Abstract
This book mainly describes the fracture behavior of heat-resistant austenitic stainless steel SUS304 under high-temperature creep-fatigue, especially under the conditions that exhibit inner cracking type fracture, from the onset to the final failure. Typical damage of austenitic stainless steel SUS304 caused by creep-fatigue is grain boundary cavities, small intergranular cracks, and large cracks.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Copyright information
© 2024 The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.
About this chapter
Cite this chapter
Zhou, W., Tada, N., Sakamoto, J. (2024). Conclusions. In: Creep-Fatigue Fracture: Analysis of Internal Damage. Springer Series in Materials Science, vol 344. Springer, Singapore. https://doi.org/10.1007/978-981-97-1879-5_9
Download citation
DOI: https://doi.org/10.1007/978-981-97-1879-5_9
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-97-1878-8
Online ISBN: 978-981-97-1879-5
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)