Relationship Between Applied Stress and Hydrogen-Related Fracture Behavior in Martensitic Steel

  • Yasunari Takeda
  • Takashi Yonemura
  • Yuji Momotani
  • Akinobu Shibata
  • Nobuhiro Tsuji
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

In the present study, a relationship between the applied stress and the hydrogen-related fracture behavior in an 8Ni-0.1C martensitic steel was investigated by means of constant loading tensile tests under various applied stresses ranging from 400 to 1000 MPa. The time to fracture in hydrogen charged specimens increased from 0.5 to 30.5 s with decreasing the applied stress from 1000 to 400 MPa. Area fractions of brittle fracture surfaces, especially that of intergranular fracture surface, increased as the applied stress decreased. Orientation analysis using EBSD showed that micro-cracks observed in the vicinity of the main crack initiated along prior austenite grain boundaries regardless of the applied stress. The hydrogen-related fracture processes under various applied stresses were reconstructed by fracture surface topography analysis and the results indicated that intergranular fracture was dominant under the lower applied stress, while the fracture mode changed from intergranular fracture to quasi-cleavage fracture with progress of crack propagation under the higher applied stress.

Keywords

Martensitic steel Hydrogen embrittlement Fracture surface EBSD Fracture surface topography analysis 

Notes

Acknowledgements

This study was financially supported by a Grant-in-Aid for Scientific Research (B) (No. 15H04158) and the Elements Strategy Initiative for Structural Materials (ESISM) through the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan, and Industry-Academia Collaborative R&D Program ‘Heterogeneous Structure Control: Towards Innovative Development of Metallic Structural Materials’ (No. 20100113) through the Japan Science and Technology Agency.

References

  1. 1.
    Banerji SK, McMahon C, Feng HC (1978) Intergranular fracture in 4340-type steels: effects of impurities and hydrogen. Metall Mater Trans A 9(2):237–247CrossRefGoogle Scholar
  2. 2.
    Craig BD, Krauss G (1980) The structure of tempered martensite and its susceptibility to hydrogen stress cracking. Metall Trans A 11(11):1799–1808CrossRefGoogle Scholar
  3. 3.
    Wang M, Akiyama E, Tsuzaki K (2005) Effect of hydrogen and stress concentration on the notch tensile strength of AISI 4135 steel. Mater Sci Eng A 398(1):37–46CrossRefGoogle Scholar
  4. 4.
    Wang M, Akiyama E, Tsuzaki K (2007) Effect of hydrogen on the fracture behavior of high strength steel during slow strain rate test. Corros Sci 49(11):4081–4097CrossRefGoogle Scholar
  5. 5.
    Wang G et al (2013) Hydrogen embrittlement assessment of ultra-high strength steel 30CrMnSiNi2. Corros Sci 77:273–280CrossRefGoogle Scholar
  6. 6.
    Momotani Y et al (2017) Effect of strain rate on hydrogen embrittlement in low-carbon martensitic steel. Int J Hydrog Energy 42(5):3371–3379CrossRefGoogle Scholar
  7. 7.
    Nagao A et al (2012) The role of hydrogen in hydrogen embrittlement fracture of lath martensitic steel. Acta Mater 60(13):5182–5189CrossRefGoogle Scholar
  8. 8.
    Shibata A, Takahashi H, Tsuji N (2012) Microstructural and crystallographic features of hydrogen-related crack propagation in low carbon martensitic steel. ISIJ Int 52(2):208–212CrossRefGoogle Scholar
  9. 9.
    Shibata A et al (2015) Characterization of hydrogen-related fracture behavior in As-quenched low-carbon martensitic steel and tempered medium-carbon martensitic steel. Metall Mater Trans A 46(12):5685–5696CrossRefGoogle Scholar
  10. 10.
    Shibata A et al (2017) Microstructural and crystallographic features of hydrogen-related fracture in lath martensitic steels. Mater Sci Technol 33(13):1524–1532CrossRefGoogle Scholar
  11. 11.
    Takeda Y, McMahon CJ (1981) Strain controlled vs stress controlled hydrogen induced fracture in a quenched and tempered steel. Metall Trans A 12(7):1255–1266CrossRefGoogle Scholar
  12. 12.
    Nagumo M, Matsuda H (2002) Function of hydrogen in intergranular fracture of martensitic steels. Philos Mag A 82(17–18):3415–3425CrossRefGoogle Scholar
  13. 13.
    Kobayashi T, Shockey DA (1987) A fractographic investigation of thermal embrittlement in cast duplex stainless steel. Metall Trans A 18(11):1941–1949CrossRefGoogle Scholar
  14. 14.
    Shibata A et al (2017) Fracture surface topography analysis of the hydrogen-related fracture propagation process in martensitic steel. Int J Fract 205(1):73–82CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2018

Authors and Affiliations

  • Yasunari Takeda
    • 1
  • Takashi Yonemura
    • 1
  • Yuji Momotani
    • 1
  • Akinobu Shibata
    • 1
    • 2
  • Nobuhiro Tsuji
    • 1
    • 2
  1. 1.Department of Materials Science and EngineeringKyoto UniversityKyotoJapan
  2. 2.Elements Strategy Initiative for Structural MaterialsKyoto UniversityKyotoJapan

Personalised recommendations