In order to obtain the solubility of carbon in vanadium-bearing hot metal, graphite powder is used for the carburization experiments. The other kinds of carburizers, namely low nitrogen carburizer, anthracite and coke are used for carburization of vanadium-bearing hot metal weighing 500 g at temperature of 1450, 1500 and 1550 °C respectively. Carbon increments of low nitrogen carburizer, anthracite and coke fall in descending order. It was found by comprehensive analysis that anthracite is the most cost-effective carburizer among three carburizers. Magnitude of apparent rate constant of carburization reactions is 10−4 s−1. It is found that the carburization rate increase with temperature.
Foundation Item: Item Sponsored by National Science Foundation of China (51674092).
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Rohrmann B (1985) Vanadium in South Africa. J South Africa Inst Mining Metall 85(5):141–150
Gustafsson S, Wenzhong W (1985) Recovery of vanadium from hot metal. Intern J Mineral Process 15:103–115
Lindvall M (2006) Selective oxidation of vanadium prior to iron and phosphorus. Master thesis, Luleå University of Technology
Smirnov LA, Kushnarev AV, Fomichev MS et al (2013) Oxygen-converter processing of vanadium-bearing hot metal. Steel Trans 43(9):587–592
Huang X (2008) Principle of iron and steel metallurgy. Metallurgical Industry Press, Beijing. (In Chinese)
Dai J (2005) The study and application of the new style of the carburizer in steel. Master thesis, Harbin University of Science. (In Chinese)
Chen S, Wei B, Long L (2008) Application of carburization material on production of cast iron. Foundry Technol Die Casting 29(6):823–826. (In Chinese)
Chen J (2012) Development and application of carbon-alloy material for steelmaking. Steelmaking 28(5):16–19. (In Chinese)
Li S (2005) Experimental study on increasing Si and C element using the waste material of graphite electrode during metallurgical melting process. Master thesis, Jilin University. (In Chinese)
Gan Z, Jin Y, Bi X et al (2003) Technology of recarburization process in melting cast iron. Foundry 52(3):157–160. (In Chinese)
Gu J, Li C, Liang S et al (1992) Study on carburization effect of different carburization material and the effect on steel quality 13(2):18–26. (In Chinese)
Cai T, Lin M, Yang Q et al (1990) Recarburization and desulfurization of flow carbon hot metal containing vanadium. Iron Steel 25(7):22–26. (In Chinese)
Wright JK, Baldock BR (1988) Dissolution kinetics of particulate graphite injected into iron/carbon melts. Metall Trans B 19(3):375–382
Marcelo MB, Krishna Murthy GG, John EF (1993) Experimental investigation of dissolution rates of carbonaceous materials in liquid iron-carbon melts. Metall Mater Trans B 24(4):629–637
Wu C, Sahajwalla V (2000) Dissolution rates of coals and graphite in Fe–C–S melts in direct ironmaking: Influence of melt carbon and sulfur on carbon dissolution. Metall Mater Trans B 31(2):243–251
Bandyopadhyay D, Singh SD, Sanyal D et al (2003) A study on dissolution kinetics of carbon in liquid iron bath. Chem Eng J 94(2):79–92
Michael CW, Brian MJ, Sharon NA et al (2008) Formation of a mineral layer during coke dissolution into liquid iron and its influence on the kinetics of coke dissolution rate. Metall Mater Trans B 39(3):418–430
Michael CW, Brian MJ, Sharon NA et al (2011) The effect of sulfur concentration in liquid iron on mineral layer formation during coke dissolution. Metall Materi Trans B 42(4):642–651
Acknowledgements
Thanks for National Science Foundation of China (51674092).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Ma, D. (2018). Experimental Study on Carburization of Higher Vanadium-Bearing Hot Metal. In: Hwang, JY., et al. 9th International Symposium on High-Temperature Metallurgical Processing. TMS 2018. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-319-72138-5_52
Download citation
DOI: https://doi.org/10.1007/978-3-319-72138-5_52
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-72137-8
Online ISBN: 978-3-319-72138-5
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)