Preparation of Ceramics Added Tailings and Electromagnetic Properties

  • M. M. Wang
  • Z. L. Zhang
  • Z. J. Xin
  • L. Fan
  • R. Li
  • M. Q. Peng
Conference paper
Part of the Springer Proceedings in Energy book series (SPE)


Electromagnetic functional ceramics added iron tailings were prepared using the burning method, and the EMWA properties were tested through the arch testing method at 2–18 GHz. It was found that the minimum reflection loss (RL) peak was −16.0 dB at 17.0 GHz, and that the thickness of ceramics was 2.00 cm. With the thickness increasing, the RL value went up, and the RL peak number also increased. The magnetic and dielectric losses of tailing powders acting as an absorbent were the main mechanisms of EMWA properties for ceramics, which could be used for electromagnetic radiation protection of architectural spaces.


Tailings Ceramics preparation Electromagnetic properties Electromagnetic wave absorption (EMWA) analysis 


  1. 1.
    S.H. Liu, J.M. Liu, X.L. Dong, Electromagnetic Wave Shielding and Absorbing Materials (Chemical Industry Press, 2007), pp. 20–40Google Scholar
  2. 2.
    A.J. Douglas, et al., IEEE Transac. Microw. Theory Techn. 50, 721 (2002)Google Scholar
  3. 3.
    S.H. Wang, et al., Environ. Sci. Technol. 29, 96–98 (2006)Google Scholar
  4. 4.
    W.J. Hao, Sci. Technol. Foreign Building Mat. 25, 74–76 (2004)Google Scholar
  5. 5.
    T. Simizu, Absorb and shield of electromagnetic wave. Econ. Technol. Book 150–180 (1989)Google Scholar
  6. 6.
    W. Wang, The micro-structure and electromagnetic property study of anti-EMI FeSiAl soft magnetic flakes (Zhejiang University, Hangzhou, 2007)Google Scholar
  7. 7.
    Y.D. Zhou, Studies on preparation, structures and characteristics of FeSiAl flaky powders (University of Electronic Science and Technology of China, Chengdu, 2004).Google Scholar
  8. 8.
    X.Z. Che, Elelctromagnetic shield and decorative function ceramic and its preparation method. CN 1699272A, China, 2005-11-23Google Scholar
  9. 9.
    C. Gao, Q. Xu, P. Ji, A kind of electromagnetic protective artificial stone. CN 103951316A, China, 2014-04-15Google Scholar
  10. 10.
    R. Yao, et al., Effects of ZnO and NiO on material properties of microwave absorptive glass-ceramic tile derived from ion ore tailings. Ceram. Int. 42(2016), 8179–8189 (2016)Google Scholar
  11. 11.
    R. Yao, et al., Preparation and characterization of novel glass-ceramic tile with microwave absorption properties from iron ore tailings. J. Magn. Mag. Mat. 378, 367–375 (2015)Google Scholar
  12. 12.
    H.B. Li, A.X. He, T.X. Deng, et al. Research on the proportioning schedule and sintering -shaping process of ceramic tile with the tailings of V-bearing titanonmagenitite. China Ceram. 35, 31–33 (1999)Google Scholar
  13. 13.
    L. Ning, Preparation and Properties of Antistatic Ceramics with High Fe2O3 Content (South China University of Technology, Guangzhou, 2013) Google Scholar
  14. 14.
    T.L. Chen, Preparation and Mechanism of Fired Bricks and Titles with Low-Silicon Iron Tailings from Western Hubei (Wuhan University of Science and Technology, 2012)Google Scholar
  15. 15.
    Y.J. Guan, The preparation and electric-magnetic properties of the multiferroic composite ceramics. Ceramics 7, 24–28 (2016)Google Scholar
  16. 16.
    C.Y. Yang, Preparation, Microstructure, Electrical and Magnetic Properties of YMnO3 Based Multiferroic Ceramics (Wuhan University of Science and Technology, 2014)Google Scholar
  17. 17.
    J.Y. Zhang, Study on the Properties of High Iron Fly-Ash and the Absorption of Cement-Based Composites Materials (Chongqing University, 2010)Google Scholar
  18. 18.
    M. Toru, et al., J. Magn. Magn. Mater. 281, 195–205 (2004)Google Scholar
  19. 19.
    Y.T. Zhu, Synthesis and Microwave Absorption Properties of Ferric Oxide/Graphene (Polyaniline) Composite Materials (Anhui University of Science and Technology, 2016)Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • M. M. Wang
    • 1
  • Z. L. Zhang
    • 1
  • Z. J. Xin
    • 1
  • L. Fan
    • 1
  • R. Li
    • 1
  • M. Q. Peng
    • 1
  1. 1.China Building Materials AcademyBeijingChina

Personalised recommendations