Abstract
Total normal emittance measurements have been performed on AISI 316 L samples in temperature range 400–1050 K. Two sets of mirror finished samples, with the same average roughness, have been obtained by means of polishing wheels and metallographical procedure and then etched with different acid mixtures.
Emittance tests were carried out on all samples oxidized at 1050 K for a period of 3 and 14 hours.
Experimental results show a remarkable influence of surface finishing on the total normal emittance of oxidized samples. The influence of surface finishing becomes negligible when an electropolishing process is made after etching.
Zusammenfassung
Der normale Gesamtemissionsgrad an Proben von AISI 316 L wurde für Temperaturen von 400 bis 1060 K gemessen. Zwei Sätze von spiegelblanken Proben mit gleicher Rauhigkeit wurden mit Hilfe von Polierscheiben oder durch eine metallographische Prozedur vorbehandelt und dann mit verschiedenen Säuremischungen geätzt. An allen oxidierten Proben wurde der Emissionsgrad bei 1050 K über 3 und 14 Stunden gemessen. Die Versuche zeigen einen starken Einfluß der Oberflächenbehandlung auf den Emissionsgrad der oxidierten Proben, der jedoch zu vernachlässigen war, wenn die Proben nach dem Ätzen elektropoliert wurden.
Similar content being viewed by others
References
Bennet, H.E.: Influence of surface roughness, surface damage, and oxide films on emittance. NASA SP-55 (1964) 145–151
Wong, H.Y.; Aggarwal, S.R.: Total hemispher- ical emittance of stainless steel AISI 321. Iron Steel Inst. (1971) 635–637
Isetti, C.; Nannei, E.; Pisoni, C: Oxidation and roughness effects on the total normal emittance of stainless steel. High Temp. -High Pressures 11 (1979) 393–397
Krinninger, H.: Messung des Emissionsvermögens austenitischer Stähle für den Schnellen Natriumgekühlten Brutreaktor. Wärme- und Stoffübertrag. 3 (1970) 139–145
Brannon, Jr. R.R.; Goldstein, R.J.: Emittance of oxide layers on a metal substrate. J. Heat Transf. (1970) 257–263
Donovan, T.M.; Ashley, E.J.; Bennet, H.E.: Effect of surface damage on the reflectance of germanium in the 2650–10000 OHA region. J. Opt. Soc. Am. 53 (1963) 1403–1409
Zanzucchi, P.J.; Duffy, M.T.: Surface damage and the optical reflectance of single-crystal silicon. Appl. Opt. 17 (1978) 3477–3481
Ruffino, G.; Pisoni, C.: An apparatus for emissivity measurements. High Temp. High Pressures 8 (1976) 419–424
Alfano, G.: Apparent thermal emittance of cylindrical enclosures with and without diaphragms. Int. J. Heat Mass Transf. 15 (1972) 2671–2674
Samuels, L.E.: Modern ideal on the mechanical polishing of metals. Res. Appl. Ind. 13 (1960) 344–349
Author information
Authors and Affiliations
Additional information
Research sponsored by C.N.R.-Consiglio Nazionale delle Ricerche, Roma, Italy
Rights and permissions
About this article
Cite this article
Isetti, C., Nannei, E. Influence of surface treatments on the total normal emittance of AISI316 stainless steel. Wärme- und Stoffübertragung 14, 211–215 (1980). https://doi.org/10.1007/BF01637703
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01637703