmuir, Freundlich, Tempkin, and Dubinin-Radushkevich isotherm equations. Coefficient of determination (R 2 ) and average percentage errors (APE%) function determined using Eq. (6) were used to determine the validity of the isotherm models fitted by the nonlinear regression method [68].
The temperature effect on the adsorption process of DB-86 dye was investigated by adding 0.05 g of CrossPANI/P-AC (1:0.2) into flasks containing 100 mL solutions of 50 mg/L dye concentration at temperatures 35,40,45, and 50 ± 1 °C. The parameters of thermodynamic study such as Gibbs free energy (ΔG, J/mol), entropy change (ΔS, J/K mol) and enthalpy change (ΔH, J/mol) use van't Hoff Eqs. (11,12,13) [78]: where K d is distribution coefficient (K d = q e /C e , L/g), R (8.314 J/mol K), T (K) are the universal gas constant and the absolute temperature, respectively. The values of ΔH and ΔS were determined from the plot of ln K d versus 1/T. Desorption experiments were studied through the following two steps. First, the samples utilized in the adsorption experiments performed with 50 mg/L initial concentration of DB-86 dye solution and 50 mg CrossPANI/P-AC(1:0.2) dose at pH 2.2 conditions and shaking at speed 200 rpm for three hours were collected and then dried at 70 °C. Secondly, 50 mg of DB-86 dye-loaded composites was immersed in 100 mL elution media NaOH (0.1 M) under shaking at a speed of 200 rpm at a temperature 27 ± 1 °C for 2 h, and then, the sample was rinsed with distilled water several times until neutral pH and dried. The eluted DB-86 dye per gram of adsorbent (q des ) from the concentration of DB-86 dye desorbed (C des ) in the solution is calculated by Eq. (14).
Polanyi potential [75][76][77] where V is the volume of the eluent used in liters and m is the weight of the adsorbent in grams. Desorption % was calculated by comparing DB-86 dye desorbed (q des ) to the DB-86 dye adsorbed (q) using Eq. (15).
Three adsorption-desorption cycles were performed on the samples to ensure that the composites could function as practical DB-86 dye adsorbents.

Results and discussion
Characterization

SEM and EDX analysis
The surface morphology of CrossPANI/P-AC (1:0), Cross PANI/P-AC(1:0.2), and DB-86 dye adsorbed onto CrossPANI/P-AC (1:0.2) was obtained by SEM and is presented in Fig. 2a, b, c, respectively. CrossPANI/P-AC (1:0) shows its relatively amorphous structure, and CrossPANI/P-AC (1:0.2) indicates that the polymerization has occurred on the surface of P-AC. After adsorption of DB-86 dye, the surface became more a denser structure, indicating that adsorption occurred on the surface of the CrossPANI/P-AC (1:0.2). EDX data of CrossPANI/P-AC (1:0) and CrossPANI/P-AC (1:0.2) showed that the overall amount of the carbon (C), nitrogen (N), and oxygen (O) elements present in the fabricated composite were estimated using EDX analysis that confirmed the presence of PANI[(C 6 H 5 NH-) n ] (Fig. 3). Besides, sulfur and chloride were also presented in the EDX analysis, presumably due to ammonium persulfate (APS) and the reaction medium, respectively. The mass % of carbon on CrossPANI/P-AC (1:0.2) is higher than in CrossPANI/P-AC (1:0) due to addition of P-AC. peaks at 3852-3707 and 3195 cm -1 representing bonded and non-bonding -OH groups, respectively, on their surface [79]. The band of C = O at 1590 cm -1 is characteristic of aldehydes, ketones, quinone and carboxylated groups [80,81]. Also, the band at 1190 cm -1 represented the C-O stretching vibrations, and the band at 886-756 cm -1 indicated H 2 PO 4and PO 4 2disulfide or aromatic structures [82]. Meanwhile, the band at 467 cm -1 indicates metal oxide or aromatic structures [65,83]. CrossPANI/P-AC (1:0.2) shows similar transmittance bands to CrossPANI/P-AC (1:0). Figure 4b, c of CrossPANI/P-AC (1:0) and CrossPANI/P-AC (1:0.2) shows the main characteristic peak positions of PANI; the broadband at ~ 3223.52 and 3372.92 cm −1 , respectively, is attributed to the N-H stretching vibration due to the protonation of nitrogen [84,85]; and the characteristic band at ~ 2966.29 and 2930.89 cm −1 , respectively, can be assigned to the stretching vibration of the methyl group (-CH 3 ). The stretching vibrations of the quinoid and benzenoid rings are represented by the two bands at 1591.06, 1593.86 cm -1 and 1499.75-1492.75 cm -1 , respectively. The C-N = stretching vibration between benzenoid and quinoid units in CrossPANI/P-AC(1:0) is responsible for the peak at 1384.22 cm -1 [84,86]. The band at ~ 1291.33, 1294.13 cm −1 and ~ 820.81, 814.95 cm -1 , respectively, can be assigned for the stretching of C-N and bending of C-H (out of plane) in the benzene ring [87]. The peaks at ~ 1054.59 and 1060.50 cm -1 are related to the S = O and S-O stretching vibrations of the sulfonate groups linked to the aromatic rings, indicating that the produced PANI nanostructures were doped [84]. FTIR spectra of CrossPANI/P-AC (1:0.2) (Fig. 4d) after adsorption of DB-86 dye showed the same characteristic peak of CrossPANI/P-AC (1:0.2) with a small shift in peaks, and its intensity due to adsorption of DB-86 dye, indicating that the adsorption process occurred.  Figure 5 shows the X-ray diffraction of P-AC, CrossPANI/P-AC(1:0), and CrossPANI/P-AC(1:0.2). The XRD pattern of P-AC showed characteristic diffraction peaks of crystalline structures of the graphitic-activated carbon. The presence of a sharp peak around 2θ = 21.14°, 26°, and 42° was due to the formation of a disordered graphitic phase [88][89][90]. The diffraction patterns of CrossPANI/P-AC(1:0) consisted of broad crystalline peaks; the prominent diffracted peaks at an angle of 2θ = 17.114°, 20.740°, 24.715°, respectively, due to the repeating of benzenoid and quinoid rings in PANI chains, poor crystallinity for conductive polymers are ascribed to the polymer chain, showing low crystallinity for conductive polymers [46,51,91,92]. According to Ali et al. [93], new PANI peaks occurred at 2θ = 43.822°, 49.958°, and 63.974° due to new arrangements or cross-linking in the PANI structure. The CrossPANI/P-AC(1:0.2) peaks were found to slightly shift than CrossPANI/P-AC(1:0) peaks to 16.208, 20.88, 25.064, 43.682, 50.307, 63.974. The gross intensity of the peaks was raised following the addition of P-AC nanoparticles to the PANI matrix due to an interaction between P-AC nanoparticles and PANI caused by the creation of hydrogen bonding between H-N and oxygen of P-AC.

Thermal analysis
The TGA/DTA thermograms of CrossPANI/P-AC(1:0) and CrossPANI/P-AC(1:0.2) were examined in the temperature range of 30 to 900 °C at a heating rate of 10 °C min -1 under a nitrogen atmosphere. Figure 7a,b indicates TGA/DTA plots of the decomposition of CrossPANI/P-AC(1:0) and CrossPANI/P-AC(1:0.2). The first stage involves water evaporation with approximately weight loss of 4.637, 4.293%, and an exothermic peak of 81.19, 84.30 °C is found in the DTA curve, respectively [93]. The second weight-loss stage had an exothermic peak at 290.62 and 284.29 °C, respectively, and a weight loss of 12.22 and 1.84 percent. This is due to the loss of amine groups as low molecular weight polymers degrade (NH 2 ) [61]. In the third weight-loss stage for CrossPANI/P-AC(1:0), the weight loss was 23.56 with two exothermic peaks at 568.43 and 753.97 °C; for CrossPANI/P-AC(5:1) the weight loss was 66.66% with an exothermic peak at 644.29 °C due to thermal degradation of low molecular weight of PANI chains, loss of amine groups (NH 2 ) and the elimination of P-AC [51]. The CrossPANI/P-AC(1:0.2) also shows the same stages of weight loss of CrossPANI/P-AC(1:0), with higher weight loss in the third stage as compared to CrossPANI/P-AC(1:0) due to the incorporation of P-AC in PANI matrix and a weight loss of 66.66% was observed. On examining TGA curves, it is observed that CrossPANI/P-AC(1:0) has higher thermal stabilities than CrossPANI/P-AC(1:0.2), as indicated by the decreased weight loss.

Points of zero charge PZCs
The point of zero charges is the pH required to affect a net zero charge on a solid surface without particular sorption (pH PZC ). The adsorbent CrossPANI/P-AC(1:0.2) surface may exhibit positive and negative surface charges at pH < 3.15 and pH > 3.15, respectively, as presented in Fig. 8. From these values, it can be assumed that when immersed in a solution with a pH below 3.15, the composite surface will be positively charged, thus favoring the adsorption of anionic specimens. When the pH is greater than 3.15, the surface becomes negatively charged, facilitating the adsorption of cationic materials.

Adsorption behavior toward DB-86 dye
The  experimental. It can be noticed that the addition of P-AC to PANI increased DB-86 dye removal% at 0.2 dose and then decreased removal % with an increase dose than 0.2 dose. This can be explained by increased P-AC, blocking the adsorption sites on the PANI surface.

Influence of pH
The  where the maximum capacity reaches 83.69 mg/g at pH 2.2 and the minimum adsorption capacity reaches 15.48 mg/g at both pH 7.3 and 8.5 (Fig. 10). That may be attributed to the point of zero charge (pH PZC ) of CrossPANI/P-AC(1:0.2) surface, which is equal to 3.15. This leads to assuming that when CrossPANI/P-AC(1:0.2) is immersed in a DB-86 dye solution with pH below 3.15, the composite surface will be positively charged, thus favoring the adsorption of anionic specimens of DB-86 dye. Because the surface of CrossPANI/P-AC(1:0.2) is negatively charged, adsorption decreases as pH rises, creating conflict between anionic DB-86 dye and excess OH ions in the solution. The adsorption of DB-86 dye on activated carbon produced from orange peel [95], shrimp chitosan [96], and alginate-encapsulated activated carbon (PnsAC-alginate) [97] followed a similar trend of pH impact.

Influence of initial concentration
The adsorption experiments at initial DB-86 dye concentrations from 50 to 150 mg/L were performed with CrossPANI/P-AC(1:0.2) doses (0.5, 0.75, 1.0, 1.25 and 1.5 g/L), and the results are represented in Fig. 11. The results indicated that the percentage removal of DB-86 dye adsorbed on CrossPANI/P-AC(1:0.2) was inversely proportional to DB-86 dye concentration. The percentage of DB-86 dye removed was higher at lower initial DB-86 dye concentrations and smaller at higher initial concentrations, indicating that DB-86 dye adsorption from its aqueous solution was dependent on its initial concentration and that increasing DB-86 dye concentration reduced active surface size [80]. The percentage removal of DB-86 dye at dose 0.5 g/L, 1.5 g/L decreased from 83.69 to 56.83 and 97.14 to 91.11% when the initial DB-86 dye concentration increased from 50 to 150 mg/L, respectively. On the other hand, the maximum adsorption capacity at doses of 0.5 g/L and 1.5 g/L increased from 38.69 to 170.48 mg/g and 32.38

Adsorption kinetics
The kinetic adsorption data of DB-86 dye onto CrossPANI/P-AC(1:0.2) were processed to understand and predict the nature of the adsorption process. Table 1 summarizes the five linear equations of kinetic models employed to understand the reaction mechanism. Figure 14 and Table 4 display the pseudo-first-order and pseudo-second-order kinetics model of DB-86 adsorption onto CrossPANI/P-AC(1:0.2) parameters values. Data showed that in the pseudo-first-order kinetic model, the q e(exp) values are not in agreement with the predicted q e(th) values but they are in agreement with predicted q e(th) values of pseudo-second-order with R 2 values greater than 0.993. The rate constant of pseudo-second-order adsorption increased with increase DB-86 dye concentration and CrossPANI/P-AC(1:0.2) doses. Therefore, the pseudo-second-order kinetic model is more adequate to describe the adsorption process of DB-86 dye onto CrossPANI/P-AC(1:0.2). Meanwhile, Fig. 14 and Table 5   CrossPANI/P-AC(1:0.2) doses. The film diffusion plots are linear, but they do not pass through the origin, explaining how the film diffusion mechanism affects the adsorption rate. With DB-86 dye concentration and CrossPANI/P-AC(1:0.2) dosages, the values of K FD and C play a wavy and indefinite role.

Adsorption isotherm
To describe the experimental result of DB-86 dye removal isotherm on CrossPANI/P-AC(1:0.2) composite, four isotherm models, which are Langmuir, Freundlich, Tempkin, and Dubinin-Radushkevich (D-R) isotherms, have been investigated. The equations representing these models are compiled in Table 2. Fig. 15 and Table 6 illustrate each linearized isotherm model's plots and related parameters. However, the arrangement of adsorptive removal of DB-86 dye by

3
CrossPANI/P-AC(1:0.2) isotherm as Langmuir < Dubinin-Radushkevich < Tempkin< Freundlich based on the coefficient of determination values (R 2 ) and the low value of APE% error model. According to the Langmuir model, DB-86 dye adsorption occurs on a homogenous surface via monolayer adsorption, without interaction between adsorbed species [98][99][100]. The maximum monolayer capacity (Q m ) was 163.93 mg/g at dose 0.5 g/L. The separation factor R L is calculated using the following equation: [33,83]. It was found that the adsorption process of DB-86 dye onto CrossPANI/P-AC(1:0.2) is a favorable process. Meanwhile, Freundlich isotherm suggested the adsorption process of DB-86 dye based on adsorption heterogeneous surface. The degree of nonlinearity between solution concentration and adsorption is indicated by the n value [68]. Results showed that the adsorption process is a favorable physical process where the value of n < 1. According to the Tempkin isotherm model, the heat of adsorption of all molecules in the layer declines linearly with coverage due to adsorbate-adsorbate interactions, and adsorption is characterized by a uniform distribution of binding energies up to some maximum binding energy. Table 6 shows the values of the Tempkin isotherm parameters. D-R isotherm was

Thermodynamic study
The removal of DB-86 dye onto CrossPANI/P-AC(1:0.2) as a function of reaction temperature was estimated in the temperature range 25-50 °C and is represented in Fig. 16. The capacity of DB-86 dye onto CrossPANI/P-AC(1:0.2) was directly proportional to temperature. The adsorptive removal processes of DB-86 dye are proceeding in endothermic reactions. The maximum DB-86 adsorption capacity was 94.76 mg/g using the initial concentration of solution 50 mg/L at about 50 °C, pH 2.2 and 0.5 g/L adsorbent dosage.  According to Table 7, all ∆G° values were negative and increased with increasing temperature, indicating that the DB-86 dye adsorption process on CrossPANI/P-AC(1:0.2) was spontaneous suggesting stronger adsorptive forces between adsorbent and adsorbate. The positive ∆H° value (13.720 kJ/mol) of DB-86 dye adsorption on CrossPANI/P-AC(1:0.2) confirmed the involvement of an endothermic process. The enthalpy changes ΔH° were less than 84 kJ/mol, indicating that the physisorption adsorption process was taking place [102,103]. The entropy (∆S°) value was also positive (65.05 J/K mol), which explains the enhanced randomness at the solid/solution interface during the adsorption of DB-86 dye onto CrossPANI/P-AC(1:0.2).

Mechanism of adsorption
The chemical structure of the adsorbents influences the adsorption phenomena. The following steps in order could be used to describe the adsorption mechanism of DB-86 dye onto CrossPANI/P-AC(1:0.

Desorption and regeneration studies
Desorption experiments of DB-86 dye from the loaded CrossPANI/P-AC(1:0.2) were performed using 0.1 N NaOH as an eluted medium to investigate the economic Fig. 17 Probable sorption mechanism of DB-86 dye on CrossPANI/P-AC(1:0.2) feasibility and reusability CrossPANI/P-AC(1:0.2) adsorbents. In this condition, the desorption % decreased with increased regeneration cycles, as shown in Fig. 18a. The regenerated CrossPANI/P-AC(1:0.2) composite was applied in three consecutive cycles of adsorption/desorption. The adsorption amount presented was consistent through the cycles and experienced the adsorption capacity decreased by 24.29 mg/g after third generation, which suggests it may be used as a sustainable DB-86 dye removal (Fig. 18b).

Comparative adsorption capacities of different adsorbents for DB-86 dye
The adsorption capacity of CrossPANI/P-AC(1:0.2) composite was compared with some previously reported adsorbents (Table 8).

Conclusion
The in situ polymerization method was used to synthesize crosslinked polyaniline /Pterocladia capillacea-activated carbon composites (CrossPANI/P-AC) at different ratios (1:0, 1:0.2, 1:0.6, and 1:1). The samples were characterized by FTIR, BET, XRD, TGA, SEM, and EDX. Analysis showed that the main characteristic peak positions of CrossPANI/P-AC by FTIR, low crystallinity nature by XRD, 166.10 m 2 /g a high specific surface area for CrossPANI/P-AC(1:0.2) were achieved by BET, amorphous nature and polymerization occurred at the surface of activated carbon by SEM. The performance of CrossPANI/P-AC (1:0.2) composite on the DB-86 dye removal from aqueous solution was reviewed in detail. The pH of the reaction was discovered to play a significant influence in the DB-86 dye removal process, with pH 2.2 being the ideal pH for DB-86 dye removal. The maximum monolayer capacity (Q m ) was 163.93 mg/g at dose 0.5 g/L. The results for DB-86 dye sorption fit the Langmuir isotherm model better than the Freundlich model. The values (ΔG°, ΔH°, and ΔS°) of thermodynamic parameters support that the DB-86 dye adsorption by CrossPANI/P-AC(1:0.2) composite was physical adsorption, endothermic, and spontaneous in nature. The kinetic data were then fitted into a pseudo-second-order model. Based on these findings, the CrossPANI/P-AC(1:0.2) composite can be considered a promising adsorbent for effectively removing DB-86 dye ions from industrial effluent while also being recyclable.