Mechanical Performance of Fly Ash Geopolymeric Mortars Containing Phase Change Materials

  • M. Kheradmand
  • Z. Abdollahnejad
  • F. Pacheco Torgal
Conference paper

Abstract

European Union (EU) aims to achieve nearly zero-energy (public) building (NZEB) by the end of 2018. This very ambitious target would be more easily fulfilled if high-thermal performance materials like phase change materials (PCMs) are to be used. This paper reports experimental results on the mechanical properties of geopolymeric mortars containing PCMs at ambient temperature and after exposure to high temperature. The results show that the inclusion of PCMs is responsible for a reduction of the mechanical strength of the mortars. Several mixtures showed an increase in compressive strength after being exposed to high temperatures. Since PCMs are made of flammable materials, geopolymeric mortars are more advantageous than Portland cement-based mortars for PCM incorporation.

References

  1. 1.
    Hook, M., & Tang, X. (2013). Depletion of fossil fuels and anthropogenic climate change-a review. Energy Policy, 52, 797–809.CrossRefGoogle Scholar
  2. 2.
    COM. (2011). 885/2, Energy Roadmap 2050. European Commission, Brussels.Google Scholar
  3. 3.
    Lund, H., & Hvelplund, F. (2012). The economic crisis and sustainable development: The design of job creation strategies by use of concrete institutional economics. Energy, 43, 192–200.CrossRefGoogle Scholar
  4. 4.
    European Union. (2010). Directive 2010/31/EU of the European Parliament and of the Council of May 19th, 2010 on the energy performance of buildings (recast). Official Journal of the European Union.Google Scholar
  5. 5.
    Pacheco-Torgal, F. (2014). Eco-efficient construction and building materials research under the EU Framework Programme Horizon 2020. Construction and Building Materials, 51, 151–162.CrossRefGoogle Scholar
  6. 6.
    European Commission. (2011). Roadmap to a resource efficient Europe. COM (2011) 571. EC, Brussels.Google Scholar
  7. 7.
    COM. (2014, July 2). 398 final. Towards a circular economy: A zero waste programme for Europe. Communication from the commission to the European Parliament, The council, the European economic and social committee and the committee of the regions. BrusselsGoogle Scholar
  8. 8.
    Payá, J., Monzó, J., Borrachero, M., & Tashima, M. (2014). Reuse of aluminosilicate industrial waste materials in the production of alkali-activated concrete binders. In F. Pacheco-Torgal, J. Labrincha, A. Palomo, C. Leonelli, & P. Chindaprasirt (Eds.), Handbook of alkali-activated cements, mortars and concretes (pp. 487–518). Cambridge: WoddHead Publishing.Google Scholar
  9. 9.
    Bernal, S., Rodríguez, E., Kirchheim, A., & Provis, J. (2016). Management and valorisation of wastes through use in producing alkali-activated. Cement materials. Journal of Chemical Technology & Biotechnology, 91, 2365–2388.CrossRefGoogle Scholar
  10. 10.
  11. 11.
    Van Deventer, J. S., Provis, J. L., & Duxson, P. (2012). Technical and commercial progress in the adoption of geopolymer cement. Minerals Engineering, 29, 89–104.CrossRefGoogle Scholar
  12. 12.
    Pacheco-Torgal, F., Castro-Gomes, J. P., & Jalali, S. (2008). Investigations on mix design of tungsten mine waste geopolymeric binder. Construction and Building Materials, 22(9), 1939–1949.CrossRefGoogle Scholar
  13. 13.
    ASTM C618 – 15. (2015). Standard specification for coal fly ash and raw or calcined natural Pozzolan for use in concrete, ASTM International, West Conshohocken, PA. www.astm.org
  14. 14.
    Zhang, H., Xing, F., Cui, H.-Z., Chen, D.-Z., Ouyang, X., Xu, S.-Z., Wang, J.-X., Huang, Y.-T., Zuo, J.-D., & Tang, J.-N. (2016). A novel phase-change cement composite for thermal energy storage: Fabrication, thermal and mechanical properties. Applied Energy, 170, 130–139.CrossRefGoogle Scholar
  15. 15.
    Kong, D., Sanjayan, J., & Sagoe-Crentsil, K. (2007). Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures. Cement and Concrete Research, 37, 1583–1589.CrossRefGoogle Scholar
  16. 16.
    Kong, D., & Sanjayan, J. (2008). Damage behavior of geopolymer composites exposed to elevated temperatures. Cement and Concrete Composites, 30, 986–991.CrossRefGoogle Scholar
  17. 17.
    Luna-Galiano, Y., Cornejo, Y., Leiva, C., Vilches, L., & Fernández-Pereira, C. (2015). Properties of fly ash and metakaolín based geopolymer panels under fire resistance tests. Materiales de Construcción, 65(319), e059.CrossRefGoogle Scholar
  18. 18.
    Pan, Ζ., Sanjayan, J. G., & Rangan, B. V. (2009). An investigation of the mechanisms for strength gain or loss of geopolymer mortar after exposure to elevated temperature. Journal of Materials Science, 44, 1873–1880.CrossRefGoogle Scholar
  19. 19.
    Guerrieri, M., & Sanjayan, J. (2010). Behavior of combined fly ash/slag-based geopolymers when exposed to high temperatures. Journal of Fire Mater, 34, 163–175.Google Scholar
  20. 20.
    Cunha, S., Aguiar, J., & Pacheco-Torgal, F. (2015). Effect of temperature on mortars with incorporation of phase change materials. Construction and Building Materials, 98, 89–101.CrossRefGoogle Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  • M. Kheradmand
    • 1
  • Z. Abdollahnejad
    • 1
  • F. Pacheco Torgal
    • 1
    • 2
  1. 1.University of MinhoGumarãesPortugal
  2. 2.University of SungkyunkwanSuwonRepublic of Korea

Personalised recommendations