Theoretical and experimental research of edge inclination angle effect on minimum uncut chip thickness in oblique cutting of C45 steel

The minimum uncut chip thickness (MUCT) is an important phenomenon observed both in orthogonal and oblique cutting. Rounding the cutting edge influences the initiation of the cutting process and chip formation. In a previous study, the authors presented a theoretical analysis and experimental validation on the effect of edge inclination angle λs in the range of 0° to 60° on hmin in radial-free turning of C45 steel. The current work investigated the MUCT hmin in oblique cutting process of C45 steel, for extremely high value of edge inclination angle λs. In this research, a special technique based on milling tool machine using a special tool and sample is presented. Enabled model tests in the unprecedented range of angles λs not used in research to date. The samples were machined using a cutting speed vc = 0.063 m/min. Vertical feed of edge fv was determined by association on the applied sample slope (τ = 0.60–0.85 mm/m) and cutting speed vc. as fv = 37.8—53.5 μm/min. MUCT hmin parameter was measured using compensation for the effects of deformation, based on profilogram analysis. The machining experiments were carried out using a tool with rn = 185 μm. It was found that in the range of angles of 50° ≤ λs ≤ 85°, the MUCT decreases from hmin = 12 μm for λs = 50° to hmin = 4 μm for λs = 85°. Increasing λs by 35° resulted in up to threefold reduction in MUCT. The analysis of the experimental results of hmin for the range of studied λs angle confirmed authors previously reported theory for extreme values of λs. In optimization procedure based on LSM, chip flow angle coefficient was determined as k = 0.75 and critical value of rake angle γcf = -64.8°. This feature provides prediction of results with great accuracy to experimental value. The findings from this study opens the possibility of developing new tools for finishing operations in the field of oblique cutting with high values of λs angle. In addition, the results introduce new area for research on improving the surface quality based on lowering the effect of MUCT on surface roughness and explaining some aspects related to surface wear in the friction process.


P n
Normal section plane P o Main section plane P f Feed section plane P s Plane of cutting P cf Chip flow section plane λ s Edge inclination angle (°) κ rN Major cutting edge angle (°) γ f , γ fi Rake angle in feed direction (°) γ o , γ oi Main rake angle (°) γ n , γ ni Normal rake angle (°) γ cf , γ cfi Rake angle in the chip flow direction (°) η cf Angle of chip flow direction (°)

Introduction
The surface roughness is an important factor, which can directly affect the integrity of the machined part, and regions of high surface roughness can initiate corrosion or increase surface adhesion. As being an ultimate aim of the operation, surface roughness-related variables need to be improved for longer service life of industrially important materials [1]. Meeting such expectation surface roughness depends on many factors that are related to the cutting parameters, machine setup, and the characteristics of the cutting tool [2].
One of the important factors affecting the surface condition resulting from the geometric and kinematic mapping and the effect of cutting speed is the phenomenon of minimum uncut chip thickness (MUCT). This is the uncut chip thickness (UCT) [3] value at which chip removal occurs [4,5]. Specifications of MUCT are critical to avoid plowing effect and reduce residual stresses [6,7]. Therefore, there has been a significant number of studies in the previous literature, which investigated the MUCT in micro-cutting operations for investigating its impact on the machinability characteristics. Wojciechowski [8] presents analysis of MUCT influence on surface roughness based on Brammertz approach [9] employed by the authors of [10,11]. Mikolajczyk et al. [12] used Brammertz approach [9] to prepare software to visualization influence of MUCT on surface roughness for turning. Wu et al. [6] analyzed the effective rake angle using cutting force signal peaks. Their results showed that the MUCT caused higher cutting energy and poor surface quality as a result of plowing. Chen et al. [13] analyzed the cutting forces and surface quality to model chip shaping for predicting MUCT. Their findings showed that under certain cutting conditions, there is an optimum surface quality at which the plowing effect is eliminated. Chen et al. [14] performed surface quality analysis for chip thickness. An optimal solution-based work was carried out for minimal surface roughness. Yao et al. [7] studied the effect of plowing depth on residual stresses by developing a model using cutting forces and finite element simulation. The authors found that the energy accumulation on the surface of the body increased with the increase of plowing depth. Dib et al. [15] performed a study to determine the MUCT at the moment of chip formation during micro-end milling. The method proposed in this study allowed for the determination of MUCT along with an estimation of tool radius for monitoring the tool wear. Sahoo and Patra [16] developed a theoretical-mathematical model in micro-end milling considering tool run out, minimum chip thickness, and tooth-overlapping effects on the cutting forces and tool wear along with chip thickness. The results of their model showed good agreement with experimental findings on cutting forces. Sahoo et al. [17] carried out a study to determine the MUCT based on the ratio between MUCT and edge radius in micro-milling operations. Their results showed that high MUCT values produced curled and helical chips while using lower feed rates under MUCT produced irregular chips. Shi et al. [18] attempted to determine MUCT via acoustic emission signals with obtaining satisfactory surface quality during micro-end milling. Their procedure could be useful for surface quality analysis and optimization in a way that the prediction of MUCT using acoustic signals was found as a highly successful technique. Vipindas et al. [19] evaluated the cutting-edge radius effect in micro-end milling considering the chip thickness effect. They determined the critical threshold for the feed rate value that can cause plowing. Xiong et al. [20] observed the chip formation mechanism according to tests and simulation during orthogonal cutting considering chip formation, shear plane, strain rate, and temperature. The authors indicated that comparative results of the test and finite element simulation were reliable when considering different cutting conditions. Molnar et al. [21] utilized a high-speed camera for recording the chip formation during orthogonal cutting under machine tool vibrations. Their aim was to determine the effect of cutting forces on chip thickness variation, surface quality, and stability of cutting direction. The findings of their investigation were used to evaluate models for shear angle and chip formation. Previous studies also investigated different aspects of MUCT during orthogonal cutting. Cutting using edge divide in orthogonal and oblique cutting depends on the value of inclination angle. Orthogonal cutting occurs for free cutting with λ s = 0° and was observed 2 components of forces [22]. Chip flow is perpendicular to cutting edge. Past studies used tools with a low value of inclination angle of cutting. Burak et al. [22] presented review of important articles on the mechanistics of orthogonal and oblique cutting. They present experimental results of oblique cutting for λ s = 7° and 11°.
Recently, a number of analyses have been published in the field of oblique cutting when the edge inclination angle (λ s ) is significantly different from 0° [23]. This angle is also known as the back rake angle (BR) since it has a strong influence on the cutting process [24].
Owing to the difference between orthogonal and oblique cutting in plastic flow throughout cutting-edge chip formation become distinctive [23,25]. Liu et al. [26] found that for a three-dimensional orthogonal cutting process, the side flow effects can be eliminated by applying lower cutting speeds and a higher ratio between chip width and chip thickness. Fang [27] improved a model for oblique cutting to control chip flow direction and chip flow speed. Adibi-Sedeh et al. [28] performed an analysis to study the effects of using flat-faced nose radius tools for calculating the chip flow angle. Validation of the model was presented in the research. Similarly, a number of studies can be found in the open literature on mechanistic modeling of oblique cutting with different operating approaches. Jia et al. [29] performed sub-surface damage analysis using a three-dimensional oblique cutting model in machining to determine the optimum cutting parameters. Lotfi et al. [30] developed an oblique cutting theory for a friction model using three-dimensional turning operation based on measuring the cutting forces. Vinogradov [31] studied chip formation mechanisms during oblique cutting as orthogonal free cutting with a tool whose rake is a function of the face sharpening angle and cutting-edge inclination. Results of comparison between the calculated and experimental values of the forces showed a good fit. Liu et al. [32] modeled the cutting forces for analyzing the oblique cutting operation by taking into account the fracture toughness and thermo-mechanical properties of the material. Moufki et al. [33] presented a predictive theory of oblique cutting considering cutting forces in the view of the thermomechanical approach. Onozuka et al. [34] worked on the long oblique cutting edges during end milling operation for improving tool life, machining accuracy, and surface finish within the light of cutting forces and cutting temperatures. Lin et al. [35] also derived equations for modeling cutting forces for oblique milling operation. Ghosh et al. [36] performed and experimentally verified chip flow during oblique cutting by classifying the chip deviation by incorporating the effect of λ s . Moufki et al. [37] were worked on thermomechanical modeling of oblique cutting operation, which allows for estimation of chip flow, contact length, and cutting forces. The developed model permits the prediction of the cutting forces, the chip flow direction, the contact length between the chip, and the tool and the temperature distribution. Wojciechowski [38] described the methods for the determination of MUCT via experimental, numerical, and analytical techniques during cutting with defined geometry tools. Presented methods concern mainly orthogonal turning. In [8], Wojciechowski presented more methods of experimental techniques of MUCT research. The previous research on the MUCT phenomenon was conducted mainly in the field of orthogonal cutting. The test results show the influence of the edge-rounding radius on the initiation of the cutting process and the formation of the chip. Mikolajczyk et al. present in [23] an analysis and research of the influence of the λ s angle value on MUCT. The developed theory showed a decrease in MUCT with the increase of λ s angle. The authors explain this by changing the configuration of the cutting-edge shape in the chip flow direction from the circular (orthogonal cutting) to the elliptical (oblique cutting). This theory was confirmed in research of MUCT for radial turning of C45 steel for 0° ≤ λ s ≤ 60°. In this work, the authors adopt the concept of Stabler [39] to determine the chip flow angle based on the edge inclination angle. It has been hypothesized that this influence also remains in the range of angles higher than those previously studied. Tools with high λ s are not yet trading tools. Mikolajczyk et al. [40] present innovative tools for oblique cutting with λ s = 60°. Was presented tools for external turning with straight and round cutting edge and tools for internal turning with round insert. Mikolajczyk et al. [41] present design and prototype special tool for oblique cutting with controlled inclination angle of cutting edge. Filippov [42] applied special cutting tools with round edge and λ s = 45° for developing an analytical model for calculating cutting-edge length in oblique cutting. Grzesik et al. [43] studied the use of an oblique tool with a straight cutting edge and λ s = 55°. Wojciechowski [8] in yours review paper describe results of authors paper [23] as an example of MUCT research in oblique cutting. Aydın and Köklü [44] developed a simulation technique based on arbitrary Lagrangian Eulerian to evaluate the performance of the finite element analysis approach. They indicated that proposed methodology was proactive way to improve the efficiency of the finite element simulation. Aydın and Köklü [45] used finite element analysis technique to evaluate the chip morphology and cutting forces in high speed machining of titanium based alloys. Milling force constants were analyzed in order to find the characteristics during cutting a hard material. Chip formation can be analyzed effectively to seek out the optimum chip type.
The purpose of this paper is to study the influence of oblique cutting conditions on MUCT phenomena for extremely high values of the inclination edge angle (50° ≤ λ s ≤ 85°). This is important in understanding the cutting mechanism with a defined edge rounding in terms of extreme cutting-edge configurations. Section 2 presented the state of the art on λ s angle and the effect of the rounding of the cutting edge on MUCT phenomenon. Section 3 provides details regarding the experimental setup and the measurement of h min via machining tests. Section 4 presents the results and discussion of the machining experiment. Section 5 presented the conclusions from this study.

Theoretical aspects of inclination angle and rounding of cutting-edge effect on MUCT
The theory regarding the influence of λ s on MUCT was elaborated in authors' study [23]. Fig. 1 shows 2D sketches of edge geometry in oblique cutting. Fig. 1a shows a view on the plane of cutting-Ps for the sample and rectilinear edge inclined to the main plane on λ s (similarly, as presented in Sect. 3, Fig. 3). Fig. 1b shows the geometry of the real tool with a rounded edge-r n . For the cutting edge presented in P s plane, the location of the axes of Oxyz and Olmn systems is marked. The sections of edge in P o = P f (Oxyz system) and Pn (Olmn system) can be also seen. Based on the analysis presented in our previous work on MUCT [23], it is critical to study the cutting-edge geometry in chip flow direction P cf plane-that is associated with the cutting edge in Olmn system (Fig. 1b). In addition, the position of this plane is determined by the angle of chip flow η cf [46,47]. As previously discussed in the work of Mikołajczyk et al. [23], the angle of chip flow direction (η cf ) is related to λ s by the following equation proposed by Stabler [39]: where k is a dimensionless coefficient usually 0.8 to 1.
(1) cf = k. In P cf direction, the round cutting-edge configuration was changed from a circle in the normal section (P n plane) to an ellipse (Fig. 1b). Based on theory [48], it can be seen that the radius of the circle r e is strictly tangential to the ellipse top. In the previous work of the authors, it was found that there is a sharp decrease in r e with the increase of λ s . Fig. 1b also showed the rake and clear angle for Oxyz and Olmn. The uncut chip thickness (UCT) is also denoted as c i . The chip begins to form when UCT (c i ) reaches a value that defines the limit value of the rake angle (γ cfi ). At this instance, the value of MUCT = h min is determined. Based on the theory presented in [23], the value γ cfi angle can be obtained using h min and η cf = kλ s from equation: Also, based on the transformation of Eq. (2), h min can be calculated for the known value of γ cfi and η cf = kλ s using the following equation: The square root in Eq. (3) makes it possible to obtain two values of h min . Only positive values of the solution make physical sense, and these are considered in the paper. In validation experiment [23] made for different values of r n (18, 29, 90 μm) in terms of angles 0° ≤ λ s ≤ 60°, it was found that Eq. (3) adequately predicted the result of h min with the increase of λ s value for k = 0.9 (it was found for conditions of experiment). In the experiment presented in [23], the oblique cutting process was made in the radial free turning of C45 steel. This caused a certain variability of the rake and clear angles along the edge [23]. For planned cutting tests with λ s > 60°, it is advisable to use a new technique of cutting to prevent changes in the geometry being observed in previous research [23]. Therefore, in the current study, the analysis involved studying the h min phenomena for large values of λ s in oblique cutting. The proposed research method as opposed to the previously used technique provides a constant rake angle along a straight cutting edge.

Machine setup and testing technique
To verify the hypothesis on the effect of very large values of λ s on MUCT (h min ), a research setup was developed, which uses the milling machine feed as the cutting speed. Kinematics of cutting process corresponds to the technique of the planning process [49]. The tests were performed on a vertical milling machine, type FB 25 V NC (made in the Czech Republic Fig. 2a). The proposed technique ensures that the rake angle is kept constant along the straight edge (Fig. 2b). The samples were cut with a wide (w) rectilinear edge inclined at an angle λ s to the cutting direction determined by the cutting speed vector (v c ). Free oblique cutting experiments were developed for constant position of the sample and the controlled edge position connected with its holder mounted in the stopped spindle (Fig. 2b). Due to the significant values of the λ s , the relationship were developed for determining the edge length-l (Fig. 2c).
Presented graph (Fig. 2c) shows strong increase of cutting-edge length l for angle λ s in terms of λ s = 75°-85°. In view of the need to reasonably limit the length of cutting edge special samples with a width of 2.5 mm and edges with l = 30 mm were accepted for the tests. Samples for the experiment that was made of steel C45 are heavily used in many manufacturing companies and this material is from specific material list with guaranteed chemical structure and mechanical properties [50]. Chemical composition of C45 steel was presented in (Table 1). View of prepared sample is shown in Fig. 3.
The results of the h min phenomena for oblique cutting presented in the analysis were used to develop the design of the edge for the tests [23]. The tool geometry was calculated based on the extreme value of clear angle α o which changed with the increase of λ s according to following developed equation: The value of α o can be obtained from Eq. (5): The form of the Eq. 6 is a simplification of the general solution due to the practical scope of o angle. Since the value of α o is strongly depends on λ s , special diagram is created (Fig. 4), which shows the influence of λ s angle on clear angle α o for different values of α n in the normal section of edge. The geometry of the edge rake surface was adopted as the tool that was designed to test the initiation of the cutting process, which takes place at the rounded cutting edge. Therefore, γ nN = -30° was adopted, which was considered sufficient.
Based on presented analysis (Fig. 4), a cutting tool from HSS SW18 was fabricated with the following geometry: α nN = 30° and κ rN = 90° (Fig. 5a). The rounding the cutting edge r n was achieved by abrasive brushes. The measurements of r n were carried out using a profilometer Hommel Tester T2000 (Hommel Werke Germany Fig. 5b).
(4) I = w∕cos s (5) tan a• = tan a n .cos s (6) a• = atan(tan a n .cos s ) The profilograms were made using that same vertical and horizontal zoom and repeated in different places 6 times. The mean value of the measurements of rounding the cutting edge was determined r n = 185 µm. Surfaces of samples (Fig. 3) using grinding process were prepared (R a = 0.32 µm), for achieve repetitive conditions for all attempts. Surface roughness of sample was measured using ISO 4287 standard.
The edge (Fig. 5a) was placed in a special holder ( Fig. 5c and 5d) and was mounted in the milling spindle chuck.
The milling spindle is stopped and a tool allowing accurate positioning relative to the sample. The λ s angle was carried out by turning the tool in the spindle and was set using a workshop protractor with a magnifying glass MKMb 315. Samples (see Fig. 3) were inclined relative to the table plane  on τ to obtain the effect of vertical feed with high accuracy. Sample alignment was carried out using a digital sensor with an accuracy of 1 μm. This was achieved by clamping the sample in a vise mounted on a milling table (see Fig. 2a). In the used technique, the vertical feed of the tool f v depends on the v c and the τ inclination of the sample (see Fig. 2b).
Machining conditions and tool geometry specifications are presented in Table 2.

Measurement of hmin
During the cutting process, in the case of the adopted model for testing, we observed the stress-strain behavior of the workpiece material (Fig. 6).
There are three consecutive phases of the workpiece behavior which can be seen in Fig. 6a: 1. a-elastic deformations 2. b-elastic and plastic deformations 3. c-chip formation-cutting, elastic, and plastic deformation In a phase due to the occurrence of elastic deformations of the workpiece material flowing onto the cutting edge is plowed under the tool flank face [8]. In this phase, the workpiece is only subjected to elastic deformation and returns to the nominal position after the tool passes.
In b phase when UCT value is lower than h min causes the formation of elastic-plastic and plastic deformations of the workpiece. The result is the formation of a plastic flash, which, however, is not transformed into a chip [8].
In c phase when increase UCT to the value within the range h ≥ h min induces the cutting process and chip formation [8,23].
The main challenge was to determine the moment at which the chip begins to form. MUCT (h min ) was indicated mating of surface accompanying the chips formation after tool sliding on the work surface (gloss appears) [23]. The method of solving this problem was presented in a previous study [23] but it cannot be used in the current work due to using a different cutting model (free cutting-no flashing).   An original method of determining the moment of transition from plastic deformation to cutting was adopted, consisting of the analysis of the profilogram made in the cutting direction (Fig. 6b). In addition, the profilometer was used to record the registration of surface profile. Because the cutting forces appeared to be quite high in combination with the machine rigidity, which could disturb the results of the cutting tests (measurements of the order of several micrometers), a system was used during the tests to record the elastic deformation of the main part of machine tool, which were taken into account when calculating h min , as shown in Fig. 7.
Then, based on the analysis of profilogram from each cutting test and deformation measurements results using the setup shown in Fig. 7, similar as in [23] h r was determined using the following equation: In this case, the vertical movement elements of cutting zone of tool m T and sample m S were considered. In this way, the actual UCT value of h r can be read off with a high degree of accuracy.

Plan of experiment
For the experiment, constant factors such as workpiece material, edge geometry, and machining parameters such as cutting speed and feed rate were used [8,23]. The cutting speed was derived from the process modeling technique used on the mill tool machine. The feed rate was provided by setting up the sample for high accuracy of the chip initiation process. The variable factor in the study was the inclination angle of edge λ s .  After substituting the used to Eq. 8 τ inclination, it was found that f v = 0.0378 -0.0535 m/min. Because these are very low values, it can be presented as f v = 37.8-53.5 μm/ min. The edge was set at 30 µm from the surface to ensure that the tool contact with the surface was achieved after a displacement of approximately 50-35 mm, depending on the τ inclination of the specimen. The distance was set using an optical method and controlled with a slit gage (Vogel, Germany). Next, λ s inclination angle is set. Once the tool had been locked in place, the machining process begins by switching on the feed rate. The cutting process was stopped after a certain pre-determined machining time until the cutting initiation occurred. A profilogram was taken of the machined specimen and from this, based on the observation of the effect of the cutting process on profilogram (Fig. 6b) the nominal chip thickness h was determined. Next based on measuring the tool m T and the sample m S vertical resilient movement as shown in Fig. 7, the h min value was calculated using Eq. 7. The trials for each inclination angle value were repeated three times. The tests were carried out for large values of the inclination angle 50° ≤ λ s ≤ 85°. The plan of experiments is presented in Table 3 4 Results and discussion Table 4 shows the results of MUCT according to different λ s ranging from 50° to 85°. For λ s = 50° was achieved h min = 12 µm, and for λ s = 85° was obtained h min = 4 µm.

Results of experiments
The results show the relationship between λ s and MUCT is approximately inversely proportional. Increasing λ s by 35° resulted in up to threefold reduction in h min value clearly shows the very significant impact of λ s on MUCT.

Prediction of hmin based on theory [23]
Results of experiment presented in Table 4 were used for found parameters of oblique cutting process: γ cf angle and k parameter based of Eq. 2 and Eq. 3 from theory elaborated by authors [23]. The calculations were performed using the least-squares method (LSM) to obtain the lowest value of the mean square deviation (MSD). To Eq. 2, the experimental values of h min and successively different values of the k-factors (k = 0.65, 0.70, 0.75, 0.80, and 0.85) for calculate η cf were substituted. For each λ s value, the values of γ cf were determined in this way. For these values, the mean was determined and for successive λ s angles the square deviation was determined. The smallest error was obtained for k = 0.75 as shown in Table 5 and Fig. 8a. The theoretical values of the angles γ cf for k = 0.75 was determined as presented in Table 5 and shown in Fig. 8b. The optimization procedure yielded results in the range η cf = -64.51° to -65.43°. In further calculations, the mean value γ cf = -64.8° was used for the test conditions. Table 6 shows a comparison of the theoretical and experimental values of h min based on approximation of results using Eq. 3 for η cf = 0.75 λ s and γ cf = -64.8°. Table 6 also shows the predicted h min values calculated using Eq. 3 for 0° ≤ λ s ≤ 40° an extrapolation of results of experiments prepared for area our previous research [23]. The comparison of the experimental MUCT with the theoretically predicted ones based on Eq. 3 is presented in Fig. 9. Extrapolation of predicted results of h min for 0° ≤ λ s ≤ 40° is signed using dashed lines. In Fig. 9, it can be seen that the h min values determined theoretically from Eq. 3 based on the parameters obtained by the optimization procedure coincide with the experimental results. This confirms the theory presented in the paper [23]. The extrapolation results for the obtained parameters show an increase in the h min value with a decrease in the value of the angle λs. However, this change is not as pronounced as for the experimental range. The presented graph indicates that in the range of significant values of the angle λs, very significant changes in the mechanics of the cutting process occur, especially in the MUCT range.

Analysis of cutting edge section in the chip flow direction
Experimental results and analyses, based on the theoretical model [23], are related to the geometry of the cutting edge in the P cf section (Fig. 1). In chip flow direction the circular contour of edge for λ s = 0° changes into an elliptical for λ s > 0°. The contour of the ellipse depends on the angle of chip flow η cf . It was found that in when calculating h min , coefficient k = 0.75 was used for the calculation of η cf value. Based on this, the values for the ellipse half-axes were calculated. Taking into account that A = r n , B = r n / cosη cf (Fig. 1), the influence of λ s for η cf = 0.75λ s is given in Table 7. Also based on chip flow direction, the radius r e was strictly a tangential circle to the ellipse top [46] and was calculated using the equation presented in Fig. 1.
The changes in the shape of the cutting edge drawn based on data from Table 7 are visualized in Table 8. In Fig. 10   was presented comparison of the theoretical values of h min and shape of cutting edge in P cf section for orthogonal and oblique cutting for γ cf = -64.8°. As presented in Table 3, it is possible to determine h min using Eq. (3), based on the γ cf angle and η cf , h min value adequately to the edge curvature, which significantly change as it can be seen from the comparison presented in Table 8.
However, the observed change in h min is much larger than the observed change of circle radius strictly tangential to top of ellipse r e . For example, for λ s = 50°, h min = 12 μm was obtained and for λ s = 85°, h min = 4 μm was found, i.e., a decrease of 3 times, while the radius r e = 146.81 µm for λ s = 50° and r e = 81.92 µm for λ s = 85°, i.e., they decreased by less than 2x. This is since h min is governed by the angle γ cf which is found on the curvature of the ellipse. In Fig. 10, the theoretical values of h min are presented for λ s = 50°

System of cutting process regulation of MUCT in oblique cutting
Results of experiments and its analysis based proposed theory show that for the defined edge (r n ), one material and value of cutting speed we can get values of: γ cf angle and k coefficient of chip flow direction, which solve problem of prediction h min . Based on results of research and analysis using of proposed theory [23] was proposed system of cutting process regulation of MUCT in oblique cutting (Fig. 11). Figure 11 presents diagram of cutting process regulation when λ s was changed and influenced on cf angle based on k value, which defined stereometry of cutting edge with r n value and predicted using Eq. 3 h min based on obtained γ cfi and k values for experimental conditions. Results of presented research confirm the statement from previous literature [23] which states that for a tool with a specific r n radius, the reduction in h min value with the increase of λ s to 60° is also confirmed in the extremely high values of λ s (up to 85°).
The presented result of this research supports these possibilities, which can be also applied for very high values of the λ s angles which are not else used in practice. The results confirmed the significant lowering h min value with the increase of λ s angle opens the possibility of developing new tools [40,41] for finish machining in the field of oblique cutting. These tools can be designed and manufactured using market inserts [40,41]. Presented result open new subject of research improve surface quality based on lowering of h min value which influenced on surface roughness [8,12]. Also, it is possible to explain some issues of surface wear in the process of friction [51].

Conclusions
The current work investigated the MUCT h min in oblique cutting process of C45 steel, for extremely high value of edge inclination angle λ s , in research was used special technique based on milling tool machine using a special tool and sample. Enabled model tests in the unprecedented range of angles λ s not used in research to date. This is novelty of presented article. According to the results from this study and results of previous presented authors article paper [23], the following conclusions were made: • In experimental studies made using tool with r n = 185 μm, it was found that in the range of angles 50° ≤ λ s ≤ 85° significantly decrease the MUCT value from h min = 12 μm for λ s = 50° to h min = 4 μm for λ s = 85°. Increasing λ s by 35° resulted in up to threefold reduction in MUCT • Analyses of the experimental results of h min for used λ s angle confirmed authors theory [23]. With use of Eq. (3) was determined chip flow angle coefficient k = 0.75 and critical value of rake angle γ cf = -64.8° based LSM. This provides prediction of results with great accuracy to experimental value • Analysis of shape cutting edge in chip flow direction show that on cutting process influenced critical value of rake angle • The applied test technique, using mill tool machine with compensation for the effects of deformation, allows for a sufficiently precise determination of the h min based on profilograms analyses. Used cutting method limits cutting speed range to a very low value • Practical effect of presented research is opening the possibility of developing new tools for finish machining in the field of oblique cutting with high values of λ s angle [40,41] • Presented results open new subject of research possibility to improve surface quality based on lowering of MUCT effect on surface roughness [8,12]. Also, it is possible to explain some issues of surface wear in the process of friction [51] Funding No funding was received for conducting this study.

Data availability
The data used in this work can be requested by contacting the first author.
Code availability Not applicable.

Declarations
Ethics approval Not applicable.

Consent to participate Not applicable.
Consent for publication Not applicable.

Competing interests
The authors declare no competing interests.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.