Abstract
Both uncoated and coated exposed panels were taken out after 18 m of exposure from sites. No appreciable changes were noted for coated panels exposed at all the sites. However, for coated and scribed panels a light attack of rust was visible along scribed lines. Rust product developed at all sites was brownish, loosely bound on MS and adherent brownish black on WS (Table 3.1). Uncoated panels had different pitting attack and WS exhibited less pitting marks than MS. The variation of pitting densities and distribution at different sites depended on the material and the environment prevalent at the site.
The results obtained from experiments as recorded in Chapter 3 are discussed in three parts viz. field tests, laboratory tests and simulation tests.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Madlangbayan, M., Otsuki, N., Saito, T., Min, A.K.: Corrosion behaviour of coated steel plates with defects exposed to marine environment. J. Soc. Mat. Sc. 58(5), 437–442 (2009)
Knotkova, D.: Atmospheric corrosion of metals, American Society for Testing and Materials 767, Philadelphia, p. 7 (1982)
Kihira, H., Ito, S., Murata, T.: Passive rust layer on low alloy steel exposed in atmospheric environment. Corros. Sci. 31, 383–388 (1990)
Nishimura, T., Katayama, H., Noda, K., Kodama, T.: Electrochemical behaviour of rust formed on carbon steel in a wet/dry environment containing chloride ions. Corros. Sci. 56, 935 (2000)
Macdonald, J.R.: Impedance spectroscopy and its use in analysing the steady state AC restorage of solid and liquid electrolytes. J. Electrochem. Soc. 223, 25 (1987)
Selected Powder Diffraction Data for Metals & Alloys Data Book, 1st. Edn., vol I & II, JCPDS International Centre for Diffraction Data, USA
International Table for X ray Crystallography, Kyonoch Press, Birmingham, vol. 3, p. 161 (1962)
Loader, J.: Basic Laser Raman Spectroscopy. Heyden and Son, London (1970)
Gui, J., Devine, T.M.: Proceedings of 12th International Corrosion Congress, NACE, p 2052 (1993)
Dunnwald, J., Otto, A.: An investigation of phase transition in rust layers using Raman spectroscopy. Corros. Sci. 29, 1167–1176 (1989)
Ohtsuka, T., Kubo, K., Sato, N.: Raman spectroscopy of thin corrosion films on iron at 100 to 150 °C in air. Corrosion 42, 476–481 (1986)
Ohtsuka, T.: Raman spectra of passive films of iron in neutral borate solution. Mat. Trans. JIM. 37, 67(1996)
Brown, C.W., Heidersbach, R.H.: Raman spectra of possible corrosion products of iron. Appl. Spectrosc. 32(6), 532–535 (1978)
Boucherit, N., Delicher, P., Joiret, S., Hugot, A.: Mater. Sci. Forum 51, 44 (1989)
Faria, D.L.A., Silva, S.V., Oliveira, M.T.: Raman spectroscopy of some iron oxides and oxyhydroxides. J. Raman. Spectrosc. 28, 873–878 (1997)
Sato, N.: An overview on passivity of metals. Corros. Sci. 31, p1 (1990)
Jones, D.A.: Principles and Prevention of Corrosion. Prentice Hall, USA (1996)
Goidanich, S., Lazzari, L., Ormellese, M., Pedeferri, M.: Influence of AC on corrosion kinetics for carbon steel, zinc and copper, Corrosion 5 and 2 (2005)
Sam, C.S., Balaya, P.: Investigation of structural disorder in electrode materials. http://www.nus.edu.sg/nurop/2009/FoE/U066456W.PDF (2010) Accessed Jan 2010
Matsubara, E., Suzuki. S., Waseda. Y.: Corrosion mechanism of iron from an X ray structural viewpoint. Book on Characterisation of Corrosion Products on Steel Surfaces
Ohtsuka, T.: Passivation oxide films and rust layers on iron. Characterization of Corrosion Products on Steel Surfaces, Springer, Heidelberg (2006)
Pourbaix, M.: Atlas of Electrochemical Equilibria in Aqueous Solutions. Pergamon, New York (1966)
Leygraf, C., Graedel, T.: Atmospheric corrosion. J. Electrochem. Soc. 1497, 1010 (2000)
Thibeau, R.J., Brown, C.W., Heidersbach, R.H.: Raman spectra of possible corrosion products of iron. Appl. Spectrosc. 32, 532 (1978)
Dong, J.H., Han, E.H., Ke, W.: Progress in research on rust layer of weathering steel. Corros. Sci. 18, 414 (2006)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Copyright information
© 2013 Springer India
About this chapter
Cite this chapter
Saha, J.K. (2013). Field Exposure Test. In: Corrosion of Constructional Steels in Marine and Industrial Environment. Engineering Materials. Springer, India. https://doi.org/10.1007/978-81-322-0720-7_4
Download citation
DOI: https://doi.org/10.1007/978-81-322-0720-7_4
Published:
Publisher Name: Springer, India
Print ISBN: 978-81-322-0719-1
Online ISBN: 978-81-322-0720-7
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)