Abstract
High Tc oxide supercdonducting filaments with high Jc were successfully prepared using a technique in which suspension spun and subjected to heating treatment. High Jc at 77 K,0 T of more than 10 4 A/cm2 was attained for Tl-(Ba,Sr)-Ca-Cu-O filaments by phase decomposition from 2223 phase to 1223 or 1234 phase, for Bi-Sr-Ca-Cu-O filaments by zone melting and for Y-Ba-Cu-O filament by Quench and Melt Growth process, respectively.
This is a preview of subscription content, log in via an institution to check access.
Preview
Unable to display preview. Download preview PDF.
References
Takei H, Torii Y, Hikata H, Sato K, Hitotsuyanagi H, Tada,K (1989) in: Ishiguro T, Kajimura K (eds) in Addvances in Superconductivity jj.SpringsVerlag,Tokyo, p. 475
Jin S, Tiefel HT, Nakahara S, Graebner JE, Bryan HMO, Fastnacht RA, Kammlott GW (1990) Appl.Phys.Lett. 56: 1287
Fujimoto H, Murakami M, Gotoh S, Koshizuka N, Oyama T, Shiohara S, Tanaka S (1989) in: Ishiguro T, Kajimura K (eds) in Addvances in Superconductivity II. Springs-Verlag,Tokyo, p-285
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1991 Springer-Verlag Tokyo
About this paper
Cite this paper
Goto, T., Yamaoka, C., Kino, Y., Iwata, S., Kojima, K. (1991). Suspension-Spun High-Tc Oxide Superconducting Filament with High Jc . In: Kajimura, K., Hayakawa, H. (eds) Advances in Superconductivity III. Springer, Tokyo. https://doi.org/10.1007/978-4-431-68141-0_157
Download citation
DOI: https://doi.org/10.1007/978-4-431-68141-0_157
Publisher Name: Springer, Tokyo
Print ISBN: 978-4-431-68143-4
Online ISBN: 978-4-431-68141-0
eBook Packages: Springer Book Archive