Abstract
The evolution of damage in laminated fiber reinforced composites is a complex phenomenon, which involves interaction of different modes of failure like fiber breakage, matrix cracking, fiber-matrix debonding and delamination. In the present work the effect of fiber volume fraction and different damage mechanisms such as fiber breakage, fiber-matrix debond and matrix cracks on the effective properties of unidirectional fiber-reinforced composites is predicted based on a micromechanical analysis. The material properties are calculated using a three-dimensional micromechanical representative volume element (RVE). A finite element based progressive damage model is developed to predict failure behavior of a laminate in respective load-constraint conditions. The proposed model also helps to determine where and how failure occurs first and how the damage evolves. Hashin’s and Puck’s failure models are used for laminated composite plates of various stacking sequences and their respective numerical results are compared. The influences of the failure criteria and material degradation model are studied through a numerical analysis. The case studies considered vary from a unidirectional laminate with a hole, laminates with single bolt lap joint.
This is a preview of subscription content, log in via an institution.
Buying options
Tax calculation will be finalised at checkout
Purchases are for personal use only
Learn about institutional subscriptionsReferences
V. Murari, C. Upadhyay, Micromechanics based ply level material degradation model for unidirectional composites. Compos. Struct. (Elsevier). 94, 671–680 (2012)
V. Murari, C. Upadhyay, Micromechanics based diffuse damage model for unidirectional composites. Compos. Struct. (Elsevier). 96, 419–432 (2013)
L. Harish, A. Rajagopal, Computational Homogenization and Failure Modeling of Periodic Composites. Master Thesis, Indian Institute of Technology Hyderabad (2012)
S.A. Bhalchandra, Y. Shiradhonkar, S.S. Daimi, Comparison of properties of transversely isotropic lamina using method of cells and composite cylinder assemblage. Int. J. Adv. Sci. Technol. SERSC 64, 43–58 (2014)
W. Wu, J. Owino, Applying Periodic Boundary Conditions in Finite Element Analysis. SIMULIA Community Conference (2014)
D. Gay, S.V. Ho, S.W. Tsai, Composite Materials Design and Applications (CRC Press LLC, 2003)
R.M. Jones, Mechanics of Composite Materials (Taylor & Francis, 1998)
U.P. Jabir, Damage Prediction in Fiber Reinforced Composites (Indian Institute of Technology, Hyderabad, 2013)
A.S. Kaddour, M.J. Hinton, Maturity of 3d failure criteria for fiber reinforced composites: Comparison between theories and experiments: Part b of wwfe-ii. J. Compos. Mater. 47(6–7), 925–966 (2013)
E.A. Alexandros, K. Christoph, P.P. Theodore, Mechanical behavior of glass/epoxy tubes under combined static loading. part ii: Validation of FEA progressive damage model. Compos. Sci. Technol. 69(13), 2248–2255 (2009)
Z. Libin, Q. Tianliang, Z. Jianyu, A.S. Ramanand, Modified maximum stress failure criterion for composite joints. J. Compos. Mater. 47(23), 2995–3008 (2013)
G. Catalanotti, P.P. Camanho, A.T. Marques, Three-dimensional failure criteria for fiber-reinforced laminates. Compos. Struct. 95, 63–79 (2013)
Q. Tianliang, Z. Libin, Z. Jianyu, Fastener effects on mechanical behaviors of double-lap composite joints. Compos. Struct. 100, 413–423 (2013)
J. Meisam, C. Gergely, R.W. Michael, Numerical modeling of the damage modes in ud thin carbon/glass hybrid laminates. Compos. Sci. Technol. 94, 39–47 (2014)
P.F. Liu, Z.P. Gu, Y.H. Yang, X.Q. Peng, A nonlocal finite element model for progressive failure analysis of composite laminates. Compos. B Eng. 86, 178–196 (2016)
Z. Hashin, Failure criteria for unidirectional fiber composites. J. Appl. Mech. 47(2), 329–334 (1980)
P. Giovanni, P.V. Nils, T.E. Andreas, Numerical Analyses of Low Velocity Impacts on Composite. Advanced Modelling Techniques. In Proceedings of the SIMULIA Customer Conference_2012, (2012)
Acknowledgement
The authors would like to acknowledge the financial support of Indo Russian Collaborative project grant from DST-RFBR vide project number from DST side DST/INT/RFBR/IDIR/P-11/2016 and vide project number from RFBR 16-58-48009 IND_omi.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 Springer International Publishing AG, part of Springer Nature
About this paper
Cite this paper
Reddy, K.S.S., Nasedkina, A.A., Nasedkin, A.V., Saswata, B., Rajagopal, A. (2018). Comparative Study on Progressive Damage Models for Composites. In: Parinov, I., Chang, SH., Gupta, V. (eds) Advanced Materials . PHENMA 2017. Springer Proceedings in Physics, vol 207. Springer, Cham. https://doi.org/10.1007/978-3-319-78919-4_31
Download citation
DOI: https://doi.org/10.1007/978-3-319-78919-4_31
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-78918-7
Online ISBN: 978-3-319-78919-4
eBook Packages: Physics and AstronomyPhysics and Astronomy (R0)