Abstract
In the usual tests to determine strength or lifetime under tension, bending or compression loading a uniaxial stress state is present. In components very often multi-axial stresses occur. Also under uniaxial external loading multiaxial stresses are possible, for instance in notched components. Rotating structures and components under internal pressure exhibit multiaxial stresses. Also thermal stresses are in general multiaxial. In this section, failure criteria under multiaxial loading are presented.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
Sauter, J., Kuhn, P. (1991): Formulierung einer neuen Theorie zur Bestimmung des Fließ- und Sprödbruchversagens bei statischer Belastung unter Angabe der Übergangsbedingung, Z. angew. Math. Mech. 71, T383 - T387.
Takagi, J., Shaw, M.C. (1983): Brittle fracture initiation under complex stress states, Trans. ASME, J. Engng. Ind. 105, 143–149.
Shaw, M.C., Avery, J.P. (1986): Tensile fracture loci for brittle material containing spherical voids, Trans. ASME, J. Engng. Mater. Technol. 108, 222–229.
Timoshenko, S.P., Goodier, J.N. (1970): Theory of Elasticity, McGraw-Hill Kogakusha, Japan.
Paul, B., Mirandy, L. (1976): An improved fracture criterion for three-dimensional stress state, Trans. ASME, J. Engng Mater. Technol. 98, 159–163.
Petrovic, J.J. (1985): Mixed-mode fracture of hot-pressed Si3N4, J. Am. Ceram. Soc. 68, 348–355.
Shetty, S.K., Rosenfield, A.R., Duckworth, W.H. (1987): Mixed-mode fracture in biaxial stress state: Application of the diametral-compression (brazilian disk) test, Engng. Fract. Mech. 26, 825–840.
Alpa, G. (1984): On a statistical approach to brittle rupture for multiaxial states of stress, Engng. Fract. Mech. 19, 881–901.
Batdorf, S.B., Crose, J.G. (1974): A statistical theory for the fracture of brittle structures subjected to nonuniform stress, J. Appl. Mech. 41, 459–461.
Batdorf, S.B., Heinisch, H.L. (1978): Weakest link theory reformulated for arbitrary fracture criterion, J. Am. Ceram. Soc. 61, 355–358.
Evans, A.G. (1978): A general approach for the statistical analysis of multiaxial fracture, J. Am. Ceram. Soc. 61, 302–308.
Matsuo, Y. (1981): A probabilistic analysis of fracture loci under bi-axial stress state, Bull. JSME 24, 290–294.
Gyekenyesi, J.P., Nemeth, N.N. (1987): Surface flaw reliability analysis of ceramic components with the SCARE finite element postprocessor program, Trans. ASME, J. Engng. Gas Turbines and Powers 109, 247–281.
Lemon, J. (1988): Statistical approaches to failure of ceramics reliability assessment, J. Am. Ceram. Soc. 71, 106–112.
Heger, A., Brückner-Foit, A., Munz, D. (1991): STAU — ein Programm zur Berechnung der Ausfallwahrscheinlichkeit mehrachsig beanspruchter keramischer Komponenten als Post-Prozessor für Finite-Elemente-Programme, Internal Report, Institute for Reliability and Failure Analysis, University of Karlsruhe, Germany.
Thiemeier, T., Brückner-Foit, A., Kölker, H. (1991): Influence of the fracture criterion on the failure prediction of ceramics loaded in biaxial flexure, J. Am. Ceram. Soc. 74, 48–52.
Brückner-Foit, A., Heger, A., Munz, D. (1996): On the contribution of notches to the failure probability of ceramic components, J. Europ. Ceram. Soc. 16, 1027–1034.
Giovan, M.N., Sines, G. (1981): Strength of a ceramic at high temperatures under biaxial and uniaxial tension, J. Am. Ceram. Soc. 64, 68–73.
Schmitt, W., Blank, K., Schönbrunn, G. (1983): Experimentelle Spannungsanalyse zum Doppelringversuch, Sprechsaal 116, 397–405.
Fessier, H., Fricker, D.C. (1984): A theoretical analysis of the ring-on-ring loading disc test, J. Am. Ceram. Soc. 67, 582–588.
Soltész, U., Richter, H., Kienzier, R. (1987): The concentric-ring test and its application for determining the surface strength of ceramics, in High Tech Ceramics, Elsevier Science Publishers, Amsterdam 149–158.
Chao, L.Y., Shetty, D.K. (1991): Reliability analysis of structural ceramics subjected to biaxial flexure, J. Am. Ceram. Soc. 74, 333–344.
Shetty, K.D., Rosenfield, A.R., McGuire, P., Duckworth, W.H. (1980): Biaxial flexure test for ceramics, Am. Ceram. Soc. Bulletin 59, 1193–1197.
Shetty, K.D., Rosenfield, A.R., McGuire, Bansal, G.K., Duckworth, W.H. (1981): Biaxial fracture studies of a glass ceramic, J. Am. Ceram. Soc. 64, 1–4.
de With, G, Wagemans, H.H.M. (1989): Ball-on-ring test revisited, J. Amer. Ceram. Soc. 72, 1538–1541.
Carneiro, F.L.L.B., Barcellos, A. (1949): Résistance à la traction des bétons, Instituto Nacional de Technologia, Rio de Janeiro.
Wright, P.J.F. (1955): Comments on an indirect tensile test on concrete cylinders, Magazine of Concrete Research 7, 87–96.
Shaw, M.C., Braiden, P.M., De Salvo, G.J. (1975): The disk test for brittle materials, Trans. ASME, J. Basic Engng. Industry, 77–87.
Hondros, G. (1959): The evaluation of Poisson’s ratio and the modulus of materials of a low tensile resistance by the Brazilian (indirect tensile) test with particular reference to concrete, Australian J. Appl. Sci. 10, 243–268.
Marion, R. H., Johnstone, J.K. (1977): A parametric study of the diametral compression test for ceramics, Am. Ceram. Soc. Bull. 56, 998–1002.
Spriggs, R.M., Brissette, L.A., Vasilos, T. (1964): Tensile strength of polycrystal-line ceramics by the diametral compression test, J. Mater. Res. Stand. 4, 218.
Szendi-Horvath, G. (1980): Fracture toughness determination of brittle materials using small to extremely small specimens, Engng. Fract. Mech. 13, 955–961.
Petroski, H.J., Ojdrovic, R.P. (1987): The concrete cylinder: Stress analysis and failure modes, Int. J. Fract. 53, 263–279.
Brückner-Foit, A., Fett, T., Munz, D., Schirmer, K. (1997): Discrimination of multiaxiality criteria with the Brazilian disc test, J. Europ. Ceram. Soc. 17, 689–696.
Sato, S., Awaji, H., Kawamata, K., Kurumada, A., Oku, T. (1987): Fracture criteria of reactor graphite under multiaxial stresses, Nuclear Engng. Design 103, 291–300.
Ely, R.E. (1972): Strength of titania and aluminum silicate under combined stresses, J. Am. Ceram. Soc. 55, 347–350.
Adams, M., Sines, G. (1976): Determination of biaxial compressive strength of a sintered alumina ceramic, J. Am. Ceram. Soc. 59, 300–304.
Broutman, L.J., Krishnakuman, S.M., Mallick, P.K. (1970): Effects of combined stresses on fracture of alumina and graphite, J. Am. Ceram. Soc. 53, 649–654.
Stout, M.G., Petrovic, J.J. (1984): Multiaxial loading fracture of A12O3 tubes: I, experiments, J. Am. Ceram. Soc. 67, 14–18.
Ikeda, K., Igaki, H. (1984): Fracture criterion for alumina ceramics subjected to triaxial stresses, J. Am. Ceram. Soc. 67, 538–544.
Ikeda, K., Igaki, H., Kuroda, T. (1986): Fracture strength of alumina ceramics under uniaxial and triaxial stress states, Am. Ceram. Soc. Bull. 65, 683–688.
Schirmer, K.S. (1995): Entwicklung von Versagenskriterien fur keramische Bauteile unter mehrachsiger Belastung, Thesis, University of Karlsruhe, Germany, Fortschritt-Berichte VDI Nr 174, Reihe 18, VDI-Verlag, Düsseldorf, Germany.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1999 Springer-Verlag Berlin Heidelberg
About this chapter
Cite this chapter
Munz, D., Fett, T. (1999). Multiaxial Failure Criteria. In: Munz, D., Fett, T. (eds) Ceramics. Springer Series in Materials Science, vol 36. Springer, Berlin, Heidelberg. https://doi.org/10.1007/978-3-642-58407-7_10
Download citation
DOI: https://doi.org/10.1007/978-3-642-58407-7_10
Publisher Name: Springer, Berlin, Heidelberg
Print ISBN: 978-3-642-63580-9
Online ISBN: 978-3-642-58407-7
eBook Packages: Springer Book Archive