Screening Encapsulated Polymeric Healing Agents for Carbonation-Exposed Self-Healing Concrete, Service Life Extension, and Environmental Benefit

  • Philip Van den Heede
  • Bjorn Van Belleghem
  • Maria Adelaide Araújo
  • João Feiteira
  • Nele De Belie
Conference paper

Abstract

By incorporating encapsulated polymers in concrete, cracks can be healed autonomously upon occurrence. This is of high value for steel reinforced concrete structures subject to carbonation-induced corrosion. This paper presents the results of a rapid colorimetric screening test to assess the carbonation resistance of self-healing concretes containing encapsulated polymer-based healing agents. Four systems were tested for inhibition of further carbonation near artificially induced cracks (width: 300 μm). Next, the time to steel depassivation was assessed probabilistically in comparison with cracked concrete. With an adequately working pressurized PU precursor, the concrete would remain repair-free for at least 100 years. Subsequent life cycle assessment in SimaPro showed a potential environmental benefit (72–78%) for the ten CML-IA baseline impact categories which is mainly due to the service life extension possible with a properly working self-healing concrete.

Notes

Acknowledgments

This research under the program SHE (Engineered Self-Healing materials), project ISHECO (Impact of Self-Healing Engineered materials on steel COrrosion of reinforced concrete) was funded by SIM (Strategic Initiative Materials in Flanders) and VLAIO (Flanders Innovation & Entrepreneurship). Their financial support as well as the one from the EU 7th Framework Program (FP7/2007–2013) under grant agreement n° 309451 (HEALCON) is gratefully acknowledged.

References

  1. 1.
    Van den Heede, P., et al. (2016). Neutron radiography based visualization and profiling of water uptake in (un)cracked and autonomously healed cementitious materials. Materials, 9, 1–28.Google Scholar
  2. 2.
    Van den Heede, P., et al. (2017). Screening of different encapsulated polymer-based healing agents for chloride exposed self-healing concrete using chloride migration tests. In Proceedings of the 6th international conference on non-traditional cement and concrete (pp. 1–7). Brno.Google Scholar
  3. 3.
    Van Belleghem, B., et al. (2017). Quantification of the service life extension and environmental benefit of chloride exposed self-healing concrete. Materials, 10, 1–22.Google Scholar
  4. 4.
    Van den Heede, P., & De Belie, N. (2015). Durability based life cycle assessment of concrete with supplementary cementitious materials exposed to carbonation. In Proceedings of the international conference on sustainable structural concrete I (pp. 13–24). La Plata.Google Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  • Philip Van den Heede
    • 1
    • 2
  • Bjorn Van Belleghem
    • 1
    • 2
  • Maria Adelaide Araújo
    • 1
    • 3
  • João Feiteira
    • 1
  • Nele De Belie
    • 1
  1. 1.Magnel Laboratory for Concrete Research, Department of Structural EngineeringGhent UniversityGhentBelgium
  2. 2.Strategic Initiative Materials (SIM vzw), project ISHECO within the program ‘SHE’GhentBelgium
  3. 3.Polymer Chemistry and Biomaterials Group, Department of Organic and Macromolecular ChemistryGhent UniversityGhentBelgium

Personalised recommendations