Research and Manufacture of Short-Flow Hot Extrusion Forming and Seamless Pipe for GH3625 Superalloy

  • Yubi Gao
  • Yutian Ding
  • Bin Meng
  • Zhengyi Dou
  • Xin Gao
  • Zhi Jia
Conference paper
First Online:

Abstract

In order to obtain GH3625 superalloy seamless pipe, the GH3625 superalloy seamless pipe with Φ28 × 5.5 mm was developed through short-flow hot extrusion forming and cold rolling molding process. And a comprehensive evaluation for the microstructure and mechanical properties of GH3625 superalloy seamless pipe was conducted. The results showed that the hollow tube has been successfully extruded the GH3625 superalloy tube with Φ43 × 9.5 mm under the condition of fixed extrusion speed of 50 mm/s, preheating temperature of 1150 °C and extrusion ration of 7.4. The alloy tube was composed of a small amount of deformation twin and a large number of equiaxed crystal mixed crystal structure, the average grain size was about 8.6, and the tensile strength at room temperature and elongation at break were 771 MPa and 52.33%, respectively, showing good cold working performance and mechanical properties. The performance of GH3625 superalloy seamless pipe after cold rolling and annealing is in accordance with ASTM-B163-04 international standard.

Keywords

GH3625 superalloy Short-flow Hot extrusion Cold rolling deformation Seamless pipe 
This is a preview of subscription content, log in to check access.

Notes

Acknowledgements

This study was funded by the National Natural Science Foundation of China (No. 51661019), The Science and Technology Projects of Gansu Province (No. 145RTSA004), the State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology.

References

  1. 1.
    H.B. Zhang, Inconel 625 alloy progress abroad, [J]. Spec. Steel Technol. 3 (2000) 69–80.Google Scholar
  2. 2.
    J. Ye, Nickel Base Superalloy [M]. Beijing: Science press, 1978, pp 228.Google Scholar
  3. 3.
    X.J. Di, X X Xing, B S Wang, Nucleation and coarsening mechanism of δ phase in Inconel 625 deposited metal, [J]. Acta Metall. Sin. 3 (2014) 323–328.Google Scholar
  4. 4.
    J. Mittra, J.S. Dubey, S. Banerjee, Acoustic emission technique used for detecting early stages of precipitation during aging of Inconel 625[J]. Scr. Mater., 49(12) (2003) 209–1214.Google Scholar
  5. 5.
    R. Cozar, M. Rouby, B. Mayonobe, et al. Mechanical Properties, Corrosion Resistance and Microstructure of Both Regular and Titanium Hardened 625 Alloys[C]//Superalloys. 1991.Google Scholar
  6. 6.
    Q.M. Guo, H.T. Li, D.F. Li, et al. Hot extrusion moulding process and microstructure evolution of GH625 superalloy tubes, [J]. Rare Metals. 35(5) (2011) 684–689.Google Scholar
  7. 7.
    X.B. Huang, Research on manufacture process of G3 seamless steel tube, [J].Spec. Steel Technol., 14(3) (2008) 17–20.Google Scholar
  8. 8.
    Z.T. Wang, S H Zhang, M Cheng, et al. Study on technology and microstructure of superalloy GH4169 during tube coating extrusion, [J]. Forging & Stamping Technolgy. 35(4) (2010) 48–51.Google Scholar
  9. 9.
    P X Zhang, Development and application of new forging technology of Nickel base superalloy, [J]. Hot Working Technology. 5 (2016) 11–13.Google Scholar
  10. 10.
    P.X. Zhang, Development and application of new forging technology of Nickel base superalloy, [J]. Hot Working Technology. 5 (2016) 11–13.Google Scholar
  11. 11.
    M. Cai, J.P. Liu, X.J. Wu et al. Technical study on GH625 alloy forging, Journal of Shenyang Aerospace University. 28(4) (2011) 52–59.Google Scholar
  12. 12.
    G.H. Xu, M.Z. Pei, Y.J. Yang et al. Hot-extrusion process for GH202 Nickel-based alloy seamless tube, [J]. Hot Working Technology. 40(1) (2011) 90–91.Google Scholar
  13. 13.
    W.M. Mao, Metal Recrystallization and Grain Growth, [M]. Metallurgical Industry Press, 1994.Google Scholar
  14. 14.
    X.Y. Ye, J.X. Dong, M.C. Zhang, Cold deformation of GH738 alloy and its recrystallization behavior during intermediate annealing, [J].Rare. Metal. Mat. Eng. 42(7) (2013) 1423–1428.Google Scholar
  15. 15.
    C.H. Peng, H. Chang, R.Hu, et al. Static recrystallization kinetics of Haynes 230 superalloy, J. Aeronaut. Mater. 31(2) (2011) 8–12.Google Scholar
  16. 16.
    Z.Q. Wang, Y.J. Yang, S.X. Tian, et al. Influence of cold drawing process on microstructures and tensile properties of alloy GH3625, J. Iron. Steel. Res. Int. 23 (2011) 92–95.Google Scholar
  17. 17.
    Y.X. Zhao, Cold deformation behavior of GH625 alloy and their effects on the mechanical properties, J. Mater. Eng. 9 (2000) 36–37.Google Scholar
  18. 18.
    Z.Q. Cui, B.X. Liu, Metallurgy and Heat treatment Theogy, Harbin Institute of Technology Press, 2004.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yubi Gao
    • 1
  • Yutian Ding
    • 1
  • Bin Meng
    • 1
  • Zhengyi Dou
    • 1
  • Xin Gao
    • 1
  • Zhi Jia
    • 1
  1. 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous MetalsLanzhou University of TechnologyLanzhouChina

Personalised recommendations

Cite paper

Buy options