Application of Grain Boundary Diffusion Method into High-Throughput Synthesis Materials Chip for Sintered Nd–Fe–B Magnets

  • Xing Yu
  • Guang Feng
  • Yifei Zhu
  • Lei Zhao
  • Yunhai Jia
  • Haizhou Wang
Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)

Abstract

Grain boundary diffusion method is usually applied on the sintered Nd–Fe–B magnets via surface attachment of compounds by Dy or Tb or other heavy rare earth elements. These elements could penetrate into the magnet through the grain boundary under the diffusion treatment at high temperatures above the melting point of the Nd-rich magnet phase. In this investigation the surface attachment method, the diffusion condition, the depth distribution of the diffusion element and the microstructure of the magnet were investigated. On the basis of the results and discussion, it is proposed that the sintered Nd–Fe–B magnets can be utilized to synthesize gradient changing materials chip by a heat treatment process in a single sample. The reasons are that that during the grain boundary diffusion process, there are in parallel the diffusion process of heavy rare earth elements at the grain boundary and the diffusion and substitution process within the main phase grains. The difference of the diffusion rates between the two processes can be adjusted by changing the temperature and time of the diffusion treatment. The thickness, type and combination of the rare earth/non rare earth element compounds attached to the sample surface can be decided accordingly. Finally, the micro-region units at different depth are along the diffusion direction exhibit gradient or different composition-structure-properties, hence the aim to achieve high-throughput synthesis the Nd–Fe–B materials chip by the grain boundary diffusion method could be realized.

Keywords

Sintered Nd–Fe–B Grain boundary diffusion High-throughput synthesis Materials chip 

Notes

Acknowledgements

This research was supported by the National Key Research and Development Program of China (No. 2016YFB0700203).

References

  1. 1.
    M. Sagawa, S. Fujimura, N. Togawa et al., New material for permanent magnets on a base neodymium and iron. J. Appl. Phys. 55, 2083–2087 (1984)CrossRefGoogle Scholar
  2. 2.
    S. Hirosawa, Y. Matsuura, H. Yamamoto et al., Magnetization and magnetic anisotropy of R2Fe14B measured on single crystals. J. Appl. Phys. 59, 873–879 (1986)CrossRefGoogle Scholar
  3. 3.
    H. Sepehriamin, T. Ohkubo, K. Hono, Grain boundary structure and chemistry of Dy-diffusion processed Nd–Fe–B sintered magnets. J. Appl. Phys. 107, 873-264 (2010)Google Scholar
  4. 4.
    D. Li, S. Suzuki, T. Kawasaki et al., Grain interface modification and magnetic properties of Nd-Fe-B sintered magnets. Jpn. J. Appl. Phys. 47, 7876–7878 (2008)CrossRefGoogle Scholar
  5. 5.
    U.M.R. Seelam, T. Ohkubo, T. Abe et al., Faceted shell structure in grain boundary diffusion-processed sintered Nd–Fe–B magnets. J. Alloy. Compd. 617, 884–892 (2014)CrossRefGoogle Scholar
  6. 6.
    H. Sepehri-Amin, T. Ohkubo, K. Hono, The mechanism of coercivity enhancement by the grain boundary diffusion process of Nd–Fe–B sintered magnets. Acta Mater. 61, 1982–1990 (2013)CrossRefGoogle Scholar
  7. 7.
    D. Li, M. Nishimoto, S. Suzuki et al., Coercivity enhancement of Nd-Fe-B sintered magnets by grain boundary modification via reduction-diffusion process. Mater. Sci. Eng. 1, 012020 (2009)Google Scholar
  8. 8.
    A.G. Popov, D.Y. Vasilenko, T.Z. Puzanova et al., Effect of diffusion annealing on the hysteretic properties of sintered Nd-Fe-B magnets. Phys. Met. Metall. 111, 471–478 (2011)CrossRefGoogle Scholar
  9. 9.
    M. Soderžnik, K.Ž. Rožman, S. Kobe et al., The grain-boundary diffusion process in Nd–Fe–B sintered magnets based on the electrophoretic deposition of DyF3. Intermetallics 23, 158–162 (2012)CrossRefGoogle Scholar
  10. 10.
    Z. Samardžija, P. Mcguiness, M. Soderžnik et al., Microstructural and compositional characterization of terbium-doped Nd-Fe-B sintered magnets. Mater. Charact. 67, 27–33 (2012)CrossRefGoogle Scholar
  11. 11.
    M. Komuro, Y. Satsu, H. Suzuki, Increase of coercivity and composition distribution in fluoride-diffused NdFeB sintered magnets treated by fluoride solutions. IEEE Trans. Magn. 46, 3831–3833 (2010)CrossRefGoogle Scholar
  12. 12.
    H. Suzuki, Y. Satsu, M. Komuro, Magnetic properties of a Nd–Fe–B sintered magnet with Dy segregation. J. Appl. Phys. 105, 07A734–07A734-3 (2009)CrossRefGoogle Scholar
  13. 13.
    X. Sun, X. Bao, X. Gao et al., Effect of dysprosium addition by pack cementation on magnetic properties and microstructure of Nd-Fe-B sintered magnets. J. Chin. Rare Earth Soc. 27, 86–91 (2009)Google Scholar
  14. 14.
    K. Löewe, C. Brombacher, M. Katter et al., Temperature-dependent Dy diffusion processes in Nd–Fe–B permanent magnets. Acta Mater. 83, 248–255 (2015)CrossRefGoogle Scholar
  15. 15.
    H. Nakamura, K. Hirota, T. Ohashi et al., Coercivity distributions in Nd-Fe-B sintered magnets produced by the grain boundary diffusion process. J. Phys. D Appl. Phys. 44, 064003 (2011)CrossRefGoogle Scholar
  16. 16.
    X. Fang, Effects of Grain Boundary Structure and Chemistry on the Coercivity of NdFeB Materials. (Shanghai Jiao Tong University, 2011)Google Scholar
  17. 17.
    E. Niu, Z.A. Chen, X.Z. Ye et al., Anisotropy of grain boundary diffusion in sintered Nd-Fe-B magnet. Appl. Phys. Lett. 104, 2909–2911 (2014)Google Scholar
  18. 18.
    T.H. Kim, S.R. Lee, H.J. Kim et al., Simultaneous application of Dy-X, (X = F or H) powder doping and dip-coating processes to Nd–Fe–B sintered magnets. Acta Mater. 93, 95–104 (2015)CrossRefGoogle Scholar
  19. 19.
    K. Hirota, H. Nakamura, T. Minowa et al., Coercivity enhancement by the grain boundary diffusion process to Nd–Fe–B sintered magnets. IEEE Trans. Magn. 42, 2909–2911 (2006)CrossRefGoogle Scholar
  20. 20.
    N. Oono, M. Sagawa, R. Kasada et al., Production of thick high-performance sintered neodymium magnets by grain boundary diffusion treatment with dysprosium–nickel–aluminum alloy. J. Magn. Magn. Mater. 323, 297–300 (2011)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Xing Yu
    • 1
    • 2
    • 3
  • Guang Feng
    • 1
    • 2
    • 3
  • Yifei Zhu
    • 1
    • 2
    • 3
  • Lei Zhao
    • 1
    • 2
    • 3
  • Yunhai Jia
    • 1
    • 2
    • 3
  • Haizhou Wang
    • 1
    • 2
    • 3
  1. 1.Beijing Advanced Innovation Center of Materials Genome EngineeringBeijingChina
  2. 2.Central Iron and Steel Research InstituteBeijingChina
  3. 3.Beijing Key Laboratory of Metal Materials CharacterizationBeijingChina

Personalised recommendations