Abstract
In this paper understanding of the role of inclusions in the consolidation process of powder composite is attempted. A nickel base superalloy powder was mixed with alumina particles and consolidated by hot isostatic pressing. Densification kinetics were estimated from interrupted HIP tests, and compacted specimens were observed by microscopy. Simple compression tests were also performed at high temperature on dense samples. From these results explanations for the retardation in densification due to the inclusions are suggested.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
Bouvard D. and Lafer M., Determination of the densification kinetics of metal powders by interrupted hot isostatic pressing tests. Powder Metal. Int., 1989, 21, pp. 11–15.
Bouvard D., Cheynet M.C. and Saint-Antonin F., Densification behaviour of argon atomized powders during hot isostatic pressing. In Proceedings of the 3rd Int. Conf. on Isostatic Pressing. MPR Publishing Services, Stratford/Avon, 1986.
Lange F.F., Atteraas L., Zok F., and Porter J.R., Deformation consolidation of metal powders containing steel inclusions. Acta Metall. Mater., 1991, 39, pp. 209–219.
Bouvard D. and Lange F.F., Correlation between percolation and particle coordination in binary powder mixtures. Submitted to Acta Metall. Mater., 1991.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1992 Elselvier Science Publishers Ltd
About this paper
Cite this paper
Lafer, M., Bouvard, D., Stutz, P., Pierronnet, M., Raisson, G. (1992). Densification Behaviour of Particle-Reinforced Superalloy Powder During Hot Isostatic Pressing. In: Koizumi, M. (eds) Hot Isostatic Pressing— Theory and Applications. Springer, Dordrecht. https://doi.org/10.1007/978-94-011-2900-8_32
Download citation
DOI: https://doi.org/10.1007/978-94-011-2900-8_32
Publisher Name: Springer, Dordrecht
Print ISBN: 978-1-85166-744-4
Online ISBN: 978-94-011-2900-8
eBook Packages: Springer Book Archive