Flat Glass as a Construction Material

  • Chapter
Glass Structures

  • 1582 Accesses

Abstract

Glass is a product of fusion. In nature it occurs as solidified volcanic lava and was used by humans in the manufacture of jewellery and other objects at least as long as 5000 years ago. Glass in a hot, viscous state can be formed by mechanical processes into planar, linear or compact semi-finished products. All the products manufactured from glass and used in the construction industry — these include profiled glass and glass blocks but mostly flat glass — are classed as construction materials. Over 70 percent of all flat glass is used in new buildings or in the renovation of building skins. [3.1/1]

This is a preview of subscription content, log in via an institution to check access.

Access this chapter

Log in via an institution

Institutional subscriptions

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. Klindt, L. B.; Klein, W.: Glas als Baustoff, Cologne 1977, pp. 10 et seqq.

    Google Scholar 

  2. Petzold, A.; Marusch, H.; Schramm, B.: Der Baustoff Glas, Berlin 1990, p. 13

    Google Scholar 

  3. DIN EN 572, Glass in Building, Basiserzeugnisse aus Kalk-Natronglas, Berlin 2004

    Google Scholar 

  4. Wörner, J.-D.; Schneider, J.; Fink, A.: Glasbau — Grundlagen, Berechnung, Konstruktion, Berlin 2001, pp. 61–76

    Google Scholar 

  5. Sedlacek, G.: Glas im Konstruktiven Ingenieurbau, Berlin 1999, pp. 23 et seq.

    Google Scholar 

  6. Button, D.; Pye, B.: Glass in Building, Oxford 1993, p. 215

    Google Scholar 

  7. Heiringhoff, R: Reflexion und andere optische Phänomene von Glas, Studienarbeit am Lehrstuhl Tragkonstruktionen, RWTH Aachen 2001, pp. 16, 20, 25

    Google Scholar 

  8. Schittich, Chr.; Staib, G.; Balkow, D.; Schuler, M.; Sobek, W.: Glass Construction Manual, Basel, Boston, Berlin 1999, p. 115

    Google Scholar 

  9. The calculation of the g-value is in accordance with European standards EN 410 and ISO 9050.

    Google Scholar 

  10. Wurm, J. P.: Archioptix, Kleine Einführung in die Optik für Architekten, Heidelberg 2003

    Google Scholar 

  11. DIN EN 673, January 2001; Glass in Building — Determination of Thermal Transmittance (U value) — Calculation Method (German version)

    Google Scholar 

  12. Winter, M.: “Farbiges Glas”, in: ARCH+, vol. 134/135, December 1996, pp. 110 et seqq.

    Google Scholar 

  13. DIN EN 572-4, November 1994; Basic soda lime silicate glass products — Drawn sheet glass (German version)

    Google Scholar 

  14. Technical information OPALIKA, Schott AG, 2004

    Google Scholar 

  15. Technical information IMERA and ARTISTA, Schott AG, 2004

    Google Scholar 

  16. Hager, W.: Saint-Gobain Glass, “Werk Mannheim setzt auf die Solartechnik”, in: GFF vol. 10/2002, p. 100

    Google Scholar 

  17. Hübinger, A.: Glasbearbeitung — über das Trennen, Schleifen, Bohren und Biegen von Glas, Studienarbeit am Lehrstuhl für Tragkonstruktionen, RWTH Aachen 2002

    Google Scholar 

  18. Veer, F. A.; Zuidema, J.: The strength of glass, effect of edge quality, Glass Processing Days 2003

    Google Scholar 

  19. Bucak, O.: Gutachterliche Stellungnahme zur gebogenen Überkopfverglasung beim Bauvorhaben Neubau Loggia Wasseralfingen, FH Munich, 2002

    Google Scholar 

  20. Kasper, P.: “Die Polygenese elementarer Bauformen”, in: GFF-Zeitschrift für Glas Fenster Fassade, 10/2002, pp. 28 et seq.

    Google Scholar 

  21. Scholze, Th.: Reversibel gekrümmte Verbundglaselemente, Diplomarbeit am Institut für leichte Flächentragwerke, University of Stuttgart 2000, p. 132

    Google Scholar 

  22. DIN 1259-1, Glass — Part 1: Terminology for glass types and groups, Issue 2001–09 (German version)

    Google Scholar 

  23. DIN EN 12150-1, Glass in building — Thermally toughened soda-lime silicate safety glass, Part 1: Defi nition and description, Issue 2000–11 (German version)

    Google Scholar 

  24. DIN EN 1863-1, Glass in building — Heat-strengthened soda-lime silicate glass, Part 1: Defi nition and description, Issue 2000–03 (German version)

    Google Scholar 

  25. Kasper, A.: Spontanbruch von Einscheibensicherheitsgläsern am Bau — ein lösbares Problem, Tagungsband Glas im Konstruktiven Ingenieurbau 2, FH Munich, November 2001

    Google Scholar 

  26. Wörner, J.-D.; Schneider, J.; Fink, A.: Glasbau — Grundlagen, Berechnung, Konstruktion, Berlin 2001, pp. 13 et seq.

    Google Scholar 

  27. Richtlinie zur Beurteilung der visuellen Qualität von Glas im Bauwesen, Bundesinnungsverband des Glaserhandwerks und Bundesverband Flachglas, Version June 2004

    Google Scholar 

  28. Technical information berlinglas, http://www.berlinglas.de

  29. Technical information BI-Color, BI-ThermColor, BGT Bischoff Glastechnik, 2004

    Google Scholar 

  30. Glashandbuch von Flachglas Markenkreis, Issue 2004, pp. 146 et seq.

    Google Scholar 

  31. Scholze, Th.: “Thermische Veredelung von Flachglas”, in: GLASS II, Pub.: Verband Deutscher Maschinen-und Anlagenbau e.V. (VDMA) und Messe Düsseldorf GmbH, 2002, pp. 128–141

    Google Scholar 

  32. Technical information Tambest, 2004

    Google Scholar 

  33. Scheideler, J.: “Die Statik gebogenen Glases”, in: Glaswelt 08/2000

    Google Scholar 

  34. DIN EN ISO 12543-1 to-6, Glass in building — Laminated glass and laminated safety glass, Parts 1 to 6, Issue 1998–08 (German version)

    Google Scholar 

  35. Brockmann, W.: “Flachglas-Veredelung durch Fügen”, in: GLASS II, Pub.: Verband Deutscher Maschinen-und Anlagenbau e.V. (VDMA) und Messe Düsseldorf GmbH, 2002, pp. 160 et seq.

    Google Scholar 

  36. Handbuch der Trosifol AG, http://www.trosifol.com/ger/handbuch

  37. Bucak, Ö.: “Glas im konstruktiven Ingenieurbau”, in: Stahlbaukalender 1999, Berlin 1999, pp. 534 et seq.

    Google Scholar 

  38. Bucak, Ö.; Heger, F.: “Fassaden”, in: Stahlbaukalender 2003, Berlin 2003, pp. 632 et seq.

    Google Scholar 

  39. Schuler, Chr.; Gräf, H.: “Verbundtragverhalten von VSG”, paper at seminar Glas im Konstruktiven Ingenieurbau at FH Munich on 8 November 2001

    Google Scholar 

  40. Bohmann, D.: Ein numerisches Verfahren zur Berechnung von Verbundglasscheiben, Dissertation at Lehrstuhl für Stahlbau, RWTH Aachen, 1999

    Google Scholar 

  41. Product information Vanceva Design-Folien, Solutia, 2002

    Google Scholar 

  42. Product information Sentry Glass Expressions, DuPont, 2002

    Google Scholar 

  43. Technical information Gesellschaft für Licht und Bautechnik mbH, Cologne 2000

    Google Scholar 

  44. Technical information PRIVA-LITE von SGG Germany, 2002

    Google Scholar 

  45. Haase, W.: Smart Materials — “Intelligente” Werkstoffe, Anwendungsmöglichkeiten in Hüllsystemen, Proc. GlasKon Munich 2003, pp. 12–23

    Google Scholar 

  46. Erban, Chr.: Photovoltaik zur Gebäudeintegration, Proc. GlasKon Munich 2001, pp. 23–27

    Google Scholar 

  47. Scheideler, J.: “Verfahren zur Veränderung der Flachglasoberfl äche”, in: GLASS II, Pub.: Verband Deutscher Maschinen-und Anlagenbau e.V. (VDMA) and Messe Düsseldorf GmbH, 2002, pp. 144–157

    Google Scholar 

  48. Product information “Sunenergy” and “Sungate” from PPG and “Sunguard” from Guardian, 2002

    Google Scholar 

  49. Technical information Amiran, SCHOTT AG, 2004

    Google Scholar 

  50. Reuters, N.: James Carpenter — “Glas und Licht”, student research project at the Lehrstuhl für Tragkonstruktionen, RWTH Aachen 2000, pp. 111–114

    Google Scholar 

  51. Technical information Prinz Optics GmbH, 2000

    Google Scholar 

  52. Technical information Spacia, Nippon Sheet Glass http://www.nsg-spacia.co.jp

  53. Product information GEWE-therm TPS, Scholl Glas, 2004

    Google Scholar 

  54. Siebert, G.: Entwurf und Bemessung von tragenden Bauteilen aus Glas, Berlin 2001, pp. 98–110

    Google Scholar 

  55. Product information Thermur HM, Glasfi scher, 2004

    Google Scholar 

  56. Product information Kapilux, Okatech and Okalux, Okalux GmbH, 2004

    Google Scholar 

  57. Product information Micro solar control louvre, Siteco Beleuchtungstechnik GmbH, 2004

    Google Scholar 

  58. Haase, W.: “Smart Materials”, in: Proc. GlasKon 2003, pp. 18 et seq.

    Google Scholar 

  59. The weighted sound reduction index RW is determined in accordance with DIN EN 20140-3, Issue 1995–05 and DIN EN ISO 717-1, Issue 1997–01.

    Google Scholar 

Download references

Rights and permissions

Reprints and permissions

Copyright information

© 2007 Birkhäuser Verlag AG

About this chapter

Cite this chapter

(2007). Flat Glass as a Construction Material. In: Glass Structures. Birkhäuser Basel. https://doi.org/10.1007/978-3-7643-8317-6_3

Download citation

  • DOI: https://doi.org/10.1007/978-3-7643-8317-6_3

  • Publisher Name: Birkhäuser Basel

  • Print ISBN: 978-3-7643-7608-6

  • Online ISBN: 978-3-7643-8317-6

  • eBook Packages: Architecture and DesignEngineering (R0)

Publish with us

Policies and ethics

Search

Navigation