Different Interfaces of Primary Transition and Eutectic Transition

Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)

Abstract

Solidification interfaces of the primary phase transition and eutectic transition for Ni–B alloy were investigated by high-speed video techniques. With increasing undercooling, the interface morphology for primary phase transition changes from single tip to multi-tip and to smooth plane, while for eutectic transition, it changes from multi-dendrite to single dendrite. The interface moving velocity of primary solidification is about a constant, but it is not the case for eutectic transition. This difference indicates that the primary phase transition is controlled by far-distance diffusion mechanism while the eutectic transition is controlled by short-distance diffusion mechanism. The different controlling mechanisms imply that under a similar undercooling, the velocity of an eutectic transition is much higher than that of a primary transition.

Keywords

Undercooling Solidification interface Eutectic 

Notes

Acknowledgements

The authors are grateful for the Natural Science Foundation of China (Nos. 51401156 and 51671151) and the Science and Technology Program of Shaanxi Province (No. 2016KJXX-87).

References

  1. 1.
    J.F. Xu, F. Liu, D. Zhang, In situ observation of solidification of undercooled hypoeutectic Ni–Ni3B alloy melt. J. Mater. Res. 28, 1891–1902 (2013)CrossRefGoogle Scholar
  2. 2.
    J.F. Xu, F. Liu, B. Dang, Phase selection in undercooled Ni-3.3 wt Pct B alloy melt. Metall. Mater. Trans. A 44, 1401–1408 (2013)CrossRefGoogle Scholar
  3. 3.
    T. Aoyama, K. Kuribayashi, Rapid solidification processes of semiconductors from highly undercooled melts. Metall. Mater. Trans. A 304–306, 231–234 (2001)Google Scholar
  4. 4.
    K. Nagashio, M. Li, K. Kuribayashi, Containerless solidification and net shaping by splat quenching of undercooled Nd2Fe14B melts. Mater. Trans. 44, 853–860 (2003)CrossRefGoogle Scholar
  5. 5.
    K. Nozaki, K. Nagashio, K. Kuribayashi, In-situ observation of solidification behaviour from undercooled α-Fe2Si5 melt using an electromagnetic levitator. Rev. Adv. Mater. Sci. 18, 439–443 (2008)Google Scholar
  6. 6.
    W. Löser, T.G. Woodcock, O. Shuleshova, R. Hermann, H.G. Lindenkreuz, B. Gehrmann, S. Schneider, T. Volkmann, Metastable solidification in undercooled liquid droplets of Fe-Ni based soft-magnetic alloys under terrestrial and microgravity conditions. J. Phys: Conf. Ser. 327, 111–118 (2011)Google Scholar
  7. 7.
    D.M. Herlach, B. Feuerbacher, Non-equilibrium solidification of undercooled metallic melts. Adv. Space Res. 4, 255–262 (1991)CrossRefGoogle Scholar
  8. 8.
    M. Li, K. Nagashio, K. Kuribayashi, Reexamination of the solidification behavior of undercooled Ni–Sn eutectic melts. Acta Mater. 50, 3241–3252 (2002)CrossRefGoogle Scholar
  9. 9.
    L. Liu, J.F. Liu, Y.H. Zhou, Solidification interface morphology pattern in the undercooled Co–24.0 at.% Sn eutectic melt. Acta Mater. 59, 5558–5567 (2011)CrossRefGoogle Scholar
  10. 10.
    C.R. Clopet, R.F. Cochrane, A.M. Mullis, Spasmodic growth during the rapid solidification of undercooled Ag-Cu eutectic melts. Appl. Phys. Lett. 102, 384–393 (2013)CrossRefGoogle Scholar
  11. 11.
    H.R. Peng, M.M. Gong, Y.Z. Chen, F. Liu, Thermal stability of nanocrystalline materials: thermodynamics and kinetics. Int. Mater. Rev. 66, 303–333 (2017)CrossRefGoogle Scholar
  12. 12.
    X.L. Xu, F. Liu, Nonequilibrium solidification, grain refinements, and recrystallization of deeply undercooled Ni-20 At. Pct Cu alloys effects of remelting and stress. Metall. Mater. Trans. A 10, 4777–4785 (2017)Google Scholar
  13. 13.
    B. Dang, X. Zhang, Y.Z. Chen, C.X. Chen, H.T. Wang, F. Liu, Breaking through the strength ductility trade-off dilemma in an Al-Si-based casting alloy. Sci. Rep. 6, 30874 (2016)CrossRefGoogle Scholar
  14. 14.
    Y.Z. Chen, A. Herz, Y.J. Li, C. Borchers, P. Choi, D. Raabe, R. Kirchheim, Nanocrystalline Fe–C alloys produced by ball milling of iron and graphite. Acta Mater. 61, 3172–3185 (2013)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  1. 1.School of Materials and Chemical EngineeringXi’an Technological UniversityXi’anPeople’s Republic of China

Personalised recommendations