Effect of Intergranular Microstructure on Properties of Si3N4 Based Composite Ceramic Materials

  • E. Maria Knutson-Wedel
  • Lena K. L. Falk
  • Tommy Ekström


The microstructures of Si3N4 based ceramic materials containing ZrO2 have been characterized by analytical electron microscopy and x-ray diffractometry. The ceramics were fabricated by hot isostatic pressing (HIP) and contained different additions of Al2O3, AlN and Y2O3 as sintering additives. Ceramics fonned without the separate addition of Y2O3 were densinfied in the presence of a transient liquid phase; these microstructures contained an extremely small volume fraction of residual glass. Increased volumes of intergranular glass fonned in materials containing larger additions of separately added Y2O3. These larger glass volumes had a negative influence on hardness. Formation of prismatic β-Si3N4 grains was promoted by additions of Y2O3 either separately or in the form of Y2O3 stabilized ZrO2 starting powder. This morphology of the Si3N4, as well as larger additions of ZrO2, increased toughness.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    M.H. Lewis and R.J. Lumby, “Nitrogen ceramics: liquid phase sintering”. Powder. Met., 1983, 26, 73.CrossRefGoogle Scholar
  2. 2.
    F.F. Lange, “Dense Si3N4: interrelation between phase equilibria, microstructure and mechanical properties”. In Nitrogen Ceramics, ed. F.L. Riley, Noordhoff, Leyden, 1977, pp.491.CrossRefGoogle Scholar
  3. 3.
    W.D. Kingery, “Densification during sintering in the presence of a liquid phase”. J. Appl. Phys., 1959, 30, 301CrossRefGoogle Scholar
  4. 4.
    M.H. Lewis, B.D. Powell, P. Drew, R.J. Lumby, B. North and A.J. Taylor, “The formation of single-phase Si-Al-O-N ceramics”. J. Mater. Sci., 1977, 12, 61.CrossRefGoogle Scholar
  5. 5.
    L.K.L. Falk and G.L. Dunlop, “Crystallisation of the Glassy Phase in a Si3N4 Material by Post-Sintering Heat Treatments”. J. Mater. Sci., 1987, 22, 4369CrossRefGoogle Scholar
  6. 6.
    R.A.L. Drew, S. Hampshire and K.H. Jack, “Nitrogen glasses”. In Special Ceramics, ed. D. Taylor and P. Popper, Proc. Brit. Ceram. Soc., 1981, 31, 119.Google Scholar
  7. 7.
    T. Ekström, L.K.L. Falk and E.M. Knutson-Wedel,, “Si3N4-ZrO2 Composites with Small Al2O3 and Y2O3 Additions-Prepared by HIP”. Accepted for publication in J. Mater. Sci. Google Scholar
  8. 8.
    G.R. Anstis, P. Chantikul, B.R. Lawn and D.B. Marshall, “A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements”. J. Amer. Cer. Soc., 1981, 64, 533.CrossRefGoogle Scholar
  9. 9.
    L.K.L. Falk and M. Holmstrom, “Microstructural Development During Processing of a Si3N4/ZrO2 Material”. In Euroceramics, ed. G. de With, R.A. Terpstra and R. Metselaar, Elsevier Applied Science, London, 1989, pp. 1.373.Google Scholar
  10. 10.
    E. M. Knutson, L.K.L. Falk, H. Bjorklund and T. Ekström, “Si3N4 Ceramics Formed by HIP using Different Oxide Additions — Relation between Microstructure and Properties”. Accepted for publication in J. Mater. Sci. Google Scholar
  11. 11.
    E. M. Knutson, L.K.L. Falk and T. Ekström, “Microstructures of Si3N4 Ceramics Formed by HIP”. In Euroceramics, ed. G. de With, R.A. Terpstra and R. Metselaar, Elsevier Applied Science, London, 1989, pp. 1.416Google Scholar
  12. 12.
    F.F. Lange, “Compressive Surface Stresses Developed in Ceramics by an Oxidation-Induced Phase Change”. J. Amer. Cer. Soc., 1980, 63, 38.CrossRefGoogle Scholar
  13. 13.
    F.F. Lange, L.K.L. Falk and B.I. Davis, “Structural ceramic composites based on Si3N4-ZrO2(+Y2O3) compositions”. J. Mater. Res., 1987, 2, 66.CrossRefGoogle Scholar
  14. 14.
    M.H. Lewis, A.R. Bhatti, R.J. Lumby and B. North, “The microstructure of sintered Si-Al-O-N ceramics”. J. Mater. Sci., 1980, 15, 103.CrossRefGoogle Scholar

Copyright information

© Elsevier Science Publishers Ltd and MPA Stuttgart 1992

Authors and Affiliations

  • E. Maria Knutson-Wedel
    • 1
  • Lena K. L. Falk
    • 1
  • Tommy Ekström
    • 2
  1. 1.Department of PhysicsChalmers University of TechnologyGöteborgSweden
  2. 2.AB Sandvik Hard MaterialsStockholmSweden

Personalised recommendations