New Engineering Solutions in the Production of Laminated Composite Pipes for the Oil Industry

Chapter
Part of the Innovation and Discovery in Russian Science and Engineering book series (IDRSE)

Abstract

The oil industry of Russia currently needs innovative development projects intended for a radical improvement of the performance of material resources and a decrease of their consumption. One of the most promising trends in corrosion protection is the production and use of pipes made of laminated composite materials. There are several principal ways of producing them by metal forming processes. World practice shows that lining technology is reasonable for oil well tubing. Lining consists of simultaneous expansion of pipes made of dissimilar materials, which possess different properties. A pipe of the kind manages to combine high corrosion resistance and mechanical strength, and this makes its service life more than four times higher than that of pipes made by conventional methods. However, previous foreign experience of manufacturing and using these pipes prompts the necessity of improving some pipe-making processes. This paper discusses new engineering solutions in the production of lined pipes, as well as in situ testing results.

Keywords

Oil well tubing Lining Lined pipes Bimetal pipes Oil production Field conditions Service life 

References

  1. 1.
    Ioffe, A. V., Vyboishchik, M. A., Trifonova, E. A., & Suvorov, P. V. (2010). Effect of chemical composition and structure on the resistance of oil pipelines to carbon dioxide corrosion. Metal Science and Heat Treatment, 52(1–2), 46–51.CrossRefGoogle Scholar
  2. 2.
    Ioffe, A. V., Tetyueva, T. V., Vyboyshchik, M. A., Trifonova, E. A., & Lutsenko, E. S. (2010). Tubing with high corrosion resistance. Metal Science and Heat Treatment, 52(1–2), 13–19.CrossRefGoogle Scholar
  3. 3.
    Ioffe, A. V., Tetyueva, T. V., Vyboyshchik, M. A., Knyaz’kin, S. A., & Zyryanov, A. O. (2010). Corrosion-mechanical fracture of tubing from carbon and alloy steels operating in environments containing hydrogen sulfide. Metal Science and Heat Treatment, 54(9–10), 492–497.Google Scholar
  4. 4.
    Knyaz’kin, S. A., Ioffe, A. V., Vyboyshchik, M. A., & Zyryanov, A. O. (2010). Special features of corrosion fracture of tubing operating in environments with elevated content of carbon dioxide. Metal Science and Heat Treatment, 54(9–10), 498–503.Google Scholar
  5. 5.
    Ioffe, A. V., Tetyueva, T. V., Revyakin, V. A., Borisenkova, E. A., Knyaz’kin, S. A., & Denisova, T. V. (2010). Corrosion-mechanical fracture of tube steel in operation. Metal Science and Heat Treatment, 54(9–10), 512–518.Google Scholar
  6. 6.
    Smith, L. (1999). Control of corrosion in oil and gas production tubing. British Corrosion Journal, 34(4), 247–253.CrossRefGoogle Scholar
  7. 7.
    Brondel, D., Edwards, R., Hayman, A., Hill, D., Mehta, S., & Semerad, T. (1994). Corrosion in the oil industry. Oilfield review, 6(2), 4–18.Google Scholar
  8. 8.
    GOST R 52203–2004. Pump-compressor tubes and couplings for them. Specifications.Google Scholar
  9. 9.
    API Specification 5CT. Specification for casing and tubing. 8th ed, July 1, 2005. ISO 11960:2004, Petroleum and natural gas industries – Steel pipes for use as casing or tubing for wells.Google Scholar
  10. 10.
    Cerruti, S. (1998). An overview of corrosion resistant alloy steel selection and requirements for oil and gas industry. Conference: Convegno IGF XIV Trento. 1–9.Google Scholar
  11. 11.
    Craig, B. D., & Smith, L. (2011). Corrosion Resistant Alloys (CRAs) in the oil and gas industry – selection guidelines update. 3rd ed. US: The Nickel Institute.Google Scholar
  12. 12.
    Craig, B. D. (2011). Selection guidelines for corrosion resistant alloys in the oil and gas industry. Materials selection for the oil and gas industry, Nickel Institute Technical, 10(73), 1–11.Google Scholar
  13. 13.
    Safonov, V. N., & Kim, S. K. (2012). Performance of the wells of the OOO Lukoil-Komi under corrosive conditions. Inzh. Praktika, 1, 50–59.Google Scholar
  14. 14.
    Smith, L. M. (1992). Engineering with clad steel. NiDI Series, 10(064), 20.Google Scholar
  15. 15.
    Wang, X., Li, P., & Wang, R. (2005). Study on hydro-forming technology of manufacturing bimetallic CRA-lined pipe. International Journal of Machine Tools & Manufacture, 45, 373–378.CrossRefGoogle Scholar
  16. 16.
    Koning, A. C., Nakasugi, H., & Ping, L. (2004). TFP and TFT back in town (Tight Fit CRA lined Pipe and Tubing). Stainless steel world, 53–61.Google Scholar
  17. 17.
    Bogatov, N. A., Bogatov, A. A., & Salikhyanov, D. R. (2014). Corrosion-resistant lined pump and compressor pipe. Steel in Translation, 44(11), 867–869.CrossRefGoogle Scholar
  18. 18.
    Bogatov, N. A., Bogatov, A. A., & Salikhyanov, D. R. (2014). Use of the lining method to restore the service characteristic of pump-compressor tubing that has exhausted its original service life. Metallurgist, 58(11–12), 1006–1010.Google Scholar
  19. 19.
    Bogatov, N. A. Patent № 2344266 RF, IPC E21V17/01, “Method of making pump-compressor tubing”, subm. 04.17.2007, publ. 09.20.2007.Google Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  • N. A. Bogatov
    • 1
  • A. Bogatov
    • 2
  • D. R. Salikhyanov
    • 2
  1. 1.“TEMP” Limited Scientific Production AssociationMoscowRussia
  2. 2.Institute of Material Science and MetallurgyUral Federal UniversityYekaterinburgRussia

Personalised recommendations