Metallurgical Controlling of La in a Superalloy

  • Yong-ji Niu
  • Hai-wen Liu
  • Zhi-wei Zhang
  • Ning An
  • Yang Gao
  • Jian-jun Tian
Conference paper

Abstract

In this paper, the burning law of La in VIM + ESR double-smelting-processing was studied in an alloy containing La. The results showed that the added La was almost burn out when added in after the refining in a vacuum induction melting process. However, when La was added at the end of smelting and before tapping, La can be effectively preserved. The burning rules of electroslag remelting slag system of CaF2:Al2O3, CaF2:Al2O3:CaO and CaF2:Al2O3:CaO:La2O3 was examined, and the results showed that the recovery rate of the first two slag series La was between 13 and 19%, and the burning loss of the two slag series La was not very different. The recovery rate of La in the slag system with La2O3 was 10–13%, the loss of La was significantly over the previous two large slag systems. But in terms of the La uniform in different parts of alloy ingot the slag containing La2O3 was the best.

Keywords

Superalloy VIM ESR La 

References

  1. 1.
    Guo Jian-ting, solid solution strengthening wrought Co-based alloy GH5188, high temperature alloy materials science (2), science and Technology Press, 2010, 30–34.Google Scholar
  2. 2.
    Editorial board of China aviation materials, GH5188, Aviation Materials Manual (The Second Volume Wrought Superalloy Casting Superalloy), China Standard Press, 2001, P510.Google Scholar
  3. 3.
    K. BHANU SANKARA RAO, M.G. CASTELLI, G.P. ALLEN, and J.R. ELLIS, A Critical Assessment of the Mechanistic Aspects in HAYNES 188 during Low-Cycle Fatigue in the Range 25 °C to 1000 °C, METALLURGICAL AND MATERIALS TRANSACTIONS A, 1997,VOLUME 28A, 347–361.Google Scholar
  4. 4.
    Shu Yi, The Preliminary Studies on GH188 Alloy Process, Structure and Properties Used in Rings, Aerospace and Aerospace, 1999, Issue third, 6–13.Google Scholar
  5. 5.
    Wang Zhongyuan, Zhang Weiqiang, Xin Xin, et al. Microstructure and Homogenization Process of GH188 alloy. Journal of ShenYang Ligong University, 2011, 30 (6): 12–16.Google Scholar
  6. 6.
    Dai Tongfu, Wang Shuhe, Shi Changxu, Effect of ESR on the Chemical Composition Nearby Grain Boundary in a Co-based superalloy. Journal of Metals, 1984, 20 (1): A47 to A53.Google Scholar
  7. 7.
    Meng Zhaobin, Wang Zhigang, Zeng Bingsheng, Study on Lanthanide Precipitate Type and Magnesium Segregation to Grain Boundary in Cobalt-Base Superalloy GH188, Journal of Iron and Steel Research, 1999, 11 (3): 30–33.Google Scholar
  8. 8.
    Huang Xihu. Principle of Ferrous Metallurgy. Beijing: Metallurgical Industry Press, 1987, P9.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yong-ji Niu
    • 1
    • 2
  • Hai-wen Liu
    • 2
  • Zhi-wei Zhang
    • 2
  • Ning An
    • 2
  • Yang Gao
    • 2
  • Jian-jun Tian
    • 2
  1. 1.University of Science and Technology BeijingBeijingChina
  2. 2.Beijing Beiye Functional Materials CorporationBeijingChina

Personalised recommendations