Hot Deformation Behavior of NiCr19Co6W10Ti3AlB Superalloy

  • Min Yu
  • Kaihong Cai
  • Zhenrui Li
  • Donghui Xie
Conference paper


NiCr19Co6W10Ti3AlB alloy is a kind of precipitation hardening nickel-base superalloy, also is a kind of high temperature and high elasticity alloy. The chemical elements of the alloy composition is very complex, it includes more than 4.5% aging strengthening elements of Al and Ti, and nearly 37% solid solution strengthening elements of Cr, W, Co etc. Because of composition segregation in the alloy ingot, the difficulty of hot working is faced. In this paper, the composition segregation and homogenization annealing process of cast NiCr19Co6W10Ti3AlB alloy were studied. The dendrite segregation and its elimination method were investigated by homogenization annealing experiment. High temperature plastic deformation behavior of NiCr19Co6W10Ti3AlB alloy was also studied in this paper. By thermal simulation compression test, the thermal deformation behavior and microstructure change under different deformation conditions were analyzed, which provides a good reference for practical production.


NiCr19Co6W10Ti3AlB superalloy Homogenization annealing Thermal simulation 


  1. 1.
    Zhang Ming-yuan, Sun Jian-chun et al. Effect of aging on the mechanical property of NI36CrTIAl alloy, J. Journal of Functional Materials, S2(44) (2013) 198–200.Google Scholar
  2. 2.
    F. Diologent, P. Caron, T. d’Almeida, A. Jacques, P. Bastie. The γ/γ′ mismatch in Ni based superalloys: In situ measurements during a creep test, J. Nuclear Inst. and Methods in Physics Research, B, 2002.Google Scholar
  3. 3.
    T Link, A Epishin, U Brückner, P Portella. Increase of misfit during creep of superalloys and its correlation with deformation, J. Acta Materialia. 8 (2000).Google Scholar
  4. 4.
    Pyczak, Florian, Neumeier, Steffen, G ken, Mathias. Influence of lattice misfit on the internal stress and strain states before and after creep investigated in nickel-base super alloys containing rhenium and ruthenium, J. Journal of Materials Science. 2009.Google Scholar
  5. 5.
    PAN Xiao-lin, YU Hai-yan, TU Gan-feng, SUN Wen-ru, HU Zhuang-qi. Segregation and diffusion behavior of niobium in a highly alloyed nickel-base super alloy, J. Nonferrous Met. Soc. China, 21 (2011) 2402–2407.Google Scholar
  6. 6.
    Pyczak, F, Devrient, B, Mughrabi. H. The effects of different alloying elements on the thermal expansion coefficients, lattice constants and misfit of nickel-based superalloys investigated by X-ray diffraction, J. Superalloys, 2004.Google Scholar
  7. 7.
    Rikizo Watanabe, Yoshitaka Chiba, Kuno T. Alloy design of nickel-base solution strengthened superalloys, J. Trans ISIJ. 1976.Google Scholar
  8. 8.
    Shibuya S, Kaneno Y, Yoshida M. Dual multi-phase intermetallic alloys composed of geometrically close packed Ni3X(X:Al, Ti and V)type structures-II Mechanical properties, J. Acta Materialia. 2006.Google Scholar
  9. 9.
    Lee D, Santella M L. Thermal aging effects on the mechanical properties of as-cast Ni3Al-based alloy, J. Journal of Materials Science. 2006.Google Scholar
  10. 10.
    Yin-ben HAN, Xiang-yi XUE, Tie-bang ZHANG, Rui HU, Jin-shan LI. Effects of hot compression on carbide precipitation behavior of Ni − 20Cr − 18 W − 1Mo superalloy, J. Nonferrous Met. Soc. China, 26 (2016) 2883–2891.Google Scholar
  11. 11.
    LI Bo, WANG Wenhao, CHEN Congping, WU Haihua, YE Xicong, SUN Yu. Hot Compression Deformation Behavior of New Type Ni-Cr-Co-Mo Alloy, J. Hot Working Technology 46(7) (2017) 55–59.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  1. 1.Beijing Beiye Functional Materials CorporationBeijingChina

Personalised recommendations