Experimental investigations on longitudinal-torsional vibration-assisted milling of Ti-6Al-4V

In vibration-assisted milling (VAM), an additional high-frequency oscillation is superimposed on the kinematics of a conventional machining process. This generates oscillations of the cutting edge in the range of a few micrometers, thereby causing a high-frequency change in the cutting speed and/or the feed. Consequently, a reduction of cutting forces, an increase of the tool life, and an improvement of the workpiece quality can be achieved. This paper shows and compares the effects of longitudinal and longitudinal-torsional (L-T) vibrations on the cutting force, the tool life, and the surface quality when milling Ti-6Al-4V. In comparison with the conventional milling process, the cutting forces are significantly reduced and the surface finish of the workpiece can be improved by introducing ultrasonic vibrations to the milling process. Longitudinal-torsional vibration assistance showed better overall process performance than the pure longitudinal vibration assistance.


Introduction
The continuing trend toward lightweight construction is increasingly leading to the use of high-strength construction materials. For example, high-temperature titanium alloys are used in gas and steam turbines to increase the maximum possible temperatures in the turbine-and thus its efficiency. In medical technology, biocompatible and highly wear-resistant materials are required for the manufacture of implants and endoprotheses (e.g., teeth, hip, or knee joints) Philipp [23]. In aerospace technology, the titanium alloy Ti-6Al-4V is used to produce structural components due to its high strength and low density [18]. For structural components of Ti-6Al-4V, the material removal by machining can be up to 95% of the total workpiece mass [8]. Considering conventional machining processes, these high-performance materials can only be machined with high cutting forces, high tool wear, and a low material removal rate. It has been proven that these problems can be successfully mitigated using vibration-assisted machining [4,7,24].
In vibration-assisted machining, high-frequency oscillations are added to the conventional kinematics of the machining process, thereby causing a high-frequency change in the cutting speed and/or the feed. The tool usually oscillates at a frequency over 16 kHz, with an amplitude of 1 to 20 μm. When the tool oscillates with the frequency f and a vibration amplitude A, the vibration velocity v os,crit = 2 · π · f os · A can be calculated [30]. In the case of a vibration superimposition in the cutting direction, the tool separates from the workpiece in each vibration cycle if the vibration velocity exceeds the cutting speed. This periodically interrupted process leads to several advantages compared with the conventional cutting process [25,29]: Figure 1 shows different types of vibration-assisted machining, which can be distinguished by the characteristics of the tooltip trajectory. In 1D vibration-assisted machining, the cutting tool vibrates either in the cutting direction or in direction perpendicular thereto. If the tooltip vibrates simultaneously in both the cutting and normal direction at different frequencies or with a phase difference, the tooltip will perform an elliptical motion [19]. This process is called 2D vibration-assisted machining. In vibration-assisted turning, the influence of the tooltip trajectory on the process performance has already been studied extensively [10,20,30]. Most of the publications state that a vibration superimposition in cutting direction yields more benefits regarding a reduction in cutting forces and tool wear than a superimposition perpendicular to the workpiece surface [30].
Vibration-assisted machining has already been studied for over 50 years [2]. It has been applied to machining processes like turning, drilling, milling, and grinding. The vibration assistance can be achieved by either vibrating the tool or the workpiece. Most of the researches were focused on vibration assisted turning (VAT), as it is easier to apply ultrasonic vibrations to a stationary turning tool rather than to a rotating, drilling, milling, or grinding tool. Nath et al. [11] studied the effects of vibration-assisted turning of Inconel 718 with vibrations in the cutting direction regarding cutting forces, tool wear, surface quality, and chip formation. During the experiments, the cutting speed and the feed rate were varied and the ultrasonic vibration frequency and the amplitude were kept constant at 19 kHz and 15 μm respectively. The results showed that the surface quality depends mostly on the tool-to-workpiece contact ratio and the relative speed between the tool and e p y T  Fig. 1 Types of vibration-assisted milling the workpiece when machining with vibration assistance. It was found that to achieve high cutting qualities, the toolworkpiece contact ratio must be kept low, which can be achieved by increasing the amplitude and the frequency of the vibration or decreasing the cutting speed. The resulting cutting forces during vibration-assisted turning were reduced by 75 to 88% compared with conventional turning. The tool life of the cubic boron nitride cutters used was increased 4 to 8 times during turning with vibration assistance with a cutting speed of 10 m/min. However, beyond 10 m/min cutting speed, tools catastrophically failed under ultrasonic vibration assistance. Ultrasonic vibration assistance enabled surface finishes of R a ≤ 1 μm, whereas the best surface roughness achieved with conventional turning was R a = 2.4 μm. It was mentioned that vibration assistance caused longer, thinner chips, which is favorable for high-quality machining. Patil et al. [16] studied the effects of feed direction ultrasonic vibration assistance during dry turning of Ti-6Al-4V. The cutting speed and the feed rate were varied and the ultrasonic vibration frequency and the amplitude were kept constant at 20 kHz and 20 μm, respectively. A cutting force reduction of up to 50% was observed due to the vibration assistance, and an increasing tool-workpiece contact ratio resulted in a decrease in force reduction. Better surface quality and thinner, longer chips were observed with vibration assistance. Another important effect of vibration-assisted machining is the influence on the residual stress state near the surface of the machined workpiece. Nestler et al. [12] showed that higher compressive residual stresses can be achieved by applying the vibration assistance perpendicular to the machined surface. Similar results are shown in [29] regarding residual stresses. For vibration-assisted turning of Ti-6Al-4V, several approaches for numerical modelling of the cutting mechanism exist [16,22]. Cakir et al. [3] modelled the chip formation mechanism and showed that the average cutting force significantly drops with vibration assistance due to the intermittent cutting effect, which in turn may improve the tool life. Although the cutting edge has the possibility to cool down when the tool separates from the workpiece, the peak temperature during each vibration cycle was found to be higher compared with conventional turning.
Compared with VAT, VAM has not yet been thoroughly investigated. In VAM, two different methods for superimposing an ultrasonic vibration exist. The first one involves using an ultrasonic worktable, which excites the workpiece with the ultrasonic vibration [1]. Although the installation of an ultrasonic worktable is relatively easy, this method has some disadvantages. When different workpieces are milled, the ultrasonic system needs to be adjusted because of a change of the systems' resonance frequency. A more flexible method is achieved by superimposing the vibration on the milling tool. Usually, the tool is superimposed with a longitudinal vibration along its axis (longitudinal vibrationassisted milling (LVAM)). Many researchers reported positive effects regarding surface roughness, cutting forces, and tool life [9,13,24,25,27,31]. Razfar et al. [17] studied the effects of longitudinal vibration-assisted milling of AISI 1020 steel by superimposing a vibration on the workpiece. Experiments were carried out at a constant vibration frequency of 20 kHz. During the experiments, the depth of cut, the cutting speed, and the feed rate were varied. While the positive effect of vibration superimposition tended to decrease with increasing cutting speed and feed rates, an increase in depth of cut did not result in a significant deterioration of the surface quality. A decrease in the cutting force was observed during the intermittent cutting process, which was explained both by an aerodynamic lubrication effect and by the improved cooling behavior of the tool. A positive correlation between the tool-workpiece separation time and the reduction in cutting forces was found. Niu et al. [15] studied longitudinal-torsional vibration-assisted milling (LTVAM) of Ti-6Al-4V by superimposing the vibrations on the milling tool. The torsional vibrations were produced by degenerating longitudinal vibrations into torsional vibrations by helical grooves in the sonotrode. The research included the influence of the ultrasonic vibration on residual stresses, surface hardness, and surface quality of the milled workpiece. The ultrasonic vibration frequency was kept constant at 35 kHz and the amplitude was varied between 2 and 6 μm. The experiments showed that the vibration amplitude has the least significant effect on residual stresses. However, sensitivity analysis revealed that a higher vibration amplitude increases the surface hardness of the bottom surface, which is explained by the increase of the impact energy with the increasing vibration amplitude. Zhou et al. [33] studied the cutting mechanisms in the holemaking process of longitudinal-torsional ultrasonic-assisted helical milling. The results showed a reduction in the axial cutting force of up to 12%, whereas the other cutting force components did not change significantly compared with conventional helical milling. An overall reduction in the burr height at the hole entry was also achieved. Similar experiments were performed by Wu et al. [28], who studied a longitudinal-torsional vibration-assisted side milling process. The measured reduction in the cutting forces was 45.8% in the x-direction, 27.6% in the y-direction, and 48% in the z-direction. Wu et al. also stated that the cutting force reduction is in correlation with the total contact time between the tool and the workpiece. With a higher contact time, a decrease of the force reduction was observed. Thus, a higher cutting speed also resulted in a lower force reduction.
In the present work, the influence of LVAM and LTVAM on machining Ti-6Al-4V is demonstrated and compared with each other for the first time. After analyzing the process kinematics of LVAM and LTVAM in chapter 4, an ultrasonic actuator is presented that is capable of superimposing longitudinal and longitudinal-torsional vibrations onto an endmill. Experiments were carried out for slot and peripheral milling. In Section 4.1, the effects of LVAM and LTVAM on the cutting forces are discussed. The resulting workpiece properties in the form of surface roughness, residual stresses, hardness, and burr formation are described in Section 4.2. The effect on the tool life is shown in Section 4.3.

Kinematic analysis of LTVAM with helical end mills
In vibration-assisted milling, the conventional kinematic of the cutting tool is superimposed by an additional vibration. The resulting process kinematics of a L-T vibration will be discussed in the following. The movement of the cutting tool in conventional milling consists of the cutting motion and the feed motion. The two-dimensional trajectory of a point at the cutting edge is shown in Fig In order to determine whether the cutting tool loses contact with the workpiece due to the vibration assistance, the vibration velocity in the cutting direction can be calculated for LVAM and LTVAM by v os,crit = 2 · π · f os · A t + 2 · π · f os · A l · tan(β) (2) where β is the helix angle of the milling tool. When the vibration velocity v os,crit exceeds the cutting speed v c , the cutting edges will lose contact with the workpiece in each vibration cycle, resulting in an intermittent cutting process. If the vibration velocity v os,crit does not exceed the cutting speed v c , the tool will not lose contact with the workpiece, resulting in a continuous cutting process with an ultrasonically modulated cutting speed. The principle of the intermittent cutting process can be seen in Fig. 3. The figure shows the position of a point on the cutting edge in cutting direction for conventional machining (p con ) and for vibration-assisted machining (p os ), which can be derived from Eq. 2. When the cutting edge moves opposite to the direction of cutting, the rake face of the tool loses contact with the chip (exit point t e ). From that point on, the cutting forces drop significantly. It should be noted that although the cutting process stopped, the flank face of the tool is still in contact with the workpiece, creating frictional forces. Between the points t e and t t (turning point), the friction force acts opposite to the cutting direction. When the cutting edge passes the turning point t t , the friction force acts in the cutting direction. The cutting process starts again when the cutting edge reaches the start point (t s ). The result is an intermittent cutting process, which is repeated periodically Many researchers already stated that the relative cutting time is directly proportional to the cutting force in vibrationassisted machining. In order to achieve a lower cutting time T c , the vibration amplitude and the frequency must be increased or the cutting speed must be decreased.

Experimental setup
The experiments were carried out on a CNC milling machine (Hermle UWF 900), as seen in Fig. 4. The cutting forces were measured in x-, y-, and z-directions with a dynanometer (Kistler 9257A). To determine the surface roughness in accordance with DIN EN ISO 4287, a 3D laser scanning microscope (Keyence VK-X1000) was used. The residual stresses were analyzed with an X-ray diffractometer (Stresstech XSTRESS G2R with Ti-X-ray tube). Hardness measurements were carried out with a Vickers hardness tester (LECO LV-Series). The workpiece made from Ti-6Al-4V had the dimensions 100 × 100 × 5 mm. The chemical properties of the titanium alloy are shown in Table 1.
The solid carbide milling tool with 3 flutes has a diameter of 8 mm, a helix angle of 55 • , a positive rake angle,

Ultrasonic actuator
To superimpose an ultrasonic vibration onto the milling tool, an ultrasonic actuator was designed in ANSYS. The actuator consists of a Langevin-Bolt transducer that converts a highfrequency electrical current into a mechanical vibration. The   Fig. 6 Ultrasonic converter with milling tool; the vibration amplitude is schematically shown along the actuator with its amplitude maximum at the tooltip transducer is powered by an ultrasonic generator (Weber Typ ULC MD/MFD). The electrical energy is transferred via induction through a stator and rotor coil to the rotating transducer. In order to generate a pure longitudinal vibration at the tool center point, a customized milling tool that resonates at its first longitudinal eigenmode at 34 kHz was designed and fabricated. The milling tool is attached to the transducer using a screw connection with an axial centering. This method ensures minimal damping of the vibration amplitude when compared with conventional collet chucks. The length of the cutting edges was kept short to prevent the longitudinal vibration mode from being converted into a torsional vibration mode through the helix form of the cutting edges.
In order to generate a longitudinal-torsional vibration output at the tool center point, a slitted horn was designed. By means of geometrical changes of the cross section of the horn, a part of the longitudinal vibration is converted into a torsional vibration. The helical form of the cutting Fig. 7 Longitudinal and torsional vibration amplitude (peak to peak) at the cutting edges in LTVAM (left) and LVAM (right); the amplitude can be adjusted by changing the generator power output edges further amplifies the torsional vibration output. The actuator is shown in Fig. 5, and the converter in Fig. 6, and the longitudinal and torsional vibration output on the cutting edge is depicted in Fig. 7. The achieved ratio between torsional and longitudinal vibration outputs in LTVAM (A t /A l ) is about 1.3. In the following descriptions, only the longitudinal vibration amplitude A l will be given. For LTVAM, the corresponding torsional amplitude can be calculated by: The amplitude at the cutting edges can be adjusted to a certain extent (A l between approximately 4 and 12 μm) by adjusting the output power of the ultrasonic generator.

Results and discussion
In the following, the effects of ultrasonic vibration assistance on the milling forces, workpiece properties, and tool wear will be discussed. Figure 8 shows the cutting force in relation to the longitudinal vibration amplitude A l for LVAM and LTVAM for different cutting speeds for peripheral milling. Ultrasonic assistance reduces the cutting forces significantly due to the intermittent cutting process and the reduced macroscopic friction coefficient between the tool and the workpiece. The highest cutting force reduction for LVAM in comparison with conventional milling (A l = 0) is 44% for F x , 47% for F y , and 44% for F z at a vibration amplitude A l of 11.8 μm. In LTVAM, the highest force reduction is 53% for F x , 59% for F y , and 61% for F z at a vibration amplitude A l of 11.8 μm. The gray parts in Fig. 8 indicate the regions in which the cutting tool was in constant contact with the workpiece according to Eq. 2. For a cutting speed of v c = 30 m/min, the tool loses contact with the workpiece at a vibration amplitude of A l = 4.6 μm for LVAM, whereas in LTVAM, only a longitudinal vibration amplitude of 1.7 μm is needed. For a cutting speed of v c = 80 m/min, no toolworkpiece separation occurs for LVAM. In the region, where v os,crit < v c , the reduction in cutting forces is moderate.

Effect on the cutting force
Here, the force reduction can be explained by an ultrasonic modulation of the cutting speed, which decreases the macroscopic friction coefficient between the rake face and the flowing chip, and between the flank face and the workpiece, thus creating a higher shear angle when compared with conventional machining. When the vibration amplitude is increased until the vibration velocity v os,crit equals the cutting speed v c , the cutting edge loses contact. In this

Effect on surface roughness, residual stresses, and burr formation
The effects of vibration-assisted milling on the workpiece properties are discussed in the following. The results are described for the side wall of the workpiece for peripheral milling and for the bottom surface for slot milling. Figure 9 (top) shows the resulting average roughness value R a for different vibration amplitudes. At a vibration amplitude of A l = 4 μm, the surface roughness decreased for both LVAM and LTVAM from R a = 0.9 to 0.78 μm and 0.75 μm, respectively. Microscopic images (Fig. 10) show that the feed marks are reduced compared with conventional milling, which reduces the corresponding surface roughness. When the vibration amplitude is increased further, the surface roughness also increases slightly for both LVAM and LTVAM. The surface shows vibration marks that increase with rising vibration amplitude. In all cases, LTVAM shows a better surface roughness when compared with LVAM.

Surface roughness of the bottom surface
Surface roughness of the side wall Different results occur when the surface roughness of the side wall for peripheral milling is analyzed. With increasing amplitude, the surface  Fig. 11. The effect of the ultrasonic vibration smoothens the surface as micropeaks are flattened by the oscillating cutting edge. Other researchers stated that the resulting surface has beneficial properties such as a higher oil-locking property, which can improve the friction coefficient [21,25].

Residual stresses and surface hardness
The machining of Ti-6Al-4V inevitably leads to changes in the near-surface residual stresses, due to the high mechanical and thermal loads between the tool and the workpiece during the milling process [5]. The thermal load usually causes tensile stresses near the surface. The friction between the tool and the workpiece (especially the friction between the flank face and the workpiece) causes the surface layer to heat up locally and expand, which initially induces compressive stresses. If the yield point of the material is exceeded by these loads, plastic compression occurs. When the previously compressed region cools down and stretches, tensile residual stresses occur. The mechanical load usually generates compressive residual stresses in the  cutting direction by preventing elastic deformation through areas where plastic deformation has already occurred. The residual stress state influences the workpiece properties regarding fatigue life and corrosion resistance. Compressive stresses are to be preferred since tensile stresses applied must first exceed the level of the residual compressive stresses before the material would be loaded at all [29]. The influence of the vibration amplitude in LVAM and LTVAM on the surface residual stresses in the feed, as well as in its corresponding normal direction, is shown in Fig. 12 for peripheral and slot milling. In slot milling (Fig. 12  left), the compressive residual stresses on the surface rise with higher amplitudes for both LVAM and LTVAM. The longitudinal vibration component causes repeated impacts between the tool and the bottom surface. These impacts have an effect similar to shot peening, thus creating higher compressive residual stresses. LVAM shows a rise in compressive stresses in feed direction from 240 MPa for conventional milling to 508 MPa with an amplitude A l of 12 μm. In LTVAM, on the other hand, the compressive stresses in feed direction increase from 240 to 465 MPa at a vibration amplitude A l of 11.4 μm. The lower compressive stresses in LTVAM may be explained by the reduced contact time between the tool and the workpiece due to the torsional vibration component and its correspondingly higher reduction of cutting forces. The reduced contact time in vibration-assisted milling also results in a lower temperature in the process zone, as has already been described by [26]. Figure 14 shows temperatures measured with thermoelements that were embedded in the workpiece for LVAM and LTVAM. The thermoelements were placed in drilled holes at a distance of 0.1 mm from the milled surface. Although the measured temperatures do not represent the temperatures in the cutting zone (as these are much higher), it is possible to conclude that the heat transfer into the workpiece is lower for both LVAM and LTVAM than for conventional milling. LTVAM shows a greater drop in temperature, mainly due to a lower tool-workpiece contact time and reduced friction. The lower heat transfer into the workpiece and the corresponding lower temperatures also contribute to higher compressive residual stresses because high temperatures lead to tensile residual stresses. In peripheral milling, the effect of the ultrasonic vibration on the residual stresses of the side wall showed a different effect than in slot milling. The resulting residual stresses for different vibration amplitudes are depicted in Fig. 12 (right) for LVAM. With higher amplitudes, the residual stresses tend to become less compressive. This can be explained by reduced cutting forces, and thus lower mechanical loads on the surface. In comparison with slot milling, in peripheral milling, there is no impact mechanism through the vibration that causes higher compressive residual stresses.
The surface hardness correlates with the measured residual stresses. Figure 13 provides the Vickers hardness for LVAM for the side wall and the bottom surface. On the bottom surface, the hardness increases from HV 322 to HV 359 with rising amplitude because of the hardening effect of the tool-workpiece impacts. On the side wall, the hardness decreases from HV 328 to HV 322 with rising amplitude. The lower cutting forces with rising amplitude lead to a lower hardness (Fig. 14).
Burr formation A burr is a part of the material that remains attached to the edge of a workpiece after the machining process [6]. As the deburring process of machined parts is time consuming and expensive, burr formation should be minimized [32]. In this study, the burr height at the downmilling side is analyzed. The burr height was measured at 5 different defined points at the edge of a workpiece and the average burr height was calculated. Figure 15 presents the result in relation to different cutting speeds as well as  At higher cutting speeds, no significant differences in burr height between vibration-assisted milling and conventional milling were observed. The mechanisms of burr formation in milling are very complex and are not yet fully understood [14], but it has already been stated that the top burr height increases with a higher friction coefficient. Thus, vibrationassisted machining can reduce burr formation as it reduces the friction between the tool and the workpiece.

Effect on tool wear
Due to the poor thermal conductivity of titanium, a considerable amount of the heat generated during machining is dissipated via the tool, which leads to high thermal loads on the cutting edge and promotes chemical reactions between the workpiece and the cutting edge. In addition, the low modulus of elasticity combined with high tensile strength causes a high load on the cutting edges, resulting in high tool wear. As shown in Fig. 16, vibration-assisted machining has a significant influence on the tool wear.
For peripheral milling (Fig. 16 top), the primary cutting edge was analyzed in regard to abrasive flank wear, adhesion wear, and chipping. Both LVAM and LTVAM showed less tool wear compared with conventional dry milling. With LTVAM, the milling distance was increased from 12 to 15 m (+ 20%) until a wear mark of 0.20 mm was reached. LVAM increased the tool life to 14.5 m traverse in feed direction (+ 17.2%). The predominant tool wear mechanism was abrasive flank wear. Occasionally, chipping was observed along the cutting edge. Abrasion wear mostly occurs due to the friction between the tool and the workpiece. Because of the lower cutting forces and temperatures, as well as the lower friction between the tool and the workpiece in vibration-assisted milling, abrasive wear is reduced. LTVAM demonstrates better performance than LVAM because of even lower forces and temperatures. Furthermore, adhesive wear in the form of built-up edge was reduced in LTVAM and LVAM. Adhesive wear occurs when a part of the workpiece material adheres to the tool because of high pressures, high temperatures, and a high chemical affinity between the tool and the workpiece. The lower temperatures and cutting forces and the reduced Fig. 16 Tool wear for conventional milling, LVAM, and LTVAM on the primary (top) and minor (bottom) cutting edges friction in vibration-assisted milling significantly reduced the occurrence of built-up edges, whereas conventional milling showed small amounts of built-up layers. Another factor that could have caused the reduced tool wear in VAM is the lower contact time between the tool and the workpiece, as diffusion mechanisms are suppressed if there is no contact. For slot milling, different wear mechanisms were observed (Fig. 16 bottom). In comparison with conventional milling, both LVAM and LTVAM showed higher flank wear. The tool life decreased in LTVAM from 11 to 9 m traverse (− 18.2%) and in LVAM to 8 m (− 33.3%) until a wear mark of 0.20 mm was reached. The predominant factor in increasing the flank wear seems to be the longitudinal part of the vibration, which creates a ploughing force on the flank face of the milling tool. LTVAM shows slightly less tool wear which is because of the lower friction and temperature in comparison with LVAM. At cutting lengths above 4 m, occasional chipping on the tool nose was observed in LVAM and LTVAM. Chipping occurs due to high mechanical stresses and high temperatures at the cutting edge. These stresses lead to microscale cracks, which will eventually cause chipping through crack propagation. Although the temperature is lower in LVAM and LTVAM than that in Fig. 17 Images of the tool wear for conventional milling, LVAM, and LTVAM on the primary (left) and minor (right) cutting edges conventional milling, the probability of chipping is higher. This may be due to the mechanical loads that are caused by the longitudinal vibration component. The longitudinal vibration causes high-frequency impacts between the minor cutting edge and the workpiece that enhance the formation and propagation of microcracks, which eventually will lead to chipping of the outer cutting edge (Fig. 17).

Conclusion and outlook
This paper presents an approach to enhance the machining performance during milling of materials that are difficult to cut, such as Ti-6Al-4V. An ultrasonic actuator for superimposing longitudinal and longitudinal-torsional vibrations on an end mill is shown. The resulting kinematics of the milling tool is described. Experimental results for peripheral milling and slot milling allow the following conclusions: • Cutting forces decrease significantly in vibration-assisted milling of Ti-6Al-4V. In LVAM, an average maximum decrease in the cutting force of 44.3% can be observed for peripheral milling. A positive correlation between the cutting forces and the contact time between the tool and the workpiece was observed. A higher contact time leads to less force reduction. LTVAM leads to a further decrease in cutting forces (57%), as the torsionalvibration component leads to a lower contact ratio. • The bottom surface roughness of the slot-milled specimens decreases from R a = 0.9 to 0.78 μm (LVAM) and 0.75 μm (LTVAM) with a vibration amplitude A l of 4 μm. With a further increase in vibration amplitude, the surface roughness increases. The surface roughness of the side wall improves for both LVAM and LTVAM with increasing vibration amplitude. • LVAM and LTVAM can significantly increase the compressive residual stresses and the surface hardness in slot milling. For peripheral milling, the ultrasonic vibration only has a small influence on residual stresses. • Burr formation can be slightly reduced by vibration assistance. • Vibration assistance increases the tool wear of the minor cutting edges, whereas the tool wear of the primary cutting edges is reduced by up to 20%. LTVAM consistently shows lower tool wear than LVAM.
The reductions in cutting forces in LVAM and LTVAM, even in the region without an interruption of the cutting process, need further investigation and modeling in order to get a better understanding of the friction forces between the tool and the workpiece and its influence on the chip formation. In the region of an interrupted cutting process, different cutting fluids and coolants have a significant potential to further improve process performance, as the vibration may make the cutting zone more accessible for the coolant. Future research will investigate the influence of cryogenic cooling or minimum quantity lubrication on the process.
Funding information Open Access funding provided by Projekt DEAL. This work was funded by the Deutsche Forschungsgemeinschaft (DFG) within the research project "Machining of highperformance materials with ultrasonically modulated cutting speed" (Project number 406283248).
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creativecommonshorg/licenses/by/4.0/.