Application of Fluoride Technology for Processing of Off-Grade Aluminum Raw Materials

We used the process of hydrofluoride desilication for off-grade aluminum raw materials widely distributed in the Komi Republic. The optimal ratios of fluorinating agent (NH4HF2) to the target component (SiO2) were determined by the method of differential thermal analysis. At a fluorination temperature 300 °C and timing 30 min, we obtained concentrates containing up to 80% Al2O3 and up to 10% SiO2.


Introduction
One of the most important problems of Russian aluminum industry is the deficit of high-quality alumina raw materials, forcing to import it from other countries.
A major source of alumina raw materials is the Vezhayu-Vorykvinskoe and Verkhneshchugorskoe bauxite deposits, which are part of the Vorykvinskaya group of deposits in Middle Timan and developed by the United Company RUSAL. Mined bauxites are predominantly consumed for alumina production by the Bayer method.
The share of low-quality sintered bauxites is significant and amounts from 5 to 55% of balance reserves for Vezhayu-Vorykvinskoe and Verkhneshchugorskoe deposits. A sharp reduction in consumption of sintered bauxites makes an alternative processing a rather actual question. In addition, the prospected reserves contain a significant amount of off-balance ores, off-grade in quality: high-silica low-modulus (better M Si 2.6-3.8) bauxites and associated high-aluminous allites.
Gravitational, flotation, magnetic, chemical, and other methods have been proposed to enrich the bauxites, but their use for enriching Middle Timan bauxite is limited due to a fine size of the minerals, a large proportion of amorphous phases, and a small efficiency of used processes in general .
Fluoride technologies are one of the most promising ways to process mineral raw materials (Dyachenko and Kraidenko 2007;Medkov et al. 2011). The purpose of the researchto assess the prospects for the use of fluorination to desilicate off-grade aluminum raw materials (bauxite, allite, kaolinite clays), which are widespread in the Komi Republic.

Methods and Approaches
The objects of research -representative samples of bauxite, allite, kaolinite clays from the Vezhayu-Vorykvinskoe (V-V), Verkhneshchugorskoe (Vsch) deposits and occurrences of the Izhma area (IA). Samples were grinded in a disk eraser (ID-200) and separated by size classes 0.125-0.250 and 0.25-0.5 mm. Analytical work was carried out by the equipment of the Center for Collective Use GeoScience of the Institute of Geology Komi SC UB RAS using XRD, XRF, DTA. Fluorination was carried out in a tube furnace equipped with a gas-extraction system. Ammonium hydrodifluoride (NH 4 HF 2 ) was used as a fluorinating component, which is an ecologically safe matter under standard conditions.

Results and Discussion
X-ray fluorescence analysis showed that the granulometric differentiation did not lead to a change in the chemical composition and silicon module of the samples (Table 1). We diagnosed reflexes of kaolinite with hematite admixture on diffraction patterns of samples No. 1, 2, and 3, and boehmite, kaolinite with anatase admixture on the patterns of sample No. 4.
Thermodynamic calculations of fluorination of kaolinite NH 4 HF 2 are given elsewhere (Rimkevich et al. 2016). However, the theoretical equation turns out to be complicated in stoichiometric terms, which leads to the overconsumption of the fluorination component. Our works on fluorination of titanium ores of the Yarega deposit in the Komi Republic showed the efficiency of applying the ratio calculation to the target component-silicon oxide (Perovskiy and Ignat'ev 2013;Perovskiy and Burtsev 2016). SiO 2 fluorination can be described by the following equation: We studied the process of fluorination of off-grade bauxites at molar ratios SiO 2 : NH 4 HF 2 equal to 1: 1 and 1: 1.5 with the help of DTA. We established that ratio 1:1 was preferred. Excessive ammonium fluoride (1:1.5) did not result in a positive effect, but was accompanied by passivation of fluorination reactions and formation of a larger volume of gaseous products.
Taking into account DTA data, the temperature regime of fluorination consisted of sintering the sample with NH 4 HF 2 at temperature 200°C (30 min.) with subsequent sublimation of resulting salt (NH 4 ) 2 SiF 6 at 300°C (30 min.). Upon completion of the fluorination, we carried out water leaching, which allowed transferring the undecomposed fluoroammonium salts into the solution.
The results of fluorination, given in Table 2, show that SiO 2 content is significantly reduced in the samples. At the same time, the size of material does not affect the effectiveness of desilication.

Conclusions
The process of hydrofluoride desilication has been applied to off-grade aluminum raw materials widespread in the Komi Republic. The optimal ratio of NH 4 HF 2: SiO 2 equal to 1:1 was determined by DTA method. At the fluorination temperature 300°C and timing 30 min, concentrates with Al 2 O 3 content more than 70-80%, and SiO 2 -less than 10% were produced. This technology is an alternative to the acid and alkaline processing of high-siliceous aluminum raw materials. The use of fluoride technology allows not only to improve the quality of ores because of desilication, but also to obtain products that can be directly processed by electrothermal methods to silumin (Lepezin et al. 2014), ferroalloys (Bukin and Seregin 2014) and other products with high added value.
Acknowledgements. The work was carried out with the financial support of the State task "Scientific basis for effective subsoil use, development and exploration of mineral resource base,